PEROVSKITES OXYGEN STORAGE AND RELEASE MATERIALS AND THEIR USE FOR EXHAUST GAS TREATMENT

Abstract

A catalyst system includes an oxygen storage and release material that has at least one compound of the structure YMO.sub.3+δ, where M is selected from Mn, Co, Cu, Ce, Ti, Ni, Zn, Fe and any combination thereof, and where δ is ≥0. The oxygen storage and release material is configured to allow absorption and release oxygen depending on the conditions of a reagent stream such that sufficient oxygen is maintained for the catalytic removal of at least one of incompletely combusted hydrocarbons, CO, and NO. The catalyst system is useful in a catalytic converter such that oxygen is supplied under rich combustion conditions in an engine upstream of the catalytic converter inlet and oxygen is adsorbed and absorbed under lean rich combustion conditions in the engine.

Claims

1. A catalytic converter for removal of pollutants from an exhaust gas stream, the catalytic converter comprising: an inlet configured to receive the exhaust gas stream into an enclosure; an outlet configured to allow the exhaust gas stream to exit the enclosure; and a catalyst system contained inside the enclosure, the catalyst system comprising at least one metal catalyst and an oxygen storage and release material comprising at least compound of the structure YMO.sub.3+δ, where M is selected from the group consisting of Mn, Co, Cu, Ce, Ti, Ni, Zn, Fe and any combination thereof and where δ is ≥0, and where the catalyst system is configured for selective absorption/adsorption and release of oxygen to promote sufficient oxygen for the catalytic removal of at least one of incompletely combusted hydrocarbons, CO, and NO.

2. The catalytic converter according to claim 1, wherein M is Mn.

3. The catalytic converter according to claim 1, wherein the YMO.sub.3+δ is dispersed on a surface of a support within the catalytic converter.

4. The catalytic converter according to claim 1, wherein the metal catalyst comprises at least one metal from the group consisting of platinum, palladium, and rhodium.

5. A catalyst system contained inside an enclosure, the catalyst system comprising an oxygen storage and release material comprising at least one compound of the structure YMO.sub.3+δ, where M is selected from the group consisting of Mn, Co, Cu, Ce, Ti, Ni, Zn, Fe and any combination thereof, where δ is ≥0, configured for selective absorption/adsorption and release of oxygen to promote sufficient oxygen for the catalytic removal of at least one of incompletely combusted hydrocarbons, CO, and NO.sub.x from a gas stream.

6. The catalyst system according to claim 5, wherein M is Mn.

7. A method for the removal of incompletely oxidized compounds from an exhaust gas stream, the method comprising: flowing the exhaust gas stream through a catalyst system and contacting the exhaust gas stream with at least one metal catalyst dispersed on a surface of a support, wherein the metal catalyst is within a catalyst system comprising an oxygen storage and release material for selectively storing oxygen and releasing oxygen, the storage and release material comprising at least one compound of the structure YMO.sub.3+δ, where M is selected from the group consisting of Mn, Co, Cu, Ce, Ti, Ni, Zn, Fe and any combination thereof and where δ is ≥0, and wherein hydrocarbons, CO and NO are removed from the exhaust gas stream

8. The method according to claim 7, wherein M is Mn.

9. The method according to claim 7, wherein the metal catalyst comprises at least one metal from the group consisting of platinum, palladium, and rhodium.

10. The method according to claim 7, wherein oxygen is released from the oxygen storage and release material when the exhaust gas stream flowing from an engine is reductive.

11. The method according to claim 7, wherein oxygen is absorbed/adsorbed into the oxygen storage and release material when the exhaust gas stream flowing from an engine is oxidative.

12. The method according to claim 7, wherein the storage and release of oxygen occurs over a temperature range of about 200° C. to about 650° C.

13. The method according to claim 7, wherein the storage and release of oxygen occurs over a temperature range of about 400° C. to about 650° C.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0012] The present teachings will become more fully understood from the detailed description and the accompanying drawings, wherein:

[0013] FIG. 1 illustrates the temperature program desorption (TPD) above 400° C. vs. the oxygen storage capacity OSC for various Perovskite compounds including some YMO.sub.3+δ, according to an embodiment of the invention.

[0014] FIG. 2 shows a plot of molar oxygen storage per gram of YMnO.sub.3 (circles) or a common production catalytic converter oxygen storage material (squares) before (broken line) or after (solid line) aging at 1,000° C. where the storage was enabled by flowing O.sub.2 at a given temperature and removing O.sub.2 by pulsing CO over the surface to produce CO.sub.2.

[0015] It should be noted that the figure set forth herein is intended to exemplify the general characteristics of the methods, algorithms, and devices among those of the present technology, for the purpose of the description of certain aspects. The figure may not precisely reflect the characteristics of any given aspect, and are not necessarily intended to define or limit specific embodiments within the scope of this technology.

DETAILED DESCRIPTION

[0016] The present teachings provide a catalyst system including an oxygen storage and release material for the maintenances of sufficient oxygen content within a catalytic converter, where the oxygen storage material augments the oxygen content. The oxygen storage and release material releases oxygen under conditions that typically display insufficient oxygen to achieve the stoichiometry needed to decompose the impurities in an exhaust stream from an engine, and absorbs oxygen under conditions that the exhaust stream has an excess of oxygen to that required for reaction with the impurities.

[0017] In various embodiments, the oxygen storage and release material includes at least one compound of the structure YMO.sub.3+δ, where M is a transition metal selected from Mn, Co, Cu, Ce, Ti, Ni, Zn, Fe and a combination thereof. M can be a combination of the transition metals, and the oxygen storage and release material can be a combination of different YMO.sub.3+δcompounds. The oxygen storage and release material can reside on a supporting structure in the form of nanoparticles, microparticles, or even larger particles or a continuous film, where the oxygen storage and release material can be of any porosity such that the available surface area is high overall, for example, but not limited to, a surface area equivalent to a film derived from non-porous particle of about 100 nm or less.

[0018] As detailed herein, the oxygen storage and release material may be employed in a catalyst system. The catalyst system is useful where the high surface area oxygen storage and release material is supported on one or more surfaces within a catalytic converter for vehicles, automobiles, and the like, where the catalyst system promotes a high extent of reaction for the removal of incompletely combusted hydrocarbons, either un-combusted or partially combusted hydrocarbons and undesirable partially oxidized products, such as CO and NO, within the exhaust stream. The catalytic system includes at least one metal, for example, platinum, palladium, and rhodium in forms typical of state of the art catalyst systems for catalytic converters. Advantageously, the oxygen storage and release material absorbs (chemisorbs) and adsorbs (physisorbs) oxygen when a vehicle engine is under lean fuel-to-air combustion conditions, where the oxygen levels are relatively high and the temperatures are relatively low in the exhaust stream. The oxygen storage and release material releases oxygen under when the vehicle engine is under rich fuel-to-air combustion conditions, where oxygen levels in the exhaust stream can be insufficient and the temperatures are relatively high. Under the rich conditions, the oxygen released from the oxygen storage material provides oxygen for meeting the required reagent stoichiometry at the active site of the catalyst when the available oxygen delivered in the inlet exhaust stream is insufficient. When employed in a catalyst system for a catalytic converter, the reversible oxygen storage and release compound undergoes a transformation of its structure between a first crystal phase conducive for oxygen absorption and a second crystal phase conducive for oxygen release.

[0019] Embodiments are also directed to a method of providing oxygen to an oxygen poor gas stream that can augment a deficiency in oxygen over a period of time. The method of providing oxygen is by including an oxygen storage and release material that includes one or more compounds of the structure YMO.sub.3+δ into a chamber where the temperature fluctuates in response to a feed of a fuel to a combustion system. The YMO.sub.3+δ has an M metal ion that is a transition metal that can vary in crystal phase where transformation of a first and at least a second crystal phase occurs reversibly, depending upon the composition and physical properties to which the compound is exposed. The transition metal can be any transition metal that can vary in coordination with oxygen anions depending upon temperature and oxygen concentration in its environment. In various aspects, the transition metal can be Mn, Co, Cu, Ce, Ti, Ni, Zn, Fe or any combination of the transition metals that displays a change in coordination with its environment but is not prone to non-reversible oxidation, such as often observed with iron. The method can be performed in any catalytic system including, but not limited to catalytic converters for vehicles, automobiles, and the like.

[0020] The oxygen storage and release material need not be of a single YMO.sub.3+δ species, but can be an admixture of a plurality of different YMO.sub.3+δ compounds having different transition metals, where the conditional regime for oxygen absorption and absorption and desorption varies such that in composite a larger window of temperatures and gas compositions are included. The oxygen storage and release material includes compounds that can vary in structure, for example, YMnO.sub.3+δ, which can vary between a hexagonal space group and a Perovskite space group. The compound can transform based on the environmental conditions of its environment.

[0021] The catalyst systems of the present disclosure can be used in a chamber or an enclosure, such as a catalytic converter, having an inlet and an outlet. As is commonly known to those of ordinary skill in the art, such a chamber or enclosure can be configured to receive an exhaust gas stream through the inlet and to exit the exhaust gas stream through the outlet, such that the exhaust gas stream has a particular or defined flow direction. In a catalytic conversion, the uptake and release of the oxygen must occur in an atmosphere that is rich in nitrogen, water vapor, and carbon dioxide.

EXAMPLES

[0022] Various aspects of the present disclosure are further illustrated with respect to the following Examples. It is to be understood that these Examples are provided to illustrate specific embodiments of the present disclosure and should not be construed as limiting the scope of the present disclosure in or to any particular aspect.

Performance Evaluation

[0023] A plot of the temperature programmed desorption (TPD) vs the oxygen storage capacity of various YMO.sub.3+δ compounds and other compositions is shown in FIG. 1 The oxygen storage capacity and desorption above 400° C. Hence, a moderate (YCoO.sub.3 and YCuO.sub.3) to high (YCeO.sub.3 and YMnO.sub.3) oxygen storage is observed with desorption being observed above 400° C.

[0024] The degree of oxygen storage particularly at temperatures in excess of about 300° C. for the oxygen storage and release material including at least compound of the structure YMO.sub.3+δ is greater than a common state of the art oxygen storage and release material, as shown in FIG. 2, where the performance is comparable at temperatures lower than about 300° C., but is significantly greater, at higher temperatures, for example, at temperatures about 400° C. or greater. The robustness of the oxygen storage and release material is evident from the general retention of storage capacity after aging at 1,000° C.

[0025] The preceding description is merely illustrative in nature and is in no way intended to limit the disclosure, its application, or uses. As used herein, the phrase at least one of A, B, and C should be construed to mean a logical (A or B or C), using a non-exclusive logical “or.” It should be understood that the various steps within a method may be executed in different order without altering the principles of the present disclosure. Disclosure of ranges includes disclosure of all ranges and subdivided ranges within the entire range.

[0026] The headings (such as “Background” and “Summary”) and sub-headings used herein are intended only for general organization of topics within the present disclosure, and are not intended to limit the disclosure of the technology or any aspect thereof. The recitation of multiple embodiments having stated features is not intended to exclude other embodiments having additional features, or other embodiments incorporating different combinations of the stated features.

[0027] As used herein, the terms “comprise” and “include” and their variants are intended to be non-limiting, such that recitation of items in succession or a list is not to the exclusion of other like items that may also be useful in the devices and methods of this technology. Similarly, the terms “can” and “may” and their variants are intended to be non-limiting, such that recitation that an embodiment can or may comprise certain elements or features does not exclude other embodiments of the present technology that do not contain those elements or features.

[0028] The broad teachings of the present disclosure can be implemented in a variety of forms. Therefore, while this disclosure includes particular examples, the true scope of the disclosure should not be so limited since other modifications will become apparent to the skilled practitioner upon a study of the specification and the following claims. Reference herein to one aspect, or various aspects means that a particular feature, structure, or characteristic described in connection with an embodiment or particular system is included in at least one embodiment or aspect. The appearances of the phrase “in one aspect” (or variations thereof) are not necessarily referring to the same aspect or embodiment. It should be also understood that the various method steps discussed herein do not have to be carried out in the same order as depicted, and not each method step is required in each aspect or embodiment.

[0029] The foregoing description of the embodiments has been provided for purposes of illustration and description. It is not intended to be exhaustive or to limit the disclosure. Individual elements or features of a particular embodiment are generally not limited to that particular embodiment, but, where applicable, are interchangeable and can be used in a selected embodiment, even if not specifically shown or described. The same may also be varied in many ways. Such variations should not be regarded as a departure from the disclosure, and all such modifications are intended to be included within the scope of the disclosure.