The invention relates to a high strength steel with a careful selection of the normal alloying elements C, Mn, Si and Al, together with micro-element addition. This a steel with a high strength and high hole expansion ratio can be produced. The invention also relates to the method to manufacture this high strength steel.

Provided is a steel sheet and a method for manufacturing same, the steel sheet, which is optimized a composition and microstructure, and which can be used for automobile parts and the like, having superb bendability, and superior balance of strength and ductility and of strength and hole expansion ratio.

Disclosed are a low-silicon and low-carbon equivalent GPa grade multi-phase steel plate/steel strip and a manufacturing method therefor. The steel plate/steel strip comprises the following components in percentages by weight: 0.03-0.07% of C, 0.1-0.5% of Si, 1.7-2.0% of Mn, P<0.02%, S<0.01%, N<0.01%, 0.01-0.05% of Al, 0.4-0.7% of Cr, 0.001-0.005% of B, and 0.07-0.15% of Ti, and also comprises one or both of 0.15-0.4% of Mo or 0.02-0.08% of Nb, with the balance being Fe and other inevitable impurities; and at the same time, the steel plate/steel strip satisfies: the content of available B*>0.001, the content of available B*=B-[Ti-3.4N-1.2(C—Nb/7.8)]/22, CE<0.58, and CE=C+Mn/6+(Cr+Mo+V)/5+(Si+Ni+Cu)/15. The steel plate has a tensile strength of >980 MPa and a yield strength of >780 MPa, and the hole expansion rate satisfies: if an original hole is a punched hole, the hole expansion rate is >50%; and if the original hole is a reamed hole, the hole expansion rate is >60%. The steel plate is mainly used in the preparation of vehicle chassis and suspension system parts.

Provided is a steel sheet which can be used for automobile parts and the like, and relates to a steel sheet having a superior balance of strength and ductility and strength and hole expansion ratio and superior bending formability, and a method for manufacturing same.

Disclosed are a low-cost ultra-high-strength multiphase steel plate/steel strip and its manufacturing method. Said steel plate/steel strip comprises the following components in percentage by weight: 0.03 to 0.07% of C, 0.1 to 0.5% of Si, 1.3 to 1.9% of Mn, less than or equal to 0.02% of P, less than or equal to 0.01% of S, 0.01 to 0.05% of Al, 0.2 to 0.5% of Cr, 0.07 to 0.14% of Ti, less than 0.03% of (Ni+Nb+Mo+V), and the balance being Fe and other inevitable impurities; and Mn+1.5Cr+5(Ti+Al+Cu)+10(Mo+Ni)+20(Nb+V)<3.0; Mn+2Cr+4Ti+4Nb+4V+4Mo—Si/3+2C≤3.0. The steel plate is mainly used for the manufacturing of automotive chassis and suspension system parts.

The present disclosure relates to a wear resistant steel material that is not cracked even after being cut using gas, etc., and a method of manufacturing the wear resistant steel material.

Provided is a steel sheet which can be used for automobile parts and the like, and relates to a steel sheet having a superior balance of strength and ductility and strength and a hole expansion ratio and superior bending formability, and a method for manufacturing same.

A high-strength hot-rolled steel sheet that has excellent punching workability and hole expandability, and a method for manufacturing the same. The hot-rolled steel sheet has a tensile strength of 980 MPa or more. The hot-rolled steel sheet has a chemical composition containing C, Si, Mn, P, S, Al, N, Ti, Cr, and B, and has a microstructure including a bainite phase having an area ratio of 85% or more as a main phase, and a martensite phase or martensite-austenite constituent having an area ratio of 15% or less as a second phase, the balance being a ferrite phase. The second phase has an average grain diameter of 3.0 μm or less, prior-austenite grains have an average aspect ratio of 1.3 or more and 5.0 or less, and recrystallized prior-austenite grains have an area ratio of 15% or less relative to non-recrystallized prior-austenite grains.

The present invention relates to a hot stamped component, a precoated steel sheet used for hot stamping, and a hot stamping process. The hot stamped component of the present invention is provided with a coating of aluminium or an aluminium alloy on at least one surface of the base steel, the coating is produced by interdiffusion between the base steel and a precoating of aluminium or aluminium alloy, and the coating has a thickness of 6 to 26 μm.

An ultra-high-strength hot-rolled steel plate and steel strip having good fatigue and reaming properties and a manufacturing method therefor. The weight percentages of the components of the steel plate and the steel strip are: C: 0.07-0.14%, Si: 0.1-0.4%, Mn: 1.55-2.00%, P≤0.015%, S≤0.004%, Al: 0.01-0.05%, N≤0.005%, Cr: 0.15-0.50%, V: 0.1-0.35%, Nb: 0.01%-0.06%, Mo: 0.15-0.50%, Ti≤0.02%, and the balance of Fe and unavoidable impurities. Such components need to meet: 1.0≤[(Cr/52)/(C/4)+(Nb/93+Ti/48+V/51+Mo/96)/(C/12)]≤1.6. The tensile strength of the ultrahigh-strength hot-rolled steel plate and steel strip is ≥780 MPa, the yield strength thereof is ≥660 MPa, the tensile fatigue limit (10 million cycles) FL thereof is ≥570 MPa, or the fatigue limit to tensile strength FL/Rm thereof is ≥0.72. The reaming rate meets: if an original hole is a punched hole, the reaming rate thereof is >85%; and if the original hole is a reamed hole, the reaming rate thereof is >120%.