The present disclosure provides a composite coating and a method for fabricating the composite coating. The composite coating comprises a polymer layer, a metal interlayer and an amorphous metal coating. The polymer layer is formed on a substrate and acts as a diffusion barrier layer, which is thick and dense enough to prevent the corrosive substances from penetrating into the substrate. The metal interlayer is formed between the polymer layer and the amorphous metal coating for improving the adhesion of the amorphous metal coating to the substrate.

An embodiment relates to an ultrasonic additive manufacturing process, comprising joining a foil comprising a bulk metallic glass to a substrate; and forming a cladded composite comprising the foil and the substrate; wherein a thickness of the cladded composite is greater than a critical casting thickness of the bulk metallic glass, wherein the cladded composite comprises a cladding layer of the bulk metallic glass on the substrate and the bulk metallic glass comprises approximately 0% crystallinity, approximately 0% porosity, less than 50 MPa thermal stress, approximately 0% distortion, approximately 0 inch heat affected zone, approximately 0% dilution, and a strength of about 2,000-3,500 MPa.

A composite structure with an aluminum-based alloy layer containing boron carbide and a manufacturing method thereof are provided. The composite structure includes a substrate with an open hole in that surface and the aluminum-based alloy layer containing boron carbide. The aluminum-based alloy layer is disposed in the open hole and contains aluminum, boron, carbon, and oxygen, wherein the content of aluminum is between 4 at. % and 55 at. %, the content of boron is between 9 at. % and 32 at. %, the content of carbon is between 13 at. % and 32 at. %, the content of oxygen is between 2 at. % and 38 at. %, and the ratio of the content of boron to carbon is between 0.3 and 2.7.

A manufacturing method of a home appliance including a hairline according to disclosed embodiment includes forming at least one plating layer on the base material, processing the transverse hairline on the upper surface of the plating layer by tilting the hairline processing wheel at a predetermined angle, and forming a coating layer on the hairline.

An embodiment relates to an ultrasonic additive manufacturing process, comprising joining a foil comprising a bulk metallic glass to a substrate; and forming a cladded composite comprising the foil and the substrate; wherein a thickness of the cladded composite is greater than a critical casting thickness of the bulk metallic glass, wherein the cladded composite comprises a cladding layer of the bulk metallic glass on the substrate and the bulk metallic glass comprises approximately 0% crystallinity, approximately 0% porosity, less than 50 MPa thermal stress, approximately 0% distortion, approximately 0 inch heat affected zone, approximately 0% dilution, and a strength of about 2,000-3,500 MPa.

Systems, methods, components, and parts are provided for improving casting and electroplating performance of a plated cast part by doping a semiconductor material with an electrically active dopant before mixing the semiconductor material into a base material. The doped semiconductor material improves the castability of the base material and has an improved electrical conductivity which is closer to that of the base material such that a consistency of a subsequent plating on the part is improved.

A composite structure with an aluminum-based alloy layer containing boron carbide and a manufacturing method thereof are provided. The composite structure includes a substrate with an open hole in that surface and the aluminum-based alloy layer containing boron carbide. The aluminum-based alloy layer is disposed in the open hole and contains aluminum, boron, carbon, and oxygen, wherein the content of aluminum is between 4 at. % and 55 at. %, the content of boron is between 9 at. % and 32 at. %, the content of carbon is between 13 at. % and 32 at. %, the content of oxygen is between 2 at. % and 38 at. %, and the ratio of the content of boron to carbon is between 0.3 and 2.7.

An embodiment relates to an ultrasonic additive manufacturing process, comprising joining a foil comprising a bulk metallic glass to a substrate; and forming a cladded composite comprising the foil and the substrate; wherein a thickness of the cladded composite is greater than a critical casting thickness of the bulk metallic glass, wherein the cladded composite comprises a cladding layer of the bulk metallic glass on the substrate and the bulk metallic glass comprises approximately 0% crystallinity, approximately 0% porosity, less than 50 MPa thermal stress, approximately 0% distortion, approximately 0 inch heat affected zone, approximately 0% dilution, and a strength of about 2,000-3,500 MPa.

A coating system for a surface of a superalloy component is provided. The coating system includes a MCrAlY coating on the surface of the superalloy component, where M is Ni, Fe, Co, or a combination thereof. The MCrAlY coating generally has a higher chromium content than the superalloy component. The MCrAlY coating also includes a platinum-group metal aluminide diffusion layer. The MCrAlY coating includes Re, Ta, or a mixture thereof. Methods are also provided for forming a coating system on a surface of a superalloy component.

A sliding-hearing composite material includes a steel supporting layer (10), an intermediate layer (12) based on an aluminum alloy that is free of lead, and a bearing metal layer (14) based on an aluminum alloy that is free of lead, wherein the aluminum alloy of the intermediate layer (12) has a composition having 3.5 to 4.5 wt % copper, 0.1 to 1.5 wt % manganese, 0.1 to 1.5 wt % magnesium, and the usual admissible impurities, the remainder being aluminum, and wherein the aluminum alloy of the bearing mental layer (14) has a composition having wt % tin, 1.0-3.0 wt % nickel, 0.5-1.0 wt % manganese, 0.5-1.0 wt % copper, 0.15-0.25 wt % chromium, 0.1-0.3 wt % vanadium, and the usual admissible impurities, he remainder being aluminum. A sliding bearing element and the use of the sliding-bearing composite material for sliding bearing element, particularly sliding bearing shells, sliding bearing bushes, or thrust washers is also disclosed.