A sliding member includes a back metal layer and a sliding layer on the back metal layer. The sliding layer includes a synthetic resin matrix and graphite particles dispersed in the matrix in a volume ratio of 5-50% of that of the sliding layer. The graphite particles are composed of spheroidal and flake-like particles. The flake-like particles have a volume ratio of 10-40% of total graphite particles. The spheroidal particles have a cross-sectional structure with a plurality of AB planes of a graphite crystal laminated along a curved particle surface, from the surface toward a center direction. The flake-like graphite particles have a cross-sectional structure with the plurality of AB planes laminated in a thickness direction of the thin plate shape. The spheroidal particles have an average particle size of 3-50 μm, and the flake-like graphite particles have an average particle size of 1-25 μm.

An oil tempered wire includes a steel wire and a lubricant coating disposed around an outer circumference of the steel wire, wherein the lubricant coating includes a lubricant component resin and a binder resin, the lubricant component resin is at least one selected from polyacetals, polyimides, melamine resins, acrylic resins and fluororesins, the deposited mass of the lubricant coating is not less than 1.0 g/m2 and not more than 4.0 g/m2, and the surface roughness Rz of the steel wire is not more than 8.0 m.

This invention provides a preparation method of solid self-lubricating material with high temperature resistance, including steps described as follows: first, mixing polymer matrix resin and nano lubricating filler to compose a uniform raw material powders; then, placing the raw material powders in the cavity of hot-press die; keeping the temperature for 90-120 min at the first prepressing temperature, controlling the hot-pressing pressure under the third pre-loading pressure, and gradually increasing the temperature to the solid-phase molding temperature of the material; gradually reducing the temperature to the first preloading temperature after the solid-phase molding is completed; next, removing the pressure, finally, obtaining the solid self-lubricating material by naturally cooling to normal temperature and demoulding. This invention adjusts the hot-pressing molding temperature according to the drift value of glass transition temperature, in order to avoid the degradation of tribological properties and mechanical properties caused by uneven plasticization and overheating of composite materials during the compression molding process.

An oil tempered wire includes a steel wire and a lubricant coating disposed around an outer circumference of the steel wire, wherein the lubricant coating includes a lubricant component resin and a binder resin, the lubricant component resin is at least one selected from polyacetals, polyimides, melamine resins, acrylic resins and fluororesins, the deposited mass of the lubricant coating is not less than 1.0 g/m2 and not more than 4.0 g/m2, and the surface roughness Rz of the steel wire is not more than 8.0 m.

This invention provides a preparation method of solid self-lubricating material with high temperature resistance, including steps described as follows: first, mixing polymer matrix resin and nano lubricating filler to compose a uniform raw material powders; then, placing the raw material powders in the cavity of hot-press die; keeping the temperature for 90-120 min at the first prepressing temperature, controlling the hot-pressing pressure under the third pre-loading pressure, and gradually increasing the temperature to the solid-phase molding temperature of the material; gradually reducing the temperature to the first preloading temperature after the solid-phase molding is completed; next, removing the pressure, finally, obtaining the solid self-lubricating material by naturally cooling to normal temperature and demoulding. This invention adjusts the hot-pressing molding temperature according to the drift value of glass transition temperature, in order to avoid the degradation of tribological properties and mechanical properties caused by uneven plasticization and overheating of composite materials during the compression molding process.

A sliding member according to the present disclosure contains, in a sliding layer, a synthetic resin, a solid lubricant, and an additive. The synthetic resin is a polyimide, a polyamide imide, a polybenzimidazole, a polyphenyl sulfone, a polyether sulfone, a polyether ether ketone, or a combination thereof. The solid lubricant is a polytetrafluoroethylene, a tetrafluoroethylene-perfluoroalkoxyethylene copolymer, molybdenum disulfide, a tetrafluoroethylene-hexafluoropropylene copolymer, or a combination thereof. The contained amount of the solid lubricant in the sliding layer is 5.0-40.0 vol. %. The additive is bentonite, smectite clay mineral, silica, a polyamide, or a combination thereof. The contained amount of the additive in the sliding layer is 0.1-9.0 vol. %.