In one aspect, a cohesive product comprises a substrate and a cohesive layer provided on at least one surface of the substrate. The cohesive layer comprises a cohesive composition including a cohesive component admixed with a glitter component. The cohesive component further comprising a thickening agent in an amount sufficient to maintain the glitter component substantially uniformly distributed in the cohesive composition. In a further aspect, a method of manufacturing a cohesive produce is provided.

A method for producing a polymer latex, includes a step of emulsifying a polymer solution of a synthetic polyisoprene and/or a styrene-isoprene-styrene block copolymer, in water in the presence of a rosin and/or a rosin metal salt, thereby obtaining an emulsified liquid, wherein the rosin and/or the rosin metal salt to be used have/has a total content rate of abietic acid, neoabietic acid and palustric acid, and salts thereof, of 5% by weight or less.

A method for producing a polymer latex, includes a step of emulsifying a polymer solution of a synthetic polyisoprene and/or a styrene-isoprene-styrene block copolymer, in water in the presence of a rosin and/or a rosin metal salt, thereby obtaining an emulsified liquid, wherein the rosin and/or the rosin metal salt to be used have/has a total content rate of abietic acid, neoabietic acid and palustric acid, and salts thereof, of 5% by weight or less.

The aqueous adhesive for a tennis ball includes rubber latex. The rubber latex is a mixture of liquid rubber latex and solid rubber latex. When a solid content in the aqueous adhesive is measured at a temperature of 140° C. by a curelastometer, a torque is not less than 0.26 N.Math.m after 10 minutes from start of heating. The tennis ball includes a seam portion formed of the aqueous adhesive for a tennis ball.

The aqueous adhesive for a tennis ball includes rubber latex. The rubber latex is a mixture of liquid rubber latex and solid rubber latex. When a solid content in the aqueous adhesive is measured at a temperature of 140° C. by a curelastometer, a torque is not less than 0.26 N.Math.m after 10 minutes from start of heating. The tennis ball includes a seam portion formed of the aqueous adhesive for a tennis ball.

The aqueous adhesive for a tennis ball includes rubber latex. The rubber latex is a mixture of liquid rubber latex and solid rubber latex. When a solid content in the aqueous adhesive is measured at a temperature of 140° C. by a curelastometer, a torque is not less than 0.26 N.Math.m after 10 minutes from start of heating. The tennis ball includes a seam portion formed of the aqueous adhesive for a tennis ball.

A latex of a synthetic rubber, wherein the content rate of a particle having a particle size of 5 m or more in a particle size distribution of a synthetic rubber particle included in the latex, as determined on a number basis, is less than 3,000 ppm by weight. A latex of a synthetic rubber is excellent in mechanical stability and can provide a film molded article such as a dip molded article excellent in tensile strength and elongation.

A latex of a synthetic rubber, wherein the content rate of a particle having a particle size of 5 m or more in a particle size distribution of a synthetic rubber particle included in the latex, as determined on a number basis, is less than 3,000 ppm by weight. A latex of a synthetic rubber is excellent in mechanical stability and can provide a film molded article such as a dip molded article excellent in tensile strength and elongation.

A synthetic polyisoprene latex containing synthetic polyisoprene, wherein the synthetic polyisoprene constituting the synthetic polyisoprene latex includes a low-molecular weight synthetic isoprene chain having a molecular weight of less than 1,000,000 at a content rate of 10 to 70% by weight and a high-molecular weight synthetic isoprene chain having a molecular weight of 1,000,000 or more at a content rate of 30 to 90% by weight. Also, a method for producing the synthetic polyisoprene latex, wherein the synthetic polyisoprene containing the low-molecular weight synthetic isoprene chain and the high-molecular weight synthetic isoprene chain is obtained by polymerizing a monomer containing isoprene in an organic solvent by use of an organic alkali metal catalyst.

A synthetic polyisoprene latex containing synthetic polyisoprene, wherein the synthetic polyisoprene constituting the synthetic polyisoprene latex includes a low-molecular weight synthetic isoprene chain having a molecular weight of less than 1,000,000 at a content rate of 10 to 70% by weight and a high-molecular weight synthetic isoprene chain having a molecular weight of 1,000,000 or more at a content rate of 30 to 90% by weight. Also, a method for producing the synthetic polyisoprene latex, wherein the synthetic polyisoprene containing the low-molecular weight synthetic isoprene chain and the high-molecular weight synthetic isoprene chain is obtained by polymerizing a monomer containing isoprene in an organic solvent by use of an organic alkali metal catalyst.