A biodegradable cellulose fiber-based substrate, at least one side of which is coated with a release coating including: a) at least one water-soluble polymer (WSP) containing hydroxyl groups, and b) at least one lactone substituted with at least one linear or branched and/or cyclic C.sub.8-C.sub.30 hydrocarbon chain which may contain heteroatoms. The biodegradable substrate is certified biodegradable in accordance with EN 13432. A method of production thereof is also disclosed.

A water-based, carbon filler-dispersed coating formulation for forming a conductive coating film contains (1) a hydroxyalkyl chitosan as a resin binder, (2) a conductive carbon filler, and (3) a polybasic acid or its derivative in a water-based medium containing at least water as a polar solvent. In 100 parts by mass of the coating formulation, the hydroxyalkyl chitosan (1) is contained in a range of from 0.1 to 20 parts by mass, and the conductive carbon filler (2) is contained in a range of from 1 to 30 parts by mass. An electricity-imparting material, an electrode plate for an electricity storage device, a process for producing the electrode plate, and the electricity storage device are also disclosed.

A cellulose fiber-based substrate, at least one side of which is coated with an aqueous mixture composed of: a) at least one water-soluble polymer (WSP) containing hydroxyl groups, b) at least one lactone substituted with at least one linear or branched and/or cyclic C.sub.8-C.sub.30 hydrocarbon chain which may contain heteroatoms, c)at least one crosslinking agent. A method of production and use thereof.

A biodegradable cellulose fiber-based substrate, at least one side of which is coated with a release coating including: a) at least one water-soluble polymer (WSP) containing hydroxyl groups, and b) at least one lactone substituted with at least one linear or branched and/or cyclic C.sub.8-C.sub.30 hydrocarbon chain which may contain heteroatoms. The biodegradable substrate is certified biodegradable in accordance with EN 13432. A method of production thereof is also disclosed.

A cellulose fiber-based substrate, at least one side of which is coated with an aqueous mixture composed of: a) at least one water-soluble polymer (WSP) containing hydroxyl groups, b) at least one lactone substituted with at least one linear or branched and/or cyclic C.sub.8-C.sub.30 hydrocarbon chain which may contain heteroatoms, c) at least one crosslinking agent. A method of production and use thereof.

Protection barriers, such as floor protection barriers, and methods for making and using same. The protection barrier can include a base sheet and an energy absorbing layer. The base sheet can have two or more paperboard layers and one or more sizing layers. A first paperboard layer can form a first surface of the base sheet, a second paperboard layer can form a second surface of the base sheet, and the one or more sizing layers can be disposed between the first and second paperboard layers. The energy absorbing layer can be secured to the second paperboard layer.

The present application relates to wood boards, particularly post-cured wood boards and more particularly to particle board with excellent swelling properties; it also relates to a process for production of such boards.

A process for reducing the permeability of a paper wrapper used in the construction of a smoking article is disclosed. The paper wrapper is treated with a film-forming composition that forms treated discrete areas on the wrapper. The treated discrete areas have a permeability within a predetermined range sufficient to reduce the ignition proclivity properties of a smoking article made with the wrapper. In accordance with the present invention, the film-forming composition contains a film-forming material. The film-forming material has a relatively low viscosity. In this manner, the film-forming composition can have a relatively high solids content and still be applied to the wrapper using conventional techniques, such as by using a gravure printer.

The present invention relates to a curtain coatable gas barrier coating composition comprising polyvinyl alcohol and a surfactant, in which the surfactant is a water-soluble non-ionic ethoxylated alcohol. The present invention also relates to a method for providing a substrate with a gas barrier layer by means of the coating composition, and a coated substrate having at least one gas barrier layer obtained by coating the substrate with the coating composition. Further, the invention relates to a packaging material comprising a coated paperboard coated with the coating composition, and a liquid package comprising such a packaging material.

A process for reducing the permeability of a paper wrapper used in the construction of a smoking article is disclosed. The paper wrapper is treated with a film-forming composition that forms treated discrete areas on the wrapper. The treated discrete areas have a permeability within a predetermined range sufficient to reduce the ignition proclivity properties of a smoking article made with the wrapper. In accordance with the present invention, the film-forming composition contains a film-forming material. The film-forming material has a relatively low viscosity. In this manner, the film-forming composition can have a relatively high solids content and still be applied to the wrapper using conventional techniques, such as by using a gravure printer.