The present application provides a method for producing a cured product that includes: (I) heating a thermosetting composition containing a styrene-butadiene-styrene block copolymer (SBS) (A) and a thermal radical generator (B) within a temperature range of 120° C. to 180° C. until 30% or more of double bonds derived from 1,2-bond structure in a butadiene block react; and (II) then heating the thermosetting composition within a temperature range of 181° C. to 300° C. until 50% or more of the double bonds derived from 1,2-bond structure in a butadiene block react.

The present application provides a method for producing a cured product that includes: (I) heating a thermosetting composition containing a styrene-butadiene-styrene block copolymer (SBS) (A) and a thermal radical generator (B) within a temperature range of 120° C. to 180° C. until 30% or more of double bonds derived from 1,2-bond structure in a butadiene block react; and (II) then heating the thermosetting composition within a temperature range of 181° C. to 300° C. until 50% or more of the double bonds derived from 1,2-bond structure in a butadiene block react.

An encapsulant film is made from a composition comprising (A) a non-polar ethylene-based polymer having a density of 0.850 g/cc to 0.890 g/cc; (B) an organic peroxide; (C) a silane coupling agent; and (D) a co-agent comprising triallyl phosphate.

An encapsulant film is made from a composition comprising (A) a non-polar ethylene-based polymer having a density of 0.850 g/cc to 0.890 g/cc; (B) an organic peroxide; (C) a silane coupling agent; and (D) a co-agent comprising triallyl phosphate.

An encapsulant film is made from a composition comprising (A) a non-polar ethylene-based polymer having a density of 0.850 g/cc to 0.890 g/cc; (B) an organic peroxide; (C) a silane coupling agent; and (D) a co-agent comprising triallyl phosphate.

Provided are a thermosetting resin composition and a prepreg, laminate and printed circuit board using same. The thermosetting resin composition comprises a resin component, the resin component comprising a modified cyclic olefin copolymer having a structure as shown in formula I and another unsaturated resin. By introducing a methacrylate end group having a certain polarity into a cyclic olefin copolymer, a modified cyclic olefin copolymer is formed. The modified cyclic olefin copolymer can form a thermosetting material by means of cross-linking with itself or another unsaturated resin, whereby the bonding property can be significantly improved while retaining the excellent dielectric properties of the cyclic olefin copolymer itself. The laminate prepared using the thermosetting resin composition has good dielectric properties, a good peel strength and a good heat resistance, and can meet all the performance requirements for printed circuit board substrates in the current high-frequency and high-speed communication field.

Provided are a thermosetting resin composition and a prepreg, laminate and printed circuit board using same. The thermosetting resin composition comprises a resin component, the resin component comprising a modified cyclic olefin copolymer having a structure as shown in formula I and another unsaturated resin. By introducing a methacrylate end group having a certain polarity into a cyclic olefin copolymer, a modified cyclic olefin copolymer is formed. The modified cyclic olefin copolymer can form a thermosetting material by means of cross-linking with itself or another unsaturated resin, whereby the bonding property can be significantly improved while retaining the excellent dielectric properties of the cyclic olefin copolymer itself. The laminate prepared using the thermosetting resin composition has good dielectric properties, a good peel strength and a good heat resistance, and can meet all the performance requirements for printed circuit board substrates in the current high-frequency and high-speed communication field.

A vehicle bond filler formulation is provided that includes a part A having curable resin and a monomer reactive diluent. A part B storage-separate, cure initiator package contains a free-radical cure initiator. At least one color changing dye adapted to change color upon mixing the part A and the part B and within ±5 minutes of cure of the curable resin to a sandable condition is present in either the part A or a separate part C, a guide coat colorant, or a combination thereof. A process of for repairing a vehicle body is also provided that includes mixing a part A containing the at least one color changing dye with the part B to form an internal guide coat mixture applied to a substrate of the vehicle body in need of repair. The mixture cures causing the color changing dye to the terminal change color within ±5 minutes of cure of the curable resin to a sandable condition.

The present disclosure discloses a low-water-vapor-permeability polyolefin-elastomer film and its preparation method. The film comprises: 50-100 mass parts of a matrix resin, 0-40 mass parts of a modified resin, 0.001-2 mass parts of an activator, 0.1-3 mass parts of an organic peroxide, 0.02-5 mass parts of an assistant cross-linker, 0.02-2 mass parts of a silane coupling agent, 0.005-2 mass parts of a light stabilizer, and 0-20 mass parts of a water blocking filler. In the present disclosure, by adding the modified resin and the activator that have an active group, a cross-linking degree and a cross-linking density of the film are improved, and a water-vapor permeability is reduced; by adding the water blocking filler, the water blocking property of the film is further improved, thereby ensuring reliability of the assembly, and prolonging service life of the assembly.

The present disclosure discloses a low-water-vapor-permeability polyolefin-elastomer film and its preparation method. The film comprises: 50-100 mass parts of a matrix resin, 0-40 mass parts of a modified resin, 0.001-2 mass parts of an activator, 0.1-3 mass parts of an organic peroxide, 0.02-5 mass parts of an assistant cross-linker, 0.02-2 mass parts of a silane coupling agent, 0.005-2 mass parts of a light stabilizer, and 0-20 mass parts of a water blocking filler. In the present disclosure, by adding the modified resin and the activator that have an active group, a cross-linking degree and a cross-linking density of the film are improved, and a water-vapor permeability is reduced; by adding the water blocking filler, the water blocking property of the film is further improved, thereby ensuring reliability of the assembly, and prolonging service life of the assembly.