CARBON-BASED ANODE MATERIAL WITH HIGH SLOPECAPACITY AND PREPARATION METHOD THEREFOR AND USE THEREOF

Abstract

A carbon-based anode material with high ramp capacity, a preparation method therefore, and a use thereof. The method includes placing a carbon source precursor into a crucible and heating to 400° C-1000° C. at a heating rate of 0.2° C./min-30° C./min under an inert atmosphere, wherein the precursor includes any one or a combination of at least two of fossil fuel, biomass, resin, and organic chemicals; and carrying out heat treatment on the precursor at a temperature of 400° C. to 1000° C. for 0.5-48 hours to carbonize the precursor to obtain a carbon-based negative electrode material. The specific surface area of the anode material is less than 10 m.sup.2/g. and assembling the obtained electrode material into a sodium ion battery and then carrying out charging and discharging between 0 and 2.5 V, to obtain a voltage curve. The ramp capacity being above 180 mAh/g and the first-cycle Coulombic efficiency is above 75%.

Claims

1. A preparation method of a carbon-based anode material with high slope capacity, comprising: placing a carbon source precursor in a crucible, placing the crucible in a heating device, and heating to 400° C.-1000° C. at a heating rate of 0.2° C./min-30° C./min under an inert atmosphere, wherein the carbon source precursor includes: any one or a combination of at least two of fossil fuels, biomass, resins, and organic chemicals; wherein the fossil fuels comprise: one or more of anthracite, bituminous coal, pitch, coal tar, and paraffin; the biomass comprises one or more of corn stalks, lignin, cellulose, glucose, and starch; the resins comprise one or more of phenolic resin, epoxy resin, polyamide resin, polyester resin, and rosin; the organic chemicals comprise: one or more of sodium carboxymethyl cellulose and sodium citrate; and carrying out low-temperature heat treatment on the carbon source precursor at 400° C.-1000° C. for 0.5-48 hours of time, to carbonize the carbon source precursor, thus obtaining the carbon-based anode material with high slope capacity, wherein, the carbon-based anode material obtained by the low-temperature heat treatment has a specific surface area of less than 10 m.sup.2/g, a slope capacity of 180 mAh/g or above, and an initial Coulombic efficiency of 75% or above.

2. The preparation method according to claim 1, wherein temperature for the low-temperature heat treatment is 600° C.-900° C., the time is from 0.5 hours to 10 hours, and the heating rate is 1° C./min-10° C./min.

3. The preparation method according to claim 1, wherein inert gas forming the inert atmosphere comprises any one of N.sub.2, Ar, Ar-5%H.sub.2, Ar-10%H.sub.2, and Ar-40%H.sub.2.

4. The preparation method according to claim 3, wherein the carrying out low-temperature heat treatment on the carbon source precursor further comprises: introducing the inert gas and a hydrocarbon-containing gas during the low-temperature heat treatment process, so that the carbon source precursor is subjected to surface coating during carbonization, wherein the hydrocarbon-containing gas comprises one or more of methane, ethane, toluene, ethylene, acetylene, and propyne, with a flow rate of 0.5-200 mL/min.

5. The preparation method according to claim 1, wherein before the carbonization of the carbon source precursor, the method further comprises: pretreating the carbon source precursor, wherein the pretreatment comprises one or more of pre-oxidation, acid washing, alkali washing, water washing, organic solvent washing, and carbon coating treatment.

6. The preparation method according to claim 1, wherein after the carbonization of the carbon source precursor, the method further comprises: carrying out acid washing, alkali washing, water washing, organic solvent washing and/or carbon coating treatment on carbonization product.

7. A carbon-based anode material prepared by the preparation method according to claim 1, wherein the specific surface area of the carbon-based anode material is less than 10 m.sup.2/g, and an intensity ratio ID/IG of the D-peak and G-peak in a Raman spectrum is between 1.5 and 5.

8. The carbon-based anode material according to claim 7, wherein the carbon-based anode material is used as an anode material of a secondary battery.

9. A secondary battery, comprising the carbon-based anode material according to claim 8.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0023] FIG. 1 is an X-ray diffraction (XRD) pattern of the carbon-based anode material prepared in Embodiment 1;

[0024] FIG. 2 is a scanning electron microscope (SEM) image of the carbon-based anode material prepared in Embodiment 1;

[0025] FIG. 3 is a charge-discharge curve diagram of the carbon-based anode material prepared in Embodiment 1;

[0026] FIG. 4 is a Raman spectrum of the carbon-based anode material prepared in Embodiment 2;

[0027] FIG. 5 is a charge-discharge curve diagram of the carbon-based anode material prepared in Embodiment 3;

[0028] FIG. 6 is a transmission electron microscope (TEM) image of the carbon-based anode material prepared in Embodiment 4;

[0029] FIG. 7 is a diagram of the cycle performance of the carbon-based anode material prepared in Embodiment 5;

[0030] FIG. 8 is a charge-discharge curve diagram of the carbon-based anode material prepared in Embodiment 7;

[0031] FIG. 9 is a charge-discharge curve diagram of the carbon-based anode material prepared in Embodiment 8;

[0032] FIG. 10 is a diagram of the rate performance of the carbon-based anode material prepared in Embodiment 9;

[0033] FIG. 11 is a scanning electron microscope (SEM) image of the carbon-based anode material prepared in Embodiment 11;

[0034] FIG. 12 is a scanning electron microscope (SEM) image of the carbon-based anode material prepared in Embodiment 12;

[0035] FIG. 13 is an X-ray diffraction (XRD) pattern of the carbon-based anode material prepared in Embodiment 13;

[0036] FIG. 14 is a scanning electron microscope (SEM) image of the carbon-based anode material prepared in Embodiment 13;

[0037] FIG. 15 is a charge-discharge curve diagram of the carbon-based anode material prepared in Embodiment 13;

[0038] FIG. 16 is a charge-discharge curve diagram of the carbon-based anode material prepared in Embodiment 14;

[0039] FIG. 17 is an X-ray diffraction (XRD) pattern of the carbon-based anode material prepared in Comparative Embodiment 1;

[0040] FIG. 18 is a scanning electron microscope (SEM) image of the carbon-based anode material prepared in Comparative Embodiment 1;

[0041] FIG. 19 is a transmission electron microscope (TEM) image of the carbon-based anode material prepared in Comparative Embodiment 1;

[0042] FIG. 20 is a charge-discharge curve diagram of the carbon-based anode material prepared in Comparative Embodiment 1;

[0043] FIG. 21 is a charge-discharge curve diagram of the carbon-based anode material prepared in Comparative Embodiment 2; and

[0044] FIG. 22 is a comparison diagram of charge-discharge curves of the carbon-based anode materials of Embodiment 1, comparative Embodiment 1, and comparative Embodiment 2.

DETAILED DESCRIPTION

[0045] The technical solutions of the present disclosure will be further described in detail below through the accompanying drawings and embodiments.

[0046] An embodiment of the present disclosure provides a preparation method of a carbon-based anode material with high slope capacity, including:

[0047] placing a required amount of a carbon source precursor in a crucible, placing the crucible into a heating device, heating to 400° C.-1000° C. at a heating rate of 0.2° C./min-30° C./min under an inert atmosphere, and then carrying out low-temperature heat treatment on the carbon source precursor at 400° C.-1000° C. for 0.5-48 hours to carbonize the carbon source precursor, thus obtaining a carbon-based anode material.

[0048] Wherein the carbon source precursor compound is any one or a combination of at least two of fossil fuels, biomass, resins, and organic chemicals, such as a combination of fossil fuel and biomass, a combination of fossil fuel and resin, a combination of fossil fuel and organic chemicals, a combination of biomass and resin, a combination of biomass and organic chemicals, a combination of resin and organic chemicals, a combination of fossil fuel, biomass, and resin, a combination of fossil fuel, biomass, and organic chemicals, a combination of biomass, resin, and organic chemicals, and a combination of fossil fuel, biomass, resin, and organic chemicals.

[0049] The fossil fuels include: one or more of anthracite, bituminous coal, pitch, coal tar, and paraffin; the biomass includes one or more of corn stalks, cotton, lignin, cellulose, and glucose; the resins include one or more of phenolic resin, epoxy resin, polyamide resin, polyester resin and rosin; the organic chemicals include: one or more of sodium carboxymethyl cellulose, sodium alginate, sodium citrate, calcium hydroxyphosphate, and calcium gluconate.

[0050] In a preferred solution, the temperature of the low-temperature heat treatment ranges from 600° C. to 900° C., and, for example, specifically may be 600° C., 700° C., 800° C., or 900° C.; the time of the low-temperature heat treatment ranges from 0.5 hour to 10 hours, for example, preferably 40 minutes, 1 hour, 2 hours, 4 hours, 6 hours, or 8 hours; the heating rate ranges from 1° C./min to 10° C./min, for example, preferably 1° C./min, 3° C./min, 5° C./min, or 10° C./min.

[0051] The inert gas forming the inert atmosphere specifically includes any one of N.sub.2, Ar, Ar-5%H.sub.2, Ar-10%H.sub.2, and Ar-40%H.sub.2.

[0052] The carbon source precursor undergoes low-temperature heat treatment to form a carbon-based anode material with a special microstructure where the surface is slightly ordered, the interior is disordered, and no obvious graphitized crystallite area exists.

[0053] Preferably, the process of performing low-temperature heat treatment on the carbon source precursor may further include introducing inert gas and hydrocarbon-containing gas at the same time during the carbonization of the carbon source precursor, so that the carbon source precursor is also subjected to surface coating during carbonization. The hydrocarbon-containing gas may include one or more of methane, ethane, toluene, ethylene, acetylene, and propyne, with a flow rate of 0.5-200 mL/min.

[0054] In a preferred solution, the carbon source precursor may further be pretreated before the carbon source precursor is subjected to low-temperature heat treatment and carbonization, and the pretreatment includes one or more of pre-oxidation, acid washing, alkali washing, water washing, organic solvent washing, and carbon coating treatment.

[0055] In addition, after being carbonized, the carbon source precursor is taken out of the heating device and the crucible and then subjected to acid washing, alkali washing, water washing, organic solvent washing and/or carbon coating treatment, thus obtaining the carbon-based anode material with high slope capacity.

[0056] The carbon-based anode material with high slope capacity prepared by the present disclosure can be applied in the anode material of the secondary battery, such as the anode material of the sodium ion battery, and has excellent performance.

[0057] Compared with the prior art, the preparation method and the prepared material of the present disclosure have the following beneficial effects:

[0058] (1) Compared with the traditional carbonization process, the carbonization in the preparation process of the present disclosure is carried out at a significantly lower temperature, is simple and easy, needs a short processing time, and can be put into large-scale preparation.

[0059] (2) Compared with other materials obtained at higher temperatures (usually higher than 1000° C.), the carbon-based material prepared by the method provided by the present disclosure has high intensity ratio (ID/IG) of the D-peak and G-peak calculated by Raman spectroscopy, between 1.5 and 5, and high degree of disorder, and when the carbon-based material is applied to a sodium ion battery, in the case of charge and discharge between 0 and 2.5 V, a voltage curve with high slope capacity is obtained, where the slope capacity is 180 mAh/g or above, and the initial Coulombic efficiency is 75% or above. In a specific embodiment, the reversible specific capacity can be as high as 231.4 mAh/g, and the initial Coulombic efficiency can be as high as 80%.

[0060] (3) As compared with that of other existing materials prepared at low temperatures (600-1000° C.) the method provided by the present disclosure , by optimizing the precursor, carbonization temperature, and carbonization time, and in cooperation with the pre- and post-treatment process, and through adjusting the microstructure of the material, may obtain a higher reversible specific capacity, the specific surface area of the material less than 10 m.sup.2/g; and a higher initial Coulombic efficiency at the same time as the higher reversible specific capacity is obtained; wherein with a reversible specific capacity of up to 231.4 mAh/g, the initial Coulombic efficiency can be as high as 80%. During the carbonization process, inert gas and hydrocarbon-containing gas are introduced at the same time for surface coating, which can further reduce the specific surface area, improve the initial efficiency and reversible specific capacity.

[0061] (4) The present disclosure forms a carbon-based anode material with a special microstructure by selecting a suitable precursor and a lower treatment temperature. Taking pitch as the carbon source precursor as an example, the pitch is carbonized at a preferred temperature between 600° C. and 900° C. to form a carbon-based anode material with a special microstructure, where the ID/IG value calculated by Raman spectrum is large, the surface is slightly ordered, the interior is disordered, and no obvious graphitized crystallite area exists. The slightly ordered surface can improve the electronic conductance of the carbon-based anode material, and also facilitate the diffusion of alkali metal ions, thereby improving the reversible specific capacity and rate performance of the material, and also improving the initial reversible specific capacity of the material and the initial charge-discharge efficiency. The internal disordered structure can adjust the interaction between alkali metal ions and the carbon layers, thereby adjusting the potential, and obtaining an electrochemical curve with a high slope capacity. In addition, the prepared carbon-based anode material has a small specific surface area, which reduces the side reactions between the electrode and the electrolyte and improves the initial efficiency. The prepared carbon-based anode material has an initial efficiency of up to 80% and an initial charge capacity of up to 234 mAh/g, almost all of which comes from the slope section. The carbon-based anode material with high slope capacity has fast ion diffusion speed, low polarization and good rate performance during charge and discharge process, which is beneficial to high-current charge and discharge of full batteries.

[0062] Hereinafter, some specific embodiments are used to further illustrate the preparation method and material properties of the carbon-based anode material of the present disclosure. The following examples are intended to illustrate the present disclosure, but not to further limit the present disclosure.

Embodiment 1

[0063] 1 g of pitch is placed into a 20 mL graphite crucible, and the graphite crucible is then placed into a tube furnace where the pitch is carbonized at 950° C. for 2 hours under an Ar atmosphere, thus obtaining the final carbon-based anode material. The X-ray diffraction (XRD) pattern and scanning electron microscope (SEM) image of the carbon-based anode material are shown in FIG. 1 to FIG. 2. The X-ray diffraction (XRD) pattern has no obvious diffraction peak, indicating that the obtained carbon-based anode material is an amorphous carbon-based anode material. The obtained carbon-based anode material is made into a pole piece, which is assembled into a button cell with sodium metal as a counter electrode and 1 mol/L NaPF6 EC/DMC (1:1) as electrolyte. Its charge-discharge curve is measured at 0.1C. As shown in FIG. 3, the test results show that the electrochemical curve basically only includes a slope section (see FIG. 21 of Comparative Embodiment 2. In Comparative Embodiment 2, the electrochemical curve includes both a plateau section and a slope section. In such embodiment of the disclosure, there is almost no platform section, only a slope section), the reversible specific capacity is 231.4 mAh/g, and the initial Coulombic efficiency is 80%.

Embodiment 2

[0064] 1 g of anthracite is placed in a 20 mL graphite crucible, and the crucible is then placed in a muffle furnace to keep the anthracite at 350° C. for 12 hours. The material taken out is treated at 650° C. for 24 hours under an Ar atmosphere, thus obtaining the final carbon-based anode material. The Raman spectrum of the carbon-based anode material is shown in FIG. 4, and the ID/IG value calculated by the Raman spectrum is 2.57, which shows that the prepared carbon-based anode material has a high degree of disorder and small graphitized flakes. The obtained carbon-based anode material is made into a pole piece, which is assembled into a button cell with sodium metal as a counter electrode and 1 mol/L NaPF.sub.6 EC/DMC (1:1) as electrolyte. Its charge-discharge curve is measured at 0.1C. The first-cycle charge capacity is as high as 219.1 mAh/g, almost all of which comes from the slope section, and the initial Coulombic efficiency is as high as 79%.

Embodiment 3

[0065] 2 g of corn stalks are crushed, dispersed in 50 mL of water, and placed in a 100 mL beaker, and the beaker is then placed in an oven where the resulting material is heated to 180° C. and kept at 180° C. for 24 hours. Then the washed and dried powder is put in a tube furnace and treated at 700° C. for 10 hours in a N.sub.2 atmosphere, thus obtaining the final carbon-based anode material. The obtained carbon-based anode material is made into a pole piece, which is assembled into a button cell with sodium metal as a counter electrode and 1 mol/L NaPF.sub.6 EC/DMC (1:1) as electrolyte. Its charge-discharge curve is measured at 0.1C. As shown in FIG. 5, the test results show that the capacity is as high as 230.5 mAh/g, almost all of which comes from the slope section, and the initial Coulombic efficiency is as high as 75.9%.

Embodiment 4

[0066] 2 g of phenolic resin is dispersed in 50 mL of 3 mol/L HCl, the resulting material is sealed and put in an oven to be kept at 180° C. for 12 hours, and then the resulting material is washed with deionized water to be neutral and dried at 60° C. Then the material is treated at 750° C. for 15 hours under a N.sub.2 atmosphere, thus obtaining the final carbon-based anode material. The TEM spectrum of the carbon-based anode material is shown in FIG. 6. The TEM spectrum shows that there is no obvious graphitized crystallite area in the prepared carbon-based anode material, and there are curved carbon layers on the surface, the surface is slightly ordered, but the interior is disordered. The obtained carbon-based anode material is made into a pole piece, which is assembled into a button cell with sodium metal as a counter electrode and 1 mol/L NaPF.sub.6 EC/DMC (1:1) as electrolyte. Its charge-discharge curve is measured at 0.1C. The first-cycle charge capacity is as high as 227.2 mAh/g, almost all of which comes from the slope section, and the initial Coulombic efficiency is as high as 78.8%.

Embodiment 5

[0067] 2 g of cellulase is dispersed in 50 mL of 4 mol/L NaOH, the resulting material is sealed and put in an oven to be kept at 180° C. for 2 hours, and then the resulting material is washed with deionized water to be neutral and dried at 60° C. The resulting material is treated at 850° C. for 1 hour under an Ar atmosphere, thus obtaining the final carbon-based anode material. The obtained carbon-based anode material is made into a pole piece, which is assembled into a button cell with sodium metal as a counter electrode and 1 mol/L NaPF.sub.6 EC/DMC (1:1) as electrolyte. Its charge-discharge curve is measured at 0.1C. The first-cycle charge capacity is as high as 229.3 mAh/g, almost all of which comes from the slope section, and the initial Coulombic efficiency is as high as 80.3%. The cycle performance of the carbon-based anode material is shown in FIG. 7. There is no obvious capacity decay after 100 cycles at 0.1C.

Embodiment 6

[0068] 2 g of rosin is dispersed in 40 mL of 6 mol/L HCl; the resulting material is sealed and put in an oven to be kept at 80° C. for 24 hours; and then the resulting material is washed twice with 1 mol/L NaOH solution, then washed once with deionized water, and dried at 60° C. The resulting material is treated at 750° C. for 40 hour under an Ar-5%H.sub.2 atmosphere, thus obtaining the final carbon-based anode material. The obtained carbon-based anode material is made into a pole piece, which is assembled into a button cell with sodium metal as a counter electrode and 1 mol/L NaPF.sub.6 EC/DMC (1:1) as electrolyte. Its charge-discharge curve is measured at 0.1C. The first-cycle charge capacity is as high as 217.2 mAh/g, almost all of which comes from the slope section, and the first-cycle Coulombic efficiency is as high as 80.6%.

Embodiment 7

[0069] 10 g of calcium gluconate is placed into a 100 mL graphite crucible, and the graphite crucible is then placed into a tube furnace where the calcium gluconate is carbonized at 650° C. for 1 hour under an Ar-10%H.sub.2 atmosphere. The obtained carbon-based anode material is washed 6 times with 6 mol/L HCl, and then washed with deionized water to be neutral, thus obtaining the final carbon-based negative electrode material. The obtained carbon-based anode material is made into a pole piece, which is assembled into a button cell with sodium metal as a counter electrode and 1 mol/L NaPF.sub.6 EC/DMC (1:1) as electrolyte. Its charge-discharge curve is measured at 0.1C. As shown in FIG. 8, the test results show that the capacity is as high as 181 mAh/g, almost all of which comes from the slope section, and the initial Coulombic efficiency is as high as 78.4%.

Embodiment 8

[0070] 1 g of glucose is dissolved in 50 ml of water and placed in a 100 mL beaker, and the beaker is then placed in an oven to keep at 180° C. for 24 hours. Then the washed and dried powder is put in a tube furnace and treated at 700° C. for 2 hours in a mixed atmosphere of Ar and methylbenzene, and surface carbon coating is also completed during the carbonization process. The obtained powder is the final carbon-based anode material. The obtained carbon-based anode material is made into a pole piece, which is assembled into a button cell with sodium metal as a counter electrode and 1 mol/L NaPF.sub.6 EC/DMC (1:1) as electrolyte. Its charge-discharge curve is measured at 0.1C. As shown in FIG. 9, the first-cycle charge capacity is as high as 206.2 mAh/g, most of the reversible specific capacity comes from the slope section, and the initial Coulombic efficiency is as high as 75.1%.

Embodiment 9

[0071] 1 g glucose and 1 g of pitch are mixed mechanically and placed in a 100 mL graphite crucible, and the crucible is then placed in a tube furnace where the material is treated at 800° C. for 12 hours in an Ar-40%th atmosphere. The glucose is cracked to obtain a carbon nucleus, and the pitch is melt-coated on the surface of the glucose carbon-based anode material. The obtained material is the final carbon-based anode material. The obtained carbon-based anode material is made into a pole piece, which is assembled into a button cell with sodium metal as a counter electrode and 1 mol/L NaPF.sub.6 EC/DMC (1:1) as electrolyte. Its charge-discharge curve is measured at 0.1C. The first-cycle charge capacity is as high as 230.1 mAh/g, almost all of which comes from the slope section, and the initial Coulombic efficiency is as high as 76.8%. The rate performance of the carbon-based anode material is shown in FIG. 10. The reversible specific capacity at 8C is 122 mAh/g, which is 53% of the capacity at 0.1C.

Embodiment 10

[0072] 1 g of coal tar and 1 g of phenolic resin are mixed in 100 mL of ethanol, and dried at 60° C. and then put in a 20 mL alumina crucible; and the crucible is placed in a tube furnace where the material is treated at 900° C. for 5 hours under a N.sub.2 atmosphere. The resulting material is the final carbon-based anode material. The obtained carbon-based anode material is made into a pole piece, which is assembled into a button cell with sodium metal as a counter electrode and 1 mol/L NaPF.sub.6 EC/DMC (1:1) as electrolyte. Its charge-discharge curve is measured at 0.1C. The first-cycle charge capacity is as high as 198.2 mAh/g, almost all of which comes from the slope section, and the initial Coulombic efficiency is as high as 75%.

Embodiment 11

[0073] 1 g of calcium hydroxyphosphate and 1.8 g of pitch are mechanically mixed and ground, and then placed in a 50 mL alumina crucible; and the crucible is then placed in a muffle furnace and kept at 300° C. for 24 hours. The material taken out is treated at 850° C. for 1 hour in a N.sub.2 atmosphere. The resulting material is the final carbon-based anode material. The SEM image of the carbon-based anode material is shown in FIG. 11. The obtained carbon-based anode material is made into a pole piece, which is assembled into a button cell with sodium metal as a counter electrode and 1 mol/L NaPF.sub.6 EC/DMC (1:1) as electrolyte. Its charge-discharge curve is measured at 0.1C. The first-cycle charge capacity is as high as 217 mAh/g, almost all of which comes from the slope section, and the initial Coulombic efficiency is as high as 79.8%.

Embodiment 12

[0074] 1 g of bituminous coal, 3 g of cellulose, and 0.5 g of sodium citrate are dissolved in 20 mL of ethanol solution and placed in a 50 mL beaker; and the beaker is then placed in an oven and heated to 220° C. and kept at 220° C. for 48 hours. The material taken out is treated at 1000° C. for 5 hours under an Ar-10%H.sub.2 atmosphere. The resulting material is the final carbon-based anode material. The SEM image of the carbon-based anode material is shown in FIG. 12. The obtained carbon-based anode material is made into a pole piece, which is assembled into a button cell with sodium metal as a counter electrode and 1 mol/L NaPF.sub.6 EC/DMC (1:1) as electrolyte. Its charge-discharge curve is measured at 0.1C. The first-cycle charge capacity is as high as 221 mAh/g, almost all of which comes from the slope section, and the initial Coulombic efficiency is as high as 80%.

Embodiment 13

[0075] 2 g of anthracite, 2.4 g of cotton, 1.2 g of epoxy resin, and 0.4 g of calcium gluconate are well mixed and ground and placed in a 40 mL alumina crucible; and the crucible is then placed in a tube furnace where the material is carbonized at 1000° C. for 48 hours in an Ar atmosphere. The XRD pattern and SEM image of the obtained carbon-based anode material are shown in FIGS. 13-14. The XRD pattern has no obvious diffraction peak, indicating that the obtained carbon-based anode material is an amorphous carbon-based anode material. The obtained carbon-based anode material is made into a pole piece, which is assembled into a button cell with sodium metal as a counter electrode and 1 mol/L NaPF.sub.6 EC/DMC (1:1) as electrolyte. Its charge-discharge curve is measured at 0.1C, as shown in FIG. 15. The test results show that the capacity is as high as 198.3 mAh/g, almost all of which comes from the slope section, and the initial Coulombic efficiency is as high as 78%.

Embodiment 14

[0076] The carbon-based anode material obtained in Embodiment 7 is mixed and ground with pitch in a ratio of 1:0.1, and the resulting material is kept at 350° C. for 2 hours in an air atmosphere, and then carbonized in a mixed atmosphere of Ar and acetylene at 800° C. for 1 hour, thus obtaining the carbon-based anode material. The obtained carbon-based anode material is made into a pole piece, which is assembled into a button cell with sodium metal as a counter electrode and 1 mol/L NaPF.sub.6 EC/DMC (1:1) as electrolyte. Its charge-discharge curve is measured at 0.1C. As shown in FIG. 16, the first-cycle efficiency is increased to 85%, and the reversible specific capacity is increased to 230 mAh/g, almost all of which comes from the slope section.

Comparative Embodiment 1

[0077] 1 g of pitch is placed into a 20 mL graphite crucible, and the graphite crucible is then placed into a tube furnace where the pitch is carbonized at 1400° C. for 2 hours under a N.sub.2 atmosphere, thus obtaining the final carbon-based anode material. The XRD pattern, SEM image, and the transmission electron microscope (TEM) image of the carbon-based anode material are shown in FIG. 17 to FIG. 19. The X-ray diffraction (XRD) pattern has an obvious diffraction peak, indicating that the obtained carbon-based anode material has an obvious graphitized structure. The SEM image shows that the surface of the obtained material has an obvious graphite layered structure. It can also be seen from the TEM spectrum that the carbon-based anode material prepared in Comparative Embodiment 1 has obvious graphitized carbon layers, of which the carbon layer spacing is small, and the graphitized flakes are larger. The obtained carbon-based anode material is made into a pole piece, which is assembled into a button cell with sodium metal as a counter electrode and 1 mol/L NaPF.sub.6 EC/DMC (1:1) as electrolyte. Its charge-discharge curve is measured at 0.1C. As shown in FIG. 20, the test results show that the electrochemical curve basically only includes a slope section, but the first-cycle charge specific capacity is 89.7 mAh/g, and the initial Coulombic efficiency is 59.13%.

Comparative Embodiment 2

[0078] 2 g of anthracite is placed in a 40 mL alumina crucible, and the crucible is then placed in a tube furnace where the anthracite coal is carbonized at 1400° C. for 1 hour in an Ar-10% H.sub.2 atmosphere. The obtained carbon-based anode material is made into a pole piece, which is assembled into a button cell with sodium metal as a counter electrode and 1 mol/L NaPF.sub.6 EC/DMC (1:1) as electrolyte. Its charge-discharge curve is measured at 0.1C. As shown in FIG. 21, the test results show that the first-cycle charge specific capacity is 218.8 mAh/g and the slope section capacity (greater than 0.2 V) only accounts for 34%.

[0079] FIG. 22 is a comparison diagram of charge-discharge curves of the carbon-based anode materials of Embodiment 1, Comparative Embodiment 1, and Comparative Embodiment 2. It can be clearly seen from FIG. 22 that the curve of Embodiment 1 obtained by the preparation method of the carbon-based anode material with high slop capacity of the present disclosure almost only includes a slope section, and the reversible specific capacity is greater than 231.4 mAh/g. Although the curve obtained in Comparative Embodiment 1 basically only includes a slope section, the first-cycle charge specific capacity is only 89.7 mAh/g; the curve in Comparative Embodiment 2 has a first-cycle charge specific capacity of 218.8 mAh/g, but its slope section capacity only accounts for 34%. In the process of high-current charge and discharge, the plateau section is highly polarized, resulting in poor rate performance.

[0080] In summary, it can be seen that the present disclosure only needs to perform a short low-temperature heat treatment process at a relatively low temperature to obtain a carbon-based anode material with high capacity, high rate, and high first-cycle efficiency. By choosing a proper precursor, selecting a relatively low pyrolysis temperature, optimizing the pyrolysis temperature and in cooperation with the pre- and post-treatment process, and by virtue of a further carbon coating process, the purpose of adjusting the microstructure, macromorphology, crystallinity of the product and reducing the specific surface area of the material can be reached, and the reversible specific capacity, first-cycle efficiency, cycle and rate performance of the obtained carbon-based anode material can also be ensured.

[0081] The specific embodiments described above further explain the objectives, technical solutions and beneficial effects of the present disclosure. It should be understood that the above description is only the specific embodiments of the present disclosure, and not intended to limit the scope of the present disclosure. Any modifications, equivalents, improvements and the like made without departing from the spirit and principle of the present disclosure should be included in the scope of the present disclosure.