Substrates that are bonding targets are bonded in ambient atmosphere via bonding films, including oxides, formed on bonding faces of the substrates. The bonding films, which are metal or semiconductor thin films formed by vacuum film deposition and at least the surfaces of which are oxidized, are formed into the respective smooth faces of two substrates having the smooth faces that serve as the bonding faces. The bonding films are exposed to a space that contains moisture, and the two substrates are overlapped in the ambient atmosphere such that the surfaces of the bonding films are made to be hydrophilic and the surfaces of the bonding films contact one another. Through this, a chemical bond is generated at the bonded interface, and thereby the two substrates are bonded together in the ambient atmosphere. The bonding strength γ can be improved by heating the bonded substrates at a temperature.

A method for fabricating an external element or a timepiece dial from non-conductive material, by performing or repeating a basic cycle of making a base from a non-conductive, or ceramic, or glass. or sapphire substrate; dry coating the base with a first sacrificial protective metal layer; etching a decoration with an ultrashort pulse laser to a depth at least equal to the local thickness of the first layer; dry coating the decoration and the remaining part of the first layer with a second metal and/or coloured decorative treatment layer; chemically removing each first layer; and before or after chemical removal of each first layer, mechanically levelling on the upper level of the base the compound thus formed.

Thermoregulated multilayer material characterized in that it comprises at least one substrate and one thermoregulated layer, said thermoregulated multilayer material having: for λ radiation of between 0.25 and 2 μm, an absorption coefficient αm≥0.8; and, for incident λ radiation of between 7.5 and 10 μm, a reflection coefficient ρm: ρm≥0.85, when the temperature T of said multilayer material 1 is ≤100° C.; ρm between 0.3 and 0.85, when the temperature T of said multilayer material is between 0 and 400° C.

A film forming method includes: providing the substrate into the processing container; forming a metal-based film on the substrate within the processing container; and subsequently, supplying a Si-containing gas into the processing container in a state in which the substrate is provided within the processing container.

A black plated steel sheet includes a steel sheet and an Al—Mg—Si-based plating layer disposed on one surface or both surfaces of the steel sheet; in which the plating layer includes a black layer on the outermost surface thereof, and the black layer has a weight ratio of O to (Al+Mg+Si+O) of 0.01 to 0.6.

The invention relates to the manufacturing method of high performance electro-chromic devices containing transition metal oxide based compounds, wherein it comprises the steps of enlarging of the metal contact with Pt (Platinum) (1) sputtering method on one edge of the 80-150 nm thick Indium-Tin oxide alloy (ITO) (2), which was previously enlarged on the glass (3) by the sputter method, growing vertical nano-wall structures at 15-25 mTorr, 300-500° C. substrate temperature and at 3-45 minutes intervals on glass (3) with sputter method, by using transition metal chalcogen targets on previously enlarged ITO (2) with a thickness of 80-150 nm, oxidizing the grown structures in the oxidizing furnace for 10-60 minutes under oxygen gas in the temperature range 300-450° C., preparing the electro-chromic device by placing a counter glass/ITO (80-150 nm) in propylene carbonate (PC) to face 1 Mole/Liter Lithium perchlorate (LiClO4) ion-conducting electrolyte (6) with a 0.5-1 mm distance between them and closing it.

A fabrication method of a surface acoustic wave (SAW) filter includes obtaining a piezoelectric substrate, forming a back electrode on a first portion of the piezoelectric substrate, forming a first dielectric layer on the first portion of the piezoelectric substrate, forming a trench in the first dielectric layer, forming a second dielectric layer on the first dielectric layer formed with the trench, forming a third dielectric layer on the second dielectric layer, removing a second portion of the piezoelectric substrate to obtain a piezoelectric layer, forming an interdigital transducer (IDT) on the piezoelectric layer, and etching and releasing a portion of the first dielectric layer surrounded by the trench to form a cavity below the back electrode.

A method of manufacturing high capacitance anode and cathode films of capacitors is revealed. Perform sputter deposition on a cathode aluminum foil in a vacuum chamber to form a cathode metal layer which is a titanium layer on a surface of the cathode aluminum foil. Then titanium continuously reacts with nitrogen to form cathode columnar crystal deposition on a surface of the cathode metal layer and get a cathode film. Perform sputter deposition on an anode aluminum foil in a vacuum chamber to form an anode metal layer which is a titanium layer on a surface of the anode aluminum foil. Then titanium continuously reacts with oxygen and nitrogen to form anode columnar crystal deposition on a surface of the anode metal layer and get an anode film. Next use the cathode and anode films with high capacitance to form cathode and anode electrodes of the capacitor.

A method of manufacturing high capacitance anode and cathode films of capacitors is revealed. Perform sputter deposition on a cathode aluminum foil in a vacuum chamber to form a cathode metal layer which is a titanium layer on a surface of the cathode aluminum foil. Then titanium continuously reacts with nitrogen to form cathode columnar crystal deposition on a surface of the cathode metal layer and get a cathode film. Perform sputter deposition on an anode aluminum foil in a vacuum chamber to form an anode metal layer which is a titanium layer on a surface of the anode aluminum foil. Then titanium continuously reacts with oxygen and nitrogen to form anode columnar crystal deposition on a surface of the anode metal layer and get an anode film. Next use the cathode and anode films with high capacitance to form cathode and anode electrodes of the capacitor.

Conventional electrochromic devices frequently suffer from poor reliability and poor performance. Improvements are made using entirely solid and inorganic materials. Electrochromic devices are fabricated by forming an ion conducting electronically-insulating interfacial region that serves as an IC layer. In some methods, the interfacial region is formed after formation of an electrochromic and a counter electrode layer. The interfacial region contains an ion conducting electronically-insulating material along with components of the electrochromic and/or the counter electrode layer. Materials and microstructure of the electrochromic devices provide improvements in performance and reliability over conventional devices. In various embodiments, a counter electrode is fabricated to include a base anodically coloring material and one or more additives.