Fire-Retardant Resins and Composite Materials

Abstract

An epoxide resin for the manufacture of a fibre-reinforced composite material having fire retardant properties and/or for use as an adhesive or hot-melt adhesive having fire retardant properties, the epoxide resin being halogen-free and phenolic resin-free, the epoxide resin comprising: A. a mixture of (i) at least one first non-halogenated multifunctional epoxide-containing resin which has an epoxide functionality of greater than 2 and (ii) at least one second non-halogenated multifunctional epoxide-containing resin which has an epoxide functionality of less than or equal to 2; B. at least one catalyst for curing the mixture of epoxide-containing resins to form a cured epoxy resin; and C. at least one fire retardant additive for forming an intumescent char when the cured epoxy resin is exposed to a fire, wherein the at least one fire retardant additive comprises expandable flake graphite and wherein the expandable flake graphite is present in a concentration of from 0.09 to 2.5 wt % based on the weight of the epoxide resin.

Claims

1. An epoxide resin for the manufacture of a fibre-reinforced composite material having fire retardant properties and/or for use as an adhesive or hot-melt adhesive having fire retardant properties, the epoxide resin being halogen-free and phenolic resin-free, the epoxide resin comprising: A. a mixture of (i) at least one first non-halogenated multifunctional epoxide-containing resin which has an epoxide functionality of greater than 2 and (ii) at least one second non-halogenated multifunctional epoxide-containing resin which has an epoxide functionality of less than or equal to 2; B. at least one catalyst for curing the mixture of epoxide-containing resins to form a cured epoxy resin; and C. at least one fire retardant additive for forming an intumescent char when the cured epoxy resin is exposed to a fire, wherein the at least one fire retardant additive comprises expandable flake graphite and wherein the expandable flake graphite is present in a concentration of from 0.09 to 2.5 wt % based on the weight of the epoxide resin.

2. An epoxide resin according to claim 1 wherein the expandable flake graphite is present in a concentration of from 0.09 to 2.0 wt %, or from 0.45 to 2.0 wt %, or from 0.45 to 1.5 wt %, or from 0.75 to 1.25 wt %, based on the weight of the epoxide resin.

3. (canceled)

4. (canceled)

5. (canceled)

6. An epoxide resin according to claim 1 wherein the expandable flake graphite comprises an intercalated graphite comprising intercalant material between graphene layers of graphite flakes.

7. An epoxide resin according to claim 1 wherein the intercalant material comprises a sulfate intercalation compound.

8. An epoxide resin according to claim 1 wherein the expandable flake graphite comprises graphite flakes having a particle size of less than 75 microns.

9. An epoxide resin according to claim 1 wherein the expandable flake graphite comprises graphite flakes having a carbon content of at least 80 wt %, a moisture content of from 0.8 to 1.5 wt %, a sulfur content of from 2.5 to 3.0 wt %, and optionally a pH of from 5-10.

10. An epoxide resin according to claim 1 wherein the expandable flake graphite has an expansion ratio of from 50:1 cm.sup.3/g to 100:1 cm.sup.3/g, from 50:1 cm.sup.3/g to 75:1 cm.sup.3/g, wherein the expansion ratio is the volume in cm.sup.3 of a test sample of the expandable flake graphite having a mass of 1 gram after heating to a temperature of 950° C.

11. (canceled)

12. An epoxide resin according to claim 1 wherein the at least one fire retardant additive further comprises a blowing agent for generating a non-combustible gas, wherein the blowing agent comprises or consists of melamine, the blowing agent being present in a concentration of from 3.5 to 6 wt %, or from 3.7 to 5.5 wt %, based on the weight of the epoxide resin.

13. (canceled)

14. (canceled)

15. An epoxide resin according to claim 1 wherein the at least one fire retardant additive further comprises an acid donor for decomposing to form a phosphoric acid when the cured epoxy resin is exposed to a fire, wherein acid donor comprises or consists of ammonium polyphosphate and wherein the ammonium polyphosphate is present in a concentration of from 20 to 35 wt %, or from 27 to 32.5 wt %, or from 28.5 to 32 wt %, based on the weight of the epoxide resin.

16. (canceled)

17. (canceled)

18. (canceled)

19. (canceled)

20. An epoxide resin according to claim 1 wherein the at least one fire retardant additive further comprises, as a further intumescent char former, at least one or both of (a) a ceramic or glass material and (b) a ceramic or glass material precursor for to form a ceramic or glass material when the cured epoxy resin is exposed to a fire.

21. An epoxide resin according to claim 20 wherein the further intumescent char former comprises or consists of at least one of, or a mixture of any two or more of, the following: (i) a salt of a divalent metal cation and an oxoanion; (ii) a salt of a trivalent metal and an oxoanion; (iii) a glass material in particulate form; or (iv) a clay or ceramic material in particulate form.

22. An epoxide resin according to claim 21 wherein the further intumescent char former comprises or consists of one or any mixture of (a) a salt of a zinc or calcium cation and an oxoanion selected from borate, molybdate, phosphate, phosphite, hypophosphite and hydroxyl stannate; (b) a salt of aluminium and an oxoanion selected from borate, molybdate, phosphate, phosphite, hypophosphite and hydroxyl stannate; and/or (c) an aluminosilicate clay in particulate form.

23. An epoxide resin according to claim 20 wherein the further intumescent char former is present in a concentration of from 5 to 9 wt %, or from 6 to 8 wt %, or from 6.75 to 7.5 wt %, based on the weight of the epoxide resin.

24. (canceled)

25. (canceled)

26. An epoxide resin according to claim 1, wherein the at least one fire retardant additive further comprises a blowing agent for generating a non-combustible gas wherein the blowing agent, an acid donor for decomposing to form a phosphoric acid when the cured epoxy resin is exposed to a fire, and as a further intumescent char former, at least one or both of (a) a ceramic or glass material and (b) a ceramic or glass material precursor for to form a ceramic or glass material when the cured epoxy resin is exposed to a fire, wherein the blowing agent, acid donor and further intumescent char former are present in a mixture in a weight ratio of 1:6-6.5:1.3-1.7, or in a weight ratio of 1:6.1-6.4:1.5-1.6, wherein the mixture further comprises the expandable flake graphite.

27. (canceled)

28. An epoxide resin according to claim 26 wherein in the mixture the acid donor and further intumescent char former are present in a weight ratio of greater than 4:1 to up to 4.5:1.

29. An epoxide resin according to claim 1 wherein component A in the epoxide-resin has a viscosity of from 1.5 to 15 Pa.Math.s (1.5 to 15 kg/m-s), or from 2 to 14 Pa.Math.s (2 to 13 kg/m-s), or from 2 to 7 Pa.Math.s (2 to 7 kg/m.Math.s), or from 7 to 13 Pa.Math.s (7 to 13 kg/m-s), measured at a temperature of 85° C., measured using a viscometer with a cone number 3, a rotational velocity of 50 rpm, and for a period of 20 seconds.

30. (canceled)

31. (canceled)

32. (canceled)

33. An epoxide resin according to claim 1 wherein in component A, the mixture of epoxide-containing resins comprises a blend comprising at least one first epoxide-containing resin which is solid at 20° C., and at least one second epoxide-containing resin which is liquid at 20° C., wherein the blend comprises from 20 to 40 wt % of at least one first epoxide-containing resin which is solid at 20° C., and from 10 to 30 wt % of at least one second epoxide-containing resin which is liquid at 20° C., each wt % being based on the weight of the epoxide resin.

34. (canceled)

35. An epoxide resin according to claim 33 wherein the blend further comprises at least one third epoxide-containing resin which is semi-solid at 20° C., wherein the blend comprises from 5 to 15 wt % of the at least one third epoxide-containing resin which is semi-solid at 20° C., the wt % being based on the weight of the epoxide resin.

36. (canceled)

37. An epoxide resin according to claim 33 wherein in component A, the mixture of epoxide-containing resins, the at least one first non-halogenated multifunctional epoxide-containing resin which has an epoxide functionality of greater than 2 is present in a concentration of from 8 to 12 wt %, or from 9 to 11 wt %, based on the weight of the epoxide resin.

38. (canceled)

39. An epoxide resin according to claim 1 wherein in component A, the mixture of epoxide-containing resins, the at least one first non-halogenated multifunctional epoxide-containing resin which has an epoxide functionality of greater than 2 comprises or consists of a solid bisphenol-A epoxy novolac resin.

40. An epoxide resin according to claim 1 wherein in component A the mixture of epoxide-containing resins, the at least one second non-halogenated multifunctional epoxide-containing resin which has an epoxide functionality of less than or equal to 2 is present in a concentration of from 45 to 52 wt %, or from 47 to 50 wt %, based on the weight of the epoxide resin.

41. (canceled)

42. An epoxide resin according to claim 1 wherein in component A, the mixture of epoxide-containing resins, the at least one second non-halogenated multifunctional epoxide-containing resin which has an epoxide functionality of less than or equal to 2 comprises or consists of a mixture of a solid bisphenol-A epoxy resin and a liquid bisphenol-A epoxy resin.

43. An epoxide resin according to claim 42 wherein in component A, the mixture of epoxide-containing resins further comprises an epoxy novolac resin.

44. An epoxide resin according to claim 43 wherein in the mixture of a solid bisphenol-A epoxy resin, a liquid bisphenol-A epoxy resin, and an epoxy novolac resin, the solid bisphenol-A epoxy resin is present in a concentration of from 22 to 26 wt %, the liquid bisphenol-A epoxy resin is present in a concentration of from 12 to 17 wt %, and the epoxy novolac resin is present in a concentration of from 8 to 12 wt %, each based on the weight of the epoxide resin, or wherein in the mixture of a solid bisphenol-A epoxy resin and a liquid bisphenol-A epoxy resin, and an epoxy novolac resin, the solid bisphenol-A epoxy resin is present in a concentration from 23 to 25 wt %, the liquid bisphenol-A epoxy resin is present in a concentration from 13 to 15 wt %, and the epoxy novolac resin is present in a concentration of from 9 to 11 wt %, each based on the weight of the epoxy resin.

45. (canceled)

46. A prepreg comprising the epoxide resin of claim 1 and a fibrous reinforcement, wherein the epoxide resin forms an epoxide resin matrix which and at least partially impregnates the fibrous reinforcement.

47. (canceled)

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0065] Embodiments of the present invention will now be described in greater detail by way of example only, with reference to the accompanying drawings, in which:

[0066] FIG. 1 is a graph produced by isothermal DSC testing showing the relationship between epoxide monomer conversion and time at various curing temperatures for epoxide-containing resins used in an epoxide resin in accordance with an Example of the present invention;

[0067] FIG. 2 is a graph produced by isothermal DSC testing showing the relationship between epoxide monomer conversion, as a percentage of total enthalpy, and time at various curing temperatures for the epoxide-containing resins tested in FIG. 1; and

[0068] FIG. 3 is a graph produced by isothermal DSC testing showing the relationship between epoxide monomer conversion, as a percentage of total enthalpy, and time at various curing temperatures for an epoxide resin in accordance with a Comparative Example not according to the present invention.

DETAILED DESCRIPTION

[0069] The present invention is at least partly predicated on the finding by the present inventors that the combination of (i) a specific epoxide-containing resin system to provide a low viscosity prior to curing and a high cross-link density after curing and (ii) a specific fire retardant filler system, including expandable flake graphite and optionally a specific blend of three further fire retardant fillers, can provide the combination a cured epoxy resin with high quality fire-retardancy and structural properties, together with good processability and cost for the uncured epoxide resin.

[0070] In developing the fibre-reinforced composite material of the present invention, the present inventors aimed to employ an epoxide resin as the matrix resin for the composite material, and to select epoxide functionality to achieve a high cross-link density, which in turn enhances the toughness of the cured resin matrix, which otherwise would be significantly reduced by the addition of the fire retardant filler(s). The cured epoxy resin matrix can bond satisfactorily to honeycomb cores for sandwich panel construction as used in interior panels incorporated into vehicles, such as aircraft and train, interiors.

[0071] The cured epoxy resin can also function as an adhesive to bond satisfactorily to a variety of substrates, for example also to be incorporated into vehicles, such as aircraft and train, interiors.

[0072] The fire retardance and smoke release characteristics of the epoxide resin can be significantly improved by the addition of the specific fire retardant filler system, including expandable flake graphite and optionally the specific blend of three further fire retardant fillers, and can be of a sufficient level to act as a global replacement for phenolic materials for such vehicle applications. This is a major technical and commercial advance.

[0073] However, a primary advantage of the present invention is that good FST properties can be achieved in an epoxy resin incorporating one or more FST fillers, which nevertheless, even in the embodiments with a reasonably high filler content, provides good mechanical properties in the resultant cured epoxy resin composite material component.

[0074] The epoxide resin employed in accordance with the embodiments of the present invention is an addition-cured resin. Therefore no volatiles are released during cure. As compared to condensation-cured resins, such as phenolic resins, this provides the advantage of allowing components to be cured using lower-cost vacuum bag technology with significantly reduced refinishing and processing costs.

[0075] The epoxide resin employed in accordance with the embodiments of the present invention is a halogen-free, epoxide matrix resin and unlike phenolic systems, does not contain residual phenol or solvents. This means that it can be used in aircraft interior parts such as air-conditioning ducting without the risk of toxic phenol being leached into the passenger air supply. Its high toughness facilitates its application in aircraft flooring, previously the domain of toughened halogenated epoxides, with the additional advantage that the halogen-free, epoxide matrix resin avoids the smoke toxicity issues associated with halogenated epoxides.

[0076] One or more fire-retardant fillers were added to the epoxide resin matrix employed in accordance with the embodiments of the present invention to improve the heat release, and preferably also the smoke release and smoke toxicity, properties of the matrix resin.

[0077] The present invention has particular application in the manufacture of multilaminar composite sandwich panels comprising a central core, for example of a honeycomb material itself known in the art, and two opposed outer plies comprising fibre-reinforced composite material incorporating a resin matrix produced in accordance with the present invention.

[0078] The resin matrix must display two main behaviours in order to achieve sufficient peel adhesion to a core such as a honeycomb core:

a. The matrix resin must flow sufficiently during cure in order to form sufficient contact area with the honeycomb cell surface to achieve good adhesion. Yet flow must be adequately ‘controlled’ to prevent excessive resin flow resulting in resin scarce areas of the prepreg laminate skins.
b. The matrix must exhibit toughness to withstand multiple impacts during service and resist premature matrix cracking, for example which would result in reduced peel strength.

[0079] The present inventors found that the use of a specific blend of multifunctional epoxide resins provided enhanced toughness in the resultant cured resin matrix as a result of cross-linking. Consequently, conventional elastomeric or thermoplastic toughening additives, such as a dispersed nitrile rubber in the resin matrix, can be avoided, which is advantageous since such additives would otherwise provide a source of carbon on combustion which would increase the smoke density.

[0080] The various components of the epoxide-resin matrix used in accordance with the preferred embodiments of the present invention are discussed in greater detail below.

Epoxide Component

[0081] The epoxide resin comprises a mixture of (i) at least one first non-halogenated multifunctional epoxide-containing resin which has an epoxide functionality of greater than 2 and (ii) at least one second non-halogenated multifunctional epoxide-containing resin which has an epoxide functionality of less than or equal to 2.

[0082] Preferably, the epoxide-containing resin mixture of component A in the epoxide-resin has a viscosity of from 1.5 to 15 Pa.Math.s (1.5 to 15 kg/m-s) measured at a temperature of 85° C., in particular measured using a viscometer sold under the trade name Brookfield® CAP2000HT viscometer, with a cone number 3, a rotational velocity of 50 rpm, and for a period of 20 seconds. A preferred viscosity range for this parameter measured under these conditions is for example from 7 to 13 Pa.Math.s (7 to 13 kg/m-s) for manufacturing epoxy prepreg skins for honeycomb panels, for example for aerospace applications, and from 2 to 7 Pa.Math.s (2 to 7 kg/m-s) for manufacturing epoxy prepreg panels for railway applications. To prevent the addition of fillers increasing resin, the final resin viscosity is optimised by balancing the liquid epoxide functional resin to the higher-functionality epoxide resin blend.

[0083] Preferably, in component A, the mixture of epoxide-containing resins comprises a blend comprising at least one first epoxide-containing resin which is solid at 20° C., and at least one second epoxide-containing resin which is liquid at 20° C., optionally further comprising at least one third epoxide-containing resin which is semi-solid. In this specification, the term “semi-solid” means materials which are neither true solids or true liquids but shares the properties of both states. Therefore a semi-solid resin cannot be poured in the same way as a liquid resin however will deform and flow under pressure or shear unlike a solid resin at 20° C.

[0084] Optionally, the blend comprises from 20 to 40 wt % of at least one first epoxide-containing resin which is solid at 20° C., and from 10 to 30 wt % of at least one second epoxide-containing resin which is liquid at 20° C., optionally further comprising from 5 to 15 wt % of at least one third epoxide-containing resin which is semi-solid at 20° C., each wt % being based on the weight of the epoxide resin.

[0085] Preferably, in the mixture of epoxide-containing resins, the at least one first non-halogenated multifunctional epoxide-containing resin which has an epoxide functionality of greater than 2 is present in a concentration of from 8 to 12 wt %, more preferably from 9 to 11 wt %, based on the weight of the epoxide resin. That resin may comprise or consist of a solid bisphenol-A epoxy novolac resin.

[0086] Preferably, in the mixture of epoxide-containing resins, the at least one second non-halogenated multifunctional epoxide-containing resin which has an epoxide functionality of less than or equal to 2 is present in a concentration of from 45 to 52 wt %, more preferably from 47 to 50 wt %, based on the weight of the epoxide resin. That resin may comprise or consist of a mixture of a solid bisphenol-A epoxy resin and a liquid bisphenol-A epoxy resin, optionally in addition an epoxy novolac resin. The solid bisphenol-A epoxy resin may be present in a concentration of from 22 to 26 wt %, the liquid bisphenol-A epoxy resin may be present in a concentration of from 12 to 17 wt %, and the optional epoxy novolac resin may be present in a concentration of from 8 to 12 wt %, each based on the weight of the epoxide resin. Alternatively, the solid bisphenol-A epoxy resin may be present in a concentration of from 23 to 25 wt %, the liquid bisphenol-A epoxy resin may be present in a concentration of from 13 to 15 wt %, and the optional epoxy novolac resin may be present in a concentration of from 9 to 11 wt %, each based on the weight of the epoxide resin.

[0087] Preferably, to achieve high FST properties the epoxide resin is free of any elastomeric material or elastomeric toughening additive. In particular, the epoxide-containing resin preferably is free of any toughening additives which comprise an elastomer and/or a thermoplastic having a molecule capable of reacting with the epoxide molecule so as to be chemically bonded as a co-monomer into the epoxide resin matrix. In contrast, the epoxide resin system is formulated to provide sufficient tack to the adhesive, hot-melt adhesive, or prepreg and to provide enhanced toughness of the cured epoxy resin.

[0088] In alternative embodiments for applications with lower FST requirements but requiring high toughness of the cured epoxy resin, such any elastomeric material or elastomeric toughening additive, or thermoplastic toughening additives may be present.

[0089] Suitable epoxy resins include diglycidyl ethers of bisphenol A, diglycidyl ethers of bisphenol F, epoxy novolac resins and N-glycidyl ethers, glycidyl esters, aliphatic and cycloaliphatic glycidyl ethers, glycidyl ethers of aminophenols, glycidyl ethers of any substituted phenols and blends thereof.

[0090] In a particularly preferred embodiment, the epoxide-containing resin is a solid at room temperature, 20 degrees Centigrade.

[0091] The epoxide-containing resin is formulated to comprise a mixture of solid and liquid resins, and optionally also semi-solid resins, so that when heated during curing the epoxide resin has a liquid content, resulting from liquefied epoxide resins and the associated catalyst system, and a solid content, resulting from the fillers, which has a reduced viscosity of the resin matrix to allow hot-melt processing, prepreg flexibility (drape) and sufficient prepreg tack to allow ease of handling.

[0092] The epoxide-containing resin may further comprise a catalyst carrier which acts to assist incorporation of the latent catalyst for the epoxide resin into the composition. Typically, the catalyst carrier comprises a diglycidyl ether of bisphenol F liquid resin. For example, the catalyst carrier may comprise a diglycidyl ether of bisphenol F liquid resin available in commerce under the trade name Epikote® 862 from Resolution Performance Products. The catalyst carrier may typically be present in the resin composition in an amount of up to 10 wt %, based on the total weight of the resin composition.

[0093] Preferably, the epoxide resin is free of any epoxide-containing molecule that has been chemically reacted with a phosphinic acid derivative or dihydro-oxa-phospha-phenanthrene-oxide (DOPO).

Catalyst/Curing Agent Component

[0094] The epoxide-containing resin further comprises as a second component a catalyst or curing agent suitable for curing epoxide resins, optionally together with at least one additional catalyst additive or modifier. Any suitable catalyst may be used. The catalyst will be selected to correspond to the resin used. The catalyst may be accelerated. The catalyst or curing agent may typically be selected from a dicyandiamide, sulphanilamide, urone, urea, imidazole, amine, halogenated boron complex, anhydride, lewis base, phenolic novolac, or a nitrogen containing compound. Latent curing agents such as dicyandiamide, femurone and imidazole may be cured. Suitable accelerators include Diuron, Monuron, Fenuron, Chlortoluron, urea of toluene diisocyanate and other substituted homologues.

[0095] Preferably, the at least one catalyst for curing the epoxide-containing resin comprises or consists of a dicyanamide-based catalyst. Typically, the curing catalyst for the epoxide-containing resin is dicyandiamide, most preferably being in micronized form, and such a catalyst is available in commerce under the trade name Amicure® CG1200E from Air Products Inc. Such a dicyandiamide-based catalyst has a high functionality to enable the resultant cured epoxy resin to have high cross-linking density and thereby a high glass transition temperature (Tg).

[0096] Optionally, the at least one catalyst comprises plural catalysts, each having a respective curing temperature range, and the plural temperature ranges overlap to provide a cumulative curing temperature range for the epoxide-containing resin.

[0097] The epoxide resin typically further comprises at least one accelerator for the at least one catalyst, for example an imidazole-based accelerator and/or a urea-based accelerator, typically a substituted/blocked urea. Such an imidazole-based accelerator can reduce the onset of reaction, thereby allowing curing at a reduced temperature. The imidazole-based accelerator preferably can be selected to provide a shelf life of the prepreg which is sufficiently long, for example >4 weeks at 21° C., to enable a useable shelf and storage life. Such a substituted/blocked urea can accelerate and control the curing profile.

[0098] The curing catalyst may typically be present in the resin composition in an amount of from 1 to 15 wt %, more typically from 6 to 12 wt %, based on the total weight of the epoxide component A of the resin composition. In one example, the catalyst is added at 4.9 wt % of the total composition of components A, B and C, which may correspond to 8.7 wt % of component A. Too low an amount of the curing catalyst may cause a reduced cure of the resin material, whereas too high an amount may cause an excessively exothermic cure.

[0099] The curing catalyst may be combined with an additional catalyst additive to reduce the activation energy, and hence the curing temperature, of the primary curing catalyst such as dicyandiamide. Such an additive may comprise urone, which has the chemical formula N,N″-(4-methyl-m-phenylene)bis[N′,N′-dimethylurea] and is available in commerce under the trade name Amicure® UR2T from Evonik Industries Inc. or under the trade name UR500 from Alzchem AG.

[0100] Such an additive may typically be present in the resin composition in an amount of up to 15 wt %, more typically from 1 to 4 wt %, based on the total weight of the epoxide component A of the resin composition. In one example, the urone is added at 0.67 wt % of the total composition of components A, B and C, which may correspond to 1.18 wt % of component A. A low amount of the additional catalyst additive may cause a reduced cure speed and/or reduced curing temperature of the resin material, whereas too high an amount may cause reduced fire, smoke and toxicity resistance properties.

[0101] The curing catalyst may be yet further be combined with an additional additive imidazole-based catalyst or curing agent provided to further reduce the activation energy, and hence the curing temperature, of the urone. In addition, the C═N bonds present in imidazole have been shown to improve the fire-retardancy properties of the resultant cured epoxide-resin compared to other catalysts. Such an imidazole-based catalyst or curing agent is available in commerce under the trade name 2MZ-Azine-S from Shikoku, Japan.

[0102] The imidazole-based catalyst or curing agent may typically be present in the resin composition in an amount of up to 15 wt %, more typically from 1 to 4 wt %, based on the total weight of the epoxide component A of the resin composition. In one example, the imidazole-based catalyst is added at 2 wt % of the total composition of components A, B and C, which may correspond to 3.5 wt % of component A. A low amount of the imidazole-based catalyst or curing agent may cause a reduced cure speed and/or reduced curing temperature of the resin material, whereas too high an amount may cause an excessively exothermic cure.

Fire-Retardant/Smoke Suppressant Fillers

[0103] The epoxide resin comprises at least one fire retardant additive for forming an intumescent char when the cured epoxy resin is exposed to a fire. In accordance with the present invention, the at least one fire retardant additive comprises expandable flake graphite and the expandable flake graphite is present in a concentration of from 0.09 to 2.5 wt % based on the weight of the epoxide resin.

[0104] In preferred embodiments of the present invention, the expandable flake graphite is present in a concentration of from 0.09 to 2.0 wt %, or from 0.45 to 2.0 wt %, or from 0.45 to 1.5 wt %, or from 0.75 to 1.25 wt %, based on the weight of the epoxide resin.

[0105] Preferably, the expandable flake graphite comprises an intercalated graphite comprising intercalant material between graphene layers of graphite flakes. Typically, the intercalant material comprises a sulfate intercalation compound. However, other intercalant materials may be used that are known to those skilled in the art, for example halogens, alkali metals, nitrates, organic acids, aluminum chloride, ferric chloride, other metal halides, arsenic sulfide, or thallium sulfide.

[0106] Preferably, the expandable flake graphite comprises graphite flakes having a particle size of less than 75 microns. However, other particle sizes may be used. Nevertheless, the preferred particle size has been found to be particularly suitable for mixing into the epoxy resin matrix for forming a prepreg.

[0107] Preferably, the expandable flake graphite comprises graphite flakes having a carbon content of at least 80 wt %, a moisture content of from 0.8 to 1.5 wt %, a sulfur content of from 2.5 to 3.0 wt %. Optionally this expandable flake graphite composition has a pH of from 5-10, although alternatively the PH may be from 1-6.

[0108] Preferably, the expandable flake graphite has an expansion ratio of from 50:1 cm.sup.3/g to 100:1 cm.sup.3/g, optionally from 50:1 cm.sup.3/g to 75:1 cm.sup.3/g, wherein the expansion ratio is the volume in cm.sup.3 of a test sample of the expandable flake graphite having a mass of 1 gram after heating to a temperature of 950° C.

[0109] A particularly preferred expandable flake graphite is sold under the trade name “3538 Expandable Flake Graphite” by Asbury Graphite Mills, Inc. Asbury N.J., USA. The “3538 Expandable Flake Graphite” has a sulfate intercalation compound and has a particle size of less than 75 microns, a carbon content of at least 80 wt %, a moisture content of 1.4 wt %, a sulfur content of 2.6 wt %, a pH of from 5-10 and an expansion ratio of 60:1 cm.sup.3/g.

[0110] Preferably, the at least one fire retardant additive further comprises a blowing agent, and/or an acid donor and/or a further intumescent char former. Typically the blowing agent, the acid donor and the further intumescent char former, hereinafter respectively called “first”, “second” and “third” fire retardant additives, are present in a mixture thereof.

[0111] The expandable flake graphite component within the cured epoxy resin can function independently to form an intumescent char when the cured epoxy resin is exposed to a fire.

[0112] The optional additional mixture of first, second and third fire retardant additives also react together independently to form an intumescent char when the cured epoxy resin is exposed to a fire. These fire retardant additives comprises fillers used to promote fire-retardancy and/or reduce generation of smoke, opacity of smoke or toxicity of smoke.

[0113] When both the expandable flake graphite and the mixture of first, second and third fire retardant additives are present in the epoxide resin, preferably all of these additives being in a common mixture within the epoxide resin, all four of these fire retardant additives cumulatively act to form a common intumescent char.

[0114] Optionally, such fillers are dispersed homogeneously throughout the resin matrix. However, the dispersion may alternatively be heterogeneous, for example being present in surface layers. Many improvements in properties do not require such homogeneous dispersion and so this may result in a material which is thus either over-engineered for the application or, conversely, reduced in one or more other properties.

[0115] The first fire retardant additive comprises a blowing agent for generating a non-combustible gas. Preferably, the first fire retardant additive comprises or consists of melamine. The first fire retardant additive may be present in a concentration of from 3.5 to 6 wt %, more preferably from 3.7 to 5.5 wt %, based on the weight of the epoxide resin.

[0116] The second fire retardant additive comprises an acid donor for decomposing to form a phosphoric acid when the cured epoxy resin is exposed to a fire, for example ammonium polyphosphate. Preferably, the ammonium polyphosphate of the second fire retardant additive is present in a concentration of from 20 to 35 wt %, more preferably from 27 to 32.5 wt %, still more preferably from 28.5 to 32 wt %, based on the weight of the epoxide resin. An ammonium polyphosphate fire retardant mineral filler is available under the trade name Exolit® AP 422 from Clariant, Leeds, UK.

[0117] The third fire retardant additive comprises at least one or both of (a) a ceramic or glass material and (b) a ceramic or glass material precursor to form a ceramic or glass material when the cured epoxy resin is exposed to a fire.

[0118] Preferably, the third fire retardant additive comprises or consists of at least one of, or a mixture of any two or more of, the following: (i) a salt of a divalent metal cation and an oxoanion; (ii) a salt of a trivalent metal and an oxoanion; (iii) a glass material in particulate form; or (iv) a clay or ceramic material in particulate form.

[0119] In one preferred embodiment, the third fire retardant additive comprises or consists of a salt of a zinc or calcium cation and an oxoanion selected from borate, molybdate, phosphate, phosphite, hypophosphite and hydroxyl stannate. The third fire retardant additive may comprise or consist of a salt of aluminium and an oxoanion selected from borate, molybdate, phosphate, phosphite, hypophosphite and hydroxyl stannate. Alternatively, the third fire retardant additive may comprise or consist of an aluminosilicate clay in particulate form. One particular smoke suppressant mineral filler is zinc borate, available in commerce under the trade name Firebrake ZB from Borax Europe Limited.

[0120] In another preferred embodiment, the third fire retardant additive comprises or consists of a glass material in particulate form, for example glass microbeads having a diameter d(0.5) within the range of from 15 to 30 microns, and optionally a diameter d(0.9) within the range of from 30 to 80 microns.

[0121] In another preferred embodiment, the third fire retardant additive comprises or consists of a clay or ceramic material in particulate form, for example an aluminosilicate clay.

[0122] Preferably, the third fire retardant additive is present in a concentration of from 5 to 9 wt %, based on the weight of the epoxide resin, more preferably from 6 to 8 wt %, yet more preferably from 6.75 to 7.5 wt %, based on the weight of the epoxide resin.

[0123] Preferably, in the mixture of first, second and third fire retardant additives, the first, second and third fire retardant additives are present in a weight ratio of 1:6-6.5:1.3-1.7, typically a weight ratio of 1:6.1-6.4:1.5-1.6.

[0124] Preferably, in the mixture of first, second and third fire retardant additives, the second and third fire retardant additives are present in a weight ratio of greater than 4:1 to up to 4.5:1.

[0125] Preferably, the mixture of epoxide-containing resins, and the mixture of first, second and third fire retardant additives, are present in a weight ratio of 52-68:32-48, typically a weight ratio of 56-62:38-44.

[0126] Preferably, the mixture of first, second and third fire retardant additives, provides the epoxide resin with a phosphorous content of from 7.5 to 10.5 wt %, more preferably from 8 to 9.25 wt %, based on based on the weight of the epoxide resin.

[0127] Preferably, the mixture of first, second and third fire retardant additives, provides the epoxide resin with a nitrogen content of from 5.8 to 8.25 wt %, %, more preferably from 7 to 7.5 wt % based on based on the weight of the epoxide resin.

[0128] The acid donor, for example ammonium polyphosphate, can act both in the condensed and gas phase during a fire. Ammonium polyphosphate decomposes at >240° C. releasing water and ammonia to cool and dilute the gaseous phase, and releasing phosphoric acid. The phosphoric acid acts as an acid catalyst in the dehydration of carbon-based poly-alcohols to form heat-unstable phosphate esters. The esters decompose to release carbon dioxide and phosphoric acid is regenerated.

[0129] A carbonaceous char is formed by the expandable flake graphite and the mixture of the blowing agent, acid donor and glass/ceramic or precursors thereof when the cured epoxy resin is subjected to exposure to a fire.

[0130] The carbonaceous char shields the substrate from attack by oxygen and radiant heat. In the gas phase, the release of non-flammable carbon dioxide helps to dilute the oxygen of the air and flammable decomposition products of the substrate. Any P* and PO* radicals liberated during the combustion can act as scavengers of oxygen radicals, thereby reducing the energy of the radicals in the gas phase and reducing volatilization.

[0131] The inorganic mineral fillers such as zinc borate act as a multifunctional fire retardant and smoke suppressant. The metal, e.g. zinc, species remains in the condensed phase and acts as a catalyst for char formation by promoting cross-linking in the expanded resin protective surface layer. Char formation in turn suppresses smoke formation which is reinforced by the glass-forming ability of metal oxides, e.g. borate oxides, which can increase mechanical performance of char/intumescence.

[0132] The acid donor, for example ammonium polyphosphate, and the metal cation/oxyanion, for example zinc borate, interact synergistically whilst degrading, thereby stabilizing the phosphorus species.

[0133] Without being bound by any theory, it is believed by the present inventors that the glass beads work synergistically with the ammonium polyphosphate by the glass beads forming a fused/protective layer that minimises volatile/gas phase release. However typically, smoke density is also reduced through any one or more of reduced carbon-carbon bond saturation (i.e. alkanes burn cleaner than alkenes), lower carbon content in the resin and by allowing complete combustion (i.e. ensuring CO.sub.2 rather than CO is formed).

[0134] The blowing agent, for example melamine, degrades at combustion temperatures, for example >300° C., thereby releasing nitrogen gas which forces the char formation to intumesce.

[0135] The expandable flake graphite, and the preferred weight ratio of the optional three fillers of the blend of first, second and third fire retardant additives, can produce a strong, toughened intumescence which protects the polymeric substrate from further heat and oxygen, and traps volatiles to prevent further combustion.

[0136] If the fire retardant and smoke suppressant mineral fillers, are present in too high an amount, the resin composition may exhibit high viscosity, reduced toughness and poor adhesion, for example to a core, whereas if the fire retardant mineral filler is present in too low an amount, the fire, smoke and toxicity resistance properties may be reduced.

[0137] The mineral fillers may optionally be provided together with a filler dispersion additive to aid wetting and dispersion of fillers during manufacture of the matrix resin. Such a filler dispersion additive is available in commerce under the trade name BYK W980 from BYK Chemie, Wesel, Germany. The filler dispersion additive may typically be present in the resin composition in an amount of up to 1 wt %, based on the total weight of the resin composition.

Further Additives

[0138] The epoxide-containing matrix resin may comprise additional additives known in the art to improve resin processing or properties, or both.

[0139] In particular, an anti-settling agent may be provided to reduce or prevent settling of the at least one mineral filler, for example in the resin formulation during storage/processing and/or during curing of the resin. The anti-settling agent may also control resin flow during resin curing. In addition, such an agent can prevent settling of powder particles, such as the fire-retardant and/or smoke suppressant fillers. A typical anti-settling agent comprises silicon dioxide, optionally amorphous silicon dioxide, most typically hydrophobic fumed silica, for example available under the trade name Cabot® TS-720. The at least one anti-settling agent is typically present in an amount of from 0.5 to 1.5 wt % based on the weight of the epoxide resin.

[0140] In a prepreg, the fibrous reinforcement may comprise one or more materials such as glass fibre, aramid fibre, carbon fibre, or PAN or pitch based carbon fibre. The present invention is particularly directed to an epoxide resin system which has sufficiently low viscosity during impregnation so that carbon fibres, which are generally harder to impregnate than glass fibres, can be reliably and uniformly impregnated to form a carbon-fibre prepreg.

[0141] The modified epoxide-containing matrix resin of preferred embodiments of the present invention may be used in prepregs and composite materials of the present invention, which in turn have particular application for use for interior panel construction for mass transport applications where a fire, smoke and toxicity requirement is necessary. The composite materials made using such a resin can provide significant advantages over the known resins discussed above, such as phenolic, cyanate-ester, SMC, modified vinyl-ester and halogenated epoxides which have been used in the past for these applications.

[0142] The epoxide-containing matrix resin of the preferred embodiments of the present invention may be used in a number of applications.

[0143] The epoxide-containing matrix resin of the preferred embodiments of the present invention may be used in structural applications where fire, smoke and toxicity performance that is similar to phenolic materials is required yet with greatly increased mechanical properties. Additional advantages include ease of processing and reduced refinishing which allow substantial cost reductions especially on large civil structures. Phenolic panels tend to be dark brown in colour and so are commonly painted to achieve the desired component colour. Problems can occur during service whereby if the material is scratched; the base colour of the phenolic becomes highly visible. The epoxide-containing matrix resin of the preferred embodiments of the present invention may be white in colour which reduces the visual impact of such scratching during use.

[0144] The modified epoxide-containing matrix resin of preferred embodiments of the present invention may alternatively be used in adhesives or hot-melt adhesives.

[0145] The resultant cured resins exhibit FST properties.

[0146] The epoxide-containing matrix resin of the preferred embodiments of the present invention can provide a number of technical benefits as compared to known prepregs and composite materials having fire and/or smoke resistance. In particular, there may be provided in accordance with the present invention: a phenol-free alternative to phenolic prepregs; good regulatory labelling for handling uncured material; halogen-free for reduced toxicity during combustion compared to brominated systems; no volatiles are released during cure—improved mechanical properties; can achieve increased filler loadings without forsaking processing capability or fibre wet-out; does not require high-pressure press tooling to process, can use low-cost vacuum-bag technology; can achieve an out-of-autoclave cure; high-quality surface finish “straight from tooling”—does not require expensive and time-consuming refinishing, no pitting, reduced time and cost to rework surface in post processing stages; higher reactivity allowing either lower temperature curing and/or faster curing compared to halogenated and DOPO modified systems; reduced material cost through use of lower cost chemistry; and pale-colour—requires less surface coating to achieve desired aesthetic and results in increased longevity during operation (i.e. scratches etc. are less visible).

[0147] The present invention can solve a number of problems associated with known fire retardant epoxide based structural prepregs, and in particular can provide the combination of high mechanical properties combined with excellent FST properties for an epoxy system using a specific intumescent filler system, which comprises a specific concentration of expandable flake graphite and optionally additionally a combination of a blowing agent, an acid donor and a glass or ceramic material or precursor thereof.

[0148] The modified epoxide material produced in accordance with the present invention may be used by manufactures of composite prepregs for use in a wide-range of fire-retardant applications. The prepreg would offer a unique alternative to a wide-range of existing fire-retardant materials including (but not limited to) phenolics, halogenated epoxides, and cyanate esters but with significant advantages of the combination of enhanced fire-retardant, smoke and toxicity (FST) properties and mechanical properties, together with good resin processing.

EXAMPLES

[0149] The epoxide-containing resin of the preferred embodiments of the present invention is further illustrated with reference to the following non-limiting examples.

[0150] The development of the epoxide-containing resin of the present invention required the determination of high fire-retardancy which is essential for providing a fire retardant epoxy resin having high structural properties, and in addition although not tested the compositions would also exhibit high smoke suppression and low toxicity. In addition to meeting these performance criteria, it was necessary to ensure that the epoxide-containing matrix resin was suitable for manufacture using hot-melt (non-solvent impregnation) impregnation methods. To benchmark the epoxide-containing matrix resin against current industry standards, the resin was tested to determine that it had thermal, mechanical and handling properties which complied with the specification established by Airbus Industries, Toulouse, France for interior FST materials, in particular (AIMS 05-10-034-01).

Example 1

[0151] A resin composition was formulated as set out in Table 1 (which had the applicant's product code SPX26425). The base epoxide resin comprised a blend of semi-solid, solid and liquid epoxide resin monomers of component A. The epoxide resin functionality was 3.3 for the total epoxide resin monomer blend. The liquid to solid resin weight ratio was 0.6.

[0152] The base epoxide resin blend was mixed with a blend of expandable flake graphite, ammonium polyphosphate (acid donor), Microperl™ glass beads (glass material) and melamine (blowing agent) fire retardant additives, which is component C, as set out in Table 1. The resin composition further comprised hydrophobic fumed silica as an anti-settling agent, sold under the trade name Cabot® TS-720. Titanium dioxide was also present as a whitening pigment. The melamine/ammonium polyphosphate/glass beads weight ratio was 1/6.3/1.5.

[0153] The expandable flake graphite was present in a concentration of 0.9 wt % based on the total weight of the epoxide resin. The weight ratio of the resin/fillers in the base resin was 58.1/42.8. The weight ratio of the liquid (resin and catalyst)/solid fillers was 1.68. The phosphorous content of the epoxide resin was 9.1 wt % and the nitrogen content of the epoxide resin was 7.3 wt %.

[0154] The resin composition further comprised, as component B and in wt % values with respect to the combination of components A, B and C, 2.25 wt % of dicyandiamide, in micronized form, as a primary resin curing catalyst, 0.67 wt % of urone as an additional catalyst additive to reduce primary catalyst activation energy, and 2.02 wt % of an imidazole-based catalyst additive to further reduce the primary catalyst activation energy.

[0155] The resin constituents liquefied on heating to 85° C. and component A had a viscosity of 5.5+/−0.6 Pa.Math.s (5.5+/−0.6 kg/m-s) measured at 85° C., and measured using a viscometer sold under the trade name Brookfield® CAP2000HT viscometer, with a cone number 3, a rotational velocity of 50 rpm, and for a period of 20 seconds.

[0156] The base resin, comprising the combination of components A and C, i.e. the resin and fillers, had a base resin viscosity of 192+/−30 Pa.Math.s (192+/−30 kg/m-s) measured at 85° C., and measured using a viscometer sold under the trade name Brookfield® CAP2000HT viscometer, with a cone number 3, a rotational velocity of 50 rpm, and for a period of 20 seconds.

[0157] The resin was used to make a prepreg, which comprised 46 wt % of the resin composition and 54 wt % of a glass fibre fabric with a satin weave, in particular a 7781 style 8H satin 300 gsm glass fabric, which was then cured.

[0158] The curing temperature was varied, and a series of isothermal differential scanning calorimetry (DSC) plots of the cure profile were measured. The results are shown in FIG. 1, and these plots show the speed of cure conversion at different curing temperatures. FIG. 1 shows that there is a trend of increasing isothermal temperatures to reduce the time to 100% cure conversion, the latter parameter being the time to reach the maximum cure at a given cure temperature.

[0159] FIG. 2 correspondingly shows the actual cure conversion, calculated as a percentage of the total possible enthalpy observed in a dynamic DSC trace. As can be seen, a reduction in isothermal cure temperature, reduces the cure conversion, and therefore would increase the amount of residual uncured material within the resultant composite material laminate.

[0160] The resin system of Example 1 had a minimum cure temperature of 85° C., and a cure dwell time at that minimum cure temperature of 5 hours. Alternatively, when the resin system of Example 1 was subjected to a faster cure at a higher temperature of 120° C., the cure dwell time at the faster cure temperature was only 40 minutes.

[0161] One plot in FIG. 2 shows 80% cure conversion after 5 hours at 85° C.

[0162] The fire-retardancy of the prepreg resin of Example 1 in accordance with the present invention was tested in the laboratory for fire-retardant properties, in accordance with a number of industry standard FST tests. The tests were conducted by a UKAS-accredited fire testing agency external to the Applicant.

[0163] A sandwich panel was constructed having a aramid honeycomb core (composed of Nomex™) having a thickness of 6.35 mm (0.25 inches) with opposite plies of epoxy resin matrix reinforced with glass fibres, each ply being formed from the prepreg described above. The panels were cured for 10 minutes at a curing temperature of 155° C. under a pressure of 1.2 MPa (12 bar).

[0164] The Maximum Average Rate of Heat Release MAHRE (kWm.sup.−2), the peak rate of heat release (kWm.sup.−2) and the total heat released (MJm.sup.−2) were measured. The tests used a cone calorimeter in accordance with ISO 5660-1, using a heat flux of 50 kW.

[0165] The height of the intumescent char was measured by calculating a mean value from five separate test coupons. The results are shown in Table 1.

[0166] It may be seen that the resin of Example 1 exhibited very low MAHRE, 42 kWm.sup.−2, peak rate of heat release, 73 kWm.sup.−2, and total heat released, 1.6 MJm.sup.−2, for an epoxide resin. The height of the intumescent char was 19.3 mm.

Example 2

[0167] An alternative resin formulation as shown in Table 1 was used as Example 2 (which had the applicant's product code SPX26425). As compared to Example 1, the modification was that the expandable flake graphite was present in a concentration of 1.8 wt % based on the total weight of the epoxide resin.

[0168] Again, it may be seen that the resin of Example 2 exhibited low MAHRE, 59 kWm.sup.−2, peak rate of heat release, 82 kWm.sup.−2, and total heat released, 2.5 MJm.sup.−2, for an epoxide resin. The height of the intumescent char was 13.0 mm.

Examples 3 and 4

[0169] Alternative resin formulations as shown in Table 1 were used as Examples 3 and (which had the applicant's product codes SPX26663 and SPX26665 respectively). As compared to Example 1, the modification was that the expandable flake graphite was respectively present in a concentration of 0.09 wt % for Example 3 or 0.45 wt % for Example 4 based on the total weight of the epoxide resin.

[0170] For the resin of Examples 3 and 4 the heat release values, i.e. MAHRE, peak rate of heat release, and total heat released were not measured (due to an equipment fault in the measuring equipment). The height of the intumescent char was 18.8 mm for Example 3 and 14.5 mm for Example 4.

Comparative Example 1

[0171] An alternative resin formulation as shown in Table 2 was used as Comparative Example 1 (which had the applicant's product code SPX25211). As compared to Examples 1 and 2, no expandable flake graphite was present in the epoxide resin but otherwise the epoxide resin composition was the same as in Examples 1 and 2.

[0172] The resin of Comparative Example 1 exhibited worse heat release and intumescent properties than the Examples. It may be seen from Table 2 that the resin of Comparative Example 1 exhibited a higher MAHRE, 65 kWm.sup.−2, a higher peak rate of heat release, 124 kWm.sup.−2, and a higher total heat released, 4.5 MJm.sup.−2, than Examples 1 and 2. The height of the intumescent char of Comparative Example 1 was only 5.6 mm, lower than in Examples 1, 2, 3 and 4.

[0173] The mechanical properties of the cured resin of Comparative Example 1 were tested. An 8 ply 7781 glass fabric monolithic panel was made and the Interlaminar Shear Strength (ILSS) was tested; the value was 58 MPa. The same panel was tested for flexural strength and flexural modulus; the value of flexural strength was 558 MPa and the value of flexural modulus was 20 GPa. Furthermore, a sandwich panel having a two ply skin with the same glass fabric was made and the Climbing Drum Peel Strength was tested; the value was 257 N/75 mm.

[0174] Examples 1, 2, 3 and 4 have a very similar epoxide resin composition to Comparative Example 1, respectively differing only by 0.09, 0.45, 0.9 and 1.8 wt % expandable graphite flake. Accordingly, the resins of Examples 1, 2, 3 and 4 would provide similar high mechanical properties as tested above for Comparative Example 1.

Comparative Example 2

[0175] An alternative resin formulation as shown in Table 2 was used as Comparative Example 2 (which had the applicant's product code SPX26196). As compared to Examples 1, 2, 3 and 4, a higher concentration of expandable flake graphite was present in the epoxide resin, i.e. 3.6 wt % based on the weight of the total epoxide resin.

[0176] The resin of Comparative Example 2 exhibited worse heat release and intumescent properties than the Examples. It may be seen from Table 2 that the resin of Comparative Example 2 exhibited a higher or similar MAHRE, 58 kWm.sup.−2, a higher peak rate of heat release, 96 kWm.sup.−2, and a higher total heat released, 2.7 MJm.sup.−2, than Examples 1 and 2. The height of the intumescent char of Comparative Example 1 was only 11.4 mm, lower than for Examples 1, 2, 3 and 4.

[0177] It is to be noted that for Comparative Example 2, due to outlier results in the measured data fewer than 5 test coupons were tested, which may explain why the MAHRE value of Comparative Example 2 is slightly lower than that of Example 2, even though the peak rate of heat release and the total heat released are higher than those of Example 2.

Comparative Example 3

[0178] An alternative resin formulation as shown in Table 2 was used as Comparative Example 3 (which had the applicant's product code SPX26424). As compared to Examples 1, 2, 3 and 4, a higher concentration of expandable flake graphite was present in the epoxide resin, i.e. 7.2 wt % based on the weight of the total epoxide resin.

[0179] The resin of Comparative Example 3 exhibited worse heat release and intumescent properties than the Examples. It may be seen from Table 2 that the resin of Comparative Example 3 exhibited a higher MAHRE, 84 kWm.sup.−2, a higher peak rate of heat release, 133 kWm.sup.−2, and a higher total heat released, 3.6 MJm.sup.−2, than Examples 1 and 2. The height of the intumescent char of Comparative Example 1 was only 6.4 mm, lower than for Examples 1, 2, 3 and 4.

[0180] As for Comparative Example 2, in Comparative Example 3 due to outlier results in the measured data fewer than 5 test coupons were tested.

[0181] These tested FST and mechanical properties showed that the epoxide resin of the present invention, when used to form prepregs that are subsequently used to form fibre-reinforced cured epoxy resin matrix composite materials, for example in the form of panels, can exhibit good mechanical properties, in conjunction with good FST properties.

Comparative Example 4

[0182] As a further comparative example FIG. 3 shows an isothermal DSC cure conversion graph for the DOPO-based mixed resin system disclosed in the Applicant's earlier WO-A-2011/015611. The tested formulation is in Table 3 as Comparative Example 4. For that known DOPO-based mixed resin system, as can be seen from FIG. 3, the cure conversion is only <80% after 16 hours at 95° C. The known DOPO-based resin system had a minimum cure temperature of 95° C., and a cure dwell time at that minimum cure temperature of 16 hours. Alternatively, when the resin system of Comparative Example 4 was subjected to a faster cure at a higher temperature of 140° C., the cure dwell time at the faster cure temperature was 120 minutes.

[0183] In other words, the resin system of Examples 1 and 2 provided a lower temperature and more complete cure that the known DOPO-based mixed resin system of Comparative Example 4.

Comparative Example 5

[0184] Referring to Table 3, Comparative Example 5 was an epoxide resin system that, as compared to Examples 1 and 2, included a resin system blend of epoxide resins that were unable to accommodate a large filler content system because the epoxide resins comprised a blend of only a semi-solid bisphenol-A epoxy resin and a solid bisphenol-A epoxy resin. The melamine, aluminium polyphosphate and zinc borate fillers as fire retardant additives were each present in a lower concentration than for the corresponding first, second and third fire retardant additives in Examples 1 and 2, because the higher resin viscosity in Comparative Example 5 limited the effective concentrations of these fillers that could be practically incorporated into the epoxide resin system.

Comparative Example 6

[0185] In contrast to Comparative Example 1, the same panels were made using the same glass fabric and number of plies but instead of the epoxide resin of Examples 1 and 2 and Comparative Example 1 a typical phenolic resin having FST properties was employed. The mechanical properties of the cured phenolic resin panels were tested. An 8 ply 7781 glass fabric monolithic panel was made and the Interlaminar Shear Strength (ILSS) was tested; the value was 34 MPa. The same panel was tested for flexural strength and flexural modulus; the value of flexural strength was 542 MPa and the value of flexural modulus was 24 GPa. Furthermore, a sandwich panel having a two ply skin with the same glass fabric was made and the Climbing Drum Peel Strength was tested; the value was 100 N/75 mm.

[0186] A comparison of the tested FST and mechanical properties for Examples 1 to 4 and Comparative Example 6 showed that the epoxide resin of the present invention, when used to form prepregs that are subsequently used to form fibre-reinforced cured epoxy resin matrix composite materials, for example in the form of panels, can exhibit improved mechanical properties, in conjunction with good FST properties, and an overall improved performance as compared to phenolic resin panels. In particular, the improved mechanical properties as compared to the phenolic resin panel can enable a reduced weight epoxy resin panel to replace a phenolic resin panel with equivalent mechanical performance. Furthermore, the epoxide resin of the present invention also provides, as compared to phenolic resins, lower toxicity, since the epoxy resin is free of phenol and formaldehyde, improved surface finish and improved processing since the epoxy resin does not release water and/or volatile materials when curing.

TABLE-US-00001 TABLE 1 Example 1 Example 2 Example 3 Example 4 SPX26426 SPX26425 SPX26663 SPX26665 Formulation-wt % Semi-solid 9.7 9.7 9.7 9.7 epoxy novolac resin Solid bisphenol-A 20.7 20.7 20.7 20.7 epoxy resin Solid epoxy novolac 9.6 9.6 9.6 9.6 resin Liquid bisphenol-A 18.1 18.1 18.1 18.1 epoxy resin Hydrophobic fumed 1.0 1.0 1.0 1.0 silica Titanium dioxide 0.5 0.5 0.5 0.5 Melamine 4.6 4.6 4.6 4.6 Ammonium 28.9 28.9 28.9 28.9 polyphosphate Microperl ™ glass beads 6.9 6.9 6.9 6.9 Grade 3538 Expandable 0.9 1.8 0.09 0.45 Flake Graphite Properties MAHRE (kW/m.sup.2) 42 59 Not Not Measured Measured Peak Rate of Heat 73 82 Not Not Release (kW/m.sup.2) Measured Measured Total Heat Released 1.6 2.5 Not Not (MJ/m.sup.2) Measured Measured Height of Intumescent 19.3 13.0 18.8 14.5 Char (mm)

TABLE-US-00002 TABLE 2 Comp. Comp. Comp. Example 1 Example 2 Example 3 SPX25211 SPX26196 SPX26424 Formulation-wt% Semi-solid 9.7 9.7 9.7 epoxy novolac resin Solid bisphenol-A 20.7 20.7 20.7 epoxy resin Solid 9.6 9.6 9.6 epoxy novolac resin Liquid bisphenol-A 18.1 18.1 18.1 epoxy resin Hydrophobic fumed 1.0 1.0 1.0 silica Titanium dioxide 0.5 0.5 0.5 Melamine 4.6 4.6 4.6 Ammonium 28.9 28.9 28.9 polyphosphate Microperl ™ glass beads 6.9 6.9 6.9 Grade 3538 Expandable 0 3.6 7.2 Flake Graphite Properties MAHRE (kW/m.sup.2) 65 58 84 Peak Rate of Heat 124 96 133 Release (kW/m.sup.2) Total Heat Released 4.5 2.7 3.6 (MJ/m.sup.2) Height of Intumescent 5.6 11.4 6.4 Char (mm)

TABLE-US-00003 TABLE 3 Comparative Comparative Example 4 Example 5 Formulation-wt % Semi-solid bisphenol-A 44.6 43.3 epoxy resin Solid bisphenol-A 8.9 8.6 epoxy resin Hydrophobic fumed 1.0 1.0 Silica Aluminium trihydrate 15.6 0 filler Red phosphorous 21.9 21.3 Melamine 0 2.9 Ammonium polyphosphate 4.0 17.6 Zinc borate 4.0 5.3 Properties Melamine/APP/ZB weight ratio 0/1/1 1/6.1/1.8 Resin/fillers in base resin-by 53.5/46.5 51.9/48.1 weight Phosphorus content-wt % 1.3 5.5 Nitrogen content-wt % 0.6 4.5