Multilayer film, in particular sealing film

Abstract

The invention relates to a multilayer film, especially sealing film, suitable as food packaging, especially as packaging for food containers, drinks capsules, coffee capsules or the like, wherein the film consists of at least one first layer and at least one second layer, wherein at least one of the layers of the film is a biodegradable and home-compostable plastic.

Claims

1. A multilayer film as packaging for at least one of food containers, drinks capsules, and coffee capsules, wherein the film consists of at least one first layer and at least one second layer.

2. The film as claimed in claim 1, wherein the film consists of at least one first layer, at least one second layer, and at least one third layer or film ply.

3. The film as claimed in claim 1, wherein the first layer consists of filter paper, and the second layer consists of a gas-impermeable film.

4. The film as claimed in claim 3, wherein the gas-impermeable film comprises cellulose acetate and/or regenerated cellulose.

5. The film as claimed in claim 3, wherein the gas-impermeable film layer comprises of cellulose acetate and/or regenerated cellulose, and forms a layer coated on one and/or both sides with polyvinylidene chloride.

6. The film as claimed in claim 3, wherein the gas-impermeable film comprises a gastight plastic.

7. The film as claimed in claim 1, wherein at least one of the layers of the film is a biodegradable and home-compostable plastic.

8. The film as claimed in claim 7, wherein the first and/or third layer is formed by a polymer web and consists of one of the following materials, or a mixture thereof: PBS/PBSA, PLA, PHA, S.sup.2PC-PBS, S.sup.2PC-PB SA, S.sup.2PC PBS/PBSA.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0016] Advantages and embodiments by way of example of the invention are described in greater detail hereinafter with reference to the drawings.

[0017] FIG. 1 shows an exemplary film according to an embodiment of the invention.

DETAILED DESCRIPTION

[0018] The object of the invention is achieved, for example, by means of a film that has been developed on the basis of S.sup.2PC-PBS. The thickness of the film here may be between 50 μm and 1500 μm, with particular preference for use of the 300 μm version.

[0019] The object of the invention is also achieved by a film in a multilayer composite, in which an interlayer of about 15 to 50 μm, preferably about 30 μm, of PVOH or “G polymer” is used. This allows the film to achieve an oxygen barrier effect of up to 0.4 cm.sup.3, m.sup.2×d×bar.

[0020] The multilayer method may also be applied to the capsule wall material. For this purpose, the coffee capsule is provided in a convection method in which the barrier layer consists of PVOH or G polymer. In this way, it is likewise possible to achieve high oxygen barrier values. These constitute a preferred execution variant of the invention.

[0021] A further variant for achievement of the object consists of a multilayer film, said film consisting of one or two plies of filter paper (in principle, these are papers that are also used for tea filters) and one ply (layer) of polymer film. The layer of filter paper and the polymer film, for example of S.sup.2PC-PBS, PBS, PBS/PBSA, PLA, PHA or the like, are bonded, e.g. laminated, to one another by a lamination process.

[0022] Also particularly useful in accordance with the invention as polymer film is a mixture of PBS/PBSA.

[0023] The advantage of the paper ply is that it is naturally porous; the advantage of the polymer film is that it is gas-impermeable. This is also the case to a sufficient degree when the polymer film consists of a home-compostable plastic, e.g. S.sup.2PC-PBS, PBS PLA or the like.

[0024] The filter paper ply may alternatively also be formed by a ply/layer, e.g. web layer, composed of polymer fibers of compostable raw materials, especially home-compostable raw materials, for example S.sup.2PC-PBS, PBS, PBSA, mixture of PBS/PBSA, PLA, PHA, or mixtures thereof.

[0025] The aforementioned film plies of the multilayer composite may all be configured such that the film has a total thickness of preferably below 0.2 mm.

[0026] An example of this film shown in the drawing is shown in FIG. 1.

[0027] It is clearly apparent therein that the sealing film consists of a first, second and third (optional) layer, namely a first layer of porous filter paper having a thickness of about 40-100 μm.

[0028] This is followed by a gas-impermeable film having a thickness in the range between 10 μm and 30 μm, preferably in the range of 13-25 μm, more preferably 14-19 μm.

[0029] This is in turn followed by a porous filter paper having a thickness of about 30 to 100 μm.

[0030] This film composed of the three layers described is bonded, laminated, welded etc. onto the flange-like edge of the capsule wall. The capsule wall here forms the side wall of the capsule.

[0031] Rather than the three-layer design of the film shown, a two-layer design is also possible, in which case either the outer ply of porous filter paper or the inner ply of porous filter paper is omitted. A gas-impermeable film is always required in order to provide sufficient oxygen barrier action.

[0032] A particularly thin or particularly porous filter paper promotes sealing without additional polymer fibers in the paper.

[0033] A particularly thin paper is one having a basis weight of below 12 g/m.sup.2 and a thickness of about 40 μm. Particularly porous papers are understood to mean those having an air permeability of more than 1500 l/m.sup.2*s.

[0034] Another aim of the invention is thus to use the sealing film and the corresponding drinks capsule material not just to provide a home-compostable solution, but also to provide a solution in which a sufficient oxygen barrier is provided solely by virtue of the capsule and its coverage by the film itself.

[0035] In a known solution in which, for example, the sealing film consists solely of paper, development of an adequate oxygen barrier requires the entire filled drinks capsule to be accommodated in an additional barrier package, said barrier package typically consisting of or comprising PE, aluminum or PE-EVOH-PE or the like. Before the use of the drinks capsule, the capsule is then removed from the barrier package, which in turn produces additional waste in the form of the barrier package, and this barrier package is not home-compostable but has to go through the customary plastic or waste disposal route.

[0036] In order to avoid too much waste of this kind, a multitude of capsules, for example 10 of them, are therefore frequently packed in a common outer package. If, however, this package is opened in order to remove the first capsule, the shelf life of the other products already begins to fall, because the air that penetrates into the outer package also degrades and ages the interior of the drinks capsule contents.

[0037] If a simple paper film were to be provided as sealing film, the contents of the capsule, i.e. coffee for example, would at some point be spoiled or degraded in taste to such an extent that it is no longer an attractive product.

[0038] It would also be possible to use solely a polymer film as lid for the drinks capsule. As mentioned, however, these are generally too flexible to break at the required moment. Even brittle films that break at the correct moment, as a result of the hot water under pressure and the associated softening of the film material, subsequently block the holes of the extraction sieve of the extraction machine.

[0039] It is also possible to use a regenerated cellulose rather than cellulose acetate, or a mixture of a cellulose acetate and a regenerated cellulose. Regenerated celluloses used may be any of the known regenerated cellulose materials; preference is given to viscose (rayon staple) and or cellulose hydrate (cellophane).

[0040] In the example shown in the FIGURE, the gas-impermeable film preferably consists of or comprises a cellulose acetate. Such a cellulose acetate film having a thickness of 10 to 50 μm assures an excellent oxygen barrier of up to 1 cm.sup.3/m.sup.2×24 hours and a water vapor barrier of up to 20 g/m.sup.2×24 hours.

[0041] This is assured by coating the cellulose acetate film with polyvinylidene chloride (PVDC). If this coated film is used as sealing film for food containers, however, in the case of use in a Nespresso-compatible drinks capsule, this leads to blockage of the machine during the brewing operation. In order to prevent this, the pressure that acts on the film during the brewing should be reduced. However, this must not lead to such a great fall in the pressure that a satisfactory brewing outcome is no longer achieved. This is because there must also be sufficient water pressure in the sealing film in order to assure tearing of the film caused by this pressure and hence release of the beverage. The object of the invention can also be achieved, for example, with a paper (filter paper) where the porosity exceeds 1600 l/m.sup.2s for the lower paper ply.

[0042] Suitable pressure reducers for this purpose have been found to be cellulose-rich papers having a grammage of 10 to 30 g/m.sup.2. The porosity of these papers varies between about 80 and 1600 l/m.sup.2s according to EN ISO 9237.

[0043] One disadvantage of the construction of the sealing film described hitherto as multilayer, for example including two-layer, under some circumstances is that when the paper and film are torn, no beverage powder, e.g. coffee powder, may escape and get into the cup. In order to prevent this, a third layer has been introduced, which likewise consists of the papers already described above and which can be applied to the side of the films that is still clear. This can prevent the problem of coffee escaping from the capsule during the brewing operation and associated blockage of the capsule machines.

[0044] In order to be able to introduce the 2- or 3-layer film into a capsule filling system, the film layers must be permanently bonded to one another. For this purpose, the three individual component films, i.e. paper-cellulose acetate film(-paper), are run together over various rolls in a laminating system and joined, i.e. bonded, to one another at 120 to 200° Celsius.

[0045] The adhesive used is the PVdC (polyvinylidene chloride) already present on the cellulose acetate film; the finished sealing film thus laminated together can then be cut to any width and dispatched and applied to the filled capsule.

[0046] As described, the function of the film is to seal a food container, for example a drinks capsule/coffee capsule or the like, and in an oxygen-tight and moisture-tight manner, in order to keep the foodstuff present therein, i.e. beverage powder, coffee powder, etc., fresh for a long period of time. This is a particular challenge especially in the case of coffee, since coffee reacts even to small amounts of oxygen with changes/degradations in taste. Since the storage time in the capsule can be one year or longer, it is not possible on production of the capsule to determine the date of use. The capsule and film must thus keep the oxygen out of the capsule interior and hence away from the beverage powder, coffee, etc. present therein, which is the case to the best possible degree with a minimum oxygen transmission rate of the film and naturally of the capsule.

[0047] Furthermore, the film is also to achieve an optimal brewing result for various foodstuffs. For example, for a caffè lungo (110 ml of coffee), it is necessary for the interplay of coffee, capsule and film to lead to a brewing time of about 40 seconds. If the value is well below that, the coffee is distinctly underextracted, and in that case tastes thin (watery) and shows only a low level of crema with little color and volume. If the value is well above that, the coffee is overextracted and tastes unpleasantly strong (Robusta-like), and the crema becomes very dark. But since there are very many different tastes, coffee varieties and preparation methods, it is not possible to meet the demand for an optimal coffee with a single film; therefore, it is an object of this invention to disclose a portfolio of multilayer films that give a satisfactory result depending on the coffee (variety, roast, grind, production time of the machine, etc.).

[0048] At the same time, according to the invention, the film is also to be compostable, which is the case with cellulose acetate and paper as described.

[0049] As set out, the at least one layer of filter paper and the water-impermeable film are bonded to one another by a lamination process.

[0050] In order to improve the sealability of this arrangement, it is also possible to scatter polymer powder between the paper ply and film in the lamination process, such that this polymer powder lies between the paper ply and the polymer film after the lamination process. The polymer powder used here preferably consists of compostable, more preferably home-compostable, material, for example S.sup.2PC, PBS, PBSA, PBS/PBSA, PLA, PHA or the like.

[0051] The powder here preferably has a particle size in the range from 50 to 500 μm, more preferably 200 to 400 μm.

[0052] Where reference is made to the property of home compostability in the present application, this is understood to mean the fulfillment of the corresponding standards in this regard, namely: EN13432. Home compostability differs from industrial compostability.

[0053] The latter requires that, for composting, the material to become composted is exposed to a synthetic atmosphere in a factory, in a vessel, and hence to accomplish compostability. Home compostability, by contrast, is understood to mean composting as proceeds on a compost heap, for example in the garden.