PRODUCTION METHOD FOR A SPOT WELDED JOINT USING HIGH STRENGTH AND HIGH FORMING STEEL
A spot welded joint of at least two steel sheets is provided. At least one of the steel sheets presents yield strength above or equal to 600 MPa, an ultimate tensile strength above or equal to 1000 MPa, uniform elongation above or equal to 15%. The base metal chemical composition includes 0.05≤C≤0.21%, 4.0≤Mn≤7.0%, 0.5≤Al≤3.5%, Si≤2.0%, Ti≤0.2%, V≤0.2%, Nb≤0.2%, P≤0.025%, B≤0.0035%, and the spot welded joint contains a molten zone microstructure containing more than 0.5% of Al and containing a surface fraction of segregated areas lower than 1%, said segregated areas being zones larger than 20 μm.sup.2 and containing more than the steel nominal phosphorus content.
HOT ROLLED HIGH STRENGTH STEEL STRIP HAVING HIGH HOLE EXPANSION RATIO
The invention relates to a high strength steel with a careful selection of the normal alloying elements C, Mn, Si and Al, together with micro-element addition. This a steel with a high strength and high hole expansion ratio can be produced. The invention also relates to the method to manufacture this high strength steel.
HIGH-STRENGTH STEEL SHEET HAVING SUPERIOR WORKABILITY AND MANUFACTURING METHOD THEREFOR
Provided is a steel sheet and a method for manufacturing same, the steel sheet, which is optimized a composition and microstructure, and which can be used for automobile parts and the like, having superb bendability, and superior balance of strength and ductility and of strength and hole expansion ratio.
LOW-SILICON AND LOW-CARBON EQUIVALENT GPA GRADE MULTI-PHASE STEEL PLATE/STEEL STRIP AND MANUFACTURING METHOD THEREFOR
Disclosed are a low-silicon and low-carbon equivalent GPa grade multi-phase steel plate/steel strip and a manufacturing method therefor. The steel plate/steel strip comprises the following components in percentages by weight: 0.03-0.07% of C, 0.1-0.5% of Si, 1.7-2.0% of Mn, P<0.02%, S<0.01%, N<0.01%, 0.01-0.05% of Al, 0.4-0.7% of Cr, 0.001-0.005% of B, and 0.07-0.15% of Ti, and also comprises one or both of 0.15-0.4% of Mo or 0.02-0.08% of Nb, with the balance being Fe and other inevitable impurities; and at the same time, the steel plate/steel strip satisfies: the content of available B*>0.001, the content of available B*=B-[Ti-3.4N-1.2(C—Nb/7.8)]/22, CE<0.58, and CE=C+Mn/6+(Cr+Mo+V)/5+(Si+Ni+Cu)/15. The steel plate has a tensile strength of >980 MPa and a yield strength of >780 MPa, and the hole expansion rate satisfies: if an original hole is a punched hole, the hole expansion rate is >50%; and if the original hole is a reamed hole, the hole expansion rate is >60%. The steel plate is mainly used in the preparation of vehicle chassis and suspension system parts.
ANNEALING SEPARATOR COMPOSITION FOR GRAIN-ORIENTED ELECTRICAL STEEL SHEET, GRAIN-ORIENTED ELECTRICAL STEEL SHEET, AND MANUFACTURING METHOD THEREFOR
An annealing separator composition for a grain-oriented electrical steel sheet according to an exemplary embodiment of the present invention contains a composite metal oxide containing Mg and a metal M, wherein the metal M is one or more of Be, Ca, Ba, Sr, Sn, Mn, Fe, Co, Ni, Cu, and Zn.
HIGH STRENGTH STEEL SHEET HAVING SUPERIOR WORKABILITY AND METHOD FOR MANUFACTURING SAME
Provided is a steel sheet which can be used for automobile parts and the like, and relates to a steel sheet having a superior balance of strength and ductility and strength and hole expansion ratio and superior bending formability, and a method for manufacturing same.
WEAR RESISTANT STEEL MATERIAL WITH EXCELLENT CUT CRACK RESISTANCE AND METHOD OF MANUFACTURING SAME
The present disclosure relates to a wear resistant steel material that is not cracked even after being cut using gas, etc., and a method of manufacturing the wear resistant steel material.
NON-ORIENTED ELECTRICAL STEEL SHEET, AND METHOD FOR MANUFACTURING SAME
A non-oriented electrical steel sheet according to an exemplary embodiment of the present invention includes, in wt%, Si: 1.5 to 4.0%, Al: 0.5 to 1.5%, Mn: 0.05 to 0.55%, C: 0.005% or less, Ti: 0.004% or less (excluding 0%), N: 0.005% or less (excluding 0%), S: 0.005% or less (excluding 0%), and Cu: 0.01% or less (excluding 0%), and the balance of Fe and inevitable impurities, and satisfies Formula 1 and Formula 2 below.
[N]≤0.005×([Al]×[Ti]) [Formula 1]
[S]≤0.01×([Mn]+[Cu]) [Formula 2]
(In Formula 1 and Formula 2, [N], [Al], [Ti], [S], [Mn], and [Cu] represent a content (wt %) of N, Al, Ti, S, Mn, and Cu, respectively).
HIGH STRENGTH STEEL SHEET HAVING SUPERIOR WORKABILITY AND METHOD FOR MANUFACTURING SAME
Provided is a steel sheet which can be used for automobile parts and the like, and relates to a steel sheet having a superior balance of strength and ductility and strength and a hole expansion ratio and superior bending formability, and a method for manufacturing same.
NON-ORIENTED ELECTRICAL STEEL SHEET AND METHOD FOR MANUFACTURING SAME
An embodiment of the present invention provides a non-oriented electrical steel sheet including. in wt%: Si: 2.5 to 4.0 %, Mn: 0.1 to 1.0 %, Al: 0.5 to 1.5 %, P: 0.002 to 0.015 %, and As: 0.002 to 0.01 %, and the balance of Fe and inevitable impurities, and satisfying Formula 1 and Formula 2.
(In Formula 1, [P] and [As] represent a content (wt%) of P and As, respectively.)
([GS] is an average grain size (.Math.m) measured when 10,000 or more grains having a grain size of 5 to 500 .Math.m are observed on a surface of the steel sheet, and STD is a standard deviation (.Math.m) at that time.)