The present disclosure provides a hot-press formed part comprising a plated steel sheet and an aluminum alloy plated layer formed on the plated steel sheet, wherein the aluminum alloy plated layer comprises: an alloying layer (I) formed on the plated steel sheet and containing, by weight %, 5-30% of Al; an alloying layer (II) formed on the alloying layer (I) and containing, by weight %, 30 to 60% of Al; an alloying layer (III) formed on the alloying layer (II) and containing, by weight %, 20-50% of Al and 5-20% of Si; and an alloying layer (IV) formed continuously or discontinuously on at least a part of the surface of the alloying layer (III), and containing 30-60% of Al, wherein the rate of the alloying layer (III) exposed on the outermost surface of the aluminum alloy plated layer is 10% or more.

The present invention relates to a method and to a device (10) for producing a wheel rim (1) for a vehicle wheel (3), and to a method for producing a vehicle wheel (3).

A hot-stamping formed body has a predetermined chemical composition and includes microstructure which includes residual austenite of which an area ratio is in a range of 20% to 30%. Among grain boundaries of crystal grains of bainite and tempered martensite in the microstructure, a ratio of a length of a grain boundary having a rotation angle in a range of 55° to 75° to a total length of a grain boundary having a rotation angle in a range of 4° to 12°, a grain boundary having a rotation angle in a range of 49° to 54°, and a grain boundary having a rotation angle in a range of 55° to 75° to the <011> direction as a rotation axis is 30% or more.

An method of manufacturing a hot press-formed member comprises heating a blank of an aluminum-based plated steel sheet in a heating furnace, removing the heated blank from the heating furnace and conveying the removed blank between an upper mold portion and a lower mold portion of a mold, mounted on a press, to be seated; and performing a forming process after the upper mold portion of the mold is in contact with the seated blank.

Method of hot press forming an article from zinc or zinc alloy coated steel, wherein the steel is a product obtained by: casting the molten steel into slabs; reheating the slabs; hot rolling the steel into a strip, preferably with an FRT above Ar3; coiling the hot rolled steel strip; pickling the hot rolled steel strip; continuous annealing the strip; hot dip coating the steel strip with the zinc or zinc alloy whilst: using a dipping time of 3 seconds or more; maintaining in the hot dip bath a bath temperature of 420° C. to 500° C.; wherein the zinc bath contains essentially zinc, at least 0.1% Al, and optionally up to 5% Al and optionally up to 4% Mg, the rest of the bath including further elements all individually less than 0.3%, and unavoidable impurities; hot press forming the article.

The invention relates to a process for producing an at least partly quenched and tempered sheet steel component, where the process comprises the following steps: providing a sheet steel, at least partly austenitizing the sheet steel at a temperature of at least Ac1, at least partly hardening the at least partly austenitized sheet steel to give an at least partly hardened sheet steel component, where the at least partly austenitized sheet steel is cooled to a temperature below Ms, at least partly annealing the at least partly hardened sheet steel component at a temperature of less than Ac1 for producing an at least partly quenched and tempered sheet steel component. A further subject of the invention is an at least partly quenched and tempered sheet steel component.

Disclosed are thermoformed component having excellent coating adhesion and a method for manufacturing the same. The thermoformed component comprises a substrate layer and an aluminum coating coated on at least one surface of the substrate layer, wherein the average roughness Ra of a surface of the thermoformed component is between 1.0 μm and 3.0 μm, the peak height and the peak-to-valley height Rt are between 8 μm and 30 μm, and the roughness peak count Rpc is greater than or equal to 50. The thermoformed component has good paintability, good coating adhesion and good corrosion resistance, and is very suitable for automotive parts.

A high-performance thermoformed component provided with a coating, and a manufacturing method therefor. The thermoformed component comprises a substrate and a coating thereon. The substrate comprises the following ingredients in percentage by weight: 0.01-0.8% of C, 0.05-1.0% of Si, 0.1-5% of Mn, 0.001-0.3% of P, 0.001-0.1% of S, 0.001-0.3% of Al, 0.001-0.5% of Ti, 0.0005-0.1% of B, 0.001-0.5% of Nb, 0.001-0.5% of V, and the remainder being Fe and other unavoidable impurities. The appearance of the thermoformed component has no color difference and no mottling. The surface oxygen content of the thermoformed component is 0.1-20 wt. %, and the ratio of the standard deviation to the average value of the surface oxygen content satisfies: 0<standard deviation of oxygen content/average value of oxygen content ≤0.3. In the manufacturing method, a coated steel plate that has undergone heat treatment, transfer processing, and hot stamping is not treated with oil.

An embodiment of the present invention provides steel for hot forming, a hot-formed member, and methods for manufacturing same, the steel comprising, by wt %, 0.06-0.1% of C, 0.05-0.6% of Si, 0.6-2% of Mn, 0.05% or less of P, 0.02% or less of S, 0.01-0.1% of Al, 0.01-0.8% of Cr, 0.01-0.5% of Mo, 0.02% or less of N, and the remainder of Fe and inevitable impurities, wherein an alloy factor represented by relational expression 1 below is 7 or more, and the number of carbides having a circular equivalent diameter of 0.5 μm or greater is 10.sup.5/mm.sup.2 or less.

Alloy factor=I(Mn)×I(Si)×I(Cr)×I(Mo)  [Relational expression 1] where the I values for the components are I(Mn)=3.34×Mn+1, I(Si)=0.7×Si+1, I(Cr)=2.16×Cr+1, and I(Mo)=3×Mo+1, respectively, and the content of each component is expressed as wt %.

A hot-stamping formed body has a predetermined chemical composition and includes microstructure which includes residual austenite of which an area ratio is 10% or more and less than 20%, Among grain boundaries of crystal grains of bainite and tempered martensite a ratio of a length of a grain boundary having a rotation angle in a range of 55° to 75° to a total length of a grain boundary having a rotation angle in a range of 4° to 12°, a grain boundary having a rotation angle in a range of 49° to 54°, and the grain boundary having a rotation angle in, a range of 55° to 75° to the <011> direction as a rotation axis is 30% or more.