Provided is a steel sheet and a method for manufacturing same, the steel sheet, which is optimized a composition and microstructure, and which can be used for automobile parts and the like, having superb bendability, and superior balance of strength and ductility and of strength and hole expansion ratio.

Provided is a steel sheet which can be used for automobile parts and the like, and relates to a steel sheet having a superior balance of strength and ductility and strength and hole expansion ratio and superior bending formability, and a method for manufacturing same.

A non-oriented electrical steel sheet according to an exemplary embodiment of the present invention includes, in wt%, Si: 1.5 to 4.0%, Al: 0.5 to 1.5%, Mn: 0.05 to 0.55%, C: 0.005% or less, Ti: 0.004% or less (excluding 0%), N: 0.005% or less (excluding 0%), S: 0.005% or less (excluding 0%), and Cu: 0.01% or less (excluding 0%), and the balance of Fe and inevitable impurities, and satisfies Formula 1 and Formula 2 below.

[N]≤0.005×([Al]×[Ti])  [Formula 1]

[S]≤0.01×([Mn]+[Cu])  [Formula 2]

(In Formula 1 and Formula 2, [N], [Al], [Ti], [S], [Mn], and [Cu] represent a content (wt %) of N, Al, Ti, S, Mn, and Cu, respectively).

Provided is a steel sheet which can be used for automobile parts and the like, and relates to a steel sheet having a superior balance of strength and ductility and strength and a hole expansion ratio and superior bending formability, and a method for manufacturing same.

A high chromium and silicon-rich corrosion resistant steel is disclosed, which comprises, in weight percent: 22-30% Cr, 2-10% Si, and the balance Fe and incidental impurities, of which a content amount of Cr and Si is less than 37%. Experimental data reveal that, samples of the high chromium and silicon-rich corrosion resistant steel all have a pitting potential greater than 0.8 V and a hardness in a range between HV170 and HV500 in the as-homogenized condition. As a result, experimental data have proved that the high chromium and silicon-rich corrosion resistant steel of the present invention can replace conventional stainless steels having poor pitting resistance like type 304 and type 316 L, and then be adopted for the applications of components and/or structural parts requiring high corrosion resistance.

A high chromium and silicon-rich corrosion resistant steel is disclosed, which comprises, in weight percent: 22-30% Cr, 2-10% Si, and the balance Fe and incidental impurities, of which a content amount of Cr and Si is less than 37%. Experimental data reveal that, samples of the high chromium and silicon-rich corrosion resistant steel all have a pitting potential greater than 0.8 V and a hardness in a range between HV170 and HV500 in the as-homogenized condition. As a result, experimental data have proved that the high chromium and silicon-rich corrosion resistant steel of the present invention can replace conventional stainless steels having poor pitting resistance like type 304 and type 316 L, and then be adopted for the applications of components and/or structural parts requiring high corrosion resistance.

A high-strength hot-rolled steel sheet that has excellent punching workability and hole expandability, and a method for manufacturing the same. The hot-rolled steel sheet has a tensile strength of 980 MPa or more. The hot-rolled steel sheet has a chemical composition containing C, Si, Mn, P, S, Al, N, Ti, Cr, and B, and has a microstructure including a bainite phase having an area ratio of 85% or more as a main phase, and a martensite phase or martensite-austenite constituent having an area ratio of 15% or less as a second phase, the balance being a ferrite phase. The second phase has an average grain diameter of 3.0 μm or less, prior-austenite grains have an average aspect ratio of 1.3 or more and 5.0 or less, and recrystallized prior-austenite grains have an area ratio of 15% or less relative to non-recrystallized prior-austenite grains.

A high-strength hot-rolled steel sheet that has excellent punching workability and hole expandability, and a method for manufacturing the same. The hot-rolled steel sheet has a tensile strength of 980 MPa or more. The hot-rolled steel sheet has a chemical composition containing C, Si, Mn, P, S, Al, N, Ti, Cr, and B, and has a microstructure including a bainite phase having an area ratio of 85% or more as a main phase, and a martensite phase or martensite-austenite constituent having an area ratio of 15% or less as a second phase, the balance being a ferrite phase. The second phase has an average grain diameter of 3.0 μm or less, prior-austenite grains have an average aspect ratio of 1.3 or more and 5.0 or less, and recrystallized prior-austenite grains have an area ratio of 15% or less relative to non-recrystallized prior-austenite grains.

This heat-resistant sintered material has, as an overall composition, a composition including, in terms of % by mass, Cr: 15% to 30%, Ni: 8% to 30%, Si: 2.0% to 6.0%, and C: 0.5% to 2.5% with a remainder being Fe and inevitable impurities, wherein the heat-resistant sintered material has a structure in which hard phases are dispersed in a matrix, the matrix includes Fe, Cr, Ni, and Si, the hard phase includes Fe, Cr, and C, and a porosity is 2.0% or less.

A grain-oriented electrical steel sheet having excellent iron loss property is produced from a steel slab containing, by mass %, C: 0.002-0.15%, Si: 2.5-6.0%, Mn: 0.01-0.80%, Al: 0.010-0.050% and N: 0.003-0.020%, when: a heating rate between 500-700° C. in decarburization annealing is not less than 80° C./s, a surface roughness Ra of a work roll in final cold rolling is 0.01-3.0 μm, a total content of alkaline earth metals to MgO in annealing separator is 0-5 mass %, an average length L in rolling direction of passed crystal grains is not more than 25 mm, a ratio of crystal grains having a length in rolling direction of not more than 5 mm is 40-90%, and an existence ratio of alkaline earth metal sulfides having a size corresponding to circle of not less than 0.5 μm in a cross section of forsterite film is not more than 0.2/μm per unit length in sheet width direction.