METHOD FOR FORMING A SLEEVE FOR INSULATING A JOINT OF DOWNHOLE TUBING

Abstract

A method for forming a sleeve for wrapping around and insulating a joint of a downhole tubing string is provided. The method includes the steps of providing a mold, applying insulation around the mold, winding an interfacing material around the insulation; and applying a polymer onto the interfacing material to bind to the interfacing material to form the sleeve.

Claims

1. A method for forming a sleeve for wrapping around and insulating a joint of a downhole tubing string, the method comprising: providing a mold; applying insulation around the mold; winding an interfacing material around the insulation; and applying a polymer onto the interfacing material to bind to the interfacing material to form the sleeve.

2. The method of claim 1, further comprising: cutting the sleeve longitudinally to separate the sleeve from the mold after the sleeve is formed.

3. The method of claim 1, wherein the interfacing material comprises 2-way tape.

4. The method of claim 1, further comprising: winding reinforcement material over the interfacing material.

5. The method of claim 4, wherein the polymer is applied over the reinforcement material to encapsulate the reinforcement material.

6. The method of claim 4, wherein the reinforcement material comprises a wire, rope, cord or strip, or a combination thereof.

7. The method of claim 6, wherein the wire, rope, cord or strip, or the combination thereof comprises one or more of metallic wire, carbon fibre, Kevlar, fiberglass, or thermoform monofilament.

8. The method of claim 1, wherein the insulation comprises aerogel.

9. The method of claim 1, further comprising the step of applying a base layer around the mold before applying the insulation around the mold, wherein the step of applying the polymer onto the interfacing material to bind to the interfacing material to form the sleeve comprises applying the polymer to at least an end of the sleeve to bind to the base layer at the at least the end of the sleeve.

10. The method of claim 9, wherein the base layer is a sheet elastomer which is compatible with the polymer.

11. The method of claim 4, wherein the reinforcement material is spirally wound around the interfacing layer to provide a rippled pattern that increases the available surface area for bonding to the polymer.

12. The method of claim 11, wherein the reinforcement material spirally wound around the interfacing layer has a spacing between flights.

13. The method of claim 11, wherein the reinforcement material spirally wound around the interfacing layer compresses the interfacing layer.

14. The method of claim 1, wherein the polymer is a phenolic resin polymer, a thermoset plastic polymer, a thermoplastic polymer, a thermoform plastic polymer, an epoxy polymer, a polyaspartic polymer, a silicone polymer, or an elastomeric polymer.

15. The method of claim 1, wherein the mold is pipe-shaped.

16. A sleeve for wrapping around and insulating a joint of a downhole tubing string, the sleeve produced by the method of claim 1.

17. A method for insulating a tubing string, the method comprising: connecting a plurality of insulated tubulars to form an insulated tubing string; wrapping the sleeve of claim 16 around one or more joints of the tubing string; and securing the sleeve around the joints of the tubing string.

18. The method of claim 17, further comprising the step of securing the sleeve around the joints with stainless steel strapping.

19. The method of claim 17, further comprising attaching collars above or below the sleeve to hold the sleeve in place.

20. The method of claim 17, further comprising applying sealant to edges of the sleeve.

Description

BRIEF DESCRIPTION OF THE FIGURES

[0017] Embodiments will now be described with reference to the figures, in which like reference characters denote like elements, by way of example, and in which:

[0018] FIG. 1 is a schematic section view through an insulated downhole tubular.

[0019] FIG. 2 is a side view of insulated tubulars before being joined for insertion

[0020] FIG. 3 is a closeup schematic side cutaway view of a joint of a tubing string showing an insulated sleeve about the joint string.

[0021] FIG. 1 is a schematic section downhole use.

[0022] FIG. 4 is a flow diagram showing a method of insulating a downhole tubing

[0023] FIG. 5 is a flow diagram showing a method of forming an insulated tubular for

[0024] FIG. 6 is a flow diagram showing a method for forming a sleeve for wrapping around and insulating a joint of a downhole tubing string.

DETAILED DESCRIPTION

[0025] Immaterial modifications may be made to the embodiments described here without departing from what is covered by the claims. In the claims, the word “comprising” is used in its inclusive sense and does not exclude other elements being present. The indefinite articles “a” and “an” before a claim feature do not exclude more than one of the feature being present. Each one of the individual features described here may be used in one or more embodiments and is not, by virtue only of being described here, to be construed as essential to all embodiments as defined by the claims.

[0026] FIG. 1 schematically shows a tubular for downhole use, the tubular comprising, in the innermost part of the tubular, a pipe 10, which may be of conventional construction. An insulative cladding 20 surrounds the pipe, formed for example as follows. In this example, an insulation layer 12 surrounds the pipe 10. An interfacing layer 14 surrounds the insulation layer. The interfacing layer, as may other layers described, may comprise plural layers. The interfacing layer contacts the insulation layer and a protective layer 16. The protective layer 16 may comprise a polymer sprayed onto the interfacing layer.

[0027] There may be reinforcing material 18 within the protective layer, shown schematically as a single line though typically it would wind around the pipe.

[0028] Insulation layer may be any insulation, but is preferably an aerogel. An aerogel is a synthetic porous ultralight material derived from a gel, in which the liquid component for the gel has been replaced with a gas. The result is a solid with extremely low density and low thermal conductivity. Aerogels can be made from a variety of chemical compounds. The aerogel should be selected to withstand downhole temperatures such as temperatures up to ISOC or as much as 280 C.

[0029] FIG. 5 is a flow diagram showing a method of forming an insulated tubular for downhole use. In step 80, a pipe is provided. In step 82, insulation is applied around the pipe. Insulation may be applied to the product in “blanket” form. The insulation may be in the form of pre-cut rectangular sheets. These sheets may then be cut them down to the size needed to surround the pipe. They may then be formed, for example by hand, around the tubular. The sheets may be loosely fastened at several points using adhesive tape or film, depending on tubular diameter.

[0030] In a tubular of approximately 9.6 m length there are usually 4 separate pieces of insulation blanket butt jointed and wrapped.

[0031] The insulation may also arrive on large rolls which can then be cut down to appropriate width prior to the manufacturing process.

[0032] The tape is applied tangentially to the tubular holding the insulation in place for transport to the next step, winding, as well as ensuring the butt joints in the insulation stay together.

[0033] An adhesive may be used to secure the insulation layer to the pipe, but this is not preferred as it negatively impacts the compaction process and can result in an unacceptably irregular product.

[0034] The initial insulation layer may be applied to the entire tubular except for the ends. For example, approximately 3 ft from the box end (threaded coupling) and 1.5 ft from the pin (threaded end) may be left bare, in order to allowing the elevators (lifting device on the rig) and the tongs (large capacity self-locking wrenches used to assemble downhole tubulars and apply torque) to grip the bare steel. This area that is not coated during the initial process may then be covered with the pre made sleeves, described below, if the thermal demands of the customer require full coverage, after the threaded connection is made on site.

[0035] The interfacing layer may be a compression layer, applied to the insulation to compress it against the pipe. In step 84 of FIG. 5, a compression material is wound around the insulation. The interfacing layer may include, for example an adhesive backed (2-way) fabric tape, which may be spiral wound around the insulation layer, partially compacting it as well as isolating it from the other layers. A plastic wrap may be used to provide a more thorough barrier, but this is not preferred as this may result in bubbles in the outer polymer layer. The fabric tape may have micro porosity so that the polymer has something to adhere to. Another layer that was considered was a fabric wrap around the fabric tape, but this is not considered necessary as the outer layer can adequately bond to the fabric tape and no additional separation from the insulation is required.

[0036] In optional step 86 of FIG. 5, a reinforcement material is wound over the compression material. Examples of possible reinforcement materials include a wire, rope, cord or strip, for example steel wire or rope, or metal bands, or synthetic wires, ropes or bands, such as made of an aramid fibre such as Kevlar™. A wire, rope, cord or strip wound around the insulation may have a spacing determined by the pipe diameter. For example, on a pipe 2⅜ inches in diameter, the spacing between flights of the wound material may be 1 h inch.

[0037] The reinforcement material may include a high tensile strength filament and may also be spirally wound around the product further compressing the insulation. This filament may be a metallic wire, or other unidirectional continuous filament. Examples include carbon fibre, kevlar, fibreglass, or thermoform monofilaments.

[0038] Presently the reinforcement is wound as a single uniform layer, this makes it easier to avoid pinching due to unbalanced pressures. The pipe may be chucked up in a lathe and an employee may traverse the length with the filament spool resting on a cart, using a braking mechanism to control the tension and spacing. Other approaches include a tunnel wrapper approach or a braiding machine, either of which the insulation covered tubular will pass through as the spool or spools rotate around. The braiding machine may be used to provide the balanced pressure using multiple layers. The fabric tape or other compression material may be wound using the same winding station (e.g. lathe setup, tunnel wrapper or braiding machine).

[0039] The filament winding produces a rippled pattern that increases the available surface area for the outer coating to bond to. If the filament chosen for the application is not of a monofilament nature then the high strand count also increases the available surface area for the outer coating to bond to.

[0040] In step 88 of FIG. 5, a polymer is applied onto the compression material. This may include applying the polymer onto another layer around the compression material. This polymer may form at least part of a protective layer of the tubular. The polymer may be, for example a phenolic resin, thermoset plastic, thermoplastic, thermoform plastics, epoxies, polyaspartics, and silicones. In an example, the polymer is an elastomer and is a thermoset plastic or thermoplastic. The polymer may be selected to be resistant to temperatures up to 150 C, 200 C or 280 C for example. The outer polymer layer may be for example 50-60 mil thick. If the pipe has an outer diameter of 2⅜ inches, the insulated tubular may have a thickness in the order of 3⅜ inches.

[0041] The polymer may be spray applied. In the case that application of the polymer produces gases, to allow for gasses to escape during application of the polymer the spray pattern may be applied from either right to left or left to right. If using an exothermic thermoset polymer, normally this heat is absorbed by the substrate and isn't an issue, though by applying this to a highly insulated substrate the heat causes any trapped air to expand. If the coating is not applied in a linear pattern this expanding hot air cannot escape and bubbles up through the coating. With traditional coatings there is a long enough wet film time to allow the coating to re-level itself, but if the polymer has a rapid setup time, the coating cures while the hot gases escape resulting in tunnelling down to the compression layer. By moving in one direction the expanding gases can continue to travel through the insulation matrix to escape as opposed to travelling up through the coating. When the end of the tubular is reached a small amount of coating is applied to verify that the gases are still not rushing out, and once they have stopped the end is sealed with the polymer. This left to right or right to left pattern may be applied at the winding station.

[0042] The coating should be applied so as to fully wet out the compression layer as well as the reinforcing material as this then produces a composite matrix that gives the outer coating its strength. This composite that is produced reinforces the properties of the outer layer increasing its abrasion resistance as well as its tensile strength, ensuring the integrity of the insulation envelope during transport and down hole installation. The coating may harden with the reinforcement material already under tension.

[0043] Before insulation is applied, the pipe may be blasted to an 8-10 mil profile so that the polymer can adhere to the bare tubing. When the polymer layer is applied, it may also be applied to the ends of the insulated section so that it binds to the bare tubing and seals in the insulation and otherlayers.

[0044] The above description indicates how tubulars can be insulated. To obtain full insulated coverage, additional insulation of the tubing may be completed after makeup is completed on the rig floor. Pre-sprayed sleeves are made up before deployment at a predetermined length to cover the make-up distance. The sleeves can then be attached to the uninsulated connection and secured. The sleeve can then be sprayed with the polymer to result in a fully sealed joint that will not lose heat due to an uninsulated connection.

[0045] A sleeve may be produced using the same process as for the regular insulation as described above, albeit on a mold, which may be a pipe or another pipe-shaped mold, and then cut longitudinally (parallel to the mold) and removed as a “C” shaped tubular sleeve.

[0046] The sleeve can then be used to insulate joints and exposed ends of the tubulars. The Sleeve is produced to a given length dictated by customer demands. Being preformed to the diameter the tubular greatly increases the ease of installation.

[0047] FIG. 6 is a flow diagram showing a method for forming a sleeve for wrapping around and insulating a joint of a downhole tubing string. In step 90, a mold is provided. In optional step 92 of FIG. 6, a base layer is applied around the mold. The base layer is adjacent to the mold, but when the polymer is sprayed onto the outside of the sleeve in step I 00, it may also be sprayed onto the ends of the sleeve so that it seals to the base layer. The base layer may extend some distance beyond the edge of the sleeve to give more room to stick to and so that the polymer doesn't stick to the pipe shaped mold. The optional base layer may be selected to be compatible with the polymer as the outer coating has to seal to it on the edges to fully encapsulate the insulation and improve the strength of the sleeve. Once we cut the sleeve to remove it from the pipe shaped mold, without the base layer if care is not taken the insulation can separate from the polymer and reinforcement matrix. While this careful handling is fine in some applications in others a more robust package needs to be created.

[0048] Sleeves have been fabricated with and without a base layer on the underside. Because of the hydrophobic nature of the insulation fluid intrusion is usually not much of an issue. The main concern with using a base layer is to ensure cleanliness during transport and installation as well as to ensure no metallic contamination can occur which could result in a corrosion cell underneath the sleeve.

[0049] Using a base layer and sealing it to the polymer creates an air and water tight envelope. In some applications fluid does not travel through the space between the production string and the casing tubings, and as a result the insulation is not at risk of fluid entrapment in this area. In other production situations, where the insulated tubular is secured in place with cement, we need to fully isolate the insulation and steel substrates from the cement to inhibit corrosion. There are also further applications where fluid is pumped down this space between the casing and production tubing and again we would want to fully insulate and protect the steel and insulation from this liquid.

[0050] The base layer may be formed, for example of a sheet elastomer that is compatible with the polymer top coat. For our current polymer, we use flexible pvc sheeting which provides the required moisture resistance as well as being compatible with the system to provide an air and water tight bond.

[0051] In step 94 of FIG. 6, insulation is applied around the mold. If there is a base layer applying the insulation around the mold comprises applying the insulation around the base layer. In steps 96-100, and interfacing material is wound around the insulation, a reinforcement material is optionally wound over the interfacing material, and a polymer is applied onto the interfacing material, including the reinforcement material. In step 102, the sleeve is removed from the mold. This may comprise cutting the sleeve longitudinally. FIG. 3 schematically shows, not to scale, a sleeve 42 around a joint 44.

[0052] In this embodiment, a base layer 46 is shown as a single line bounding insulation layer 12 next to pipe 10. Pipes 10 are connected at joint 44 to form a tubing string 11. The base layer 46 would typically contact pipe 10 but is shown separated from pipe 10 for clarity. The base layer 46 has a portion 48 that extends out from insulation layer 12 and is contacted by protective layer 16. An interfacing layer 14 and reinforcing material 18 as shown in FIG. 1 would typically also be present but are omitted in this figure. A sealant 50 is shown filling a gap 52 between the sleeve 42 and regular insulative cladding 20. Layers of the regular insulative cladding 20 are not shown in this figure but are shown in FIG. 1. The sealant 50 may be formed of the same material forming the protective layer to form a unitary outer coating. Metal bands 54 are also shown around the sleeve 42 to secure it to the pipes 10.

[0053] While the sleeve 42 is shown covering the joint 44 and adjacent portions of the pipes only, plural sleeves could also be used to cover an entire tubing string.

[0054] During installation the tubulars are connected as normal on the rig floor.

[0055] Prior to insertion down hole but after the connection is made the sleeve is placed around the connection and then secured with stainless steel strapping 54 (e.g. stainless steel zip ties). An alternative method can incorporate collars that can be welded or set screwed to the bare pipe above or below the makeup area to hold the blanket in place. If additional isolation is required, the edges and seams can be coated on the rig floor by spraying an additional top coat. The top coat may be the same material that is used for the normal outer coat, which provides a monolithic envelope and ensures the entire tubular string is insulated. A different sealant could also be used.

[0056] FIG. 4 is a flow diagram showing a method of insulating a downhole tubing string. In step 60, tubulars are connected to form a tubing string. The tubulars can be insulated tubulars such as tubulars with an insulative cladding as shown for example in FIG. 1. In step 62 an insulative sleeve, such as for example a sleeve 42 as shown in FIG. 3, is wrapped around at least a joint of the tubing string. In step 64, the insulative sleeve is secured around the at least a joint. This securing may be, for example, with metal bands as shown in FIG. 3. In optional step 66, sealant is applied to edges of the sleeve, which may include a longitudinal edge where the sleeve was cut off a mold, and may include end edges where the sleeve terminates and may contact another sleeve or a regular insulative cladding. The sealant may be an additional amount of the same material used for an outer coating of the sleeve. In step 68, the tubing string is inserted downhole. Inserting the tubing string downhole may include, for example, progressing a tubing string that is already partially downhole further downhole. In step 70, an additional tubular or tubulars are obtained so that steps 60-68 can be repeated for another length of tubing string. The step of connecting tubulars to form a tubing string may comprise connecting a tubular or tubulars to an existing tubing string.

[0057] The thickness of the insulation may be determined after a thermal conductivity simulation has calculated the starting and exiting temperature.

[0058] The distance that the insulation is from either the pin end and/or the upset end may be selected based on measurements of rig components, such as slips on the rig floor, makeup tongs being used (open faced) and slip type elevators used for pulling and holding the weight of the string after makeup. FIG. 2 shows an example of pipe uninsulated area dimensions in schematic form and is not to scale. In FIG. 2, insulative cladding 20 is separated by thread gap 22 from threads 24 at a pin end 26 of the pipe 10. In an example, the thread gap 22 is 12 inches. At the box end 28, upset gap 30 between upset 32 and insulative cladding 20 comprises space 34 for slips 36 and an additional uncovered gap 38 between the top of slips 36 and upset 32. In an example, the upset gap 30 is 44 inches with 19 inches of space 34 allowed for slips 36 and the additional uncovered gap 38 being 25 inches. If slip-type elevators are used, additional space, for example 14 additional inches, may be required. Rig floor 40 is also shown in this figure with slips 36 between rig floor 40 and pipe 10.