Method of oligomerization of olefins

Abstract

The present invention relates to a method of preparing -olefins by oligomerization of C.sub.2-C.sub.4 olefins. The method is carried out by oligomerization of C.sub.2-C.sub.4 olefins in the presence of a catalyst system comprising a transition metal source, an activator, which is an alkylaluminoxane, and a compound of formula (I), Ar.sup.1Ar.sup.2PN(R)PAr.sup.3Ar.sup.4 [formula I], wherein Ar.sup.1-4 are the same or different and are selected from substituted or unsubstituted C.sub.6-C.sub.10 aryl, R is selected from linear or branched C.sub.1-C.sub.4 alkyl, substituted or unsubstituted C.sub.6-C.sub.10 aryl, and substituted or unsubstituted C.sub.3-C.sub.10 cycloalkyl, wherein the oligomerization is carried out in a solvent, which is a bicyclic compound or a mixture of bicyclic compounds, preferably decalin. The claimed method provides a significant increase in the activity of the catalyst during the oligomerization process and, as a consequence, a reduction in the catalyst unit consumption, as well a reduction in the formation of polymer by-product.

Claims

1. A method for preparing -olefins by oligomerization of C.sub.2-C.sub.4 olefins in the presence of a catalyst system comprising a transition metal source, an activator, which is an alkylaluminoxane, and a compound of formula (I),
Ar.sup.1Ar.sup.2PN(R)PAr.sup.3Ar.sup.4[formula I], wherein Ar.sup.1-4 are the same or different and selected from substituted or unsubstituted C.sub.6-C.sub.10 aryl groups; R is selected from linear or branched C.sub.1-C.sub.4 alkyl group, substituted or unsubstituted C.sub.6-C.sub.10 aryl group, and substituted or unsubstituted C.sub.3-C.sub.10 cycloalkyl group; wherein the oligomerization process is carried out in a solvent, which is a bicyclic compound or a mixture of bicyclic compounds.

2. The method of claim 1, wherein the oligomerization is trimerization or tetramerization.

3. The method of claim 1, wherein C.sub.2-C.sub.4 olefin is ethylene.

4. The method of claim 1, wherein the transition metal is selected from the group comprising Ti, Zr, Hf, Ni, Cr, Fe, Co, Pd, Pt, and a combination thereof, preferably Cr.

5. The method of claim 1, wherein the transition metal source is a compound of the formula: MeX.sub.n, wherein Me is a transition metal selected from the group comprising Ti, Zr, Hf, Ni, Cr, Fe, Co, Pd, Pt, and a combination thereof, X is an organic or inorganic substituent, the same or different, and n is an integer from 1 to 6.

6. The method of claim 5, wherein X is an organic substituent having 1 to 20 carbon atoms and is selected from the group comprising alkyl, alkoxyl, carboxyl, acetylacetonate, amino, amido, and a combination thereof.

7. The method of claim 5, wherein X is an inorganic substituent and is selected from the group comprising halides, sulfates, and oxides of transition metals.

8. The method of claim 5, wherein the transition metal source is a Cr compound of the formula: CrXn, selected from the group comprising chromium (III) chloride, chromium (III) acetate, chromium (III) tris-ethylhexanoate, chromium (III) acetylacetonate, chromium (III) pyrrolide, chromium (II) acetate, or chromium (IV) dioxide dichloride.

9. The method of claim 1, wherein alkylaluminoxane is methylaluminoxane.

10. The method of claim 1, wherein the bicyclic compound is decalin (decahydronaphthaline).

11. The method of claim 10, wherein decalin may be cis-decalin, trans-decalin, or a mixture thereof.

12. The method of claim 10 or claim 11, wherein decalin comprises not more than 30 wt. % of impurities.

13. The method of claim 1, wherein the catalyst system further comprises a zinc compound.

14. The method of claim 13, wherein the zinc compound is selected from the group comprising alkylzinc compounds, arylzinc compounds, zinc amides, zinc oxygenates, zinc halides, and a combination thereof.

15. The method of claim 13, wherein the zinc compound is zinc metal (Zn).

16. The method of claim 14, wherein the zinc compound is diethylzinc.

17. The method of claim 1, wherein Ar.sup.1-4 are alkylaryl selected from the group comprising phenyl, tolyl, ethylphenyl, cumyl, and naphthyl.

18. The method of claim 1, wherein R is a radical selected from the group comprising methyl, ethyl, propyl, butyl, isobutyl, benzyl, allyl, cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl, and cyclononyl.

19. The method of claim 1, wherein the catalyst system is prepared by mixing the transition metal source and a compound of formula (I), wherein the mixing is carried out under ultrasonic exposure to prepare a homogenous mixture, followed by mixing the prepared mixture with alkylaluminoxane.

20. The method of claim 1, wherein the catalyst system is homogenous or heterogeneous.

21. The method of claim 19, wherein the mixing of the transition metal source and a compound of formula (I) is carried out in a solvent selected from the group comprising benzene, toluene, ethylbenzene, xylene, mesitylene, and cumene, preferably toluene and ethylbenzene.

22. The method of claim 19, further comprising adding a zinc compound when preparing the catalyst system.

23. The method of claim 1, wherein a ratio of aluminum:transition metal in the catalyst system is from 10:1 to 5000:1, preferably from 100:1 to 1000:1, most preferably from 200:1 to 500:1.

24. The method of claim 1, wherein a ratio of compound of formula (I):transition metal in the catalyst system is from 2:1 to 1:2, preferably from 1.5:1 to 1:1.5.

25. The method of claim 13, wherein a ratio of zinc:transition metal in the catalyst system is from 2:1 to 1000:1, preferably from 20:1 to 200:1.

26. The method of claim 1, comprising: mixing the catalyst system with a solvent, which is a bicyclic compound or a mixture of bicyclic compounds; feeding the resulting mixture to an oligomerization reactor; and feeding C.sub.2-C.sub.4 olefins to the oligomerization reactor and carrying out the oligomerization to prepare -olefins.

27. The method of claim 26, wherein the oligomerization reactor is selected from the group comprising a continuous reactor with a stirrer, a batch reactor, a plug-flow reactor, and a tubular reactor.

28. The method of claim 26, wherein the catalyst system is added for not more than 60 minutes, preferably 20 minutes, most preferably 5 minutes, after preparing thereof.

29. The method of claim 26, wherein the oligomerization is carried out at a temperature of from 0 to 160 C., preferably from 30 to 120 C., most preferably from 40 to 80 C.

30. The method of claim 26, wherein the time of oligomerization in the reactor is from 30 to 60 minutes.

31. The method of claim 26, further comprising feeding gaseous hydrogen.

32. The method of claim 10, wherein the content of aromatic hydrocarbons in decalin is not more than 2 wt. %.

33. The method of claim 10, wherein decalin is substantially free of tetralin.

34. The method of claim 1, wherein the prepared -olefins comprise C.sub.5-C.sub.40 -olefins.

35. The method of claim 34, wherein -olefins preferably contain hexene-1 and octene-1.

36. The method of claim 26, further comprising a step of cooling an effluent from the reactor to a temperature of from 100 C. to 20 C., preferably to a temperature of less than 95 C., less than 90 C., less than 85 C., less than 80 C., less than 75 C., less than 70 C., less than 65 C., less than 60 C., less than 55 C., less than 50 C., less than 45 C., less than 40 C., less than 35 C., less than 30 C., and less than 25 C.

37. The method of claim 36, wherein the effluent from the reactor is cooled to a temperature of from 20 to 25 C.

38. The method of claim 26, further comprising a step of treating the effluent from the reactor with a deactivation agent selected from the group comprising water, alcohols, amines, aminoalcohols, and a mixture thereof.

39. The method of claim 38, wherein the deactivation agent is selected from the group comprising methanol, ethanol, n-propanol, isopropanol, n-butanol, isobutanol, tert-butanol, 2-ethylhexanol, and a mixture thereof.

40. The method of claim 38, wherein the deactivation agent is selected from the group comprising ammonia, methylamine, dimethylamine, trimethylamine, ethylamine, diethylamine, triethylamine, tri-n-propylamine, diisopropylethylamine, tri-n-butylamine, piperazine, pyridine, ethylenediamine, diethylenetriamine, and a mixture thereof.

41. The method of claim 38, wherein the deactivation agent is selected from the group comprising ethanolamine, diethanolamine, triethanolamine, methyldiethanolamine, dodecyldiethanolamine, 1-amino-2-propanol, and a mixture thereof.

Description

BRIEF DESCRIPTION OF DRAWINGS

(1) FIG. 1 is a PMR spectrum of a PNP ligand for ethylene tetramerization.

DETAILED DESCRIPTION OF THE INVENTION

(2) The present invention relates to a method for preparing -olefins by oligomerization of C.sub.2-C.sub.4 olefins in the presence of a catalyst system in a solvent, which is a bicyclic compound or a mixture of bicyclic compounds.

(3) The bicyclic compound used as the solvent may be decalin or derivatives thereof. Decalin may be cis-decalin, trans-decalin or a mixture thereof, in any suitable ratio. Decalin may comprise not more than 30 wt. % of impurities, in particular inert to the catalyst, such as alkyl derivatives of decalin, in particular 1-methyldecalin, 2-methyldecalin, ethyldecalin, propyldecalin, butyldecalin, and other alkyl and isoalkyl derivatives; perhydroindane (bicyclo[4.3.0]nonane), perhydroazulene (bicyclo[5.3.0]decane) and alkyl derivatives thereof, and the like.

(4) The source of the above bicyclic compounds and their derivatives, in particular of decalin, perhydroindane, perhydroazulene, and derivatives thereof, is coal tar and heavy pyrolysis resin. They contain naphthalene, alkylnaphthalenes, indene, and azulene, which can be converted into the corresponding perhydro derivatives by exhaustive hydrogenation on noble metals. Tetrahydronaphthalene (tetralin) is a large-tonnage product of incomplete hydrogenation of naphthalene, used as a solvent for brown coal, and decalin is a by-product of the process of tetralin production.

(5) The present inventors have found for the first time that decalin promotes active oligomerization, namely trimerization and tetramerization, in the presence of MAO.

(6) The claimed method of oligomerization of olefins comprises reaction of alpha-olefin-containing raw materials under oligomerization conditions, in the presence of a catalyst comprising a transition metal source, a PNP ligand and an activator, which is alkylaluminoxane. Said reaction runs in decalin.

(7) The claimed method may be used for different processes of oligomerization, including for oligomerization of olefins, for example, for trimerization and tetramerization of C.sub.2-C.sub.4 olefins, for example, ethylene.

(8) As shown above, the oligomerization process is carried out in the presence of a catalyst comprising a transition metal source, a PNP ligand and an activator, which is alkylaluminoxane.

(9) The transition metal may be Ti, Zr, Hf, Ni, Cr, Fe, Co, Pd, Pt, or the like, or a combination thereof. Preferably, the transition metal is chromium (Cr), titanium (Ti), or zirconium (Zr). Most preferably, the transition metal is chromium (Cr).

(10) The transition metal source may be an organic and/or inorganic compound. The oxidation degree of a metal depends on the metal used. In general, the metal source is a compound of the general formula MeX.sub.n, wherein Me is a transition metal selected from the group consisting of Ti, Zr, Hf, Ni, Cr, Fe, Co, Pd, Pt, and the like, and a combination thereof, X may be the same or different, and n is an integer from 1 to 6. X may be an organic or inorganic substituent. When X is an organic substituent, it may contain from 1 to 20 carbon atoms and may be alkyl group, alkoxyl group, carboxyl group, acetylacetonate group, amino group, amido group, or the like. Suitable inorganic substituents of X include halides, sulfates, oxides and other of transition metals.

(11) Examples of the transition metal source include, but are not limited to, titanium (III) chloride, titanium (IV) chloride, titanium (IV) butoxide, titanium (IV) isopropoxide, zirconium (IV) chloride, zirconium (IV) oxychloride, zirconium (IV) butoxide, cobalt (II) ethylhexanoate, hafnium (IV) chloride, nickel (II) chloride, iron (III) chloride, cobalt (II) ethylhexanoate, palladium (II) chloride, hydrogen hexachloroplatinate (IV), etc.

(12) When the transition metal is chromium, the chromium source may be an organic and/or inorganic chromium compound. The oxidation degree of chromium in compounds may vary and be equal to 0, +1, +2, +3, +4, +5, and +6. Generally, the chromium source is a compound of the general formula CrX.sub.n, wherein X may be the same or different, and n is an integer from 1 to 6. X may be an organic or inorganic substituent. When X is an organic substituent, it may contain from 1 to 20 carbon atoms and may be alkyl group, alkoxyl group, carboxyl group, acetylacetonate group, amino group, amido group, or the like. Suitable inorganic substituents of X include halides, sulfates, chromium oxides, and the like. Examples of the chromium source include chromium (III) chloride, chromium (III) acetate, chromium (III) tris-ethylhexanoate, chromium (III) acetylacetonate, chromium (III) pyrrolide, chromium (II) acetate, chromium (IV) dioxide dichloride (CrO.sub.2Cl.sub.2), and the like.

(13) The PNP ligand being a component of the catalyst system can be represented by the general formula:
Ar.sup.1Ar.sup.2PN(R)PAr.sup.3Ar.sup.4,

(14) wherein

(15) Ar.sup.1-4 may be the same or different and are substituted or unsubstituted C.sub.6-C.sub.10 aryl groups, such as phenyl, tolyl, ethylphenyl, cumyl, naphthyl, most preferably alkylaryl without an o-substituent, in particular, p-tolyl, m-ethylphenyl, or unsubstituted phenyl;

(16) R is linear or branched C.sub.1-C.sub.4 alkyl, substituted or unsubstituted C.sub.6-C.sub.10 aryl, substituted or unsubstituted C.sub.3-C.sub.10 cycloalkyl, such as methyl, ethyl, propyl, butyl, isobutyl, benzyl, allyl, most preferably alkyl having one -branch, for example isopropyl, sec-butyl, cycloalkyl, such as cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl, cyclononyl, and the like.

(17) The PNP ligand can be prepared by reacting alkylamine and diarylchlorophosphine(s) in the presence of a base.

(18) The activator used for alkylation of the transition metal to form a metal alkyl and a counterion (aluminate) for a cationic transition metal complex is an unmodified alkylaluminoxane. An unmodified methylaluminoxane (aluminoxane) is preferred. It is more preferable to use MAO in the form of a 10% solution in toluene. However, based on data in the literature, the use of other aluminoxanes (ethylaluminoxane, isobutylaluminoxane) is less preferred due to their lower ionizing capacity (D.B. Malpass, Commercially Available Metal Alkyls and Their Use in Polyolefin Catalysts, p. 13 (part 1.5.4), in: Handbook of Transition Metal Polymerization Catalysts Ed. by Ray Hoff and Robert T. Mathers 2010 John Wiley & Sons, Inc.)

(19) The catalyst system comprising a chromium source, a PNP ligand and alkylaluminoxane can be prepared by mixing the chromium source and the PNP ligand, wherein the mixing is preferably carried out under ultrasonic exposure to homogenize the catalyst system, followed by mixing the resulting mixture with alkylaluminoxane. The organometallic catalyst may be homogeneous or heterogeneous.

(20) The ratio of the components of the catalyst system may vary. The molar ratio of transition metal:PNP ligand:aluminum can be 1:0.1-10:10-5000, preferably 1:0.5-2:100-1000, more preferably 1:0.6-1.5:200-500.

(21) The mixing of the metal source and the PNP ligand can be carried out in solvents dissolving both the metal source, in particular chromium, and the ligand. Said solvents may be both aromatic and aliphatic, as well as cycloaliphatic solvents, including benzene, toluene, ethylbenzene, xylene, mesitylene, cumene, and other aromatic solvents; however, it is more preferable to use toluene or ethylbenzene since the catalyst prepared by using these solvents, exhibit greater stability.

(22) The organometallic catalyst prepared by the above-indicated method is preferably stored at a low temperature, preferably not higher than minus 78 C., to prolong its storage life.

(23) The catalyst concentration in said solvents is from 1 to 15 mol/L, preferably from 3 to 10 mol/L, more preferably from 5 to 8 mol/L.

(24) The catalyst system obtained by the above-described method, before being fed to the oligomerization reactor, is mixed with a solvent, which is a bicyclic compound or a mixture of bicyclic compounds, for example decalin, in a weight ratio of organometallic catalyst:solvent of from 1:100 to 1:10000, preferably from 1:150 to 1:5000, most preferably from 1:200 to 1:2000.

(25) Along with the above-indicated components of the catalyst system, the oligomerization process can further involve one or more zinc compounds. They may be added to the catalyst system directly at the step of preparing the system or separately to an oligomerization reactor. The zinc compound may be used as an activator of the catalytic center, in particular chromium. The zinc compound may be zinc (Zn (0)), alkylzinc, in particular dialkylzinc, for example dimethylzinc, diethylzinc, dibutylzinc; arylzinc, for example, diphenylzinc, ditolylzinc; zinc amides, for example zinc pyrrolide or zinc-porphyrin complexes, for example zinc-5,10,15,20-tetraphenylporphyrin, zinc oxygenates, for example, zinc formate, zinc acetate, zinc 2-ethylhexanoate; zinc halides, for example, anhydrous zinc chloride; or a combination thereof. It is preferred to use zinc compounds soluble in the solvents used in the oligomerization process, in particular, in decalin. The zinc compound may be used in the form of a solution.

(26) The ratio of the components in the catalyst system, including the zinc compound, may vary. The molar ratio of aluminum:transition metal may be from 10:1 to 5000:1, from 100:1 to 1000:1, most preferably from 200:1 to 500:1. The molar ratio of ligand:transition metal may vary from 2:1 to 1:2, preferably from 1.5:1 to 1:1.5. The molar ratio of zinc:transition metal may vary and ranges from 2:1 to 1000:1, preferably 20:1 to 200:1.

(27) The time between the preparation of the catalyst system and the feeding thereof to the reactor should not exceed 60 minutes, preferably 20 minutes, most preferably 5 min. It is preferred to limit the time between the preparation of the catalyst system and the feeding thereof to the reactor, thereby minimizing the formation of a large amount of a polymer.

(28) The raw materials for preparing -olefins may be olefins, such as ethylene (ethene), propylene (propene), and butene (butene). In a preferred embodiment, the starting olefin is ethylene.

(29) The oligomerization process of olefins is carried out to obtain higher olefins. Industrially important processes are processes for preparing alpha-olefins (-olefins). -Olefins are compounds with a carbon-carbon double bond (CC) at the alpha position. -Olefins prepared in the oligomerization process can include various C.sub.5-C.sub.40 olefins and a mixture thereof. For example, -olefins prepared in the oligomerization process may be pentene-1, hexene-1, heptene-1, octene-1, nonene-1, decene-1, undecene-1, dodecene-1, higher -olefins, or a mixture thereof. Preferably, the oligomerization process is a process of tri- and/or tetramerization of ethylene to form hexene-1 and/or octene-1.

(30) The claimed method for preparing -olefins by oligomerization of C.sub.2-C.sub.4 olefins is carried out in any reactor known in the art. The catalyst system mixed with a solvent, which is a bicyclic compound or a mixture of bicyclic compounds, in particular decalin, is fed to the reactor. The reactor is then filled with C.sub.2-C.sub.4 olefins and optionally with hydrogen as a diluent, and then the oligomerization process is carried out to obtain -olefins.

(31) The oligomerization process may be carried out in any reactor known in the art. Suitable reactors include a continuous reactor with a stirrer, a batch reactor, a plug-flow reactor, and a tubular reactor. The reactor may be a gas-liquid reactor, for example, an autoclave with a stirrer, a bubble column (bubble reactor) with co- or countercurrent gas and liquid flows, or a bubbling gas-lift reactor.

(32) In a preferred embodiment of the method, when the oligomerization process is trimerization and tetramerization of C.sub.2-C.sub.4 olefins, in particular ethylene, to produce hexene-1 and octene-1, a pressure of C.sub.2-C.sub.4 olefins may vary from 1 to 200 bar, preferably from 5 to 100 bar, most preferably from 20 to 60 bar. It is preferred to elevate the pressure to increase the rate of oligomerization.

(33) The temperature of the oligomerization process may range from 0 to 160 C., preferably from 30 to 120 C. It is most preferred to maintain the temperature in the reactor between 40 and 80 C. At this temperature a polymer by-product, in particular polyethylene, is precipitated from the solution and discharged from the reactor in the form of slurry, and the catalyst system is the most active and selective. The oligomerization process at a higher temperature (above 80 C.) can lead to deactivation of the catalyst system.

(34) In accordance with the claimed method, the reaction time may vary. The reaction time may be defined as a residence time of raw materials and a solvent in the oligomerization reaction zone. In the case of a continuous flow reactor, the reaction time can be defined as an average residence time. The reaction time may vary depending on olefins used as raw materials, a reaction temperature, pressure and other process parameters. In embodiments of the method, the reaction time does not exceed 1 day. The reaction time may be less than 12 hours, less than 6 hours, less than 3 hours, less than 2 hours, less than 1 hour, less than 30 minutes, less than 15 minutes, less than 10 minutes, less than 5 minutes, less than 3 minutes, less than 2 minutes, less than 1 minute, less than 30 sec, less than 15 sec, less than 10 sec, less than 5 sec, less than 3 sec, and less than 1 sec. The reaction time of from 30 min to 60 min is most preferred.

(35) According to the claimed method, the olefin and the catalyst system can contact with hydrogen that is fed to the oligomerization reactor and is used as a diluent. Hydrogen can accelerate the oligomerization reaction and/or increase the activity of the organometallic catalyst. Further, hydrogen can reduce the amount of the formed polymer by-product and limit its deposition on the walls of the equipment.

(36) The solvent in the oligomerization process is a bicyclic compound, namely decahydronaphthalene (decalin). Decalin purified from tetralin impurities with the content of aromatic compounds of not more than 2 wt. % is preferred. Decalin may be a mixture of cis- and trans-decalin in various ratios. The weight ratio of the cis- and trans-decalin may range from 1:99 to 99:1, preferably from 2:98 to 98:2, most preferably from 3:97 to 50:50.

(37) Decalin can be purified from tetralin impurities by the treatment with sulfuric acid according to the method disclosed, for example, in application US 2007/0156003.

(38) The oligomerization process of olefins is carried out in the absence of water and oxygen. The presence of water and oxygen can cause hydrolysis and oxidation of low-oxidation state organometallic compounds, resulting in complete or partial deactivation of the catalyst.

(39) According to the claimed method, the effluent from the reactor may contain the organometallic catalyst, a variety of products, by-products, the solvent, and polymers formed during oligomerization.

(40) The effluent from the reactor can be treated with a deactivation agent. Suitable deactivation agents known in the art include water, alcohols, amines, amino alcohols, and a mixture thereof. The alcohols include methanol, ethanol, n-propanol, isopropanol, n-butanol, isobutanol, tert-butanol, 2-ethylhexanol, and a mixture thereof. Examples of suitable amines include ammonia, methylamine, dimethylamine, trimethylamine, ethylamine, diethylamine, triethylamine, tri-n-propylamine, diisopropylethylamine, tri-n-butylamine, piperazine, pyridine, ethylenediamine, diethylenetriamine, and a mixture thereof. Examples of aminoalcohols include ethanolamine, diethanolamine, triethanolamine, methyldiethanolamine, dodecyldiethanolamine, 1-amino-2-propanol, and a mixture thereof. According to the claimed method, the deactivation agent can be water.

(41) The effluent from the reactor optionally can be cooled by passing thereof, for example, through a heat exchanger. The cooling of the effluent from the reactor may include mixing the hot effluent from the reactor with a cooled effluent. The cooling of the effluent from the reactor is carried out to a temperature of from 100 C. to 20 C., preferably to a temperature of less than 95 C., less than 90 C., less than 85 C., less than 80 C., less than 75 C., less than 70 C., less than 65 C., less than 60 C., less than 55 C., less than 50 C., less than 45 C., less than 40 C., less than 35 C., less than 30 C., or less than 25 C. The effluent from the reactor may be cooled to ambient temperature, for example, from 20 to 25 C. The temperature to which the effluent from the reactor is cooled is so as to allow the control of the polymer precipitation from the solvent. Thus, the effluent from the reactor can be cooled in a decanter, from which polyolefin slurry is periodically discharged.

(42) This method allows a significant increase in the catalyst activity (up to 78,000 g of olefins/one g of metal per hour) during the oligomerization process and, as a consequence, reduces the catalyst unit consumption. When the system capacity, in terms of olefins, is 1000 kg/h, the catalyst consumption is 12 to 27.8 g/h based on transition metal. Furthermore, the method allows an increase in the efficiency of the process of preparing hexene-1 and octene-1 and a reduction in the formation of a polymer by-product (down to 1% of the total yield of the reaction products).

(43) The invention is further illustrated by the following examples.

(44) The used raw materials were methylaluminoxane (a 10% solution in toluene), phosgene (a 10% solution in toluene), chromium (III) acetylacetonate (Aldrich), cyclohexylamine, and diphenylphosphine (Acros Organics).

(45) The PNP-ligand (PMR spectrum is presented in FIG. 1) was synthesized from cyclohexylamine and diphenylchlorophosphine by the procedure described in [Cooley N. A., Green S. M., and Wass D. F. Nickel Ethylene Polymerization Catalysts Based on Phosphorus Ligands//Organometallics 2001, Vol. 20, P. 4769-4771].

(46) Diphenylchlorophosphine was prepared from diphenylphosphine and phosgene as disclosed in [Henderson W. A. Jr., Buckler S. A., Day N. E., Grayson M. Preparation of Alkyl Chlorophosphines//J. Org. Chem. 1961. Vol. 26. P.4770-4771],

Example 1. Synthesis of a PNP-Ligand

(47) Diphenylchlorophosphine (8.5 g, 38.6 mmol, 2 eq.) was fed into a flask with a solution of cyclohexylamine (1.9 g, 19.3 mmol, 1 eq.) and triethylamine (3.9 g, 38.5 mmol, 2 eq.) in 100 mL of dichloroethane under a nitrogen atmosphere. The reaction mixture was stirred for 20 hours at room temperature. Water in an amount of 50 ml was added, stirred, and the organic layer (solution in dichloroethane) was separated in a separating funnel and then filtered through Celite 500. After that, the solvent was evaporated, 30 ml of methanol was added to the resulting honey-like mass and cooled until white crystals are precipitated. The precipitate was filtered off and dried at room temperature under vacuum. The resulting compound is a white crystalline solid (3.7 g). .sup.31P NMR analysis: 50.7 ppm, br.; .sup.1H NMR, see FIG. 1.

Example 2. Oligomerization with MAO in Decalin

(48) The PNP-ligand (179.8 mg, 0.385 mmol) and chromium (III) acetylacetonate (67.1 mg, 0.192 mmol) were mixed in toluene (5 ml) under ultrasonic exposure. MAO in toluene (25.5 mL, 38.5 mmol) was added, and immediately after mixing, the blue-green solution was used as a source of the active catalyst. The catalyst in an amount of 3 ml was taken and mixed with 150 ml of dry decalin in a nitrogen box.

(49) The resulting mixture was transferred to an evacuated 250 ml Parr reactor by a differential pressure at 50 C. Hydrogen (1 atm) was fed to the reactor, and its content was thermostated under stirring (800 rpm) due to the circulation of the coolant inside the jacket of the reactor to stabilize temperature within a range of 57 to 62 C. Then, ethylene was continuously dosed to the reactor to the total pressure of up to 31 bar, and the dosing was continued at a constant pressure as the gas was depleted (60-70 C.), under stirring the reaction mass. After 30-60 min, the dosing of ethylene was stopped, the mixture was cooled to 40 C. and degassed, and the reaction mixture was discharged through a lower ball valve. The liquid phase was analyzed (GC, GC-MS).

(50) The results of the experiment are given in Table 1.

Example 3. Oligomerization with MAO in Decalin Purified from Tetralin Impurities

(51) The process was carried out as described in Example 2, except that the duration of the process was 15 minutes, and the solvent was decalin purified from tetralin impurities.

(52) Decalin was purified as follows.

(53) Technical decalin (1.5 L) containing impurities of ethylbenzene (0.5%), butylbenzene (0.5%), indane (0.5%), and tetralin (6%) was mixed with a high-grade sulfuric acid (96% solution, 1 L) and stirred vigorously at room temperature for 24 hours. After that, the stirring was stopped, and the resulting mixture was allowed to separate. The upper layer was separated, washed in a separatory funnel with 500 mL of a 10% aqueous solution of sodium hydrogencarbonate 2 times and with distilled water to pH 6-7. Then, the organic phase was dried over sodium sulfate and distilled over molten sodium.

(54) The results of the experiment are given in Table 1.

Example 4. Oligomerization with MAO in Decalin Purified from Tetralin Impurities with a Reduced Toluene Content

(55) The decalin used in this example was purified according to the procedure described in Example 3.

(56) The PNP-ligand (179.8 mg, 0.385 mmol) and chromium (III) acetylacetonate (67.1 mg, 0.192 mmol) were mixed in toluene (5 ml) under ultrasonic exposure. MAO in toluene (25.5 mL, 38.5 mmol) and then decalin (20 mL) were added, and 20 mL of toluene was distilled off under vacuum. The blue-green solution was used as a source of the active catalyst. The catalyst in an amount of 3 mL was taken and mixed with 150 ml of dry decalin in a nitrogen box.

(57) The oligomerization process was carried out as described in Example 2.

(58) The results of the experiment are given in Table 1.

Example 5. Oligomerization with MAO in Toluene (Comparative Experiment According to Example 2 of the Prototype WO2004/056479)

(59) The process was carried out as described in Example 2 according to WO2004/056479, except that the used solvent was toluene, and the ligand was a compound of the formula: (phenyl)2PN(cyclohexyl)-P(phenyl)2.

(60) A solution of 29.0 mg of the PNP ligand (0.073 mmol) in 5 mL of toluene was fed into a Schlenk flask containing 12.4 ml of a solution of CrCl3 (tetrahydrofuran)3 (0.033 mmol) in 15 mL of toluene. The resulting solution was stirred for 5 minutes at room temperature and transferred to a 250 ml Parr reactor containing a mixture of toluene and MAO (9.9 mmol), at 80 C. Then ethylene was dosed to the reactor. The temperature in the reactor was maintained at 85 C., and the pressure of ethylene was maintained at 30 bar. The reaction mass was stirred at 1100 rpm. After 60 minutes, the dosing of ethylene was stopped, and the reaction mass was cooled to 40 C. and degassed. The reaction mass was treated with a deactivation agent, which was ethanol and a 10% aqueous solution of hydrochloric acid (HCl). A sample of the resulting mixture was dried over anhydrous sodium sulfate and analyzed by gas chromatography (GC). In the assay, heptane was used as an internal standard.

(61) The results of the experiment are given in Table 1.

Example 6. Oligomerization with MAO in Cyclohexane (Comparative Experiment According to Example 22 of the Prototype WO2004/056479)

(62) The process was carried out as described in Example 22 according to WO2004/056479, except that the chromium (III) acetylacetonate was introduced into the reaction system in the form of a solution in toluene since it is insoluble in cyclohexane. The used ligand was a compound of the formula: (phenyl).sub.2PN(cyclohexyl)-P(phenyl).sub.2.

(63) 5.8 mg of a solution of the PNP ligand (0.014 mmol) obtained in Example 1 in 10 ml of cyclohexane was fed into a Schlenk flask comprising a solution of 3.5 mg of chromium (III) acetylacetonate (0.01 mmol) in 10 mL of toluene. The resulting solution was stirred for 5 minutes at room temperature. Then, the solution and a 7% solution of MAO (2 mmol) in toluene were added by a differential pressure to a 250 ml Parr reactor containing cyclohexane (170 ml), at 45 C. Then ethylene was dosed to the reactor. The temperature in the reactor was maintained at 45 C., the pressure of ethylene was maintained at 45 bar, under stirring the reaction mass. After 39 minutes, the dosing of ethylene was stopped, and the reaction mass was cooled to 40 C. and degassed. The reaction mass was treated with a deactivation agent, which was ethanol and a 10% aqueous solution of hydrochloric acid (HCl). A sample of the resulting mixture was dried over anhydrous sodium sulfate and analyzed by gas chromatography (GC). In the assay, heptane was used as an internal standard.

(64) The results of the experiment are given in Table 1.

Example 7. Oligomerization with MAO in the Presence of Diethylzinc in Decalin Purified from Tetralin Impurities

(65) The PNP-ligand (89.9 mg, 0.192 mmol) and chromium (III) acetylacetonate (67.1 mg, 0.192 mmol) were mixed in toluene (5 ml) under ultrasonic exposure. MAO in toluene (40 mL, 60.4 mmol) was added, and immediately after mixing, the blue-green solution was used as a source of the active catalyst. The catalyst in an amount of 3 mL was taken and mixed with 150 mL of a dry solvent (decalin), and a 1M solution of diethylzinc in hexane (0.38 mL, 0.38 mmol) was added in a nitrogen box.

(66) Then the mixture was transferred to an evacuated 250 ml Parr reactor by a differential pressure at 45 C. Hydrogen (1 atm) was dosed to the reactor, and its content was thermostated under stirring (800 rpm) due to the circulation of the coolant inside the jacket of the reactor to stabilize temperature within a range of 43 to 47 C. Then, ethylene was continuously dosed to the reactor to the total pressure of up to 41 bar, and the dosing was continued at a constant pressure as the gas was depleted (45-50 C.), under stirring the reaction mass. After 30 min, the dosing of ethylene was stopped, the mixture was cooled to 30 C. and degassed, and the reaction mixture was discharged through a lower ball valve. The liquid phase was analyzed (GC).

(67) Decalin was purified according to the procedure disclosed in Example 3.

(68) The results of the experiment are given in Table 1.

Example 8. Oligomerization with MAO in Decalin Purified from Tetralin Impurities, Using a Catalyst System with a 2-Hour Storage Time

(69) The process was carried out as described in Example 2 except that the catalyst system was kept under nitrogen atmosphere for 2 hours before mixing with the solvent.

(70) The results of the experiment are given in Table 1.

Example 9. Synthesis of Butylindene

(71) Butyllithium (2.5 M, 300 ml) was added to a solution of indene (87 g, 0.75 mol) in THF (216 g) and cyclohexane (400 g) under ice-cooling for 2 hours, warmed to room temperature over 1 h, then a solution of butylbromide (102.8 g, 0.75 mol) in cyclohexane (100 g) was added for 15 min, heated for 3 hours at 50 C., and then stirred for 16 hours at 25 C. A saturated NaCl solution (200 mL) was then added to the mixture and shaken in a separatory funnel, the organic layer was separated, washed with water (200 ml), then again the saturated NaCl solution (200 ml of) was added, and was dried over sodium sulfate. The organic layer was evaporated in a rotary evaporator at 300 mbar/65 C., the residue was distilled under vacuum, and the main fraction with a boiling point of 120-130 C./20 mbar was collected. The yield was 77 g, purity was 79%, and the impurities (GC-MS) were dibutylindenes.

Example 10. 1-Butyl-perhydroindane in Decalin. Mixture of Isomers

(72) The product of Example 9 was mixed with a purified decalin (100 g) and hydrogenated at 250-270 C. and 100-120 bar on a 5% Pt-10% PdC catalyst (10 g) for 72 hours. The resulting product comprised less than 2% of aromatic compounds (GC-MS). The catalyst was filtered off, washed with 50 ml of decalin, the mixed solvent was subjected to purification with sulfuric acid as described above in Example 3, and then the mixture was distilled over sodium under vacuum. The mixture contained four diastereomeric pairs of butyl-perhydroindanes in an amount of: 5.4%; 10.0%; 1.1%; and 3.6%, in the decalin solution (the total amount of decalin74% PID area).

Example 11. Perhydroindane

(73) Indene (250 ml) was hydrogenated at 250-270 C. and 100-120 bar on a 5% Pt-10% PdC catalyst (10 g) for 72 hours. The purity of the obtained product was 97% (a mixture of cis- (69.2%) and trans- (26.1%) isomers). The product was subjected to purification with sulfuric acid and distilled similarly to decalin and butylperhydroindane.

Example 12. Oligomerization in Mixed Solvents

(74) The PNP-ligand (89.9 mg, 0.192 mmol) and chromium (III) acetylacetonate (67.1 mg, 0.192 mmol) were mixed in ethylbenzene (4 ml) under ultrasonic exposure. MAO in toluene (25.5 mL, 38.5 mmol) and diethylzinc (0.4 mL) was added, and immediately after mixing, the blue-green solution was used as a source of the active catalyst. The catalyst in an amount of 3 mL (corresponds to 1 mg of chromium) was taken and mixed with 150 mL of the dry solvent in a nitrogen box. The remaining part of the catalyst solution was frozen at (196) C., and unfreezed to 0 C. immediately before the synthesis.

(75) The resulting mixture was transferred to an evacuated 250 ml Parr reactor by a differential pressure at 50 C. Hydrogen (1 atm) was dosed to the reactor, and its content was thermostated under stirring (800 rpm) due to the circulation of the coolant inside the jacket of the reactor to stabilize temperature within a range of 57 to 62 C. Then, ethylene was continuously dosed to the reactor to the total pressure of up to 31 bar, and the dosing was continued at a constant pressure as the gas was depleted (60-70 C.), under stirring the reaction mass. After 30-60 min, the dosing of ethylene was stopped, and the reaction mixture was discharged, while being degassed, through a lower ball valve. Silicagel in an amount of 5 g was added and kept for 30 minutes. The liquid phase was analyzed (GC, GC-MS).

(76) The results of the experiments are shown in Table 2 (Examples 12.1-12.4).

(77) TABLE-US-00001 TABLE 1 Results of the experiments on ethylene oligomerization Catalyst Calculated activity, catalyst olefin (g)/ consumption, C.sub.6-1 + Toluene Tetralin chromium chromium C.sub.6-1 Purity, C.sub.8-1 Purity, C.sub.8-1 content, content, (g), per (g)/olefin (t), yield, C.sub.6, yield, C.sub.8, selectivity, C.sub.8/ Polymer, Example Solvent % % hour per hour g % g % % C.sub.6 g 2 Decalin 1.4 6.0 5700 175 0.84 73.0 2.55 98.3 59 3.0 0.3 3 Decalin 1.8 0.04 36000 27.8 1.8 83.5 4.05 99.3 65 2.3 0.08 4 Decalin 0.5 0.04 42000 23.8 4.0 80.5 12.0 99.3 75 3.0 0.2 5 Toluene 2300 435 0.46 83.2 1.38 97.0 80 3.0 0.3 (comparative, according to the prototype) 6 Cyclohexane 6.5 600 1670 0.29 68.6 0.34 91.5 ND 1.2 0.5 (comparative, according to the prototype) 7 (with ZnEt.sub.2) Decalin 1.8 0.04 78000 12.8 2.86 83.0 9.2 99.5 85 3.2 0.15 8 (catalytic Decalin 1.8 0.04 6000 167 0.88 78.0 2.68 99.0 ND 3.0 12.0 system with 2-hour storage time

(78) TABLE-US-00002 TABLE 2 Results of the experiments on ethylene oligomerization in bicyclic solvents Solvent Content of Activity, Butyl aromatic olefin C6-1 C8-1 C8-1 Reaction Perhydroindane, Decalin, perhydroindane, compounds, (g)/chromium yield, yield, purity, C8/ Example time, min % % % % (g), per hour g g % C6 12.1 60 18.8 70.7 0 1.9 7500 1.72 6.16 97.7 3.6 12.2 45 83.0 10.6 0 3.3 1100 0.25 0.61 92.0 2.4 12.3 60 14.3 61.6 17.2 2.3 1100 0.35 0.84 94.0 2.4 12.4 40 4.5 70.7 4.3 4.1 12500 5.03 11.07 98.4 2.2

(79) The results of the experiments show the advantage of using decalin as a solvent in the oligomerization process. As can be seen from Table 1, the activity of the catalyst system during the oligomerization process in decalin reaches 42,000 g of olefins per 1 g of chromium per hour (Table 1, Example 4), whereas the activity of the catalyst system during the oligomerization process in cyclohexane or toluene reaches only 600 and 2,300 g of olefins per 1 g of chromium per hour, respectively (Examples 5 and 6). The addition of alkylzinc also has a positive effect on the activity of the catalyst system (Example 7, Table 1). In such a case, the activity of the catalyst system reaches 78,000 g of olefins per 1 g of chromium per hour.

(80) A reduction in the catalyst consumption also should be noted. When the system capacity, in terms of olefins, is 1000 kg/h, the consumption of the catalyst is not more than 12.8 to 27.8 g/h based on elemental chromium.

(81) It should be also noted that when the oligomerization process is carried out in decalin, the formation of by-products reduces to 0.08 g (Example 3, Table 1). In addition, as can be seen from the obtained data, when the content of decalin in the solvent is less than 70 wt. %, the activity of the catalyst and the yield of the product drop sharply (Table 2, Examples 12.2 and 12.3); therefore, as the content of decalin in the solvent increases and the content of impurities in the solvent decreases, the activity of the catalyst increases (Table 1, Examples 2, 3, and 4).

(82) Thus, it can be concluded that the use of a bicyclic compound or a mixture of bicyclic compounds, in particular decalin, results in an increased catalyst activity, and a reduced formation of a polymer by-product.