The present invention relates to multi-layered hybrid and functional graded aluminum foam obtained from waste aluminum beverage cans, and to the production method thereof. This multi-layered aluminum composite foam can be used in bullet-proof armors in many fields such as aviation, defense industry, automotive and rail systems, in decreasing the impact effect in fast trains and automobiles, in vibration damping, in absorbing energy during impact and shock, in electromagnetic shields, as air buffer panel in carrying heavy vehicles such as tanks, in providing sound insulation on motorways and for flame retardant purposes.

A highly-productive method for manufacturing a metal foam, capable of easily manufacturing a molded article having a desired shape is provided. A method for manufacturing a metal foam includes dissolving hydrogen in a mixture containing a molten metal and a thickener, and thereby manufacturing a precursor in which an amount of solid-soluted hydrogen in the metal is saturated, charging the precursor into a mold, and solidifying the precursor charged into the mold under a reduced-pressure atmosphere, or solidifying the precursor charged into the mold and then heating the solidified precursor under a reduced-pressure atmosphere.

A highly-productive method for manufacturing a metal foam, capable of easily manufacturing a molded article having a desired shape is provided. A method for manufacturing a metal foam includes dissolving hydrogen in a mixture containing a molten metal and a thickener, and thereby manufacturing a precursor in which an amount of solid-soluted hydrogen in the metal is saturated, charging the precursor into a mold, and solidifying the precursor charged into the mold under a reduced-pressure atmosphere, or solidifying the precursor charged into the mold and then heating the solidified precursor under a reduced-pressure atmosphere.

Morphology, microstructure, compressive behavior, and biocorrosive properties of magnesium or magnesium alloy foams allow for their use in biodegradable biomedical, metal-air battery electrode, hydrogen storage, and lightweight transportation applications. Magnesium or Mg alloy foams are usually very difficult to manufacture due to the strong oxidation layer around the metallic particles; however, in this invention, they can be synthesized via a camphene-based freeze-casting process with the addition of graphite powder using precisely controlled heat-treatment parameters. The average porosity ranges from 45 to 85 percent and the median pore diameter is about a few tens to hundreds of microns, which are suitable for bio and energy applications utilizing their enhanced surface area. This invention based on powder-slurry freeze-casting method using camphene as a volatile solvent is also applicable for other metal foams such as iron, copper, or others to produce three-dimensional metal foams with high strut connectivity.

Morphology, microstructure, compressive behavior, and biocorrosive properties of magnesium or magnesium alloy foams allow for their use in biodegradable biomedical, metal-air battery electrode, hydrogen storage, and lightweight transportation applications. Magnesium or Mg alloy foams are usually very difficult to manufacture due to the strong oxidation layer around the metallic particles; however, in this invention, they can be synthesized via a camphene-based freeze-casting process with the addition of graphite powder using precisely controlled heat-treatment parameters. The average porosity ranges from 45 to 85 percent and the median pore diameter is about a few tens to hundreds of microns, which are suitable for bio and energy applications utilizing their enhanced surface area. This invention based on powder-slurry freeze-casting method using camphene as a volatile solvent is also applicable for other metal foams such as iron, copper, or others to produce three-dimensional metal foams with high strut connectivity.

Morphology, microstructure, compressive behavior, and biocorrosive properties of magnesium or magnesium alloy foams allow for their use in biodegradable biomedical, metal-air battery electrode, hydrogen storage, and lightweight transportation applications. Magnesium or Mg alloy foams are usually very difficult to manufacture due to the strong oxidation layer around the metallic particles; however, in this invention, they can be synthesized via a camphene-based freeze-casting process with the addition of graphite powder using precisely controlled heat-treatment parameters. The average porosity ranges from 45 to 85 percent and the median pore diameter is about a few tens to hundreds of microns, which are suitable for bio and energy applications utilizing their enhanced surface area. This invention based on powder-slurry freeze-casting method using camphene as a volatile solvent is also applicable for other metal foams such as iron, copper, or others to produce three-dimensional metal foams with high strut connectivity.