ELASTIC FLAME-RETARDANT POLYMER-ENCAPSULATED ANODE PARTICLES FOR LITHIUM BATTERIES AND METHOD OF MANUFACTURING
20220246937 · 2022-08-04
Assignee
Inventors
Cpc classification
C08F220/14
CHEMISTRY; METALLURGY
C08L39/04
CHEMISTRY; METALLURGY
C08G79/04
CHEMISTRY; METALLURGY
C08L43/02
CHEMISTRY; METALLURGY
C08F220/14
CHEMISTRY; METALLURGY
H01M10/0525
ELECTRICITY
International classification
H01M4/62
ELECTRICITY
C08G79/04
CHEMISTRY; METALLURGY
Abstract
A composite particulate for a lithium battery, wherein the composite particulate has a diameter from 10 nm to 50 μm and comprises one or more than one anode active material particles that are dispersed in a high-elasticity polymer matrix or encapsulated by a high-elasticity polymer shell, wherein the high-elasticity polymer matrix or shell has a recoverable elastic tensile strain no less than 5%, when measured without an additive or reinforcement dispersed therein, and a lithium ion conductivity no less than 10.sup.−8 S/cm at room temperature and wherein the high-elasticity polymer comprises a polymer derived from a monomer selected from the group consisting of phosphates, phosphonates, phosphonic acids, phosphorous acid, phosphites, phosphoric acids, combinations thereof, and combination thereof with phosphazenes. These polymers are also highly flame-resistant.
Claims
1. A composite particulate for a lithium battery, wherein said composite particulate has a diameter from 10 nm to 50 μm and comprises one or more than one anode active material particles that are dispersed in a high-elasticity polymer matrix or encapsulated by a high-elasticity polymer shell, wherein said high-elasticity polymer matrix or shell has a recoverable elastic tensile strain no less than 5%, when measured without an additive or reinforcement dispersed therein, and a lithium ion conductivity no less than 10.sup.−8 S/cm at room temperature and wherein said high-elasticity polymer comprises a polymer derived from a monomer selected from the group consisting of phosphates, phosphonates, phosphoric acids, phosphorous acid, phosphites, phosphoric acids, combinations thereof, and combination thereof with phosphazenes.
2. The composite particulate of claim 1, wherein the polymer derived from phosphoric acid comprises chains of a polyester of phosphoric acid represented by the following structure: ##STR00021## wherein 2<x≤10, R is selected from Li, H, a methyl, ethyl, propyl, vinyl, allyl, acrylate, phenol, alkyl, aryl, or CH.sub.2Cl, and R′ or R″ is independently selected from Li, CH.sub.3, C.sub.2H.sub.5, n-C.sub.3H.sub.7, i-C.sub.3H.sub.7; n-C.sub.4H.sub.9, CCl.sub.3CH.sub.2, C.sub.6H.sub.5, —OH, —COOH, —O—CH.sub.2CH.sub.2—R′″, an alkyl, or an aryl, where R′″═—(CH.sub.2).sub.yCH.sub.3 and 0≤y≤10.
3. The composite particulate of claim 1, wherein the monomer is selected from the group consisting of 2-alkoxy (or phenoxy)-2-oxo-1,3,2-dioxaphospholane (I) and 2-alkoxy (or phenoxy)-2-oxo-1,3,2-dioxaphosphorinane (II), derivatives thereof, and combinations thereof: ##STR00022##
4. The composite particulate of claim 1, wherein the phosphate, phosphonate, phosphonic acid, or phosphite is selected from TMP, TEP, TDP, DPOF, DMMP, DMMEMP, tris(trimethylsilyl)phosphite (TTSPi), alkyl phosphate, triallyl phosphate (TAP), a combination thereof, wherein TMP, TEP, TEP, TDP DPOF, DMMP, and DMMEMP have the following chemical formulae: ##STR00023## wherein end groups comprise unsaturation for polymerization.
5. The composite particulate of claim 1, wherein the monomer comprises phosphonate vinyl monomer selected from the group consisting of phosphonate bearing allyl monomers, phosphonate bearing vinyl monomers, phosphonate bearing styrenic monomers, phosphonate bearing (meth)acrylic monomers, vinylphosphonic acids, and combinations thereof.
6. The composite particulate of claim 5, wherein the phosphonate bearing allyl monomer is selected from a Dialkyl allylphosphonate monomer or Dioxaphosphorinane allyl monomer; the phosphonate bearing vinyl monomers is selected from a Dialkyl vinyl phosphonate monomer or Dialkyl vinyl ether phosphonate monomer; the phosphonate bearing styrenic monomer is selected from α-, β-, or p-vinylbenzyl phosphonate monomers; or the phosphonate bearing (meth)acrylic monomer is selected from a monomer having a phosphonate group linked to the acrylate double bond, a phosphonate groups linked to the ester, or a phosphonate groups linked to the amide.
7. The composite particulate of claim 1, wherein said high-elasticity polymer contains a cross-linked network of chains crosslinked by a crosslinking agent to a degree of crosslinking that imparts an elastic tensile strain from 5% to 500%.
8. The composite particulate of claim 7, wherein said crosslinking agent is selected from poly(diethanol) diacrylate, poly(ethyleneglycol)dimethacrylate, poly(diethanol) dimethylacrylate, poly(ethylene glycol) diacrylate, N,N-methylene bisacrylamide, epichlorohydrin, 1,4-butanediol diglycidyl ether, tetrabutylammonium hydroxide, cinnamic acid, ferric chloride, aluminum sulfate octadecahydrate, diepoxy, dicarboxylic acid compound, poly(potassium 1-hydroxy acrylate) (PKHA), glycerol diglycidyl ether (GDE), ethylene glycol, polyethylene glycol, polyethylene glycol diglycidyl ether (PEGDE), citric acid, acrylic acid, methacrylic acid, a derivative compound of acrylic acid, a derivative compound of methacrylic acid, glycidyl functions, N,N′-Methylenebisacrylamide (MBAAm), Ethylene glycol dimethacrylate (EGDMAAm), isobornyl methacrylate, poly (acrylic acid) (PAA), methyl methacrylate, isobornyl acrylate, ethyl methacrylate, isobutyl methacrylate, n-Butyl methacrylate, ethyl acrylate, 2-Ethyl hexyl acrylate, n-Butyl acrylate, a diisocyanate, an urethane chain, a chemical derivative thereof, or a combination thereof.
9. The composite particulate of claim 7, wherein the crosslinking agent comprises a compound having at least one reactive group selected from a phenylene group, a hydroxyl group, an amino group, an imino group, an amide group, an acrylic amide group, an amine group, an acrylic group, an acrylic ester group, or a mercapto group in the molecule.
10. The composite particulate of claim 1, wherein the polymer is synthesized with an initiator selected from an azo compound, azobisisobutyronitrile, azobisisoheptonitrile, dimethyl azobisisobutyrate, benzoyl peroxide tert-butyl peroxide and methyl ethyl ketone peroxide, benzoyl peroxide (BPO), bis(4-tert-butylcyclohexyl)peroxydicarbonate, t-amyl peroxypivalate, 2,2′-azobis-(2,4-dimethylvaleronitrile), 2,2′-azobis-(2-methylbutyronitrile), 1,1-azobis(cyclohexane-1-carbonitrile, benzoylperoxide (BPO), hydrogen peroxide, dodecamoyl peroxide, isobutyryl peroxide, cumene hydroperoxide, Cert-butyl peroxypivalate, diisopropyl peroxydicarbonate, lithium hexafluorophosphate (LiPF.sub.6), lithium borofluoride (LiBF.sub.4), lithium hexafluoroarsenide (LiAsF.sub.6), lithium trifluoro-metasulfonate (LiCF.sub.3SO.sub.3), bis-trifluoromethyl sulfonylimide lithium (LiN(CF.sub.3SO.sub.2).sub.2), lithium bis(oxalato)borate (LiBOB), lithium oxalyldifluoroborate (LiBF.sub.2C.sub.2O.sub.4), lithium oxalyldifluoroborate (LiBF.sub.2C.sub.2O.sub.4), or a combination thereof.
11. The composite particulate of claim 1, wherein said high-elasticity polymer matrix or shell further contains from 0.01% to 30% by weight of a graphite, graphene, or carbon material dispersed therein.
12. The composite particulate of claim 11, wherein said graphite, graphene, or carbon material is selected from polymeric carbon, amorphous carbon, chemical vapor deposition carbon, coal tar pitch, petroleum pitch, meso-phase pitch, carbon black, coke, acetylene black, activated carbon, graphite particles, carbon particles, meso-phase microbeads, carbon or graphite fibers, carbon nanotubes, carbon nano-fibers, graphitic nano-fibers, graphene sheets, or a combination thereof and said graphite, graphene, or carbon material forms a 3D network of electron-conducting pathways that are in electronic contacts with said anode material particles.
13. The composite particulate of claim 1, wherein said anode active material is selected from the group consisting of: (a) silicon (Si), germanium (Ge), tin (Sn), lead (Pb), antimony (Sb), phosphorus (P), bismuth (Bi), zinc (Zn), aluminum (Al), titanium (Ti), nickel (Ni), cobalt (Co), and cadmium (Cd); (b) alloys or intermetallic compounds of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Ni, Co, or Cd with other elements; (c) oxides, carbides, nitrides, sulfides, phosphides, selenides, and tellurides of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Fe, Ni, Co, V, or Cd, and their mixtures, composites, or lithium-containing composites; (d) salts and hydroxides of Sn; (e) lithium titanate, lithium manganate, lithium aluminate, lithium titanium niobium oxide, lithium-containing titanium oxide, lithium transition metal oxide, ZnCo.sub.2O.sub.4; (f) carbon or graphite particles (g) prelithiated versions thereof; and (h) combinations thereof.
14. The composite particulate of claim 1, wherein said anode active material contains a prelithiated Si, prelithiated Ge, prelithiated Sn, prelithiated SnO.sub.x, prelithiated SiO.sub.x, prelithiated iron oxide, prelithiated V.sub.2O.sub.5, prelithiated V.sub.3O.sub.8, prelithiated Co.sub.3O.sub.4, prelithiated Ni.sub.3O.sub.4, or a combination thereof, wherein x=1 to 2.
15. The composite particulate of claim 1, wherein said anode active material particles, the composite particulates, or both are porous.
16. The composite particulate of claim 1, wherein one or a plurality of said particles is coated with a layer of carbon or graphene disposed between said one or said plurality of particles and said high-elasticity polymer matrix.
17. The composite particulate of claim 1, wherein said high-elasticity polymer has a lithium ion conductivity from 10.sup.−6 S/cm to 10.sup.−2 S/cm.
18. The composite particulate of claim 1, wherein said composite particulate is further coated with or encapsulated by a shell of a conducting material selected from carbon, graphene, a conducting polymer, a conducting composite, or a combination thereof.
19. The composite particulate of claim 1, wherein said high-elasticity polymer matrix or shell further comprises from 0.1% to 50% by weight of a lithium ion-conducting additive dispersed therein.
20. The composite particulate of claim 1, wherein said high-elasticity polymer forms a mixture or co-polymer with an elastomer selected from natural polyisoprene, synthetic polyisoprene, polybutadiene, chloroprene rubber, polychloroprene, butyl rubber, styrene-butadiene rubber, nitrile rubber, ethylene propylene rubber, ethylene propylene diene rubber, epichlorohydrin rubber, polyacrylic rubber, silicone rubber, fluorosilicone rubber, perfluoroelastomers, polyether block amides, chlorosulfonated polyethylene, ethylene-vinyl acetate, thermoplastic elastomer, protein resilin, protein elastin, ethylene oxide-epichlorohydrin copolymer, polyurethane, urethane-urea copolymer, or a combination thereof.
21. The composite particulate of claim 1, wherein said high-elasticity polymer contains a lithium ion-conducting additive dispersed therein wherein said lithium ion-conducting additive is selected from Li.sub.2CO.sub.3, Li.sub.2O, Li.sub.2C.sub.2O.sub.4, LiOH, LiX, ROCO.sub.2Li, HCOLi, ROLi, (ROCO.sub.2Li).sub.2, (CH.sub.2OCO.sub.2Li).sub.2, Li.sub.2S, Li.sub.xSO.sub.y, or a combination thereof, wherein X═F, Cl, I, or Br, R=a hydrocarbon group, 0<x≤1, 1≤y≤4.
22. The composite particulate of claim 1, wherein said high-elasticity polymer further comprises a lithium ion-conducting additive dispersed therein and said additive is selected from lithium perchlorate (LiClO.sub.4), lithium hexafluorophosphate (LiPF.sub.6), lithium borofluoride (LiBF.sub.4), lithium hexafluoroarsenide (LiAsF.sub.6), lithium trifluoro-methanesulfonate (LiCF.sub.3SO.sub.3), bis-trifluoromethyl sulfonylimide lithium (LiN(CF.sub.3SO.sub.2).sub.2), lithium bis(oxalato)borate (LiBOB), lithium oxalyldifluoroborate (LiBF.sub.2C.sub.2O.sub.4), lithium nitrate (LiNO.sub.3), Li-fluoroalkyl-phosphate (LiPF.sub.3(CF.sub.2CF.sub.3).sub.3), lithium bisperfluoro-ethylsulfonylimide (LiBETI), lithium bis(trifluoromethanesulfonyl)imide, lithium bis(fluorosulfonyl)imide, lithium trifluoromethanesulfonimide (LiTFSI), an ionic liquid-based lithium salt, or a combination thereof.
23. The composite particulate of claim 1, wherein said anode active material is lithiated to contain from 0.1% to 54.7% by weight of lithium.
24. An anode comprising multiple composite particulates as defined in claim 1 as an anode material.
25. An anode comprising multiple particles of an anode active material and a conductive additive that are dispersed in, bonded by, or encapsulated by a high-elasticity polymer, wherein said high-elasticity polymer has a recoverable elastic tensile strain no less than 5%, when measured without an additive or reinforcement dispersed therein, and a lithium ion conductivity no less than 10.sup.−8 S/cm at room temperature and wherein said high-elasticity polymer comprises a polymer derived from a monomer selected from the group consisting of vinyl sulfite, ethylene carbonate, methyl methacrylate, vinyl acetate, fluorinated monomers having unsaturation for polymerization, sulfones, sulfides, nitriles, sulfates, siloxanes, silanes, and combinations thereof.
26. A process for producing the anode of claim 25, said process comprising (1) dispersing multiple particles of an anode active material and a conductive additive in a precursor polymer solution to form a suspension wherein the precursor solution comprises at least a curing agent dissolved or dispersed in a reactive liquid medium that comprises a monomer or oligomer, wherein the monomer or oligomer is selected from the group consisting of vinyl sulfite, ethylene carbonate, methyl methacrylate, vinyl acetate, fluorinated monomers having unsaturation for polymerization, sulfones, sulfides, nitriles, sulfates, siloxanes, silanes, and combinations thereof; (ii) dispensing and depositing a layer of the suspension onto a solid substrate surface; and (iii) curing the monomer or oligomer to form the anode.
27. The process of claim 26, further comprising a step of partially or fully removing the liquid solvent before or after step (iii).
28. The process of claim 26, wherein a lithium salt is also dispersed in the precursor polymer solution.
29. The process of claim 26, wherein the reactive liquid medium also includes a non-aqueous liquid solvent.
30. A lithium battery comprising the anode of claim 24, a cathode, and an electrolyte in ionic contact with said anode and said cathode.
31. The lithium battery of claim 30, which is a lithium-ion battery, lithium metal battery, lithium-sulfur battery, lithium-selenium battery, or lithium-air battery.
32. The lithium battery of claim 30, further including a porous separator that electrically isolates said anode from said cathode.
33. A method of manufacturing multiple composite particulates of claim 1, said method comprising: (a) Dispersing multiple particles of an anode active material in a precursor polymer solution to form a suspension wherein these particles are fully embedded or immersed in said precursor solution, which comprises at least a curing agent dissolved or dispersed in a reactive liquid medium that comprises a monomer or oligomer, wherein the monomer or oligomer is selected from the group consisting of vinyl sulfite, ethylene carbonate, methyl methacrylate, vinyl acetate, fluorinated monomers having unsaturation for polymerization, sulfones, sulfides, nitriles, sulfates, siloxanes, silanes, and combinations thereof; (b) operating a secondary particle-forming procedure to shape the suspension into multiple droplets and remove the liquid solvent from the droplets; and (c) curing the monomer or oligomer to form said composite particulates wherein a particulate comprises one or a plurality of anode active material particles that are dispersed and embedded in a polymer matrix or encapsulated by a polymer shell.
34. The method of claim 33, wherein said secondary particle-forming procedure comprises a procedure selected from solution dipping, coating or casting on a solid substrate, pan-coating, air-suspension coating, centrifugal extrusion, vibration-nozzle encapsulation, spray-drying, coacervation-phase separation, interfacial polycondensation or interfacial cross-linking, in-situ polymerization, matrix polymerization, extrusion and palletization, or a combination thereof.
35. The method of claim 33, wherein said suspension in step (a) further comprises an elastomer or its precursor, an electronically conductive polymer or its precursor, a lithium-ion conducting material, a reinforcement material, a foaming or blowing agent, or a combination thereof that is dispersed therein.
36. The method of claim 33, wherein said anode active material particles, prior to step (a), are pre-coated with a layer of carbon, graphene, a conducting polymer, a conducting composite, or a combination thereof.
37. The method of claim 33, wherein the reactive liquid medium also includes a non-aqueous liquid solvent.
Description
BRIEF DESCRIPTION OF THE DRAWINGS
[0056]
[0057]
[0058]
[0059]
[0060]
[0061]
[0062]
[0063]
[0064]
[0065]
[0066]
[0067]
DETAILED DESCRIPTION
[0068] This disclosure provides an anode (negative electrode) comprising composite particulates (each having one or more than one anode active material particles dispersed in a high-elasticity polymer matrix or encapsulated by a shell of high-elasticity polymer) for a lithium secondary battery, which is preferably a secondary battery based on a non-aqueous electrolyte, a polymer gel electrolyte, an ionic liquid electrolyte, a quasi-solid electrolyte, or a solid-state electrolyte. The shape of a lithium secondary battery can be cylindrical, square, button-like, etc. The present disclosure is not limited to any battery shape or configuration or any type of electrolyte. For convenience, we will primarily use Si, Sn, and SnO.sub.2 as illustrative examples of a high-capacity anode active material. This should not be construed as limiting the scope of the disclosure.
[0069] As illustrated in
[0070] In a less commonly used cell configuration, as illustrated in
[0071] In order to obtain a higher energy density cell, the anode in
[0076] In other words, there are several conflicting factors that should be considered concurrently when it comes to the design and selection of an anode active material in terms of material type, shape, size, porosity, and electrode layer thickness. Thus far, there has been no effective solution offered by any prior art teaching to these often conflicting problems. We have solved these challenging issues that have troubled battery designers and electrochemists alike for more than 30 years by developing the multi-functional composite particulates.
[0077] The present disclosure provides a solid powder mass of composite particulates for a lithium battery, wherein at least one of the composite particulates (preferably a majority or all of these particulates or “secondary particles”) has a diameter from 50 nm to 50 μm and comprises a plurality of anode active material particles (the “primary particles”) that are dispersed in a high-elasticity polymer matrix or encapsulated by a shell of high-elasticity polymer having a recoverable tensile strain no less than 5% (typically from 5% to 700% and more typically from 10% to 300%), when measured without an additive or reinforcement, and a lithium ion conductivity no less than 10.sup.−8 S/cm (preferably >10.sup.−4 S/cm, more preferably >10.sup.−3 S/cm) when measured at room temperature. In the structure of a polymer matrix, the polymer forms a continuous material phase. This continuous phase makes physical and ionic contact with all the anode active material particles dispersed in this continuous phase (matrix).
[0078] In certain embodiments, the disclosure provides a composite particulate for a lithium battery, wherein said composite particulate has a diameter from 10 nm to 50 μm and comprises one or more than one anode active material particles that are dispersed in a high-elasticity polymer matrix or encapsulated by a high-elasticity polymer shell, wherein the high-elasticity polymer matrix or shell has a recoverable elastic tensile strain no less than 5%, when measured without an additive or reinforcement dispersed therein, and a lithium ion conductivity no less than 10.sup.−8 S/cm at room temperature and wherein the high-elasticity polymer comprises a polymer derived from a monomer selected from the group consisting of phosphates, phosphonates, phosphonic acids, phosphorous acid, phosphites, phosphoric acids, combinations thereof, and combination thereof with phosphazenes.
[0079] Many of these monomers are not known to be polymerizable and, if polymerized, the products are not known to be sufficiently elastic to protect the anode materials that can undergo large volume expansion.
[0080] The polymer may comprise a polyvinyl phosphonate polymer comprising chains derived from a phosphonate vinyl monomer. The polymer refers to a phosphorus-containing polymer functionalized at the side chain (herein referred to as a polyvinyl phosphonate), instead of that at the main chain or backbone chain (e.g., polyphosphazene having P in the main chain). The polyvinyl phosphonate herein also includes polyvinylphosphonic acid and its various copolymers. The phosphonate vinyl monomer also includes the vinylphosphonic acid monomer.
[0081] The phosphonate vinyl monomer may include allyl-type, vinyl-type, styrenic-type and (meth)acrylic-type monomers bearing phosphonate groups (i.e., either mono or bisphosphonate). In certain embodiments, the phosphonate vinyl monomer is selected from the group consisting of phosphonate bearing allyl monomers (e.g., Dialkyl allylphosphonate monomers and Dioxaphosphorinane allyl monomers), phosphonate bearing vinyl monomers (e.g., Dialkyl vinyl phosphonate monomers and Dialkyl vinyl ether phosphonate monomers), phosphonate bearing styrenic monomers (e.g., α-, β-, and p-vinylbenzyl phosphonate monomers), phosphonate bearing (meth)acrylic monomers (e.g., phosphonate groups linked to the acrylate double bond, phosphonate groups linked to the ester, and phosphonate groups linked to the amide), vinylphosphonic acids, and combinations thereof. Examples of Phosphonate bearing (meth)acrylic monomers include α-(dialkylphosphonate) acrylate, β-(dialkylphosphonate) acrylate, dialkylphosphonate (meth)acrylate, and N-(dialkylphosphonate) (meth)acrylamide.
[0082] In some embodiments, the monomer is selected from phosphate, alkyl phosphonate, phosphazene, phosphit; e.g., tris(trimethylsilyl) phosphite (TTSPi), alkyl phosphate, triallyl phosphate (TAP), or a combination thereof. The phosphate or alkyl phosphonate may be selected from the following:
##STR00004##
wherein end groups or terminal groups comprise unsaturation for polymerization.
[0083] For the desired reactive phosphonate vinyl monomers, phosphonate moieties can be readily introduced into vinyl monomers to produce allyl-type, vinyl-type, styrenic-type and (meth)acrylic-type vinyl monomers bearing phosphonate groups (e.g., either mono or bisphosphonate) in the side chain.
[0084] First example of phosphonate bearing allyl monomers include Dialkyl allylphosphonate monomers, which can be produced by following Reaction schemes 1-3, shown below:
##STR00005##
[0085] The radical homopolymerization of dialkylphosphonate allyl monomers in the presence of chain transfer agents (CTAs) tends to result in low molecular weight oligomers. In order to be efficiently polymerized, dialkylphosphonate allyl monomers have to be involved in radical copolymerizations in the presence of electron-accepting monomers. For instance, low molecular weight copolymers (about 7 000 g mol:1) can be produced by radical copolymerization of diethyl-1-allyl phosphonate with maleic anhydride. These copolymers are a good choice for use as an electrolyte, which shows excellent flame retardant effects.
[0086] As examples of dioxaphosphorinane allyl monomers, dioxaphosphorinanes bearing P-alkyl or P-aryl groups may be synthesized according to the following Reactions 4-5:
##STR00006## ##STR00007##
When R is an alkyl or phenyl group, dioxaphosphorinane allyl monomers can undergo radical polymerization that leads to adducts, especially in the presence of chain transfer agents. These oligomers showed a high content of residue from thermal gravimetric analysis, and thus could be employed as an electrolyte ingredient having good flame retardant characteristics. However, when R═H, a high degree of polymerization could be achieved.
[0087] Examples of phosphonate bearing vinyl monomers include Dialkyl vinyl phosphonate monomers, which can be produced according to Reactions 6-8.
##STR00008##
[0088] Thiol-ene reaction may be used to polymerize vinyl phosphonate monomers by using CTAs. However, it is more efficient to carry out radical copolymerization of diethyl vinyl phosphonate (DEVP) with styrene carried out at 100° C., which can result in copolymers with a high molecular weight. When DEVP is copolymerized with styrene or acrylonitrile in emulsion, copolymers showed Mw values up to 100, 000 g mol/l.
[0089] Dimethyl vinyl phosphonate as examples of Dialkyl vinyl ether phosphonate monomers may be produced according to Reactions 9-10.
##STR00009##
[0090] Vinyl ether monomers are good candidates in order to reach high molecular weight polymers either by cationic homopolymerization or by radical copolymerization (when associated with an electron-accepting monomer). The polymerization may be conducted by reaction of chloroethyl vinyl ether with triethylphosphite.
[0091] As examples of phosphonate bearing styrenic monomers, dimethylvinylbenzyl phosphonate can be produced in a high yield from vinylbenzyl chloride (VBC) according to Reactions 11-12 below:
##STR00010##
The radical homopolymerization of diethylbenzyl phosphonate (DEVP) may be conducted in the presence of chain transfer agents in order to control both the chain length and the chain-end functionality. The p-Vinylbenzyl phosphonate monomers are used in radical copolymerization as a co-monomer, bringing the specific properties of the phosphonate groups. For instance, DEVP-acrylonitrile copolymers are an effective flame-retardant compounds. The phosphonate moieties will act as a nucleophilic non-volatile phosphorus-containing residue, and will be able to promote cross-linking. Indeed, poly(acrylonitrile) cyclizes at high temperatures and thus becomes more thermally stable; this intracyclization is enhanced by the presence of phosphonic species.
[0092] The p-benzyl alkyl phosphonate monomers may participate in radical copolymerization with N-heterocycle monomers, such as 1-vinylimidazole:
##STR00011##
[0093] Phosphonate bearing (meth)acrylic monomers exhibit high reactivity in radical polymerization, due to the activation of the (meth)acrylic double bond by the polar substituent. Phosphonate bearing (meth)acrylic monomers can be classified according to either the double bond (acrylic, acrylonitrile, acrylamide, etc.) or to the phosphonate linkage (linked the double bond, to the ester group, etc.).
[0094] Phosphonate bearing (meth)acrylic monomers may be obtained according to reactions 14-18:
##STR00012##
##STR00013##
[0095] Homopolymerization of β-(dialkylphosphonate) acrylate monomers can be slow but lead to good yields. The reduction of the rate of polymerization may be due to the occurrence of chain transfer processes, which decreases the molecular weight values.
[0096] The initiators for anionic or hulk polymerization of these monomers may be selected from n-C.sub.4H.sub.9Li, (C.sub.5H.sub.5).sub.2Mg, or (i-C.sub.4H.sub.9).sub.3Al, carbenium salts, and certain lithium salts. The reactions may be conducted at a temperature from −60° C. to 30° C., leading to high molecular weights, typically from 3×10.sup.3 to 10.sup.5. Cationic polymerization may be initiated with CF.sub.3S0.sub.3CH.sub.3, CF.sub.3S0.sub.3C.sub.2H.sub.5, (CF.sub.3SO.sub.2)O, Ph.sub.3C.sup.+AsF.sub.6.sup.−, and certain other lithium salts, leading to colored, oily products with number average molecular weights typically up to 10.sup.3.
[0097] In certain embodiments, the high-elasticity polymer comprises chains of a polyester of phosphoric acid, represented by the following structure (Chemical formula 1 or formula 2):
##STR00014##
wherein 2≤x≤10, R is selected from Li, H, a methyl, ethyl, propyl, vinyl, allyl, acrylate, alkyl, aryl, or CH.sub.2Cl, and R′ or R″ is independently selected from Li, CH.sub.3, C.sub.2H.sub.5, n-C.sub.3H.sub.7, i-C.sub.3H.sub.7; n-C.sub.4H.sub.9, CCl.sub.3CH.sub.2, C.sub.6H.sub.5, —OH, —COOH, —O—CH.sub.2CH.sub.2—R′″, an alkyl, or an aryl, where R′″═—(CH.sub.2).sub.yCH.sub.3 and 0≤y≤10.
[0098] The monomers for the preparation of polyester of phosphoric acid may include the two cyclic phosphate esters—phospholanes (I) and phosphorinanes (II)—five- and six-membered cyclic compounds, respectively, and their derivatives. According to the UPAC nomenclature, the names of these compounds are 2-alkoxy (or phenoxy)-2-oxo-1,3,2-dioxaphospholane (I) and 2-alkoxy (or phenoxy)-2-oxo-1,3,2-dioxaphosphorinane (II).
##STR00015##
Phosphonate moieties can be readily introduced into vinyl monomers to produce allyl-type, vinyl-type, styrenic-type and (meth)acrylic-type liquid solvents bearing phosphonate groups (e.g., either mono or bisphosphonate). Examples include diethyl vinylphosphonate, dimethyl vinylphosphonate, vinylphosphonic acid, diethyl allyl phosphate, and diethyl allylphosphonate:
##STR00016##
[0099] Representative monomers for the preparation of a polyester of phosphoric acid include 2-Alk(aryl)oxy-2-oxo-1,3,2-dioxaphospholans:
##STR00017##
wherein R is selected from Li, H, a methyl, ethyl, propyl, vinyl, allyl, acrylate, alkyl, aryl, or CH.sub.2Cl, and R′ is selected from Li, CH.sub.3, C.sub.2H.sub.5, i-C.sub.3H.sub.7, n-C.sub.4H.sub.9, CCl.sub.3CH.sub.2, C.sub.6H.sub.5, —OH, —COOH, —O—CH.sub.2CH.sub.2—R′″, alkyl, aryl, where R′″═—(CH.sub.2).sub.yCH.sub.3 and 0≤y≤10.
[0100] The initiators for anionic or bulk polymerization of these monomers may be selected from n-C.sub.4H.sub.9Li, (C.sub.5H.sub.5).sub.2Mg, or (i-C.sub.4H.sub.9).sub.3Al, carbenium salts, and certain lithium salts. The reactions may be conducted at a temperature from −60° C. to 30° C., leading to high molecular weights, typically from 3×10.sup.3 to 10.sup.5. Cationic polymerization may be initiated with CF.sub.3S0.sub.3CH.sub.3, CF.sub.3S0.sub.3C.sub.2H.sub.5, (CF.sub.3SO.sub.2)O, Ph.sub.3C.sup.+AsF.sub.6.sup.−, and certain other lithium salts, leading to colored, oily products with number average molecular weights typically up to 10.sup.3. The initiator may comprise a lithium salt selected from lithium hexafluorophosphate (LiPF.sub.6), lithium borofluoride (LiBF.sub.4), lithium hexafluoroarsenide (LiAsF.sub.6), lithium trifluoro-metasulfonate (LiCF.sub.3SO.sub.3), bis-trifluoromethyl sulfonylimide lithium (LiN(CF.sub.3SO.sub.2).sub.2), lithium bis(oxalato)borate (LiBOB), lithium oxalyldifluoroborate (LiBF.sub.2C.sub.2O.sub.4), lithium oxalyldifluoroborate (LiBF.sub.2C.sub.2O.sub.4), or a combination thereof. In other words, we have surprisingly observed that certain lithium salts actually participate in the polymerization reactions.
[0101] The initiator or a co-initiator may be selected from an azo compound (e.g., azodiisobutyronitrile, AIBN), azobisisobutyroninile, azobisisoheptonitrile, dimethyl azobisisobutyrate, benzoyl peroxide tert-butyl peroxide and methyl ethyl ketone peroxide, benzoyl peroxide (BPO), bis(4-tert-butylcyclohexyl)peroxydicarbonate, t-amyl peroxypivalate, 2,2′-azobis-(2,4-dimethylvaleronitrile), 2,2′-azobis-(2-methylbutyronitrile), 1,1-azobis(cyclohexane-1-carbonitrile, benzoylperoxide (BPO), hydrogen peroxide, dodecamoyl peroxide, isobutyryl peroxide, cumene hydroperoxide, tert-butyl peroxypivalate, diisopropyl peroxydicarbonate, or a combination thereof.
[0102] In addition to an initiator, the reactive monomer solution for the preparation of the presently disclosed high-elasticity polymer may further comprise a curing agent (a crosslinking agent or co-polymerization species) selected from an amide group, such as N,N-dimethylacetamide, N,N-diethylacetamide, N,N-dimethylformamide, N,N-diethylformamide, or a combination thereof. The crosslinking agent may comprise a compound having at least one reactive group selected from a hydroxyl group, an amino group, an imino group, an amide group, an acrylic amide group, an amine group, an acrylic group, an acrylic ester group, or a mercapto group in the molecule. In certain embodiments, the crosslinking agent is selected from poly(diethanol) diacrylate, poly(ethyleneglycol)dimethacrylate, poly(diethanol) dimethylacrylate, or poly(ethylene glycol) diacrylate.
[0103] The crosslinking agent preferably comprises a compound having at least one reactive group selected from a hydroxyl group, an amino group, an imino group, an amide group, an amine group, an acrylic group, or a mercapto group in the molecule. The amine group is preferably selected from Chemical Formula 4:
##STR00018##
[0104] The crosslinking agent is preferably selected from N,N-methylene bisacrylamide, epichlorohydrin, 1,4-butanediol diglycidyl ether, tetrabutylammonium hydroxide, cinnamic acid, ferric chloride, aluminum sulfate octadecahydrate, diepoxy, dicarboxylic acid compound, poly(potassium 1-hydroxy acrylate) (PKHA), glycerol diglycidyl ether (GDE), ethylene glycol, polyethylene glycol, polyethylene glycol diglycidyl ether (PEGDE), citric acid (Formula 4 below), acrylic acid, methacrylic acid, a derivative compound of acrylic acid, a derivative compound of methacrylic acid (e.g. polyhydroxyethylmethacrylate), glycidyl functions, N,N′-Methylenebisacrylamide (MBAAm), Ethylene glycol dimethacrylate (EGDMAAm), isobornyl methacrylate, poly (acrylic acid) (PAA), methyl methacrylate, isobornyl acrylate, ethyl methacrylate, isobutyl methacrylate, n-Butyl methacrylate, ethyl acrylate, 2-Ethyl hexyl acrylate, n-Butyl acrylate, a diisocyanate (e.g. methylene diphenyl diisocyanate, MDI), an urethane chain, a chemical derivative thereof, or a combination thereof.
[0105] High-elasticity polymer refers to a polymer, typically a lightly cross-linked polymer, which exhibits an elastic deformation that is at least 5% when measured (without an additive or reinforcement in the polymer) under uniaxial tension. In the field of materials science and engineering, the “elastic deformation” is defined as a deformation of a material (when being mechanically stressed) that is essentially fully recoverable and the recovery is essentially instantaneous upon release of the load. The elastic deformation is preferably greater than 30%, more preferably greater than 50%, further more preferably greater than 100%, still more preferably greater than 150%, and most preferably greater than 200%.
[0106] Three examples of the disclosed composite particulates are illustrated in
[0107] As illustrated in
[0108] The primary particles themselves may be porous having porosity in the form of surface pores and/or internal pores.
[0109] This amount of pore volume inside the particulate (surface or internal pores of porous primary anode particles) provides empty space to accommodate the volume expansion of the anode active material so that the polymer matrix and the entire composite particulate would not have to significantly expand (not to exceed 50% volume expansion of the particulate) when the lithium battery is charged. Preferably, the composite particulate does not increase its volume by more than 20%, further preferably less than 10% and most preferably by approximately 0% when the lithium battery is charged. Such a constrained volume expansion of the particulate would not only reduce or eliminate the volume expansion of the anode electrode but also reduce or eliminate the issue of repeated formation and destruction of a solid-electrolyte interface (SEI) phase. We have discovered that this strategy surprisingly results in significantly reduced battery capacity decay rate and dramatically increased charge/discharge cycle numbers. These results are unexpected and highly significant with great utility value.
[0110] Multiple non-lithiated Si particles can be dispersed in or encapsulated by a high-elasticity polymer to form a composite particulate. As the lithium-ion battery is charged, the anode active material particles (e.g. Si) are intercalated with lithium ions and, hence, the Si particle expands. Due to the high elasticity of the polymer, the polymer may simply expand accordingly without breaking up into pieces. That the high-elasticity polymer remains intact prevents the exposure of the embedded Si particles to liquid electrolyte and, thus, prevents the Si from undergoing undesirable reactions with electrolyte during repeated charges/discharges of the battery. This strategy prevents continued consumption of the electrolyte and lithium ions to form additional SEI.
[0111] The particulate may further contain a graphite, graphene, and/or carbon material dispersed in the high-elasticity polymer matrix. The carbon or graphite material may be selected from polymeric carbon, amorphous carbon, chemical vapor deposition carbon, coal tar pitch, petroleum pitch, meso-phase pitch, carbon black, coke, acetylene black, activated carbon, fine expanded graphite particle with a dimension smaller than 100 nm, artificial graphite particle, natural graphite particle, carbon nano-tubes (single-walled or multi-walled), carbon nano-fibers (vapor-grown or carbonized polymer fibers), graphitic nano-fibers, graphene sheets, or a combination thereof. Graphene may be selected from pristine graphene, graphene oxide, reduced graphene oxide, graphene fluoride, hydrogenated graphene, nitrogenated graphene, functionalized graphene, etc.
[0112] The carbon/graphite/graphene particles, fibers, nanotubes, and/or nano sheets dispersed in the high-elasticity polymer or encapsulated in the high-elasticity polymer shell preferably and typically constitute a 3D network of electron-conducting paths that preferably are in contact with individual primary particles of the anode active material. The high-elasticity polymer matrix, being a continuous phase and making contact with individual primary particles (being substantially totally immersed in the polymer matrix) provide a 3D network of lithium ion-conducting paths. In other words, there are dual networks of conducting pathways for electrons and lithium ions inside the multi-functional composite particulate.
[0113] The anode active material may be selected from the group consisting of: (a) silicon (Si), germanium (Ge), tin (Sn), lead (Pb), antimony (Sb), phosphorus (P), bismuth (Bi), zinc (Zn), aluminum (Al), titanium (Ti), nickel (Ni), cobalt (Co), and cadmium (Cd); (b) alloys or intermetallic compounds of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Ni, Co, or Cd with other elements; (c) oxides, carbides, nitrides, sulfides, phosphides, selenides, and tellurides of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Fe, Ni, Co, V, or Cd, and their mixtures, composites, or lithium-containing composites; (d) salts and hydroxides of Sn; (e) lithium titanate, lithium manganate, lithium aluminate, lithium titanium niobium oxide, lithium-containing titanium oxide, lithium transition metal oxide, ZnCo.sub.2O.sub.4; (f) carbon or graphite particles (g) prelithiated versions thereof; and (h) combinations thereof.
[0114] Pre-lithiation of an anode active material can be conducted by several methods (chemical intercalation, ion implementation, and electrochemical intercalation). Among these, the electrochemical intercalation is the most effective. Lithium ions can be intercalated into non-Li elements (e.g. Si, Ge, and Sn) and compounds (e.g. SnO.sub.2 and Co.sub.3O.sub.4) up to a weight percentage of 54.68% (see Table 1 below). For Zn, Mg, Ag, and Au encapsulated inside an elastomer shell, the amount of Li can reach 99% by weight.
TABLE-US-00001 TABLE 1 Lithium storage capacity of selected non-Li elements. Atomic weight of Intercalated Atomic weight of active material, Max. wt. % compound Li, g/mole g/mole of Li Li.sub.4Si 6.941 28.086 49.71 Li.sub.4.4Si 6.941 28.086 54.68 Li.sub.4.4Ge 6.941 72.61 30.43 Li4.4Sn 6.941 118.71 20.85 Li.sub.3Cd 6.941 112.411 14.86 Li.sub.3Sb 6.941 121.76 13.93 Li.sub.4.4Pb 6.941 207.2 13.00 LiZn 6.941 65.39 7.45 Li.sub.3Bi 6.941 208.98 8.80
[0115] The particles of the anode active material may be in the form of a nano particle, nano wire, nano fiber, nano tube, nano sheet, nano platelet, nano disc, nano belt, nano ribbon, or nano horn. They can be non-lithiated (when incorporated into the anode active material layer) or pre-lithiated to a desired extent (up to the maximum capacity as allowed for a specific element or compound.
[0116] Preferably and typically, the high-elasticity polymer has a lithium ion conductivity no less than 10.sup.−5 S/cm, more preferably no less than 10.sup.−4 S/cm, further preferably no less than 10.sup.−3 S/cm, and most preferably no less than 10.sup.−2 S/cm. In some embodiments, the high-elasticity polymer is a neat polymer having no additive or filler dispersed therein. In others, the high-elasticity polymer is a polymer matrix composite containing from 0.1% to 50% (preferably 1% to 35%) by weight of a lithium ion-conducting additive dispersed in the high-elasticity polymer matrix material. The high-elasticity polymer should have a high elasticity (elastic deformation strain value >5%).
[0117] An elastic deformation is a deformation that is fully recoverable and the recovery process is essentially instantaneous (no significant time delay) upon release of the mechanical stress. The high-elasticity polymer can exhibit an elastic deformation from 5% up to 1,000% (10 times of its original length), more typically from 10% to 800%, and further more typically from 50% to 500%, and most typically and desirably from 70% to 300%.
[0118] It may be noted that although a metal typically has a high ductility (i.e. can be extended to a large extent without breakage), the majority of the deformation is plastic deformation (non-recoverable) and only a small amount of elastic deformation (typically <1% and more typically <0.2%).
[0119] Typically, a high-elasticity polymer is originally in a monomer, oligomer, or linear or branched chain states that can be cured to form a cross-linked polymer that is highly elastic. Prior to curing, these polymers or oligomers are soluble in an organic solvent or, preferably, water to form a polymer solution. Particles of an anode active material (e.g. SnO.sub.2 nano particles and Si nano-wires) can be dispersed in this polymer solution to form a suspension (dispersion or slurry) of an active material particle-polymer (monomer or oligomer) mixture. This suspension can then be subjected to a solvent removal treatment. The polymer (or monomer or oligomer) precipitates out to form a continuous phase or matrix in which the active material primary particles are dispersed (if a polymer content is high), or to form a coating encapsulating the anode particles (if a polymer content is low). This can be accomplished, for instance, via solution dipping, coating or casting on a solid substrate surface, spray drying, ultrasonic spraying, air-assisted spraying, aerosolization, and other secondary particle formation procedures.
[0120] It is essential for these materials to form a lightly cross-linked network of polymer chains. In other words, the network polymer or cross-linked polymer should have a relatively low degree of cross-linking or low cross-link density to impart a high elastic deformation.
[0121] The cross-link density of a cross-linked network of polymer chains may be defined as the inverse of the molecular weight between cross-links (Mc). The cross-link density can be determined by the equation, Mc=ρRT/Ge, where Ge is the equilibrium modulus as determined by a temperature sweep in dynamic mechanical analysis, p is the physical density, R is the universal gas constant in J/mol*K and T is absolute temperature in K. Once Ge and p are determined experimentally, then Mc and the cross-link density can be calculated.
[0122] The magnitude of Mc may be normalized by dividing the Mc value by the molecular weight of the characteristic repeat unit in the cross-link chain or chain linkage to obtain a number, Nc, which is the number of repeating units between two cross-link points. We have found that the elastic deformation strain correlates very well with Mc and Nc. The elasticity of a cross-linked polymer derives from a large number of repeating units (large Nc) between cross-links. The repeating units can assume a more relax conformation (e.g. random coil) when the polymer is not stressed. However, when the polymer is mechanically stressed, the linkage chain uncoils or gets stretched to provide a large deformation. A long chain linkage between cross-link points (larger Nc) enables a larger elastic deformation. Upon release of the load, the linkage chain returns to the more relaxed or coiled state. During mechanical loading of a polymer, the cross-links prevent slippage of chains that otherwise form plastic deformation (non-recoverable).
[0123] Preferably, the Nc value in a high-elasticity polymer is greater than 5, more preferably greater than 10, further more preferably greater than 100, and even more preferably greater than 200. These Nc values can be readily controlled and varied to achieve different elastic deformation values by using different cross-linking agents with different functionalities, and by designing the polymerization and cross-linking reactions to proceed at different temperatures for different periods of time.
[0124] Alternatively, Mooney-Rilvin method may be used to determine the degree of cross-linking. Crosslinking also can be measured by swelling experiments. In a swelling experiment, the crosslinked sample is placed into a good solvent for the corresponding linear polymer at a specific temperature, and either the change in mass or the change in volume is measured. The higher the degree of crosslinking, the less swelling is attainable. Based on the degree of swelling, the Flory Interaction Parameter (which relates the solvent interaction with the sample, Flory Huggins Eq.), and the density of the solvent, the theoretical degree of crosslinking can be calculated according to Flory's Network Theory. The Flory-Rehner Equation can be useful in the determination of cross-linking.
[0125] The high-elasticity polymer matrix may contain a simultaneous interpenetrating network (SIPN) polymer, wherein two cross-linking chains intertwine with each other, or a semi-interpenetrating network polymer (semi-IPN), which contains a cross-linked polymer and a linear polymer.
[0126] The aforementioned high-elasticity polymers may be used alone to serve as a matrix. Alternatively, the high-elasticity polymer can be mixed with a broad array of elastomers, electrically conducting polymers, lithium ion-conducting materials, and/or strengthening materials (e.g. carbon nanotube, carbon nano-fiber, or graphene sheets).
[0127] A broad array of elastomers can be mixed with a high-elasticity polymer. Substantially all the anode primary particles in a particulate are fully embedded in and surrounded by the polymer, preventing direct contact between the particle(s) and the liquid electrolyte in the battery.
[0128] The high-elasticity polymer may further contain an elastomeric material selected from natural polyisoprene (e.g. cis-1,4-polyisoprene natural rubber (NR) and trans-1,4-polyisoprene gutta-percha), synthetic polyisoprene (IR for isoprene rubber), polybutadiene (BR for butadiene rubber), chloroprene rubber (CR), polychloroprene (e.g. Neoprene, Baypren etc.), butyl rubber (copolymer of isobutylene and isoprene, IIR), including halogenated butyl rubbers (chloro butyl rubber (CIIR) and bromo butyl rubber (BIIR), styrene-butadiene rubber (copolymer of styrene and butadiene, SBR), nitrile rubber (copolymer of butadiene and acrylonitrile, NBR), EPM (ethylene propylene rubber, a copolymer of ethylene and propylene), EPDM rubber (ethylene propylene diene rubber, a terpolymer of ethylene, propylene and a diene-component), epichlorohydrin rubber (ECO), polyacrylic rubber (ACM, ABR), silicone rubber (SI, Q, VMQ), fluorosilicone rubber (FVMQ), fluoroelastomers (FKM, and FEPM; such as Viton, Tecnoflon, Fluorel, Aflas and Dai-El), perfluoroelastomers (FFKM: Tecnoflon PFR, Kalrez, Chemraz, Perlast), polyether block amides (PEBA), chlorosulfonated polyethylene (CSM; e.g. Hypalon), and ethylene-vinyl acetate (EVA), thermoplastic elastomers (TPE), protein resilin, protein elastin, ethylene oxide-epichlorohydrin copolymer, polyurethane, urethane-urea copolymer, and combinations thereof.
[0129] The urethane-urea copolymer usually consists of two types of domains, soft domains and hard ones. Entangled linear backbone chains consisting of poly(tetramethylene ether) glycol (PTMEG) units constitute the soft domains, while repeated methylene diphenyl diisocyanate (MDI) and ethylene diamine (EDA) units constitute the hard domains. The lithium ion-conducting additive can be incorporated in the soft domains or other more amorphous zones.
[0130] In some embodiments, a high-elasticity polymer can form a polymer matrix composite containing a lithium ion-conducting additive dispersed in the high-elasticity polymer matrix material, wherein the lithium ion-conducting additive is selected from Li.sub.2CO.sub.3, Li.sub.2O, Li.sub.2C.sub.2O.sub.4, LiOH, LiX, ROCO.sub.2Li, HCOLi, ROLi, (ROCO.sub.2Li).sub.2, (CH.sub.2OCO.sub.2Li).sub.2, Li.sub.2S, Li.sub.xSO.sub.y, or a combination thereof, wherein X═F, Cl, I, or Br, R=a hydrocarbon group, 0<x≤1, 1≤y≤4.
[0131] In some embodiments, the high-elasticity polymer can be mixed with a lithium ion-conducting additive, which contains a lithium salt selected from lithium perchlorate (LiClO.sub.4), lithium hexafluorophosphate (LiPF.sub.6), lithium borofluoride (LiBF.sub.4), lithium hexafluoroarsenide (LiAsF.sub.6), lithium trifluoro-methanesulfonate (LiCF.sub.3SO.sub.3), bis-trifluoromethyl sulfonylimide lithium (LiN(CF.sub.3SO.sub.2).sub.2), lithium bis(oxalato)borate (LiBOB), lithium oxalyldifluoroborate (LiBF.sub.2C.sub.2O.sub.4), lithium nitrate (LiNO.sub.3), Li-fluoroalkyl-phosphate (LiPF.sub.3(CF.sub.2CF.sub.3).sub.3), lithium bisperfluoro-ethylsulfonylimide (LiBETI), lithium bis(trifluoromethanesulfonyl)imide, lithium bis(fluorosulfonyl)imide, lithium trifluoromethanesulfonimide (LiTFSI), an ionic liquid-based lithium salt, or a combination thereof.
[0132] The high-elasticity polymer may form a mixture or blend with an electron-conducting polymer selected from polyaniline, polypyrrole, polythiophene, polyfuran, a bi-cyclic polymer, derivatives thereof (e.g. sulfonated versions), or a combination thereof.
[0133] In some embodiments, the high-elasticity polymer may form a mixture with a lithium ion-conducting polymer selected from poly(ethylene oxide) (PEO), Polypropylene oxide (PPO), poly(acrylonitrile) (PAN), poly(methyl methacrylate) (PMMA), poly(vinylidene fluoride) (PVdF), Poly bis-methoxy ethoxyethoxide-phosphazene, Polyvinyl chloride, Polydimethylsiloxane, poly(vinylidene fluoride)-hexafluoropropylene (PVDF-HFP), a derivative thereof (e.g. sulfonated versions), or a combination thereof.
[0134] The present disclosure also provides a method of producing composite particulates comprising anode active material particles dispersed in a high-elasticity polymer. As schematically illustrated in
[0135] Alternatively, one may first mix certain ingredient(s) in one pot and other ingredients in other pot(s) and then combine them together in one pot. For instance, one may mix the monomer and the initiator in one pot, allowing the mixture to proceed to form a reactive oligomer (low molecular weight chains). A separate pot may be used to contain the curing agent (crosslinker). The primary particles of anode active material and other ingredients may be dispersed into either pot or both pots. The ingredients in two pots are then combined together and then heated or radiation-exposed to initiate the polymerization and crosslinking reactions (if appropriate).
[0136] The present disclosure also provides a method of manufacturing the composite particulates described above, the method comprising: (a) dispersing multiple particles of an anode active material in a precursor polymer solution to form a suspension wherein these particles are fully embedded or immersed in the precursor solution, which comprises at least a curing agent dissolved or dispersed in a reactive liquid medium that comprises a monomer or oligomer, and an optional non-aqueous liquid solvent, wherein the monomer or oligomer is selected from the group consisting of phosphates, phosphonates, phosphoric; acids, phosphorous acid, phosphites, phosphoric acids, combinations thereof, and combination thereof with phosphazenes; (b) operating a secondary particle-forming procedure to shape the suspension into multiple droplets and remove the liquid solvent from the droplets; and (c) curing the monomer or oligomer to form said composite particulates wherein a particulate comprises one or a plurality of anode active material particles that are dispersed and embedded in a polymer matrix or encapsulated by a polymer shell. Preferably, the high-elasticity polymer has a lithium-ion conductivity from 1×10.sup.−8 S/cm to 5×10.sup.−2 S/cm. In some embodiments, the high-elasticity polymer has a recoverable tensile strain from 35% to 700% (more preferably >50%, and most preferably >100%).
[0137] Several composite droplet forming processes require the high-elasticity polymer or its precursor (monomer or oligomer) to be dissolvable in a solvent. Fortunately, all the high-elasticity polymers or their precursors used herein are either in a liquid state at room temperature or are soluble in some common solvents. The un-cured polymer or its precursor can be readily dissolved in a common organic solvent or water to form a solution. This solution can then be used to embed, immerse, engulf or encapsulate the solid particles (anode particles along with other additive or reinforcement materials) via several of the micro-droplet-forming methods to be discussed in what follows. Upon formation of the droplets, the polymer matrix is then polymerized and cross-linked.
[0138] There are three broad categories of micro-encapsulation methods that can be implemented to produce high-elasticity polymer composite: physical methods, physico-chemical methods, and chemical methods. The physical methods include extrusion and pelletizing, solution dipping and drying, suspension coating or casting on a solid substrate (e.g. slot-die coating, Comma coating, spray-coating) followed by drying and scratching off particles from the substrate, pan-coating, air-suspension coating, centrifugal extrusion, vibration nozzle, and spray-drying methods. The physico-chemical methods include ionotropic gelation and coacervation-phase separation methods. The chemical methods include interfacial polycondensation, interfacial cross-linking, in-situ polymerization, and matrix polymerization.
[0139] It may be noted that some of these methods (e.g., pan-coating, air-suspension coating, and spray-drying) may be used to coat or encapsulate primary particles or particulates (secondary particles) by adjusting the solid content, degree of dispersion, spraying and drying conditions, etc. Similar processes may be used to produce composite particulates wherein the particles are fully dispersed in a polymer matrix, not just coating on some surfaces. This can be accomplished by providing a higher amount of the reacting monomer, oligomer, or polymer with respect to the anode particles, for instance.
[0140] Pan-coating method: The pan coating process involves tumbling the anode active material primary particles (along with any desired additive or reinforcement materials) in a pan or a similar device while the matrix material (e.g., monomer/oligomer liquid or uncured polymer/solvent solution; possibly containing a lithium salt dispersed or dissolved therein) is applied slowly until a desired amount of matrix is attained.
[0141] Air-suspension coating method: In the air suspension coating process, the solid primary particles of anode active material are dispersed into the supporting air stream in an embedding chamber. A controlled stream of a reactive precursor solution (e.g., polymer or its monomer or oligomer dissolved in a solvent; or its monomer or oligomer alone in a liquid state) is concurrently introduced into this chamber, allowing the solution to hit and embed the suspended particles. These suspended particles are embedded in the reactive precursor (monomer, oligomer, etc. which is polymerized/cured concurrently or subsequently) while the volatile solvent is removed, leaving behind a composite comprising a matrix of network polymer and anode active material particles. This process may be repeated several times until the required parameters, such as full embedding, are achieved. The air stream which supports the anode particles also helps to dry them, and the rate of drying is directly proportional to the temperature of the air stream, which can be adjusted for optimized polymer network amount.
[0142] In a preferred mode, the particles in the embedding zone portion may be subjected to re-circulation for repeated embedding. Preferably, the chamber is arranged such that the particles pass upwards through the embedding zone, then are dispersed into slower moving air and sink back to the base of the encapsulating chamber, enabling repeated passes of the particles through the embedding zone until the desired matrix amount is achieved.
[0143] Centrifugal extrusion: Primary anode particles may be embedded in a polymer network or precursor material using a rotating extrusion head containing concentric nozzles. In this process, a stream of core fluid (slurry containing anode particles dispersed in a solvent) is surrounded by a sheath of shell solution or melt containing the polymer or precursor. As the device rotates and the stream moves through the air it breaks, due to Rayleigh instability, into droplets of core, each coated with the shell solution. While the droplets are in flight, the molten shell may be hardened or the solvent may be evaporated from the shell solution. If needed, the capsules can be hardened after formation by catching them in a hardening bath. Since the drops are formed by the breakup of a liquid stream, the process is only suitable for liquid or slurry. A high production rate can be achieved. Up to 22.5 kg of microcapsules can be produced per nozzle per hour and extrusion heads containing 16 nozzles are readily available.
[0144] Vibrational nozzle encapsulation method: matrix-encapsulation of anode particles can be conducted using a laminar flow through a nozzle and vibration of the nozzle or the liquid. The vibration has to be done in resonance with the Rayleigh instability, leading to very uniform droplets. The liquid can include any liquids with limited viscosities (1-50,000 mPa.Math.s): emulsions, suspensions or slurry containing the anode active material particles and the polymer or precursor.
[0145] Spray-drying: Spray drying may be used to encapsulate and embed anode particles when the particles are suspended in a melt or polymer/precursor solution to form a suspension. In spray drying, the liquid feed (solution or suspension) is atomized to form droplets which, upon contacts with hot gas, allow solvent to get vaporized and a polymer matrix to fully embed the particles.
[0146] In-situ polymerization: In some micro-encapsulation processes, anode particles are fully embedded in a monomer or oligomer first. Then, direct polymerization of the monomer or oligomer is carried out with the presence of these material particles dispersed therein.
[0147] Matrix polymerization: This method involves dispersing and embedding anode primary particles in a polymeric matrix during formation of the particles. This can be accomplished via spray-drying, in which the particles are formed by evaporation of the solvent from the matrix material. Another possible route is the notion that the solidification of the matrix is caused by a chemical change.
[0148] In summary, in certain embodiments, the disclosure provides a method of producing the multi-functional particulates, the method comprising (A) dispersing a plurality of primary particles of an anode active material, having a diameter or thickness from 0.5 nm to 20 μm, in a liquid mixture of a monomer or oligomer of a phosphorus-containing compound or derivative (selected from the group consisting of phosphates, phosphonates, phosphoric acids, phosphorous acid, phosphites, phosphoric acids, combinations thereof, and combination (hereof with phosphazenes), an initiator, and a cross-linking agent to form a reactive slurry; (B) forming the reactive slurry into micro-droplets and polymerizing and curing the monomer or oligomer in the micro-droplets to form the multi-functional particulates. The reactive mixture may further comprise a dopant, a reinforcement material, a lithium ion-conducting additive, an electron-conducting additive, or a combination thereof.
[0149] A foaming agent or blowing agent may be introduced into the reactive slurry and can be activated to produce pores in the micro-droplets when the reactive species are polymerized or crosslinked.
[0150] In some embodiments, the reactive slurry further comprises a high-strength material selected from carbon nanotubes, carbon nano-fibers, carbon or graphite fibers, graphene sheets, expanded graphite flakes, polymer fibrils, glass fibers, ceramic fibers, metal filaments or metal nano-wires, or a combination thereof. Some of these high-strength materials are electron-conducting.
[0151] The step (B) of forming micro-droplets may comprise a procedure selected from solution dipping, coating or casting on a solid substrate, pan-coating, air-suspension coating, centrifugal extrusion, vibration-nozzle encapsulation, spray-drying, coacervation-phase separation, interfacial polycondensation or interfacial cross-linking, in-situ polymerization, matrix polymerization, extrusion and palletization, or a combination thereof.
[0152] In certain embodiments, the micro-droplets as formed may contain a liquid solvent and the method further comprises a step of removing the solvent.
[0153] The following examples serve to provide the best modes of practice for the present disclosure and should not be construed as limiting the scope of the disclosure:
Example 1: Encapsulating Polymer from Vinylphosphonic Acid (VPA) and Triethylene Glycol Dimethacrylate (TEGDA) or Acrylic Acid (AA)
[0154] Si particles were encapsulated with a high-elasticity polymer. The free radical polymerization of acrylic acid (AA) with vinylphosphonic acid (VPA) can be catalyzed with benzoyl peroxide as the initiator. In a vessel provided with a reflux condenser, 1.50 parts vinylphosphonic acid were dissolved in 150 parts isopropanol and heated for 5 hours at 90° C. together with 0.75 parts benzoyl peroxide and 20 parts of lithium bis(oxalato)borate (LiBOB). A very viscous clear solution of polyvinylphosphonic acid was obtained. On a separate basis, a similar reactive mixture was added with a desirable amount (e.g., 10-50 parts) of AA or TEGDA as a co-monomer. Si particles were then added into the solution to form a slurry, which was then dried and cured in a vacuum oven at 90° C. for 5 hours to obtain a solid mass of polymer-encapsulated Si particles. The solid mass was subjected to mechanical shearing in a food processor to produce composite particulates.
[0155] In a separate experiment, vinylphosphonic acid was heated to >45° C. (melting point of VPA=36° C.), which was added with benzoyl peroxide, LiBOB. After rigorous stirring, the resulting paste was cast onto a glass surface and cured at 90° C. for 5 hours to form a layer for use in tensile testing. Several tensile testing specimens were cut from each polymer film and tested with a universal testing machine. The representative tensile stress-strain curves indicate that this series of network polymers have an elastic deformation from approximately 35% to 224%.
[0156] For electrochemical testing, the working electrodes were prepared by mixing 85 wt. % active material particles (polymer-protected and non-protected particulates of Si, separately), 7 wt. % acetylene black (Super-P), and 8 wt. % polyvinylidene fluoride (PVDF) binder dissolved in N-methyl-2-pyrrolidinoe (NMP) to form a slurry of 5 wt. % total solid content. After coating the slurries on Cu foil, the electrodes were dried at 120° C. in vacuum for 2 h to remove the solvent before pressing. Then, the electrodes were cut into a disk (ϕ=12 mm) and dried at 100° C. for 24 h in vacuum. Electrochemical measurements were carried out using CR2032 (3V) coin-type cells with lithium metal as the counter/reference electrode, Celgard 2400 membrane as separator, and 1 M LiPF.sub.6 electrolyte solution dissolved in a mixture of ethylene carbonate (EC) and diethyl carbonate (DEC) (EC-DEC, 1:1 v/v). The cell assembly was performed in an argon-filled glove-box. The CV measurements were carried out using an-6 electrochemical workstation at a scanning rate of 1 mV/s. The electrochemical performance of the particulates of high-elasticity polymer-encapsulated Si particles and non-protected Si particles were evaluated by galvanostatic charge/discharge cycling at a current density of 50-200 mA/g, using an electrochemical workstation.
[0157]
[0158] In contrast, as demonstrated
Example 2: Free Radical Polymerization of Diisopropyl-p-Vinylbenzyl Phosphonate and 1-Vinylimidazole
[0159] Copolymers of diisopropyl-p-vinylbenzyl phosphonate (DIPVBP) and 1-vinylimidazole (1VI) were prepared by free radical polymerization. First, Diisopropyl-p-vinylbenzyl phosphonate was synthesized by taking the following procedure: Potassium tert-butoxide (8.16 g, 72.7 mmol) in dry THF (40 mL) was added dropwise into stirred solution of diisopropyl phosphate (14.19 g, 85.4 mmol) and p-vinylbenzyl chloride (10.72 g, 70.25 mmol) in THF within 2 h. The reaction was maintained at room temperature throughout by occasional cooling with an ice bath. The mixture was under stirring for another hour at room temperature and then filtered, diluted with diethyl ether (200 mL), and washed with water (100 mL) three times. The organic component was then dried over sodium sulfate. The raw product was then purified by flash column chromatography on silica. Residual vinylbenzyl chloride was eluted with toluene, and subsequently the product was washed off with ethyl acetate to yield colorless oil.
[0160] Synthesis of Poly(diisopropyl-p-vinylbenzyl phosphonate-co-1-vinylimidazole) was conducted with various feed ratios of 1VI and DIPVBP in toluene solution at 70° C. with AIBN as initiator. Specifically, the copolymers (with feed ratios of monomers from 1/9 to 9/1) were synthesized by dissolving 1VI and DIPVBP in toluene. Approximately 1% by weight of AIBN (relative to the total monomer weight) in toluene was added into the solution. The reaction mixture was stirred under a nitrogen atmosphere at 70° C. for 1 hour. Particles of an anode active material (SiO.sub.x or Sn) were added into the reacting mixture and the reaction was allowed to proceed for another hour to obtain the copolymer. The polymerization was illustrated in Reaction 13 presented in an earlier section. The resulting suspension was spray-dried to obtain composite particulates containing the anode primary particles dispersed in a co-polymer matrix
[0161] The homopolymer of DIPVBP was synthesized by free radical polymerization in toluene under similar conditions to the copolymers. Again, the anode particles were added half way through the polymerization reaction. The polymerized reaction mixture of DIPVBP and anode particles dispersed therein was spray-dried to obtain composite particulates.
[0162] In an additional experiment, poly(diisopropyl-p-vinylbenzyl phosphonate-co-1-vinylimidazole) prepared above was dissolved in ethanol and reacted with excess HCl aqueous solution (10 mol/L) at 100° C. for 24 h, and the corresponding poly(vinylbenzylphosphonic acid-co-1-vinylimidazole) was obtained after purification. This co-polymer was cast on a glass surface to obtain a layer for tensile testing and lithium ion conductivity measurement.
[0163] The room temperature lithium-ion conductivity values of the poly(diisopropyl-p-vinylbenzyl phosphonate) homo-polymer, the poly(diisopropyl-p-vinylbenzyl phosphonate-co-1-vinylimidazole) copolymer, and the poly(vinylbenzylphosphonic acid-co-1-vinylimidazole) copolymer (each containing approximately 5% by weight lithium salt) were approximately 2.5×10.sup.−5 S/cm, 7.4×10.sup.−4 S/cm, and 5.6×10.sup.−3 S/cm, respectively. The encapsulating polymers are flame resistant and relatively safe.
Example 3: Homo-Polymers and Copolymers from Dimethyhmethacryloyloxy)-Methyl Phosphonate (MAPC1)
[0164] Tin oxide (SnO.sub.2) nano particles were obtained by the controlled hydrolysis of SnCl.sub.4.5H.sub.2O with NaOH using the following procedure: SnCl.sub.4.5H.sub.2O (0.95 g, 2.7 m-mol) and NaOH (0.212 g, 5.3 m-mol) were dissolved in 50 mL of distilled water each. The NaOH solution was added drop-wise under vigorous stirring to the tin chloride solution at a rate of 1 mL/min. This solution was homogenized by sonication for 5 m in. Subsequently, the resulting hydrosol was reacted with H.sub.2SO.sub.4. To this mixed solution, few drops of 0.1 M of H.sub.2SO.sub.4 were added to flocculate the product. The precipitated solid was collected by centrifugation, washed with water and ethanol, and dried in vacuum. The dried product was heat-treated at 400° C. for 2 h under Ar atmosphere.
[0165] A phosphonated methacrylate, namely din ethyl(methacryloylox)-methyl phosphonate (MAPC1), was synthesized using paraformaldehyde and potassium carbonate. This began with the synthesis of Dimethyl-a-Hydroxymethylphosphonate by following the procedure below: Ten grams (0.09 mol) of dimethyl hydrogenophosphonate, 2.73 g (0.09 mol) of paraformaldehyde, 30 mL of methanol, and 0.62 g of anhydrous K.sub.2CO.sub.3 were introduced in a two-necked flask equipped with a condenser. The solution was vigorously stirred under methanol refluxing for 2 h. Dimethyl-a-hydroxymethylphosphonate was obtained under high vacuum with 98% yield.
[0166] For the synthesis of Dimethyl(methacryloxy)methyl Phosphonate (MAPC1), ten grams (0.071 mol) of dimethyl-a-hydroxymethylphosphonate, 6.15 g (0.071 mol) of methacrylic acid, and 30 mL of chloroform were introduced in a two-necked flask equipped with a condenser. Temperature was dropped until 0° C. and, after degassing, 14.73 g (0.0071 mol) of dicyclohexylcarbodiimide (DCCI), 0.872 g (0.0071 mol) of N,N-dimethyl-4-aminopyridine (DMAP) were added in a dropwise manner. The solution was vigorously stirred at room temperature for 2 h. After filtration, MAPC1 is obtained by distillation under high vacuum (100° C. with 2×10.sup.−2 mmHg) with 90% yield.
[0167] The synthesis of Methyl(methacryloxy)methyl Phosphonic Hemi-Acid MAPC1 (OH) was conducted in the following manner: Four grams (0.019 mol) of MAPC1, 2 g (0.019 mol) of NaBr, and 20 mL of methylethylketone were introduced in a two-necked flask equipped with a condenser and with a magnetic stirrer. The reaction mixture was heated under reflux with stirring for 13 h and at room temperature for 4 h. The sodium salt was precipitated, filtered, and washed several times with acetone to remove residues. The white powder was dried under high vacuum for 2 h (88% yield). The salt was solubilized in methanol and passed through a column filled with sulfonic acid resin. The column was washed with methanol until reaching neutral pH, and the final MAPC1 (OH) was obtained with 97% yield.
[0168] Homo and copolymerization of MAPC1 and MAPC1(OH) with MMA were conducted in a three-necked flask equipped with a condenser, a septum cap (to be able to take aliquots), and a magnetic stirrer in acetonitrile refluxing and with AIBN as initiator. Radical polymerization of MAPC1 was performed at 80° C. in acetonitrile, initiated with AIBN (1 mol %) for 2 h, and the MAPC1 conversion was monitored over time. Radical copolymerizations of both MAPC1 and MAPC1(OH) with MMA were then carried out in acetonitrile at 80° C. initiated by AIBN (1 mol %). SnO.sub.2 nano particles were added mid-way before completion of the polymerization reactions. The room temperature lithium-ion conductivities of these polymers were approximately from 4.5×10.sup.−6 S/cm to 1.3×10.sup.−4 S/cm. The elasticity value of these polymers, upon irradiation to electron beam to generate a low degree of crosslinking was from 25% to 120%.
Example 4: Diethyl Vinylphosphonate and Diisopropyl Vinylphosphonate Polymers for Si Encapsulation
[0169] Both diethyl vinylphosphonate and diisopropyl vinylphosphonate were polymerized by a peroxide initiator (di-tert-butyl peroxide), along with LiBF.sub.4, to clear, light-yellow polymers of low molecular weight. In a typical procedure, either diethyl vinylphosphonate or diisopropyl vinylphosphonate (being a liquid at room temperature) is added with di-tert-butyl peroxide (0.5-2% by weight) and LiBF.sub.4 (5-10% by weight) to form a reactive solution. Si nanowires and nano particles were separately dispersed into the reactive solution. The resulting suspension was heated to 45° C., allowing bulk polymerization to proceed for 2-12 hours. Subsequently, the suspension was spray-dried to form composite particulates.
[0170] Additionally, layers of diethyl vinylphosphonate and diisopropyl vinylphosphonate polymer electrolytes were cast on glass surfaces and polymerized under comparable conditions. The lithium ion conductivity of these materials was measured. The lithium ion conductivity of diethyl vinylphosphonate derived polymers was found to be in the range from 5.4×10.sup.−5 S/cm-7.3×10.sup.−4 S/cm and that of diisopropyl vinylphosphonate polymer electrolytes in the range from 6.6×10.sup.−5 S/cm-8.4×10.sup.−4 S/cm. Both are highly flame resistant.
Example 5: Curing of Cyclic Esters of Phosphoric Acids
[0171] As selected examples of polymers from phosphates, five-membered cyclic esters of phosphoric acid of the general formula, —CH.sub.2CH(R)OP(O)—(OR′)O—, were polymerized to solid, soluble polymers of high molecular weight by using n-C.sub.4H.sub.9Li, (C.sub.5H.sub.5).sub.2Mg, or (i-C.sub.4H.sub.9).sub.3Al as initiators. The resulting polymers have a repeating unit as follows:
##STR00019##
where R is H, with R′═CH.sub.3, C.sub.2H.sub.5, n-C.sub.3H.sub.7, i-C.sub.3H.sub.7; n-C.sub.4H.sub.9, CCl.sub.3CH.sub.2, or C.sub.6H.sub.5, or and R′ is C.sub.2H.sub.5. The polymers typically have M.sub.n=10.sup.4-10.sup.5.
[0172] In a representative procedure, initiators n-C.sub.4H.sub.9Li (0.5% by weight) and 5% lithium bis(oxalato)borate (LiBOB) as a lithium salt were mixed with 2-alkoxy-2-oxo-1,3,2-dioxaphospholan (R′═H in the following chemical formula):
##STR00020##
Temperature or a second solvent may be used to adjust the viscosity of the reactant mixture, where necessary. The mixture, with added graphene-embraced Si particles dispersed therein, was allowed to undergo the anionic polymerization at room temperature (or lower) overnight to form a solid mass. This solid mass was subjected to light ball milling to produce powder of composite particulates. The room temperature lithium ion conductivities of this series of solid polymers (without the anode material particles) are in the range from 2.5×10.sup.−5 S/cm-1.6×10.sup.−3 S/cm.
[0173] Separately, the reacting mass (without anode particles) was cast onto a glass surface to form several films which were cured to obtain polymers. Tensile testing was conducted on these films. This series of polymers can be elastically stretched up to approximately 68%.
[0174] The present study led to the following additional observations: [0175] (1) The high-elasticity polymer matrix embedding or shell encapsulating strategy is surprisingly effective in alleviating the anode expansion/shrinkage-induced capacity decay problems. Such a strategy appears to have significantly reduced or eliminated the possibility of repeated SEI formation and breakage that would otherwise continue to consume electrolyte and active lithium ions. [0176] (2) It is quite surprising that the group of polymers herein investigated (commonly used as an additive in a battery liquid electrolyte) can be so elastic and lithium ion-conducting (even without the presence of a lithium salt), having a lithium ion conductivity typically in the range from 10.sup.−6 to 10.sup.−3 S/cm at room temperature. [0177] (3) These phosphonate or phosphoric acid-based encapsulating polymers provides flame retardance to the battery as well. This is highly beneficial since thermal runaway issues of conventional lithium-ion batteries are often initiated at the anode side.