Soft touch laminates constructed with improved fire retardant properties for transportation

Abstract

Soft touch fire retardant laminates with PVC middle layers, foamed or unfoamed, and multiblock copolymer or polyurethane or silicone top layers which meet FAA requirements are disclosed.

Claims

1. A laminate material comprising: a) a base layer comprising a fluoropolymer b) a middle layer formed of a plurality of layers of poly(vinyl chloride) (PVC), with at least one of the layers of poly(vinyl chloride) (PVC) being foamed, the middle layer having a thickness of 2-10 mils; and c) a top layer of a polyurethane-silicone blend with a thickness of 0.1-0.5 mils, wherein the laminate material complies with the 60 sec vertical burn requirements of FAR 25.853, and has NBS smoke density of <200 and OSU heat release peak kw/m.sup.2 of <65 and total kw min/m.sup.2 of <65, wherein the fluorpolymer layer is formed of polyvinylidene flouride (PVDF) or polyvinyl flouride (PVF).

2. The laminate material of claim 1 in which at least one of the PVC layers is unfoamed.

3. The laminate material of claim 1 in which the PVC middle layer further comprises at least one pigment.

4. The laminate material of claim 1 in which the PVC middle layer further comprises at least one flame retardant.

5. The laminate material of claim 1 in which an adhesive is provided on the base layer.

6. The laminate material of claim 5 in which the adhesive is from 1-5 oz/yd.sup.2.

7. The laminate material of claim 1 further comprising an adhesive layer on the bottom of the laminate comprised of acrylic, polyester, polyurethane or phenolic resins.

8. The laminate material of claim 7 in which the adhesive layer further comprises flame retardants.

9. The laminate material of claim 1 wherein the middle layer is calendared, extruded or coated.

10. The laminate material of claim 1 wherein the laminate is vacuum formed into place to form a surface.

Description

DESCRIPTION OF THE DRAWING FIGURES

(1) FIG. 1 is a schematic representation of a first embodiment of a laminate of the present disclosure;

(2) FIG. 2 is a schematic representation of a second embodiment of a laminate of the present disclosure;

(3) FIG. 3 is a schematic representation of a third embodiment of a laminate of the present disclosure, and

(4) FIG. 4 is a schematic representation of a fourth embodiment of a laminate of the present disclosure.

DETAILED DESCRIPTION OF PREFERRED AND ALTERNATE EMBODIMENTS

(5) The present invention is an engineered high performance decorative laminate that has a soft feel, for example like leather or synthetic leather. It will meet or exceed all Federal Aviation Administration (FAA) regulations. Specifications for fire, smoke and toxic gases for use in all areas of commercial aircraft are considered. It will also have excellent stain resistance and durability. By coating a poly(vinyl halide) or a poly(vinylidene halide) film with a flame retarded multiblock copolymer and optimizing this layer for feel and burn these limitations were overcome.

(6) Multiblock copolymers as used herein include polyurethanes (PU), copolyamides (COPA), copolyesters (COPE), and styrenics such as SIS, SBS, SIBS and the like. These copolymers are preferably cross-linkable thermoplastics or thermosets.

(7) Poly(vinyl chloride) or PVC, as used herein, includes homopolymers of vinyl chloride, as well as polymerization products of vinyl chloride and one or more co-monomers. For example, the PVC resin can be a copolymer of vinyl chloride and ethylene, or a copolymer of vinyl chloride and propylene. The PVC resin can also be the polymerization product of vinyl chloride and an ester monomer having formula H.sub.2CC(R.sup.1)OC(O)R.sup.2 or H.sub.2CC(R.sup.1)C(O)OR.sup.2, where R.sup.1 and R.sup.2 are, independently, C.sub.1-12 alkyl. An example of such a resin is a copolymer of a vinyl chloride monomer and a methyl methacrylate monomer. Another example of such a resin is a copolymer of a vinyl chloride monomer and a vinyl acetate monomer. Combinations of these PVC resins may also be used.

(8) Poly(vinylidene fluoride) or PVDF, as used herein, includes homopolymers of vinylidene floride, as well as polymerization products of vinylidene fluoride and one or more co-monomers. For example, the PVDF resin can be a copolymer of vinylidene fluoride and hexafluoropropylene, or a copolymer of vinylidene fluoride and chlorotrifluoroethylene. The PVDF resin can also be the polymerization product of vinylidene fluoride and an ester monomer having formula H.sub.2CC(R.sup.1)OC(O)R.sup.2 or H.sub.2CC(R.sup.1)C(O)OR.sup.2, where R.sup.1 and R.sup.2 are, independently, C.sub.1-12 alkyl. An example of such a resin is a copolymer of a vinylidene fluoride monomer and a methyl methacrylate monomer. Another example of such a resin is a copolymer of a vinylidene fluoride monomer and a vinyl acetate monomer. Combinations of these PVDF resins may also be used. Blends of PVDF with other polymers can also be used, for example PVDF/acrylic blends.

(9) Prepreg are coatings in which polymers such as PET, PPS, and PEEK are suspended in an organic liquid, optionally with flame retardants.

(10) Silicone foam is a silicone material containing open and/or closed cells and are available from a variety of manufacturers. Foams are available in a wide variety of durometers and with glass backing for durability. Specifically selected and designed systems with improved flame retardant properties beyond the natural flame retardant properties of silicone based materials is required to meet the intent of the invention.

(11) Organosols are coatings in which PVC is suspended in an organic liquid optionally with flame retardants.

(12) Suitable adhesives and primers include, but are not limited to: phenolic resins, polyesters, epoxies, polyurethanes, and methacrylics. Because the adhesives need to be compatible with the materials they are bonding and provide the requisite strength for the application, typically the manufacturer of the laminate layer will specify which adhesives or primers are compatible in use with their products.

(13) The compositions contain one or more flame retardant or combinations of flame retardants. The flame retardants can be liquid or solid. Preferred flame retardants include but are not limited to aluminum trihydroxide, available from various suppliers, including Alcoa, under the product name Hydrated Aluminas; magnesium hydroxide, available from various suppliers, including Albermarle, under the trade name MAGNIFIN (e.g., MAGNIFIN H-10 or MAGNIFIN H-5); flame-retardant plasticizer such as phosphate ester plasticizers, available from various suppliers, including Ferro, under the trade name SANTICIZER (e.g., SANTICIZER 2148), tetrabromophthalates, polymeric plasticizers (for example, Admix 412, available from Teknor Apex), combinations of bromo and chlorophthalates (for example, Unitex 44-55), and chlorinated hydrocarbons (for example, Cercelor S52); and ammonium octamolybdate, available from various suppliers, including Polymer Additives Group, under the trade name Climax AOM; Alkyl aluminum phosphonates and phosphinates such as AMMP and DEPAL sold by ICL-IP and Clariant, respectively, zinc sulfides, sold by Sachtleben, zinc borates sold by US Borax Inc, and zinc hydroxy stannates sold as ZS 286 by 3N International; bismuth oxide, sold by 3N International. Additional flame retardants are described in Linsky et al., U.S. Pat. No. 5,886,072, and Shtekler et al., WO 2012/088080, which are hereby incorporated by reference in its entirety. The compositions preferably include at least about 50 parts total flame retardant per 100 parts polyvinyl chloride resin, and more preferably from about 50 parts to about 200 parts total flame retardant per 100 parts polyvinyl chloride resin. The composition may include, for example, from about 5 parts to about 60 parts, from about 10 parts to about 50 parts, or from about 20 parts to about 40 parts flame retardant plasticizer per 100 parts polyvinyl chloride resin.

(14) In one embodiment of the present invention, as schematically illustrated in FIG. 2, the laminate comprises a top layer of clear flame retarded multiblock copolymer film bonded to a clear poly(vinyl halide) or a poly(vinylidene halide) film, optionally containing fire retardants. This laminate is then bonded to a flame retarded PVC layer containing pigments and flame retardants. It may be necessary to use a primer in order to attain good adhesion between the laminate and the PVC layer. These layers are bonded with a suitable glass fabric that has been impregnated with a fused organosol material. Optionally there may be a fluoropolymer layer bonded to the other side of the impregnated glass in which case an optional primer layer would be required. Commercially available examples of suitable materials for this embodiment are set forth below:

(15) TABLE-US-00001 FAA Soft Touch Film specification 1 2 3 4 5 6 7 8 OSU Peak 65 62 76 53 59 71 43 49 53 Heat kw/m.sup.2 Release Total 65 51 50 49 44 37 44 37 42 kw min/m.sup.2 Smoke Ds 200 99 126 94 97 86 104 121 100 4 min

(16) The soft touch film is a grade of available from Akzo Nobel, preferably the 8901 that is 2.5-2.7 mils thick and is composed of a polyurethane over a PVC base. The glass fiber is sold as 7628 Greige glass from BGF. The middle PVC layer was S1670 sold by Spectrum. The prepreg was S1687 sold by Spectrum. The acrylic primer is 68080 a flexible product adhesive sold by Dupont.

(17) In another embodiment of the present invention the laminate comprises a top layer of clear urethane/polycarbonate film bonded to a clear PVDF/acrylic film containing fire retardants which is then bonded to a PVC layer containing pigments and flame retardants. These layers are bonded with a suitable adhesive to a fire resistant silicone foam/glass fabric. Optionally there may be a fluoropolymer layer between the PVC layer and the silicone foam.

(18) Referring to FIG. 1, in this embodiment the laminate comprises a top ply of a clear layer that is about from 0.5 mil to about 3 mil of a flame retarded multiblock copolymer on a poly(vinyl halide) or a poly(vinylidene halide) layer. Suitable films are, for example sold as AEROFINE 8900 by Akzo Nobel. Optionally bound to the top ply using a suitable primer up to 0.5 mil in thickness. The prior materials are then bonded to a PVC layer that is 1 to 25 mil in thickness which can be foamed or unfoamed. An organosol impregnated glass fabric is optionally bound to the PVC layer, wherein the glass fabric weighs from about 1 to about 10 oz/yd.sup.2, and the organosol is fused. A fluoropolymer layer (PVF or PVDF) such as Tedlar offered by Dupont or Fluorex products offered by Akzo Nobel is optionally indirectly bonded to PVC, indirectly as a primer layer is required to be used in conjunction with the optional fluoropolymer layer. The fluoropolymer layer is preferably from about 0.5-3.0 mils thick. An adhesive layer is then bonded as the final layer; the adhesive layer is preferably 1 to 5 oz/yd.sup.2.

(19) Referring to FIG. 3, in this embodiment the laminate comprises a top ply of clear 1.0-3 mil urethane/polycarbonate film. Suitable films are manufactured by Akzo Nobel. Bound to the top ply using a suitable adhesive, such as Dupont 68080 adhesive primer, is a 0.8-1.5 mil clear PVDF/acrylic film containing fire retardants such as AIRFILM LHR (Low Heat Release) offered by Schneller. The prior materials are then bonded to a fluoropolymer layer (PVF or PVDF) such as Tedlar offered by Dupont of Soliant products offered by Akzo Nobel. The fluoropolymer layer is preferably from about 0.5-2.0 mils thick. A silicone foam with glass backing is bound to the fluoropolymer layer using a suitable adhesive such as HA 211 from Schneller. In one embodiment the silicone foam is 63 mils thick. Suitable silicone foams can be purchased from Rogers Corporation under the brand Bisco.

(20) Referring to FIG. 4, in this embodiment the laminate comprises a fluoropolymer backing such as PVDF or PVF onto which a PVC material from 2-10 mils in thickness is applied. The PVC can be calendared, extruded or coated; it may contain pigments for coloration and fire retardants. In some instances it may be comprised of a couple of different layers of PVC and some or all of it may be foamed. A top ply of 0.1-0.5 mils polyurethane/silicone is applied to the PVC.

(21) Table 1 below sets forth the desired characteristics for the laminates of the present invention including relevant regulations where applicable.

(22) Laminates of the present invention can be applied by any suitable means. In certain instances they may be vacuum formed into place using means known in the art or applied using rollers or other means of exterior pressure.

(23) One of skill in the art will appreciate that a substantial degree of deviation from the processes and materials described herein is possible and still be within the spirit of the invention.

(24) TABLE-US-00002 TABLE 1 Targets plus team inputs Test method Characteristics 1 With Pressure Adhesion (ISO 4578) and sensitive burn (FAA), 65/65/200 adhesive and FAA and OEM toxicity 2 With Heat active adhesives 3 Resistance to AIMS 04-09-000, AIMS cleaning agent 04-09-001 and typical Durability house cleaning agents 4 Tensile and elongation min. 70N. 60 ISO 527 to 80% 5 Tear ISO 4674 min. 0.8N 6 Dimensional changes less than 1.5% AIMS 04-09-000 change after 75 C. for 24 h. 7 Taber weight loss. 10 to 20 mg loss ISO 9352 8 Five fingers scratch visually as good as or ASTM 7027 our laminates 9 60 sec Vertical FAR 25.853 150, 10, 0 Burn 10 NBS smoke <200 density 11 OSU Peak/total: 65/65, all substrate and all adhesives 12 Toxicity ABD 0031, vs Boeing Hydrogen Fluoride < D6-51377 100/200 ppm Hydrogen chloride < 150/500 ppm Hydrogen cyanide < 150/150 ppm Sulfur dioxide < 100/100 ppm Nitrous gases < 100/100 ppm Carbon monoxide < 1000 ppm