The present disclosure provides a cold-rolled steel sheet having excellent high-temperature properties and room-temperature workability, including, by weight: carbon (C): 0.0005 to 0.003%, manganese (Mn): 0.20 to 0.50%, aluminum (Al): 0.01 to 0.10%, phosphorus (P): 0.003 to 0.020%, nitrogen (N): 0.0005 to 0.004%, sulfur (S): 0.015% or less, niobium (Nb): 0.005 to 0.040%, chromium (Cr): 0.10 to 0.50%, tungsten (W): 0.02 to 0.07%, and a balance of iron (Fe) and other inevitable impurities, wherein C, Nb, and W satisfy the following relationship 1, a microstructure comprises 95 area % or more of polygonal ferrite and 5 area % or less of acicular ferrite, and the cold-rolled steel sheet comprises (Nb,W)C-based precipitates having an average size of 0.005 to 0.10 μm and a method for manufacturing the same:
0.00025≤(2×Nb/93)×(W/184)/(C/12)≤0.0015  [Relationship 1]
where, C, Nb, and W are in weight %.

Systems and methods for low-manganese welding alloys are disclosed. An example arc welding consumable may comprise: less than 0.4 wt % manganese; strengthening agents selected from the group consisting of nickel, cobalt, copper, carbon, molybdenum, chromium, vanadium, silicon, and boron; and grain control agents selected from the group consisting of niobium, tantalum, titanium, zirconium, and boron. The grain control agents may comprise greater than 0.06 wt % and less than 0.6 wt % of the welding consumable. The resulting weld deposit may comprise a tensile strength greater than or equal to 70 ksi, a yield strength greater than or equal to 58 ksi, a ductility (as measured by percent elongation) of at least 22%, and a Charpy V-notch toughness greater than or equal to 20 ft-lbs at −20° F. The welding consumable may provide a manganese fume generation rate less than 0.01 grams per minute during the arc welding operation.

A hot stamped component, includes: a base material; and a Zn-based plating layer provided in contact with the base material as an upper layer of the base material and containing Zn and Ni. A region of the Zn-based plating layer on a base material side is a Fe—Zn solid solution containing Ni, and two or more twins exist in 10 crystal grains of the Fe—Zn solid solution containing Ni adjacent to an interface between the base material and the Zn-based plating layer.

A process for manufacturing a coated metal strip having a metallic corrosion protection coating is provided. The process includes passing a metal strip through a molten metal bath comprising from 2 to 8 wt % aluminum, 0 to 5 wt % magnesium, up to 0.3 wt % additional elements, and a balance including zinc and inevitable impurities, to yield a molten metal coated metal strip, wiping the molten metal coated metal strip with a nozzle spraying a gas on either side of the molten metal coated metal strip and cooling the coating in a controlled manner until the coating has completely solidified, to obtain the coated metal strip. A temperature of the molten metal bath is from 350 to 700° C., and the cooling is conducted at a rate less than 15° C./s between a temperature on leaving a unit where the wiping occurs and a start of solidification of the coating, and then at a rate greater than or equal to 15° C./s between a start and an end of solidification of the coating.

A high-strength galvanized steel sheet that includes a chemical composition containing, by mass %, C: 0.15% or more and 0.25% or less, Si: 0.50% or more and 2.5% or less, Mn: 2.3% or more and 4.0% or less, P: 0.100% or less, S: 0.02% or less, Al: 0.01% or more and 2.5% or less, and Fe and inevitable impurities. The steel sheet having a microstructure containing, by an area percentage basis, a tempered martensite phase: 30% or more and 73% or less, a ferrite phase: 25% or more and 68% or less, a retained austenite phase: 2% or more and 20% or less, and other phases: 10% or less (including 0%), the other phases containing a martensite phase: 3% or less (including 0%) and a bainitic ferrite phase: less than 5% (including 0%).

Disclosed herein is a high-strength plated steel sheet having a plated layer on the surface of a base steel sheet and containing predetermined steel components. The steel sheet includes, in the order from the interface of the base steel sheet and the plated layer towards the base steel sheet: a soft layer having a Vickers hardness that is 90% or less of the Vickers hardness at a portion t/4 of the base steel sheet, where t is a sheet thickness of the base steel sheet; and a hard layer consisting of a structure which is mainly composed of martensite and bainite and in which the average grain size of prior austenite is 20 μm or less. The average depth D of the soft layer is 20 μm or greater, and the average depth d of an internal oxide layer is 4 μm or greater and smaller than D.

The high-strength plated steel sheet of the present invention has a plated layer on the surface of a base steel sheet and contains predetermined steel components. The steel sheet includes, in the order from the interface of the base steel sheet and the plated layer towards the base steel sheet: a soft layer having a Vickers hardness that is 90% or less of the Vickers hardness at a portion t/4 of the base steel sheet, where t is a sheet thickness of the base steel sheet: and a hard layer containing martensite, bainite, and ferrite in predetermined ranges. The average depth D of the soft layer is 20 μm or greater, and the average depth d of an internal oxide layer is 4 μm or greater and smaller than D.

Provided is a plated steel material which can be used for an automobile, a household appliance, a building material, and the like and, more particularly, to a zinc alloy plated steel material having excellent corrosion resistance after being processed and a method for manufacturing the same.

A hot stamped component, includes: a base material; and a Zn-based plating layer provided in contact with the base material as a layer above the base material and containing Zn. A base material side of the Zn-based plating layer is a Fe—Zn solid solution, and two or more twins exist in 10 crystal grains of the Fe—Zn solid solution adjacent to an interface between the base material and the Zn-based plating layer.

The present invention provides a nickel-plated heat-treated steel sheet for a battery can (1), having a nickel layer with a nickel amount of 4.4 to 26.7 g/m.sup.2 on a steel sheet (11), wherein when the Fe intensity and the Ni intensity are continuously measured along the depth direction from the surface of the nickel-plated heat-treated steel sheet for a battery can, by using a high frequency glow discharge optical emission spectrometric analyzer, the difference (D2-D1) between the depth (D1) at which the Fe intensity exhibits a first predetermined value and the depth (D2) at which the Ni intensity exhibits a second predetermined value is less than 0.04 μm.