A high chromium and silicon-rich corrosion resistant steel is disclosed, which comprises, in weight percent: 22-30% Cr, 2-10% Si, and the balance Fe and incidental impurities, of which a content amount of Cr and Si is less than 37%. Experimental data reveal that, samples of the high chromium and silicon-rich corrosion resistant steel all have a pitting potential greater than 0.8 V and a hardness in a range between HV170 and HV500 in the as-homogenized condition. As a result, experimental data have proved that the high chromium and silicon-rich corrosion resistant steel of the present invention can replace conventional stainless steels having poor pitting resistance like type 304 and type 316 L, and then be adopted for the applications of components and/or structural parts requiring high corrosion resistance.

A high chromium and silicon-rich corrosion resistant steel is disclosed, which comprises, in weight percent: 22-30% Cr, 2-10% Si, and the balance Fe and incidental impurities, of which a content amount of Cr and Si is less than 37%. Experimental data reveal that, samples of the high chromium and silicon-rich corrosion resistant steel all have a pitting potential greater than 0.8 V and a hardness in a range between HV170 and HV500 in the as-homogenized condition. As a result, experimental data have proved that the high chromium and silicon-rich corrosion resistant steel of the present invention can replace conventional stainless steels having poor pitting resistance like type 304 and type 316 L, and then be adopted for the applications of components and/or structural parts requiring high corrosion resistance.

A method of manufacturing a cutting member include cutting a first metal material to form a first portion of the cutting member; cutting second metal material to form a second portion of the cutting member, wherein a first edge of the second portion has at least two line segments, a curve formed by the at least two line segments being mathematically continuously differentiable; welding the first portion and the second portion together; raising the cutting member blank to a first temperature at a first rate and holding raising the cutting member blank from the first temperature to a second temperature at a second rate lower than the first rate and holding, and raising the cutting member blank from the second temperature to a third temperature at a third rate not higher than the second rate and holding.

A hot-stamping formed body has a predetermined chemical composition and includes microstructure which includes residual austenite of which an area ratio is in a range of 20% to 30%. Among grain boundaries of crystal grains of bainite and tempered martensite in the microstructure, a ratio of a length of a grain boundary having a rotation angle in a range of 55° to 75° to a total length of a grain boundary having a rotation angle in a range of 4° to 12°, a grain boundary having a rotation angle in a range of 49° to 54°, and a grain boundary having a rotation angle in a range of 55° to 75° to the <011> direction as a rotation axis is 30% or more.

A hot-stamping formed body has a predetermined chemical composition and includes microstructure which includes residual austenite of which an area ratio is in a range of 20% to 30%. Among grain boundaries of crystal grains of bainite and tempered martensite in the microstructure, a ratio of a length of a grain boundary having a rotation angle in a range of 55° to 75° to a total length of a grain boundary having a rotation angle in a range of 4° to 12°, a grain boundary having a rotation angle in a range of 49° to 54°, and a grain boundary having a rotation angle in a range of 55° to 75° to the <011> direction as a rotation axis is 30% or more.

This steel sheet has a specific chemical composition, the tensile strength is 1300 MPa or more, the ratio (R/t) of the limit bend radius to the sheet thickness is less than 3.5, when a depth position of 30 μm from the surface in the sheet thickness direction is defined as a position A and a depth position of ¼ of the sheet thickness from the surface in the sheet thickness direction is defined as a position B, the number density of AIN at the position A is 3000 pieces/mm.sup.2 or more and 6000 pieces/mm.sup.2 or less, a metallographic structure at the position B includes 90% or more of martensite by volume percentage, and the hardness at the position A is 1.20 times or higher than the hardness at the position B.

Provided is a steel sheet and a method for manufacturing same, the steel sheet which can be used for automobile parts and the like, having excellent bending workability, and excellent balance of strength and ductility and of strength and hole expansibility.

Provided is a steel sheet and a method for manufacturing same, the steel sheet which can be used for automobile parts and the like, having excellent bending workability, and excellent balance of strength and ductility and of strength and hole expansibility.

A method of making a forged, martensitic, stainless steel alloy is provided. The alloy is a forged preform of martensitic, pitting corrosion resistant stainless steel alloy comprising, by weight: 12.0 to 16.0 percent chromium; greater than 16.0 to 20.0 percent cobalt, 6.0 to 8.0 percent molybdenum, 1.0 to 3.0 percent nickel, 0.02 to 0.04 percent carbon; and the balance iron and incidental impurities. The alloy has a microstructure that comprises a retained austenite phase less than or equal to 2 percent by volume of the microstructure. The method heats the preform to a solutionizing temperature to form a solutionized microstructure. The preform is cooled with a liquid to room temperature. The preform is immersed in a cryo-liquid to transform the retained austenite phase in the microstructure to martensite. The preform is heated to a temperature of less than 600° F. for a time sufficient to form a tempered forged preform.

Provided is a steel component with excellent surface fatigue strength. The steel component has a nitride compound layer with a thickness of 5.0 μm to 30.0 μm and a hardened layer in an order from a component surface to a component inside, where a thickness of a porous layer on an outermost surface of the nitride compound layer is 3.0 μm or less and 40.0% or less of a thickness of the nitride compound layer, and the hardened layer has a hardness of HV600 or more at a position of 50 μm inward from the component surface, a hardness of HV400 or more at a position from the component surface to the component inside of 400 μm, and a hardness of HV250 or more at a position from the component surface to the component inside of 600 μm.