The present disclosure provides a cold-rolled steel sheet having excellent high-temperature properties and room-temperature workability, including, by weight: carbon (C): 0.0005 to 0.003%, manganese (Mn): 0.20 to 0.50%, aluminum (Al): 0.01 to 0.10%, phosphorus (P): 0.003 to 0.020%, nitrogen (N): 0.0005 to 0.004%, sulfur (S): 0.015% or less, niobium (Nb): 0.005 to 0.040%, chromium (Cr): 0.10 to 0.50%, tungsten (W): 0.02 to 0.07%, and a balance of iron (Fe) and other inevitable impurities, wherein C, Nb, and W satisfy the following relationship 1, a microstructure comprises 95 area % or more of polygonal ferrite and 5 area % or less of acicular ferrite, and the cold-rolled steel sheet comprises (Nb,W)C-based precipitates having an average size of 0.005 to 0.10 μm and a method for manufacturing the same:
0.00025≤(2×Nb/93)×(W/184)/(C/12)≤0.0015  [Relationship 1]
where, C, Nb, and W are in weight %.

A coating-substrate combination includes: a Ni-based superalloy substrate comprising, by weight percent: 2.0-5.1 Cr; 0.9-3.3 Mo; 3.9-9.8 W; 2.2-6.8 Ta; 5.4-6.5 Al; 1.8-12.8 Co; 2.8-5.8 Re; 2.8-7.2 Ru; and a coating comprising, exclusive of Pt group elements, by weight percent: Ni as a largest content; 5.8-9.3 Al; 4.4-25 Cr; 3.0-13.5 Co; up to 6.0 Ta, if any; up to 6.2 W, if any; up to 2.4 Mo, if any; 0.3-0.6 Hf; 0.1-0.4 Si; up to 0.6 Y, if any; up to 0.4 Zr, if any; up to 1.0 Re, if any.

The present disclosure provides a composite coating and a method for fabricating the composite coating. The composite coating comprises a polymer layer, a metal interlayer and an amorphous metal coating. The polymer layer is formed on a substrate and acts as a diffusion barrier layer, which is thick and dense enough to prevent the corrosive substances from penetrating into the substrate. The metal interlayer is formed between the polymer layer and the amorphous metal coating for improving the adhesion of the amorphous metal coating to the substrate.

The present invention provides a nickel-plated heat-treated steel sheet for a battery can (1), having a nickel layer with a nickel amount of 4.4 to 26.7 g/m.sup.2 on a steel sheet (11), wherein when the Fe intensity and the Ni intensity are continuously measured along the depth direction from the surface of the nickel-plated heat-treated steel sheet for a battery can, by using a high frequency glow discharge optical emission spectrometric analyzer, the difference (D2-D1) between the depth (D1) at which the Fe intensity exhibits a first predetermined value and the depth (D2) at which the Ni intensity exhibits a second predetermined value is less than 0.04 μm.

The present disclosure relates to coated non-metallic substrates and coated metallic substrates, and methods for producing such coated substrates. A variant of the method is characterized in that a mat or glossy coating is underneath a metallic layer obtained in some cases by way of vapor deposition and/or sputtering. In another variant, the metallic is sufficiently thin so that it remains transparent or translucent to visible light. The coated substrates may include multiple layers such as metallic layers, polysiloxane layers, a color layer, a conversion layer, a primer layer, and/or a transparent or colored layer. An application system for applying a metallic layer to at least one surface of a substrate may include a plasma generator and/or a corona system for treating one or more layers by plasma treatment and/or corona treatment.

A gas turbine engine article includes a substrate and an environmental barrier coating disposed on the substrate. The environmental barrier coating includes oxygen-scavenging particles. Each oxygen-scavenging particle includes a silicon-containing core particle encased in an oxygen barrier shell.

In a terminal material with a silver coating film including a silver layer on a surface, a terminal and a terminal material having high reliability are easily manufactured with low cost without a heat treatment. A base material formed of copper or a copper alloy; and nickel layer, an intermediate layer, and a silver layer laminated on the base material in this order are included, the nickel layer has a thickness of 0.05 μm to 5.00 μm and is formed of nickel or a nickel alloy, the intermediate layer has a thickness of 0.02 μm to 1.00 μm and is an alloy layer containing silver (Ag) and a substance X, and the substance X includes one or more kinds of tin, bismuth, gallium, indium, and germanium.

The disclosure provides for a layered metal with resistance to hydrogen induced cracking and method of production thereof, comprising a core metal alloy and a skin metal alloy. The core metal alloy comprises twinned boundaries. The core metal alloy has undergone plastic deformation and a heat treatment. The core metal alloy comprises nickel and cobalt. The skin metal alloy is disposed on the core metal alloy, wherein the skin metal alloy comprises an entropy greater than the core metal alloy. The core metal alloy comprises a greater density of twinned boundaries than the skin metal alloy. The skin metal alloy comprises a stacking fault energy of at least about 50 mJ/m.sup.2, and the skin metal alloy comprises iron, aluminum, and boron.

An object of the present invention is to provide a new electroless plating film which can prevent the diffusion of molten solder to a metal material constituting a conductor. The present invention is an electroless Co—W plating film, wherein content of W is in an amount of 35 to 58 mass % and a thickness of the film is 0.05 μm or more.

The present invention relates to a protective layer against CMAS, to a CMAS-resistant article comprising the protective layer according to the invention, and to a process for preparing a corresponding article.