The invention relates to a method for coating surfaces, to a corresponding coating, and to the use of the objects coated in accordance with said method. The invention relates to a method for coating metal surfaces of substrates, comprising or consisting of the following steps: I. providing a substrate having a cleaned metal surface, II. contacting and coating metal surfaces with an aqueous composition in the form of a dispersion and/or suspension, IX. optionally rinsing the organic coating, and X. drying and/or baking the organic coating or XI. optionally drying the organic coating and coating with a coating composition of the same type or a further coating composition before a drying process and/or baking process, wherein in step II the coating is performed with an aqueous composition in the form of a dispersion and/or suspension containing 2.5 to 45 wt % of at least one non-ionic stabilized binder and 0.1 to 2.0 wt % of a gelling agent, wherein the aqueous composition has a pH value in the range of 0.5 to 7 and forms, with the cations eluted from the metal surface in the pretreatment step and/or during the contacting in step II, a coating based on an ionogenic gel.

A method for coating a metal substrate with a white, off-white or gray colored autodeposited coating comprising water, polymeric resin, HF and pigment particles comprising a core of titanium dioxide, an intermediate zirconia and/or alumina layer, and an outer organic layer, optionally the particles are treated with an anionic surfactant.

The invention relates to a method for coating surfaces, to a corresponding coating, and to the use of the objects coated in accordance with said method. The invention relates to a method for coating metal surfaces of substrates, comprising or consisting of the following steps: I. providing a substrate having a cleaned metal surface, II. contacting and coating metal surfaces with an aqueous composition in the form of a dispersion and/or suspension, IX. optionally rinsing the organic coating, and X. drying and/or baking the organic coating or XI. optionally drying the organic coating and coating with a coating composition of the same type or a further coating composition before a drying process and/or baking process, wherein in step II the coating is performed with an aqueous composition in the form of a dispersion and/or suspension containing 2.5 to 45 wt % of at least one non-ionic stabilized binder and 0.1 to 2.0 wt % of a gelling agent, wherein the aqueous composition has a pH value in the range of 0.5 to 7 and forms, with the cations eluted from the metal surface in the pretreatment step and/or during the contacting in step II, a coating based on an ionogenic gel.

The invention relates to a method for coating surfaces, to a corresponding coating, and to the use of the objects coated in accordance with said method. The invention relates to a method for coating metal surfaces of substrates, comprising or consisting of the following steps: I. providing a substrate having a cleaned metal surface, II. contacting and coating metal surfaces with an aqueous composition in the form of a dispersion and/or suspension, IX. optionally rinsing the organic coating, and X. drying and/or baking the organic coating or XI. optionally drying the organic coating and coating with a coating composition of the same type or a further coating composition before a drying process and/or baking process, wherein in step II the coating is performed with an aqueous composition in the form of a dispersion and/or suspension containing 2.5 to 45 wt % of at least one non-ionic stabilized binder and 0.1 to 2.0 wt % of a gelling agent, wherein the aqueous composition has a pH value in the range of 0.5 to 7 and forms, with the cations eluted from the metal surface in the pretreatment step and/or during the contacting in step II, a coating based on an ionogenic gel.

The invention is directed to an acidic aqueous metal pretreatment solution that comprises amino-functional organosilanes, complex anions of the elements Zr, Ti, Hf and/or Si as well as oxyacids of phosphorus; a process for the treatment of metal substrates, especially selected from zinc and zinc-coated steel substrates, wherein metal pretreatment solutions of this invention are applied to reduce corrosion when applied to metal surfaces and in addition confer good adhesion properties for subsequently coated organic lacquers.

A method and composition for coating surfaces, a corresponding coating and the use of objects coated according to said method. A cleaned, metallic surface is contacted with an aqueous composition that is a dispersion or suspension, and drying and/or baking the organic coating or optionally, drying the organic coating and coating with an equivalent or additional coating composition prior to a drying and/or baking. The aqueous composition has a pH of 4 to 11 and contains an anionic polyelectrolyte in a quantity of 0.01 to 5.0 wt. % relative to the total mass of the composition, which may have a solids content of from 2 to 40 wt. %. The solids have an average particle size from 10 to 1000 nm. A coating forms on the basis of an ionogenic gel which binds cations released from the metallic surface that originate from a pretreatment stage or from the contacting.

A method for electroless coating of a substrate by applying an activating coat of polyelectrolyte or salt with a first aqueous composition, rinsing of the activating coat such that the activating coat is not entirely removed The activated surface that has remained after rinsing is then contacted with an aqueous composition in the form of a solution, emulsion or suspension to form an organic secondary coat (precipitation coat), and drying. The activating coat contains at least one cationic polyelectrolyte or at least one cationic salt in solution in water. The aqueous composition which forms the secondary coat contains constituents which can be precipitated, deposited and/or salted out and which are anionically, zwitterionically, sterically or cationically stabilized. The dry film formed in the process, which is made of the activating coat and the secondary coat, has a thickness of at least 1 m.

A method for electroless coating of substrates by applying an activating coat of polyelectrolyte or salt with a first aqueous composition; rinsing the activating coat such that the activating coat not being entirely removed; contacting and coating of the activated surfaces that have remained after rinsing with an aqueous composition in the form of a solution, emulsion or suspension, to form an organic secondary coat; and drying. The activating coat is a solution, emulsion or suspension containing a anionic polyelectrolyte or at least one anionic salt in solution in water. The aqueous composition forming the secondary coat has constituents which can be precipitated, deposited or salted out and which are anionically, zwitterionically, sterically or cationically stabilized. The dry film formed in the process, comprising the activating coat and the secondary coat, has a thickness of at least 1 m.