THERMALLY CONDUCTIVE SILICONE RESIN COMPOSITION

Abstract

One of the objects of the present invention is to provide a thermally conductive silicone resin composition which has good thermal conductivity, a light weight (namely, a light weight per unit volume), and good reliability in high humidity, and a molded body thereof. The present invention provides a thermally conductive silicone resin composition comprising the following components (A) to (E): (A) an organopolysiloxane having at least two alkenyl groups each bonded to a silicon atom in an amount of 100 parts by mass, (B) an organohydrogen polysiloxane having at least two hydrogen atoms each bonded to a silicon atom in an amount such that a ratio of the number of the hydrogen atom bonded to a silicon atom relative to the number of the alkenyl group in component (A) is 0.1 to 2, (C) a thermally conductive filler in an amount of 2500 to 6000 parts by mass, (D) a catalytic amount of an addition reaction catalyst, and (E) an addition-reaction controlling agent in an amount of 0.01 to 1 part by mass, wherein the thermally conductive filler (C) comprises magnesium oxide having a specific surface area of 0.4 m.sup.2/g or less in an amount of 20 to 50 wt % and aluminum hydroxide in an amount of 10 to 30 wt %, relative to a total weight of component (C).

Claims

1. A thermally conductive silicone resin composition comprising the following components (A) to (E): (A) an organopolysiloxane having at least two alkenyl groups each bonded to a silicon atom in an amount of 100 parts by mass, (B) an organohydrogen polysiloxane having at least two hydrogen atoms each bonded to a silicon atom in an amount such that a ratio of the number of the hydrogen atom bonded to a silicon atom relative to the number of the alkenyl group in component (A) is 0.1 to 2, (C) a thermally conductive filler in an amount of 2500 to 6000 parts by mass, (D) a catalytic amount of an addition reaction catalyst, and (E) an addition-reaction controlling agent in an amount of 0.01 to 1 part by mass, wherein the thermally conductive filler (C) comprises magnesium oxide having a specific surface area of 0.4 m.sup.2/g or less in an amount of 20 to 50 wt % and aluminum hydroxide in an amount of 10 to 30 wt %, relative to a total weight of component (C).

2. The thermally conductive silicone resin composition according to claim 1, wherein the thermally conductive filler (C) comprises at least one selected from aluminum oxide, aluminum nitride, boron nitride, zinc oxide and magnesium hydroxide.

3. The thermally conductive silicone resin composition according to claim 2, wherein the thermally conductive filler (C) comprises 20 to 70 wt % of aluminum oxide having a volume average particle diameter of 1 to 90 μm, relative to the total weight of component (C).

4. The thermally conductive silicone resin composition according to claim 1, wherein the volume average particle diameter of the magnesium oxide is 50 to 120 μm.

5. The thermally conductive silicone resin composition according to claim 1, wherein the volume average particle diameter of the aluminum hydroxide is 1 to 50 μm.

6. The thermally conductive silicone resin composition according to claim 1, further comprising 100 to 300 parts by mass of (F) a dimethylpolysiloxane represented by the following formula (1) and having a trialkoxysilyl group at one end of the molecular chain: ##STR00008## wherein R5 is, independently of each other, an alkyl group having 1 to 6 carbon atoms and c is an integer of from 5 to 100.

7. The thermally conductive silicone resin composition according to claim 1, further comprising 1 to 40 parts by mass of (G) an organopolysiloxane represented by the following general formula (2):
R.sup.6—(SiR.sup.6.sub.2O).sub.dSiR.sup.6.sub.3  (2) wherein R6 is, independently of each other, a monovalent hydrocarbon group having 1 to 8 carbon atoms and no aliphatic unsaturated bond, and d is an integer of from 5 to 2000, and having a kinematic viscosity at 25° C. of 10 to 100,000 mm2/s.

8. The thermally conductive silicone resin composition according to claim 1, having a viscosity at 25° C. from 50 Pa.Math.s to 600 Pa.Math.s.

9. A cured product obtained by curing the thermally conductive silicone resin composition according to claim 1.

10. The cured product according to claim 9, having a specific gravity of 3.1 g/cm3 or less.

11. The cured product according to claim 9, having a thermal conductivity of 3.5 W/m-K or more.

12. The cured product according to claim 9, having an Asker C hardness of 60 or less.

13. A thermally conductive silicone heat-dissipating sheet comprising a PET film and the cured product according to claim 9.

14. The thermally conductive silicone resin composition according to claim 2, wherein the volume average particle diameter of the magnesium oxide is 50 to 120 μm.

15. The thermally conductive silicone resin composition according to claim 3, wherein the volume average particle diameter of the magnesium oxide is 50 to 120 μm.

16. The thermally conductive silicone resin composition according to claim 2, wherein the volume average particle diameter of the aluminum hydroxide is 1 to 50 μm.

17. The thermally conductive silicone resin composition according to claim 3, wherein the volume average particle diameter of the aluminum hydroxide is 1 to 50 μm.

18. The thermally conductive silicone resin composition according to claim 4, wherein the volume average particle diameter of the aluminum hydroxide is 1 to 50 μm.

19. The thermally conductive silicone resin composition according to claim 2, further comprising 100 to 300 parts by mass of (F) a dimethylpolysiloxane represented by the following formula (1) and having a trialkoxysilyl group at one end of the molecular chain: ##STR00009## wherein R5 is, independently of each other, an alkyl group having 1 to 6 carbon atoms and c is an integer of from 5 to 100.

20. The thermally conductive silicone resin composition according to claim 3, further comprising 100 to 300 parts by mass of (F) a dimethylpolysiloxane represented by the following formula (1) and having a trialkoxysilyl group at one end of the molecular chain: ##STR00010## wherein R5 is, independently of each other, an alkyl group having 1 to 6 carbon atoms and c is an integer of from 5 to 100.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0024] The present invention will be described below in further detail.

[Alkenyl Group Containing Organopolysiloxane]

[0025] An alkenyl group-containing organopolysiloxane (A) is an organopolysiloxane having at least two alkenyl groups each bonded to a silicon atom per molecule, and is the main agent of the composition of the present invention. Generally, the main chain consists of repeating diorganosiloxane units. The molecule may contain a branched structure in a part of the molecular structure, or the molecule may be circular. A linear diorganopolysiloxane is preferred in view of the physical properties such as the mechanical strength of the cured product.

[0026] Examples of a functional group other than an alkenyl group bonded to a silicon atom include an unsubstituted or substituted monovalent hydrocarbon group, for example, an alkyl group such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, isobutyl group, tert-butyl group, a pentyl group, a neopentyl group, a hexyl, a heptyl group, an octyl group, a nonyl group, a decyl group and a dodecyl group; a cycloalkyl group such as a cyclopentyl group, a cyclohexyl group and a cycloheptyl group; an aryl group such as a phenyl group, a tolyl group, a xylyl group, a naphthyl group and a biphenyl group; an aralkyl group such as a benzyl group, a phenylethyl group, a phenylpropyl group and a methylbenzyl group; and those hydrocarbon groups wherein a part or all of the hydrogen atoms bonded to a carbon atom of these groups is substituted with a halogen atom such as a fluorine atom, a chlorine atom, or a bromine atom, or a cyano group, including, for example, a chloromethyl group, a 2-bromoethyl group, a 3-chloropropyl group, a 3,3,3-trifluoropropyl group, a chlorophenyl group, a fluorophenyl group, a cyanoethyl group and a 3,3,4,4,5,5,6,6,6-nonafluorohexyl group. Typical examples are hydrocarbons with 1 to 10 carbon atoms and, in particular, typical examples are hydrocarbons with 1 to 6 carbon atoms. An unsubstituted or substituted alkyl group having 1 to 3 carbon atoms such as a methyl group, an ethyl group, a propyl group, a chloromethyl group, a bromoethyl group, a 3,3,3-trifluoropropyl group and a cyanoethyl group, and an unsubstituted or substituted phenyl group such as a phenyl group, a chlorophenyl group and a fluorophenyl group are preferable. The functional groups other than the alkenyl group bonded to a silicon atom are not limited to being the same.

[0027] Examples of the alkenyl group include hydrocarbons with 2 to 8 carbon atoms such as a vinyl group, an allyl group, a propenyl group, an isopropenyl group, a butenyl group, a hexenyl group and a cyclohexenyl group. Among them, a low-molecular-weight alkenyl group such as a vinyl group and an allyl group is preferable, and a vinyl group is particularly preferable.

[0028] The organopolysiloxane may have a kinematic viscosity at 25° C. of 10 to 100,000 mm.sup.2/s, preferably have a kinematic viscosity in the range of 500 to 50,000 mm.sup.2/s. If the viscosity is too low, the storage stability of the composition obtained becomes poor. If the viscosity is too high, the extensibility of the composition obtained may become poor. In the present invention, the kinematic viscosity is the value determined by an Ostwald Viscometer.

[0029] The organopolysiloxane (A) may be either alone, or organopolysiloxanes having different viscosities may be used in combination.

[Organohydrogenpolysiloxane]

[0030] Component (B) is an organohydrogenpolysiloxane which has an average of 2 or more, preferably 2 to 100 hydrogen atoms directly bonded to a silicon atom (SiH) per molecule and functions as a cross-linking agent of component (A). The SiH in component (B) and the alkenyl group in component (A) are subjected to a hydrosilylation reaction in the presence of (D) a platinum group catalyst, which will be described later in detail, to provide a three-dimensional network structure having a crosslinked structure. If the number of the SiH group is less than 1 on average, there is the risk that the composition may not cure.

[0031] An example of the average structural formula of the organohydrogen polysiloxane is represented as follows.

##STR00001##

wherein R.sup.7 is, independently of each other, an unsubstituted or a substituted monovalent hydrocarbon group having no aliphatic unsaturated bond or a hydrogen atom, and at least two of R.sup.7 are hydrogen atoms, and n is an integer of 1 or more.

[0032] In formula (3), examples of an unsubstituted or substituted monovalent hydrocarbon group represented by R.sup.7 having no aliphatic unsaturated bond preferably include a hydrocarbon group having 1 to 10 carbon atoms, and particularly preferably 1 to 6 carbon atoms. Examples of the hydrocarbon group include an alkyl group such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a tert-butyl group, a pentyl group, a neopentyl group, a hexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group and a dodecyl group; a cycloalkyl group such as a cyclopentyl group, a cyclohexyl group and a cycloheptyl group; an aryl group such as a phenyl group, a tolyl group, a xylyl group, a naphthyl group and a biphenyl group; an aralkyl group such as a benzyl group, a phenylethyl group, a phenylpropyl group and a methylbenzyl group; and those hydrocarbon groups wherein a part or all of the hydrogen atoms bonded to a carbon atom of these groups is substituted with a halogen atom such as a fluorine atom, a chlorine atom, or a bromine atom, or a cyano group; including, for example, a chloromethyl group, a 2-bromoethyl group, a 3-chloropropyl group, a 3,3,3-trifluoropropyl group, a chlorophenyl group, a fluorophenyl group, a cyanoethyl group and a 3,3,4,4,5,5,6,6,6-nonafluorohexyl group. A substituted or unsubstituted alkyl group having 1 to 3 carbon atoms such as a methyl group, an ethyl group, a propyl group, a chloromethyl group, a bromoethyl group, a 3,3,3-trifluoropropyl group and cyanoethyl group, and an unsubstituted or substituted phenyl group such as a phenyl group, a chlorophenyl group and a fluorophenyl group are preferable. The groups represented by R.sup.7 are not limited to being the same.

[0033] The amount of component (B) is an amount that the ratio of the number of SiH groups in component (B) relative to the number of alkenyl groups in component (A) is 0.1 to 2, preferably 0.3 to 1.5 mol, and more preferably 0.5 to 1. If the amount of component (B) is less than the aforementioned lower limit, there is the risk that the composition may not cure, or the strength of the cured product may be insufficient and the shape cannot be maintained as a molded body and handled. If the amount of component (B) is excess the aforementioned upper limit, the flexibility of the cured product may be lost, and thermal resistance increases significantly, which are not preferable.

[Thermally Conductive Filler]

[0034] Component (C) is a thermally conductive filler. The present invention is characterized in that the composition has a specific blending ratio of magnesium oxide having a specific surface area and aluminum hydroxide as the thermally conductive filler (C). The amount of the thermally conductive filler (C) in the silicone resin composition of the present invention is 2500 to 6000 parts by mass, preferably 3500 to 6000 parts by mass, relative to 100 parts by mass of component (A). If the amount of the thermally conductive filler is less than the aforementioned lower limit, the thermal conductivity of the silicone resin composition obtained may be lost, and a storage stability of the composition may be poor. If the amount is in excess of the aforementioned upper limit, there is the risk that the strength of the cured product of the thermally conductive silicone composition decreases, and the cured product may become difficult to handle which is not preferable.

[0035] The ratio of magnesium oxide and aluminum hydroxide, as the thermally conductive filler, is such that the amount of the magnesium oxide having a specific surface area of 0.4 m.sup.2/g or less is 20 to 50 wt % relative to the total weight of component (C) and the amount of aluminum hydroxide is 10 to 30 wt % relative to the total weight of component (C).

[0036] The amount of magnesium oxide is preferably 23 to 45 wt %, and more preferably 25 to 40 wt %. If the amount of magnesium oxide is less than the aforementioned lower limit, the thermally conductivity of the cured product decreases, the intended specific gravity cannot be obtained, and a light weight product is difficult to be provided. If the amount of magnesium oxide is in excess of the aforementioned upper limit, the viscosity of the thermally conductive silicone resin composition increases and the moldability of the cured product becomes poor.

[0037] Magnesium oxide is characterized as having a specific surface area of 0.4 m.sup.2/g or less. The specific surface area is preferably 0.3 m.sup.2/g or less, more preferably 0.2 to 0.01 m.sup.2/g, and even more preferably 0.1 to 0.01 m.sup.2/g. If the specific surface area of magnesium oxide is greater than the aforementioned upper limit, moisture absorption is likely to occur in high humidity, and the conversion from magnesium oxide to magnesium hydroxide is promoted and, therefore, the reliability of the silicone resin cured product (which will be described later in detail) decreases significantly in high humidity. Note that, in the present invention, the specific surface area may be determined by a gas adsorption method, for example, determined by an automated specific surface area analyzer, ex Shimadzu Corporation.

[0038] The volume average particle diameter of magnesium oxide is preferably 30 to 120 μm, and more preferably 50 to 90 μm. Here, the volume average particle diameter indicates the diameter at which the large side and the small side are equivalent when divided in two with the average particle size as a boundary, when the volumetric distribution of the particles was determined by Microtrac (laser diffraction scattering method). Note that, all of the average particle sizes described in the following text are defined by this.

[0039] The amount of aluminum hydroxide is 10 to 30 wt %, preferably 13 to 29 wt %, and more preferably 15 to 25 wt %, relative to the total weight of component (C) as described above. If the amount of the aluminum hydroxide is less than the aforementioned lower limit, it is difficult to contribute a weight reduction to the thermally conductive silicone resin composition. If the amount is in excess of the aforementioned upper limit, the thermal conductivity of the thermally conductive silicone resin composition tends to decrease which is not preferable.

[0040] The volume average particle diameter of the aluminum hydroxide is preferably 2 to 50 μm, and more preferably 5 to 20 μm. The measurement method of the volume average particle diameter is as described above. The specific surface area of the aluminum hydroxide is not particularly limited, and is typically 0.1 to 5 m.sup.2/g.

[0041] The thermally conductive silicone resin composition of the present invention may further comprise a thermally conductive filler as component (C) other than magnesium oxide and aluminum hydroxide. A conventionally known thermally conductive filler may be used as the other thermally conductive filler. For example, at least one selected from aluminum oxide, aluminum nitride, boron nitride, zinc oxide, and magnesium hydroxide is preferable. When a thermal conductivity, an electrical insulation and costs are considered comprehensively, aluminum oxide is particularly preferable. The volume average particle diameter of the aluminum oxide is preferably 1 to 90 μm, and more preferably 10 to 70 μm. One type or combinations of thermally conductive fillers having different volume average particle diameters may be used. The amount of thermally conductive filler other than magnesium oxide and aluminum hydroxide should be a residual amount by which the total weight of the thermally conductive filler is 100 wt %. For example, the amount of aluminum oxide is preferably 20 to 70 wt %, and more preferably 30 to 50 wt %.

[0042] In the present invention, magnesium oxide having a low Mohs hardness is used together with aluminum hydroxide and, therefore, wear to the reaction kettle is less likely to occur, compared to a composition comprising aluminum oxide alone as the thermally conductive filler. When the reaction kettle was made of a metal such as aluminum, the contamination of the conductive components with respect to the insulator may occur.

[Addition-Reaction Catalyst]

[0043] Component (D) is an addition-reaction catalyst, and promotes the addition-reaction of the alkenyl group of component (A) with an SiH group of component (B). The catalyst may be a well-known catalyst based on a platinum group metal which is used in a hydrosilylation reaction. Examples of the catalyst include elemental platinum group metals such as platinum (including platinum black), rhodium, and palladium; platinum chlorides such as H.sub.2PtCl.sub.4.Math.nH.sub.2O, H.sub.2PtCl.sub.6.Math.nH.sub.2O, Na.sub.2PtCl.sub.6.Math.nH.sub.2O, KaHPtC.sub.6.Math.nH.sub.2O, Na.sub.2PtCl.sub.6.Math.nH.sub.2O, K.sub.2PtCl.sub.4.Math.nH.sub.2O, PtCl.sub.4.Math.nH.sub.2O, PtCl.sub.2, Na.sub.2HPtCl.sub.4.Math.nH.sub.2O, provided that, in the aforesaid formulas, n is an integer of from 0 to 6, and is preferably 0 or 6, chloroplatinic acid and chloroplatinic salts, alcohol-modified chloroplatinic acid (refer to U.S. Pat. No. 3,220,972), complexes of chloroplatinic acid with olefins (refer to U.S. Pat. Nos. 3,159,601, 3,159,662, and 3,775,452), platinum group metals such as platinum black and palladium supported on carriers such as alumina, silica and carbon; rhodium-olefin complexes; chlorotris(triphenylphosphine)rhodium (known as Wilkinson catalyst); and platinum chloride, chloroplatinic acid or chloroplatinic salts with vinyl-containing siloxanes, particularly complexes of vinyl-containing cyclic siloxanes. The amount of component (D) may be a catalytic amount, that is, an effective amount for promoting the addition-reaction. Typically, the amount of the catalyst may be such that a volume of a platinum group metal element is in the range of 0.1 to 1000 ppm, relative to component (A).

[Addition-Reaction Controlling Agent]

[0044] The silicone composition of the present invention comprises (E) an addition-reaction controlling agent. Component (E) may be a well-known addition-reaction controlling agent used in an addition-reaction curable silicone composition, and is not particularly limited. Examples of the addition-reaction controlling agent include acetylene compounds such as 1-ethynyl-1-hexanol and 3-butin-1-ol; various nitrogen compounds, organic phosphorus compounds, oxime compounds, and organic chloro compounds. The amount of component (E) may be an effective amount which controls the addition-reaction. The amount may be 0.01 to 1 part by mass, more preferably 0.05 to 0.5 part by mass, relative to 100 parts by mass of component (A).

[Surface Treatment Agent]

[0045] The silicone resin composition of the present invention may further contain a surface treatment agent (F). In preparing the composition, component (F) functions to uniformly disperse the thermally conductive filler (C) in a matrix consisting of the organopolysiloxane (A). A dimethylpolysiloxane which is represented by the following general formula (1) in which one end of the molecular chain is blocked by a trialkoxy group is preferable as the surface treatment agent (F):

##STR00002##

wherein R.sup.5 is, independently of each other, an alkyl group having 1 to 6 carbon atoms, and c is an integer of from 5 to 100.

[0046] The amount of component (F) in the composition is 100 to 300 parts by mass, preferably 150 to 250 parts by mass, relative to 100 parts by mass of component (A). On account of the amount within the range, a thermally conductive filler may be uniformly dispersed in the matrix consisting of the organosiloxane. If the amount of component (F) relative to component (A) is too large, oil separation may be induced which is not preferable. If the amount of component (F) is too small, the wettability of the polyorganosiloxane and the thermally conductive filler decreases, and there is the risk that the composition cannot be formed.

[Plasticizer]

[0047] The composition of the present invention may further comprise, as a plasticizer, (G) an organopolysiloxane which is represented by the following general formula (2):

R.sup.6—(SiR.sup.6.sub.2O).sub.dSiR.sup.6.sub.3  (2)

wherein R.sup.6 is, independently of each other, a monovalent hydrocarbon group having 1 to 8 carbon atoms and no aliphatic unsaturated bond, and d is an integer of from 5 to 2000. The organopolysiloxane (G) has a kinematic viscosity at 25° C. of 10 to 100,000 mm.sup.2/s. The component may be appropriately used to impart properties such as a viscosity modifier of the thermally conductive composition, and is not particularly limited. The component may be used singly, or combinations thereof may be used together.

[0048] The aforementioned R.sup.6 is, independently of each other, a monovalent hydrocarbon group having 1 to 8 carbon atoms and no aliphatic unsaturated bond. Examples of R.sup.6 include an alkyl group such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a tert-butyl group, a pentyl group, a neopentyl group, a hexyl group, a heptyl group, and an octyl group; a cycloalkyl group such as a cyclopentyl, a cyclohexyl and a cycloheptyl group; an aryl group such as a phenyl group, a tolyl group and a xylyl group; an aralkyl group such as a benzyl group, a phenylethyl group, a phenylpropyl group and a methylbenzyl group; and those hydrocarbon groups wherein a part or all of the hydrogen atoms bonded to a carbon atom of these groups is substituted with a halogen atom such as a fluorine atom, a chlorine atom, or a bromine atom, or a cyano group; including, for example, a chloromethyl group, a 2-bromoethyl group, a 3-chloropropyl group, a 3,3,3-trifluoropropyl group, a chlorophenyl group, a fluorophenyl group, a cyanoethyl group and a 3,3,4,4,5,5,6,6,6-nonafluorohexyl group. Typical examples are a monovalent hydrocarbon group with 1 to 10 carbon atoms, and, in particular, typical examples are a monovalent hydrocarbon group with 1 to 6 carbon atoms. An unsubstituted or substituted alkyl group having 1 to 3 carbon atoms such as a methyl group, an ethyl group, a propyl group, a chloromethyl group, a bromoethyl group, a 3,3,3-trifluoropropyl group and a cyanoethyl group, and an unsubstituted or substituted phenyl group such as a phenyl group, a chlorophenyl group and a fluorophenyl group are preferable. A methyl group and a phenyl group are particularly preferable.

[0049] The kinematic viscosity of the organopolysiloxane at 25° C. is preferably 10 to 100,000 mm.sup.2/s, further preferably 100 to 10,000 mm.sup.2/s. If the kinematic viscosity is lower than 10 mm.sup.2/s, a cured product obtained from the composition is likely to cause oil bleeding. If the kinematic viscosity is larger than 100,000 mm.sup.2/s, there is the risk that flexibility of the thermally conductive composition obtained may be poor.

[0050] In the formula (2), d may be a value such that the kinematic viscosity of the organopolysiloxane is in the aforementioned range. “d” is preferably an integer of from 5 to 2000, and more preferably an integer of from 10 to 1000.

[0051] The amount of component (G) in the composition of the present invention is not particularly limited, as long as the desired effect as a plasticizer may be obtained. Generally, the amount is preferably 1 to 40 parts by mass, more preferably 5 to 20 parts by mass, relative to 100 parts by mass of component (A). When the amount of component (G) is in the aforementioned range, it is easy to maintain a good flowability and workability in the thermally conductive composition prior to curing, and it is easy to fill the thermally conductive filler (C) in the composition.

[Viscosity of the Composition]

[0052] The resin composition of the present invention has a viscosity at 25° C. of 600 Pa.Math.s or less in an uncured state, preferably 500 Pa.Math.s or less, and even more preferably 400 Pa.Math.s or less. The lower limit of the viscosity is not particularly limited, but is 50 Pa.Math.s or more, preferably 75 Pa.Math.s or more, and in particular 100 Pa.Math.s or more. The viscosity is determined at 25° C. using a rotational rheometer viscometer.

[0053] The curing method of the thermally conductive silicone resin composition of the present invention is not particularly limited, and may be similar to the curing conditions of a well-known addition-reaction curable silicone rubber composition. For example, curing may be sufficiently conducted at room temperature, and may be conducted with heating if need. The additional curing is preferably conducted at 120° C. for 10 minutes. The cured product (molded body) which is obtained from the composition of the present invention has an excellent thermal conductivity. The molding method of the composition is not particularly limited. Depending on the molding method, a cross-linking reaction may be promoted in the vicinity of the surface so that the molded product may be handled sufficiently, and the internal crosslink density may be decreased to thereby obtain a good compressibility and low thermal resistance. Since the inside is cross-linked, a thermally conductive silicone molded product with oil bleed resistance is produced.

[Method of Preparing the Silicone Thermally Conductive Molded Product]

[0054] The thermally conductive silicone resin composition of the present invention is applied on a substrate such as a resin film and cured to obtain a silicone thermally conductive molded product. The resin film may be a film having a thermal deformation temperature of 100° C. or more which may tolerate a heat treatment after bonding, for example, may be properly selected from a film made of PET or PBT polycarbonate. A post-measurement type blade coater, a gravure coater, a kiss-roll coater, or a spray coater may be used as a coating device for applying the organohydrogen polysiloxane oil to the resin film at a uniform thickness.

[Thermal Conductivity of the Molding]

[0055] The thermal conductivity of the cured product (molded body) in the present invention has a value at 25° C., determined by the hot-disk method, of desirably 3.5 W/m.Math.K or more, preferably 4.0 W/m.Math.K or more, and more preferably 4.5 W/m, K or more. If the thermal conductivity is less than 3.5 W/m.Math.K, it is difficult to apply the cured product to a heat generating body which generated a large amount of heat and requires high heat dissipation, and the practical range of the molded body is narrowed. The upper limit is not limited, and generally is 15 W/m.Math.K or less, and particularly 10 W/m.Math.K or less. The cured product of the present invention may have a specific gravity of 3.1 g/cm.sup.3 or less, preferably 3.0 g/cm.sup.3 or less, and particularly 2.6 to 3.0 g/cm.sup.3, and has a light weight.

EXAMPLES

[0056] The present invention will be explained below in further detail with reference to a series of the Examples and the Comparative Examples, though the present invention is in no way limited by these Examples.

[0057] Components (A) to (G) used in the following Examples and Comparative Examples are as follows.

Component (A):

[0058] (A-1) organopolysiloxane represented by the following formula (4) and having a kinematic viscosity of 400 mm.sup.2/s.
(A-2) organopolysiloxane represented by the following formula (4) and having a kinematic viscosity of 5000 mm.sup.2/s.

##STR00003##

wherein, X is a vinyl group, and n is the number such that the organopolysiloxane has the aforesaid viscosity.
Component (B): organohydrogen polysiloxane represented by the following formula.

##STR00004##

[0059] Average degree of polymerization: o=28, p=2

Component (C):

[0060] (C-1) Aluminum oxide having an average particle size of 1 μm

[0061] (C-2) Aluminum oxide having an average particle size of 10 μm

[0062] (C-3) Aluminum hydroxide having an average particle size of 8 μm

[0063] (C-4) Aluminum oxide having an average particle size of 70 μm

[0064] (C-5) Magnesium oxide having an average particle size of 60 μm and a BET of 0.05 m.sup.2/g

[0065] (C-6) Magnesium oxide having an average particle size of 60 μm and a BET of 0.2 m.sup.2/g

[0066] (C-7) Magnesium oxide having an average particle size of 80 μm and a BET of 0.5 m.sup.2/g

Component (D): 5% solution of 2-ethylhexanol chloroplatinic acid (addition-reaction catalyst)
Component (E): ethynyl methylidene carbinol (addition-reaction controlling agent)
Component (F): dimethylpolysiloxane represented by the following formula and in which one end was blocked by a trimethoxysilyl group.

##STR00005##

Component (G): dimethylpolysiloxane represented by the following formula (plasticizer).

##STR00006##

Examples 1 to 6 and Comparative Examples 1 to 6

[0067] The amounts of the aforementioned components (A) to (G) are as described in the following Tables 1 and 2.

[0068] The components (A), (C), (F) and (G) were mixed for 60 minutes with a planetary mixer to which component (D) and component (E) were added and an effective amount (5 parts) of an internal releasing agent (represented by the following formula (a)) was further added, and further mixed for 60 minutes. The internal releasing agent functions to promote leaving off a cured product from a separator. Component (B) was added to the mixture, and mixed for 30 minutes to obtain a thermally conductive silicone resin composition. The ratio of the number of the hydrogen atoms bonded to the silicon atom in component (B) relative to the number of alkenyl groups in component (A), SiH/SiVi, was 1.1.

[0069] The internal releasing agent is described below.

##STR00007##

The viscosity (Pa.Math.s) at 25° C. of each thermally conductive silicone resin composition was determined with a rotational rheometer viscometer.
The results are shown in Tables 3 and 4.

[0070] The thermally conductive silicone resin composition obtained was placed between two PET films and, then, cured with a press at 120° C. for 10 minutes to obtain a thermally conductive silicone molded body having a thickness of 6 mm. The thermal conductivity and the specific gravity were determined for the obtained molded body according to the following methods. The hardness of the molded body before and after aging at 85° C. and 85% Rh for 1000 hours were determined and compared them so as to evaluate the reliability of the molded product. The results are shown in Tables 3 and 4.

[Evaluation]

[0071] (1) Moldability: When the thermally conductive silicone resin composition was molded, the composition which could be easily completed to pour into the mold evaluated as “Good”. The thermally conductive silicone resin composition whose viscosity was too high and handling was difficult and which was difficulty completed to pour into the mold was evaluated as “Poor”.
(2) Thermal conductivity: A thermal conductivity of two of the molded body having a thickness of 6 mm obtained as described above were determined by a thermal conductivity meter (TPA-501, product name, ex Kyoto Electronics Manufacturing Co., Ltd.).
(3) Specific gravity: The specific gravity was determined by the underwater substitution method.
(4) Reliability under a high humidity: The initial hardness of the molded body was determined by an Asker C Durometer. Then, the molded body was aged for 1000 hours in the conditions of 85° C. and 85% RH and, then, the hardness of the molded body was determined again. The results are shown in Table 1. If the degree of change was 30 or more, cracking of the silicone highly occurs and the reliability is poor.

TABLE-US-00001 TABLE 1 Example 1 2 3 4 5 6 7 Composition, (A) Alkenyl group-containing organosiloxane 100 100 100 100 100 100 100 part by (B) Organohydrogensiloxane 14 14 14 14 14 14 14 mass (C) C1: Aluminum oxide 1420 700 600 1500 1500 900 1250 Thermally C2: Aluminum oxide 600 300 300 600 600 500 650 conductive C3: Aluminum hydroxide 880 540 810 830 1000 1100 800 filler C4: Aluminum oxide 800 1200 700 570 1000 900 800 C5: Magnesium oxide, BET 0.05 m.sup.2/g 1400 900 900 2000 1500 1900 C6: Magnesium oxide, BET 0.2 m.sup.2/g 1350 Total parts by mass of component C 5100 3640 3310 5500 5600 5300 4850 Proportion of aluminum hydroxide, % 17 15 24 15 18 21 16 Proportion of magnesium oxide, % 27 25 27 36 27 36 28 (D) Addition-reaction catalyst 0.5 0.5 0.5 0.5 0.5 0.5 0.5 (E) Addition-reaction controlling agent 0.2 0.2 0.2 0.2 0.2 0.2 0.2 (F) Surface treatment agent 200 200 200 200 200 200 200 (G) Plasticizer 10 10 10 10 10 10 10

TABLE-US-00002 TABLE 2 Comparative Example 1 2 3 4 5 6 Composition, (A) Alkenyl group-containing organosiloxane 100 100 100 100 100 100 part by (B) Organohydrogensiloxane 14 14 14 14 14 14 mass (C) C1: Aluminum oxide 500 1420 500 1800 1500 600 Thermally C2: Aluminum oxide 300 600 200 900 600 250 conductive C3: Aluminum hydroxide 450 880 1300 200 800 880 fille C4: Aluminum oxide 400 800 700 700 2000 550 C5: Magnesium oxide, BET 0.05 m.sup.2/g 600 900 1500 700 2800 C7: Magnesium oxide, BET 0.5 m.sup.2/g 1250 Total parts by mass of component C 2250 4950 3600 5100 5600 5080 Proportion of aluminum hydroxide, % 20 18 36 4 14 17 Proportion of magnesium oxide, % 27 25 25 29 13 55 (D) Addition-reaction catalyst 0.5 0.5 0.5 0.5 0.5 0.5 (E) Addition-reaction controlling agent 0.2 0.2 0.2 0.2 0.2 0.2 (F) Surface treatment agent 200 200 200 200 200 200 (G) Plasticizer 10 10 10 10 10 10

TABLE-US-00003 TABLE 3 Example 1 2 3 4 5 6 7 Evaluation Viscosity (Pa .Math. s) of composition @ 25° C. 168 124 105 237 208 242 237 Moldability of composition Good Good Good Good Good Good Good Thermal conductivity, W/m .Math. K 5.2 4.0 3.6 5.9 5.6 5.1 5.6 Specific gravity, g/cm.sup.3 2.9 2.9 2.8 3 3 2.8 2.9 Hardness (Initial) 19 15 14 23 22 21 24 Hardness after aging 85° C. 35 30 27 39 40 37 46 and 85% Rh for 1000 hours Degree of hardness increase 16 15 13 16 18 16 23

TABLE-US-00004 TABLE 4 Comparative Example 1 2 3 4 5 6 Evaluation Viscosity (Pa .Math. s) of composition @ 25° C. 128 242 154 132 175 302 Moldability of composition Good Good Good Good Good Poor Thermal conductivity, W/m .Math. K 2.9 5.1 3.1 5.3 5.2 — Specific gravity, g/cm.sup.3 2.7 2.9 2.7 3.2 3.2 — Hardness (Initial) 16 18 16 17 20 — Hardness after aging 85° C. 30 58 30 35 32 — and 85% Rh for 1000 hours Degree of hardness increase 14 40 14 18 12 —

[0072] As described in the Tables 3 and 4, the composition of Comparative Example 1 has a total amount of the thermally conductive filler (C) of less than 2500 parts by mass. The thermal conductivity of the molded product obtained from the composition was below 3.5 W. The molding cannot be applied to parts having a high calorific value.

[0073] The composition of Comparative Example 2 comprises the magnesium oxide having a specific surface area of greater than 0.4 m.sup.2/g. The hardness of the molded product obtained from the composition greatly increased after aging at high temperatures and high humidity, and the reliability was poor.

[0074] The composition of Comparative Example 3 has a proportion of aluminum hydroxide greater than 30 wt %. The molded body obtained had a thermal conductivity of lower than 3.5 W/m.Math.K. In particular, on account of the comparison with the composition of Example 3 in which components other than the proportion of aluminum hydroxide are the same, it can be confirmed that when the proportion of aluminum hydroxide is high, the thermal conductivity decreases.

[0075] The composition of Comparative Example 4 has a proportion of aluminum hydroxide less than 10 wt %. The specific gravity of the molded body obtained highly increased and exceeded 3.1 g/cm.sup.3. In particular, on account of the comparison with the composition of Example 1 in which components other than the proportion of aluminum hydroxide are the same, it can be confirmed that when the proportion of aluminum hydroxide is low, the specific gravity highly increases.

[0076] The composition of Comparative Example 5 has a proportion of magnesium oxide less than 20 wt %. The molded body which may be obtained had a large increase in the specific gravity and exceeded 3.1 g/cm.sup.3. In particular, on account of the comparison with the composition of Example 5 in which components other than the proportion of magnesium oxide are the same, it can be confirmed that if the proportion of magnesium oxide is low, the increase in the specific gravity becomes large.

[0077] The composition of Comparative Example 6 has a proportion of magnesium oxide of greater than 50 wt %. The thermally conductive silicone resin composition had a remarkably high viscosity and was difficult to mold and provide a cured product.

[0078] In contrast, as shown in Tables 1 and 2, the thermally conductive silicone resin composition of the present invention has a good handling property, and the moldability was good. All of the obtained molded bodies had good thermally conductivity, a light weight with a specific gravity of 3.1 g/cm.sup.3 or less, a thermal conductivity of 3.5 W/m K or more and the thermally conductivity was good. The molded body was excellent in reliability without a remarkable increase in the hardness even after a high humidity test.

INDUSTRIAL APPLICABILITY

[0079] The thermally conductive silicone resin composition of the present invention provides a thermally conductive silicone molded body which has a good thermal conductivity, has light weight (the specific gravity is light), and furthermore, has excellent reliability in high humidity. The resin composition is suitable as a heat transfer material which is used to cool electronic components with heat conduction. For example, the resin composition is suitable as a thermally conductive resin compound and a thermally conductive resin molded body which are arranged between a heat dissipating component and a heat dissipating part in an electronic device and used for heat dissipation.