Provided is a steel sheet and a method for manufacturing same, the steel sheet, which is optimized a composition and microstructure, and which can be used for automobile parts and the like, having superb bendability, and superior balance of strength and ductility and of strength and hole expansion ratio.

Disclosed are an R-T-B-based permanent magnet material, a preparation method therefor and the use thereof. The R-T-B-based permanent magnet material comprises R, B, M, Fe, Co, X and inevitable impurities, wherein: (1) R is a rare earth element, and the R includes at least Nd and RH, M being one or more of Ti, Zr and Nb, and X including Cu, “Al and/or Ga”; and (2) in percentage by weight, R: 30.5-32.0 wt%, B: 0.95-0.99 wt%, M: 0.3-0.6 wt%, X: 0.8-1.8 wt%, and Cu: 0.35-0.50 wt%, and the balance is Fe, Co and inevitable impurities. According to the present invention, under the condition of 0.3-0.6 wt% of a high melting point metal, a permanent magnet material with an excellent magnet performance and a good squareness is obtained.

Provided is a steel sheet which can be used for automobile parts and the like, and relates to a steel sheet having a superior balance of strength and ductility and strength and hole expansion ratio and superior bending formability, and a method for manufacturing same.

Provided is a steel sheet which can be used for automobile parts and the like, and relates to a steel sheet having a superior balance of strength and ductility and strength and a hole expansion ratio and superior bending formability, and a method for manufacturing same.

An austenitic stainless steel material that has a passivation film on a surface is provided. The austenitic stainless steel material has a chemical composition consisting of, in mass%, C: 0.10% or less, Si: 1.0% or less, Mn: 8.0-10.0%, P: 0.030% or less, S: 0.003% or less, Cr: 15.0-18.0%, Ni: 7.0-9.0%, N: 0.15-0.25%, Al: 0.005-0.20%, Ca: 0.0005-0.01%, Cu: less than 1.0%, Mo: less than 1.0%, B: 0-0.0050%, Nb: 0-0.50%, Ti: 0-0.50%, V: 0-0.50%, W: 0-0.50%, Zr: 0-0.50%, Co: 0-0.50%, Mg: 0-0.005%, Ga: 0-0.005%, Hf: 0-0.10%, REM: 0-0.10%, and the balance: Fe and impurities. An f value, namely, [Ni + 0.72Cr + 0.88Mo + 1.11Mn - 0.27Si + 0.53Cu + 12.93C + 7.55N], is more than 29.5 and less than 32.5.

A steel sheet includes a predetermined composition satisfying Expression (1), in which the microstructure at the ¼ thickness position from the surface in the sheet thickness direction includes, by vol %, ferrite: 95% or more and a remainder of the microstructure: 5% or less, has a proportion of unrecrystallized ferrite in the ferrite of 5% or less, and a half width w and an X-ray wavelength λ at a peak of (200) plane of the ferrite satisfy Expression (2).

0.80≤{(Ti/48−N/14)+Nb/93}/(C/12)≤5.00  (1)

w×λ≥0.20  (2)

This hot-rolled steel sheet has a predetermined chemical composition, in which a metallographic structure contains, by area %, more than 92.0% and 100.0% or less of martensite and tempered martensite in total, less than 3.0% of residual austenite, and less than 5.0% of ferrite, has a ratio S.sub.60/S.sub.7, which is a ratio of a density S.sub.60 of a length of a grain boundary having a crystal misorientation of 60° to a density S.sub.7 of a length of a grain boundary having a crystal misorientation of 7° about a <110> direction, of more than 0.34 and less than 0.60, has a standard deviation of a Mn concentration of 0.60 mass % or less, and has a tensile strength of 980 MPa or more.

What is provided is a steel sheet for a non-oriented electrical steel sheet containing, in mass %, C: 0.0040% or less, Si: 1.9% or more and 3.5% or less, Al: 0.10% or more and 3.0% or less, Mn: 0.10% or more and 2.0% or less, P: 0.09% or less, S: 0.005% or less, N: 0.0040% or less, B: 0.0060% or less, and the remainder consisting of Fe and impurities, in which the recrystallization rate of the structure of a sheet thickness-direction cross section at each position 10 mm apart toward the sheet width center from each of both end portions in the sheet width direction is less than 50%, and, when the sheet width is represented by W, the recrystallization rate of the structure of a sheet thickness-direction cross section at the position of ¼W from each of both end portions in the sheet width direction is 50% or more.

Provided herein is a stainless steel seamless pipe having a composition that contains, in mass %, C: 0.06% or less, Si: 1.0% or less, Mn: 0.01% or more and 1.0% or less, P: 0.05% or less, S: 0.005% or less, Cr: 15.2% or more and 18.5% or less, Mo: 1.5% or more and 4.3% or less, Cu: 1.1% or more and 3.5% or less, Ni: 3.0% or more and 6.5% or less, Al: 0.10% or less, N: 0.10% or less, O: 0.010% or less, and Sb: 0.001% or more and 1.000% or less, and in which C, Si, Mn, Cr, Ni, Mo, Cu, and N satisfy the predetermined formula, and the balance is Fe and incidental impurities, the stainless steel seamless pipe having a microstructure containing 30% or more martensitic phase, 65% or less ferrite phase, and 40% or less retained austenite phase by volume.

Disclosed herein is an electroslag welding wire containing, by mass % based on total mass of the wire: C: more than 0% and 0.07% or less; Si: more than 0% and 0.50% or less; Mn: more than 0% and 1.0% or less; Ni: 6.0 to 15.0%; and Fe: 79% or more. The electroslag welding wire satisfies the following relationship (1): 0.150≤C+Si/30+Mn/20+Ni/60≤0.300 (1).