An exemplary embodiment in the present disclosure provides a grain-oriented electrical steel sheet containing, by wt %: 3.0 to 4.5% of Si; 0.05 to 0.2% of Mn; 0.015 to 0.035% of Al; 0.0015% or less (excluding 0%) of C; 0.0015% or less (excluding 0%) of N; 0.0015% or less (excluding 0%) of S; and a balance of Fe and other unavoidable impurities, wherein the grain-oriented electrical steel sheet satisfies the following Relational Expressions 1 and 2:

(W.sub.13/50/W.sub.17/50)≤0.57  [Relational Expression 1]

(W.sub.15/50/W.sub.17/50)≤0.76  [Relational Expression 2] where Wx/y represents a core loss value under conditions in which a magnitude of an applied magnetic field is x/10 T and a frequency is y Hz.

An annealing separator for an oriented electrical steel sheet includes: a first component including a Mg oxide or a Mg hydroxide; and a second component including one kind among oxides and hydroxides of a metal selected from Al, Ti, Cu, Cr, Ni, Ca, Zn, Na, K, Mo, In, Sb, Ba, Bi, and Mn, or two or more kinds thereof.

An annealing separator for an oriented electrical steel sheet includes: a first component including a Mg oxide or a Mg hydroxide; and a second component including one kind among oxides and hydroxides of a metal selected from Al, Ti, Cu, Cr, Ni, Ca, Zn, Na, K, Mo, In, Sb, Ba, Bi, and Mn, or two or more kinds thereof.

An annealing separator for an oriented electrical steel sheet including: a first component includes a Mg oxide or a Mg hydroxide; and a second component including one kind among oxides and hydroxides of a metal selected from Al, Ti, Cu, Cr, Ni, Ca, Zn, Na, K, Mo, In, Sb, Ba, Bi, and Mn, or two or more kinds thereof.

An annealing separator for an oriented electrical steel sheet including: a first component includes a Mg oxide or a Mg hydroxide; and a second component including one kind among oxides and hydroxides of a metal selected from Al, Ti, Cu, Cr, Ni, Ca, Zn, Na, K, Mo, In, Sb, Ba, Bi, and Mn, or two or more kinds thereof.

A grain-oriented electrical steel sheet according to an embodiment of the present invention may comprise: by weight %, 2.0-4.0% of Si, 0.04-0.2% of Mn, 0.010% or less (exclusive of 0%) of N, 0.01-0.05% of Sb, 0.005% or less (exclusive of 0%) of C, 0.03-0.08% of Sn, 0.01-0.2% of Cr, and the balance of Fe and inevitable impurities; and precipitates which have an average particle size of 5-50 nm and contain at least one of AIN, (Al, Si)N, (Al, Si, Mn)N, Mns, and CuS.

A double-oriented electrical steel sheet according to an example of the present invention comprises, by weight 2.0 to 4.0 wt % of Si, 0.01 to 0.04 wt % of Al, 0.0004 to 0.02 wt % of S, 0.05 to 0.3 wt % of Mn, at most 0.01 wt % (exclusive of 0 wt %) of N, at most 0.005 wt % (exclusive of 0 wt %) of C, 0.005 to 0.15 wt % of P, 0.001 to 0.005 wt % of Ti, and 0.0001 to 0.005 wt % of Mg, with the balance being Fe and other inevitable impurities, wherein the area fraction of crystal grains having an orientation within 15° from {100}<001> is 60 to 99%, and the area fraction of crystal grains having an orientation within 15° from {100}<025> is 1 to 30%.

A method for producing a component made of a steel product coated with an Al—Si protective coating, includes: providing a substrate consisting of a steel produced coated with an Al—Si protective coating, heating the substrate to a temperature T1 such that the Al—Si protective coating is only partially pre-alloyed with Fe of the steel product, cooling the pre-alloyed substrate to room temperature, applying a corrosion protection oil to the surface of the pre-alloyed substrate, wherein the oil consists of a composition containing fatty acid ester, transporting the pre-alloyed substrate to which the oil has been applied, heating the pre-alloyed substrate to which the oil has been applied to a temperature T2 such that the Al—Si protective coating is fully alloyed with Fe of the steel product and the oil is removed without leaving residue, and shaping the re-heated substrate to form the component.

A method for producing a component made of a steel product coated with an Al—Si protective coating, includes: providing a substrate consisting of a steel produced coated with an Al—Si protective coating, heating the substrate to a temperature T1 such that the Al—Si protective coating is only partially pre-alloyed with Fe of the steel product, cooling the pre-alloyed substrate to room temperature, applying a corrosion protection oil to the surface of the pre-alloyed substrate, wherein the oil consists of a composition containing fatty acid ester, transporting the pre-alloyed substrate to which the oil has been applied, heating the pre-alloyed substrate to which the oil has been applied to a temperature T2 such that the Al—Si protective coating is fully alloyed with Fe of the steel product and the oil is removed without leaving residue, and shaping the re-heated substrate to form the component.

The present invention provides a cast product that can further enhance the stability of an alumina barrier layer and can exhibit further superior oxidation resistance, carburization resistance, nitriding resistance, corrosion resistance, and the like when used under a high-temperature atmosphere. The cast product according to the present invention is a cast product having an alumina barrier layer including an aluminum oxide on a surface of a matrix, and the aluminum oxide is (Al.sub.(1-x)M.sub.(x)).sub.2O.sub.3, where M is at least one of Cr, Ni, Si, and Fe, and x satisfies a relationship 0<x<0.5. Furthermore, the cast product according to the present invention is a cast product having an alumina barrier layer including an aluminum oxide on a surface of a matrix, and at least one of Cr, Ni, Si, and Fe forms a solid solution in the aluminum oxide, and at least one of Cr, Ni, Si, and Fe forming the solid solution with Al is contained so as to satisfy a relationship Al/(Cr+Ni+Si+Fe)≧2.0 in an atomic % ratio.