SELF-BONDING FLUOROPOLYMERS AND METHODS OF PRODUCING THE SAME
20210002394 ยท 2021-01-07
Assignee
Inventors
Cpc classification
B32B27/322
PERFORMING OPERATIONS; TRANSPORTING
B29K2027/18
PERFORMING OPERATIONS; TRANSPORTING
B29C65/02
PERFORMING OPERATIONS; TRANSPORTING
B32B2553/00
PERFORMING OPERATIONS; TRANSPORTING
Y10T428/139
GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
B32B3/04
PERFORMING OPERATIONS; TRANSPORTING
Y10T428/31544
GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
C08J2327/18
CHEMISTRY; METALLURGY
B29K2027/18
PERFORMING OPERATIONS; TRANSPORTING
B32B27/06
PERFORMING OPERATIONS; TRANSPORTING
B29C66/14
PERFORMING OPERATIONS; TRANSPORTING
B32B2535/00
PERFORMING OPERATIONS; TRANSPORTING
B29C66/1122
PERFORMING OPERATIONS; TRANSPORTING
B29C66/1162
PERFORMING OPERATIONS; TRANSPORTING
B29C66/43
PERFORMING OPERATIONS; TRANSPORTING
B29C66/71
PERFORMING OPERATIONS; TRANSPORTING
B29C66/71
PERFORMING OPERATIONS; TRANSPORTING
B32B7/02
PERFORMING OPERATIONS; TRANSPORTING
B29C65/8253
PERFORMING OPERATIONS; TRANSPORTING
Y10T428/1352
GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
B29C66/4322
PERFORMING OPERATIONS; TRANSPORTING
B29C66/45
PERFORMING OPERATIONS; TRANSPORTING
Y10T428/192
GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
B29C66/73921
PERFORMING OPERATIONS; TRANSPORTING
Y10T428/24752
GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
International classification
B29C65/00
PERFORMING OPERATIONS; TRANSPORTING
B29C65/02
PERFORMING OPERATIONS; TRANSPORTING
B32B27/06
PERFORMING OPERATIONS; TRANSPORTING
B32B3/04
PERFORMING OPERATIONS; TRANSPORTING
B32B7/02
PERFORMING OPERATIONS; TRANSPORTING
Abstract
A method of making expanded fluoropolymer articles thermally bonds portions of expanded fluoropolymers together, without using an adhesive or crushing force, to produce stronger bonds at the joint between the expanded fluoropolymers than the bonds within the constituent expanded fluoropolymers. The method involves placing the portions of expanded fluoropolymers to be thermally bonded together in intimate contact with each other after wet-stretching the expanded fluoropolymers, and removing the wetting agent used to wet-stretch the expanded fluoropolymers, without subsequent expansion or stretching, to yield an expanded fluoropolymer article exhibiting unexpected and superior properties that can be used in a variety of medical and industrial applications.
Claims
1. An expanded fluoropolymer thermally bonded to itself without an adhesive.
2. The fluoropolymer of claim 1, wherein the expanded fluoropolymer comprises PTFE.
3. The fluoropolymer of claim 1, wherein the expanded fluoropolymer is non-porous.
4. The fluoropolymer of claim 1, wherein at least two portions of the fluoropolymer are bonded together without the adhesive to form bonds that have an x-direction tensile strength that is greater than the x-direction tensile strength of the fluoropolymer itself.
5. The fluoropolymer of claim 4, wherein the bonds comprise a combination of bonds.
6. The fluoropolymer of claim 5, wherein the combination of bonds is selected from the group consisting of covalent bonds, van der Walls forces, hydrogen bonds, ionic bonds, electrostatic interactions and changes created in the chain entanglement of the expanded fluoropolymer.
7. The fluoropolymer of claim 5, wherein the combination of bonds comprises covalent bonds.
8. The fluoropolymer of claim 5, wherein the combination of bonds comprises van der Walls forces.
9. The fluoropolymer of claim 5, wherein the combination of bonds comprises hydrogen bonds.
10. The fluoropolymer of claim 5, wherein the combination of bonds comprises ionic bonds.
11. The fluoropolymer of claim 5, wherein the combination of bonds comprises electrostatic interactions.
12. The fluoropolymer of claim 5, wherein the combination of bonds comprises changes created in the chain entanglement of the expanded fluoropolymer.
13. The fluoropolymer of claim 1, wherein the fluoropolymer is shaped to form a sheet, a film, a tube, a balloon, or a 3-d shape.
14-39. have been cancelled.
40. A method of making an expanded fluoropolymer article thermally bonded to itself without an adhesive, comprising: providing a wet stretched fluoropolymer article by stretching a wetted expandable fluoropolymer article while wet with a wet stretch wetting agent; placing two portions of the wet stretched fluoropolymer article in intimate contact with each other while wet with the wet stretch wetting agent; and while the two portions of the wet stretched fluoropolymer article are in intimate contact with each other, removing at least the wet stretch wetting agent from at least the two portions of the wet stretched fluoropolymer article in intimate contact; and subsequent to or simultaneous with removing at least the wet stretch wetting agent from at least the two portions of the wet stretched fluoropolymer article, heating at least the two portions of the wet stretched fluoropolymer article while in intimate contact with each other.
41-107. have been cancelled.
108. An expanded fluoropolymer material having a bond strength at the joint greater than the bond strength of the expanded fluoropolymer material itself when at least a portion of the expanded fluoropolymer is sintered to itself in a joined configuration, the expanded fluoropolymer material produced by a process comprising: a) stretching a wetted fluoropolymer material to form a wet-stretched fluoropolymer material; b) removing a wetting agent from the wet-stretched fluoropolymer material while portions of the wet-stretched fluoropolymer material are in intimate contact with each other after stretching the wetted fluoropolymer material; and c) sintering the at least the portion of the expanded fluoropolymer material to itself to in the joined configuration to yield the wet-stretched fluoropolymer material having the bond strength at the joint greater than the bond strength of the material itself.
109-118. have been cancelled.
Description
BRIEF DESCRIPTION OF THE FIGURES
[0031] These and other characteristics of the present invention will be more fully understood by reference to the following detailed description in conjunction with the attached drawings, in which:
[0032]
[0033]
[0034]
[0035]
[0036]
[0037]
[0038]
[0039]
[0040]
[0041]
[0042]
[0043]
[0044]
[0045]
[0046]
[0047]
[0048]
[0049]
[0050]
[0051]
[0052]
[0053]
[0054]
[0055]
[0056]
[0057]
[0058]
[0059]
[0060]
DETAILED DESCRIPTION
[0061] An illustrative embodiment of the present invention relates to an expanded fluoropolymer thermally bonded to itself without using an adhesive and methods for producing the same. In certain illustrative embodiments, a joining force can optionally be applied to the expanded fluoropolymer to thermally bond the expanded fluoropolymer to itself without using an adhesive. In such illustrative embodiments, the expanded fluoropolymer can be thermally bonded to itself without the use of a crushing force, as defined herein and would be understood by one of skill in the art. The expanded fluoropolymers of the present invention (EFPs) possesses both superior and unexpected properties compared to conventional fluoropolymers, such as ePTFE processed according to conventional methods. It has surprisingly and unexpectedly been observed that the expanded fluoropolymers formed by the methods of the present invention possess increased density, decreased porosity, increased longitudinal and radial tensile strength, decreased crystallinity and increased amorphousness, and an ability to expand to a larger ratio than conventional fluoropolymers (e.g., as described in U.S. Pat. No. 6,616,876). In certain embodiments, expanded fluoropolymers formed by the methods of the present invention arc non-porous. The expanded fluoropolymers formed by the methods of the present invention also possess the unexpected and surprising ability to thermally bond to themselves without using an adhesive (and optionally by applying a joining force), and once bonded as such, the resulting bond exhibits a bond strength at the interface between thermally bonded portions of the expanded fluoropolymer that is greater than the strength of the expanded fluoropolymer itself. It was surprisingly and unexpectedly observed that the expanded tluoropolymers of the present invention having superior properties compared to conventionally processed ePTFE can be formed by removing a wetting agent from a wet-stretched fluoropolymer material (the wetting agent being wetting fluid that was previously added to the extruded material prior to wet stretching) while portions of the wet-stretched fluoropolymer material remain in intimate contact with each other (i.e. the portions of wet-stretched fluoropolymer material to be bonded together arc placed into intimate contact with each other after stretching). In certain illustrative embodiments, the intimately contacted portions can optionally be sintered.
[0062]
[0063] As utilized herein, a joining force generally refers to brief application of a low magnitude force sufficient to bring two items or portions into contact. A joining force is distinguished herein from a crushing force, which refers to an application (e.g., a prolonged application) of a moderate to high magnitude force used in crushing one or more materials (e.g., together, as performed in machine pressing or calendaring). Accordingly, the meaning of these terms will be fully appreciated by one of skill in the art upon reading the present specification. In accordance with one example embodiment of the present invention, the pressure resulting from the joining force can be about 25 psi or less.
[0064]
[0065] One of skill in the art should appreciate that any suitable fluoropolymer material can be processed according to the methods of the present invention to produce an expanded fluoropolymer article having surprisingly superior properties compared to conventionally processed fluoropolymer articles. In accordance with an illustrative and non-limiting embodiment of the present invention, the expanded fluoropolymer article comprises PTFE. Examples of other suitable materials that can be processed according to the methods of the present invention to produce the superior expanded fluoropolymer articles of the present invention include, but are not limited to, homopolymers of PTFE, copolymers of PTFE in which the comonomer is ethylene, chlorotrifluoroethylene, perfluoroalkoxytetrafluoroethylene, and fluorinated propylene. In certain embodiments, a polyolefin, such as polypropylene and polyethylene, can be used instead of a fluoropolymer. Likewise, polymer materials that are expandable and have a microporous structure similar to ePTFE may also be capable of experiencing the superior properties of the present invention.
[0066] In contrast to conventionally processed fluoropolymer materials which are typically porous in nature due to their increased crystalline and decreased amorphous structure, the expanded fluoropolymers articles produced according to the methods of the present invention (e.g., including the expanded fluoropolymer article 10 of
[0067] As depicted in
[0068] In accordance with an illustrative and non-limiting embodiment of the present invention,
[0069] In accordance with the illustrative and non-limiting embodiment of the present invention shown in
[0070] In accordance with the illustrative and non-limiting embodiment of the present invention shown in
[0071] It should be appreciated, however, that the present invention is not intended to be limited to any such particular vertical arrangement. For example, each layer 16 arranged as such can be arranged such that the area of overlap between each adjacent layer 16 is marginal (i.e., less than about half of the surface area of adjacent layers 16 is overlapping) or substantial (i.e., more than about half of the surface area of adjacent layers 16 is overlapping). In addition, each layer 16 can be arranged so that the multi-layer expanded fluoropolymer article 10 is symmetrical or asymmetrical, forms a particular pattern, e.g., staggered consecutively to form a staircase like shape, staggered alternatively to form an accordion-like shape, etc., or so that each layer 16 has uniform or non-uniform thickness.
[0072] Turning now to the illustrative embodiments shown in
[0073] Although
[0074] The expanded fluoropolymer articles 14, 18 of
[0075]
[0076] The expandable fluoropolymer extrudate then may be rewet with a wet-stretch wetting agent, thus forming a wetted expanded fluoropolymer extrudate (step 108). A wet-stretch wetting agent, as used herein, generally refers to the wetting agent (e.g., a liquid) that is used in the process of wet stretching an article, as would be appreciated by one of skill in the art. Wet stretching itself is a pre-existing method of expanding or deforming an expandable polymer-based article while the article is wet with a wetting agent. Step 108 of rewetting the expandable fluoropolymer article with the wet-stretch wetting agent may be performed by submerging or soaking the expandable fluoropolymer in the wet-stretch wetting agent, spraying the wet-stretch wetting agent onto the expandable fluoropolymer article, rubbing the wet-stretch wetting agent into the expandable fluoropolymer article, or otherwise applying the wet-stretch wetting agent to the expandable fluoropolymer article. The term rewetting is intended to have its ordinary meaning in the art, e.g., of applying a second wetting agent after completion of one or more activities for which a first wetting agent was intended to have been used. In general, it should be understood that as defined herein, the first wetting agent (e.g., the lubricant wetting agent) can be the same as or different from the second wetting agent (e.g., the wet-stretch wetting agent).
[0077] In accordance with conventional wet stretching methods, the wetted expanded fluoropolymer extrudate can be stretched to form an expanded fluoropolymer article (step 110). As would be appreciated by one of skill in the art, in embodiments where the wetted expanded fluoropolymer extrudate is shaped generally like a hollow cylinder, the wetted expanded fluoropolymer extrudate can be stretched by being pulling over a mandrel. This can cause the wetted expanded fluoropolymer extrudate to be stretched in the radial direction (e.g., to undergo radial expansion). Alternatively, in embodiments where the wetted expanded fluoropolymer extrudate is shaped like a sheet, step 110 can include wet stretching the wetted expanded fluoropolymer extrudate in the transverse direction (e.g., as opposed to the machine direction), as would be appreciated by one of skill in the art upon reading the present specification. For example, the wetted expanded fluoropolymer extrudate can be stretched in the transverse direction at a temperature below the flash point of the wet stretch wetting agent. U.S. Pat. No. 6,616,876, issued Sep. 9, 2003 and entitled Method for treating expandable polymer materials, describes several examples of suitable wet stretch methods that additionally or alternatively can be used to perform step 110 in the method of
[0078] Notably, after performing step 110 of wet stretching the wetted expandable fluoropolymer extrudate to produce a wet expanded fluoropolymer article, the two portions of the resulting wet expanded fluoropolymer article can be placed in intimate contact with each other, i.e., while still wet with the wet-stretch wetting agent (step 112). Step 110 of placing the two portions in intimate contact with each other while the two portions (e.g., and optionally the entire wet expanded fluoropolymer article) are still wet with the wet-stretch wetting agent can be performed in a number of different ways. In accordance with the example embodiment of
[0079] In accordance with some alternative embodiments, the two end portions of the wet expanded fluoropolymer article instead are placed in intimate contact with each other in an abutting, side-by-side manner. Furthermore, although only small portions 12 of the wet expanded fluoropolymer article 10 of
[0080] While the two portions (e.g., the two end portions) are in intimate contact with each other, the wet-stretch wetting agent can be removed at least from the wet expanded fluoropolymer article (step 114). As two non-limiting examples, the wet-stretch wetting agent can be removed by exposing the wet expanded fluoropolymer article to drying conditions, e.g., involving application of heat. In step 114, the wet-stretch wetting agent optionally can also be removed from the remainder of the wet expanded fluoropolymer article besides just the two portions placed in intimate contact, e.g., by drying or heating all of the wet expanded fluoropolymer article. Furthermore, while still in intimate contact (e.g., and without being intermittently removed from intimate contact with each other), at least the two portions of the wet expanded fluoropolymer article can be sintered (step 116). In accordance with illustrative embodiments of the present invention, step 116 of sintering occurs at a temperature and for a period of time that is sufficient to form bonds between the two portions of the expanded fluoropolymer article. In general, step 116 can occur simultaneous with or subsequent to step 114 of removing the wet-stretch wetting agent. For example, steps 114 and 116 can include sintering the entire expanded fluoropolymer article for a period of time and at a temperature that is sufficient to both (a) cause the wet-stretch wetting agent to dry out and be removed from the expanded fluoropolymer article in its entirety and (b) cause bonds to form between the two portions of the expanded fluoropolymer article. The product resulting from step 116 is an expanded fluoropolymer article (e.g., 10, as depicted in
[0081] In accordance with an example embodiment of the present invention,
[0082] It should be appreciated that the first and the second expanded fluoropolymer articles provided in steps 118 and 120 can be wet-stretched using the same or different wet-stretch wetting agent(s). Furthermore, the first and second expanded fluoropolymer articles can be formed using the same or different lubricant wetting agent(s). In general, the first and second expanded fluoropolymer articles can be formed from the same mixture or from different mixtures (in step 102), from the same billet or from different billets (in step 104 ), and/or from the same or different expandable fluoropolymer extrudate(s) (in step 106). The present invention is not limited in the particular manner in which the first and second expanded fluoropolymer articles are provided in steps 118 and 120. Two entirely separate iterations of steps 102 through 108 can be performed using separate and/or different mixtures, billets, and/or expandable fluoropolymer extrudates, or a single iteration of steps 102 through 108 can be performed to provide the first and second expanded fluoropolymer articles.
[0083] A portion of the first expanded fluoropolymer article and a portion of the second expanded fluoropolymer article can be placed in intimate contact with each other while still wet with the wet-stretch welting agent that used to wet stretch each of the first and second expanded fluoropolymer articles (step 122). Step 122 can occur in any number of suitable ways. As a first illustrative and non-limiting example, the portions of the first and second expanded fluoropolymer articles placed in intimate contact can form two fully-overlapping layers (e.g., tiers), as substantially depicted and described previously herein with reference to the multi-layer fluoropolymer article 16 of
[0084] While in intimate contact with each other, the wet-stretch wetting agent(s) used to produce the first and second expanded fluoropolymer articles can be removed at least from the portions of the first and second expanded fluoropolymer articles that are in intimate contact (step 124). The wet-stretch wetting agent(s) also may be simultaneously removed from a remainder of the first and second expanded fluoropolymer articles in step 124. As a non-limiting example, the wet-stretch wetting agent(s) can be removed by drying the portions of the first and second expanded fluoropolymer articles in intimate contact, e.g., by applying heat to at least the portions of the first and second expanded fluoropolymer articles in intimate contact.
[0085] Furthermore, while still in intimate contact (e.g., and without being intermittently removed from intimate contact with each other), at least the portions of the first and second expanded fluoropolymer articles can be sintered (step 126). Sintering, as used herein, has its normal definition in the art of causing to become a coherent mass by heating without melting. Accordingly, in step 126 of sintering, bonds are formed between the portions of the first and second expanded fluoropolymer articles. Without wishing to be bound by any particular theory, it is believed that the bonds formed comprise a combination of bonds. The combination of bonds can include, but is not limited to, one or more of covalent bonds, van der Walls forces, hydrogen bonds, ionic bonds, electrostatic interactions and/or changes created in the chain entanglement of the expanded fluoropolymer material. In certain embodiments, the combination of bonds comprises covalent bonds. In certain embodiments, the combination of bonds comprises van der Walls forces. In certain embodiments, the combination of bonds comprises hydrogen bonds. In certain embodiments, the combination of bonds comprises ionic bonds. In certain embodiments, the combination of bonds comprises electrostatic interactions. In certain embodiments, the combination of bonds comprises changes created in the chain entanglement of the expanded fluoropolymer material.
[0086] In certain embodiments, the combination of bonds comprises covalent bonds and at least one other type bond. In an embodiment, the combination of bonds comprises at least covalent bonds and van der Walls forces. In an embodiment, the combination of bonds comprises at least covalent bonds and hydrogen bonds. In an embodiment, the combination of bonds comprises at least covalent bonds and ionic bonds. In an embodiment, the combination of bonds comprises at least covalent bonds and electrostatic interactions. In an embodiment, the combination of bonds comprises at least covalent bonds and changes created in the chain entanglement of the expanded fluoropolymer material.
[0087] In certain embodiments, the combination of bonds comprises covalent bonds and at least two other types of bonds. In an embodiment, the combination of bonds comprises at least covalent bonds, van der Walls forces and hydrogen bonds. In an embodiment, the combination of bonds comprises at least covalent bonds, van der Walls forces and ionic bonds. In an embodiment, the combination of bonds comprises at least covalent bonds, van der Walls forces and electrostatic interactions. In an embodiment, the combination of bonds comprises at least covalent bonds, van der Walls forces and electrostatic interactions. In an embodiment, the combination of bonds comprises at least covalent bonds, van der Walls forces and changes in the chain entanglement of the expanded fluoropolymer material. In an embodiment, the combination of bonds comprises at least covalent bonds, hydrogen bonds and ionic bonds. In an embodiment, the combination of bonds comprises at least covalent bonds, hydrogen bonds and electrostatic interactions. In an embodiment, the combination of bonds comprises at least covalent bonds, hydrogen bonds and changes in the chain entanglement of the expanded fluoropolymer material. In an embodiment, the combination of bonds comprises at least covalent bonds, ionic bonds, and electrostatic interactions. In an embodiment, the combination of bonds comprises at least covalent bonds, ionic bonds, and changes in the chain entanglement of the expanded fluoropolymer material. In an embodiment, the combination of bonds comprises at least covalent bonds, electrostatic interactions, and changes in the chain entanglement of the expanded fluoropolymer material.
[0088] In an embodiment, the combination of bonds comprises covalent bonds and at least three other types of bonds. In an embodiment, the combination of bonds comprises at least covalent bonds, van der Walls forces, hydrogen bonds and ionic bonds. In an embodiment, the combination of bonds comprises at least covalent bonds, van der Walls forces, hydrogen bonds and electrostatic interactions. In an embodiment, the combination of bonds comprises at least covalent bonds, van der Walls forces, hydrogen bonds and changes in the chain entanglement of the expanded fluoropolymer material. In an embodiment, the combination of bonds comprises at least covalent bonds, van der Walls forces, ionic bonds, and electrostatic interactions. In an embodiment, the combination of bonds comprises at least covalent bonds, van der Walls forces, ionic bonds and changes in the chain entanglement of the expanded fluoropolymer material. In an embodiment, the combination of bonds comprises at least covalent bonds, van der Walls forces, electrostatic interactions, and changes in the chain entanglement of the expanded fluoropolymer material. In an embodiment, the combination of bonds comprises at least covalent bonds, hydrogen bonds, ionic bonds and electrostatic interactions. In an embodiment, the combination of bonds comprises at least covalent bonds, hydrogen bonds, ionic bonds and changes in the chain entanglement of the expanded fluoropolymer material. In an embodiment, the combination of bonds comprises at least covalent bonds, ionic bonds, electrostatic interactions and changes in the chain entanglement of the fluoropolymer material.
[0089] In certain embodiments, the combination of bonds comprises covalent bonds and at least four other types of bonds. In an embodiment, the combination of bonds comprises at least covalent bonds, van der Walls forces, hydrogen bonds, ionic bonds and electrostatic interactions. In an embodiment, the combination of bonds comprises at least covalent bonds, van der Walls forces, hydrogen bonds, ionic bonds and changes in the chain entanglement of the expanded fluoropolymer material. In an embodiment, the combination of bonds comprises at least covalent bonds, hydrogen bonds, ionic bonds, electrostatic interactions, and changes in the chain entanglement of the expanded fluoropolymer material.
[0090] In an embodiment, the combination of bonds comprises covalent bonds and at least five other types of bonds. In an embodiment, the combination of bonds comprises at least covalent bonds, van der Walls forces, hydrogen bonds, ionic bonds, electrostatic interactions, and changes in the chain entanglement of the expanded fluoropolymer material.
[0091] In certain embodiments, the combination of bonds does not comprise covalent bonds.
[0092] In certain embodiments, the combination of bonds comprises van der Walls forces and at least one other type of bond. In an embodiment, the combination of bonds comprises at least van der Walls forces and hydrogen bonds. In an embodiment, the combination of bonds comprises at least van der Walls forces and ionic bonds. In an embodiment, the combination of bonds comprises at least van der Walls forces and electrostatic interactions. In an embodiment, the combination of bonds comprises at least van der Walls forces and changes in the chain entanglement of the expanded fluoropolymer material. In an embodiment, the combination of bonds comprises at least van der Walls forces and covalent bonds.
[0093] In certain embodiments, the combination of bonds comprises van der Walls forces and at least two other types of bonds. In an embodiment, the combination of bonds comprises at least van der Walls forces, hydrogen bonds and ionic bonds. In an embodiment, the combination of bonds comprises at least van der Walls forces, hydrogen bonds and electrostatic interactions. In an embodiment, the combination of bonds comprises at least van der Walls forces, hydrogen bonds and changes in the chain entanglement of the expanded fluoropolymer material. In an embodiment, the combination of bonds comprises at least van der Walls forces, hydrogen bonds and covalent bonds. In an embodiment, the combination of bonds comprises at least van der Walls forces, ionic bonds and electrostatic interactions. In an embodiment, the combination of bonds comprises at least van der Walls forces, ionic bonds and changes in the chain entanglement of the expanded fluoropolymer material. In an embodiment, the combination of bonds comprises at least van der Walls forces, ionic bonds and covalent bonds. In an embodiment, the combination of bonds comprises at least van der Walls forces, electrostatic interactions and changes in the chain entanglement of the expanded fluoropolymer material. In an embodiment, the combination of bonds comprises at least van der Walls forces, electrostatic interactions and covalent bonds. In an embodiment, the combination of bonds comprises at least van der Walls forces, changes in the chain entanglement of the expanded fluoropolymer material and covalent bonds.
[0094] In certain embodiments, the combination of bonds comprises van der Walls forces and at least three other types of bonds. In an embodiment, the combination of bonds comprises at least van der Walls forces, hydrogen bonds, ionic bonds, and electrostatic interactions. In certain embodiments, the combination of bonds comprises at least van der Walls forces, hydrogen bonds, electrostatic interactions and changes in the chain entanglement of the expanded fluoropolymer material. In certain embodiments, the combination of bonds comprises van der Walls forces, hydrogen bonds, electrostatic interactions and covalent bonds. In certain embodiments, the combination of bonds comprises at least van der Walls forces, ionic bonds, electrostatic interactions and changes in the chain entanglement of the expanded fluoropolymer material. In certain embodiments, the combination of bonds comprises at least van der Walls forces, ionic bonds, electrostatic interactions and covalent bonds. In certain embodiments, the combination of bonds comprises at least van der Walls forces, ionic bonds, electrostatic interactions and covalent bonds. In certain embodiments, the combination of bonds comprises at least van der Walls forces, electrostatic interactions, changes in the chain entanglement of the expanded fluoropolymer material and covalent bonds.
[0095] In certain embodiments, the combination of bonds comprises van der Walls forces and at least four other types of bonds. In an embodiment, the combination of bonds comprises at least Van der walls forces, hydrogen bonds, ionic bonds, electrostatic interactions and changes in the chain entanglement of the expanded fluoropolymer material.
[0096] In certain embodiments, the combination of bonds does not comprise van der Walls forces.
[0097] In certain embodiments, the combination of bonds comprises changes in the chain entanglement of the expanded fluoropolymer material and at least one other type of bond. In an embodiment, the combination of bonds comprises at least changes in the chain entanglement of the expanded fluoropolymer material and covalent bonds. In an embodiment, the combination of bonds comprises at least changes in the chain entanglement of the expanded fluoropolymer material and van der Walls forces. In an embodiment, the combination of bonds comprises at least changes in the chain entanglement of the expanded fluoropolymer material and hydrogen bonds. In an embodiment, the combination of bonds comprises at least changes in the chain entanglement of the expanded fluoropolymer material and ionic bonds. In an embodiment, the combination of bonds comprises at least changes in the chain entanglement of the expanded fluoropolymer material and electrostatic interactions.
[0098] In certain embodiments, the combination of bonds comprises changes in the chain entanglement of the expanded fluoropolymers material and at least two other types of bonds. In an embodiment, the combination of bonds comprises at least changes in the chain entanglement of the expanded fluoropolymer material, covalent bonds and van der Walls forces. In an embodiment, the combination of bonds comprises at least changes in the chain entanglement of the expanded fluoropolymer material, covalent bonds and hydrogen bonds. In an embodiment, the combination of bonds comprises at least changes in the chain entanglement of the expanded fluoropolymer material, covalent bonds and ionic bonds. In an embodiment, the combination of bonds comprises at least changes in the chain entanglement of the expanded fluoropolymer material, covalent bonds and electrostatic interactions. In an embodiment, the combination of bonds comprises at least changes in the chain entanglement of the expanded fluoropolymer material, van der Walls forces and hydrogen bonds. In an embodiment, the combination of bonds comprises at least changes in the chain entanglement of the expanded fluoropolymer material, van der Walls forces and ionic bonds. In an embodiment, the combination of bonds comprises at least changes in the chain entanglement of the expanded fluoropolymer material, van der Walls forces and electrostatic interactions. In an embodiment, the combination of bonds comprises at least changes in the chain entanglement of the expanded fluoropolymer material, hydrogen bonds, and ionic bonds. In an embodiment, the combination of bonds comprises at least changes in the chain entanglement of the expanded fluoropolymer material, hydrogen bonds, and electrostatic interactions. In an embodiment, the combination of bonds comprises at least changes in the chain entanglement of the expanded fluoropolymer material, ionic bonds and electrostatic interactions.
[0099] In certain embodiments, the combination of bonds comprises changes in the chain entanglement of the expanded fluoropolymer material and at least three other types of bonds. In an embodiment, the combination of bonds comprises at least changes in the chain entanglement of the expanded fluoropolymer material, covalent bonds, van der Walls forces and hydrogen bonds. In an embodiment, the combination of bonds comprises at least changes in the chain entanglement of the expanded fluoropolymer material, covalent bonds, van der Walls forces and ionic bonds. In an embodiment, the combination of bonds comprises at least changes in the chain entanglement of the expanded fluoropolymer material, covalent bonds, van der Walls forces and electrostatic interactions. In an embodiment, the combination of bonds comprises at least changes in the chain entanglement of the expanded fluoropolymer material, van der Walls forces, hydrogen bonds, and ionic bonds. In an embodiment, the combination of bonds comprises at least changes in the chain entanglement of the expanded fluoropolymer material, van der Walls forces, hydrogen bonds, and electrostatic interactions. In an embodiment, the combination of bonds comprises at least changes in the chain entanglement of the expanded fluoropolymer material, hydrogen bonds, ionic bonds and electrostatic interactions.
[0100] In certain embodiments, the combination of bonds comprises changes in the chain entanglement of the expanded fluoropolymer material and at least four other types of bonds.
[0101] In certain embodiments, the combination of bonds does not comprise the chain entanglement of the expanded fluoropolymer material.
[0102] In certain embodiments, the combination of bonds comprises hydrogen bonds and at least one other bond type. In an embodiment, the combination of bonds comprises at least hydrogen bonds and ionic bonds. In an embodiment, the combination of bonds comprises at least hydrogen bonds and electrostatic interactions.
[0103] In certain embodiments, the combination of bonds comprises hydrogen bonds and at least two other bond types. In an embodiment, the combination of bonds comprises at least hydrogen bonds, ionic bonds and electrostatic interactions.
[0104] In certain embodiments, the combination of bonds comprises hydrogen bonds and at least two three other bond types.
[0105] In certain embodiments, the combination of bonds comprises hydrogen bonds and at least two four other bond types.
[0106] In certain embodiments, the combination of bonds does not comprise hydrogen bonds.
[0107] In certain embodiments, the combination of bonds comprises ionic bonds and at least one other bond type. In an embodiment, the combination of bonds comprises at least ionic bonds and electrostatic interactions,
[0108] In certain embodiments, the combination of bonds comprises ionic bonds and at least two other bond types.
[0109] In certain embodiments, the combination of bonds comprises ionic bonds and at least three other bond types.
[0110] In certain embodiments, the combination of bonds comprises ionic bonds and at least four other bond types.
[0111] In certain embodiments, the combination of bonds does not comprise ionic bonds.
[0112] In general, step 126 can occur simultaneous with or subsequent to step 124 of removing the wet-stretch wetting agent(s). For example, steps 124 and 126 can include sintering all of the first and the second expanded fluoropolymer articles for a period of time and at a temperature that is sufficient to both (a) cause the wet-stretch wetting agent(s) to dry out and be removed from both the first and the second expanded fluoropolymer article in their entirety and (b) cause bonds to form between the portions of the first and second expanded fluoropolymer article in intimate contact. The end result of step 126 is an expanded fluoropolymer article having multiple layers or portions that are thermally bonded to each other without the use of adhesive(s) (optionally applying a joining force).
[0113] In general, although the extrusion wetting agent and the wet-stretch wetting agent are referred to herein in the singular, it should be appreciated that each such wetting agent can include a blend or other combination of different wetting agents. Accordingly, the effects and functionality described herein with reference to any single wetting agent can be achieved in each instance through the use of a plurality of wetting agents. Furthermore, the extrusion wetting agent and the wet-stretch wetting agent can be the same or different wetting agents. As a few non-limiting examples, each of the extrusion wetting agent and the wet-stretch wetting agent can include ethanol, methanol, IPA, Isopar-H, Isopar-E, Isopar-V, or any combination thereof. Upon reading the present specification, one of skill in the art will appreciate a variety of additional wetting agents that of which the wet-stretch wetting agent and/or the extrusion agent can be comprised. The present invention is not limited to the particular examples of wetting agents described herein. Any suitable wetting agent may be implemented with the present invention.
[0114] During the course of work described herein, the performance of expanded fluoropolymers processed according to the methods of the present invention were analyzed in comparison to fluoropolymers processed according to conventional methods. The results of such performance tests indicate that the expanded fluoropolymers (e.g., PTFE) processed according to the methods of the present invention outlined herein possess many characteristics and properties that are unexpected and superior compared to conventional fluoropolymers, such as perfluoroalkoxy (PFA) and expanded polytetrafluoroethylene (ePTFE). It was surprisingly and unexpectedly observed, for example, that the expanded fluoropolymers of the present invention possess the ability to be thermally bonded (e.g., joined, sealed or laminated) together without the aid of an adhesive, lamination aid, or chemical or physical treatment, such as chemical etching, plasma treatment or corona treatment. It was additionally observed that the expanded fluoropolymers of the present invention are capable of being thermally bonded together without application of a crushing force (e.g., by optionally applying a joining force). It was surprisingly and unexpectedly observed, for example, that the strength of the bonds at the interface between the expanded fluoropolymers of the present invention that are thermally bonded together is greater than the strength of the expanded fluoropolymers themselves.
[0115] These superior and unexpected properties are believed to be the result of the inventive processing methods outlined herein in which it was further unexpectedly and surprisingly discovered that, in contrast to conventional processing methods in which portions of the fluoropolymer are placed in intimate contact at the beginning of the process and require at least some stretching after being placed in intimate contact, the methods of the present invention place portions of the fluoropolymer in intimate contact further downstream in the process (i.e., after wet stretching) and no further stretching is required after a wetting agent is removed to produce the superior results obtained herein.
[0116] Conventional wisdom holds that placing the portions in intimate contact in the beginning of the process (e.g., before at least some stretching) is preferable because it maximizes contacts between fluoropolymer materials being bonded together and promotes a uniform microstructure across the interface between the fluoropolymers upon subsequent stretching to impart bond strength. Contrary to conventional wisdom, it has been unexpectedly and surprisingly observed that (a) placing portions of the wet-stretched fluoropolymer in intimate contact after stretching, (b) removing the wetting agent from the wet-stretched fluoropolymer while those portions are in intimate contact with each other, and (c) heating (e.g., sintering) collectively enable the expanded fluoropolymer to achieve a stronger material strength. Furthermore, stronger bonds are formed between those portions in intimate contact, and the improved bond strength is greater than the strength of the expanded fluoropolymer material itself.
[0117] In further contrast to conventional processing methods which produce porous PTFE, the methods of the present invention yield a substantially non-porous fluoropolymer, e.g., non-porous ePTFE, i.e., non-porous wet-stretched ePTFE. Those conventional processes typically employ a filler (e.g., of up to 50% by weight) to fill the pores and enhance the density of the final product. In contrast to conventional processes, upon completion of the methods of the present invention, and in particular upon placing portions of fluoropolymers in intimate contact after stretching, and removing the wetting agent while the wet-stretched fluoropolymer is in intimate contact with itself or another wet-stretched fluoropolymer, the expanded fluoropolymers thus formed are substantially non-porous without further processing or addition of filler.
[0118] Without being bound or limited by theory, it is believed that placing the portions of fluoropolymer to be thermally bonded together after stretching maximizes the density and decreases the porosity of the material without diminishing the contacts between the fluoropolymers, thereby increasing both the number and strength of the bonds formed in each direction. It is also believed that performing at least some stretching after removing the wetting agent from a wet-stretched fluoropolymer material while portions of the wet-stretched fluoropolymer material remain in intimate contact with each other can result in sub-optimal overall bond strength at the interface between the thermally bonded portions due to the incidental breaking of individual bonds and accompanying increased porosity achieved during the subsequent stretching.
[0119] These unexpected and superior results will be apparent to one of skill upon reviewing the results of the performance testing, which are summarized below.
Longitudinal Tensile Strength (ASM D882)
[0120] The longitudinal tensile strength of articles constructed from expanded fluoropolymers of the present invention was tested and compared to the longitudinal tensile strength of similarly constructed articles made using PFA and conventional ePTFE (e.g., via known processes of lubricating PTFE resin, preforming, extruding, calendaring, removing lubrication, and stretching in the machine direction). The PFA articles tested were produced using PFA material commercially available as a cast film from CS Hyde Company, Inc, of Lake Villa, Illinois (skived PFA film), The longitudinal tensile strength was measured using an INSTRON universal testing machine, in accordance with ASTM D882, entitled Standard Test Method for Tensile Properties of Thin Plastic Sheeting. Tubes of expanded fluoropolymer of the present invention were cut open along the length at the joint to form 12 articles of expanded fluoropolymer having thicknesses of 0.0005 inch. The fluoropolymer articles thus formed were loaded into the testing machine with a 1 gap between the grips. As shown in
TABLE-US-00001 TABLE 1 Longitudinal Tensile Strength (LTS) LTS (lbf) LTS (psi) 0.0005 EFP 8.12 16,186 0.0005 PFA 2.77 5,540 0.0005 ePTFE 2.63 5.260
Bond Strength (ASM D882) of Expanded Fluoropolymer Thermally Bonded to Itself without Adhesive
[0121] The bond strength of expanded fluoropolymer thermally bonded to itself (forming the joint) without adhesive according to the methods of the present invention was tested and compared to the bond strength of similarly constructed articles made using PFA and ePTFE by conventional methods. The bond strength was measured using an INSTRON universal testing machine, in accordance with ASTM D882, entitled Standard Test Method for Tensile Properties of Thin Plastic Sheeting. The opposing edges of an expanded fluoropolymers were thermally bonded to each other (forming a joint) according to the methods of the present invention to form expanded fluoropolymer tubes. For example, a sheet comprising expanded fluoropolymers of the present invention was wrapped around a mandrel length wise with a 0.25 inch overlap to form a joined configuration. The material was subsequently heated to 360 Celsius for approximately 15 minutes. The tubes of expanded fluoropolymer of the present invention were cut along the length opposite of the bonds (joint) to form articles having a 1-inch width and the bonds in the middle. Articles were loaded onto the testing machine with the bonds between the grips. Surprisingly and unexpectedly, all of the articles constructed from the expanded fluoropolymers thermally bonded to themselves without adhesive according to the methods of the present invention failed outside the bonded portions (i.e., outside the joint), in contrast to the PFA and ePTFE articles made using conventional methods, which all failed at or within the bonded portions (i.e., at or within the joint). This result indicates that the bond strength in the X-direction of the expanded fluoropolymers thermally bonded to themselves without adhesive is greater than the X direction strength of the expanded fluoropolymers themselves. Put differently, the strength at the joint of the expanded fluoropolymer article thermally bonded to itself without adhesive in a joined configuration is greater than the strength of the fluoropolymer article itself. As shown in
TABLE-US-00002 TABLE 2 X-Direction Tensile Strength or Joint Strength LTS (lbf) LTS (psi) EFP joint 4.2 8,400 PFA joint 1.01 2,020 ePTFE joint 0.59 1,180
Radial Tensile Strength (RTS)
[0122] The radial tensile strength of articles constructed from expanded fluoropolymers thermally bonded to themselves without adhesive according to the methods the present invention was tested and compared to the radial tensile strength of similarly constructed articles made using PFA and conventional ePTFE by conventional methods. The radial tensile strength was measured using an INSTRON universal testing machine, in accordance with ASTM D882, entitled Standard Test Method for Tensile Properties of Thin Plastic Sheeting. The articles tested were constructed in the form of 1 diameter tubes into which a split mandrel was inserted about 1 into the length of each tube after which each half of the mandrel was pulled in opposite directions until each tube failed. As shown in
TABLE-US-00003 TABLE 3 Radial Tensile Strength RTS (lbf) RTS (psi) .0005 EFP tube 14.76 29,520 .0005 PFA tube 2.30 4,600 .0005 ePTFE tube 1.76 3,520
Longitudinal Tensile Strength of Perforated Expanded Fluoropolymer Films
[0123] The longitudinal tensile strength of perforated films constructed from expanded fluoropolymers produced according to the methods the present invention was tested and compared to the longitudinal tensile strength of similarly constructed perforated articles made using PFA and conventional ePTFE by conventional methods. Perforations of approximately 100 microns were made in each of the films using a laser. Samples were made with different perforation densities and then tested for longitudinal tensile strength as described above using an INSTRON universal testing machine. The results are shown in Tables 4, 5 and 6 below.
TABLE-US-00004 TABLE 4 Longitudinal Tensile Strength of Perforated Expanded Fluoropolymers of the present invention LTS LTS Elongation Elongation (lbf) (psi) (in) (%) .0005 EFP 8.12 16,240 3.45 345% .0005 EFP 5.73 11,452 1.16 116% perforated 900 perforations (100 micron) in.sup.2 .0005 EFP 4.4 8,816 1.06 106% perforated 1,600 (100 micron) in.sup.2 .0005 EFP 2.53 5,066 0.61 61% perforated 2,500 (100 micron) in.sup.2
TABLE-US-00005 TABLE 5 Longitudinal Tensile Strength of Perforated PFA LTS LTS Elongation Elongation (lbf) (psi) (in) (%) .0005 PFA 2.77 5,540 2.38 238% .0005 PFA 1.14 2,280 1.0 100% perforated 900 (100 micron) in.sup.2 .0005 PFA 1.05 2,100 0.96 96% perforated 1600 (100 micron) in.sup.2 .0005 PFA 0.85 1,700 0.77 77% perforated 2500 (100 micron) in.sup.2
TABLE-US-00006 TABLE 6 Longitudinal Tensile Strength of Perforated ePTFE LTS LTS Elongation Elongation (lbf) (psi) (in) (%) .0005 ePTFE 2.63 5,260 0.5 50% .0005 ePTFE 1.01 2,020 0.33 33% perforated 900 (100 micron) in.sup.2 .0005 ePTFE 0.94 1,880 0.28 28% perforated 1600 (100 micron) in.sup.2 .0005 ePTFE 0.17 340 0.21 21% perorated 2500 (100 micron) in.sup.2
[0124] In accordance with an illustrative and non-limiting example embodiment of the present invention, an expanded fluoropolymer article has a longitudinal tensile strength, when formed as a 0.0005 inch thick film having about 900 perforations per square inch of approximately 100 microns, of 5.73 lbf (11,452 psi), as measured according to ASTM D882. In accordance with an illustrative and non-limiting example embodiment of the present invention, an expanded fluoropolymer article has a longitudinal tensile strength, when formed as a 0,0005 inch thick film having about 1,600 perforations per square inch of approximately 100 microns, of 4.4 lbf (8,816 psi), as measured according to ASTM D882. In accordance with an illustrative and non-limiting example embodiment of the present invention, an expanded fluoropolymer article has a longitudinal tensile strength, when formed as a 0.0005 inch thick film having about 2,500 perforations per square inch of approximately 100 microns, of 2.53 lbf (5,066 psi), as measured according to ASTM D882. As shown in
Contact Angle
[0125] The contact angle of the expanded fluoropolymers produced according to the methods of the present invention was measured using water and 0.1 mol hydrochloric acid as the test fluids and compared to the contact angle of PFA measured using the same test fluids. All measurements were taken using an AST video contact angle system. The static sessile drop method was utilized. The sessile drop method uses a contact angle goniometer with an optical subsystem to capture the profile of a liquid on a solid substrate. The angle formed between the liquid/solid interface and the liquid/vapor interface is the contact angle. The results of the water contact angle and acid contact angle measurements are provided in Tables 7 and 8 below, respectively.
TABLE-US-00007 TABLE 7 Water contact angle EFPs PFA angle 117.4 104.5 115.8 104.8 121.2 106.4 116.4 104.7 118.5 106.7 average 117.86 105.42
TABLE-US-00008 TABLE 8 .1 mol hydrochloric acid contact angle EFPs PFA angle 114.8 105.8 116.8 105.4 115.6 103.7 114.9 103.9 113.9 104.8 average 115.2 104.72
[0126] In accordance with an illustrative and non-limiting embodiment of the present invention, an expanded fluoropolymer article produced according to the methods of the present invention has a water contact angle of at least 115. In certain illustrative embodiments, the expanded fluoropolymer article has a water contact angle of about 117.86.
[0127] In accordance with an illustrative and non-limiting embodiment of the present invention, an expanded fluoropolymer article produced according to the methods of the present invention has an acid contact angle of at least 113. In certain illustrative embodiments, the expanded fluoropolymer article has an acid contact angle of about 115.2.
T-Peel Test
[0128] A T-peel test was performed to compare the relative peel resistance of bonds between layers of expanded fluoropolymer thermally bonded to each other (at the joint) without adhesive optionally applying a joining force according to the methods of the present invention and the relative peel resistance of bonds formed between layers of conventional ePTFE bonded to each other according to conventional methods. In certain illustrative embodiments, layers of expanded fluoropolymer can be thermally bonded together without adhesive by optionally applying a joining force (i.e., an active or passive force required to place the layers into intimate contact with each other in a particular configuration e.g., joined, sealed, laminated, etc.) to bring the layers into intimate contact with each other. The appropriate joining force for any particular intended application would be apparent to those skilled in the art. It should be appreciated that a joining force, which is brief application of a low magnitude force, is not a crushing force (e.g., a force involved in machine pressing or calendaring) which is a prolonged application of a moderate to high magnitude force. For the T-peel test, two layers of expanded fluoropolymer material processed according to the methods outlined herein were placed into intimate contact with each other by using a hand roller to apply a joining force to form a multi-layer expanded fluoropolymer article thermally bonded together along a joint without adhesive in a laminated configuration. The laminated multi-layer expanded fluoropolymer article was subsequently heated for 900 seconds at 360 Celsius. The results of the T-peel test are shown in
Fourier Transform Infrared (FTIR) Analysis
[0129] Fourier Transform Infrared (FTIR) Analysis was used to characterize the chemistry and morphology of unprocessed PTFE resin, PTFE processed using methods described in the prior art, and an expanded fluoropolymer of the present invention (e.g., PTFE) processed using the methods of the present invention.
Differential Scanning Calorimetry (DSC)
[0130] Differential Scanning calorimetry (DSC) is a thermal analytical technique used to characterize thermal properties of a material, including crystalline melting point and polymorph transitions. Peaks detected at room temperature are attributed to crystalline phase transitions while those detected above 320 C. are attributed to melt of the crystalline phase. A comparison of the results obtained between conventional PTFE and an expanded fluoropolymer produced according to the methods of the present invention is shown in
TABLE-US-00009 TABLE 9 Summary of DSC Data: Expanded Fluoropolymer Produced According to the Methods of the Present Invention vs. Control. Phase Transition II-IV Melt Heat of Heat of Apex Transition Apex Transition Control 21.95 C. 4.444 J/g 329.09 C. 22.63 J/g EFPs 19.78 C. 3.699 J/g 327.44 C. 21.77 J/g Difference 2.17 C. 0.745 J/g 1.65 C. 0.86 J/g
Dynamic Mechanical Analysis (DMA)
[0131] DMA measures the modulus (stiffness) properties of materials as they are deformed under periodic stress. These measurements provide information about the performance of materials. The storage modulus is a direct measurement of the energy stored, or elasticity in a material. The higher the storage modulus the more memory or elasticity the sample has. Higher storage modulus correlates to a sample with higher strength and improved stability. As shown in
Coefficient of Friction (COF) on Tissue
[0132] Samples of expanded fluoropolymers produced according to the methods of the present invention and conventional ePTFE and PFA were tested to measure the coefficient of friction between those materials and tissue (bovine intestine), according to the procedure outlined below. The results for each of the samples are reported in Tables 10, 11 and 12. As is shown in Tables 10-12 below and in
TABLE-US-00010 TABLE 10 COF for EFPs maximum force (g) coefficient of friction 35.65 0.178 36.92 0.184 26.85 0.134 28.21 0.141 26.91 0.135 Average 30.908 0.1544
TABLE-US-00011 TABLE 11 COF for conventional ePTFE maximum force (g) coefficient of friction 345.5 1.72 367.4 1.83 322.5 1.61 390.9 1.95 Average 356.575 1.7775
TABLE-US-00012 TABLE 12 COF for PFA maximum force (g) coefficient of friction 53.79 0.268 41.45 0.207 32.11 0.160 32.43 0.162 33.2 0.166 Average 38.596 0.1926
[0138] In accordance with an illustrative and non-limiting embodiment of the present invention, the methods described herein can be used to produce an expanded polymer. In certain illustrative embodiments, the expanded polymer comprises a wet-stretched to expanded polytetrafluoroethylene (ePTFE) exhibiting both a higher amorphous fraction and a lower crystalline fraction than an expanded polymer formed from a comparative non-wet-stretched ePTFE, as characterized by a DSC thermogram. In certain embodiments, the DSC thermogram of the wet-stretched ePTFE exhibits a phase transition of at least 2 degrees Celsius less than the DSC thermogram of the wet-stretched ePTFE. In certain embodiments, the DSC thermogram of the wet-stretched ePTFE exhibits a heat of fusion of 0.75 joules per mole less than the DSC thermogram of the wet-stretched ePTFE.
[0139] In accordance with an illustrative and non-limiting embodiment of the present invention, the wet-stretched ePTFE is capable of being thermally bonded to itself without adhesive, crushing force, or application of a chemical treatment to the wet-stretched ePTFE. In certain illustrative embodiments, the wet-stretched ePTFE is thermally bonded to itself without using an adhesive. In certain illustrative embodiments, the wet-stretched ePTFE is thermally bonded to itself without applying a crushing force to the wet-stretched ePTFE. In certain illustrative embodiments, the wet-stretched ePTFE is thermally bonded to itself without application of a chemical treatment to the wet-stretched ePTFE. In certain illustrative embodiments, two or more articles comprising wet-stretched ePTFE can be thermally bonded together without using an adhesive, without applying a crushing force, or without applying a chemical treatment to the wet-stretched ePTFE. It should be apparent to one skilled in the art that thermally bonding wet-stretched ePTFE to itself or together with another article comprising wet-stretched ePTFE can result in a variety of configurations (e.g., joined, sealed, or laminated, etc.).
[0140] In certain illustrative embodiments, the expanded fluoropolymer material has a joint strength greater than the material strength of expanded polytetrafluoroethylene when at least a portion of the expanded fluoropolymer is sintered to itself in a joined configuration. In some embodiments, such expanded fluoropolymer can be produced by a process comprising the steps of (a) stretching a liquefied fluoropolymer material to form an expanded fluoropolymer material; and (b) sintering at least the portion of the expanded fluoropolymer material to itself to in the joined configuration to yield the expanded fluoropolymer material having the joint strength greater than the material strength of expanded polytetrafluoroethylene.
[0141] In certain illustrative embodiments, the expanded fluoropolymer has a bond strength at the joint greater than the bond strength of the material itself when at least a portion of the wet-stretched fluoropolymer is sintered to itself in a joined configuration, produced by a process comprising the steps of (a) stretching a wetted fluoropolymer material to form a wet-stretched fluoropolymer material; (b) removing the wetting agent from the wet-stretched fluoropolymer material while portions of the wet-stretched fluoropolymer material are in intimate contact with each other after stretching the wetted fluoropolymer material; and optionally (c) sintering the at least the portion of the expanded fluoropolymer material to itself to in the joined configuration to yield the wet-stretched fluoropolymer material having the bond strength at the joint greater than the bond strength of the material itself.
[0142] In accordance with an illustrative and non-limiting embodiment of the present invention, the methods described herein can be used to produce a product comprising at least one component of which is constructed from an expanded fluoropolymer material. In certain illustrative embodiments, the expanded fluoropolymer material comprises a liquid-impermeable, shape-formable wet-stretched fluoropolymer material having at least a portion of the wet-stretched fluoropolymer material sintered to itself in a joined configuration. In some embodiments, the joint strength of the expanded fluoropolymer material is at least 7 times greater than the joint strength of an expanded polytetrafluoroethylene material similarly configured.
[0143] In certain illustrative embodiments, the product is a medical device. In some embodiments, the medical device is a graft. In some embodiments, the medical device is a conduit or catheter. In some embodiments, the medical device is a bariatric liner.
[0144] In certain illustrative embodiments, the at least one component comprises a balloon. In certain illustrative embodiments, the at least one component comprises a stent covering.
[0145] In accordance with an illustrative and non-limiting embodiment of the present invention, the methods described herein can be used to produce a polymorph of polytetrafluoroethylene (PTFE). In certain illustrative embodiments, the polymorph of PTFE has an amorphous fraction characterized by a differential scanning calorimetry (DSC) thermogram exhibiting a phase transition of less than 20 degrees Celsius and a heat of fusion of less than 4.0 joules per gram. In certain embodiments, the polymorph of PTFE has an amorphous fraction characterized by a DSC thermogram exhibiting a phase transition of about 19.78 degrees Celsius and a heat of fusion of about 3.699 joules per gram.
[0146] In some embodiments, the polymorph is thermally bonded to itself without an adhesive. In some embodiments, the polymorph is thermally laminated to itself without an adhesive. In some embodiments, the polymorph is thermally sealed to itself without an adhesive. In sonic embodiments, the polymorph is thermally joined to itself.
[0147] In certain illustrative embodiments, the PTFE polymorph is a low crystallinity polymer as compared to PTFE, wherein PTFE is a high crystallinity polymer. In certain embodiments, the lower crystallinity polymer has a melting point as determined by DSC that is less than the melting point of the high crystallinity polymer.
[0148] Expanded fluoropolymers of the present invention (e.g., an expanded fluoropolymer thermally bonded to itself without an adhesive according to the methods of the present invention) can be used in numerous and varied applications ranging from bio-materials to industrial applications. Exemplary bio-materials applications include grafts (e.g., aortic grafts, vascular grafts, a dialysis graft, a peripheral graft, etc.), conduits used in the gastrointestinal tract (e.g., a gastrointestinal tube), covering for stents (e.g., a balloon expandable covered stent), a covering material for wound care, embolic filters, liners (e.g., an abdominal liner, a gastrointestinal liner, etc.), medical balloons for angioplasty stent deployment or medicinal delivery, products for soft tissue repair, products to reduce surgical adhesions or tissue attachment to medical devices these can include a pouch of pocket for a pacemaker or implanted insulin pump, the material can also be used as a space occupying device to maintain the shape of an organ or passageway during or after surgery, or as a patch (e.g., vessel or vascular path, hernia patch, etc.) or wrap. Exemplary and non-limiting industrial applications include, but are not limited to, a performance material for clothing or apparel including shoes, socks, pants, shirts, under garments, gloves, hats and outerwear (jackets, parkas etc . . . ) liners for small or large storage vessels, protective packaging or cases, or as a protective barrier layer for use with fabrics.
[0149] Expanded fluoropolymers produced according to the methods of the present invention provide a number of advantages over expanded fluoropolymers produced according to conventional methods. For example, expanded fluoropolymers of the present invention (e.g., an expanded fluoropolymer thermally bonded to itself without an adhesive) impart any or all of the following advantages compared to PFA or conventionally processed ePTFE: increased density, decreased or eliminated porosity, increased tensile strength, increased radial tensile strength, x-direction strength at the bonds between the expanded fluoropolymers greater than the x-direction strength of the expanded fluoropolymers themselves, decreased crystallinity and increased amorphousness, an ability to expand to a larger ratio, the ability to thermally bond to themselves without using or requiring an adhesive, crushing force or other chemical or physical surface treatment, such as chemical etching, plasma etching, corona treatment, and a lower friction force to overcome.
EXAMPLE 1
EFP Abdominal or Bariatric Liner
[0150] In accordance with an illustrative and non-limiting embodiment of the present invention, an expanded fluoropolymer produced according to the methods of the present invention is used to form a film useful as a bariatric or abdominal liner that can serve as a temporary protective barrier during or after surgery, for example, abdominal or pelvic surgery. The abdominal liner can he a multi-layered expanded fluoropolymer article, e.g., as substantially shown in
Pre-Clinical Study
[0151] A preclinical study to evaluate the efficacy of a thin film comprising an expanded fluoropolymer produced according to the methods of the present invention toward covering the bowel on the formation of adhesions between the sidewall and cecum and bowel in a rabbit model.
Sidewall Model
[0152] Rabbits were anesthetized with a mixture of 55 mg/kg ketamine hydrochloride and 5 mg/kg Rompum intramuscularly. Following preparation for sterile surgery, a midline laparotomy was performed. The cecum and bowel were exteriorized and digital pressure was exerted to create subserosal hemorrhages over all surfaces. The damaged intestine was then lightly abraded with 444 ply sterile gauze until punctate bleeding is observed. A 53 cm area of peritoneum and transversus abdominous muscle were removed on the right lateral abdominal wall. The thin film comprising expanded fluoropolymer produced according to the methods of the present invention was inlaid into the peritoneal cavity to cover a large portion of the bowel creating a barrier between the bowel and the defect. The cecum and bowel were then returned to their normal anatomic position. The incision was gently closed in two layers with 3-0 VICRYL suture. Care was taken not to damage the bowel.
[0153] After 14 days, the rabbits were anesthetized. After anesthesia, a small incision was made to remove the membrane. The animals were then terminated and the percentage of the sidewall injury area involved in adhesions was determined. In addition, the tenacity of the adhesions was scored using the system in Table 13 below.
TABLE-US-00013 TABLE 13 Adhesion Scoring System 0 No Adhesions 1 mild, easily dissectible adhesions 2 moderate adhesions; non-dissectible, does not tear the organ 3 dense adhesions; non-dissectible, tears organ when removed
Data Analysis
[0154] A reduction in the area of adhesions was analyzed by the Student's t-test. The statistical significance of the incidence was analyzed using a Chi-Square test. The tenacity scores were analyzed by analysis of variance of the ranks.
Results
[0155] The film comprising expanded fluoropolymer produced according to the methods of the present invention was easily handled and applied to the peritoneum. All animals did well during the post-operative interval. In four of five animals, the film stayed at the site of placement. In the last animal, the material had moved from the site of placement and balled around the omentum. No inflammation was observed in any animal. At necropsy, the film was easily removed in 3 animals. In one animal, the edge of the material was involved in the adhesions that formed and it was difficult to remove. In the animal where the film had moved from the site of placement, the film was not found until the animal was opened after euthanasia.
[0156] As is shown in Tables 14 and 15 below, the expanded fluoropolymer film significantly reduced the area, incidence and tenacity of adhesions.
TABLE-US-00014 TABLE 14 Adhesion Scores for Animals Implanted with PTFE TS 00586 Animal Number Area Score Tenacity Score 8201 0 0 8202 0 0 8205 0 0 8206 0 0 8211 10 1 Mean/SEM 2/1.0 3.0/0.59 *This is the Mean/SEM of the rank of the score.
TABLE-US-00015 TABLE 15 Adhesion Scores for Control Animals Animal Number Area Score Tenacity Score 8203 100 2 8204 50 2 8206 100 2 8207 100 3 8209 100 3 Mean/SEM 90/5.0 8/.068 *This is the Mean/SEM of the rank of the score.
[0157] The follow results of the pre-clinical study were notable: [0158] 97.78% reduction in adhesions compared to the control group (
EXAMPLE 2
EFP Vascular Grafts
Luminal Surface
[0164] In accordance with an illustrative and non-limiting embodiment of the present invention, an expanded fluoropolymer produced according to the methods of the present invention can be used to form a luminal surface of a vascular graft. Without being hound by theory, it is believed that the non-porous structure of the expanded fluoropolymers produce according to the methods of the present invention can prevent or reduce protein and fibrin deposition onto the luminal surface of vascular grafts, with the end result being decreased thrombus formation.
[0165] Feasibility studies using the expanded fluoropolymers produced according to the methods of the present invention as the inner most layer of a multi-layered, laminated vascular graft continue to be conducted. Preliminary SEM analysis and bench testing results performed on two such grafts are provided in Table 16 below.
TABLE-US-00016 TABLE 16 Preliminary SEM and Bench Testing Results for EFP base, .010 PTFE EFP base, monofilament ePTFE cPTFE tape vs tape graft as a cover vs graft as a cover graft type (TS-00586-52) (TS-00586-51) LTS (lbf) 50 53 RTS (lbf) 78 114 suture (lbf) 2.5 3 WEP *600+ *600+ (mmHg) wall .024 .031 thickness *Equipment limit reached
EXAMPLE 3
EFP Stent Cover
[0166] In accordance with an illustrative and non-limiting embodiment of the present invention, an expanded fluoropolymer produced according to the methods of the present invention can be used to form a stent cover. Without being bound by theory, it is believed that the non-porous structure of the expanded fluoropolymers produce according to the methods of the present invention can prevent or reduce protein and fibrin deposition on the inside surface of the stent cover. The expanded fluoropolymer(s) can be included in any stent, as would be appreciated by one of skill in the art upon reading the present specification.
[0167] Numerous modifications and alternative embodiments of the present invention will be apparent to those skilled in the art in view of the foregoing description. Accordingly, this description is to be construed as illustrative only and is for the purpose of teaching those skilled in the art the best mode for carrying out the present invention. Details of the structure may vary substantially without departing from the spirit of the present invention, and exclusive use of all modifications that come within the scope of the appended claims is reserved. Within this specification embodiments have been described in a way which enables a clear and concise specification to be written, but it is intended and will be appreciated that embodiments may be variously combined or separated without parting from the invention. It is intended that the present invention be limited only to the extent required by the appended claims and the applicable rules of law.
[0168] It is also to be understood that the following claims are to cover all generic and specific features of the invention described herein, and all statements of the scope of the invention which, as a matter of language, might be said to fall therebetween.