Method for making absorbent oil fly ash powder

Abstract

A method of removing an organic pollutant from water by contacting the water with a ball milled and sonicated oil fly ash powder to adsorb the organic pollutant onto the ball milled and sonicated oil fly ash powder. A method of producing a ball milled and sonicated oil fly ash powder involving ball milling oil fly ash to provide ball milled oil fly ash particles with an average particle size of less than 1 μm and sonicating the ball milled oil fly ash particles in an aqueous medium to form the ball milled and sonicated oil fly ash powder. A method of improving recovery of valuable metals/elements from oil fly ash.

Claims

1. A method of producing a ball milled and sonicated oil fly ash powder, comprising: ball milling oil fly ash to provide ball milled oil fly ash particles with an average particle size of less than 1 μm; sonicating the ball milled oil fly ash particles in an aqueous medium to form a mixture comprising ball milled and sonicated oil fly ash particles and a supernatant; and separating the ball milled and sonicated oil fly ash particles from the supernatant and drying to form the ball milled and sonicated oil fly ash powder.

2. The method of claim 1, wherein the oil fly ash has a carbon content of greater than 65 wt. %, based on a total weight of the oil fly ash.

3. The method of claim 1, wherein the oil fly ash has a SiO.sub.2 content of less than 3 wt. %, and a Al.sub.2O.sub.3 content of less than 3 wt %, each based on a total weight of the oil fly ash.

4. The method of claim 1, wherein the oil fly ash has a vanadium content of 1,000-70,000 ppm, and a nickel content of 500-15,000 ppm.

5. The method of claim 1, wherein the ball milled and sonicated oil fly ash powder has an average particle size of less than less than 1 μm.

6. The method of claim 5, wherein the ball milled and sonicated oil fly ash powder has a bimodal particle size distribution with nanoparticles having an average particle size of 10-100 nm, and sub-micron sized particles having an average particle size of 0.2-0.9 μm.

7. The method of claim 1, wherein the oil fly ash is ball milled in a high energy ball mill at a rotational speed of 100 to 400 rpm.

8. The method of claim 1, wherein the oil fly ash is ball milled in tungsten carbide vials with tungsten carbide or stainless steel balls, and with a ball to oil fly ash weight ratio of from 8:1 to 12:1.

9. The method of claim 1, wherein the oil fly ash particles are ball milled for 5-11 hours and sonicated for at least 1 hour.

10. The method of claim 1, further comprising shaking and/or stirring the mixture for at least 30 min. after sonicating.

11. The method of claim 1, wherein after the separating the ball milled and sonicated oil fly ash powder has an average particle size of less than 1 μm and a BET surface area of 20-24 m.sup.2/g.

12. The method of claim 1, wherein after the separating the ball milled and sonicated oil fly ash powder has a bulk density of 0.3-0.6 g/cm.sup.3.

13. The method of claim 1, wherein after the separating the ball milled and sonicated oil fly ash powder has a MgO content 5-16 wt. %, based on a total weight of the ball milled and sonicated oil fly ash powder.

14. The method of claim 1, wherein after the separating the ball milled and sonicated oil fly ash powder has a Fe.sub.2O.sub.3 content of 1-4 wt. %, based on a total weight of the ball milled and sonicated oil fly ash powder.

15. The method of claim 1, wherein after the separating the ball milled and sonicated oil fly ash powder has a Na.sub.2O content of 0.1-4 wt. %, based on a total weight of the ball milled and sonicated oil fly ash powder.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) A more complete appreciation of the disclosure and many of the attendant advantages thereof will be readily obtained as the same becomes better understood by reference to the following detailed description when considered in connection with the accompanying drawings, wherein:

(2) FIG. 1 shows an illustration of the BMSFA production and their application for (1) organic pollutants adsorption from waste water and (2) metal ion extraction

(3) FIG. 2A shows a low magnification SEM image of oil fly ash.

(4) FIG. 2B shows a low magnification SEM image ball milled and sonicated oil fly ash.

(5) FIGS. 3A-3B shows high magnification SEM images of ball milled and sonicated oil fly ash.

(6) FIG. 4 shows UV-vis absorption spectra of congo red dye pollutant adsorbed by the ball milled and sonicated oil fly ash at different times.

(7) FIG. 5 shows UV-vis absorption spectra of Crystal violet dye pollutant adsorbed by the ball milled and sonicated oil fly ash at different times.

(8) FIG. 6 shows UV-vis absorption spectra of brilliant green dye pollutant adsorbed by the ball milled and sonicated oil fly ash at different times

(9) FIG. 7 shows UV-vis absorption spectra of methylene blue dye pollutant adsorbed by the ball milled and sonicated oil fly ash at different times.

(10) FIG. 8 shows the adsorption of Congo red dye at different concentrations by the ball milled and sonicated oil fly ash as a function of time.

(11) FIG. 9. shows UV-vis absorption spectra of 8 ppm mixed dye (2 ppm methylene blue+2 ppm crystal violet+2 ppm brilliant green+2 ppm congo red) pollutant adsorbed by the ball milled and sonicated oil fly ash at different times.

DETAILED DESCRIPTION OF THE EMBODIMENTS

(12) Embodiments of the present disclosure will now be described more fully hereinafter with reference to the accompanying drawings, in which some, but not all of the embodiments of the disclosure are shown.

(13) As used herein, the words “a” and “an” and the like carry the meaning of “one or more”. Additionally, within the description of this disclosure, where a numerical limit or range is stated, the endpoints are included unless stated otherwise. Also, all values and subranges within a numerical limit or range are specifically included as if explicitly written out.

(14) As used herein, the terms “optional” or “optionally” means that the subsequently described event(s) can or cannot occur or the subsequently described component(s) may or may not be present (e.g. 0 wt. %).

(15) The term “comprising” is considered an open-ended term synonymous with terms such as including, containing or having and is used herein to describe aspects of the invention which may include additional components, functionality and/or structure. Terms such as “consisting essentially of” are used to identify aspects of the invention which exclude particular components that are not explicitly recited in the claim but would otherwise have a material effect on the basic and novel properties of the ball milled and sonicated oil fly ash powder, such as absorbency and ability to release vanadium and nickel, as well as other valuable metals (e.g., Pr, Ce, Tb, Dy, Yb, Te, Mo). The term “consisting of” describes aspects of the invention in which only those features explicitly recited in the claims are included and thus other components not explicitly or inherently included in the claim are excluded.

(16) A weight percent of a component, unless specifically stated to the contrary, is based on the total weight of the formulation or composition in which the component is included. For example if a particular element or component in a composition or article is said to have 8 wt. %, it is understood that this percentage is in relation to a total compositional percentage of 100%. Further, with respect to the composition of fly ash, e.g., the oil fly ash and the ball milled and sonicated oil fly ash powder, the dry weight basis is used. That is, the wt. % is based on a total weight of dried material so that a weight of water does not significantly contribute to the total weight of material, unless stated otherwise.

(17) Methods of Producing a Ball Milled and Sonicated Oil Fly Ash Powder and Collecting Vanadium, Nickel, and Optionally Other Valuable Metals/Rare Earth Elements

(18) In many countries, coal is the most employed fuel for thermal power generation. However, heavy fuel oil, diesel and natural gas are also used for power generation. Upon burning coal or heavy fuel oil, fly and bottom ash are generated. Fly ashes of variable particle diameters are emitted leaving the bottom ash in the combustor. Fly ash (FA) is often physically trapped using an electrostatic precipitator, which is then traditionally used in concrete production or in related construction areas, or directly discharged into landfills and ash ponds.

(19) The chemical composition of fly ash is dependent upon the nature of the feeding fuel, (e.g., coal, petroleum, or sometimes wood) and each fuel source provides distinct chemical compositions and properties to the resulting fly ash. Fly ash which is derived from coal sources such as bituminous coal, sub-bituminous coal, and lignite is termed “coal fly ash”, and is characterized by high contents of SiO.sub.2, Al.sub.2O.sub.3, Fe.sub.2O.sub.3, and CaO, which make it a suitable ingredient for normal Portland cement and geopolymers. According to ASTM C618, coal fly ash is categorized into Class F or Class C based on the content of Si, Al, and Ca. Coal fly ash can be categorized as siliceous fly ash or calcareous fly ash, depending on the amount of Si or Ca present, respectively. Coal fly ash also has a low carbon content, less than 15 wt. %, and in many cases less than 5 wt. %, as determined by loss on ignition (LOI) values according to ASTM D7348 for example, or TGA-MS analysis. Table 1 shows common constituents of coal fly ash.

(20) TABLE-US-00001 TABLE 1 Composition of coal fly ash Component Bituminous Subbituminous Lignite SiO.sub.2 (%) 20-60 40-60 15-45 Al.sub.2O.sub.3 (%)  5-35 20-30 20-25 Fe.sub.2O.sub.3 (%) 10-40  4-10  4-15 CaO (%)  1-12  5-30 15-40 LOI (%)  0-15 0-3 0-5

(21) Fly ash of coal origin may also contain trace metals such as As, Be, B, Cd, Cr, Co, Mg, Mo, Pb, Se, V, Ni, Cu, and Zn, with vanadium (78-198.6 ppm) and nickel (29-232.1 ppm) being present among the highest quantities of all of these metals listed [Al-Degs, Y. S. et. al. Characterization and utilization of fly ash of heavy fuel oil generated in power stations, Fuel Processing Technology, 2014, 123, 41-46—incorporated herein by reference in its entirety].

(22) Wood fly ash, or fly ash obtained from combustion of wood or wood-based biomass varies depending of the wood source. However, most wood fly ash contains a high calcium and silica content. Table 2 illustrates the composition of a typical wood fly ash obtained from a bubbling fluidized bed boiler [Skels, P. et al. Usage of Woof Fly Ash in Stabilization of Unbound Pavement Layers and Soils, Proceedings of 13th Baltic Sea Region Geotechnical Conference, Historical Experience and Challenges of Geotechnical Problems in Baltic Sea Region, 2016, 122-125—incorporated herein by reference in its entirety].

(23) TABLE-US-00002 TABLE 2 Composition of a wood fly ash Component Content, % Accuracy, ± % SiO.sub.2 43.1-47.6 ±0.7 SiO.sub.2 active 3.5-5.0 ±0.7 R.sub.2O.sub.3(Al.sub.2O.sub.3 + Fe.sub.2O.sub.3) 5.6-9.0 ±0.7 CaO 22.7-24.7 ±0.5 MgO 1.6-3.2 ±0.3 Fe.sub.2O.sub.3 1.1-1.3 ±0.1 K.sub.2O 4.3-4.9 ±0.3 Na.sub.2O 0.6-1.2 ±0.1 Al.sub.2O.sub.3═R.sub.2O.sub.3Fe.sub.2O.sub.3 4.4-7.9 ±0.5 SO.sub.3 5.0-8.3 ±0.5 Hydraulic modulus   2-2.8 — LoI (1000° C.) 4.5-5.1 —

(24) Other waste wood combustion materials, in addition to wood fly ash, similarly has high silica and CaO contents. Table 3 below illustrates various compositions of wood waste ash obtained from various sources, W1, W2, W3, W4 [Chowdhury, S. et al. The incorporation of wood waste ash as a partial cement replacement material for making structural grade concrete: An overview, Ain Shams Engineering Journal, 2015, 6 (2), 429-437—incorporated herein by reference in its entirety].

(25) TABLE-US-00003 TABLE 3 Composition of various wood waste ash SiO2 Al.sub.2O.sub.3 Fe.sub.2O.sub.3 CaO MgO TiO.sub.2 K.sub.2O W1 67.20 4.09 2.26 9.98 5.80 — — W2 78.92 0.89 0.85 0.58 0.96 — — W3 67.20 4.09 2.26 9.98 5.80 — — W4 31.80 28.00 2.34 10.53 9.32 — 10.38 Na.sub.2O SO.sub.3 P.sub.2O.sub.5 LOI (%) W1 0.08 0.45 0.48   4.67 W2 0.43 — —   8.40 W3 0.08 0.45 0.48   4.67 W4 6.50 — — 27.0

(26) Oil fly ash, which is obtained from combustion of oil-based sources such as heavy oil, diesel, and natural gas sources in power plant stations or water desalination plants, differs greatly in composition from coal and wood fly ash. Some exemplary oil sources include, but are not limited to, residual fuel oil, light Arabian crude oil, and heavy Arabian crude oil. The inventors have discovered that oil fly ash, preferably fly ash obtained from heavy oil combustion in power plants, provides an advantageous starting material for the methods described herein. Compared to coal and wood fly ash, oil fly ash has a high carbon content and low content of Si, Al, and Ca, as determined, for example, by X-ray diffraction, ASTM D7348, and/or ASTM C618 [Al-Malack et al. Characteristics of Fly ash Produced at Power and Water Desalination Plants Firing Fuel Oil, Int. J. Environ. Res., 2013, 7(2), 455-466—incorporated herein by reference in its entirety].

(27) In some embodiments, the oil fly ash employed herein (and thus the resultant ball milled and sonicated oil fly ash powder produced herein) has a carbon content of greater than 50 wt. %, preferably greater than 65 wt. %, preferably greater than 70 wt. %, preferably greater than 75 wt. %, preferably greater than 80 wt. %, preferably greater than 85 wt. %, and up to 95 wt. %, preferably up to 90 wt. %, based on a total weight of the oil fly ash. Oil fly ash (and thus the resultant ball milled and sonicated oil fly ash powder produced herein) has a higher carbon content than other types of fly ash, but lower than that of carbonaceous combustion products such as carbon black, which has a carbon content of 96-99.5 wt. % (and only 0.2-0.5 wt. % of oxygen containing materials).

(28) Table 4 shows an example oil fly ash composition in terms of major oxides present [Al-Degs, Y. S. et. al. Characterization and utilization of fly ash of heavy fuel oil generated in power stations, Fuel Processing Technology, 2014, 123, 41-46—incorporated herein by reference in its entirety]. In some embodiments, the oil fly ash (and thus the resultant ball milled and sonicated oil fly ash powder produced herein) has a SiO.sub.2 content of less than 3 wt. %, preferably less than 2 wt. %, preferably less than 1 wt. %, preferably less than 0.9 wt. %, based on a total weight of the oil fly ash.

(29) In some embodiments, the oil fly ash (and thus the resultant ball milled and sonicated oil fly ash powder produced herein) has an Al.sub.2O.sub.3 content of less than 3 wt. %, preferably less than 2 wt. %, preferably less than 1 wt. %, preferably less than 0.6 wt. %, based on a total weight of the oil fly ash.

(30) In some embodiments, the oil fly ash (and thus the resultant ball milled and sonicated oil fly ash powder produced herein) has a CaO content of less than 5 wt. %, preferably less than 4 wt. %, preferably less than 3 wt. %, preferably less than 2 wt. %, preferably less than 1 wt. %, based on a total weight of the oil fly ash.

(31) Compared to other types of fly ash, oil fly ash also typically has a higher MgO content. In some embodiments, the oil fly ash employed herein (and thus the resultant ball milled and sonicated oil fly ash powder produced herein) has a MgO content of 5-16 wt. %, preferably 8-15 wt. %, preferably 10-14.5 wt. %, preferably 12-14 wt. %, preferably 13-13.5 wt. %.

(32) Other oxides that may be present in the oil fly ash used herein (and thus the resultant ball milled and sonicated oil fly ash powder produced herein) include, but are not limited to, Fe.sub.2O.sub.3, in amounts of 0.2-6 wt. %, preferably 0.5-5 wt. %, more preferably 1-4 wt. %, as well as Na.sub.2O, in amounts of 0.1-4 wt. %, preferably 0.5-4.5 wt. %, more preferably 2-4 wt. %, each based on a total weight of the oil fly ash.

(33) TABLE-US-00004 TABLE 4 Example oil fly ash composition: major oxides Major oxides (%) MgO 13.12 Fe.sub.2O.sub.3 4.92 Na.sub.2O 3.24 Al.sub.2O.sub.3 0.52 SiO.sub.2 0.86 CaO 0.80

(34) Oil fly ash also contains higher levels of certain heavy metals, such as vanadium and nickel, compared to other types of fly ash. For example, oil fly ash contains 1,000-70,000 ppm, preferably 2,000-60,000 ppm, preferably 3,000-50,000 ppm, preferably 5,000-40,000 ppm, preferably 10,000-30,000 ppm of vanadium and 500-25,000 ppm, preferably 1,000-20,000 ppm, preferably 1,500-15,000 ppm, preferably 2,000-10,000 ppm, preferably 2,500-8,000 ppm of nickel as determined by atomic adsorption spectroscopy and/or inductively coupled argon plasma/inductively coupled plasma mass spectroscopy (ASTM D 3682-91, ASTM D 3683-94, EPA 6020-B). Oil fly ash also contains a high concentration of other valuable metals/elements such as Pr, Ce, Tb, Dy, Yb, Te, and Mo, compared to other types of fly ash. For example, oil fly ash may contain up to 10,000 ppm, for example 500-10,000 ppm, or 1,000-5,000 ppm of Pr, Ce, Tb, Dy, Yb, Te, and Mo in total (combined).

(35) As will become clear, the distinct chemical composition of oil fly ash, compared to other types of fly ash or waste combustion materials, permits materials to be made (i.e., ball milled and sonicated oil fly ash powder) which possess superior pollutant adsorption properties, while also improving vanadium and nickel recovery, and optionally the recovery of other valuable metals during the manufacturing process.

(36) Oil fly ash powder obtained from combustion facilities (e.g., from an electrostatic precipitator) typically has micron sized particles in a range of 2-70 μm, or 5-60 μm, or 10-50 μm, or 20-40 μm, and sometimes even larger particles sizes are obtained. The oil fly ash typically has a spherical or substantially spherical shape (i.e., where the sides are rounded or well-rounded) with a sponge-like (i.e., porous) appearance (see FIG. 2A) While such raw oil fly ash has some adsorption capability, superior adsorptive properties can be bestowed by ball milling (Si) the oil fly ash particles and reducing the particle size. In some embodiments, the oil fly ash is ball milled under appropriate conditions to achieve a desired morphology and particle size. In preferred embodiments, the oil fly ash is ball milled to provide ball milled oil fly ash particles with an average particle size of less than 1 μm. In most preferred embodiments, the ball milled oil fly ash particles have a bimodal particle size distribution with nanoparticles having an average particle size of 10-100 nm, preferably 20-90 nm, preferably 30-80 nm, preferably 40-70 nm, and sub-micron sized particles having an average particle size of 0.2-0.9 μm, preferably 0.3-0.8 μm, preferably 0.4-0.7 μm, preferably 0.5-0.6 μm. In some embodiments, the ball milled oil fly ash particles are very angular (corners sharp and jagged), angular, sub-angular, or sub-rounded using visual inspection similar to characterization used in the Shepard and Young comparison chart, and possess a jagged flake-like morphology (FIGS. 3A-3B). Most preferably, the sub-micron sized particles are very angular, angular, and sub-angular flake-like structures, while the nanoparticles appear more as sub-angular or sub-rounded flake-like structures.

(37) It has been unexpectedly discovered that ball milling the oil fly ash is superior to other methods for reducing particle size, such as other types of grinding, milling, etc., in terms of both adsorption capacity and leaching of heavy metals. While not bound by theory, this may be due to the ball milling providing an advantageous mixture (i.e., bimodal particle size distribution) of both nanoparticles and sub-micron sized particles, and/or providing particles with particular morphologies as discussed above.

(38) The oil fly ash is preferably ball milled in a high energy ball mill. For example, a standard ball mill, a planetary mill (e.g., larger diameter central disk and vials/smaller diameter two cylindrical ball mills on a roller table), a vibration mill, an attritor—stirring ball mill, a pin mill, or a rolling mill may be employed. The vials and balls used for the ball milling may be one or more of agate (cryptocrystalline silica), corundum (Al.sub.2O.sub.3), zirconium oxide (ZrO.sub.2), stainless steel (Fe, Cr, Ni), tempered steel (Fe, Cr), and tungsten carbide (WC). In some embodiments, vials lined with tungsten carbide, and which are filled with stainless steel balls (e.g., SS 316 6 mm ball bearings) are employed. In some embodiments, the oil fly ash is ball milled in tungsten carbide vials with tungsten carbide balls. Other procedures may also be used [Numan Salah, Sami S. Habib, Zishan H. Khan, Ahmed Alshahrie, Adnan Memic and Attieh A. Al-ghamdi, Carbon Rich Fly Ash and their Nanostructures, Carbon letters 19, 23 (2016)—incorporated herein by reference in its entirety].

(39) In some embodiments, the weight of oil fly ash (g) per volume (1,000 cm.sup.3) of vials used in the ball milling is 50-150 g/1,000 cm.sup.3, preferably 75-130 g/1,000 cm.sup.3, preferably 90-110 g/1,000 cm.sup.3. The ball to powder ratio (BPR) or charge ratio represents the weight ratio of the milling balls to the oil fly ash charge. The BPR used herein may vary widely, for example from 1:1 to 100:1, but most preferably is from 8:1 to 12:1, or from 9:1 to 11:1, or 10:1.

(40) In some embodiments, the oil fly ash is ball milled at a rotational speed of 100 to 400 rpm, preferably 150 to 350 rpm, preferably 200 to 300 rpm, although rotational speeds outside of these ranges may also be employed herein depending for example on the ball milling duration and various other factors. In some embodiments, the oil fly ash particles are ball milled for at least 2 hours, preferably at least 3 hours, preferably at least 4 hours, preferably at least 5 hours, preferably at least 6 hours, preferably at least 8 hours, and up to 12 hours, preferably up to 11 hours, preferably up to 10 hours, preferably up to 9 hours.

(41) The ball milled oil fly ash particles are then mixed with an aqueous medium and sonicated (S2) to form a mixture comprising ball milled and sonicated oil fly ash particles and a supernatant. Preferably the aqueous medium is tap water, distilled water, twice distilled water, deionized water, deionized distilled water, reverse osmosis water, or other water sources having a relatively low content of metals or dissolved solids. Preferably, the water has a conductivity at less than 10 μS.Math.cm.sup.−1, preferably less than 1 μS.Math.cm.sup.−1, a resistivity greater than 0.1 MΩ.Math.cm, preferably greater than 1 MΩ.Math.cm, more preferably greater than 10 MΩ.Math.cm, a total solid concentration less than 5 mg/kg, preferably less than 1 mg/kg, and a total organic carbon concentration less than 1000 μg/L, preferably less than 200 μg/L, more preferably less than 50 μg/L at 25° C. Any amount of water may be mixed with the ball milled oil fly ash particles as long as sufficient mixing can take place during the sonication step. For example, for every 1 gram of ball milled oil fly ash particles, the ball milled oil fly ash particles may be combined with 0.5-20 g, preferably 1-15 g, preferably 2-10 g of aqueous medium, and the combination is then sonicated. Organic solvents which are miscible in water may also be employed herein, so long as the aqueous medium contains a higher content of water than the optional organic solvent(s). Exemplary organic solvents include, but are not limited to, C.sub.1 to C.sub.4 lower alkanols, for example, methanol, ethanol, isopropanol, butanol; polyols and polyol ethers, for example, glycol, 1,3-propanediol, 1,3-butanediol, 2-butoxyethanol, propylene glycol, diethylene glycol, ethylene glycol monomethyl ether, and propylene glycol monomethyl ether; acetone; acetonitrile; 1,4-dioxane; tetrahydrofuran; dimethyl sulfoxide; and the like.

(42) In some embodiments, the ball milled oil fly ash particles are sonicated at a frequency of 5-30 kHz, preferably 10-25 kHz, preferably 15-20 kHz, and with a power intensity of 25-50 W/cm.sup.2, preferably 30-45 W/cm.sup.2, preferably 35-40 W/cm.sup.2. The temperature at which the sonication takes place can vary, but is typically in a range of 20−80° C., preferably 22-70° C., preferably 24-60° C., preferably 26-40° C.

(43) In some embodiments, the ball milled oil fly ash particles are sonicated in the aqueous medium for at least 30 minutes, preferably at least 1 hour, preferably at least 2 hours, preferably at least 3 hours, preferably at least 4 hours, and up to 12 hours, preferably up to 10 hours, preferably up to 8 hours, preferably up to 6 hours.

(44) As will become clear, sonicating the ball milled oil fly ash particles provides ball milled and sonicated oil fly ash powder having superior adsorption and leaching of heavy metals properties compared to both unmodified (i.e., raw) fly ash and fly ash which has been ball milled alone. The sonication step may aid in breaking up any aggregates formed during the ball milling process, further reducing the particle size, and/or leaching at least some of the heavy metals such as vanadium and nickel or other valuable metals/elements from the ball milled oil fly ash into the supernatant.

(45) After sonicating the mixture as described above, additional agitation methods may optionally be performed, for example, the mixture may be further stirred and/or shaken with a mechanical stirrer and/or a mechanical shaker (S3). The additional agitation steps may be performed in the same aqueous medium used for the sonication, or alternatively, the ball milled and sonicated oil fly ash particles may be removed from the aqueous medium used in the sonication step, and then re-suspended in a second aqueous medium which may be different than, or the same as, that used for the sonication. Such optional agitation steps, when employed, may further effect leaching of vanadium and nickel or other valuable metals/elements from the ball milled and sonicated oil fly ash powder. In some embodiments, the ball milled and sonicated oil fly ash particles are shaken and/or stirred for at least 30 minutes, preferably at least 1 hour, preferably at least 2 hours, preferably at least 3 hours, and up to 10 hours, preferably up to 5 hours.

(46) The method may also optionally involve the addition of exogenous leaching agents, for example NH.sub.4Cl and/or NH.sub.3 for forming nickel leachates and Na.sub.2CO.sub.3 for forming vanadium leachates, to further aid in extracting these metals from the ball milled and sonicated oil fly ash particles. If employed, leaching agents like NH.sub.4Cl and Na.sub.2CO.sub.3 are preferred because they depress the dissolution of iron and aluminum from the ash material and hence are selective for vanadium and nickel respectively. In some embodiments, the exogenous leaching agents are sodium hydroxide or sulfuric acid. Methods for carrying out such leaching procedures are known to those of ordinary skill in the art.

(47) After sonicating and optionally stirring/shaking and/or optionally adding exogenous leaching agents, the ball milled and sonicated oil fly ash particles are then separated from the supernatant (S4), for example by filtration, centrifugation, decantation, and the like, and dried to form the ball milled and sonicated oil fly ash powder. In some embodiments, the ball milled and sonicated oil fly ash particles are dried at a temperature of 20-150° C., preferably 50-120° C., preferably 60-100° C., preferably 80-90° C. under standard pressure or under vacuum to form the ball milled and sonicated oil fly ash powder.

(48) The ball milled and sonicated oil fly ash powder thus obtained has a similar chemical composition to raw oil fly ash (i.e., oil fly ash which has not been processed using a ball mill and sonication) in terms of carbon, Si, Al, Ca, MgO, Fe.sub.2O.sub.3, and Na.sub.2O content. That is, the ball milled and sonicated oil fly ash powder has a wt. % of carbon, Si, Al, Ca, MgO, Fe.sub.2O.sub.3, and Na.sub.2O which is the same or essentially the same as the wt. % previously listed for oil fly ash.

(49) The morphology and particle size of the ball milled and sonicated oil fly ash powder is also the same as previously disclosed for the ball milled oil fly ash particles (i.e., very angular, angular, or sub-angular flake-like morphology with an average particle size of less than less than 1 μm, preferably with a bimodal particle size distribution of nanoparticles and sub-micron sized particles).

(50) In some embodiments, the ball milled and sonicated oil fly ash powder has a BET surface area of 6-30 m.sup.2/g, preferably 10-28 m.sup.2/g, preferably 15-26 m.sup.2/g, preferably 20-24 m.sup.2/g, as determined by a Brunauer-Emmett-Teller- (BET-) analyzer (Nova 3200e, Quantachrome Instruments, USA). In some embodiments, the ball milled and sonicated oil fly ash powder has a bulk density (by gas) of 0.3-0.6 g/cm.sup.3, preferably 0.35-0.55 g/cm.sup.3, preferably 0.4-0.5 g/cm.sup.3, as determined by ASTM D 6683-01.

(51) However, the ball milled and sonicated oil fly ash powder differs from the oil fly ash starting material in terms of at least vanadium and nickel content, and preferably also in terms of other valuable metal content. The ball milled and sonicated oil fly ash powder contains less vanadium and nickel, for example, 100-65,000 ppm, preferably 300-50,000 ppm, preferably 500-30,000 ppm, preferably 1,000-10,000 ppm, preferably 2,000-5,000 ppm of vanadium, and 50-20,000 ppm, preferably 100-20,000 ppm, preferably 500-15,000 ppm, preferably 1,000-10,000 ppm, preferably 1,500-8,000 ppm of nickel as determined by atomic adsorption spectroscopy and/or inductively coupled argon plasma/inductively coupled plasma mass spectroscopy (ASTM D 3682-91, ASTM D 3683-94, EPA 6020-B). This may be explained, at least in part, due to the occurrence of vanadium and nickel leaching from the ball milled oil fly ash particles into the aqueous medium during the sonication and optional shaking/stirring steps, thereby forming a supernatant more rich in vanadium and nickel. Preferably, this same trend similarly holds for other valuable metals such as Pr, Ce, Tb, Dy, Yb, Te, and Mo.

(52) Surprisingly, the combination of the ball milling and sonication steps has been found to improve the amount of vanadium and nickel released from the fly ash material into the supernatant under a given set of circumstances, with ball milled and sonicated fly ash >ball milled fly ash > to oil fly ash (which has been either ball milled or sonicated). For example, without the use of exogenous leaching agents, methods involving both ball milling and sonication provide 20-50%, 25-45%, 30-40% more vanadium and 40-85%, 43-80%, 45-75%, 50-70% more nickel compared to a process employing raw oil fly ash which is shaken and/or stirred in the aqueous medium (i.e., has not been ball milled or sonicated), with percentages based on a ppm of vanadium/nickel in the supernatant. When exogenous leaching agents (e.g., NH.sub.4Cl, NH.sub.3 sodium hydroxide, and Na.sub.2CO.sub.3) are employed, higher vanadium/nickel recoveries in the supernatant are possible, with ball milled and sonicated oil fly ash powder providing the highest leaching rates and amounts.

(53) Once the ball milled and sonicated oil fly ash particles are separated from the mixture, leaving behind a supernatant, the supernatant can be collected and processed for recovery of vanadium, nickel, and optionally any other valuable metal species (e.g., Pr, Ce, Tb, Dy, Yb, Te, and/or Mo) present therein (S5). For example, the vanadium and nickel metal species, as well as any other valuable metal leached from the ball milled oil fly ash particles during processing (e.g., during sonication, optional agitating, optional exogenous leaching agent addition, etc.), and which are present in the supernatant, can be collected using a crystal bar process, a precipitation process, or a solvent extraction process.

(54) In some embodiments, the vanadium and nickel metal species, and optionally any other valuable metals present are collected using a crystal bar process, for example by the Van Arkel deBoer iodide process [O. N. Carlson and C. V. Owen, Preparation of High-Purity Vanadium Metals by the Iodide Refining Process, Journal of the Electrochemical Society. 108, 88 (1961)—incorporated herein by reference in its entirety] or the Kroll process. Crystal bar processes primarily involve the formation of the metal iodides and their subsequent decomposition to yield pure metal, and such methods are known to those of ordinary skill in the art.

(55) In some embodiments, the vanadium and nickel metals are leached with one or more of NH.sub.4Cl, NH.sub.3 sodium hydroxide, and Na.sub.2CO.sub.3 for forming leachates as mentioned above, and then these metals may be collected using a precipitation method. For example, nickel metal species can be collected from the supernatant by the addition of Na.sub.2S, thus forming NiS precipitates. In some embodiments, vanadium metal is collected by the addition of sodium hydroxide, sodium carbonate, or ammonia to the supernatant until a pH of 7-9, preferably pH of 8 is achieved. Then the supernatant is acidified, for example by addition of sulfuric acid, to achieve a pH of 4-6, preferably 5-5.5. The supernatant may then be optionally extracted with an organic phase comprising trimethylamine and toluene, and the organic phase may be optionally back extracted with sodium carbonate. Next, enough ammonium chloride is added to the aqueous layer to reach a final ammonium chloride concentration of about 0.8-1.2 M, preferably 0.9-1.1 M, preferably about 1M, to bring about vanadium precipitation in the form of NH.sub.4VO.sub.3. [Al-Gouti, M. A. et al. Extraction and separation of vanadium and nickel from fly ash produced in heavy fuel power plants, Chemical Engineering Journal, 2011, 173, 191-197; Akita, S., Maeda, T. and Takeuchi, H. (1995), Recovery of vanadium and nickel in fly ash from heavy oil. J. Chem. Technol. Biotechnol., 62: 345-350; R. Navarro, J. Guzman, I. Saucedo, J. Revilla, E. Guibal, Vanadium recovery from oil fly ash by leaching, precipitation and solvent extraction processes, Waste Management 27, 425 (2007)—each incorporated herein by reference in its entirety]

(56) In some embodiments, the vanadium and nickel metals are collected by a solvent extraction process. For example, the supernatant may be mixed with an organic phase such as trioctylamine, kerosene, and/or isodecanol, and then treated with hydrogen peroxide.

(57) A Method of Removing an Organic Pollutant from Water

(58) The ball milled and sonicated oil fly ash powder has been found to be a powerful adsorbent, with superior adsorbent properties to oil fly ash (i.e., which has not been ball milled or sonicated), ball milled oil fly ash particles (i.e. not sonicated), and sonicated oil fly ash (i.e., fly ash which is sonicated but not ball milled). The ball milled and sonicated oil fly ash powder thus obtained by the methods described herein may be used for the removal of various pollutants, including, but not limited to, organic pollutants (e.g., pharmaceuticals, polycyclic aromatic hydrocarbons, organic dyes, pesticides, polychlorinated biphenyls), heavy metals (e.g., mercury, copper, chromium, lead), microorganisms (e.g., bacteria), or any other unwanted component present in water (S6, FIG. 1).

(59) The method involves contacting the water with the ball milled and sonicated oil fly ash powder of the present disclosure, in one or more of its embodiments, to adsorb the pollutant onto the ball milled and sonicated oil fly ash powder. Non-limiting examples of water sources include, but are not limited to, surface water that collects on the ground or in a stream, aquifer, river, lake, reservoir or ocean, ground water that is obtained by drilling wells, run-off, industrial wastewater (e.g., wastewater produced by petrochemical and manufacturing industries), public water storage towers, public recreational pools and/or bottled water. In some embodiments, the water is sourced from fresh water (contains less than 0.05% salinity), brackish water (contains 0.05-3% dissolved salts), saline or seawater (contains 3-5% dissolved salts), or brine (contains greater than 5% dissolved salts), with % being a % by weight based on the total solution weight). In some embodiments, the water has a pH in the range of 5-9, preferably 5.5-8.5, preferably 6-8.0, preferably 6.5-7.5, or about 7.0 during the contacting.

(60) The pollutant may be present in the water at concentrations up to 100 ppm, preferably up to 90 ppm, preferably up to 80 ppm, preferably up to 70 ppm, preferably up to 60 ppm, preferably up to 50 ppm, preferably up to 40 ppm, preferably up to 30 ppm, preferably up to 20 ppm, preferably up to 10 ppm, preferably up to 8 ppm, preferably up to 4 ppm, preferably up to 2 ppm, although amounts of pollutants above these ranges may also be removed by increasing the amount of the ball milled and sonicated oil fly ash powder employed, for example.

(61) In some embodiments, the pollutant is an organic pollutant, for example, an organic dye. The organic dye may be an acid dye, for example Yellow No. 203 (D&C Yellow No. 10, color index (CI) given as CI 47005), Orange No. 205 (D&C Orange No. 4, CI 15510), Red No. 227 (D&C Red No. 33, CI 17200), Violet No. 401 (Ext. D&C Violet No. 2, CI 07301), and Black No. 401, CI 20470); an indole-based dye (e.g., isatin, 5,6-dihydroxy indole, indigo); pyrimidine-based dyes (e.g., alloxan); indane-based dyes (e.g., ninhydrin); a nitrobenzene-based dye (e.g., 1,4-diamino-2-nitrobenzene, 1-amino-2-nitro-4-β-hydroxyethylaminobenzene, 1-amino-2-nitro-4-bis(β-hydroxyethyl)aminobenzene, 1,4-bis(β-hydroxyethylamino)-2-nitrobenzene, 1,2-diamino-4-nitrobenzene, or the corresponding nitropyridine variants); a quinone-based dye (e.g., anthraquinone, 1-N-methylmorpholiniumpropylamino-4-hydroxyanthraquinone, 1-aminopropylamino-4-methylaminoanthraquinone, 1-aminopropylaminoanthraquinone, 5-β-hydroxyethyl-1,4-diaminoanthraquinone, 2-aminoethylaminoanthraquinone, 1,4-bis(β,γ-dihydroxypropylamino)anthraquinone, lawsone, juglone, alizarin, purpurin, carminic acid, kermesic acid, spinulosin, Disperse Red 15, Solvent Violet 13, Disperse Violet 1, Disperse Violet 4, Disperse Blue 1, Disperse Violet 8, Disperse Blue 3, Disperse Red 11, Disperse Blue 7, Basic Blue 22, Disperse Violet 15, Basic Blue 99); an azo-based dye (e.g., 1,3-dimethyl-2-[[4-(dimethylamino)phenyl]azo]-1H-imidazolium chloride, 1,3-dimethyl-2-[(4-aminophenyl]azo]-1H-imidazolium chloride, 1-methyl-4-[(methylphenylhydrazono)methyl]pyridinium methyl sulfate, Congo red, Disperse Red 17, Basic Red 22, Basic Red 76, Basic Yellow 57, Basic Brown 16, Basic Brown 17, Disperse Black 9); an azine-based dye (e.g., Basic Blue 17, Basic Red 2); a triarylmethane-based dye (e.g., Brilliant green, Basic Green 1, Basic Violet 3, Basic Violet 14, Basic Blue 7, Basic Blue 26, crystal violet); an indoamine-based dye (e.g., 2-β-hydroxyethylamino-5-[bis(β-4′-hydroxyethyl) amino]anilino-1,4-benzoquinone, 2-β-hydroxyethylamino-5-(2′-methoxy-4′-amino)anilino-1,4-benzoquinone, 3-N-(2′-chloro-4′-hydroxy)phenylacetamino-6-methoxy-1,4-benzoquinoneimine, 3-N-(3′-chloro-4′-methylamino)phenylureido-6-methyl-1,4-benzoquinoneimine, 3-[4′-N-(ethylcarbamylmethyl)amino]phenylureido-6-methyl-1,4-benzoquinoneimine); a catechol-based dye (e.g., purpurogallin, protocatechaldehyde); a fluorescent dye, such as those of the naphthalimide, cationic or non-cationic coumarin, xanthenodiquinolizine, azaxanthene, naphtholactam, azlactone, oxazine, thiazine (e.g., methylene blue), or dioxazine families, or polycationic fluorescent dyes of the azo, azomethine or methine families; as well as mixtures thereof. In preferred embodiments, the organic dye is at least one selected from the group consisting of methylene blue, Congo red, brilliant green, and crystal violet.

(62) The contacting may involve mixing the ball milled and sonicated oil fly ash powder with the water, for example by adding the ball milled and sonicated oil fly ash powder to the water contained in a vessel or holding pond, followed by optional heating and/or stirring. In some embodiments, the contacting is performed at ambient temperature (i.e., 20-25° C.). Alternatively, the mixture may be heated to 30-80° C., or 40-70° C., or 50-60° C. The resulting mixture may be allowed to settle, or alternatively may be stirred, for example with a mechanical or magnetic stirrer.

(63) In some embodiments, the ball milled and sonicated oil fly ash powder may be immobilized onto a filter or inside a cartridge filter and the water (which may optionally be at elevated temperature) may be passed through. The eluent leaving the filter or cartridge may be optionally recycled back into the filter/cartridge such that the contacting is performed continuously until an adequate amount of the pollutant is removed from the water.

(64) In some embodiments, the ball milled and sonicated oil fly ash powder is contacted with the water for 5-60 min., preferably 10-25 min., preferably 15-20 min. While the amount of the ball milled and sonicated oil fly ash powder employed for removing the pollutant from the water may vary depending on the concentration of the pollutant in the water or other factors, typically about 0.01-1 g, preferably 0.05-0.5 g, preferably 0.1-0.4 g, preferably 0.15-0.3 g, or about 0.2 g of the ball milled and sonicated oil fly ash powder is employed per L of the water during the contacting.

(65) After contacting for a suitable amount of time to adsorb at least a portion of the pollutant present in the water onto the ball milled and sonicated oil fly ash powder, the ball milled and sonicated oil fly ash powder may then be separated from the water, for example by filtration, centrifugation, decantation, elution of the water through a cartridge or filter of immobilized ball milled and sonicated oil fly ash powder, to produce water having a lowered concentration of the pollutant. In some embodiments, the method removes at least 75%, preferably at least 80%, preferably at least 85%, preferably at least 90%, preferably at least 95%, preferably at least 97%, preferably at least 98%, preferably at least 99%, or complete removal of the organic pollutant from the water relative to an initial concentration. The % removal can be calculated by measuring the absorbance spectrum of the water before and after the contacting using UV-vis, with the absorbance intensity being correlated to the concentration of a pollutant using a standard curve. In some embodiments, when the water contains up to 30 ppm of the pollutant, at least 50%, preferably at least 60%, preferably at least 70%, preferably at least 80%, preferably at least 90% of the pollutant is adsorbed onto the ball milled and sonicated oil fly ash powder after at least 5 minutes of contacting. In some embodiments, when the water contains up to 30 ppm of the pollutant, at least 75%, preferably at least 80%, preferably at least 90%, of the pollutant is adsorbed onto the ball milled and sonicated oil fly ash powder after at least 10 minutes of contacting.

(66) After the contacting and after the ball milled and sonicated oil fly ash powder is removed, the resulting water preferably has less than 25 ppm, preferably less than 20 ppm, preferably less than 18 ppm, preferably less than 16 ppm, preferably less than 14 ppm, preferably less than 12 ppm, preferably less than 10 ppm, preferably less than 8 ppm, preferably less than 6 ppm, preferably less than 4 ppm, preferably less than 2 ppm, preferably less than 1 ppm, preferably less than 500 ppb, preferably less than 300 ppb, preferably less than 100 ppb of the pollutant, most preferably the water is substantially free (e.g., 0 wt. %) of the pollutant.

(67) Once removed from the water, the ball milled and sonicated oil fly ash powder having adsorbed pollutant may optionally be recycled upon treatment with an organic solvent (e.g., methanol, acetone, etc.), a mineral acid (e.g., hydrochloric acid, sulfuric acid), and/or a hydroxide base (e.g., sodium hydroxide, potassium hydroxide) to desorb the pollutant. After drying, the ball milled and sonicated oil fly ash powder may then be reused in the method described herein with no or minimal loss in absorbency.

(68) Having generally described this disclosure, a further understanding can be obtained by reference to certain specific examples which are provided herein for purposes of illustration only and are not intended to be limiting unless otherwise specified. The examples below are intended to further illustrate protocols for preparing the ball milled and sonicated oil fly ash powder, methods of collecting vanadium and nickel metals during said preparations, and methods of remediating pollutants and they are not intended to limit the scope of the claims.

Example 1

(69) Ball Milling

(70) Methods are illustrated in FIG. 1. Carbon rich fly ash (Oil fly ash) was obtained from Jeddah power plant, Saudi Arabia. The oil fly ash powder is of micro size particles (FIG. 2A). Samples from this ash were grounded by a high energy ball milling system for a proper time until they reached to a mixture of nanoscale and submicron sized particles (FIG. 2B). The nano and submicron sized particles are clearly observed, with the nanostructures having particles with sizes in the range 10-100 nm, and with submicron size particles being in the range 0.1-1 μm (FIGS. 3A-2B).

Example 2

(71) Sonication/Agitation

(72) Then the ball milled powder sample was sonicated in a water medium (DI water) to further reduce the particle size and release the metal ions available in the oil fly ash. They can be sonicated using a probe sonicator or sonicator bath for a determined time (i.e. 1-3 hours). Then the solution was agitated either by shaking or stirring or any other methods to further release the metal ions. After that, the precipitated powder was separated from the water solution. The supernatant contains the metal ions available in the oil fly ash like vanadium and nickel, which can be further purified by the conventional methods. The remaining BMSFA powder was dried in an oven and used for the adsorption of different organic pollutants in waste water.

Example 3

(73) Adsorption

(74) Adsorption of organic pollutants from waste water using ball milled and sonicated oil fly ash (BMSFA) powder was successfully achieved. The adsorption experiments were conducted on synthetic solutions of the desired organic pollutants i.e. methylene blue, Congo red, brilliant green and crystal violet. Effect of different parameters like adsorption time, pollutant concentration, etc. were examined. The obtained results showed almost complete adsorptions of these pollutants using BMSFA in a short time.

(75) FIG. 4 shows a UV-vis absorption spectra of Congo red dye pollutant (4 ppm) adsorbed by the ball milled and sonicated oil fly ash at different times. The peaks of this pollutant decrease with increasing the time and lost all of its intensity at 30 min indicating a complete removal of this dye from the waste water.

(76) FIG. 5 shows a UV-vis absorption spectra of crystal violet dye pollutant (4 ppm) adsorbed by the ball milled and sonicated oil fly ash at different times. The peaks of this pollutant decreases with increasing the time and lost all of more than 97% of its intensity at 30 min.

(77) FIG. 6 shows a UV-vis absorption spectra of brilliant green dye pollutant (4 ppm) adsorbed by the ball milled and sonicated oil fly ash at different times. The peaks of this pollutant decreases with increasing the time and lost more than 94% of its intensity at 30 min.

(78) FIG. 7 shows a UV-vis absorption spectra of methylene blue dye pollutant (4 ppm) adsorbed by the ball milled and sonicated oil fly ash at different times. The peaks of this pollutant decreases with increasing the time and lost more than 80% of its intensity at 30 min.

(79) FIG. 8 shows the adsorption of Congo red dye at different concentrations by the ball milled and sonicated oil fly ash as a function of time. The curves shows that the lower concentrations were adsorbed in a very short time i.e. <5 min.

(80) FIG. 9 shows a UV-vis absorption spectra of 8 ppm mixed dye (2 ppm methylene blue+2 ppm crystal violet+2 ppm brilliant green+2 ppm Congo red) pollutant adsorbed by the ball milled and sonicated oil fly ash at different times. The peaks of this pollutant decreases with increasing the time and lost more than 90% of its intensity at 60 min.

Example 4

(81) Metal Extraction

(82) Moreover, metal extraction from this BMSFA powder was significantly improved using this method. The extraction was found to be in higher quantities compared to that of the original oil fly ash powder. Valuable metals available in the oil fly ash like vanadium and nickel can be easily extracted in higher amounts using this approach through a water medium, then can be moved to further purification. The extracted vanadium and nickel ions can be further isolated and purified by the regular process i.e. by Van Arkel deBoer iodide process for vanadium ion [O. N. Carlson and C. V. Owen, Preparation of High-Purity Vanadium Metals by the Iodide Refining Process, Journal of the Electrochemical Society. 108, 88 (1961)—incorporated herein by reference in its entirety] or by a two-step leaching process [S. Akita, T. Maeda, H. Takeuchi, Recovery of vanadium and nickel in fly ash from heavy oil, Journal of Chemical Technology and Biotechnology. 62, 345 (1995)—incorporated herein by reference in its entirety]. In the leaching, nickel can be dissolved with NH.sub.4Cl in the first step, followed by vanadium leaching with Na.sub.2CO.sub.3 in the second step [S. Akita, T. Maeda, H. Takeuchi, Recovery of vanadium and nickel in fly ash from heavy oil, Journal of Chemical Technology and Biotechnology. 62, 345 (1995)—incorporated herein by reference in its entirety]. Metal recovery from these leachates involving either solvent extraction or selective precipitation [R. Navarro, J. Guzman, I. Saucedo, J. Revilla, E. Guibal, Vanadium recovery from oil fly ash by leaching, precipitation and solvent extraction processes, Waste Management 27, 425 (2007)—incorporated herein by reference in its entirety]. Solvent extraction can be done by “mixing the leachate with an organic phase (i.e. Kerosene and isodecanol). Then the leachates can be treated with hydrogen peroxide”. In the precipitation method the leachates can be “precipitated using sodium hydroxide. The pH of the solutions can be controlled to pH 5-6 using sulfuric acid. Ammonium chloride can be added to the solution to reach a final concentration of 1 M. The precipitate then can be filtered [R. Navarro, J. Guzman, I. Saucedo, J. Revilla, E. Guibal, Vanadium recovery from oil fly ash by leaching, precipitation and solvent extraction processes, Waste Management 27, 425 (2007)—incorporated herein by reference in its entirety].

(83) Table 5 demonstrates ICP results of the concentration of nickel and vanadium ions extracted from (1) oil fly ash (2) 8 hours ball milled oil fly ash (3) 8 hours ball milled and 2 hours sonicated oil fly ash.

(84) TABLE-US-00005 TABLE 5 Ni V SN Sample (ppm) (ppm) 1 Oil fly ash 41.0821 143.7492 2 8 hours ball milled oil fly ash 49.6681 161.7462 3 8 hours ball milled + 2 hours 73.8015 207.0298 sonicated oil fly ash

(85) These results show that this approach is quite effective on solving three problems: (1) making use for the oil fly ash, which is a waste byproduct that creates environmental problems, (2) treating the industrial waste water by cheap effective materials (3) efficiently extracting the useful metals available in the BMSFA like vanadium and nickel in higher quantities compared to that of the original oil fly ash powder.

(86) Thus, the foregoing discussion discloses and describes merely exemplary embodiments of the present disclosure. As will be understood by those skilled in the art, the present disclosure may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. Accordingly, the disclosure of the present invention is intended to be illustrative, but not limiting of the scope of the disclosure, as well as other claims. The disclosure, including any readily discernible variants of the teachings herein, defines, in part, the scope of the foregoing claim terminology such that no inventive subject matter is dedicated to the public.