Disclosed herein is a high-strength plated steel sheet having a plated layer on the surface of a base steel sheet and containing predetermined steel components. The steel sheet includes, in the order from the interface of the base steel sheet and the plated layer towards the base steel sheet: a soft layer having a Vickers hardness that is 90% or less of the Vickers hardness at a portion t/4 of the base steel sheet, where t is a sheet thickness of the base steel sheet; and a hard layer consisting of a structure which is mainly composed of martensite and bainite and in which the average grain size of prior austenite is 20 μm or less. The average depth D of the soft layer is 20 μm or greater, and the average depth d of an internal oxide layer is 4 μm or greater and smaller than D.

The high-strength plated steel sheet of the present invention has a plated layer on the surface of a base steel sheet and contains predetermined steel components. The steel sheet includes, in the order from the interface of the base steel sheet and the plated layer towards the base steel sheet: a soft layer having a Vickers hardness that is 90% or less of the Vickers hardness at a portion t/4 of the base steel sheet, where t is a sheet thickness of the base steel sheet: and a hard layer containing martensite, bainite, and ferrite in predetermined ranges. The average depth D of the soft layer is 20 μm or greater, and the average depth d of an internal oxide layer is 4 μm or greater and smaller than D.

A flat steel product for hot forming may be produced from a steel substrate that includes a steel comprising 0.1-3% by weight Mn and up to 0.01% by weight B, along with a protective coating that is applied to the steel substrate. The protective coating may be based on Al and may contain up to 20% by weight of other alloy elements. Also disclosed are methods for producing such flat steel products, steel components, and methods for producing steel components. Absorption of hydrogen is minimized during heating necessary for hot forming. This is achieved at least in part through an alloy constituent of 0.1-0.5% by weight of at least one alkaline earth or transition metal in the protective coating, wherein an oxide of the alkaline earth or transition metal is formed on an outer surface of the protective coating during hot forming of the flat steel product.

The present disclosure relates to coated non-metallic substrates and coated metallic substrates, and methods for producing such coated substrates. A variant of the method is characterized in that a mat or glossy coating is underneath a metallic layer obtained in some cases by way of vapor deposition and/or sputtering. In another variant, the metallic is sufficiently thin so that it remains transparent or translucent to visible light. The coated substrates may include multiple layers such as metallic layers, polysiloxane layers, a color layer, a conversion layer, a primer layer, and/or a transparent or colored layer. An application system for applying a metallic layer to at least one surface of a substrate may include a plasma generator and/or a corona system for treating one or more layers by plasma treatment and/or corona treatment.

A composite panel having a plurality of carbon plies, a perforated metallic foil comprising several apertures and being directly secured to the plurality of carbon plies, and a protective layer made from resin reinforced with fibers which is secured to the metallic foil. The perforated metallic foil is embedded in the protective layer through its apertures. A free surface of the protective layer forms a top side of the composite panel. The thickness of the protective layer between the top side of the composite panel and the perforated metallic foil is at least 15 micrometers and the perforated metallic foil has a thickness of not more than 30 micrometers. The plurality of apertures in the aggregate defines an open area of not more than 40% of the surface area and a maximum distance between two opposed points in a perimeter of an aperture is equal to or less than 3 mm.

The present invention relates to a protective layer against CMAS, to a CMAS-resistant article comprising the protective layer according to the invention, and to a process for preparing a corresponding article.

One embodiment of the disclosure provides a method of fabricating a chamber component with a coating layer disposed on an interface layer with desired film properties. In one embodiment, a method of fabricating a coating material includes providing a base structure comprising an aluminum or silicon containing material, forming an interface layer on the base structure, wherein the interface layer comprises one or more elements from at least one of Ta, Al, Si, Mg, Y, or combinations thereof, and forming a coating layer on the interface layer, wherein the coating layer has a molecular structure of Si.sub.vY.sub.wMg.sub.xAl.sub.yO.sub.z. In another embodiment, a chamber component includes an interface layer disposed on a base structure, wherein the interface layer is selected from at least one of Ta, Al, Si, Mg, Y, or combinations thereof, and a coating layer disposed on the interface layer, wherein the coating layer has a molecular structure of Si.sub.vY.sub.wMg.sub.xAl.sub.yO.sub.z.

A plated steel sheet for hot stamping including a base metal and a galvanized layer that is formed on a surface of the base metal, wherein the galvanized layer includes a galvannealed layer, a solidified zinc layer, and an oxide layer containing Al, in this order from the base metal, and a proportion of a content of Zn (g/m.sup.2) in the solidified zinc layer to a content of Zn (g/m.sup.2) in the galvanized layer is 10 to 95%.

A zinc-plated steel sheet for hot stamping according to an aspect of the present invention includes a steel substrate and a plated layer provided on a surface of the steel substrate, in which the steel substrate contains, in % by mass, C: 0.10 to 0.5%, Si: 0.7 to 2.5%, Mn: 1.0 to 3%, and Al: 0.01 to 0.5%, with the balance being iron and inevitable impurities, and the steel substrate has, in the inside thereof, an internal oxide layer consists of an oxide containing at least one of Si and Mn having a thickness of 1 μm or more, and a decarburized layer having a thickness of 20 μm or less from an interface with the plated layer toward an internal direction of the steel substrate.

The present invention relates to a hot-rolled steel sheet for a high strength galvanized steel sheet, having excellent surface quality, and a method for producing the same, the hot-rolled steel sheet comprising, by weight %: C: 0.05 to 0.15%, Si: 0.03 to 0.10%, Mn: 0.7 to 1.39%, P: 0.001 to 0.05%, S: 0.001 to 0.03%, Al: 0.002 to 0.035%, and the remainder being Fe and unavoidable impurities. The weight ratio of Mn/Si is 15 to 25, the weight ratio of C/Si is 1 to 5, and the weight ratio of Si/P is 3 to 10. The hot-rolled steel sheet has a microstructure consisting of, in area fraction, 10 to 40% of bainite, 20 to 30% of pearlite and 40 to 60% of ferrite, and includes a ternary eutectic compound of FeO, Fe.sub.2SiO.sub.4 and Fe.sub.3(PO).sub.4 formed within 50 μm from the surface.