ZSM-35 MOLECULAR SIEVE AND PRODUCTION METHOD THEREFOR, ISOMERIZATION CATALYST AND PRODUCTION METHOD THEREFOR, AND ISOMERIZATION METHOD

Abstract

The present disclosure provides a ZSM-35 molecular sieve and a preparation method therefor, an isomerization catalyst and a preparation method therefor, and an isomerization method. The preparation method for a ZSM-35 molecular sieve comprises: mixing a silicon source, an aluminum source, an alkali, a template agent and water, then adding a polyacrylamide thereto, and performing crystallization on same twice to obtain a ZSM-35 molecular sieve. The present disclosure further provides an isomerization catalyst prepared from the ZSM-35 molecular sieve and a preparation method therefor, and an isomerization method.

Claims

1. A method for producing a ZSM-35 molecular sieve, comprising: mixing a silicon source, an aluminum source, an alkali, and a template agent with water to form a mixed solution, adding polyacrylamide to the mixed solution to form a feedstock solution, and crystallizing the feedstock solution at 140-160° C. for 12-24 h and then at 120-140° C. for 48-72 h to obtain the ZSM-35 molecular sieve, wherein the template agent comprises pyrrolidine.

2. The method according to claim 1, wherein the silicon source, the aluminum source, the alkali, pyrrolidine (Py) and water are mixed in molar ratios of SiO.sub.2/Al.sub.2O.sub.3=20-110, H.sub.2O/SiO.sub.2=10-80, NaOH/SiO.sub.2=0.1-1.0, and Py/SiO.sub.2=0.1-1.0; the polyacrylamide is added in an amount of 0.1-1% by weight of the mixed solution; the silicon source comprises one or more of silica sol, solid silica gel and white carbon black; the aluminum source comprises one or more of aluminum sulfate, aluminum oxide and sodium meta-aluminate; and the alkali comprises sodium hydroxide.

3. The method according to claim 2, wherein the silicon source, the aluminum source, the alkali, pyrrolidine (Py) and water are mixed in molar ratios of SiO.sub.2/Al.sub.2O.sub.3=30-90, H.sub.2O/SiO.sub.2=20-50, NaOH/SiO.sub.2=0.2-0.5, and Py/SiO.sub.2=0.2-0.5.

4. The method according to claim 2, wherein the polyacrylamide has a weight-average molecular weight of 3 million-10 million.

5. A ZSM-35 molecular sieve obtained by the method for producing a ZSM-35 molecular sieve according to claim 1.

6. The ZSM-35 molecular sieve according to claim 5, further containing a template agent.

7. The ZSM-35 molecular sieve according to claim 5, which is lamellar crystal, and has a grain thickness of less than or equal to 50 nm, a grain length and/or the grain width of less than or equal to 500 nm, and a crystallinity of greater than or equal to 120%.

8. The ZSM-35 molecular sieve according to claim 7, having a grain thickness of less than 50 nm, a grain length and/or width of less than or equal to 200 nm, and a crystallinity of greater than or equal to 140%.

9. An isomerization catalyst, wherein a method for producing the isomerization catalyst comprises: subjecting a template agent-containing ZSM-35 molecular sieve to ammonium salt exchange, then mixing it with water, a binder, an acid and an extrusion aid, and then extruding, drying, and baking the mixture to obtain the isomerization catalyst, wherein the template agent-containing ZSM-35 molecular sieve is not subjected to a process of removing the template agent prior to the extrusion, and is not subjected to a baking process after the ammonium salt exchange.

10. The isomerization catalyst according to claim 9, wherein the acid comprises an organic acid and/or an inorganic acid; the binder comprises one or more of alumina sol, alumina, and pseudo-boehmite; the extrusion aid comprises Sesbania powder and/or methyl cellulose; and the template agent-containing ZSM-35 molecular sieve comprises the ZSM-35 molecular sieve according to claim 5.

11. The isomerization catalyst according to claim 10, wherein the organic acid comprises acetic acid and/or citric acid; and the binder comprises pseudo-boehmite.

12. The isomerization catalyst according to claim 9, wherein the baking is carried out at a temperature of 530-550° C. after the extrusion.

13. The isomerization catalyst according to claim 12, wherein the baking is carried out for 4-8 h.

14. The isomerization catalyst according to claim 9, wherein the template agent-containing ZSM-35 molecular sieve in the isomerization catalyst accounts for 80% or more of the total mass of the isomerization catalyst.

15. The isomerization catalyst according to claim 14, wherein the template agent-containing ZSM-35 molecular sieve in the isomerization catalyst accounts for 90% or more of the total mass of the isomerization catalyst.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0032] FIG. 1 shows the results for characterizing the morphological structure of the ZSM-35 molecular sieve produced in Comparative Example 1.

[0033] FIG. 2 shows the results for characterizing the morphological structure of the ZSM-35 molecular sieve produced in Example 1.

[0034] FIG. 3 shows the process flow diagram of the skeletal isomerization of light olefins in Examples 10 and 11.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

[0035] In order to have a clearer understanding of the technical features, objectives and beneficial effects of the present disclosure, the technical solutions of the present disclosure are now described in detail in the following, which, however, should not be understood as limiting the implementable scope of the present disclosure.

[0036] The weight-average molecular weight of polyacrylamide used in the following Examples and Comparative Examples is 3 million.

[0037] The crystallinity of the molecular sieve was measured using a smartlab type X-ray diffractometer of Rigaku Co. Ltd., with CuKα line as the radiation source, a tube voltage of 40 KV, a tube current of 50 mA, a scan rate of 5°/min, and a scan range of 2θ=5-85°. The crystallinity was obtained using the measurements of intensities of characteristic peaks (9.4°, 22.4°, 22.7°, 23.3°, 23.7°, 24.5°, 25.3°) by a common calculation method. The SEM characterization was carried out using a 200F type field emission scanning electron microscope from Quanta chrome Co. Ltd., with a test voltage of 200 KV. The grain size of the molecular sieve was measured by the 200F type field emission scanning electron microscope, and the results were averaged for the different grains of molecular sieve measured.

[0038] There are two important indicators for evaluating the performance of the skeletal isomerization catalyst of olefins: (1) the conversion of n-pentene (or n-butene), and the selectivity for isopentene (or isobutene), which are defined as follows:

[00001]$\mathrm{conversion}\left(n-\mathrm{pentene}\right)\frac{n-\mathrm{pentene}\mathrm{content}\mathrm{in}\mathrm{feedstock}-n-\mathrm{pentene}\mathrm{content}\mathrm{in}\mathrm{product}}{n-\mathrm{pentene}\mathrm{content}\mathrm{in}\mathrm{feedstock}}\times 100\%$$\mathrm{Selectivity}\left(\mathrm{isopentene}\right)\frac{\mathrm{isopentene}\mathrm{content}\mathrm{in}\mathrm{product}-\mathrm{isopentene}\mathrm{content}\mathrm{in}\mathrm{feedstock}}{n-\mathrm{pentene}\mathrm{content}\mathrm{in}\mathrm{feedstock}-n-\mathrm{pentene}\mathrm{content}\mathrm{in}\mathrm{product}}\times 100\%$$\mathrm{conversion}\left(n-\mathrm{butene}\right)\frac{n-\mathrm{butene}\mathrm{content}\mathrm{in}\mathrm{feedstock}-n-\mathrm{butene}\mathrm{content}\mathrm{in}\mathrm{product}}{n-\mathrm{butene}\mathrm{content}\mathrm{in}\mathrm{feedstock}}\times 100\%$$\mathrm{Selectivity}\left(\mathrm{isobutene}\right)\frac{\mathrm{isobutene}\mathrm{content}\mathrm{in}\mathrm{product}-\mathrm{isobutene}\mathrm{content}\mathrm{in}\mathrm{feedstock}}{n-\mathrm{butene}\mathrm{content}\mathrm{in}\mathrm{feedstock}-n-\mathrm{butene}\mathrm{content}\mathrm{in}\mathrm{product}}\times 100\%$

Comparative Example 1

[0039] This Comparative Example provides a method for producing a ZSM-35 molecular sieve, which comprises the following processes.

[0040] Silica sol (25.0 wt % of SiO.sub.2), aluminum sulfate (99.0%), sodium hydroxide and pyrrolidine (99.0%) were added to deionized water in the molar ratio of SiO.sub.2/Al.sub.2O.sub.3=30, H.sub.2O/SiO.sub.2=50, NaOH/SiO.sub.2=0.5, Py/SiO.sub.2=0.5, stirred well, and crystallized at 150° C. for 60 h. After crystallization, it was filtered and washed with deionized water, and then dried at 120° C. for 4 h to obtain the ZSM-35 molecular sieve.

[0041] The ZSM-35 molecular sieve was analyzed by scanning electron microscopy (SEM) and X-ray diffraction (XRD), and the SEM and XRD results are shown in FIGS. 1 (a) and (b). The ZSM-35 molecular sieve was measured and calculated to have a grain thickness of 471 nm, a grain length or grain width of 1568 nm, and a crystallinity of 105%.

Comparative Example 2

[0042] This Comparative Example provides a method for producing a ZSM-35 molecular sieve, which comprises the following processes.

[0043] Silica sol (25.0 wt % of SiO.sub.2), aluminum sulfate (99.0%), sodium hydroxide and pyrrolidine (99.0%) were added to deionized water in the molar ratio of SiO.sub.2/Al.sub.2O.sub.3=50, H.sub.2O/SiO.sub.2=40, NaOH/SiO.sub.2=0.3, Py/SiO.sub.2=0.3, stirred well, and crystallized at 150° C. for 72 h. After crystallization, it was filtered and washed with deionized water, and then dried at 120° C. for 4 h to obtain raw powders of the ZSM-35 molecular sieve.

[0044] The ZSM-35 molecular sieve was analyzed by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The ZSM-35 molecular sieve was measured and calculated to have a grain thickness of 421 nm, a grain length or grain width of 1652 nm, and a crystallinity of 100%.

Comparative Example 3

[0045] This Comparative Example provides a method for producing a ZSM-35 molecular sieve, which comprises the following processes.

[0046] Silica sol (25.0 wt % of SiO.sub.2), aluminum sulfate (99.0%), sodium hydroxide and pyrrolidine (99.0%) were added to deionized water in the molar ratio of SiO.sub.2/Al.sub.2O.sub.3=70, H.sub.2O/SiO.sub.2=30, NaOH/SiO.sub.2=0.2, Py/SiO.sub.2=0.2, stirred well, and crystallized at 160° C. for 72 h. After crystallization, it was filtered and washed with deionized water, and then dried at 120° C. for 4 h to obtain the ZSM-35 molecular sieve.

[0047] The ZSM-35 molecular sieve was analyzed by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The ZSM-35 molecular sieve was measured and calculated to have a grain thickness of 485 nm, a grain length or grain width of 1698 nm, and a crystallinity of 95%.

Comparative Example 4

[0048] This Comparative Example provides a method for producing an isomerization catalyst, which comprises the following processes.

[0049] 1000 g of the ZSM-35 molecular sieve (which retains the template agent) produced in the Comparative Example 1 was exchanged 3 times with 5% ammonium nitrate solution at a liquid-solid ratio of 5:1, and then the exchanged ZSM-35 molecular sieve was washed 3 times with deionized water at a liquid-solid ratio of 5:1. After filtration, it was dried at 120° C. for 4 h. All the dried ZSM-35 molecular sieve was mixed uniformly with 100 g of pseudo-boehmite (specific surface area: 288 m.sup.2/g, dry basis: 68%) and 30 g of Sesbania powder. 150 g of citric acid was added to 850 g of deionized water and stirred well. After that, the formed citric acid solution was added to the mixture, kneaded with a kneading machine, and then extruded with an extruder. After drying in an oven at 120° C. for 4 h, it was transferred to a muffle furnace where it was heated up to 550° C. for 4 h and kept at the constant temperature for 4 h. At the end of baking, a skeletal isomerization catalyst (A) for light olefins was produced.

Comparative Example 5

[0050] This Comparative Example provides a method for producing an isomerization catalyst, which comprises the following processes.

[0051] 1000 g of the ZSM-35 molecular sieve produced in the Comparative Example 2 was exchanged 3 times with 5% ammonium nitrate solution according to a liquid-solid ratio of 5:1, and then the exchanged ZSM-35 molecular sieve was washed 3 times with deionized water at a liquid-solid ratio of 2:1. After filtration, it was dried at 120-140° C. for 4 h. All the dried ZSM-35 molecular sieve was mixed uniformly with 100 g of pseudo-boehmite (specific surface area: 288 m.sup.2/g, dry basis: 68%) and 50 g of methyl cellulose to obtain a mixture. 50 g of nitric acid was added to 900 g of deionized water and stirred well. After that, the formed nitric acid solution was added to the mixture, kneaded with a kneading machine, and then extruded with an extruder. After drying in an oven at 140° C. for 4 h, it was transferred to a muffle furnace where it was heated up to 550° C. for 4 h and kept at the constant temperature for 4 h. At the end of baking, a skeletal isomerization catalyst (B) for light olefins was produced.

Comparative Example 6

[0052] This Comparative Example provides a method for producing an isomerization catalyst, which comprises the following processes.

[0053] 1000 g of the ZSM-35 molecular sieve produced in the Comparative Example 3 was exchanged 3 times with 5% ammonium nitrate solution according to a liquid-solid ratio of 5:1, and then the exchanged ZSM-35 molecular sieve was washed 3 times with deionized water at a liquid-solid ratio of 5:1. After filtration, it was dried at 120° C. for 4 h. All the dried ZSM-35 molecular sieve was mixed uniformly with 90 g of alumina (specific surface area: 212 m.sup.2/g, dry basis: 75%) and 30 g of Sesbania powder. 100 g of acetic acid was added to 850 g of deionized water and stirred well. After that, the formed acetic acid solution was added to the mixture, kneaded with a kneading machine, and then extruded with an extruder. After drying in an oven at 120° C. for 4 h, it was transferred to a muffle furnace where it was heated up to 550° C. for 4 h and kept at the constant temperature for 4 h. At the end of baking, a skeletal isomerization catalyst (C) for light olefins was produced.

Example 1

[0054] This Example provides a method for producing a ZSM-35 molecular sieve, which comprises the following processes.

[0055] Silica sol (25.0 wt % of SiO.sub.2), aluminum sulfate (99.0%), sodium hydroxide and pyrrolidine (99.0%) were added to deionized water in the molar ratio of SiO.sub.2/Al.sub.2O.sub.3=30, H.sub.2O/SiO.sub.2=50, NaOH/SiO.sub.2=0.5, Py/SiO.sub.2=0.5, and stirred well to form a mixed solution. To the mixed solution, 0.20% by weight of polyacrylamide was added, crystallized at 150° C. for 12 h, and then crystallized at 150° C. for 60 h. After crystallization, it was filtered and washed with deionized water, and then dried at 120° C. for 4 h to obtain the ZSM-35 molecular sieve.

[0056] This ZSM-35 molecular sieve was analyzed by scanning electron microscopy (SEM) and X-ray diffraction (XRD), and the SEM and XRD results are shown in FIGS. 2 (a) and (b). The ZSM-35 molecular sieve was measured and calculated to have a grain thickness of 47 nm, a grain length or grain width of 177 nm, and a crystallinity of 142%.

Example 2

[0057] This Example provides a method for producing a ZSM-35 molecular sieve, which comprises the following processes.

[0058] Silica sol (25.0 wt % of SiO.sub.2), aluminum sulfate (99.0%), sodium hydroxide and pyrrolidine (99.0%) were added to deionized water in the molar ratio of SiO.sub.2/Al.sub.2O.sub.3=50, H.sub.2O/SiO.sub.2=40, NaOH/SiO.sub.2=0.3, Py/SiO.sub.2=0.3, and stirred well to form a mixed solution. To the mixed solution, 0.5% by weight of polyacrylamide was added, crystallized at 150° C. for 18 h, and then crystallized at 130° C. for 72 h. After crystallization, it was filtered and washed with deionized water, and then dried at 120° C. for 4 h to obtain the ZSM-35 molecular sieve.

[0059] This ZSM-35 molecular sieve was analyzed by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The ZSM-35 molecular sieve was measured and calculated to have a grain thickness of 42 nm, a grain length or grain width of 186 nm, and a crystallinity of 145%.

Example 3

[0060] This Example provides a method for producing a ZSM-35 molecular sieve, which comprises the following processes.

[0061] Silica sol (25.0 wt % of SiO.sub.2), aluminum sulfate (99.0%), sodium hydroxide and pyrrolidine (99.0%) were added to deionized water in the molar ratio of SiO.sub.2/Al.sub.2O.sub.3=70, H.sub.2O/SiO.sub.2=30, NaOH/SiO.sub.2=0.2, Py/SiO.sub.2=0.2, and stirred well to form a mixed solution. To the mixed solution, 0.20% by weight of polyacrylamide was added, crystallized at 160° C. for 24 h, and then crystallized at 140° C. for 60 h. After crystallization, it was filtered and washed with deionized water, and then dried at 120° C. for 4 h to obtain the ZSM-35 molecular sieve.

[0062] This ZSM-35 molecular sieve was analyzed by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The ZSM-35 molecular sieve was measured and calculated to have a grain thickness of 47 nm, a grain length or grain width of 312 nm, and a crystallinity of 124%.

Example 4

[0063] This Example provides a method for producing an isomerization catalyst, which comprises the following processes.

[0064] 1000 g of the template agent-containing ZSM-35 molecular sieve with small grains and high crystallinity produced in the Example 1 was baked at 530° C. for 8 h to remove the template agent, and then exchanged 3 times with 5% ammonium nitrate solution at a liquid-solid ratio of 5:1. The exchanged ZSM-35 molecular sieve was washed 3 times with deionized water at a liquid-solid ratio of 5:1. After filtration, it was dried at 120° C. for 4 h and baked at 500° C. for 4 h. All the dried ZSM-35 molecular sieve was mixed uniformly with 100 g of pseudo-boehmite (specific surface area: 288 m.sup.2/g, dry basis: 68%) and 30 g of Sesbania powder. 150 g of citric acid was added to 850 g of deionized water and stirred well. After that, it was added to the mixture, kneaded with a kneading machine, and then extruded with an extruder. After drying in an oven at 120° C. for 4 h, it was transferred to a muffle furnace where it was heated up to 500° C. for 4 h and kept at the constant temperature for 4 h. At the end of baking, a skeletal isomerization catalyst (D) for light olefins was produced.

Example 5

[0065] This Example provides a method for producing an isomerization catalyst, which comprises the following processes.

[0066] 1000 g of the template agent-containing ZSM-35 molecular sieve with small grains and high crystallinity in the Example 2 was baked at 530° C. for 8 h to remove the template agent, and then exchanged 3 times with 5% ammonium nitrate solution at a liquid-solid ratio of 5:1. The exchanged ZSM-35 molecular sieve was washed 3 times with deionized water at a liquid-solid ratio of 2:1. After filtration, it was dried at 120-140° C. for 4 h and baked at 500° C. for 4 h. All the dried ZSM-35 molecular sieve was mixed uniformly with 100 g of pseudo-boehmite (specific surface area: 288 m.sup.2/g, dry basis: 68%) and 50 g of methyl cellulose to obtain a mixture. 50 g of nitric acid was added to 900 g of deionized water and stirred well. After that, it was added to the mixture, kneaded with a kneading machine, and then extruded with an extruder. After drying in an oven at 140° C. for 4 h, it was transferred to a muffle furnace where it was heated up to 500° C. for 4 h and kept at the constant temperature for 4 h. At the end of baking, a skeletal isomerization catalyst (E) for light olefins was produced.

Example 6

[0067] This Example provides a method for producing an isomerization catalyst, which comprises the following processes.

[0068] 1000 g of the template agent-containing ZSM-35 molecular sieve with small grains and high crystallinity in the Example 3 was baked at 530° C. for 8 h to remove the template agent, and then exchanged 3 times with 5% ammonium nitrate solution at a liquid-solid ratio of 5:1. The exchanged ZSM-35 molecular sieve was washed 3 times with deionized water at a liquid-solid ratio of 5:1. After filtration, it was dried at 120° C. for 4 h and baked at 500° C. for 4 h. All the dried ZSM-35 molecular sieve was mixed uniformly with 90 g of alumina (specific surface area: 212 m.sup.2/g, dry basis: 75%) and 30 g of Sesbania powder. 100 g of acetic acid was added to 850 g of deionized water and stirred well. After that, it was added to the mixture, kneaded with a kneading machine, and then extruded with an extruder. After drying in an oven at 120° C. for 4 h, it was transferred to a muffle furnace where it was heated up to 500° C. for 4 h and kept at the constant temperature for 4 h. At the end of baking, a skeletal isomerization catalyst (F) for light olefins was produced.

Example 7

[0069] This Example provides a method for producing an isomerization catalyst, which comprises the following processes.

[0070] 1000 g of the template agent-containing ZSM-35 molecular sieve with small grains and high crystallinity in the Example 1 was exchanged 3 times with 5% ammonium nitrate solution at a liquid-solid ratio of 5:1, and the exchanged ZSM-35 molecular sieve was then washed 3 times with deionized water at a liquid-solid ratio of 5:1. After filtration, it was dried at 120° C. for 4 h. All the dried ZSM-35 molecular sieve was mixed uniformly with 100 g of pseudo-boehmite (specific surface area: 288 m.sup.2/g, dry basis: 68%) and 30 g of Sesbania powder. 150 g of citric acid was added to 850 g of deionized water and stirred well. After that, it was added to the mixture, kneaded with a kneading machine, and then extruded with an extruder. After drying in an oven at 120° C. for 4 h, it was transferred to a muffle furnace where it was heated up to 550° C. for 4 h and kept at the constant temperature for 4 h. At the end of baking, a skeletal isomerization catalyst (G) for light olefins was produced.

Example 8

[0071] This Example provides a method for producing an isomerization catalyst, which comprises the following processes.

[0072] 1000 g of the template agent-containing ZSM-35 molecular sieve with small grains and high crystallinity in the Example 2 was exchanged 3 times with 10% ammonium nitrate solution at a liquid-solid ratio of 5:1, and the exchanged ZSM-35 molecular sieve was then washed 3 times with deionized water at a liquid-solid ratio of 2:1. After filtration, it was dried at 120-140° C. for 4 h. All the dried ZSM-35 molecular sieve was mixed uniformly with 100 g of pseudo-boehmite (specific surface area: 288 m.sup.2/g, dry basis: 68%) and 50 g of methyl cellulose to obtain a mixture. 50 g of nitric acid was added to 900 g of deionized water and stirred well. After that, it was added to the mixture, kneaded with a kneading machine, and then extruded with an extruder. After drying in an oven at 140° C. for 4 h, it was transferred to a muffle furnace where it was heated up to 550° C. for 4 h and kept at the constant temperature for 4 h. At the end of baking, a skeletal isomerization catalyst (H) for light olefins was produced.

Example 9

[0073] This Example provides a method for producing an isomerization catalyst, which comprises the following processes.

[0074] 1000 g of the template agent-containing ZSM-35 molecular sieve with small grains and high crystallinity in the Example 3 was exchanged 3 times with 5% ammonium nitrate solution at a liquid-solid ratio of 5:1, and the exchanged ZSM-35 molecular sieve was then washed 3 times with deionized water at a liquid-solid ratio of 5:1. After filtration, it was dried at 120° C. for 4 h. All the dried ZSM-35 molecular sieve was mixed uniformly with 90 g of alumina (specific surface area: 212 m.sup.2/g, dry basis: 75%) and 30 g of Sesbania powder. 100 g of acetic acid was added to 850 g of deionized water and stirred well. After that, it was added to the mixture, kneaded with a kneading machine, and then extruded with an extruder. After drying in an oven at 120° C. for 4 h, it was transferred to a muffle furnace where it was heated up to 550° C. for 4 h and kept at the constant temperature for 4 h. At the end of baking, a skeletal isomerization catalyst (I) for light olefins was produced.

Example 10

[0075] In this example, isomerization experiments were carried out using the isomerization catalysts produced in Comparative Examples 4-6 and Examples 4-9, respectively, with refinery etherified C5 light hydrocarbons as the experimental feedstock. The specific composition is shown in Table 1.

TABLE-US-00001 TABLE 1 components content, m % 1-pentene 4.27 2-methyl-1-butene 0.82 trans-2-pentene + cis-2-pentene 18.72 2-methyl-2-butene 8.14 isopentane 42.19 n-pentane 6.44 others 5.12

[0076] The experiment was carried out in a 20 ml atmospheric pressure reactor with an isothermal fixed bed reactor to pass the product through the process once. The experimental process flow is shown in FIG. 3.

[0077] The experimental process was as follows: [0078] 1. The isomerization catalyst was crushed into 20-30 mesh particles with a loading volume of 20 ml and filled in the constant temperature section of the reactor. The upper and lower part of the catalyst was loaded with 20-30 mesh quartz sand. After the completion of filling, the reactor was connected to the system. Nitrogen gas was introduced for gas tightness test, and the gas-tight pressure was gradually increased to 1.0 MPa. Once the pressure drop was not more than 0.1 MPa after standing for 2 hours, the device was determined to be gas-tight and qualified. [0079] 2. Etherified C5 light hydrocarbons were subjected to a skeletal isomerization experiment for light olefins under the conditions of a pressure of 0.1 MPa, an LHSV of 3.0 h.sup.−1 and a temperature of 260° C., and then the hydrocarbon composition of the product was analyzed.

[0080] The above experiments were carried out with isomerization catalysts from Comparative Examples 4-6 and Examples 4-9, respectively, and the obtained results are summarized in Table 2.

TABLE-US-00002 TABLE 2 Comp. Comp. Comp. Example Example Example Example Example Example Items Ex. 4 Ex. 5 Ex. 6 4 5 6 7 8 9 Catalyst A B C D E F G H I No. Convention 45.1 43.2 42.5 63.5 61.2 59.6 66.2 65.8 65.2 of n-pentene, % Selectivity 95.2 94.5 95.6 96.1 96.3 96.5 97.1 96.8 97.3 for isopentene, %

Example 11

[0081] In this example, isomerization experiments were carried out using the isomerization catalysts produced in Comparative Examples 4-6 and Examples 4-9, respectively, with refinery etherified C4/C5 light hydrocarbons as the experimental feedstock. The specific composition is shown in Table 3.

TABLE-US-00003 TABLE 3 components content, m % 1-butene 21.75 trans-2-butene 22.33 cis-2-butene 18.06 isobutene 1.16 isopentane 28.15 n-pentane 6.48 others 2.12

[0082] The experimental process flow is shown in FIG. 3.

[0083] The experimental process was as follows: [0084] 1. The isomerization catalyst was crushed into 20-30 mesh particles with a loading volume of 20 ml and filled in the constant temperature section of the reactor. The upper and lower part of the catalyst was loaded with 20-30 mesh quartz sand. After the completion of filling, the reactor was connected to the system. Nitrogen gas was introduced for gas tightness test, and the gas-tight pressure was gradually increased to 1.0 MPa. Once the pressure drop was not more than 0.1 MPa after standing for 2 hours, the device was determined to be gas-tight and qualified. [0085] 2. Etherified C4 light hydrocarbons were subjected to a skeletal isomerization experiment for light olefins under the conditions of a pressure of 0.3 MPa, an LHSV of 5.0 h.sup.−1 and a temperature of 320° C., and then the hydrocarbon composition of the product was analyzed.

[0086] The above experiments were carried out with isomerization catalysts from Comparative Examples 4-6 and Examples 4-9, respectively, and the obtained results are summarized in Table 4.

TABLE-US-00004 TABLE 4 Comp. Comp. Comp. Example Example Example Example Example Example Items Ex. 4 Ex. 5 Ex. 6 4 5 6 7 8 9 Catalyst A B C D E F G H I No Convention 33.8 32.6 30.8 38.6 37.2 36.3 42.5 41.2 39.1 of n-butene, % Selectivity 86.1 87.2 86.5 86.9 87.5 87.2 88.3 87.9 88.5 for isobutene, %

[0087] The differences between the molecular sieve production process of Comparative Examples 1-3 and that of Examples 1-3 are as follows: a traditional molecular sieve synthesis method was used in Comparative Examples 1-3, in which no polyacrylamide was added and the crystallization was carried out only once, and the synthesized molecular sieves had larger grain sizes, grain thicknesses greater than 400 nm, grain lengths or widths greater than 1500 nm, and lower crystallinities, while the molecular sieve production method of the present disclosure was used in Examples 1-3, in which polyacrylamide was added and crystallization was carried out twice, and the synthesized molecular sieves had smaller grain sizes and higher crystallinities. Specifically, the molecular sieves synthesized in Examples 1-3 had grain thicknesses less than 50 nm, grain lengths or widths less than 500 nm, and crystallinities larger than 120%; further, the molecular sieves synthesized in Examples 1-2 had grain thicknesses less than 50 nm, grain lengths or widths less than 200 nm, and crystallinities larger than 140%. The above results indicate that the ZSM-35 molecular sieve provided by the present disclosure has the characteristics of small grain size and high crystallinity.

[0088] In Comparative Examples 4-6 and Examples 7-9, the isomerization catalysts were produced using the molecular sieves synthesized in Comparative Examples 1-3 and Examples 1-3, respectively. It should be particularly noted that the isomerization catalysts produced in the above Comparative Examples and Examples were produced essentially by the same method except for the different source of molecular sieves. Specifically, in Examples 10 and 11, the isomerization experiments were carried out using the above isomerization catalyst with etherified C5 components and etherified C4 components as the feedstock, respectively. Seen from the experimental data of Examples 10 and 11, the catalysts produced by the method of the present disclosure (Examples 7-9) exhibited higher isomerization activity and selectivity in the skeletal isomerization reaction for C5 and C4 light olefins compared to the conventional catalysts (Comparative Examples 4-6).

[0089] The difference between the production process of the isomerization catalysts produced in Examples 4-6 and that of Examples 7-9 is as follows: in the catalyst production process of Examples 4-6, a total of three times of baking steps were carried out, while there was only one baking step during the process of Examples 7-9. In other words, the template agent was not removed from the template agent-containing molecular sieve with small grains and high crystallinity used in Examples 7-9 prior to extrusion, and the molecular sieve was not baked after the ammonium exchange. Seen from the experimental data of Examples 10 and 11, the catalysts produced by the process involving one baking step (Examples 7-9) exhibited higher isomerization activity and selectivity in the skeletal isomerization reaction for C5 and C4 light olefins compared to the catalysts produced by the process involving three baking steps (Examples 4-6).

[0090] The above results indicate that the isomerization catalyst obtained by controlling the preparation conditions with the template agent-containing ZSM-35 molecular sieve as the feedstock can catalyze the conversion of light straight-chain olefins to light branched olefins, and the isomerization catalyst has higher catalytic activity and selectivity at lower temperatures.

[0091] Of course, the present disclosure may also have various other embodiments. A person skilled in the art may make various corresponding changes and modifications according to the present disclosure without departing from the spirit and essence of the present disclosure, but these corresponding changes and modifications shall all fall within the protection scope of the claims of the present disclosure.