Counter-flow washing. The present invention relates to a process for washing filaments.

Counter-flow washing. The present invention relates to a process for washing filaments.

An apparatus for manufacturing open carbon fiber superfine yarn comprises a yarn feeding part for feeding a carbon fiber bundle; a tank for storing water for opening carbon fiber to immerse the carbon fiber bundle in the water for opening carbon fiber; a first drying part for drying the open carbon fiber bundle formed by the immersion in the water for opening carbon fiber; an application part for applying a catalyst to the dried open carbon fiber bundle; a second drying part for drying the catalyst-applied open carbon fiber bundle to obtain open carbon fiber resin tape; a slitting part for slitting the open carbon fiber resin tape longitudinally; and a twisting part for twisting a plurality of the open carbon fiber resin tapes slit by the slitting part to form open carbon fiber superfine yarn.

The invention relates to a water-repellent and lipophilic composite needle-punched nonwoven fabric and a preparation method thereof. The method comprises the following steps: blending a PET fiber and a polyolefin-based fiber in a mass ratio of 3:1-1:3, and performing needle punching to obtain a composite needle-punched nonwoven fabric; carrying out hot-drying treatment on the composite needle-punched nonwoven fabric at 110-160° C. for 40-90 min; and carrying out water-repellent finishing on the hot-dried fabric using 50-70 mL/L of an aqueous solution of a modified resin-based fluorine-free waterproofing agent, and drying to obtain the water-repellent and lipophilic composite needle-punched nonwoven fabric, wherein the water-repellent finishing is dip rolling, the air pressure is 1.8 kPa and the liquid carrying rate is 160-230%. The preparation method of the invention is simple, and the prepared composite needle-punched nonwoven fabric has significantly improved water repellency, lipophilicity and tensile strength compared with the fabric before treatment.

The invention relates to a water-repellent and lipophilic composite needle-punched nonwoven fabric and a preparation method thereof. The method comprises the following steps: blending a PET fiber and a polyolefin-based fiber in a mass ratio of 3:1-1:3, and performing needle punching to obtain a composite needle-punched nonwoven fabric; carrying out hot-drying treatment on the composite needle-punched nonwoven fabric at 110-160° C. for 40-90 min; and carrying out water-repellent finishing on the hot-dried fabric using 50-70 mL/L of an aqueous solution of a modified resin-based fluorine-free waterproofing agent, and drying to obtain the water-repellent and lipophilic composite needle-punched nonwoven fabric, wherein the water-repellent finishing is dip rolling, the air pressure is 1.8 kPa and the liquid carrying rate is 160-230%. The preparation method of the invention is simple, and the prepared composite needle-punched nonwoven fabric has significantly improved water repellency, lipophilicity and tensile strength compared with the fabric before treatment.

The present invention relates to a method of manufacturing a high tenacity yarn and a high tenacity yarn manufactured thereby. More particularly, the present invention relates to: a method of manufacturing a high tenacity yarn, the method including coating a yarn made of at least one of nylon and polyester to obtain a coated yarn, wherein the coating material contains 3 to 35 parts by weight of a reinforcing agent composed of a mineral material per 100 parts by weight of a coating liquid containing polyurethane; and a high tenacity yarn manufactured thereby. Therefore, it is possible to manufacture a yarn having high tenacity and improved processability by processing a nylon or polyester yarn having a relatively low tenacity as compared with a high modulus polyethylene (HMPE) yarn by use of a yarn coating technique, and further to reduce production cost.

There is provided an impregnated natural fiber including a cuticle and an interior lumen, the cuticle circumscribing the interior lumen; and insoluble particulates possessing a preselected property embedded in the fiber. The particulates comprise at least 0.1-30 wt. % of the impregnated fiber and the particulates are embedded on the cuticle and within the lumen of the fiber. The fiber has an increased strength, micronaire value and rate of water absorption. Also provided is a system for surface treating cellulose sliver fibers. The system includes a vessel containing a moist paste which comprises at least one particulate material possessing one or more preselected desired properties, a thickening agent and water. The paste from the vessel is dispensed directly onto sliver fiber ribbon(s). A bore sonotrode generates ultrasonic waves which embed the particulate material(s) in the sliver fibers.

A preparation process of spunlace intertwining type recycled cow leather comprises a material preparation process, a cow leather fiber web forming process, as well as a mixed fiber web forming process, an overlapped web forming process, a base fabric manufacturing process and a cow leather finished product manufacturing process which are sequentially arranged according to a preparation process flow; the base fabric manufacturing process comprises a buffing process, a single-side immersion treatment process and an ironing process which are sequentially arranged for manufacturing the overlapped web into the base fabric; and the single-side immersion treatment process comprises the steps of subjecting a single side of the base fabric to single-side coating treatment of the water-based PU material or the oil-based PU material by adopting an inverted feeding device and using a water-based PU material or an oil-based PU material as a coating so as to form a single-side permeable immersion layer of the base fabric.

The invention relates to a water-repellent and lipophilic composite needle-punched nonwoven fabric and a preparation method thereof. The method comprises the following steps: blending a PET fiber and a polyolefin-based fiber in a mass ratio of 3:1-1:3, and performing needle punching to obtain a composite needle-punched nonwoven fabric; carrying out hot-drying treatment on the composite needle-punched nonwoven fabric at 110-160° C. for 40-90 min; and carrying out water-repellent finishing on the hot-dried fabric using 50-70 mL/L of an aqueous solution of a modified resin-based fluorine-free waterproofing agent, and drying to obtain the water-repellent and lipophilic composite needle-punched nonwoven fabric, wherein the water-repellent finishing is dip rolling, the air pressure is 1.8 kPa and the liquid carrying rate is 160-230%. The preparation method of the invention is simple, and the prepared composite needle-punched nonwoven fabric has significantly improved water repellency, lipophilicity and tensile strength compared with the fabric before treatment.

An article includes a substrate with a surface, and a coating disposed over the surface. The coating includes a binder material and a plurality of UV scattering porous polymer particles having pores with a light scattering effective pore size of no more than 100 nm. The coating has a scattering opacity of no more than 20% in the wavelength band from 500 to 3000 nm.