METHODS, SYSTEMS, AND CATALYSTS FOR THE DIRECT CONVERSION OF SYNGAS TO HIGH-OCTANE HYDROCARBONS
20220048834 · 2022-02-17
Inventors
- Daniel Ruddy (Arvada, CO, US)
- Jesse Evan HENSLEY (Arvada, CO, US)
- Joshua A. Schaidle (Arvada, CO, US)
- Connor Patrick NASH (Lakewood, CO, US)
- Anh The TO (Denver, CO, US)
Cpc classification
B01J8/0438
PERFORMING OPERATIONS; TRANSPORTING
C10G3/49
CHEMISTRY; METALLURGY
C07C29/154
CHEMISTRY; METALLURGY
C07C29/154
CHEMISTRY; METALLURGY
C07C41/09
CHEMISTRY; METALLURGY
B01J21/066
PERFORMING OPERATIONS; TRANSPORTING
B01J8/04
PERFORMING OPERATIONS; TRANSPORTING
Y02P20/52
GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
Y02P30/20
GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
C07C41/09
CHEMISTRY; METALLURGY
B01J2208/025
PERFORMING OPERATIONS; TRANSPORTING
C07C2521/06
CHEMISTRY; METALLURGY
International classification
B01J21/06
PERFORMING OPERATIONS; TRANSPORTING
B01J29/70
PERFORMING OPERATIONS; TRANSPORTING
B01J35/00
PERFORMING OPERATIONS; TRANSPORTING
B01J8/04
PERFORMING OPERATIONS; TRANSPORTING
C07C29/154
CHEMISTRY; METALLURGY
Abstract
The present disclosure relates to a method that includes converting a gas stream that contains hydrogen (H.sub.2) and carbon monoxide (CO) to a second mixture that contains a hydrocarbon, for example, a hydrocarbon having between 3 and 15 carbon atoms, where the converting is performed using a first catalyst configured to convert H.sub.2 and CO to methanol, a second catalyst configured to convert methanol to dimethyl ether (DME), and a third catalyst configured to convert DME to the hydrocarbon.
Claims
1. A method comprising: converting a gas stream comprising hydrogen (H.sub.2) and carbon monoxide (CO) to a second mixture comprising a hydrocarbon having between 3 and 15 carbon atoms, wherein: the converting is performed using a first catalyst configured to convert H.sub.2 and CO to methanol, a second catalyst configured to convert methanol to dimethyl ether (DME), and a third catalyst configured to convert DME to the hydrocarbon.
2. The method of claim 1, wherein the first catalyst comprises copper and a zinc oxide.
3. The method of claim 2, wherein the first catalyst further comprises at least one of silica, alumina, zirconia, or ceria.
4. The method of claim 1, wherein the second catalyst comprises at least one of an alumina or silica.
5. The method of claim 1, wherein the third catalyst comprises at least one of copper or a zeolite.
6. The method of claim 5, wherein the zeolite comprises a beta zeolite having a silica to alumina ratio between about 20:1 and about 300:1.
7. The method of claim 6, wherein the copper in the third catalyst is present at a concentration between about 1 wt % and about 20 wt %, relative to the total weight of the third catalyst.
8. The method of claim 1, wherein the first catalyst and the second catalyst are present at a ratio between about 1:1 and about 8:1.
9. The method of claim 8, wherein the second catalyst and the third catalyst are present at a ratio between about 0.1:1 and about 5:2.
10. The method of claim 1, wherein the first catalyst is positioned in a first zone, the second catalyst is positioned in a second zone, and the third catalyst is positioned in a third zone; and the first zone, the second zone and the third zone are all contained in a single reactor.
11. The method of claim 10, wherein the single reactor is a packed bed.
12. The method of claim 11, wherein: the first catalyst is positioned in the packed bed in a first layer, the second catalyst is positioned in the packed bed in a second layer, the third catalyst is positioned in the packed bed in a third layer, and the second layer is positioned in series between the first layer and the second layer.
13. The method of claim 11, wherein: the first catalyst and the second catalyst are positioned in the packed bed as a well-mixed mixture in a first layer, the third catalyst is positioned in the packed bed in a second layer, and the first layer and the second layer are positioned in series.
14. The method of claim 11, wherein the first catalyst, the second catalyst, and the third catalyst are positioned in the packed bed as a well-mixed mixture in a single layer.
15. The method of claim 11, wherein: the first catalyst is positioned in the packed bed in a first layer, the second catalyst and the third catalyst are positioned in the packed bed as a well-mixed mixture in a second layer, and the first layer and the second layer are positioned in series.
16. The method of claim 1, wherein: the first catalyst and the second catalyst are positioned in a first reactor in a packed bed as a well-mixed mixture; the third catalyst is positioned in a second reactor, and the first reactor and the second reactor are positioned in series.
17. The method of claim 1, wherein the gas stream further comprises carbon dioxide (CO.sub.2).
18. The method of claim 17, wherein the gas stream has a concentration of carbon dioxide greater than or equal to 10 mol %.
19. A composition comprising: a first layer comprising copper and a zinc oxide; a second layer comprising at least one of an alumina or silica; and a third layer comprising a zeolite; and the second layer is positioned between the first layer and the third layer.
20. A system comprising: at least one of a first reactor or a second reactor, wherein: at least one of the first reactor or the second reactor contains a catalyst or composition as described herein.
Description
BRIEF DESCRIPTION OF DRAWINGS
[0014]
[0015]
[0016]
[0017]
[0018]
[0019]
[0020]
[0021]
[0022]
[0023]
[0024]
[0025]
[0026]
[0027]
[0028]
[0029]
[0030]
REFERENCE NUMERALS
[0031]
TABLE-US-00001 100 system 110 feed stream 120 product stream 125 recycle stream 130 packed bed reactor 132 catalyst bed 134 first catalyst layer 136 second catalyst layer 138 third catalyst layer
DETAILED DESCRIPTION
[0032] The embodiments described herein should not necessarily be construed as limited to addressing any of the particular problems or deficiencies discussed herein. References in the specification to “one embodiment”, “an embodiment”, “an example embodiment”, “some embodiments”, etc., indicate that the embodiment described may include a particular feature, structure, or characteristic, but every embodiment may not necessarily include the particular feature, structure, or characteristic. Moreover, such phrases are not necessarily referring to the same embodiment. Further, when a particular feature, structure, or characteristic is described in connection with an embodiment, it is submitted that it is within the knowledge of one skilled in the art to affect such feature, structure, or characteristic in connection with other embodiments whether or not explicitly described.
[0033] As used herein the term “substantially” is used to indicate that exact values are not necessarily attainable. By way of example, one of ordinary skill in the art will understand that in some chemical reactions 100% conversion of a reactant is possible, yet unlikely. Most of a reactant may be converted to a product and conversion of the reactant may asymptotically approach 100% conversion. So, although from a practical perspective 100% of the reactant is converted, from a technical perspective, a small and sometimes difficult to define amount remains. For this example of a chemical reactant, that amount may be relatively easily defined by the detection limits of the instrument used to test for it. However, in many cases, this amount may not be easily defined, hence the use of the term “substantially”. In some embodiments of the present invention, the term “substantially” is defined as approaching a specific numeric value or target to within 20%, 15%, 10%, 5%, or within 1% of the value or target. In further embodiments of the present invention, the term “substantially” is defined as approaching a specific numeric value or target to within 1%, 0.9%, 0.8%, 0.7%, 0.6%, 0.5%, 0.4%, 0.3%, 0.2%, or 0.1% of the value or target.
[0034] As used herein, the term “about” is used to indicate that exact values are not necessarily attainable. Therefore, the term “about” is used to indicate this uncertainty limit. In some embodiments of the present invention, the term “about” is used to indicate an uncertainty limit of less than or equal to ±20%, ±15%, ±10%, ±5%, or ±1% of a specific numeric value or target. In some embodiments of the present invention, the term “about” is used to indicate an uncertainty limit of less than or equal to ±1%, ±0.9%, ±0.8%, ±0.7%, ±0.6%, ±0.5%, ±0.4%, ±0.3%, ±0.2%, or ±0.1% of a specific numeric value or target.
[0035] As used herein, the term “hydrocarbon” refers to a molecule having a molecular structure comprising carbon and hydrogen. Hydrocarbons may refer to straight-chain or branching aliphatic or aromatic compounds. Hydrocarbons may be classified, as described herein, by the total number of carbons within the molecule. In some embodiments, hydrocarbons may include 0 molecules in functional groups, for example, alcohols, aldehydes, ketones, etc. In some embodiments, hydrocarbons may include other elements as functional groups, for example, N, S, P, etc.
[0036] As used herein, the term syngas refers to a mixture of H gas and carbon monoxide gas (CO). Syngas may also include some concentration of carbon dioxide gas (CO.sub.2).
[0037] Among other things, the present disclosure relates to the direct conversion of syngas to HOG in a single step, using a single reactor, operating at one process condition (e.g., no temperature or minimal pressure gradient through the reactor). Also shown herein is that CO.sub.2 with H.sub.2 can be converted to HOG in a single step, and in a single reactor, under similar process conditions to conventional three reactor systems and that CO/CO.sub.2 mixtures with H.sub.2 can be converted to HOG in a single-step, in a single reactor, operating at one process condition. A stacked catalyst bed configuration, as shown herein, is advantageous for all three feed options (syngas, CO.sub.2+H.sub.2, and CO/CO.sub.2+H.sub.2). As discussed below in detail, the advantages of a stacked catalyst bed contained in a single reactor is highlighted by the conversion of CO.sub.2 to HOG, where C4+ hydrocarbon products were not observed using a mixed catalyst bed in a single reactor. However, C4+ hydrocarbon yields of greater than 25% were achieved in a single-pass using a stacked catalyst bed configuration in a single reactor.
[0038]
[0039] In some embodiments of the present disclosure, a first catalyst layer 134 may include a first catalyst designed to convert at least one of hydrogen (H.sub.2), carbon monoxide (CO), carbon dioxide (CO.sub.2), and/or water to methanol. A catalyst for converting a feed stream 110 (e.g., of H.sub.2, CO, CO.sub.2, water) to methanol may include a solid catalyst that includes copper and zinc oxide. As shown herein, a second catalyst layer 136 may include a second catalyst designed to convert methanol to dimethyl ether (DME). In some embodiments of the present disclosure, a second catalyst for converting methanol to DME may include a solid catalyst that includes at least one of alumina and/or silica and/or a zeolite. As shown herein, a third catalyst layer 138 may include a third catalyst designed to convert DME to high-octane gas (HOG). In some embodiments of the present disclosure, a third catalyst for converting DME to HOG may include a solid catalyst that includes at least one of copper and/or a zeolite. A zeolite may for converting DME to HOG may have a silica to alumina ratio between about 20:1 and about 300:1, or between about 25:1 and about 30:1. In some embodiments of the present disclosure, a zeolite for converting DME to HOG may include a beta zeolite. In some embodiments of the present disclosure, a third catalyst for converting DME to HOG may include a zeolite and copper, where the copper is present at a concentration between about 1 wt % and about 20 wt %, relative to the total weight of the third catalyst, or between about 4 wt % and 10 wt %.
[0040] In some embodiments of the present disclosure, any of the catalysts described herein may have any solid shape or form suitable for the given application and/or scale of the process. For example, a catalyst may have a cylindrical form, spherical form, irregular granular form, etc. Further, any of the solid catalysts described herein may have any characteristic length and/or diameter needed for a specific application and/or scale. For example, a catalyst may have a characteristic diameter between about 1/16 inch and about ¼ inch, or a characteristic length between about ½ inch and about 2 inches.
[0041] Referring again to
[0042] For example, a stacked catalyst bed 132 of a packed bed reactor 130 may have only two distinct layers of catalyst, where each of the two distinct layers may include a single catalyst or a mixture of at least two catalysts. In some embodiments of the present disclosure, a stacked catalyst bed 132 may include a first catalyst layer 134 and a second catalyst layer 136 (i.e., no third catalyst layer 138), where the first catalyst layer 135 includes a mixture of at least two catalysts, a first catalyst for converting a feed stream 110 to methanol and a second catalyst for converting methanol to DME, and the second catalyst layer 136 includes essentially only one catalyst for converting DME to HOG. In some embodiments of the present disclosure, a stacked catalyst bed 132 of a packed bed reactor 130 may include a first catalyst layer 134 and a second catalyst layer 136 (i.e., no third catalyst layer 138), where the first catalyst layer 135 includes essentially only one catalyst for converting a feed stream 110 to methanol and the second catalyst layer 136 includes a mixture of a second catalyst for converting methanol to DME and a third catalyst for converting DME to HOG. In some embodiments of the present disclosure, a packed bed reactor 130 may have a mixed catalyst bed 132 having only a single catalyst layer where the single catalyst layer includes a mixture of at least three catalysts, a first catalyst for converting a feed stream 110 to methanol, a second catalyst for converting methanol to DME, and a third catalyst for converting DME to HOG.
[0043] When combining more than one catalyst into a single layer, the catalysts may be combined into a single homogeneous mixture (i.e., essentially no variation in catalyst concentration as a function of position within the catalyst layer) by standard mixing operations; e.g., tumbling, grinding, pressing, extruding. Such a homogeneous mixture may be formed by combining at least two catalyst powders, mixing them, and pressing them into pellets that contain the two or more catalysts. Or each individual catalyst may be pressed into its own batch of pellets after which the two or more batches of pellets are mixed together into a homogeneous mixture. So, in some embodiments of the present disclosure, a packed bed reactor 130 may include a stacked catalyst bed 132 having two or more distinct catalyst layers, where at least one of the catalyst layers includes two or more catalyst types. In other words, a portion of a stacked catalyst bed may include a mixed catalyst bed. Further, in some embodiments of the present disclosure, a catalyst layer (e.g., 134, 136, and/or 138) may also include an inert solid such as silicon carbide to minimize channeling, axial dispersion, and/or temperature gradients in the packed bed reactor 130.
[0044] The ratios of the catalysts present in a packed bed reactor 130 may be varied depending on, among other things, the composition and/or conditions of the feed stream 110. In addition to varying the composition of the feed stream 110, e.g., H.sub.2:CO ratio, the temperature of the feed stream 110 entering a packed bed reactor 130 may be in a range between about 180° C. and about 320° C., according to some embodiments of the present disclosure. The pressure of the feed stream 110 entering a packed bed reactor 130 may be between about 300 kPa and about 5.5 MPa. In some embodiments of the present disclosure, the pressure-drop through a packed bed reactor 130 may be between zero Pa and about 500 kPa. In some embodiments of the present disclosure, the feed stream 110 may be provided at a flow rate such that a space velocity is achieved in the packed bed reactor 130 between about 0.2 g CO/g catalyst hr and about 1.5 g CO/g catalyst hr, or between about 0.2 g CO/g catalyst hr and about 0.8 g CO/g catalyst hr. In some embodiments of the present disclosure, the feed stream 110 may be provided at a flow rate such that a space velocity is achieved in the packed bed reactor 130 between about 0.2 g DME/g catalyst hr and about 1.5 g DME/g catalyst hr, or between about 0.2 g DME/g catalyst hr and about 0.8 g DME/g catalyst hr. The ratio of the first catalyst to the second catalyst may be between about 1:1 and about 8:1, or between about 1:1 and about 32:5, according to some embodiments of the present disclosure. The ratio of the second catalyst to the third catalyst may be between about 0.1:1 and about 5:2, or between about 0.1:1 and 3:1, according to some embodiments of the present disclosure. As described herein, these catalyst ratios may be used both for the embodiment where each catalyst is provided in its own distinct layer and also for the embodiments utilizing mixtures of catalysts.
[0045] Referring again to
[0046] Referring again to
[0047] In a first example, a first packed bed reactor may include a stacked catalyst bed having a first catalyst layer that includes essentially only a catalyst for converting syngas to methanol, followed in series by a second catalyst layer that includes essentially only a catalyst for converting methanol to DME. The DME produced in the first packed bed reactor may then be directed to a second packed bed reactor (e.g., via conduit, piping, etc.) that includes a stacked catalyst bed of essentially only a single catalyst layer of only one catalyst for converting DME to HOG. In a second example, a first packed bed reactor may include a mixed catalyst bed having only a single catalyst layer of a mixture of two catalysts, a first catalyst for converting syngas to methanol and a second catalyst for converting methanol to DME. The DME produced in the first packed bed reactor may then be directed to a second packed bed reactor (e.g., via conduit, piping, etc.) that includes a stacked catalyst bed of essentially only a single catalyst layer having only a single catalyst for converting DME to HOG. In a third example, a first packed bed reactor may include a stacked catalyst bed having a single catalyst layer that includes essentially only one catalyst for converting syngas to methanol. The methanol produced in the first packed bed reactor may then be directed to a second packed bed reactor (e.g., via conduit, piping, etc.) having a stacked catalyst bed that includes a first catalyst layer of a first catalyst for converting methanol to DME and a second catalyst layer of a second catalyst in series for converting DME to HOG. In a fourth example, a first packed bed reactor may include a stacked catalyst bed having a single catalyst layer that includes essentially only one catalyst for converting syngas to methanol. The methanol produced in the first packed bed reactor may then be directed to a second packed bed reactor (e.g., via conduit, piping, etc.) having a mixed catalyst bed of a single catalyst layer of a mixture of a first catalyst and a second catalyst, where the first catalyst converts methanol to DME and the second catalyst converts DME to HOG. Among other things, the systems and methods and their corresponding features described above may improve the overall yield of HOG, reduce CO.sub.2 emissions, and improve the process economics for producing HOG.
[0048] The systems, methods, and catalysts described herein, among other things, convert CO and/or CO.sub.2 with co-fed H.sub.2 to hydrocarbons through a series of reactions performed by each catalyst in a single reactor, or in one or more reactors. As described herein, a single reactor was tested that included a first catalyst of copper-zinc oxide-alumina (CZA) to perform methanol synthesis as shown in Reaction 1, a second catalyst of gamma-alumina (A) to perform methanol dehydration as shown in in Reaction 2, and a third catalyst of Cu/BEA to perform hydrocarbon synthesis as shown in Reaction 3, where the targeted hydrocarbon product was a high-octane gasoline (HOG) mixture, rich in 2,2,3-trimethylbutane (a.k.a. triptane). When feeding syngas, Reactions 1, 2, and 3 occur sequentially in this scheme, suggesting that an optimum HOG yield can be achieved by controlling the relative activity of each catalyst and/or the mass ratio of catalysts in the reactor. Reaction 4, the water-gas shift reaction (WGSR), is a known side-reaction in this system that can be catalyzed by both CZA and Cu/BEA. When feeding CO.sub.2 and H.sub.2, the reverse-WGSR is the first step in the reaction sequence, converting CO.sub.2 to CO that can then be converted to methanol via Reaction 1. Note that all of Reactions 1-4 have a thermodynamic equilibrium at the reaction temperatures tested here (between about 220° C. and about 240° C.) that can limit the extent to which reactants may be converted. Further, the reverse of Reactions 1 and 2 can occur at high concentrations of water or MeOH in the reactor. For methanol synthesis, Reaction 1, this equilibrium limitation is especially problematic as its equilibrium constant is small, ranging from K.sub.eq,rxn1(T=220° C.)=0.0016 to K.sub.eq,rxn1(T=240° C.)=0.0006.
CO+2H.sub.2.Math.CH.sub.3OH [Reaction 1; methanol synthesis]
2CH.sub.3OH.Math.CH.sub.3OCH.sub.3+H.sub.2O [Reaction 2; methanol dehydration; i.e. DME synthesis]
xCH.sub.3OCH.sub.3+yH.sub.2.Math.C.sub.nH.sub.2n+2+xH.sub.2O [Reaction 3; HOG synthesis]
CO+H.sub.2O.Math.CO.sub.2+ [Reaction 4; water-gas shift reaction]
[0049] When these reactions take place in the same reactor and are catalyzed with a multifunctional catalyst system such as the CZA+A tested here, the equilibrium conversion of CO can be increased due to a synergistic effect between Reactions 1 and 2. Specifically, by including A to catalyze methanol dehydration (Reaction 2), the in situ concentration of MeOH can be kept low, but a greater flux of MeOH through Reaction 1 can be achieved than the thermodynamic equilibrium would allow if Reaction 1 were performed independently. Similar thermodynamic arguments can be made with the addition of Reaction 3, whereby irreversible conversion of DME over Cu/BEA (K.sub.eq,rxn3>10.sup.50) keeps the in situ DME concentration low, thus preventing Reaction 2 from reaching equilibrium.
[0050] The equilibrium constant K.sub.eq is only a function of temperature for these gas-phase reactions and is not a function of pressure or composition. However, through Le Chatelier's principle the equilibrium concentration of MeOH in the reactor can be increased by increasing the absolute reactor pressure. Assuming ideal gas behavior (fugacity coefficients=1), Equation 1 specifies the equilibrium constant for methanol synthesis:
where a.sub.i are the activities, γ.sub.i are stoichiometric coefficients, x.sub.i are the mole fractions of reactants and products and P is the reactor pressure. As K.sub.eq is constant at a given temperature, an increase in reactor pressure P at constant temperature results in an increase in x.sub.MeOH. Reactions 2 and 4 are stoichiometrically equimolar, and therefore the concentrations of reactants and products in those reactions are not directly affected by reactor pressure. The thermodynamics of syngas conversion to hydrocarbons outlined here exemplifies the need to balance reaction rates and/or equilibria of each reaction step to achieve optimal performance. One method of control is the catalyst composition (i.e., the relative CZA, A, and Cu/BEA mass loadings). Additionally, the reaction temperature and pressure are expected to alter the concentration of key intermediate species (MeOH, DME), thus requiring condition-specific compositions of CZA, A, and Cu/BEA for optimal hydrocarbon production.
Reactions of Syngas with and without Co-Fed CO.sub.2:
[0051] Mixed catalyst beds of CZA+A with BEA versus Cu/BEA: The effect of the zeolite catalyst for Reaction 3 was compared between unmodified BEA and Cu-modified BEA (Cu/BEA) in a mixed catalyst bed configuration with combined press-crush-sieve preparation procedure, denoted [CZA+A+BEA] and [CZA+A+Cu/BEA]. The reaction temperature was 220° C., SV.sub.CO was 0.3 or 0.8 h.sup.−1, H.sub.2:CO mol ratio was 1:1 or 2:1, and reaction pressure was 430 or 740 kPa. The net CO+CO.sub.2 conversion at each condition was similar when using BEA or Cu/BEA (see
[0052] Stacked versus Mixed Bed Configuration: Two catalyst bed configurations were tested. A stacked catalyst bed configuration, CZA+A|Cu/BEA, was loaded such that the top bed, or up-stream bed, consisted of physically mixed CZA and A (ca. 3.1, 0.50 g, respectively). The second, or down-stream, bed consisted of Cu/BEA (ca. 0.20 g). In this example, the two catalyst beds were isolated by a thin plug of quartz wool, which may not be necessary. The second configuration was a single, mixed catalyst bed of CZA+A+Cu/BEA (ca. 3.1, 0.50, 0.20 g, respectively). For both catalyst bed configurations, the three materials were sieved to an identical particle size distribution (between 212 μm and 300 μm) to mitigate size- and shape-dependent settling. Therefore, the mixed catalyst bed was assumed to be evenly dispersed throughout the bed.
[0053] The net CO+CO.sub.2 conversion from the mixed catalyst bed experiment exceeded that of the stacked catalyst bed over a series of SV and reaction pressure conditions, exhibiting a relative increase of 40-60% (see
[0054] The hydrocarbon yield from the stacked catalyst bed experiments exceeded that of the mixed catalyst bed. A yield of 2.3% was achieved for the stacked catalyst bed at 740 kPa with a SV of 0.3 h.sup.−1. Note that the higher C.sub.4+ yields shown in
[0055] The oxygenate-free carbon selectivity to hydrocarbon products grouped by carbon number (determined using Equation 5) are provided in
[0056] Catalyst processing procedure: The effect of catalyst processing procedure was investigated by varying whether catalyst components were pressed, crushed, and sieved together (notated in [brackets]) or separately (notated without brackets) in
[0057] The hypothesis was that bringing catalyst components in closer proximity than could otherwise occur by physical mixing of homogenous particles would lead to an increase in CO+CO.sub.2 conversion and hydrocarbon yield, however, the CO+CO.sub.2 conversion for the stacked catalyst bed was not dramatically affected by preparation procedure, and the conversion over the mixed catalyst bed exhibited a relative decrease of 10-25% (see
[0058] In contrast to the decrease in C.sub.4+ hydrocarbon yield observed over [CZA+A+Cu/BEA], comparable C.sub.1 oxygenate yield was observed between the two mixed catalyst bed configurations, CZA+A+Cu/BEA and [CZA+A+Cu/BEA] (see C). These results suggest that the catalytic activity over CZA and A remained intact (i.e., Reactions 1, 2 and 4), while the subsequent activity for conversion of MeOH/DME to hydrocarbons over Cu/BEA (i.e., Reaction 3) was considerably reduced. A reduction in the Cu/BEA activity could be due to: (i) mass transport limitations, such as limited intraparticle diffusion rendering a portion of the Cu/BEA catalyst inactive or reactant-limited, (ii) pore blockage and/or a reduction in surface area of the zeolite catalyst after the processing procedure, or (iii) an intrinsic disadvantage to having the various catalyst components in close proximity, such as additional side-reactions that are promoted under these conditions. If the lower activity is due to mass transport limitations or pore blockage/reduced surface area, one mitigation approach is a catalyst composition comprising the multiple active sites necessary for each reaction (e.g., metallic Cu, ionic Cu-zeolite, ZnO, Al.sub.2O.sub.3, BEA zeolite) assembled with a hierarchical pore structure to enable efficient mass transport.
[0059] Hydrogen to carbon monoxide ratio: In initial experiments, the selectivity to CO.sub.2 from WGSR was between 34% and 36%, which was among the highest of all carbon-containing products. Approaches to minimize the formation of CO.sub.2 would have beneficial effects on the overall carbon efficiency of the process. Increasing the H.sub.2:CO ratio should shift the WGSR reaction (Reaction 4) towards CO, leading to reduced CO.sub.2 selectivity. Calculations for Reactions 1, 2 and 4 across all conditions explored here (T, P, H.sub.2 to CO feed ratio) indicate an equilibrium CO.sub.2 selectivity between 42% and 50%, suggesting that the WGSR did not reach equilibrium in these experiments. The effect of H.sub.2:CO ratio on hydrocarbon yield was investigated at 1:1 and 2:1. The reaction temperature was 220° C., pressure was 430 or 740 kPa, SV was 0.3 or 0.8 g.sub.CO-g.sub.CA+A.sup.−1-h.sup.−1, and two bed configurations were tested: CZA+A|Cu/BEA and CZA+A+Cu/BEA. For the stacked catalyst bed, increasing the H.sub.2:CO ratio from 1:1 to 2:1 had little effect on the C.sub.4+ hydrocarbon yield (see
[0060] Increasing HOG yield from CO-Catalyst Composition: The intermediates between syngas and hydrocarbons, MeOH and DME, were observed as products for both catalyst bed configurations and all conditions described above, suggesting that a catalyst composition with a greater Cu/BEA content may enable full conversion of these oxygenate intermediates and a correspondingly greater hydrocarbon yield. Towards this end, the catalyst composition in the stacked catalyst bed configuration was adjusted from 31:5:2 (CZA:A:Cu/BEA) to 32:5:4 and 32:5:8 (i.e., ca. 2× and 4× the base case). Performance was evaluated at 220° C., 740 kPa, with SV.sub.CO of 0.3 g.sub.CO-g.sub.CA+A.sup.−1-h.sup.−1, and H.sub.2:CO molar ratios of 1:1 and 2:1. The total mass of catalyst (m.sub.CZA+m.sub.A+m.sub.Cu/BEA) in each experiment was held constant (ca. 3.75 g), however, the absolute mass of CZA, A and Cu/BEA varied to achieve the desired catalyst composition.
[0061] For each H.sub.2:CO ratio, a decrease in the net CO+CO.sub.2 conversion was observed with increasing relative Cu/BEA content, decreasing from 31.3 to 28.5 to 26.9% for the 1:1 condition and 38.3 to 35.1 to 33.2% for the 2:1 condition (see
[0062] For each H.sub.2:CO ratio tested, there was a marked increase in C.sub.4+ hydrocarbon yield with greater relative Cu/BEA content, increasing from 2.3 to 4.7 to 10% for the 1:1 condition and 2.0 to 5.7 to 13% for the 2:1 condition (see
[0063] For both H.sub.2:CO ratios, the C.sub.4+ gravimetric activity steadily increased with increasing Cu/BEA content, from 0.065 to 0.073 to 0.085 g.sub.C4+-g.sub.Cu/BEA.sup.−1-h.sup.−1 for the 1:1 condition and 0.057 to 0.089 to 0.11 g.sub.C4+-g.sub.Cu/BEA.sup.−1-h.sup.−1 for the 2:1 condition (see
[0064] The carbon selectivity of hydrocarbon products for the varying catalyst compositions at 730 kPa are illustrated in
[0065] Within the C.sub.7 hydrocarbon products, triptane (2,3,3-trimethylbutane) is a molecule of particular interest due to its high octane rating of 113 and 101 for research and motor octane number, respectively. For both H.sub.2:CO ratios, the carbon yield to triptane markedly increased with relative Cu/BEA content from 0.29 to 0.53 to 0.82% for the 1:1 condition and from 0.24 to 0.51 to 0.90% for the 2:1 condition (see
[0066] Increasing HOG yield from CO: Temperature: Another strategy toward increasing HOG yield is increasing the reaction temperature to increase the reaction rates. Stacked catalyst bed CZA+A|Cu/BEA catalysts having compositions of 32:5:4 and 32:5:8 were evaluated at three temperatures of 220° C., 230° C., and 240° C., 740 kPa, with SV.sub.CO of 0.3 g.sub.CO-g.sub.CA+A.sup.−1-h.sup.−1, and a feed composition of 1:1 mol.sub.H2-mol.sub.CO.sup.−1.
[0067] The net CO+CO.sub.2 conversion increased with increasing temperature, from 28.5 to 34.4 to 37.5% with catalyst composition 32:5:4 and from 26.9 to 33.3 to 36.5% with catalyst composition 32:5:8 (see
[0068] Similar to the selectivity presented above, the carbon number distribution from the reactions at higher temperature also closely resembles that from DME homologation, exhibiting high selectivity to C.sub.4, C.sub.5 and C.sub.7 products (see
[0069] Finally, despite the small shift in selectivity away from C.sub.7 products, the overall increase in activity resulted in increasing triptane yield with increasing temperature (see
[0070] Increasing HOG yield from CO by increasing Pressure: Another strategy toward increasing HOG yield is increasing both the reaction temperature and pressure to increase the reaction rates. Based on the reactivity trends with increasing content of Cu/BEA in the reactor, a stacked catalyst bed CZA+A|Cu/BEA catalyst having a composition of 3:1:3 was evaluated at temperatures of between 250° C. and 320° C. (see Table 1 below), 1800-5250 kPa, with SV.sub.CO of 0.3-1.5 g.sub.CO-g.sub.CA+A.sup.−1-h.sup.−1, and a feed composition of 2:1 mol.sub.H2-mol.sub.CO.sup.−1.
[0071] The CO conversion remained high (>75%) across the range of temperatures and pressures employed (see Table 1). The C.sub.4+ selectivity and per-pass C.sub.4+ yield generally increased with increasing pressure at a given temperature until unconverted DME was observed (compare conditions 3-7 at 290° C.). When temperature and pressure were increased together, comparable C.sub.4+ selectivity, yield, and total hydrocarbon production rate could be maintained across this range of conditions. These results highlight the operational flexibility of the process to operate across a range of conditions from relatively low temperatures and pressures (conditions described above, and Conditions 1 and 2 in Table 1) through relatively high temperatures and pressures (Conditions 3-12), which are important considerations for practicing the process at the commercial scale. A maximum total hydrocarbon productivity of 0.29 g.sub.HC-g.sub.Cu/BEA.sup.−1-h.sup.−1 was achieved using a SV.sub.CO of 1.5 g.sub.CO-g.sub.CA+A.sup.−1-h.sup.−1 (Condition 12).
TABLE-US-00002 TABLE 1 Catalytic performance data for reactions of syngas over a stacked catalyst bed of CZA + A|Cu/BEA catalysts with composition 3:1:3 at varying reaction conditions of temperature and pressure. The SV.sub.CO was 0.9 g.sub.CO-g.sub.CZA+A.sup.−1-h.sup.−1, unless otherwise noted, and the molar feed composition as 2:1 for H.sub.2:CO. CO Total HC Temp. Pressure Conv. C.sub.4+ Selectivity C.sub.4+ Yield productivity Condition (° C.) (kPa) (%) (C %) (C %) (g.sub.HC/g.sub.CuBEA/h) 1 250 1800 82.8 57.3 36.3 0.18 2 270 2150 83.2 59.2 41.3 0.21 3 290 2500 77.2 56.8 37.9 0.21 4 290 2840 79.3 54.8 35.9 0.20 5 290 3190 82.6 56.0 39.0 0.21 6 290 3530 85.7 55.1 36.7 0.20 7.sup.a 290 4220 87.1 29.8 21.0 0.12 8.sup.a 300 5250 88.9 39.6 28.2 0.17 9.sup.a 310 5250 86.1 48.8 36.3 0.22 10 320 5250 82.1 46.8 34.1 0.21 11.sup.a,b 305 5250 87.3 47.2 31.8 0.18 12.sup.a,b 310 5250 84.9 48.7 32.3 0.29 .sup.aDME observed as a product under this condition at greater than approximately 5% .sup.bThe SV.sub.CO was 1.5 g.sub.CO-g.sub.CZA+A.sup.−1-h.sup.−1 for this condition
Reactions of CO.SUB.2.-Rich Syngas to HOG—Improving Carbon Efficiency:
[0072] In addition to approaches to minimize the formation of CO.sub.2, approaches that co-convert CO.sub.2 with CO would increase the overall carbon efficiency. Comparable to using the H.sub.2:CO ratio to affect the WGSR equilibrium (Reaction 4), co-feeding CO.sub.2 in the presence of H.sub.2 should shift the WGSR reaction towards CO and enable the CO.sub.2 to enter into the reaction network via conversion to CO, MeOH, and DME. Stacked catalyst beds of CZA+A|Cu/BEA catalysts having catalyst compositions of 32:5:4, 32:5:8, and 3:1:3 were evaluated at 220° C., 740 kPa, with SV.sub.CO of 0.3 g.sub.CO-g.sub.CA+A.sup.−1-h.sup.−1, and a molar feed composition of 2:1 for H.sub.2:CO without co-fed CO.sub.2 and 2:1:0.8 for H.sub.2:CO:CO.sub.2.
[0073] The catalytic data for reactions with co-fed CO.sub.2 and comparisons to analogous experiments without co-fed CO.sub.2 are presented in Table 2. Compared to catalytic performance without co-fed CO.sub.2, a marked decrease in activity was observed with co-fed CO.sub.2 at the relatively high ratio explored here (i.e., CO:CO.sub.2 of 1:0.8). This may be due to the combination of a 20% relative decrease in CO partial pressure in experiments with co-fed CO.sub.2 (e.g., CO partial pressure decreased from 225 kPa to 180 kPa with co-fed CO.sub.2) and an associated doubling of the gas-hourly space velocity from 0.4 to 0.8 cm.sup.3-g.sub.total catalyst.sup.−1-min.sup.−1 as a result of co-feeding CO.sub.2. The net CO+CO.sub.2 conversion decreased to approximately one-third of the value for the syngas-only feed, accompanied by corresponding decreases in the C.sub.4+ hydrocarbon yield and triptane carbon yield. The C.sub.4+ hydrocarbon yield increased with increasing Cu/BEA content in the catalyst bed, with the 3:1:3 catalyst composition exhibiting per-pass C.sub.4+ hydrocarbon yields of 44.9% without co-fed CO.sub.2 and 23.8% with co-fed CO.sub.2. In addition, co-fed CO.sub.2 was effective in reducing the overall C-selectivity to CO.sub.2. With a catalyst composition of 32:5:4, a decrease from 31.5 to 21.4% was observed. With a catalyst composition of 32:5:8, a decrease from 31.9 to 20.1% was observed. With a catalyst composition of 3:1:3, a decrease from 38.8 to 28.4% was observed. With decreasing CO.sub.2 selectivity, the overall selectivity for C.sub.4+ hydrocarbon products (i.e., C.sub.4+ hydrocarbons among all products including oxygenates) also increased substantially, reaching 63.2% for the 3:1:3 catalyst composition with co-fed CO.sub.2. The hydrocarbon product distribution from reactions with co-fed CO.sub.2 were comparable to those without CO.sub.2, exhibiting low selectivity to C.sub.1-3 products (<5% total) and high selectivity to C.sub.4, C.sub.5, and C.sub.7 products (see
[0074] Mass spectra analysis with .sup.13CO.sub.2 co-feed: During the CO.sub.2 co-feed experiment with the catalyst composition of 3:1:3, the CO.sub.2 source was switched to isotopically-labelled .sup.13CO.sub.2 and product analysis using mass spectroscopy was employed to investigate the propagation of .sup.13C from .sup.13CO.sub.2.
TABLE-US-00003 TABLE 2 Catalytic performance data for reactions of syngas with co-fed CO.sub.2 over a stacked catalyst bed of CZA + A|Cu/BEA catalysts with catalyst compositions of 32:5:4, 32:5:8, and 3:1:3. Reaction conditions were 220° C., 740 kPa, with SV.sub.CO of 0.3 g.sub.CO-g.sub.CZA+A.sup.−1-h.sup.−1, and a molar feed composition of 2:1 for H.sub.2:CO without CO.sub.2 and 2:1:0.8 for H.sub.2:CO:CO.sub.2. The SV based on CO + CO.sub.2 was 0.35 g.sub.CO-g.sub.CZA+A.sup.−1-h.sup.−1. Catalyst composition Metric 32:5:4 32:5:8 3:1:3 CO.sub.2 co-feed No Yes No Yes No Yes CO + CO.sub.2 conversion (%) 35.1 10.5 33.2 12.5 77.3 27.0 C.sub.4+ HC yield (%) 5.7 3.4 14.4 9.6 44.9 23.8 Triptane yield (%) 0.51 0.22 1.0 0.44 2.0 0.46 CO.sub.2 C-selectivity (%) 31.5 21.4 31.9 20.1 38.8 28.4 C.sub.4+ C-selectivity (%) 12.1 15.5 28.5 39.8 53.9 63.2
Reactions of CO.SUB.2 .to Hydrocarbons:
[0075] Stacked versus Mixed Bed Configuration: Similar to the syngas conversion reactions, two different catalyst bed configurations were investigated: (i) a mixed catalyst bed configuration, CZA+A+Cu/BEA having a catalyst composition for CZA:A:Cu/BEA of 1:1:0.6, and (ii) a stacked catalyst bed configuration, CZA+A|Cu/BEA, having a catalyst composition for CZA:A:Cu/BEA of 1:1:0.5, respectively. Reactant flowrates were adjusted to achieve the same WHSV of 0.75 g.sub.CO2-g.sub.CA+A.sup.−1-h.sup.−1 to maintain comparable CO.sub.2-to-DME activity, and to study the effect of catalyst bed configuration on the subsequent MeOH and DME conversion to hydrocarbons.
[0076] Table 3 presents conversion and product C-selectivity for the reaction at 220° C. over the two bed configurations at varying pressure (at 0.5 MPa or 1.0 MPa). The CO.sub.2 conversion values were similar for the two bed configurations at each studied pressure, as expected when the same WHSV with respect to CZA+A was maintained. For the mixed catalyst bed configuration, CO.sub.2 conversion increased slightly with reaction pressure from 13.2% at 0.5 MPa to 14.6% at 1.0 MPa. The product selectivity was more strongly affected by reaction pressure, where an increased selectivity to MeOH (4.1 to 5.9 to 7.0%) and DME (13.7 to 22.9 to 29.1%) was observed with a decrease in CO selectivity (82.2 to 71.2 to 63.9%). This selectivity trend is consistent with the thermodynamic assessment for methanol formation (Reaction 1) at higher pressures, as discussed above. However, hydrocarbon formation from the subsequent conversion of MeOH and DME over Cu/BEA was negligible. For the stacked catalyst bed configuration, CZA+A|Cu/BEA, a similar trend for the CO.sub.2 conversion and product selectivity to MeOH, DME and CO with increasing reaction pressure was observed. The most important difference between the two bed configurations was the significant increase in the DME-to-hydrocarbon activity over Cu/BEA in the stacked catalyst bed configuration. The selectivity to hydrocarbons increased from 9.3 to 14.8% as reaction pressure increased from 0.5 to 1 MPa. The hydrocarbon products were predominantly isobutane and isopentane.
TABLE-US-00004 TABLE 3 Effect of catalyst bed configurations and reaction pressures to CO.sub.2 conversion and product C-selectivity in CO.sub.2 hydrogenation. Reaction conditions: 220° C., H.sub.2:CO.sub.2 = 3:1, WHSV = 1.5 (g CO.sub.2/g CZA/h); Mixed catalyst bed: physical mixture of CZA, g-Al.sub.2O.sub.3, and Cu/BEA catalysts with catalyst composition of CZA:g-Al.sub.2O.sub.3:Cu/BEA = 1:1:0.6; A stacked catalyst bed configuration includes top bed: physical mixture of CZA and g-Al.sub.2O.sub.3; and bottom bed: Cu/BEA with catalyst composition of CZA:g-Al.sub.2O.sub.3:Cu/BEA = 1:1:0.5. Pressure (MPa) 0.5 0.8 1 Bed configuration Mixed Stacked Mixed Stacked Mixed Stacked Conversion 13.2% 12.3% 14.0% 13.5% 14.6% 14.2% Carbon Monoxide (CO) 82.2% 88.0% 71.2% 78.7% 63.9% 70.2% Dimethyl Ether 13.7% 1.3% 22.9% 4.1% 29.1% 10.6% (CH.sub.3OCH.sub.3) Methanol (CH.sub.3OH) 4.1% 1.4% 5.9% 2.6% 7.0% 4.4% Totals HCs <0.1% 9.3% <0.1% 14.6% <0.1% 14.8% C.sub.4+ HCs <0.1% 8.7% <0.1% 13.8% <0.1% 13.9% C.sub.5+ HCs <0.1% 3.6% <0.1% 6.9% <0.1% 7.7%
[0077] The stark contrast in hydrocarbon production from the two catalyst bed configurations is attributed to the kinetics of MeOH and DME production along the catalyst bed, and the subsequent effect on the rate of hydrocarbon pool chemistry in the Cu/BEA zeolite. In the mixed catalyst bed configuration, as the reaction mixture (i.e., CO.sub.2+H.sub.2) travels through the catalyst bed, the MeOH/DME product concentration increases gradually. DME concentration is expected to be low at the top of the catalyst bed, leading to slow initiation of the hydrocarbon pool chemistry over Cu/BEA, and thus, a low rate of hydrocarbon formation from Reaction 3. DME concentration is greater at the downstream section of the catalyst bed, however, only a small portion of the Cu/BEA catalyst remains in this section for conversion of DME to hydrocarbons. These phenomena combine to result in low overall CO.sub.2 to hydrocarbon activity. In the stacked catalyst bed configuration, MeOH and DME concentration increased from zero in the first CZA+A bed, providing a greater concentration of oxygenates for reaction over the full portion of the downstream Cu/BEA catalyst. As a result, the bed-averaged hydrocarbon formation rate increased.
[0078] Increasing hydrocarbon yield from CO.sub.2-Catalyst composition: As presented above, MeOH and DME were not fully consumed by the Cu/BEA catalyst in the initial experiments, potentially limiting the hydrocarbon yield. One approach to increase the conversion of the oxygenate intermediates is to increase the relative amount of the Cu/BEA catalyst.
[0079] HOG yield in response to temperature and pressure: The effect of reaction temperature and pressure on yield and selectivity of desired C.sub.4+ products were investigated towards increasing C.sub.4+ production. Temperature and pressure strongly affect the thermodynamic equilibrium of MeOH synthesis, which ultimately affects hydrocarbon formation in the subsequent reactions. In general, increasing the reaction pressure increased C.sub.4+ yield, attributed to the expected increase in MeOH and DME production with increasing pressure (see
[0080] Varying reaction temperature and pressure also affected the hydrocarbon product distribution over the stacked catalyst bed with a catalyst composition of CZA:A:Cu/BEA=1:1:1. Across all conditions of temperature and pressure investigated here, the major hydrocarbon products were C.sub.4 and C.sub.5 species, consisting predominantly of isobutane and isopentane, respectively (see
[0081] At a constant pressure of 0.5 MPa, increasing the reaction temperature from 200° C. to 220° C. resulted in greater selectivity to C.sub.1-4 hydrocarbons, and an associated decrease in C.sub.5+ product selectivity (see
[0082] The total hydrocarbon product included predominantly paraffins, with an olefin-to-paraffin ratio (O/P) less than 0.06 mol.sub.C-olefin/mol.sub.C-paraffin for the variety of temperature and pressure conditions explored here. This is attributed to olefin hydrogenation under the high concentration of H.sub.2 and in the presence of metallic Cu catalysts. The major products, C.sub.4 and C.sub.5 hydrocarbons, were essentially olefin-free. Ethylene and propylene were observed, attributed to cracking of long-chain hydrocarbons. Olefins in the C.sub.6+ fraction were also observed, attributed to their participation in methylation and chain growth that ultimately results in heavier products.
Methods:
[0083] Materials: The baseline performance for the direct conversion of syngas to HOG was investigated utilizing mixed catalyst beds and stacked catalyst bed configurations containing three catalysts: (1) a commercially available Cu/ZnO/Al.sub.2O.sub.3 methanol synthesis catalyst (Megamax 800, Clariant, abbreviated “CZA”), (2) a γ-Al.sub.2O.sub.3 methanol dehydration catalyst (NorPro® SA6173, St. Gobain-Norpro, abbreviated “A”), and (3) a hydrocarbon synthesis catalyst. The hydrocarbon synthesis catalyst was either a beta zeolite (BEA; Tosoh) or a Cu-modified BEA zeolite (Cu/BEA). The CZA and A were used as received. BEA was obtained in ammonium form and had a SiO.sub.2:Al.sub.2O.sub.3 ratio of 27. To achieve the proton form, BEA was calcined under flowing air at 550° C. Cu/BEA was synthesized from BEA via incipient wetness impregnation; an aqueous solution of Cu(NO.sub.3).sub.2.2.5H.sub.2O was added dropwise to NH.sub.4-BEA until the incipient wetness point was reached, then the slurry was mixed and dried at 50° C. to yield Cu/BEA having ca. 4.5 wt % Cu. The Cu/BEA was calcined under flowing air at 550° C. prior to subsequent use.
[0084] Catalyst bed configurations: All catalysts were pressed (22 kN), crushed in a porcelain mortar and pestle, and sieved to 212-300 μm (50-70 mesh). In several cases, catalyst components were pressed, crushed and sieved together, and these are noted in brackets to indicate which species were processed together: [CZA+A] indicates Cu/ZnO/Al.sub.2O.sub.3 and γ-Al.sub.2O.sub.3 were pressed, crushed and sieved together. In other cases, catalyst components were pressed, crushed and sieved independently, and then physically mixed together and are notated without brackets: CZA+A indicates Cu/ZnO/Al.sub.2O.sub.3 and γ-Al.sub.2O.sub.3 were pressed, crushed and sieved to 212-300 μm independently, and then physically mixed together prior to loading in the reactor. The catalysts were loaded into a 7.9 mm ID stainless-steel tubular reactor, operating in top-down configuration, and positioned within the isothermal zone of an electric tube furnace using quartz chips and quartz wool. A four-point thermocouple positioned within the catalyst bed was used to monitor reaction temperatures. The reaction temperatures during an experiment were maintained within ±0.5° C. of the set point.
[0085] Catalyst mixtures were loaded into the reactor as either stacked catalyst beds or as mixed catalyst beds. For the stacked catalyst bed configuration, the top bed was separated from the bottom bed by a thin plug of quartz wool. For mixed catalyst beds, a single catalyst bed mixture was loaded. The vertical line symbol, |, is used to notate top and bottom beds, when a stacked catalyst bed configuration was used, where the first catalyst component(s) listed corresponds to top bed: CZA+A|Cu/BEA indicates a physical mixture of independently pressed, crushed and sieved CZA and A, loaded above a bed of Cu/BEA separated by a plug of quartz wool. The notation [CZA+A]|Cu/BEA would indicate a similar stacked catalyst bed configuration, with the CZA and A components pressed, crushed and sieved together. No attempt to directly measure homogeneity of mixed catalyst beds was made, although size- and shape-dependent settling differences were sought to be minimized by sieving all catalyst components to a consistent particle size range between 212 μm and 300 μm.
[0086] Reactions of syngas with or without co-fed CO.sub.2: A constant total catalyst mass (CZA+A+Cu/BEA) of 3.75 g was used, regardless of the catalyst composition, which is defined as the relative mass loading of each component. Catalyst bed volumes ranged between 4.3 cm.sup.3 and 4.6 cm.sup.3. Catalyst mixtures were diluted with 3.6 g of low surface-area, inert silicon carbide to minimize channeling, axial dispersion, and temperature gradients in the bed. Catalyst compositions of CZA:A:Cu/BEA were 30:5:2, 32:5:4, 32:5:8, or 3:1:3. Catalyst compositions were selected in an attempt to balance DME formation rates observed in preliminary CZA+A experiments (data not shown), with the DME space velocity typically used in DME-to-hydrocarbons reactions (between 0.35 g.sub.DME-g.sub.Cu/BEAh.sup.−1 and 1.5 g.sub.DME-g.sub.Cu/BEA-h.sup.−1). Prior to reaction testing, the catalyst was reduced at 230° C. under 25 sccm H.sub.2 flow for 2 hours, initially heated from room temperature at a rate of 0.5° C.-min.sup.−1. Syngas conversion experiments were performed at reactor temperatures between about 220° C. and about 320° C. Reaction pressure ranged from 430-5500 kPa absolute, the H.sub.2:CO molar ratio was either 1 or 2 (mol-mol.sup.−1) and the space velocity (SV) of CO was varied between 0.2 g.sub.CO-g.sub.CA+A.sup.−1-h.sup.−1 and 1.0 g.sub.CO-g.sub.CA+A.sup.−1-h.sup.−1, where g.sub.CZA+A is the combined mass of the CZA and A catalysts. When CO.sub.2 was co-fed, the CO:CO.sub.2 ratio was 1.1 or 2.8 (mol.sub.CO-mol.sub.CO2.sup.−1). All volumetric flow rates are given at NTP (20° C., 101.3 kPa), and all pressures are absolute. The weight-hourly space velocity of CO (SV.sub.CO) relative to the total mass loading of CZA+A was calculated with Equation 2:
where {dot over (n)}.sub.CO, in is the molar flow rate of CO into the reactor (mol-h.sup.−1), MW.sub.CO is the molecular weight of CO (g-mol.sup.−1) and m.sub.CZA and m.sub.A are the mass of CZA and A, respectively, loaded into the reactor.
[0087] The syngas mixture was prepared using H.sub.2, CO, and Ar to generate a 49:49:2 molar ratio (equimolar H.sub.2:CO ratio). To achieve greater H.sub.2:CO ratios, 95% H.sub.2/5% Ar was added using an independent mass flow controller. Mass flow controllers (Brooks Instrument) were used to control gas flow rates to the reactor system and were calibrated for the specific gas streams prior to use. Reactor pressure was maintained using a backpressure regulator and was monitored at the reactor inlet and outlet using pressure transducers.
[0088] Reactions of CO.sub.2 without syngas: Catalyst compositions of CZA:A:Cu/BEA were between 1:1:0.5 and 1:1:1. Silicon carbide diluent was not used. A greater relative A-catalyst loading was employed to increase MeOH dehydration to DME (reaction 2), and therefore facilitate the conversion of CO.sub.2 toward MeOH formation. A greater relative Cu/BEA loading was employed to increase DME and MeOH conversion to hydrocarbons. Prior to reaction testing, the catalyst was reduced at 230° C. under 50 sccm 95% H.sub.2/5% Ar flow for 2 hours, initially heated from room temperature at a rate of 0.5° C.-min.sup.−1. CO.sub.2 conversion experiments were performed at reactor temperatures between about 200° C. and about 220° C. Reaction pressure was between about 0.5 MPa and about 1.0 MPa absolute. The feed gas composition of CO.sub.2:H.sub.2:Ar was 24:72:4, corresponding to an H.sub.2:CO.sub.2 molar ratio of three. The space velocity (SV) of CO.sub.2 was set to about 0.75 g.sub.CO2-g.sub.CA+A.sup.−1-h.sup.−1, where g.sub.CZA+A is the combined mass of the CZA and A catalysts. All volumetric flow rates are given at NTP (20° C., 101.3 kPa), and all pressures are absolute.
[0089] Equations for performance evaluation: Reactor inlet and outlet gases were sampled through heated (170-200° C.) lines using two Agilent 7890 GCs. One GC was equipped with a flame ionization detector (FID) to quantify light hydrocarbons (C.sub.1-5) and two thermal conductivity detectors with argon and helium carrier gases to quantify inert and permanent gases. The second GC was fitted with two FIDs, one to quantify heavy hydrocarbons (C.sub.5+) and the second to quantify oxygenates (MeOH, DME, methyl acetate). GC responses for reactants and products (hydrocarbons C.sub.1-C.sub.4 and all other products except H.sub.2O) were calibrated using traceable gravimetric gas standards. For hydrocarbons C.sub.5 or higher, GC responses for the respective detector were linearly extrapolated from the FID response of C.sub.1-C.sub.4 compounds.
[0090] Catalyst performance was evaluated from GC measurements using Ar as an internal standard. The net CO+CO.sub.2 conversion, X.sub.CO+CO2, was calculated with Equation 3:
where {dot over (n)}.sub.C,CO,in, {dot over (n)}.sub.C,CO,out, and {dot over (n)}.sub.C,CO2,out, out represent the molar flow rate of carbon in CO (mol.sub.C-s.sup.−1), in the inlet and effluent reactor streams, and the molar flow rate of carbon in effluent CO.sub.2, respectively. This net CO+CO.sub.2 conversion metric is used to quantify the amount of carbon converted to MeOH, DME, and hydrocarbons through the sequential reaction network, and incorporates the contribution from the WGSR.
[0091] The product carbon yield for various products, and product groupings (e.g., C.sub.4+. Hydrocarbons), was calculated with Equation 4:
where {dot over (n)}.sub.C,CO,in is used as previously defined, and {dot over (n)}.sub.C,i,out is the molar flow rate of carbon in product(s) i. For example, yield to triptane (2,3,3-trimethylbutane) would use
[0092] The product carbon selectivity, S.sub.i (in carbon %, noted as C-Selectivity), was calculated via Equation 6:
where {dot over (n)}.sub.C,i,out represents the effluent molar flow rate of carbon in product i (mol.sub.C-s.sup.−1), and may be summed over a group of desired products as exemplified for Y.sub.i. The denominator term Σ{dot over (n)}.sub.C,i was summed over all products. The gravimetric activity of product(s), P.sub.i (g.sub.i-g.sub.cat.sup.−1-h.sup.−1), was calculated with Equation 7:
where {dot over (n)}.sub.i is the molar flow rate of product i (mol-h.sup.−1), MW.sub.i is the molecular weight of product i (g-mol.sup.−1) and m.sub.cat is the mass of catalyst, either Cu/BEA or cumulative CZA+A mass. For grouped gravimetric activity metrics (e.g., C.sub.4+ hydrocarbons), individual product P.sub.i values were summed.
[0093] The carbon balance was calculated, on the basis of amount of reactant carbon converted and amount of carbon observed in products, offering greater sensitivity to unquantified carbon than a balance performed on a total carbon basis due to incomplete reactant conversion. This carbon-converted balance was calculated with Equation 8:
where {dot over (n)}.sub.C,CO,in, {dot over (n)}.sub.C,CO,out are used as previously defined, and Σ{dot over (n)}.sub.C,i,out is the effluent molar flow rate of carbon in product i, summed over all products. A conventional carbon balance was calculated with Equation 9:
where Σ{dot over (n)}.sub.C,i,in, and Σ{dot over (n)}.sub.C,i,out are the summation, over all compounds i, of molar flow rate of carbon (mol.sub.C-s.sup.−1) in inlet and effluent streams, respectively.
Method Examples
[0094] Example 1. A method comprising: converting a gas stream comprising hydrogen (H.sub.2) and carbon monoxide (CO) to a second mixture comprising a hydrocarbon having between 1 and 15 carbon atoms, wherein: the converting is performed using a first catalyst configured to convert H.sub.2 and CO to methanol, a second catalyst configured to convert methanol to dimethyl ether (DME), and a third catalyst configured to convert DME to the hydrocarbon.
[0095] Example 2. The method of Example 1, wherein the H.sub.2 and the CO are initially at a ratio between 1:1 and 4:1.
[0096] Example 3. The method of Example 2, wherein the ratio is between 1:1 and 3:1.
[0097] Example 4. The method of Example 1, wherein the first catalyst comprises copper and a zinc oxide.
[0098] Example 5. The method of Example 4, wherein the first catalyst further comprises at least one of silica, alumina, zirconia, or ceria.
[0099] Example 6. The method of Example 1, wherein the second catalyst comprises at least one of an alumina or silica.
[0100] Example 7. The method of Example 1, wherein the third catalyst comprises at least one of copper or a zeolite.
[0101] Example 8. The method of Example 7, wherein the zeolite comprises a beta zeolite having a silica to alumina ratio between about 20:1 and about 300:1.
[0102] Example 9. The method of Example 8, wherein the silica to alumina ratio is between about 25:1 and about 30:1.
[0103] Example 10. The method of Example 8, wherein the copper in the third catalyst is present at a concentration between about 1 wt % and about 20 wt %, relative to the total weight of the third catalyst.
[0104] Example 11. The method of Example 10, wherein copper in the third catalyst is present at a concentration between about 4 wt % and 10 wt %.
[0105] Example 12. The method of Example 1, wherein the first catalyst and the second catalyst are present at a ratio between about 1:1 and about 8:1.
[0106] Example 13. The method of Example 1, wherein the ratio of the first catalyst and the second catalyst is between about 1:1 and about 32:5.
[0107] Example 14. The method of Example 12, wherein the second catalyst and the third catalyst are present at a ratio between about 0.1:1 and about 5:2.
[0108] Example 15. The method of Example 1, wherein the first catalyst is positioned in a first zone, the second catalyst is positioned in a second zone, and the third catalyst is positioned in a third zone; and the first zone, the second zone and the third zone are all contained in a single reactor.
[0109] Example 16. The method of Example 15, wherein the single reactor is a packed bed.
[0110] Example 17. The method of Example 16, wherein: the first catalyst is positioned in the packed bed in a first layer, the second catalyst is positioned in the packed bed in a second layer, the third catalyst is positioned in the packed bed in a third layer, and the second layer is positioned in series between the first layer and the second layer.
[0111] Example 18. The method of Example 16, wherein: the first catalyst and the second catalyst are positioned in the packed bed as a well-mixed mixture in a first layer, the third catalyst is positioned in the packed bed in a second layer, and the first layer and the second layer are positioned in series.
[0112] Example 19. The method of Example 16, wherein the first catalyst, the second catalyst, and the third catalyst are positioned in the packed bed as a well-mixed mixture in a single layer.
[0113] Example 20. The method of Example 16, wherein: the first catalyst is positioned in the packed bed in a first layer, the second catalyst and the third catalyst are positioned in the packed bed as a well-mixed mixture in a second layer, and the first layer and the second layer are positioned in series.
[0114] Example 21. The method of Example 1, wherein: the first catalyst and the second catalyst are positioned in a first reactor; the third catalyst is positioned in a second reactor, and the first reactor and the second reactor are positioned in series.
[0115] Example 22. The method of Example 21, wherein the first catalyst and second catalyst are positioned in a packed bed as a well-mixed mixture.
[0116] Example 23. The method of Example 21, wherein the first reactor is maintained at a temperature between about 180° C. and about 320° C.
[0117] Example 24. The method of Example 23, wherein the temperature is between about 200 and 250° C.
[0118] Example 25. The method of Example 21, wherein the second reactor is maintained at a temperature between about 180° C. and about 320° C.
[0119] Example 26. The method of Example 25, wherein the temperature of the second reactor is maintained between about 200° C. and 320° C.
[0120] Example 27. The method of Example 21, wherein the first reactor is a packed bed.
[0121] Example 28. The method of Example 21, wherein the second reactor is a packed bed.
[0122] Example 29. The method of Example 21, wherein the first reactor is maintained at a pressure between about 300 kPa and about 10.0 MPa.
[0123] Example 30. The method of Example 29, wherein the pressure of the first reactor is maintained between about 400 kPa and 5.5 MPa.
[0124] Example 31. The method of Example 1, wherein the CO is provided at a flow rate resulting in a space velocity between about 0.2 g/g hr and about 1.0 g/g hr.
[0125] Example 32. The method of Example 1, wherein the gas stream further comprises carbon dioxide.
[0126] Example 33. The method of Example 32, wherein the gas stream has a concentration of carbon dioxide greater than or equal to 10 wt %.
Composition Examples
[0127] Example 1. A composition comprising: a first portion comprising copper and a zinc oxide; a second portion comprising at least one of an alumina or silica; and a third portion comprising a zeolite.
[0128] Example 2. The composition of Example 1, wherein the first portion further comprises at least one of silica, alumina, zirconia, or ceria.
[0129] Example 3. The composition of Example 1, wherein the third portion further comprises copper.
[0130] Example 4. The composition of Example 1, wherein the zeolite comprises a beta zeolite having a silica to alumina ratio between about 20:1 and about 300:1.
[0131] Example 5. The composition of Example 4, wherein the silica to alumina ratio is between of about 25:1 and 30:1.
[0132] Example 6. The composition of Example 3, wherein the copper of the third portion is present at a concentration between about 1 wt % and about 20 wt %, relative to the total weight of the third portion.
[0133] Example 7. The composition of Example 6, wherein the copper of the third portion is present at a concentration between about 4 wt % and 10 wt %.
[0134] Example 8. The composition of Example 1, wherein the first portion and the second portion are present at a ratio between about 1:1 and about 8:1.
[0135] Example 9. The composition of Example 1, wherein the ratio of the first portion and the second portion is between about 0.1:1 and 32:5.
[0136] Example 10. The composition of Example 8, wherein the second portion and the third portion are present at a ratio between about 0.1:1 and about 5:2.
[0137] Example 11. The composition of Example 1, wherein the first portion, the second portion, and the third portion are thoroughly mixed into a single mixture.
[0138] Example 12. The composition of Example 1, wherein: the first portion is in a first layer, the second layer is in a second layer, the third layer is in a third layer, and the second layer is positioned between the first layer and the second layer.
System Example
[0139] Example 1. A system comprising: at least one of a first reactor or a second reactor, wherein: at least one of the first reactor or the second reactor contains a catalyst or composition as described herein.
[0140] The foregoing discussion and examples have been presented for purposes of illustration and description. The foregoing is not intended to limit the aspects, embodiments, or configurations to the form or forms disclosed herein. In the foregoing Detailed Description for example, various features of the aspects, embodiments, or configurations are grouped together in one or more embodiments, configurations, or aspects for the purpose of streamlining the disclosure. The features of the aspects, embodiments, or configurations, may be combined in alternate aspects, embodiments, or configurations other than those discussed above. This method of disclosure is not to be interpreted as reflecting an intention that the aspects, embodiments, or configurations require more features than are expressly recited in each claim. Rather, as the following claims reflect, inventive aspects lie in less than all features of a single foregoing disclosed embodiment, configuration, or aspect. While certain aspects of conventional technology have been discussed to facilitate disclosure of some embodiments of the present invention, the Applicants in no way disclaim these technical aspects, and it is contemplated that the claimed invention may encompass one or more of the conventional technical aspects discussed herein. Thus, the following claims are hereby incorporated into this Detailed Description, with each claim standing on its own as a separate aspect, embodiment, or configuration.