A steel sheet includes a predetermined composition satisfying Expression (1), in which the microstructure at the ¼ thickness position from the surface in the sheet thickness direction includes, by vol %, ferrite: 95% or more and a remainder of the microstructure: 5% or less, has a proportion of unrecrystallized ferrite in the ferrite of 5% or less, and a half width w and an X-ray wavelength λ at a peak of (200) plane of the ferrite satisfy Expression (2).

0.80≤{(Ti/48−N/14)+Nb/93}/(C/12)≤5.00  (1)

w×λ≥0.20  (2)

Provided are a high-strength steel sheet and a method for manufacturing the steel sheet. The high-strength steel sheet has a specified chemical composition with the balance being Fe and inevitable impurities, a microstructure including, in terms of area ratio, 30% or more of a ferrite phase, 40% to 65% of a bainite phase and/or a martensite phase, and 5% or less of cementite, in which, in a surface layer that is a region within 50 μm from the surface in the thickness direction, the area ratio of a ferrite phase is 40% to 55% and the total area ratio of a bainite phase having a grain diameter of more than 5 μm and/or a martensite phase having a grain diameter of more than 5 μm is 20% or less, and a tensile strength is 980 MPa or more.

A high-strength galvanized steel sheet that includes a chemical composition containing, by mass %, C: 0.15% or more and 0.25% or less, Si: 0.50% or more and 2.5% or less, Mn: 2.3% or more and 4.0% or less, P: 0.100% or less, S: 0.02% or less, Al: 0.01% or more and 2.5% or less, and Fe and inevitable impurities. The steel sheet having a microstructure containing, by an area percentage basis, a tempered martensite phase: 30% or more and 73% or less, a ferrite phase: 25% or more and 68% or less, a retained austenite phase: 2% or more and 20% or less, and other phases: 10% or less (including 0%), the other phases containing a martensite phase: 3% or less (including 0%) and a bainitic ferrite phase: less than 5% (including 0%).

Provided are a high-strength steel sheet and a method for manufacturing the steel sheet. The high-strength steel sheet has a specified chemical composition with the balance being Fe and inevitable impurities, a microstructure including, in terms of area ratio, 25% or less of a ferrite phase, 75% or more of a bainite phase and/or a martensite phase, and 5% or less of cementite, in which, in a surface layer that is a region within 50 μm from the surface in the thickness direction, the area ratio of a ferrite phase is 5% to 20%, and a tensile strength is 1180 MPa or more.

The object of the present invention is to provide a metal plate capable of manufacturing a deposition mask in which dispersion of positions of through-holes is restrained. A thermal recovery rate is defined as parts per million of a difference a distance between to measurement points on a sample before a heat treatment and a distance therebetween after the heat treatment, relative to the distance therebetween before the heat treatment. In this case, an average value of the thermal recovery rates of the respective samples is not less than −10 ppm and not more than +10 ppm, and (2) a dispersion of the thermal recovery rates of the respective samples is not more than 20 ppm.

Disclosed herein is a high-strength plated steel sheet having a plated layer on the surface of a base steel sheet and containing predetermined steel components. The steel sheet includes, in the order from the interface of the base steel sheet and the plated layer towards the base steel sheet: a soft layer having a Vickers hardness that is 90% or less of the Vickers hardness at a portion t/4 of the base steel sheet, where t is a sheet thickness of the base steel sheet; and a hard layer consisting of a structure which is mainly composed of martensite and bainite and in which the average grain size of prior austenite is 20 μm or less. The average depth D of the soft layer is 20 μm or greater, and the average depth d of an internal oxide layer is 4 μm or greater and smaller than D.

Disclosed herein is a high-strength plated steel sheet containing an internal oxidized layer, a soft layer including the internal oxidized layer, and a hard layer including a structure having metallic structure containing a low-temperature-transformation produced phase in a proportion of 70% or more by area of the whole of the metallic structure, in which polygonal ferrite is in a proportion of 0% or more by area, and 10% or less by area of the same, and retained austenite is in a proportion of 5% or more by volume of the same. The high-strength plated steel sheet satisfies the average depth D of the soft layer is 20 μm or more, the average depth d of the internal oxidized layer is 4 μm or more and less than D, and a tensile strength of 980 MPa or more.

A method of forming a cutting element comprises disposing diamond particles in a container and disposing a metal powder on a side of the diamond particles. The diamond particles and the metal powder are sintered so as to form a polycrystalline diamond material and a low-carbon steel material comprising less than 0.02 weight percent carbon and comprising an intermetallic precipitate on a side of the polycrystalline diamond material. Related cutting elements and earth-boring tools are also disclosed.

This hot-rolled steel sheet has a predetermined chemical composition, a microstructure includes 80% or more of tempered martensite by a volume percentage and a remainder consisting of one or more of ferrite, pearlite, bainite, fresh martensite, and residual austenite, the tempered martensite includes 5×10.sup.9 pieces/mm.sup.3 or more of precipitates containing Ti and having an equivalent circle diameter of 5 nm or less per unit volume, in a surface layer region that is a range from a surface to a 1/10 position of a sheet thickness, a sum of an average pole density of a crystal orientation group consisting of {211}<111> to {111}<112> and a pole density in a crystal orientation of {110}<001> is 6.0 or less, and a tensile strength is 980 MPa or more.

The present invention provides a steel sheet having excellent wear resistance and composite corrosion resistance, and a method of manufacturing same. According to one example of the present invention, a corrosion-resistant steel sheet having excellent wear resistance and composite corrosion resistance comprises, in wt %: 0.04-0.10% of carbon (C); 0.10% or less (excluding 0%) of silicon (Si); 0.20-0.35% of copper (Cu); 0.1-0.2% of nickel (Ni); 0.05-0.15% of antimony (Sb); 0.07-0.22% of tin (Sn); 0.05-0.15% of titanium (Ti); 0.01% or less (excluding 0%) of sulfur (S); 0.005% or less (excluding 0%) of nitrogen (N); 0.05-0.15% of molybdenum (Mo); and the balance of iron (Fe) and inevitable impurities, and satisfies formula 1 and formula 2 below.

[Ni]/[Cu]≥0.5   [Formula 1]

48×([Ti]/48−[S]/32−[N]/14)≥0.04   [Formula 2]

Here, in formula 1 and formula 2, [Ni], [Cu], [Ti], [S], and [N] represent Ni, Cu, Ti, S, and N content (wt %) in the steel sheet, respectively.