The composition includes a polyester resin comprising at least one α,β-unsaturated ester group, an epoxy resin, a compound comprising at least one hydroxyl group; and a photoinitiator that generates acid on exposure to actinic radiation. A method of repairing a damaged surface using the composition is also described.

The present disclosure discloses a low-water-vapor-permeability polyolefin-elastomer film and its preparation method. The film comprises: 50-100 mass parts of a matrix resin, 0-40 mass parts of a modified resin, 0.001-2 mass parts of an activator, 0.1-3 mass parts of an organic peroxide, 0.02-5 mass parts of an assistant cross-linker, 0.02-2 mass parts of a silane coupling agent, 0.005-2 mass parts of a light stabilizer, and 0-20 mass parts of a water blocking filler. In the present disclosure, by adding the modified resin and the activator that have an active group, a cross-linking degree and a cross-linking density of the film are improved, and a water-vapor permeability is reduced; by adding the water blocking filler, the water blocking property of the film is further improved, thereby ensuring reliability of the assembly, and prolonging service life of the assembly.

A crosslinked fluororesin-coated pump rotor manufacturing method is a method for manufacturing a pump rotor having flat rotor side surfaces and provided with a coating layer of a crosslinked fluororesin on each rotor side surface, the method including: screen-printing a dispersion liquid obtained by dispersing particles of a fluororesin in a solvent, on the rotor side surface by using a screen plate having an opening having a shape in which the opening does not protrude from an outer peripheral edge of the rotor side surface; then heating the pump rotor to a temperature equal to or higher than a melting point of the fluororesin to bake the fluororesin on the rotor side surface; and then irradiating the fluororesin with radiation to crosslink the fluororesin.

The present invention relates to a method for producing a three-dimensional (3D) printed article with a photocurable silicone composition involving a silicone containing as end-group specific (meth)acrylate groups.

The present invention relates to a method for producing a three-dimensional (3D) printed article with a photocurable silicone composition involving a silicone containing as end-group specific (meth)acrylate groups.

A solvent-less hybrid curable composition is prepared from grafting polyesters or polyamides onto a (meth)acrylic copolymer backbone. Besides the many benefits of a solvent-less system, the hybrid curable composition forms strong adhesion to polar substrates, widens the use temperatures, and enables faster processing speeds than conventional hybrid curable compositions. The solvent-less hybrid curable composition forms an optically clear single phase that is suitable as tapes and labels, or in electronic, optoelectronic, OLED and photovoltaic devices, and the like.

Provided is an irradiation-crosslinked ethylene propylene diene monomer (EPDM) composition containing: EPDM 30 to 80 phr (parts per hundred resin) free of a crosslinking agent, a polyolefin (PO) resin 10 to 50 phr, a silicone rubber 5 to 40 phr, a flame retardant 20 to 30 phr, a crosslinking accelerator 5 to 10 phr, a crosslinking assistant 1 to 5 phr, an antioxidant 5 to 15 phr, and a lubricant 0.25 to 5 phr. Provided is a cable produced by: providing the irradiation-crosslinked EPDM composition; first kneading the composition using a kneader; second kneading the first kneaded composition using a roll mill; extruding the second kneaded composition using an extruder, and then cutting the extruded composition to produce pellets as a raw material for the cable; forming a cable of a predetermined length by extruding the pellets using an extruder; and irradiation-crosslinking the formed cable using an electron beam accelerator.

The present invention discloses a photo-crosslinked rubber composition and application thereof. The rubber composition comprises a rubber matrix and an initiator. Based on 100 parts by weight of the rubber matrix, the rubber matrix comprises a branched polyethylene with a content represented as A, in which 0<A≤100, and an ethylene-propylene rubber with a content represented as B, in which 0≤B<100; and the initiator accounts for 0.1-10 parts, and the initiator includes at least one of a cationic photoinitiator and a free radical photoinitiator. In the rubber composition, the ethylene-propylene rubber is partially or completely replaced by the branched polyethylene. The rubber composition can be used for rubber product crosslinked by ultraviolet light, including wire, cable, film, glove, condom, and medical catheter, which achieves excellent elasticity, electrical insulation property, aging resistance and ozone resistance, and also has good mechanical strength.

The present disclosure relates to a precursor composition of a pressure sensitive adhesive comprising: a) a (co)polymeric base component having a weight-average molecular weight (M.sub.w) no greater than 500,000 g/mol and comprising at least one reactive functional group (X); and b) a multi-functional oligomeric branching compound comprising an oligomer backbone and having a weight-average molecular weight (M.sub.w) greater than 250 g/mol, wherein the multi-functional oligomeric branching compound comprises at least two complementary reactive functional groups (Y) which are capable of chemically reacting with the at least one reactive functional group (X) of the (co)polymeric base component.

There is provided a curable composition for forming an anti-reflective film. The composition includes: (a) hollow silica nanoparticles; (b) a siloxane binder having reactive groups; (c) at least one additional material having reactive groups; (d) an initiator; and (e) solvent. The siloxane binder is present in an amount that is at least 50% by weight of the total weight of (siloxane binder+additional materials having reactive groups). The weight ratio of hollow silica nanoparticles to the total of (siloxane binder+additional materials having reactive groups) is no greater than 1.75 to 1.