Non-PVC film and non-PVC film laminate

Abstract

A non-PVC film and film laminate includes a first layer including a polyurethane, a polyurethane-acrylic copolymer, a polyurethane-acrylic blend, and a urethane-acrylic hybrid polymer; and a second layer including a non-polyvinylchloride (non-PVC) based polymer. The film and laminate may be suitable for use in marketing, advertising campaigns, particularly outdoor or other environment impacted promotions, and safety applications. The film and laminate may be transparent, translucent, clear or have other desirable optical properties.

Claims

1. An optically transparent protective film comprising: a top layer; a bottom layer having a first surface and a second surface, wherein a surface area of the first surface is substantially coextensive and in continuous physical contact with the top layer; and an adhesive layer in contact with the second surface of the bottom layer, the adhesive layer including a pressure sensitive adhesive; wherein the top layer comprises at least 85.56% of a material selected from the group consisting of a polyurethane-acrylic copolymer and a urethane-acrylic hybrid polymer; and wherein the bottom layer is comprised of a non-polyvinylchloride (non-PVC) based polymer, wherein the film (i) passes an accelerated weathering test, (ii) exhibits a gloss at 60 degrees greater than 90, and (iii) exhibits a tensile elongation greater than 200%, wherein passing the accelerated weathering test requires that after weathering, the film not exhibit any visible changes after 2,000 hours and E is less than 10.

2. The film as recited in claim 1, wherein the non-PVC based polymer is selected from the group consisting of an emulsion based polymer, a solvent based polymer, and an extruded polymer.

3. The film as recited in claim 1, wherein the non-PVC based polymer is an acrylic polymer.

4. The film as recited in claim 1, further including at least one additive in at least one of the top and bottom layers of the film.

5. The film as recited in claim 4 wherein the at least one additive is selected from the group consisting of UV stabilizing agents, free-radical scavengers, cross-linking agents, thickeners, flow and leveling agents, rheology modifiers, surfactants, defoamers, dispersants, wetting agents, dyes, pigments, co-solvents, water, isopropyl alcohol and combinations thereof.

6. The film as recited in claim 1, wherein the material is a polyurethane-acrylic copolymer.

7. The film as recited in claim 1, wherein the material is created by a process comprising: forming an acrylic polymer in the presence of a polyurethane dispersion.

8. The film as recited in claim 1, wherein the material is created from a waterborne dispersion produced by a process comprising: forming a polyurethane prepolymer; adding acrylic monomers to the polyurethane prepolymer; and simultaneously polymerizing the acrylic monomers and the polyurethane prepolymer.

9. A transparent film laminate comprising: a top layer; a bottom layer having a first surface and a second surface, wherein a surface area of the first surface is in continuous physical contact with the top layer; an intermediate layer in continuous physical contact with the second surface bottom layer; a substrate layer in physical contact with the intermediate layer, and wherein the top layer comprises a material selected from the group consisting of a polyurethane-acrylic copolymer and a urethane-acrylic hybrid polymer, and the top layer has a thickness in a range from 0.5 mil (12.7 microns) to 5 mils (127 microns); the bottom layer includes a non-PVC based polymer; and the substrate layer having printed or image indicia thereon.

10. The film laminate as recited in claim 9, wherein the intermediate layer is selected from a group including an adhesive layer, a tie coating layer and an adhesive promotion layer.

11. The film laminate as recited in claim 9, further including at least one additive in at least one of the top, intermediate and bottom layers of the film.

12. The film laminate as recited in claim 11 wherein the at least one additive is selected from the group consisting of UV stabilizing agents, free-radical scavengers, cross-linking agents, thickeners, flow and leveling agents, rheology modifiers, surfactants, defoamers, dispersants, wetting agents, dyes, pigments, co-solvents, water, isopropyl alcohol and combinations thereof.

13. An advertising or informational graphic, comprising: a surface layer having promotional indicia provided thereon; a film including a first layer, a second layer having a first surface and a second surface, wherein a surface area of the first surface is in continuous physical contact with the first layer, and an adhesive layer beneath the second layer on the second surface of the second layer; wherein the adhesive layer is in contact with the second surface layer; and wherein the first layer includes at least 85.56% of a urethane-acrylic hybrid polymer and the second layer includes a non-PVC based polymer, wherein the film (i) passes an accelerated weathering test, (ii) exhibits a gloss at 60 degrees greater than 90, and (iii) exhibits a tensile elongation greater than 200%, wherein passing the accelerated weathering test requires that after weathering, the film not exhibit any visible changes after 2,000 hours and E is less than 10.

14. An advertising or informational graphic, comprising: a surface; an adhesive layer; a printable substrate having front and back faces, with the back face facing the surface and in contact with the adhesive layer and the front face having promotional indicia provided thereon; a transparent film having a top layer and a bottom layer, with the bottom layer facing the front face of the printable substrate; and wherein the top layer comprises at least 85.56% of a material selected from the group consisting of a polyurethane-acrylic copolymer and a urethane-acrylic hybrid polymer; and wherein the bottom layer includes a material selected from the group consisting of a polyurethane-acrylic copolymer, a urethane-acrylic hybrid polymer, a styrene acrylic polymer, and a vinyl acetate ethylene copolymer, wherein the film (i) passes an accelerated weathering test, (ii) exhibits a gloss at 60 degrees greater than 90, and (iii) exhibits a tensile elongation greater than 200%, wherein passing the accelerated weathering test requires that after weathering, the film not exhibit any visible changes after 2,000 hours and E is less than 10.

15. The advertising graphic as recited in claim 14, wherein the adhesive layer includes a removable adhesive.

16. The advertising graphic as recited in claim 14, wherein the promotional indicia is selected from the group consisting of alpha and/or numeric characters, images and combinations thereof.

17. The advertising graphic as recited in claim 14, wherein a second substrate layer is provided over one of the top layer and the bottom layer.

18. The advertising graphic as recited in claim 17, wherein the second substrate layer includes an ink layer.

19. The advertising graphic as recited in claim 14, further including at least one additive in at least one of the top and bottom layers of the film.

20. The advertising graphic as recited in claim 19, wherein the at least one additive is selected from the group consisting of UV stabilizing agents, free-radical scavengers, cross-linking agents, thickeners, flow and leveling agents, rheology modifiers, surfactants, defoamers, dispersants, wetting agents, dyes, pigments, co-solvents, water, isopropyl alcohol and combinations thereof.

21. A roll or sheet of graphic advertising film, comprising; a film having at least first and second layers, the first layer includes at least 85.56% of a urethane-acrylic hybrid polymer and the second layer includes a polyurethane-acrylic copolymer, a urethane-acrylic hybrid polymer, a styrene acrylic polymer, or a vinyl acetate ethylene copolymer; and one of the first and second layers is provided in operative association with advertising indicia, wherein the film (i) passes an accelerated weathering test, (ii) exhibits a gloss at 60 degrees greater than 90, and (iii) exhibits a tensile elongation greater than 200%, wherein passing the accelerated weathering test requires that after weathering, the film not exhibit any visible changes after 2,000 hours and E is less than 10.

22. The roll or sheet of graphic advertising film as recited in claim 21, where in the film further includes an adhesive layer provided on one of the first and second layers.

23. The roll or sheet of graphic advertising film as recited in claim 22, wherein a release layer is provided over the adhesive layer.

24. The roll or sheet of graphic advertising film as recited in claim 21, wherein the film further includes a substrate layer provided over one of the first and second layers.

25. The roll or sheet of graphic advertising film as recited in claim 24, wherein the substrate layer includes a print layer.

26. The roll or sheet of graphic advertising film as recited in claim 21, further including at least one additive in at least one of the first and second layers of the film.

27. The roll or sheet of graphic advertising film as recited in claim 26 wherein the at least one additive is selected from the group consisting of UV stabilizing agents, free-radical scavengers, cross-linking agents, thickeners, flow and leveling agents, rheology modifiers, surfactants, defoamers, dispersants, wetting agents, dyes, pigments, co-solvents and combinations thereof.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) These, as well as other objects and advantages of this invention, will be more completely understood and appreciated by referring to the following more detailed description of the presently preferred exemplary embodiments of the invention in conjunction with the accompanying drawings, of which:

(2) FIG. 1 is a sectional illustration of one exemplary embodiment of a film according to the present invention;

(3) FIG. 2 is a block diagram illustrating an exemplary manufacturing process for making one embodiment of the film according to the present invention;

(4) FIG. 3 is a flow chart illustrating another manufacturing process for making one embodiment of the film according to the present invention;

(5) FIG. 4 is a sectional illustration of one exemplary embodiment of a film according to the present invention;

(6) FIG. 5 is a sectional illustration of a further exemplary embodiment of a film laminate according to the present invention;

(7) FIG. 6 illustrates the top view of an exemplary embodiment of an advertising graphic applied on a surface according to the present invention; and

(8) FIG. 7 illustrates an exemplary embodiment of a roll of an advertising graphic according to the present invention.

(9) Unless otherwise indicated, the illustrations in the above figures are not necessarily drawn to scale.

DETAILED DESCRIPTION OF THE INVENTION

(10) The apparatuses and methods disclosed in this document are described in detail by way of examples and with reference to the figures. Unless otherwise specified, like numbers in the figures indicate references to the same, similar, or corresponding elements throughout the figures. It will be appreciated that modifications to disclosed and described examples, arrangements, configurations, components, elements, apparatuses, methods, materials, etc. can be made and may be desired for a specific application. In this disclosure, any identification of specific shapes, materials, techniques, arrangements, etc. are either related to a specific example presented or are merely a general description of such a shape, material, technique, arrangement, etc. Identifications of specific details or examples are not intended to be, and should not be, construed as mandatory or limiting unless specifically designated as such. Selected examples of apparatuses and methods are hereinafter disclosed and described in detail with reference made to FIGURES.

(11) The present invention relates to a film and a film laminate used for outdoor graphics applications, advertising, promotions and other marketing campaigns. More particularly, the present invention relates to a non-PVC transparent film and non-PVC film laminate for use in such applications. The film and film laminate provide suitable outdoor durability, scratch resistance, gloss, conformability, tensile elongation and tensile strength.

(12) In one exemplary embodiment of the invention, a single layer transparent film with properties suitable for use in the outdoor graphics applications is made of polyurethane, polyurethane-acrylic copolymer, polyurethane-acrylic blend or polyurethane-acrylic hybrid polymer.

(13) In another exemplary embodiment of the invention, a multi-layer transparent film provides properties suitable for use in the outdoor graphics applications. The multi-layer film has at least two layers. The first layer is made of polyurethane, polyurethane-acrylic copolymer, polyurethane-acrylic blend or urethane-acrylic hybrid polymer. The thickness of this first layer can be from about 0.3 mil (7.6 microns) to about 2 mils (50.8 microns). The other layers provide additional mechanical strength, improved adhesion, improved conformability and reduced cost to the overall construction. The number of layers can be determined based on the final requirement on the product, the cost restriction and availability of processing equipments. Such other layers can be made from emulsion polymers, solvent polymers or extruded polymers. Suitable polymers include, without limitation, acrylic polymers, styrene acrylic polymers, vinyl acetate ethylene copolymers, and polyolefins. The thickness of such other layer can vary from about 0 mil to about 2 mils. Examples of emulsion polymers include, without limitation, JONCRYL 617A JONCRYL 1987, JONCRYL 98, JONCRYL FLX5000, ACRONAL NX4612X and ACRONAL OPTIVE 410 available from BASF, Ludwigshafen, Germany; and VINNAPAS EF 811 from Wacker Chemicals, Munich, Germany or combinations thereof.

(14) In yet another exemplary embodiment of the invention, a non-PVC transparent film includes a top layer and a bottom layer. The top layer is made of polyurethane, polyurethane-acrylic copolymer, polyurethane-acrylic blend or polyurethane-acrylic hybrid polymer. The bottom layer includes a non-PVC emulsion based polymer. Generally, the non-PVC based polymer can be an emulsion based polymer, a solvent based polymer, and/or an extruded polymer. In certain embodiments, the non-PVC based polymer is an acrylic polymer.

(15) As used herein the term graphic or graphics refers to a visually perceptible presentation on some surface that is intended to brand, illustrate, entertain, inform, advertise, announce and market a product, service, event or the like.

(16) Reference is now directed to the FIGURES in which FIG. 1 provides a sectional view of an exemplary film prepared in accordance with the presently described invention. The film 100 has two layers. The film may be transparent, translucent, clear or have other desirable optical properties. The top layer 102 is, in one exemplary embodiment, a urethane-acrylic hybrid polymer. Bottom layer 104 is in the presently described embodiment a strengthening polymer layer.

(17) In addition, the film layers may have at least one additive added to either one or both, or two additives added to one or both of the layers. If an intermediate layer is included (see FIG. 4) the additive may also be present in the intermediate layer. The additives are selected from a group including UV stabilizing agents, free-radical scavengers, cross-linking agents, thickeners, flow and leveling agents, rheology modifiers, surfactants, defoamers, dispersants, wetting agents, dyes, pigments, co-solvents or combinations thereof.

(18) The urethane-acrylic hybrid polymer of the top layer 102 is a combination of urethane polymer and acrylic polymer mixed at the molecular level. In order to be environmentally friendly, the top layer 102 is preferred to be created from waterborne dispersions, although other methods for producing the urethane-acrylic hybrid polymer may also be used. Typically, there are two methods to make such hybrid polymer dispersions. In a first method, a polyurethane dispersion is prepared. Acrylic monomers are then added to the polyurethane dispersion. The acrylic polymer is formed in the presence of the polyurethane dispersion. In a second method, a polyurethane prepolymer is formed. The acrylic monomers are then added to the prepolymer. The urethane and acrylic polymerizations are completed concurrently. There are numerous publications on these methods. For example, U.S. Pat. No. 3,684,758 to Honig; 4,198,330 to Kaizerman; 4,644,030 to Loewrigkeit; and 5,594,065 to Tien describe the foregoing methods in detail. Publications, patents and patent applications are referred to throughout this disclosure. All references cited herein are hereby incorporated by reference.

(19) The urethane-acrylic hybrid polymer dispersions prepared according to the above described methods have been found to show better mechanical properties when compared to a simple blend of the two polymers due to the molecular level mixing which occurs through use of the foregoing processes. In order to make the formulation even more environmentally friendly, that is to reduce the environmental impact over other preparations, the urethane-acrylic hybrid polymer dispersions can be further improved to be free of N-methylpyrrolidone (NMP), a component typically used as a processing solvent in other applications.

(20) Suitable urethane-acrylic hybrid polymer dispersions for use in the compositions of the present invention are those with aliphatic acrylic monomers and aliphatic polyurethane components. As the film products produced will be used in an outdoor environment, the films will be exposed to moisture, such as dew, rain or snow; temperature deviations; light and other conditions which may impact the film performance. For example, moisture may cause components of the film or images thereon to bleach out or fade, and the film itself to whiten. Therefore, maintaining a proper balance of hydrophilic monomers and other components is required in order for this film to achieve the required resistance when exposed to such conditions. The monomers and other components should also be selected so as to be balanced to achieve the required tensile properties, block resistance, scratch resistance, transparency, and gloss. For example, the amount of acrylic present in the urethane-acrylic hybrid polymer controls the tensile properties of this top layer.

(21) Suitable urethane-acrylic hybrid dispersions for use in the present invention are available under the trade name HYBRIDUR from Air Products, Allentown, Pa., including HYBRIDUR 870; HYBRIDUR 570; HYBRIDUR 580; HYBRIDUR 878; and NEOPAC R9000 from DSM NeoResins, of Waalwijk, The Netherlands.

(22) UV blocking agents and free radical scavengers can be added to the top layer to improve the outdoor durability. UV blocking agents suitable for this application are typically benzotrizole based compounds, or other compounds capable of absorbing UV energy in the required region. Commercially available UV absorbing agents include, without limitation, TINUVIN 400 DW, TINUVIN 292 from BASF, Ludwigshafen, Germany; and HOSTAVIN 3310 from Clariant; Muttenz, Switzerland. The amount of UV blocking agent can range from about 0% to about 5%.

(23) Free radical scavengers may also be added to the top layer of the film to improve the weather durability of the top layer. Suitable free radical scavengers include but are not limited to TINUVIN 1130, TINUVIN 123 DW from BASF, Ludwigshafen, Germany; and HOSTAVIN 3065 from Clariant, Muttenz, Switzerland. The amount of free radical scavengers can range from about 0% to about 5%.

(24) Other UV blocking systems can also be used for improving weathering durability of this film. These include nano sized zinc oxide and cerium oxide or combinations thereof which may be used to achieve the UV resistance required for the film. Suitable nano metal oxides include but are not limited to NANOBYK 3840, NANOBYK 3810 from BYK Additives, of Altana, Wesel, Germany. The total amount of additives may range from about 0% to about 10%.

(25) Continuing with a discussion of the laminate provided in FIG. 1, the bottom layer 104 has a polymer layer that improves tensile properties of the overall film 100 which may also reduce the cost of the overall film. Examples of such strengthening polymer layer include, without limitation, emulsion based polymers, solvent based polymers, and extruded polymers. Suitable polymers include, without limitation, acrylic polymers, styrene acrylic polymers, vinyl acetate ethylene copolymers, and polyolefins. UV stabilizers and free radical scavengers can also be added to the bottom layer. The additives together can range from about 0% to about 5% of the total formulation.

(26) When acrylic polymers are used in the bottom layer 104, the acrylic polymers can be the same or different from those used in the top layer 102. Both aliphatic and aromatic acrylics can be suitable for inclusion in the bottom layer. Suitable acrylic polymers include acrylic emulsions that have superior block resistance, tensile properties and clarity, such as JONCRYL 617A available from BASF, Ludwigshafen, Germany.

(27) The thickness of the top layer 102 can range from about 0.5 mil to about 5 mils. The thickness of the bottom layer 104 can range from about 0.5 mil (12.7 microns) to about 5 mils (127 microns). When the thickness of the top layer 102 is too thin, the chemical resistance, scratch resistance and outdoor durability of the film may suffer. When the thickness of the bottom layer 104 is too thin, the tensile properties of the whole film may not be sufficient. Contrary to the above, when the top and bottom layers 102, 104 respectively, are too thick, the thickness of the construction may also impact the conformability of the film.

(28) The film 100 can be generated using any process suitable for such purpose. In one embodiment, the film compositions were first deposited onto a removable support or carrier layer by techniques well known to those skilled in the art. Examples of such techniques include die coating, knife coating, curtain coating and reverse roll coating. The removable support can be separated after the compositions have been dried. An exemplary removable support can be selected from a group including a siliconized belt, a release paper, and a release film such as PET or other suitable materials.

(29) An exemplary method of making a film according to the present invention is illustrated in the block diagram 200 of FIG. 2. After starting the process at step 205, the next step 210 is to provide the top layer components and a removable support. Next, at step 215, the top layer components are blended to form a top layer composition. The top layer composition includes polyurethane, polyurethane-acrylic copolymer, polyurethane-acrylic blend, or urethane-acrylic hybrid dispersions and at least one of free radical scavenger and UV blocking agent. Next, at step 220, the removable support is coated with the top layer composition, such as by slot die coating, curtain coating or other acceptable methods. At step 225, the top layer composition is dried. Drying may occur by using a heated or ambient air environment, curing or by other suitable methods. At step 230, the bottom layer components are provided. At step 235, the bottom layer components are blended to form a bottom layer composition. The bottom layer composition includes emulsion polymer or solvent polymer and at least one of a free radical scavenger and a UV blocking agent. The bottom layer composition is coated over the top layer at step 240, such as by slot die coating. At step 245, the bottom layer composition is dried. Alternatively, the film is further laminated with a pressure sensitive adhesive (PSA) coated release liner before proceeding to the next step. At step 250, the removable support is removed or separated from the dried two layer film. The separation or removal can be accomplished by using a peel blade or knife which serves to separate the film from the carrier or support layer. Alternatively, the film can be separated by the carrier at a sharp angle so that the film can be easily picked up from the carrier or support. The film is rolled up and ready for use. Alternatively, the film can be cut and separated into sheets or sections of equivalent sizes or of varying lengths. The method ends at step 255.

(30) The top layer and the bottom layer are substantially coextensive with one another, that is the edges and/or sides are aligned and in juxtaposition. It is of course possible, that the top layer could be applied in a pattern over the bottom layer so that the layers are not completely juxtaposed on one another.

(31) In another embodiment of the invention, the compositions of the top layer and the bottom layer can be coated onto a removable support simultaneously. Flowchart 300 in FIG. 3 illustrates such an exemplary process. After starting at step 305, the next step 310 is to provide the top layer components, the bottom layer components and a removable support. Next, at step 315, the top layer components are blended to form a top layer composition. Substantially, simultaneously, the bottom layer components are blended to form a bottom layer composition. Next, at step 320, the top layer composition and the bottom layer composition are coated simultaneously using a dual die with the top layer composition contacting the removable support and the bottom layer composition contacting the top layer composition. Additionally, the top layer and bottom layer can be formed separately and then extruded or coated on to the support or carrier through a common apparatus. At step 325, the coated compositions are dried. Alternatively, the film is further laminated with a PSA coated release liner before proceeding to the next step. After drying of the compositions, the removable support or carrier layer can be removed from the dried two layer film in step 330. The film can be rolled up and ready for use or sheeted depending on the requirements of the particular application. The film may then be printed or imaged by conventional methods such as by ink jet and electrostatic printing technologies or alternatively, the film can be applied over another substrate which may have been printed or imaged previously. The method ends at step 335.

(32) In addition to the foregoing, the film can be further overcoated with a varnish or other material to provide a glossy appearance. This step may occur during the film forming process, after printing or after collection of the material after the production process has been completed.

(33) The film of the present invention can be used in operative association with a graphic or other message. As used herein, operative association includes applying the film over the graphic or message, including the graphic or message as part of the film either as an additional layer, such as a printing layer or previously printed layer, or applying a graphic or message over the film.

(34) The film can be used as a printable media for outdoor applications, architectural and transportation type advertising campaigns and the like. The film can also be used as a protective film to be laminated over a subject, such as a protective laminate for electronic appliances, architectural, artistic or aesthetic elements, a retro-reflective license plate, a retro-reflective signage film, a name plate, a label, automotive exterior and interior parts, and the like. Additional exemplary uses may include safety signs, a graphic display, governmental mandated displays, military applications or a surface that needs protection in the outdoor environment.

(35) The film can also include an adhesive layer. The adhesive can be a pressure sensitive adhesive, glue, and any other type of adhesives that are optically transparent, and when used to contact the printed indicia, would not affect the printed indicia. The adhesive may be pattern coated, and may be selected for particular properties such as permanent, removable or repositionable and the like. The adhesive can be random copolymer adhesives or block copolymer adhesives. Random copolymer adhesives include those based upon acrylic and/or methacrylic copolymers, -olefin copolymers, silicone copolymers, chloroprene/acrylonitrile copolymers, and the like. Block copolymer adhesives including those based upon linear block copolymers (i.e., A-B and A-B-A type), branched block copolymers, star block copolymers, grafted or radial block copolymers, and the like, and natural and synthetic rubber adhesives. A description of useful pressure sensitive adhesives can be found in Encyclopedia of Polymer Science and Engineering, Vol. 13. Wiley-Interscience Publishers (New York, 1988). Additional descriptions of useful pressure sensitive adhesives can be found in Encyclopedia of Polymer Science and Technology, Vol. 1, Interscience Publishers (New York, 1964).

(36) When pressure sensitive adhesives are used, a release liner can be used to protect the adhesive from inadvertent contact with unintended surfaces. Any release liner suitable for the chosen adhesive can be used. For pressure sensitive adhesives, release liners can be coated papers or films, and super calendared paper, for example. Coating materials suitable for release liners include, for example, silicone-based and fluorine-based materials, or any other material that has the desired releasing properties, for example, waxes and carbamates.

(37) FIG. 4 illustrates one embodiment of the current invention. The film 400 has a top layer 402, a bottom layer 404, an intermediate layer 406 and a release liner 408. Upon application, the release liner can be peeled off to expose the adhesive surface. The film can be attached to the surface to be protected through the adhesive layer. The intermediate layer may include an adhesive layer, a tie coating layer or an adhesion promoting layer.

(38) The film can also be used as part of a larger film laminate. FIG. 5 illustrates a cross-sectional view of one embodiment of a film laminate. The film laminate 500 is comprised of a top layer 502, a bottom layer 504, an adhesive layer 506, an ink layer 510, and an underlying substrate layer 512. Though referred to as an ink layer, the ink may not necessarily form a continuous layer. Various printable materials can be used as the underlying substrate layer. A non-PVC based printable material is preferred to make the whole film laminate non-PVC based. International patent application PCT/US08/84812 describes various films created using non-PVC compositions and is incorporated herein by reference in its entirety. Ink or toner anchor coatings, such as polyvinyl alcohol can be added to increase the anchorage of the printing to the laminate.

(39) FIG. 6 illustrates a top view of an exemplary embodiment of an advertising graphic film applied to a surface according to the present invention. The film laminate 600 bearing advertising graphic 614 is posted on a surface 616 through the use of an adhesive.

(40) FIG. 7 illustrates an exemplary embodiment of a roll of the film laminate 700 according to the present invention.

(41) Additional components, such as thickeners, flow and leveling agents, and rheology modifiers can be added to each of the top and bottom formulations to achieve desired coating quality. Examples of suitable thickeners include, without limitation, ACRYSOL RM-2020 NPR, TM8W, and UCAR POLYPHOBE 115 TR from Dow Chemicals, Midland, Mich. Examples of suitable flow and leveling agents include without limitation, ZONYL FS300 from Dupont; Polyfox PF-156A from Omnova Solutions; and Masurf from Mason Chemical Company and others with similar chemistry. The percent incorporation can vary from 0% to 10% in both layers. Additional viscosity modifiers can be included in the formulation to modify the viscosity to a desired level and/or to impart desirable flow characteristics. These can be urethane based alkali swellable associative thickeners. Products like UCAR polyphobe 102 from Arkema Emulsion Systems or Rheolate 350 from Elementis are typical examples that can be used in the formulations. The percent incorporation can vary from between 0% to 10% in both layers. Other components, such as water or isopropyl alcohol (IPA) can also be added to the formulation at about 0% to about 10%.

(42) Cross-linking agents can be added to the top layer formulations to improve the mechanical properties of that film layer. Examples of suitable cross-linking agents include, without limitation, polyaziridine based CX-100 from DSM Neo Resins, Waalwijk, The Netherlands; UCARLINK XL-255E, ERL-4221, ERL-4234 from Dow Chemicals, Midland, Mich.; and COATOSIL 1770, SILQUEST A-187 from Momentive Performance Materials Inc., Waterford, N.Y.

(43) Without limitation, other additives, for example, surfactants, defoamers, dispersants, wetting agents, dyes, pigments and co-solvents known to those skilled in the art can be added to the composition of each of the top layer and bottom layer.

(44) Test Methods

(45) Thickness

(46) Film thickness is measured using TMI Model 49-70 Precision Micrometer available from Testing Machines Inc. in Ronkonkoma, N.Y. The specimen is placed between an upper and a lower anvil. The upper anvil rests on top of the specimen and the thickness is measured and displayed on the digital readout.

(47) CIE L*a*b* Color Space

(48) This test is used to describe the color of a sample. This 3-dimensional color space system was developed by the International Commission on Illumination (CIE), and defines L* as representing the lightness of the color, ranging from 0 (black) to 100 (white). In this system, a* represents the color's position along the red (magenta)/green axis, in which negative values represent green and positive values represent red or magenta, and b* represents the color's position along the blue/yellow axis, in which negative values represent blue and positive values represent yellow. The test is conducted using a COLOR 15 Benchtop Spectrophotometer available from X-Rite, Inc., Grand Rapids, Mich. The test method is TAPPI T524 om-94.

(49) Accelerated Weathering

(50) Accelerated weathering test simulates the damaging effects of long term outdoor exposure of materials by exposing test samples to light, moisture and temperature extremes. Sample is tested and observed for light fastness (fading of colors), and weatherability (cracking, chalking, curling, shrinkage, etc . . . ). An Atlas C165A Xenon Arc Weather-Ometer from Atlas Material Testing Technology LLC in Chicago, Ill. is used for this test.

(51) A printing pattern with white, yellow, magenta, cyan and black stripes is first printed on a printable substrate. The film of the current invention, which may be transparent, translucent, clear or have other desirable optical properties, is then laminated over the print layer to make a film laminate through the use of a pressure sensitive adhesive. The sample is first tested for CIE L*a*b* Color Space before placed in the Weather-Ometer. The sample is allowed to age in the Weather-Ometer for a designated amount of time. The sample is taken out of the Weather-Ometer for CIE L*a*b* Color Space reading and observation for any changes in shrinkage, chalking, cracking etc . . . . If there is no visible change after 2000 hours, and the changes in L*, a* and b* together, represented by E, is less than 10, the sample is given a pass grade. E value is calculated using the following formula:
E={square root over ((L.sup.2+a.sup.2+b.sup.2))}.

(52) Gloss

(53) Gloss is measured using a BYK Gardner Micro-TRI-Gloss Gloss Meter from BYK Gardner USA in Columbia, Md. The universal measurement angle 60 is used for the measurement. Typically the acceptable gloss reading is 80 or higher.

(54) Tensile Strength and Tensile Elongation

(55) The tensile elongation and tensile strength of the film is tested using Instron Model 5542 from Instron Co. in Canton, Mass. A modified ASTM D882 was used to determine the tensile strength and percentage elongation of the films of the present invention. The procedure is as follows: 1. A 1 inch4 inch (25.4 mm101.6 mm) specimen was cut out in the machine direction. 2. Grip the film 1 inch (25.4 mm) from the end at both the ends, so the separation between the grips is 2 inches (50.8 mm). 3. Set the crosshead speed at 12 inches per minute (ipm) (304.8 mm per minute). 4. Obtain the tensile strength, which is the product of tensile stress times, the thickness of the film. The tensile strength at break is the maximum stress that occurs at break times the thickness of the film. 5. The % elongation is reported by the machine.

(56) The standard requires a minimum ultimate elongation of 180% and a minimum tensile strength of 0.5 pound per square inch (psi) (6,895 N/m.sup.2). The presence or absence of pressure sensitive adhesive (PSA) on the film does not appreciably alter the strength and/or elongation of the film. As such, wherever the film in the examples below includes PSA, the tensile elongation test was performed using the same film but without the layer of PSA.

(57) Rivet Testing

(58) Test samples approximately 2.5 inch (63.5 mm)2.5 inch (63.5 mm) are applied over painted 4 inch (101.6 mm)12 inch (304.8 mm) aluminum panels from Frontier Tank Center in Richfield, Ohio. Brazier rivet heads which are 11.4 mm (diameter)3.3 mm (height)7.62 mm (shaft diameter) (0.45 (diameter)0.13 (height)0.3 (shaft diameter)) are uniformly distributed over the aluminum panel. Application is done so as to minimize forming any wrinkles especially around these rivet heads. Entrapped air is released with the use of pin pricks while a brush with hard bristles and plastic squeegee is used to get the best conformation of the film around the rivet. The sample is dwelled for 24 hours at ambient condition. The diameter of the lifted portion of the film around the rivet is measured and recorded. The sample is then placed in Atlas Ci5000 Xenon Arc Weather-Ometer from Atlas Electric Devices Co. in Chicago, Ill., using a UVB 313 bulb for 1000 hours. The sample is then taken out and the diameter of the film lifted around the rivets is measured again. When the change in diameter is less than 0.0625 inch (1.58 mm), the sample is given a pass grade.

(59) Shrinkage Test

(60) Test sample is coated with a pressure sensitive adhesive under the trade name S8072 from Avery Dennison Corporation in Pasadena, Calif. at about 30 gram per square meter (gsm) coat weight. The sample is then attached to a clean aluminum panel from O-Lab Corporation of Cleveland, Ohio. The sample is dwelled at ambient condition for 24 hours. A 5 inch (127 mm) cross hatch in both machine direction (MD) and cross-machine direction (CD) are made on the film. The sample is then aged at 160 F. (71 C.) for 48 hours. The dimension change in the MD and CD are measured. If the shrinkage is less than 0.33% in both directions, the sample is given a pass grade.

EXAMPLES

(61) The chemicals used in the following examples are listed in Table 1 with information on the function, manufacture and location of each.

(62) TABLE-US-00001 TABLE 1 Manufacturing Name of the Chemical Function Company Location HYBRIDUR 870 Top layer component Air Products Allentown, Pennsylvania JONCRYL 617 A Bottom layer BASF Ludwigshafen, component Germany TINUVIN 123 DW Free radical BASF Ludwigshafen, scavenger Germany TINUVIN 400 DW UV blocking agent BASF Ludwigshafen, Germany TINUVIN 292 UV blocking agent BASF Ludwigshafen, Germany TINUVIN 1130 Free radical BASF Ludwigshafen, scavenger Germany TEXANOL ESTER SOLVENT Solvent Eastman Chemical Kingsport, Tennessee DOWANOL DPNB Solvent Dow Chemicals Midland, Michigan VINNAPS EF 811 Component for Wacker Chemicals Munich, additional layers Germany ZONYL FS300 Flow and leveling Dupont Wilmington, DE agent UCAR POLYPHOBE 102 Viscosity modifier Arkema Emulsion Cary, NC Systems ARCRONAL NX4612X Bottom layer BASF Ludwigshafen, component Germany JONCRYL 1987 Bottom layer BASF Ludwigshafen, component Germany

(63) Table 2 lists five examples of formulations used to create the top layer.

(64) TABLE-US-00002 TABLE 2 HYBRIDUR TINUVIN TINUVIN H 870 123 DW 400 DW TEXANOL Example No. % % % % DpNB % Total % 1 95.25 1.90 2.85 0.00 0.00 100.00 2 96.78 1.27 1.95 0.00 0.00 100.00 3 93.45 1.87 2.80 0.94 0.94 100.00 4 92.60 1.85 2.77 1.39 1.39 100.00 5 94.95 1.25 1.90 0.95 0.95 100.00

Examples 1 to 5

Top Layer Compositions

(65) Table 3 lists two examples of formulations used to create the bottom layer.

Examples 6 to 7

Bottom Layer Compositions

(66) TABLE-US-00003 TABLE 3 Example JONCRYL 617 A TINUVIN 292 TINUVIN 1130 Total No. % % % % 6 99.0 0.50 0.50 100 7 98.65 0.675 0.675 100

(67) Table 4 lists five examples of the film created using Example 5 as the top layer, Example 7 as the bottom layer at various thickness of each layer.

Examples 8 to 12

Films

(68) TABLE-US-00004 TABLE 4 Thickness Thickness Example No. of Top layer (mil) of Bottom Layer (mil) 8 0.75 0.75 9 1 0.5 10 1 1 11 1.33 0.66 12 2 0.5

Example 13 Control

(69) HYBRIDUR 870 by itself was made into a film. When the film thickness is about 1.7 mils (43 microns), the tensile elongation is 80%. When the film thickness is about 2.4 mils (61 microns), the tensile elongation is around 150%. When subject to weather-o-meter test, the films show heavy shrinking.

(70) Examples 8 to 12 have been tested for various properties. The films have been tested for film thickness, gloss at 60 degrees, and tensile elongation. For scratch resistance and shrinkage test, each sample is coated with about 30 gsm of a pressure sensitive adhesive under the trade name S8072 from Avery Dennison Corporation in Pasadena, Calif. For accelerated weathering and rivet testing, the adhesive coated sample is further laminated onto a printable film. The printable film is Example No. 29B in the PCT application PCT/US08/84812, which has been incorporated by reference herein in its entirety.

(71) Table 5 lists the properties measured for each of the samples. All examples have passed the accelerated weathering test, have a gloss at 60 degree higher than 90, and tensile elongation higher than 200. All of the samples have passed the scratch resistance test, rivet testing, and shrinkage test.

(72) TABLE-US-00005 TABLE 5 Total Accelerated Tensile Shrinkage Example No. Thickness Weathering Gloss @ 60 Elongation Rivet Testing Test 8 1.5 mils Pass >80 >200 Pass Pass 9 1.5 mils Pass >80 >200 Pass Pass 10 1.5 mils Pass >80 >200 Pass Pass 11 2.0 mils Pass >80 >200 Pass Pass 12 2.0 mils Pass >80 >200 Pass Pass

Example 13 Three-layer film

(73) A three-layer film was created using HYBRIDUR 870 as the top layer, JONCRYL 617 A as the middle layer, and VINNAPAAS EF 811 as the third layer. Each layer can be from about 0.5 mil (12.7 microns) to about 2 mils (50.8 microns) thick.

Examples 14-17

(74) Table 6 lists four additional examples of formulations used to create the top layer.

(75) TABLE-US-00006 TABLE 6 UCAR Example Hybridur Tinuvin Tinuvin Zonyl DI Polyphobe Rheolate No. 870 400 DW 123 DW Texanol DPnB FS300 Water 102 350 14 89.56% 0.91% 0.73% 1.41% 1.41% 0.28% 4.70% 0.99% 15 86.25% 0.88% 0.70% 1.36% 1.36% 9.27% 0.18% 16 85.56% 0.87% 0.69% 1.35% 1.35% 9.6% 0.18% 0.40% 17 85.56% 0.87% 0.69% 1.35% 1.35% 9.59% 0.58%

Examples 18-22

(76) Table 7 lists five additional examples of formulations used to create the bottom layer.

(77) TABLE-US-00007 TABLE 7 UCAR Example Joncryl Tinuvin Tinuvin Polyphobe DI Zonyl Acronal No. 1987 292 1130 102 Water FS300 Texanol NX4612X 18 98.85% 0.45% 0.45% 0.05% 0.05% 0.15% 0.0 0.0 19 99.05% 0.45% 0.45% 0.025% 0.025% 0.0 0.0 0.0 20 0.0 0.50% 0.50% 0.10% 0.10% 0.0 2.88% 95.93% 21 49.53% 0.42% 0.42% 0.05% 0.05% 0.0 0.0 49.53% 22 74.30% 0.42% 0.42% 0.05% 0.05% 0.0 0.0 24.77

(78) All patents, published applications, and articles noted herein are hereby incorporated by reference in their entirety.

(79) All of the features disclosed in the specification, including the claims, abstract, and drawings, and all of the steps in any method or process disclosed, may be combined in any combination, except combinations where at least some of such features and/or steps are mutually exclusive. Each feature disclosed in the specification, including the claims, abstract, and drawings, can be replaced by alternative features serving the same, equivalent, or similar purpose, unless expressly stated otherwise. Thus, unless expressly stated otherwise, each feature disclosed is one example only of a generic series of equivalent or similar features.

(80) The foregoing detailed description of the present invention is provided for purposes of illustration, and it is not intended to be exhaustive or to limit the invention to the particular embodiments disclosed. The embodiments may provide different capabilities and benefits, depending on the configuration used to implement the key features of the invention. Accordingly, the scope of the invention is defined only by the following claims.