Surfacing materials and method of manufacture

Abstract

A surfacing material includes a substrate having a top side and a bottom side. A matte surface is formed on the bottom side thereof, wherein the matte surface of the surfacing material is a coating of an electron beam radiation curable material applied to the bottom side of the substrate. The coating is an epoxy acrylic or urethane acrylic laid upon the substrate. The epoxy acrylic or urethane acrylic is irradiated with UV-radiation to produce a UV-radiation layer wherein the epoxy acrylic or urethane acrylic is neither hardened nor is an entire layer of the epoxy acrylic or urethane acrylic crosslinked but rather the epoxy acrylic or urethane acrylic only crosslinked on the surface thereof, which produces a matting surface through the effects of a micro-convolution.

Claims

1. A texture-imparting surfacing material, comprising: a substrate including a top side and a bottom side; and a matte surface formed on the bottom side thereof, wherein the matte surface of the surfacing material is a coating of an electron beam radiation curable material applied to the bottom side of the substrate, the coating being an epoxy acrylic or urethane acrylic applied to the substrate, wherein the epoxy acrylic or urethane acrylic is irradiated with UV-radiation to produce a UV-irradiated layer wherein the epoxy acrylic or urethane acrylic is only crosslinked on the surface thereof, which produces a matting surface through the effects of a micro-convolution, and is subsequently subjected to electron beam irradiation to crosslink and harden the entire layer and thermal curing to complete curing of the coating due to the inclusion of a peroxide.

2. The texture-imparting surfacing material according to claim 1, wherein the peroxide is test-butyl peroxybenzoate (TBPB).

3. The texture-imparting surfacing material according to claim 1, wherein the epoxy acrylic or urethane acrylic is applied to the substrate with a layer thickness of no more than 150 microns.

4. The texture-imparting surfacing material according to claim 3, wherein the epoxy acrylic or urethane acrylic is applied to the substrate with the layer thickness in a range between 30 and 100 microns.

5. The texture-imparting surfacing material according to claim 1, wherein the substrate is a plastic, metal, or paper film material.

6. The texture-imparting surfacing material according to claim 5, wherein the plastic film material is a polypropylene film.

7. A laminate lay-up, comprising: a texture-imparting release sheet composed of a release sheet substrate including a top side and a bottom side; and a matte surface formed on the bottom side thereof, wherein the matte surface of the surfacing material is a coating of an electron beam radiation curable material applied to the bottom side of the release sheet substrate, the coating being an epoxy acrylic or urethane acrylic applied to the release sheet substrate, wherein the epoxy acrylic or urethane acrylic is irradiated with UV-radiation to produce a UV-irradiated layer wherein the epoxy acrylic or urethane acrylic is only crosslinked on the surface thereof, which produces a matting surface through the effects of a micro-convolution, and is subsequently subjected to electron beam irradiation to crosslink and harden the entire layer and thermal curing to complete curing of the coating; and a decorative laminate, the decorative laminate including, a decorative layer substrate including a top side and a bottom side; and a coating formed on the top side thereof, which is placed into contact with the matte surface of the texture-imparting release sheet, the coating being a UV and thermal curable epoxy acrylic or urethane acrylic applied to the top side of the decorative layer substrate, wherein the coating is applied to the substrate and partially cured via UV-radiation to create a UV-irradiated layer, which is subsequently and fully cured via thermal curing; a core layer adjacent the bottom side of the decorative layer substrate composed of one or more sheets of paper impregnated with resin, wherein the thermal curing of the coating of the texture imparting release sheet and the coating of the decorative laminate is effectuated when the laminate lay-up is heated and pressed and is due to the inclusion of a peroxide.

8. The laminate lay-up according to claim 7, wherein the peroxide is tert-butyl peroxybenzoate (TBPB).

9. The laminate lay-up according to claim 7, wherein the epoxy acrylic or urethane acrylic of the release sheet and/or the decorative laminate is/are applied with a layer thickness of no more than 150 microns.

10. The laminate lay-up according to claim 9, wherein the layer thickness of the epoxy acrylic or urethane acrylic of the release sheet is in a range between 30 and 100 microns and the layer thickness of the epoxy acrylic or urethane acrylic of the decorative laminate is in a range between 60 and 80 microns.

11. The laminate lay-up according to claim 7, wherein the release sheet substrate is a plastic, metal, or paper film material.

12. The laminate lay-up according to claim 11, wherein the plastic film material is a propylene film.

13. The laminate lay-up according to claim 7, wherein the decorative layer substrate is a resin impregnated decorative paper.

14. The laminate lay-up according to claim 13, wherein the decorative laminate further comprises a resin impregnated transparent overlay paper layer between the coating and the top side of the decorative layer substrate.

15. The laminate lay-up according to claim 14, wherein the overlay is initially B-stage cured and is fully cured when the laminate lay-up is heated and pressed.

16. The laminate lay-up according to claim 13, wherein the impregnated resin of the decorative layer substrate is a melamine-formaldehyde.

17. The laminate lay-up according to claim 14, wherein the impregnated resin of the overlay paper layer is a melamine-formaldehyde.

18. The laminate lay-up according to claim 7, wherein the impregnated resin of the core is a phenolic resin.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is a schematic of a laminate lay-up in accordance with an embodiment of the present invention.

(2) FIG. 2 is a schematic of a high pressure decorative laminate produced in accordance with the present invention.

(3) FIG. 3 is a schematic of a multi-laminate pressing assembly in accordance with the present invention.

(4) FIG. 4 is a schematic of a laminate lay-up in accordance with an alternate embodiment.

(5) FIG. 5 is a schematic of a high pressure decorative laminate in accordance with the alternate embodiment disclosed with reference to FIG. 4.

(6) FIGS. 6A and 6B are schematics showing the fabrication of the release sheet in accordance with the present invention.

(7) FIG. 7 is a schematic of a laminate lay-up in accordance with another embodiment of the present invention.

(8) FIG. 8 is a schematic of the high pressure decorative laminate produced in accordance with the embodiment of FIG. 7.

(9) FIG. 9 is a schematic of a multi-laminate pressing assembly in accordance with the embodiment of FIG. 7.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

(10) The detailed embodiments of the present invention are disclosed herein. It should be understood, however, that the disclosed embodiments are merely exemplary of the invention, which may be embodied in various forms. Therefore, the details disclosed herein are not to be interpreted as limiting, but merely as a basis for teaching one skilled in the art how to make and/or use the invention.

(11) With reference to FIGS. 1, 2 and 3, a decorative laminate lay-up 10 including a decorative laminate sheet assembly 12 (composed of an exterior overlay paper layer 16, a decorative layer 18, and a core layer 20 as discussed below in greater detail) and a texture imparting member in the form of a textured release sheet 14 (including a top side 14t and a bottom side 14b) is disclosed. As will be explained below in accordance with an alternate embodiment, the decorative laminate lay-up may be assembled without an overlay paper layer. The decorative laminate lay-up 10 is used in the manufacture of decorative laminates 100 (see FIG. 2) in accordance with an embodiment of the present invention. The textured release sheet 14 imparts a textured matte surface 14a (formed on the bottom side 14b thereof) to a resulting decorative laminate 100, wherein the textured matte surface 14a of the textured release sheet 14 results in a decorative laminate 100 that exhibits a matte appearance and is not susceptible to a build-up of fingerprints on the surface thereof. It is further appreciated the release sheet 14 also functions as a release mechanism between decorative laminate sheet assemblies 12 when subjected to heat and pressure in a conventional platen press manufacturing process. With this in mind, the textured release sheets 14 of the present invention may be used in gang processing of decorative laminates 100 or the present textured release sheets 14 may be used in the manufacture of single decorative laminate to simply impart a desired matte surface.

(12) The decorative laminate lay-up 10 is assembled by first stacking a decorative laminate sheet assembly 12 having a top layer (which, as explained below, is preferably an overlay paper sheet 16). That is, the sheets used in the production of the decorative laminate 100 are stacked in preparation for the heating and pressure steps used to consolidate the laminate. A textured release sheet 14 composed of a substrate 14s and a textured coating layer 14c defining the textured matte surface 14a is also prepared.

(13) The process for producing surface effects in a release coating as disclosed in European Patent Application Publication No. 2527408, entitled Method for Producing a Film with a Matt Surface, which is incorporated herein by reference, is employed in the manufacture of textured release sheets 14 for use in accordance with the present invention. Briefly, the '408 publication teaches a technique for producing surface effects on a sheet. In accordance with the disclosed methodology a coating of an electron beam radiation curable material is applied to one surface of a web substrate, and subsequently cured (ultimately producing the textured coating layer 14c with the textured matte surface 14a of the release sheet 14 in accordance with the present invention). The surface forming techniques of the '408 publication result in a film (or textured release sheet 14 in accordance with the present invention) with a textured matte surface 14a. The textured matte surface 14a exhibits good matting properties (and correspondingly low degrees of gloss as defined in and measured in accordance with DIN EN ISO 2813) having improved scratch resistance properties. Ultimately, and as will be explained below in greater detail, the film produced as a result of the manufacturing process disclosed in the '408 publication is ultimately utilized as a release sheet in the manufacture of decorative laminate.

(14) The material produced in accordance with the '408 publication is sold under the name FENIX NTM. FENIX NTM is described as a super opaque nanotech material that is an innovative interior design product, created by Arpa Industriale. FENIX NTM combines elegant aesthetic solutions with state-of-the-art technological performance. The external surface of FENIX NTM employs nanotechnology and is characterized by next generation acrylic resins, hardened and fixed with electron beam curing.

(15) With reference to FIGS. 6A & 6B, the release sheet 14 of the present invention (as produced in accordance with the '408 publication), employs a solvent-free and non-aqueous lacquer (in accordance with the present invention the lacquer is preferably an epoxy acrylic or a urethane acrylic (also referred to herein as the acrylate mixture)) in the production of the textured coating layer 14c on the substrate 14s. The matte release sheet 14 employed in accordance with the present invention is produced through the implementation of a two-stage irradiation process. First, and with reference to FIG. 6A, the epoxy acrylic or urethane acrylic 14ea (which is ultimately cured to form the textured coating layer 14c) is laid, or otherwise applied, upon the substrate 14s and the epoxy acrylic or a urethane acrylic 14ae is irradiated with UV-radiation to a create a UV-irradiated layer 14m. However, the irradiation is applied so that epoxy acrylic or urethane acrylic 14ea is neither hardened nor is the entire layer of epoxy acrylic or urethane acrylic 14ae crosslinked. Rather the epoxy acrylic or urethane acrylic 14ea is only crosslinked on the surface thereof, which produces a matting surface through the effects of a micro-convolution. In accordance with a preferred embodiment, the UV-radiation irradiates at a wavelength of approximately 200 nm-400 nm. It is, however, appreciated excimer emitter based on a Xe-emission spectrum is known, which might be particularly favorable for a large-scale production.

(16) Referring to FIG. 6B, the UV-irradiated layer 14m (on the substrate 14s) is then subjected to an electron beam irradiation to crosslink and harden the entire layer and form the final textured coating layer 14c of the release sheet 14.

(17) This procedure initially creates a shrinking process in the epoxy acrylic or urethane acrylic 14ea that ultimately becomes the epoxy acrylic or urethane acrylic textured coating layer 14c and thus the desired matting directly on the surface of the resulting release sheet 14. The production of a textured matte surface 14a is achieved according to the '408 publication with 100% lacquers, to which no separate matting agent (such as silica or the like) is added. The curing and cross-linking of the total layer by means of electron beam irradiation fixes the matte surface created by the partial curing and irradiation without influencing the matte surface in any adverse manner. The matte release sheet 14 produced in this manner is distinguished by outstanding matting properties, which gloss levels to less than 3 (measured in accordance with the cited DIN EN ISO 2813 and 60 geometry) or less than 5 (corresponding at 85 geometry) can be reached.

(18) In accordance with a preferred embodiment, the epoxy acrylic or urethane acrylic 14ea is preferably applied to the substrate 14s by a roller, with a layer thickness greater than 5 microns and up to approximately 150 microns (preferably, 30 to 100 microns). The substrate 14s is selected from various substrate plastic materials such as polypropylene, polyester or the like, as well as films made of metal or paper material. In accordance with a preferred embodiment, a plastic film substrate of polypropylene, layer thickness 150 microns, is coated by flexographic printing with an epoxy acrylic or urethane acrylic mixture to produce a coating thickness of greater than 30 microns and up to approximately 150 microns (preferably, 60 to 80 microns), wherein the acrylate mixture, in accordance with one embodiment, has the following composition as disclosed in the '408 publication:

(19) TABLE-US-00001 100 T NeoRad U 6288 (a 100% UV curable resin, which can be (Parts) used in coatings and overprint varnishes for luxury packaging and high end promotional printing. NeoRad U-6288 offers broad formulating latitude and high matte efficiency, working with most common matting agents. In particular, it is a UV curable urethane acrylate. It exhibits good adhesion, hardness, yellowing and improved flow. It has high matte efficiency, very good flexibility and excellent shrinkage. It also exhibits superior chemical- and abrasion-resistance.). 10 T Ebecryl 5129 (a hexafunctional aliphatic urethane acrylate (Parts) oligomer which provides fast cure response when exposed to ultraviolet light or electron beam. Cured films of Ebecryl 5129 exhibit high hardness, abrasion and solvent resistance combined with a good flexibility). 40 T TiO.sub.2 pigments (Parts) 10 T Matting agents (Parts) where NeoRad U 6288 is a mixture of oligomer and monomer.

(20) The acrylate mixture is preferably Ebecryl5129 added with a proportion of 5 to 10 weight percent of the total acrylate mixture, and there are titanium dioxide pigments of an average particle size of 0.1 microns admixed as white pigmentation. The coated substrate is passed under an inert gas in a continuous (in-line) process under a 200-400 nm excimer emitter, with a typical feed of 60 m/min at 0.5 cm distance from the coating surface. The result is a surface matting of gloss <4 (60 geometry, measured as before) which immediately is subjected to thereafter an electron beam crosslinking (and hence hardening) of the acrylate mixture with a record of 30 kGy.

(21) In accordance with an alternate embodiment, the acrylate mixture is as follows:

(22) TABLE-US-00002 42% Ebecryl 294/HD 25 (an aliphatic urethane triacrylate oligomer diluted with 1,6-hexanediol diacrylate (HDDA)(1) monomer.). 38% Ebecryl 5129 (a hexafunctional aliphatic urethane acrylate oligomer which provides fast cure response when exposed to ultraviolet light or electron beam.). 9% Ebecryl 8209 (a Sn-free aliphatic urethane acrylate oligomer which provides extremely fast cure response when exposed to ultraviolet (UV) light or electron beam (EB).). 5% HDDA/TMPTA (Hexanediol diacrylate (HDDA) is a difunctional reactive diluent that is commonly used as a component of ultraviolet light (UV) and electron beam (EB) curable coatings and inks. Trimethylolpropane triacrylate (TMPTA) is a trifunctional monomer used for its low volatility and fast cure response.) 2% Photoinitiator 2% Cerafak 127N (a Fischer Tropsch wax dispersion. Provides improved water repellence properties.). 1% TBPB (tert-Butyl peroxybenzoate (TBPB) a chemical compound from the group of peresters which functions as a radical initiator in a polymerization process. 1% Modaflow 9200 (an acrylic flow modifier, without silicone addition. It improves flow and leveling, substrate wetting, or maintains high gloss and substrate and inter-coat adhesion, and facilitates pigment dispersion).

(23) With the laminate sheet assembly 12 and the finished release sheet 14 prepared, the finished release sheet 14 is positioned on the top surface 16a (in the case of the present laminate sheet assembly 12 it is positioned on the upper surface of the overlay sheet 16) of the laminate sheet assembly 12 to form the laminate lay-up 10. The release sheet 14 is positioned on the overlay sheet 16 with the bottom side 14b (that is, the textured matte surface 14a) of the release sheet 14 facing the top surface 16a of the overlay sheet 16.

(24) Heat and pressure are then applied to the laminate sheet assembly 12 and the textured release sheet 14 using press plates in a conventional manner. The heat and pressure are applied in manner sufficient to bond the layers of the decorative laminate sheet assembly 12, and releasably bond the textured release sheet 14 (in particular, the bottom side 14b with the textured matte surface 14a) to the top surface 16a of the decorative laminate sheet assembly 12. The heat and pressure also effectuate the final curing where peroxide is integrated into the textured release sheet (as in the case of the second acrylate mixture embodiment disclosed above). Finally, the textured release sheet 14 is removed from the top layer 16a of the formed decorative laminate 100 to reveal a decorative laminate 100 exhibiting desired matte texture characteristics.

(25) In accordance with an embodiment of the present invention, and as discussed above, the release sheet 14 is formed with a textured matte surface 14a on the bottom side 14b thereof (the texture of which is ultimately applied to the top surface 16a of the decorative laminate 100) exhibiting matte surface characteristics leading to a fingerprint proof surface, that is, a surface not showing fingerprints and remaining clean and clear despite regular use. As discussed above, the release sheet 14 is preferably an acrylic coated polypropylene sheet, the acrylic coating of which is applied in accordance with the procedure disclosed in the '408 publication.

(26) The texture of the textured matte surface 14a applied to the release sheet 14 is ultimately applied to the top surface 16a of the resulting decorative laminate 100 as texture 16t resulting in a textured top surface 16a of the resulting decorative laminate 100) with a matte surface. When the textured matte surface 14a (that is, the texture) of the release sheet 14 is applied to the decorative laminate 100 as discussed below in greater detail, the top surface 16a of the decorative laminate 100 is imparted with a texture 16t (that is, the decorative laminate 100 is provided with a textured surface) the same as the texture of the textured matte surface 14a of the release sheet 14 making the laminate 100 less susceptible to the formation of annoying and undesirable fingerprints thereon.

(27) Summarizing, when such texture 16t is applied to the top surface 16a of the decorative laminates 100 so as to provide for a textured top surface, the resulting characteristics result in the formation of a laminate not susceptible to the formation of annoying and undesirable fingerprints.

(28) As the textured matte surface 14a of the release sheet 14 is ultimately imparted to the top layer (that is, the texture 16t of the top surface 16a of the overlay paper layer 16 in accordance with an embodiment of the present invention) of the decorative laminate 100 formed using the textured release sheet 14, the resulting decorative laminate 100 is provided with a top surface 16a having texture 16t that is the same as that of the textured surface 14a and will exhibit desired resistance to the formation of fingerprints.

(29) In accordance with one embodiment of the present invention, and as discussed above, the decorative laminate 100 includes an exterior overlay layer sheet 16, or top layer, a decorative sheet 18 and a core 20. While a specific layering pattern is disclosed in accordance with a preferred embodiment of the present invention, the layering pattern may be varied, somewhat, without departing from the spirit of the present invention.

(30) The overlay paper layer 16 is preferably a melamine-formaldehyde impregnated paper layer. The overlay paper layer 16 is preferably manufactured from a low basis weight transparent sheet impregnated with resin, for example, melamine-formaldehyde. The resin impregnated overlay paper layer 16 is subsequently dried, partially cured and finally cut into sheets. In accordance with a preferred embodiment, the overlay paper layer 16 is B-stage cured and is then coated with a UV curable epoxy acrylic or urethane acrylic film 16f that is also partially cured (and ultimately defines the top surface 16a of the overlay paper layer) prior to the platen pressing process that ultimately completes the curing process. While the paper may exhibit opaque properties prior to heating and pressing, the overlay paper layer 16 in the final fabricated laminate is preferably transparent to permit viewing of the decorative sheet 18 positioned directly beneath the overlay paper layer 16. The overlay paper used in accordance with an embodiment of the present invention is a low weight basis alpha-cellulose paper with a high porosity for resin absorption. The decorative layer 18 is a conventional pattern sheet positioned directly beneath the overlay paper layer 16. When the decorative laminate 100 is fully heated and pressed, as will be discussed below in greater detail, the overlay paper layer 16 becomes translucent, fully exposing the decorative layer 18. In addition, it is the top surface 16a of the overlay paper layer 16 which takes on the texture 16t imparted by the release sheet 14. With this in mind, the decorative layer 18 is substantially responsible for the aesthetic appearance of the finished decorative laminate 100.

(31) Decorative layers 18 are chosen from a wide array of sheets. For example, the decorative layer 18 may be a solid color (for example, white) or include an aesthetically appealing pattern. As discussed above, the decorative layer 18 provides the decorative laminate 100 with an attractive appearance. The overlay paper layer 16 and the decorative layer 18 also dictate the surface characteristics of the final decorative laminate 100. For example, the composition of the overlay paper layer 16 and decorative layer 18 help to dictate the decorative laminate's resistance to chemical agents, heat, light, shock and abrasion.

(32) Decorative sheets 18 are commonly manufactured from high quality 80-202 grams per square meter ream weight, pigment filled, alpha cellulose paper impregnated with a water alcohol or water solution of melamine-formaldehyde resin. The resin impregnated decorative sheets 18 are subsequently dried, partially cured, and finally cut into sheets. The pigment filled, alpha cellulose paper of the decorative sheet, may include a solid color, a decorative design, or a photo-gravure reproduction of natural materials, such as, wood, marble, leather, etc. The aesthetic characteristics of the cellulose paper are revealed as the laminate's decorative design upon completion of the decorative laminate.

(33) The core layer 20 is preferably composed of a plurality of phenolic resin impregnated sheets 20a, 20b, 20c, although other materials may be used without departing from the spirit of the present invention. For example, the core layer 20 includes sheets of 120-323 grams per square meter dry phenolic resin impregnated Kraft paper. The Kraft paper is impregnated throughout and bonded with a substantially cured phenolic resin which is converted to a thermoset state during the initial laminating step.

(34) In accordance with an embodiment of the present invention, the decorative laminate 100 of the present invention is formed in much the same manner as conventional decorative laminates. The layers are first stacked and placed between steel plates with the release sheet 14 covering the overlay paper layer 16. The decorative laminate lay-up (or stack) 10 is then subjected to temperatures in the range of 121 C.-160 C. and pressures of about 56.24 kg/cm.sup.2 to 112.48 kg/cm.sup.2 for a time sufficient to consolidate the laminate and cure the resins (generally about 25 minutes to an hour).

(35) The pressure and heat force the resin in the paper sheets to flow, cure and consolidate the sheets into a unitary laminated mass referred to in the art as a decorative high pressure laminate 100 having the hydrophobic textured surface 16t as described above which is imparted by the textured matte surface 14a of the release sheet 14. Generally, more than one decorative laminate is formed at one time. As shown with reference to FIG. 3, multiple decorative laminates are formed by inserting a plurality of lay-ups 10 in a stack. Conventional sheets 40 are positioned between the core lays 20 of the lay-ups 10 to separate the various decorative laminates stacked together. The textured matte surface 14a of the release sheet 14 is oriented against the top surface 16a (in this case the upper surface of the overlay paper layer 16 as defined by the UV curable epoxy acrylic or urethane acrylic film 16f) of the decorative laminate sheet assembly 12, be it the decorative sheet 18 (as discussed below with reference to an alternate embodiment) or the overlay paper layer 16, with the smooth top side (or back surface) 14t of the textured release sheet 14 positioned against the steel plate 30. A standard release sheet 40 is positioned between the adjacent lay-ups 10 along the core layer sides. Upon pressing between suitable laminate press plates, the textured release sheet 14 imparts the matte texture 16t described above to the top surface 16a of the first lay-up layer (in this case the upper surface of overlay paper layer 16 as defined by the UV curable epoxy acrylic or urethane acrylic film 16f thereby creating the textured surface 16t discussed above), and serves to allow release between the first lay-up and the adjacent lay-up. A platen press assembly, as is well known in the lamination art, provides the necessary heat and/or pressure during lamination. After consolidation, the release sheets allow the individual decorative laminates to be separated.

(36) As discussed above, and with reference to FIGS. 4 and 5, the decorative laminate 100 of an embodiment of the present invention may be manufactured without the overlay. The decorative laminate 100 is manufactured with the formation of a decorative laminate lay-up 10 including a decorative laminate sheet assembly 12 composed of a decorative layer 18 and a core layer 20. The core layer 20 is the same as discussed with regard to the embodiments disclosed with reference to FIGS. 1 to 3. The decorative layer 18 is the same as discussed above with the exception that, after the resin impregnated decorative sheet is B-stage cured, it is coated with a UV curable epoxy acrylic or urethane acrylic film 18f that is also partially cured (and ultimately defines the top surface 18a of the decorative layer 18) prior to the platen pressing process that ultimately completes the curing process.

(37) The manufacture of the decorative laminate in accordance with this embodiment also requires a texture imparting member in the form of a textured release sheet 14 (including a top side 14t and a bottom side 14b) as discussed above with regard to the embodiment disclosed with reference to FIGS. 1 to 3. Briefly, and as discussed above in detail, the textured release sheet 14 includes a textured matte surface 14a (formed on the bottom side 14b thereof) and applies the textured matte surface 14a to a resulting decorative laminate 100, wherein the textured matte surface 14a imparts the matte texture in a decorative laminate 100 that exhibits the matte appearance and is not susceptible to a build-up of fingerprints on the surface thereof. The release sheet 14 also functions as a release sheet between decorative laminate sheet assemblies 12.

(38) The decorative laminate lay-up 10 is assembled by first stacking a decorative laminate sheet assembly 12 having a top layer (which, as explained below, is preferably the UV curable epoxy acrylic or urethane acrylic film 18f of the decorative layer 18). The textured release sheet 14 is also prepared.

(39) In practice, the finished release sheet 14 is positioned on the top surface 18a (in the case of the present laminate sheet assembly 12 it is positioned on the upper surface of the decorative layer 18) of the laminate sheet assembly 12 to form the laminate lay-up 10. The release sheet 14 is positioned on the decorative layer 18 with the bottom side 14b (that is, the textured matte surface 14a) of the release sheet 14 facing the top surface 18a of the decorative layer 18. Heat and pressure are then applied to the laminate sheet assembly 12 and the textured release sheet 14 sufficient to bond the layers of the decorative laminate sheet assembly 12, and releasably bond the textured release sheet 14 (in particular, the bottom side 14b with the textured matte surface 14a) to the top surface 18a of the decorative laminate sheet assembly 12. Finally, the textured release sheet 14 is removed from the top layer 18a of the formed decorative laminate 100 to reveal a decorative laminate 100 exhibiting desired matte texture characteristics.

(40) In accordance with an embodiment of the present invention, and as discussed above, the release sheet 14 is formed with a textured matte surface 14a on the bottom side 14b thereof (the texture of which is ultimately applied to the top surface 18a of the decorative laminate 100) exhibiting matte surface characteristics leading to a fingerprint proof surface, that is, a surface not showing fingerprints and remaining clean and clear despite regular use.

(41) The texture of the textured matte surface 14a applied to the release sheet 14 is ultimately applied to the top surface 18a of the resulting decorative laminate 100 as texture 18t resulting in a textured top surface 18a of the resulting decorative laminate 100 with a matte surface. When the textured matte surface 14a (that is, the texture) of the release sheet 14 is applied to the decorative laminate 100, the top surface 18a of the decorative laminate 100 is imparted with a texture 18t (that is, the decorative laminate 100 is provided with a textured surface) that is the same as the texture of the textured matte surface 14a of the release sheet making the laminate 100 less susceptible to the formation of annoying and undesirable fingerprints thereon.

(42) In accordance with yet another embodiment of the present invention, the textured release sheet 14 of the above embodiments, may be used in conjunction with different decorative laminate lay-up 210 employing a decorative layer 218 having a UV/thermal cured coating 218c applied to a decorative sheet substrate 218s. In particular, and with reference to FIGS. 7, 8, and 9, a decorative laminate lay-up 210 including a release sheet 14 and a decorative laminate sheet assembly 212 composed of a decorative layer 218 and a core layer 220 as discussed below in greater detail is disclosed. The decorative laminate lay-up 210 is used in the manufacture of decorative laminates 300 (see FIG. 8) in accordance with the present invention.

(43) Although this embodiment discloses a decorative laminate manufactured without an overlay paper layer, it is appreciated the present invention may be adapted for decorative laminates including an overlay paper layer. In accordance with such a variation, the UV/thermal cured coating would be applied to the overlay paper layer instead of the decorative layer.

(44) With reference to FIGS. 7 to 9, the decorative layer 218 of this embodiment employs a solvent-free and non-aqueous lacquer (in accordance with the present invention the lacquer is preferably a UV/thermal curable epoxy acrylic or urethane acrylic (which is referred to below as the acrylate mixture)) in the production of the UV/thermal cured coating 218c on the decorative layer 218. In accordance with a preferred embodiment, and as will be discussed below in greater detail, the decorative layer 218 includes a base composed of a melamine-formaldehyde resin impregnated decorative sheet substrate 218s.

(45) The decorative layer 218, and ultimately the decorative laminate 300, of this embodiment are produced through the implementation of a multi-stage curing process. The substrate 218s of the decorative layer 218 is chosen from a wide array of decorative sheets. For example, the decorative sheet substrate 218s may be a solid color (for example, white) or include an aesthetically appealing pattern. As discussed above, the decorative layer 218 provides the decorative laminate 300 with an attractive appearance.

(46) The decorative sheet substrate 218s in accordance with the present embodiment is manufactured from high quality 80-202 grams per meter squared ream weight, pigment filled, alpha cellulose paper impregnated with a water alcohol or water solution of melamine-formaldehyde resin. The resin impregnated decorative sheet substrate 218s is subsequently dried, partially cured, and finally cut into sheets. The pigment filled, alpha cellulose paper of the decorative sheet substrate 218s, may include a solid color, a decorative design, or a photo-gravure reproduction of natural materials, such as, wood, marble, leather, etc. The aesthetic characteristics of the cellulose paper are revealed as the laminate's decorative design upon completion of the decorative laminate 300.

(47) Once the decorative sheet substrate 218s is prepared (in a traditional manner) as described above, the UV/thermal curable epoxy acrylic or urethane acrylic 218ea (which is ultimately cured to form the textured coating layer 218c) is applied upon the decorative sheet substrate 218s and is irradiated with UV-radiation to a create UV-irradiated layer 218m. In accordance with an alternate embodiment, the epoxy acrylic or urethane acrylic 218ea may be irradiated with electron beam radiation or by a combination of UV and electron beam radiation. However, and regardless whether UV-radiation is applied or electron beam radiation is application, the irradiation is applied so that epoxy acrylic or urethane acrylic 218ea is only partially cured. The epoxy acrylic or urethane acrylic 218ea is partially cured to the extent the epoxy acrylic or urethane acrylic 218ea is no longer tacky but before the epoxy acrylic or urethane acrylic 218ea is cured to the extent the epoxy acrylic or urethane acrylic 218ea begins curling due to too much curing.

(48) In accordance with a preferred embodiment, the epoxy acrylic or urethane acrylic 216ea is preferably applied to the substrate 216s by a roller, with a layer coating thickness of greater than 30 microns and up to approximately 150 microns (preferably, 60 to 80 microns), wherein the acrylate mixture, in accordance with one embodiment, has the following composition:

(49) TABLE-US-00003 42% Ebecryl 294/HD 25 (an aliphatic urethane triacrylate oligomer diluted with 1,6-hexanediol diacrylate (HDDA)(1) monomer.). 38% Ebecryl 5129 (a hexafunctional aliphatic urethane acrylate oligomer which provides fast cure response when exposed to ultraviolet light or electron beam.). 9% Ebecryl 8209 (a Sn-free aliphatic urethane acrylate oligomer which provides extremely fast cure response when exposed to ultraviolet (UV) light or electron beam (EB).). 5% HDDA/TMPTA (Hexanediol diacrylate (HDDA) is a difunctional reactive diluent that is commonly used as a component of ultraviolet light (UV) and electron beam (EB) curable coatings and inks. Trimethylolpropane triacrylate (TMPTA) is a trifunctional monomer used for its low volatility and fast cure response.) 2% Photoinitiator 2% Cerafak 127N (a Fischer Tropsch wax dispersion. Provides improved water repellence properties.). 1% TBPB (tert-Butyl peroxybenzoate (TBPB) a chemical compound from the group of peresters which functions as a radical initiator in a polymerization process. 1% Modaflow 9200 (an acrylic flow modifier, without silicone addition. It improves flow and leveling, substrate wetting, or maintains high gloss and substrate and inter-coat adhesion, and facilitates pigment dispersion).

(50) In addition to the curing facilitated by the application of the UV and/or electron beam radiation, the acrylate mixture of this embodiment requires a final thermal curing step to fully cure the coating layer 218c. As will be explained below, the decorative layer 218, with the UV-irradiated layer 218m thereon, is ultimately subjected to heat and pressure when the laminate lay-up is subjected to conventional high pressure laminate manufacturing through the application of pressure via press plates under traditional heating conditions. The need for the final heat curing results from the inclusion of peroxide in the acrylate mixture.

(51) As mentioned above, the laminate sheet assembly also includes a core layer 220. The core layer 220 is preferably a plurality of phenolic resin impregnated sheets 220a, 220b, 220c, although other materials may be used without departing from the spirit of the present invention. For example, the core layer 220 includes sheets of 120-323 grams per square meter dry phenolic resin impregnated Kraft paper. The Kraft paper is impregnated throughout and bonded with a substantially cured phenolic resin which has been converted to a thermoset state during the initial laminating step.

(52) With components of the laminate sheet assembly 212, including the decorative layer 218 and the core layer 220 as discussed above, and the finished release sheet 14 prepared (as discussed above with reference to the prior embodiments disclosed with reference to FIGS. 1 to 5), the finished release sheet 14 is positioned on the top surface 218a (in the case of the present laminate sheet assembly 212 it is positioned on the top surface 218a of the decorative layer 218, that is the UV-irradiated layer 218m) of the laminate sheet assembly 212 to form the laminate lay-up 210. The release sheet 14 is positioned on the exposed surface of the UV-irradiated layer 218m of the decorative layer 218 with the bottom side 14b (that is, the textured matte surface 14a) of the release sheet 14 facing the top surface 218a of the decorative layer 218.

(53) Heat and pressure are then applied to the laminate sheet assembly 212 and the textured release sheet 14 using press plates in a conventional manner. The heat and pressure are applied in manner sufficient to bond the layers of the decorative laminate sheet assembly 212, and releasably bond the textured release sheet 14 (in particular, the bottom side 14b with the textured matte surface 14a) to the top surface 218a of the decorative laminate sheet assembly 212. The heat and pressure also effectuate the final curing of the epoxy acrylic or urethane acrylic 216ea. Finally, the textured release sheet 14 is removed from the top layer 218a of the formed decorative laminate 300 to reveal a decorative laminate 300 exhibiting desired matte texture characteristics.

(54) In accordance with the present invention, and as discussed above, the release sheet 14 is formed with a textured matte surface 14a on the bottom side 14b thereof (the texture of which is ultimately applied to the top surface 218a of the decorative laminate 300) exhibiting matte surface characteristics leading to a fingerprint proof surface, that is, a surface not showing fingerprints and remaining clean and clear despite regular use. As discussed above, the release sheet 14 is preferably an acrylic coated polypropylene sheet, the acrylic coating of which is applied in accordance with the procedure disclosed in the '408 publication.

(55) The texture of the textured matte surface 14a applied to the release sheet 14 is ultimately applied to the top surface 218a of the resulting decorative laminate 300 as texture 218t resulting in a textured top surface 218a of the resulting decorative laminate 300) with a matte surface. When the textured matte surface 14a (that is, the texture) of the release sheet 14 is applied to the decorative laminate 300 as discussed below in greater detail, the top surface 218a of the decorative laminate 300 is imparted with a texture 218t (that is, the decorative laminate 300 is provided with a textured surface) the same as the texture of the textured matte surface 14a of the release sheet 14 making the laminate 300 less susceptible to the formation of annoying and undesirable fingerprints thereon. As such, the present invention provides a new product which offers a non-melamine formaldehyde surface.

(56) In accordance with the present invention, the decorative laminate 300 of the present invention is formed in much the same manner as conventional decorative laminates. The layers are first stacked and placed between steel plates with a release sheet 14 covering the decorative layer 218 as described above. The decorative laminate lay-up (or stack) 210 is then subjected to temperatures in the range of 121 C.-160 C. and pressures of about 56.24 kg/cm.sup.2 to 112.48 kg/cm.sup.2 for a time sufficient to consolidate the laminate and cure the resins (generally about 25 minutes to an hour).

(57) The pressure and heat force the resin in the paper sheets to flow, cure and consolidate the sheets into a unitary laminated mass referred to in the art as a decorative high pressure laminate 300 having the hydrophobic textured surface 218t. Generally, more than one decorative laminate is formed at one time. As shown with reference to FIG. 9, multiple decorative laminates are formed by inserting a plurality of lay-ups 210 in a stack. A standard release sheet 240 is positioned between the adjacent lay-ups 210 along their core layer sides. A platen press assembly, as is well known in the lamination art, provides the necessary heat and/or pressure during lamination. After consolidation, the release sheets allow the individual decorative laminates to be separated.

(58) While the preferred embodiments have been shown and described, it will be understood that there is no intent to limit the invention by such disclosure, but rather, it is intended to cover all modifications and alternate constructions falling within the spirit and scope of the invention.