Polymer pre-laid waterproof rolling material

Abstract

A polymer pre-laid waterproof rolling material, including a polymer base material layer, a pressure-sensitive adhesive layer on the polymer base material layer, and a sand anti-sticking layer on the pressure-sensitive adhesive layer; the pressure-sensitive adhesive layer includes: 25-35 parts by mass of a styrene-isoprene-styrene block copolymer; 32-38 parts by mass of a C5 petroleum resin; 5-12 parts by mass of a 145 pentaerythritol modified rosin resin; 25-32 parts by mass of a naphthenic oil; 0.3 parts by mass of an antioxidant; and 0.5 parts by mass of a UV light stabilizer; the C5 petroleum resin has a softening point of 95-105° C. and a color number of less than 4; the naphthenic oil has a kinematic viscosity of 9-11 mm.sup.2 at 100° C. and a density of 0.8950 g/cm.sup.3-0.9100 g/cm.sup.3 at 20° C. The pressure-sensitive adhesive layer has a stronger bonding effect with sintered sand and further improves the bonding effect with concrete.

Claims

1. A polymer pre-laid waterproof rolling material, wherein the polymer pre-laid waterproof rolling material comprising a polymer base material layer, a pressure-sensitive adhesive layer on the polymer base material layer, a sand anti-sticking layer on the pressure-sensitive adhesive layer, a lapping layer and a release film layer on the lapping layer, wherein there are two pairs of the lapping layer and release film layer, which are respectively positioned at the two ends of the polymer base material layer and are respectively positioned on the upper surface and the lower surface thereof; wherein the pressure-sensitive adhesive layer includes the following components: 25-35 parts by mass of a styrene-isoprene-styrene block copolymer; 32-38 parts by mass of a C5 petroleum resin; 5-12 parts by mass of a 145 pentaerythritol modified rosin resin; 25-32 parts by mass of a naphthenic oil; 0.3 parts by mass of an antioxidant; and 0.5 parts by mass of a UV light stabilizer; the C5 petroleum resin has a softening point of 95-105° C. and a color number of less than 4; the naphthenic oil has a kinematic viscosity of 9-11 mm.sup.2 at 100° C. and a density of 0.8950 g/cm.sup.3-0.9100 g/cm.sup.3 at 20° C.; wherein the lapping layer comprises the following components: 32-38 parts by mass of a styrene-isoprene-styrene block copolymer; 38-47 parts by mass of a hydrogenated C5 resin; 1-8 parts by mass of a terpene phenol resin; 15-20 parts by mass of polyisobutylene; 0.3 parts by mass of an antioxidant; and 0.5 parts by mass of a UV light stabilizer; the hydrogenated C5 resin has a softening point of 95-105° C. and a color number of 0, the terpene phenol resin has a softening point of 115° C., and the average molecular weight of the polyisobutylene is 1000.

2. The polymer pre-laid waterproof rolling material according to claim 1, wherein the melting index of the styrene-isoprene-styrene block copolymer of the pressure-sensitive adhesive layer is 10-15 g/10 min at 200° C., and the styrene-isoprene-styrene block copolymer of the pressure-sensitive adhesive layer contains 15-16 parts by mass of styrene, and has a diblock content of 50-60 parts by mass.

3. The polymer pre-laid waterproof rolling material according to claim 1, wherein the production process of the pressure-sensitive adhesive layer includes: step i: adding the naphthenic oil, setting the heat transfer oil in the heating equipment to 180° C., the material temperature to 180° C., and the stirring frequency to 10 Hz; step ii: when the material temperature is increased to 120° C., adding the C5 petroleum resin and the 145 pentaerythritol modified rosin resin, wherein the stirring frequency is 25 Hz; step iii, adding a rubber when the material temperature is increased to 145° C.-150° C., wherein the stirring frequency is 40 Hz; and step iv: starting vacuumizing the same when the material temperature is increased to 160° C., and discharging the same when the material temperature rises to 180±5° C.

4. The polymer pre-laid waterproof rolling material according to claim 1, wherein the pressure-sensitive adhesive layer has a thickness of 0.25 mm-0.6 mm.

5. The polymer pre-laid waterproof rolling material according to claim 1, wherein the sand anti-sticking layer is selected from a modified mullite.

6. The polymer pre-laid waterproof rolling material according to claim 5, wherein the modified mullite sand has been subjected to a surface treatment, the particle diameter is 0.3-0.5 mm, and the color of the sand particles is light yellow.

7. The polymer pre-laid waterproof rolling material according to claim 1, wherein when the sand anti-sticking layer is laminated with the pressure-sensitive adhesive layer, the surface temperature of the pressure-sensitive adhesive layer is 70° C., and the pressure of the pressure roller is ≥0.3 MPa.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) In order to illustrate the technical solutions in the particular embodiments of the present invention or in the prior art more clearly, the accompanying drawings to be used in the description of the particular embodiments or the prior art will be briefly introduced below; obviously, the accompanying drawings in the following description show some of the embodiments of the present invention, and those of ordinary skill in the art may still derive other drawings from these accompanying drawings without creative effort.

(2) FIG. 1 is a schematic structural diagram of the waterproof rolling material provided in an embodiment of the present invention.

(3) Reference numbers in the drawings: 1—Polymer substrate layer; 2—Pressure-sensitive adhesive layer; 3—Sand anti-sticking layer; 4—Lapping layer; 5—Release film layer.

DETAILED DESCRIPTION OF EMBODIMENTS

(4) The technical solutions in the present invention will be described clearly and completely below with reference to the drawings; obviously, the described embodiments are some of, rather than all of, the embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by those of ordinary skill in the art without involving any inventive effort fall within the scope of protection of the present invention.

(5) The polymer pre-laid waterproof rolling material of the present application comprises a polymer base material layer 1, a pressure-sensitive adhesive layer 2 on the polymer base layer 1, and a sand release layer 3 on the adhesive layer, as shown in FIG. 1;

(6) the pressure-sensitive adhesive layer 2 comprises the following components:

(7) 25-35 parts by mass of a styrene-isoprene-styrene block copolymer;

(8) 32-38 parts by mass of a C5 petroleum resin;

(9) 5-12 parts by mass of a 145 pentaerythritol modified rosin resin;

(10) 25-32 parts by mass of a naphthenic oil;

(11) 0.3 parts by mass of an antioxidant; and

(12) 0.5 parts by mass of a UV light stabilizer;

(13) the C5 petroleum resin has a softening point of 95-105° C. and a color number of less than 4; the naphthenic oil has a kinematic viscosity of 9-11 mm.sup.2 at 100° C. and a density of 0.8950 g/cm.sup.3-0.9100 g/cm.sup.3 at 20° C.

(14) Specifically, the melting index of the styrene-isoprene-styrene block copolymer is 10-15 g/10 min at 200° C., and the styrene-isoprene-styrene block copolymer contains 15-16 parts by mass of styrene, and has a diblock content of 50-60 parts by mass.

(15) Specifically, the production process of the pressure-sensitive adhesive layer 2 includes:

(16) step i: adding the naphthenic oil, setting the heat transfer oil in the heating equipment to 180° C., the material temperature to 180° C., and the stirring frequency to 10 Hz;

(17) step ii: when the material temperature is increased to 120° C., adding the C5 petroleum resin and the 145 pentaerythritol modified rosin resin, wherein the stirring frequency is 25 Hz;

(18) step iii, adding a rubber when the material temperature is increased to 145° C.-150° C., wherein the stirring frequency is 40 Hz; and

(19) step iv: starting vacuumizing same when the material temperature is increased to 160° C., and discharging same when the material temperature rises to 180±5° C.

(20) Specifically, the pressure-sensitive adhesive layer 2 has a thickness of 0.25 mm-0.6 mm, more preferably 0.3 mm 0.4 mm, most preferably 0.35 mm.

(21) Specifically, the sand anti-sticking layer 3 is selected from a modified mullite.

(22) Specifically, the modified mullite sand has been subjected to a surface treatment, the particle diameter is 0.3-0.5 mm, and the color of the sand is light yellow; it can reduce reflectance and prevent human eyes from being damaged during large-area construction.

(23) Specifically, when the sand anti-sticking layer 3 is laminated with the pressure-sensitive adhesive layer 2, the surface temperature of the pressure-sensitive adhesive layer 2 is 70° C., and the pressure of the pressure roller is ≥0.3 MPa.

(24) Specifically, the material also comprises a lapping layer 4 and a release film layer 5 on the lapping layer, wherein there are two pairs of the lapping layer 4 and release film layer 5, which are respectively positioned at the two ends of the polymer substrate layer 1 and are respectively positioned on the upper surface and the lower surface thereof; the release film layer 5 is made of materials such as the polyethylene release film and polyethylene terephthalate, and the thickness of the overlapping layer 4 is 0.3-0.5 mm.

(25) Specifically, the lapping layer 4 comprises the following components:

(26) 32-38 parts by mass of a styrene-isoprene-styrene block copolymer;

(27) 38-47 parts by mass of a hydrogenated C5 resin;

(28) 1-8 parts by mass of a terpene phenol resin;

(29) 15-20 parts by mass of polyisobutylene;

(30) 0.3 parts by mass of an antioxidant; and

(31) 0.5 parts by mass of a UV light stabilizer;

(32) the hydrogenated C5 resin has a softening point of 95-105° C. and a color number of 0, the terpene phenol resin has a softening point of 115° C., and the average molecular weight of the polyisobutylene is 1000.

(33) Specifically, the lapping layer 4 contains the same components as that of the pressure-sensitive adhesive layer 2.

(34) The present invention relates to a polymer pre-laid waterproof rolling material, wherein the polymer base material layer 1 mainly has a waterproof function and can be selected from one or a combination of more of polyethylene, polypropylene, an ethylene-olefin copolymer, an ethylene-vinyl acetate copolymer, polyvinyl acetate, polyethyl acrylate, polytetrafluoroethylene, polyvinylidene fluoride, polyethylene terephthalate, polyvinyl chloride and polyamide, preferably polyethylene, polypropylene and an ethylene-olefin copolymer, more preferably polyethylene, an ethylene-olefin copolymer, polyethylene terephthalate, and most preferably polyethylene; the pressure sensitive adhesive layer 2 serves to connect the base material layer and the sand layer, and to bond concrete during the construction, and can be selected from one or more of a butyl rubber-based adhesive, a polyisobutylene-based adhesive, a butyl adhesive, an acrylic adhesive and a styrene block copolymer adhesive.

(35) The styrene-isoprene-styrene block copolymer contained in the lapping layer 4 has a melt index of 25-30 g/10 min at 200° C. and a specific composition of 14-15 parts by mass of styrene; The diblock content is 40-60 parts by mass.

(36) The production method of the lapping layer 4 involves: step I: adding polyisobutene PIB, setting the temperature of the heat transfer oil to 180° C., the material temperature to 180° C., and the stirring frequency to 10 Hz; step II: when the material TEMP is increased to 120° C., adding a hydrogenated C5 resin and a terpene phenol resin, and set stirring frequency to 25 Hz; and step III: adding a styrene-isoprene-styrene block copolymer when the material temperature is increased to 145-150° C., wherein the stirring speed is 40 Hz; starting vacuumizing same when the material temperature is increased to 160° C., and discharging same when the material temperature is increased to 180±5° C.

(37) Five groups of experiments are selected for comparison according to different proportions of the two components of the pressure-sensitive adhesive layer 2 to prove that the technical scheme as claimed by the present application has better technical effects:

(38) Experiment 1

(39) The specific formulation ratio is: a mass ratio of styrene-isoprene-styrene block copolymer:C5 petroleum resin:145 Pentaerythritol modified rosin resin:naphthenic oil:antioxidant:UV light stabilizer=26:34:10:30:0.3:0.5;

(40) Experiment 2

(41) The specific formulation ratio is: a mass ratio of styrene-isoprene-styrene block copolymer:C5 petroleum resin:145 Pentaerythritol modified rosin resin:naphthenic oil:antioxidant:UV light stabilizer=37:33:5:25:0.3:0.5;

(42) Experiment 3

(43) The specific formulation ratio is: a mass ratio of styrene-isoprene-styrene block copolymer:C5 petroleum resin:145 Pentaerythritol modified rosin resin:naphthenic oil:antioxidant:UV light stabilizer=25:42:8:25:0.3:0.5;

(44) Experiment 4

(45) The specific formulation ratio is: a mass ratio of styrene-isoprene-styrene block copolymer:C5 petroleum resin:145 Pentaerythritol modified rosin resin:naphthenic oil:antioxidant:UV light stabilizer=30:38:3:29:0.3:0.5;

(46) Experiment 5

(47) The specific formulation ratio is: a mass ratio of styrene-isoprene-styrene block copolymer:C5 petroleum resin:145 Pentaerythritol modified rosin resin:naphthenic oil:antioxidant:UV light stabilizer=25:32:8:35:0.3:05.

(48) The experimental results are as shown in Table 1:

(49) TABLE-US-00001 TABLE 1 Experimental results of pressure-sensitive adhesive components at different ratios Chinese Experi- Experi- Experi- Experi- Experi- Item standard ment 1 ment 2 ment 3 ment 4 ment 5 Heat resistance 80° C., 2 Pass Pass Pass Pass Not hours No accepted flowing Low temperature flexibility Adhesive Pass Pass Pass Pass Pass layer −25° C., No crack Low temperature flexibility Adhesive Pass Pass Not Pass Pass after heat aging layer accepted −23° C., No crack Peeling No treatment ≥1.5 2.88 1.48 2.36 1.32 1.22 strength with Soaking ≥1.0 2.32 0.98 1.98 0.88 1.01 post-casted treatment concrete Sediment- ≥1.0 2.76 1.56 2.35 1.02 1.18 (N/mm) contaminated surface Ultraviolet ≥1.0 2.54 1.40 2.02 0.78 1.13 light treatment Heat treatment ≥1.0 2.48 1.66 2.22 1.06 1.24 Peeling strength with post- ≥1.0 2.23 1.02 2.05 0.56 0.96 casted concrete after soaking (N/mm) Peeling No treatment ≥0.8 1.88 1.20 1.48 0.87 0.88 strength with Soaking ≥0.8 1.56 1.05 1.32 0.79 0.86 rolling treatment material (lapping edge) (N/mm)

(50) It can be seen form Table 1 that

(51) In Experiment 1, the ratios as claimed by the present application are selected, and all the performances meet the requirements;

(52) In experiment 2, although the strength of the pressure-sensitive adhesive can be increased by increasing the amount of an SIS rubber, the sand embedding degree is deteriorated and the peeling force is deteriorated;

(53) In Experiment 3, increasing the amount of petroleum resin causes the pressure sensitive adhesive to harden, which leads to not accepted low temperature performance after thermal aging;

(54) In experiment 4, the amount of the rosin resin is reduced, resulting in poor initial adhesion of the pressure sensitive adhesive, poor adhesion of the sand and the gum layer, and a decreased peeling force; and

(55) In experiment 5, the amount of the plasticizer naphthenic oil is increased such that the cohesive force of the pressure sensitive adhesive is decreased, which leads to the pressure-sensitive adhesive failing to meet the requirements of a high temperature.

(56) Five groups of experiments are selected for comparison according to different ratios of the four components of the lapping layer 4 to prove that the technical solution as claimed by the application has better technical effects:

(57) Experiment 6

(58) The specific formulation ratio is: a mass ratio of styrene-isoprene-styrene block copolymer:hydrogenated C5 resin:terpene phenol resin:polyisobutylene PIB:antioxidant:UV light stabilizer=37:42:3:18:0.3:0.5;

(59) Experiment 7

(60) The specific formulation ratio is: a mass ratio of styrene-isoprene-styrene block copolymer:hydrogenated C5 resin:terpene phenol resin:polyisobutylene PIB:antioxidant:UV light stabilizer=30:45:7:18:0.3:0.5;

(61) Experiment 8

(62) The specific formulation ratio is: a mass ratio of styrene-isoprene-styrene block copolymer:hydrogenated C5 resin:terpene phenol resin:polyisobutylene PIB:antioxidant:UV light stabilizer=32:49:6:15:0.3:0.5;

(63) Experiment 9

(64) The specific formulation ratio is: a mass ratio of styrene-isoprene-styrene block copolymer:hydrogenated C5 resin:terpene phenol resin:polyisobutylene PIB:antioxidant:UV light stabilizer=37:38:10:15:0.3:0.5;

(65) Experiment 10

(66) The specific formulation ratio is: a mass ratio of styrene-isoprene-styrene block copolymer:hydrogenated C5 resin:terpene phenol resin:polyisobutylene PIB antioxidant:UV light stabilizer=32:42:4:22:0.3:05.

(67) The high-temperature persistent adhesivity experiment of different components above the lapping layer 4 is carried out in an oven at 50° C. The lapping layer 4 is cut into a width of 5 cm, the lapping length is 7.5 cm, and the weight at the bottom of the sample is 1 kg after lapping. The results of the high-temperature persistent adhesivity experiment are as shown in Table 2:

(68) TABLE-US-00002 Experiment Experiment Experiment Experiment Experiment Item 6 7 8 9 10 High temperature Day 20 Day 3 Day 5 Day 10 Day 2 persistent adhesivity at 50° C. Phenomenon Good Lapping Lapping Lapping Lapping adhesion opening breaking opening slipping

(69) Table 2 Experimental Results of Different Ratios of Lapping Layer Components

(70) It can be seen from Table 2 that

(71) Experiment 6: experiment 6 shows the best lapping performance;

(72) Experiment 7: the amount of the styrene-isoprene-styrene block copolymer is decreased such that the adhesive strength of the lapping layer 4 is decreased, and the lapping opening occurs after a period of time;

(73) Experiment 8: the amount of the hydrogenated C5 resin is increased such that the lapping layer 4 get hardened, and under the conditions of a high temperature, an opening appears at the lapping part and then slow breaking occurs;

(74) Experiment 9: the amount of the terpene phenol resin is increased, and after a long period of time, the lapping layer 4 is aged and cracks appears at the lapping edge with shedding; and

(75) Experiment 10: the amount of the polyisobutylene PIB becomes larger such that the cohesive force of the lapping layer 4 is decreased, and the adhesive layer slips off and separates apart with respect to the high-temperature persistent adhesivity.

(76) It should be finally noted that, the above embodiments are merely used for illustrating, rather than limiting, the technical solution of the present invention; although the present invention has been described in detail with reference to the foregoing embodiments, it should be understood by those of ordinary skill in the field; the technical solutions specified in the foregoing embodiments could still be modified, or some or all of the technical features thereof may be equivalently replaced; and the modifications or replacements do not make the essence of corresponding technical solutions depart from the scope of the technical solution of the embodiments of the present invention.