This invention relates to an oriented polyethylene film comprising polyethylene having: (A) a melt flow index of 1.0 g/10 min or more, (B) a density of 0.90 g/cm.sup.3 to less than 0.940 g/cm.sup.3, (C) a g′.sub.LCB of greater than 0.8, (D) ratio of comonomer content at Mz to comonomer content at Mw is greater than 1.0, (E) ratio of comonomer content at Mn to comonomer content at Mw is greater than 1.0, and (F) a ratio of the g′.sub.LCB to the g′.sub.Zave is greater than 1.0, where the film has a 1% secant in the transverse direction of 70,000 psi or more and Dart Drop of 350 g/mil or more.

This invention relates to an oriented polyethylene film comprising polyethylene having: (A) a melt flow index of 1.0 g/10 min or more, (B) a density of 0.90 g/cm.sup.3 to less than 0.940 g/cm.sup.3, (C) a g′.sub.LCB of greater than 0.8, (D) ratio of comonomer content at Mz to comonomer content at Mw is greater than 1.0, (E) ratio of comonomer content at Mn to comonomer content at Mw is greater than 1.0, and (F) a ratio of the g′.sub.LCB to the g′.sub.Zave is greater than 1.0, where the film has a 1% secant in the transverse direction of 70,000 psi or more and Dart Drop of 350 g/mil or more.

Provided is a curable resin composition for obtaining a cured product that can satisfy both high heat resistance and high adhesiveness to metal, a cured product thereof, and methods of producing the curable resin composition and the cured product, and a semiconductor device using the cured product as a sealant. A curable resin composition containing (A) a multifunctional benzoxazine compound having two or more benzoxazine rings, (B) a multifunctional epoxy compound having at least one norbornane structure and at least two epoxy groups, (C) a curing agent, (D) a triazole-based compound, and optionally (E) a curing accelerator and (F) an inorganic filler, a cured product thereof, and methods of producing the curable resin composition and the cured product. A semiconductor device in which a semiconductor element is disposed in a cured product obtained by curing a curable resin composition containing components (A) to (D), and optionally components (E) and (F).

Provided is a curable resin composition for obtaining a cured product that can satisfy both high heat resistance and high adhesiveness to metal, a cured product thereof, and methods of producing the curable resin composition and the cured product, and a semiconductor device using the cured product as a sealant. A curable resin composition containing (A) a multifunctional benzoxazine compound having two or more benzoxazine rings, (B) a multifunctional epoxy compound having at least one norbornane structure and at least two epoxy groups, (C) a curing agent, (D) a triazole-based compound, and optionally (E) a curing accelerator and (F) an inorganic filler, a cured product thereof, and methods of producing the curable resin composition and the cured product. A semiconductor device in which a semiconductor element is disposed in a cured product obtained by curing a curable resin composition containing components (A) to (D), and optionally components (E) and (F).

A coating agent is capable of forming a coating film that has enhanced adhesion and adherence to a substrate, and enhanced water resistance as well and composed mainly of an aqueous material. A process of forming a coating agent uses the coating agent, a primer treatment process uses the coating agent, a process of doing repairs to concretes uses the coating agent, and a process of laying down roads uses the coating agent. The coating agent is composed mainly of a polyphenol derivative and containing a polymerizing agent, and has a pH of 9 or less. The polymerizing agent contains a compound having two or more functional groups selected from the group of an amino group and a mercapto group per molecule. In the process of forming a coating film, the coating agent is applied onto a substrate in an alkaline environment having a pH of greater than 9.

A process for producing liquid overbased alkali or alkaline earth metal carboxylates is disclosed wherein a para-cumyl phenol is used as a promoter of the process and the carboxylates produced are used as stabilizers for PVC.

A process for producing liquid overbased alkali or alkaline earth metal carboxylates is disclosed wherein a para-cumyl phenol is used as a promoter of the process and the carboxylates produced are used as stabilizers for PVC.

A process for producing liquid overbased alkali or alkaline earth metal carboxylates is disclosed wherein a para-cumyl phenol is used as a promoter of the process and the carboxylates produced are used as stabilizers for PVC.

A coating agent includes a main component containing a polyphenol derivative and a polymerizing agent. The coating agent has a pH of no greater than 9, and the polymerizing agent contains a compound having two or more functional groups selected from the group consisting of an amino group and a mercapto group per molecule.

A water emulsion and film are provided comprising a polyacrylate random copolymer synthesized from acrylic acid (AA), butyl acrylate (BA), methyl methacrylate (MMA), and 2-ethylhexyl acrylate (EHA). The emulsion may be applied to a surface in liquid form, quickly drying to yield a peelable protective barrier film.