With excellent heat retention of molten metal and better productivity/work environment, regardless of low-speed or high-speed, the usable die lubricant for die casting will be provided. An aqueous die lubricant for die casting in which a phyllosilicate mineral is dispersed at a concentration of 0.005 wt % or more and less than 5 wt % and has a particle diameter of 0.1 μm or less during the dispersion.

With excellent heat retention of molten metal and better productivity/work environment, regardless of low-speed or high-speed, the usable die lubricant for die casting will be provided. An aqueous die lubricant for die casting in which a phyllosilicate mineral is dispersed at a concentration of 0.005 wt % or more and less than 5 wt % and has a particle diameter of 0.1 μm or less during the dispersion.

A sliding member includes a back metal layer and a sliding layer on the back metal layer. The sliding layer includes a synthetic resin matrix and graphite particles dispersed in the matrix in a volume ratio of 5-50% of that of the sliding layer. The graphite particles are composed of spheroidal and flake-like particles. The flake-like particles have a volume ratio of 10-40% of total graphite particles. The spheroidal particles have a cross-sectional structure with a plurality of AB planes of a graphite crystal laminated along a curved particle surface, from the surface toward a center direction. The flake-like graphite particles have a cross-sectional structure with the plurality of AB planes laminated in a thickness direction of the thin plate shape. The spheroidal particles have an average particle size of 3-50 μm, and the flake-like graphite particles have an average particle size of 1-25 μm.

Embodiments of the present disclosure provide for mixtures, methods for making mixtures, articles, methods for making articles, and methods of using articles.

Embodiments of the present disclosure provide for mixtures, methods for making mixtures, articles, methods for making articles, and methods of using articles.

The present invention addresses a problem of providing a grease composition for a speed reducer and a speed increaser, excellent in both leakage prevention performance and energy transfer efficiency. The grease composition for a speed reducer and a speed increaser contains a base oil (A), and nanofibers (B) having a thickness (d) of 1 to 500 nm, wherein the nanofibers (B) are one or more selected from cellulose nanofibers (B1) and modified cellulose nanofibers (B2).

The present invention addresses a problem of providing a grease composition for a speed reducer and a speed increaser, excellent in both leakage prevention performance and energy transfer efficiency. The grease composition for a speed reducer and a speed increaser contains a base oil (A), and nanofibers (B) having a thickness (d) of 1 to 500 nm, wherein the nanofibers (B) are one or more selected from cellulose nanofibers (B1) and modified cellulose nanofibers (B2).

With excellent heat retention of molten metal and better productivity/work environment, regardless of low-speed or high-speed, the usable die lubricant for die casting will be provided. An aqueous die lubricant for die casting in which a phyllosilicate mineral is dispersed at a concentration of 0.005 wt % or more and less than 5 wt % and has a particle diameter of 0.1 μm or less during the dispersion.

With excellent heat retention of molten metal and better productivity/work environment, regardless of low-speed or high-speed, the usable die lubricant for die casting will be provided. An aqueous die lubricant for die casting in which a phyllosilicate mineral is dispersed at a concentration of 0.005 wt % or more and less than 5 wt % and has a particle diameter of 0.1 μm or less during the dispersion.

An environmentally acceptable lubricating grease, comprising: a) 50 wt % to 90 wt % of a biodegradable base oil comprising a biodegradable ester as base oil; b) 3 wt % to 25 wt % of a thickener selected from b1) 3 wt % to 12 wt % biodegradable calcium soap, b2) 3 wt % to 25 wt % bentonites, b3) and mixtures thereof; c) 4 wt % to 40 wt % additives, comprising c1) 1 wt % to 12 wt % fumed silicon dioxide and/or polytetrafluoroethylene and/or mixtures thereof, c2) 2 wt % to 45 wt % of a polymer selected from polyisobutylene, polyisobutylene/butene copolymer, polymethacrylates, polyesters and mixtures thereof, c3) 0.5 wt % to 20 wt % of a solid lubricant.