Non-flammable laminate

Abstract

The invention relates to a laminate, in particular for manufacturing a construction panel, consisting of a combination of at least one carrier material layer made of a non-flammable non-woven impregnated with a resin and at least one decorative material layer made of a decorative paper that is impregnated with a melamine formaldehyde resin and is optionally dyed and/or printed. The invention further relates to a method for manufacturing a disclosed laminate and especially a construction panel.

Claims

1. A laminate for manufacturing a construction panel, comprising: at least one carrier material layer made of a non-flammable non-woven fabric impregnated with a first synthetic resin; and at least one decorative material layer made of a decorative paper that is impregnated with a second synthetic resin, the second synthetic resin being different from the first synthetic resin, wherein the second synthetic resin comprises melamine formaldehyde resin, wherein the decorative paper to be impregnated comprises a specific surface weight comprised between 22 g/m.sup.2 and 220 g/m.sup.2 and an ash content of at least 20% by weight, wherein the laminate comprises a total thickness of less than 2.2 mm and a calorific value of less than 2 MJ/kg according to ISO 1716, and wherein a surface of the decorative material layer which is facing away from the impregnated carrier material layer is provided with a flame retardant.

2. The laminate according to claim 1, wherein the non-woven fabric is a glass fiber non-woven fabric.

3. The laminate according to claim 1, wherein the non-woven fabric consists of quartz glass fibers.

4. The laminate according to claim 1, wherein the non-woven fabric is a random orientation fleece.

5. The laminate according to claim 1, wherein the non-woven fabric is a knitted fleece material or any other non-flammable fleece material.

6. The laminate according to claim 1, wherein the synthetic resin includes a crosslinker in the form of an additive for impregnating the non-woven fabric.

7. The laminate according to claim 1, wherein a metal hydroxide, metal carbonate, titanium oxide, calcinated loess, barium sulfate, magnesium sulfate, aluminum sulfate, zinc oxide, kaolin, chlorite, diatomite, feldspar, mica, nepheline syenite, pyrophyllite, silicon, talcum, wollastonite, montmorillonite, hectorite, saponite, calcium carbonate, magnesium carbonate, aluminum oxide, iron oxide, magnesium hydroxide and/or micro-spheres made of glass is present in the synthetic resin as a filling material for impregnating the non-woven fabric.

8. The laminate according to claim 1, wherein the decorative paper to be impregnated comprises a porosity according to Gurley of less than 20 s/100 ml according to ISO 5636/5.

9. The laminate according to claim 1, wherein the decorative paper to be impregnated comprises a smoothness of Bekk of more than 70 s/Bekk according to ISO 5627.

10. The laminate according to claim 1, wherein the decorative paper to be impregnated comprises a penetration of less than 5 s according to ISO 5633 with respect to the melamine formaldehyde resin used for the impregnation.

11. The laminate according to claim 1, wherein the decorative paper to be impregnated is produced from short fibers and/or long fibers.

12. The laminate according to claim 1, wherein the decorative paper includes a dye consisting of inorganic substances.

13. The laminate according to claim 1, wherein titanium oxide or talcum serve as a filling material in the melamine formaldehyde resin used for impregnating the decorative paper.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) Other details, features and advantages of the invention will explained in more detail in the following by means of the exemplary embodiments represented in the figures of the drawings.

(2) FIG. 1 is a schematic cut view which shows an exemplary embodiment of a laminate according to the invention;

(3) FIGS. 2a to 2d are schematic cut views which show an exemplary embodiment of a method according to the invention for manufacturing a laminate; and

(4) FIG. 3 is a schematic cut view which shows another exemplary embodiment of a laminate according to the invention.

DETAILED DESCRIPTION

(5) FIG. 1 shows a schematic cut view of a laminate 1. The laminate 1 consists of a composite formed of a carrier material layer 2 and a decorative material layer 5. Herein, the carrier material layer 2 consists of non-flammable non-woven fabric 4 which is impregnated with a synthetic resin 3. The decorative material layer 5 however consists of a decorative paper 7 that is impregnated with melamine formaldehyde resin 6. Furthermore, it is visible in FIG. 1 that in a laminate which has been manufactured by means of the method according to the invention the synthetic resin 3 used for impregnating the carrier material layer 2 and the melamine formaldehyde resin 6 used for impregnating the decorative material layer 5 have mixed with each other, which leads to a further improvement of the laminate 1 with respect to its fire behavior.

(6) FIG. 2a (first process step) is a schematic cut view which shows a non-flammable non-woven fabric 4 for a carrier material layer as well as an optionally dyed and/or printed decorative paper 7 for a decorative material layer. Neither the non-woven fabric 4 nor the optionally dyed and/or printed decorative paper 7 are impregnated with a synthetic resin and connected with each other in this process step.

(7) FIG. 2b (second process step) is a schematic cut view which shows a non-flammable non-woven fabric 4 that is now impregnated with a synthetic resin 3 as well as an optionally dyed and/or printed decorative paper 7 that has been impregnated with a melamine formaldehyde resin 6. The impregnation of the two individual components which are required for a laminate that consists of a composite, can take place sequentially or in parallel. Furthermore, it is imaginable that an already preconfigured layer of a non-woven fabric 4 that is impregnated with a synthetic resin 3 and/or of an optionally dyed and/or printed decorative paper 7 that is impregnated with a melamine formaldehyde resin 6 will be used.

(8) FIG. 2c (third process step) is a schematic cut view which shows the pressing of a non-flammable non-woven fabric 4 which is impregnated with a synthetic resin 3 with an optionally dyed and/or printed decorative paper 7 that is impregnated with a melamine formaldehyde resin 6 into a composite. Herein, the pressing operation will be carried out at an increased temperature and high surface pressure by means of a one-level or multi-level press or a continuous double belt press with or without back cooling. The laminate known from FIG. 1 can be manufactured by means of such a pressing operation.

(9) FIG. 2d (fourth process step) is a schematic cut view which shows a laminate 1 according to the invention in the form of a composite which results from the pressing of the carrier material layer 2 made of a non-flammable non-woven fabric 4 which is impregnated with a synthetic resin 3 with a decorative material layer 5 made of an optionally dyed and/or printed decorative paper 7 that is impregnated with a melamine formaldehyde resin 6. It is furthermore visible in FIG. 2d that during the pressing of both material layers, the synthetic resin 3 used for impregnating the carrier material layer 2 and the melamine formaldehyde resin 6 used for impregnating the decorative material layer 5 have mixed with each other, in particular in the border area of the two material layers. Thanks to such a mixing of the different resins the laminate is further improved with respect to its fire behavior.

(10) FIG. 3 is a schematic cut view which shows a laminate according to the invention, in which the surface of the decorative material layer 5 which is facing away from the impregnated carrier material layer 2 is provided with a flame retardant. This serves in particular to further improve the laminate 1 according to the invention with respect to its fire behavior.

(11) The exemplary embodiments represented in the figures of the drawing and the exemplary embodiments explained in connection with these ones only serve for explaining the invention and are not limiting for this one.

LIST OF REFERENCE NUMERALS

(12) 1 laminate 2 carrier material layer 3 synthetic resin 4 non-woven fabric 5 decorative material layer 6 melamine formaldehyde resin 7 decorative paper 8 flame retardant