NEGATIVE ELECTRODE COMPRISING PRE-LITHIATION LAYER FOR LITHIUM METAL BATTERY, MANUFACTURING METHOD THEREOF, AND LITHIUM METAL BATTERY COMPRISING THE SAME

Abstract

A negative electrode for a lithium metal battery includes a metal current collector substrate. A lithium metal layer is formed on at least one surface of the metal current collector substrate. A pre-lithiation layer is formed on the lithium metal layer. The pre-lithiation layer includes a prelithiated active material.

Claims

1. A negative electrode for a lithium metal battery, comprising: a metal current collector substrate; a lithium metal layer formed on at least one surface of the metal current collector substrate; and a pre-lithiation layer formed on the lithium metal layer, wherein the pre-lithiation layer comprises a pre-lithiated active material .

2. The negative electrode according to claim 1, wherein the pre-lithiated active material comprises a carbon-based material, a lithium metal oxide, a metallic compound capable of alloying with lithium, a metal oxide, a lithium-metal alloy, or a mixture of two or more thereof.

3. The negative electrode according to claim 1, wherein the metal current collector substrate comprises one selected from the group consisting of copper, stainless steel, aluminum, nickel, titanium, calcined carbon, copper that is surface-treated with dissimilar metal, stainless steel that is surface-treated with dissimilar metal, and an aluminum-cadmium alloy.

4. The negative electrode according to claim 1, wherein the metal current collector substrate comprises a metal including copper.

5. The negative electrode according to claim 1, wherein a thickness ratio of the lithium metal layer and the pre-lithiation layer is 99:1 to 1:99.

6. The negative electrode according to claim 1, wherein the pre-lithiation layer further comprises a binder and a conductive material.

7. A method for manufacturing the negative electrode according to claim 1, the method comprising the steps of: placing, electrodepositing or vapor-depositing lithium metal on at least one surface of the metal current collector substrate to form the lithium metal layer; mixing or dispersing active material particles together with a solvent to prepare a slurry or dispersion; coating the slurry or dispersion on the lithium metal layer and drying to form a protective layer, thereby producing a preliminary negative electrode; and rolling the preliminary negative electrode and reacting the lithium metal with the protective layer, thereby performing pre-lithiation of the protective layer, wherein a loading amount of the lithium metal is larger than a loading amount of the protective layer, and wherein the lithium metal layer remains after performing the pre-lithiation of the protective layer.

8. The method for manufacturing the negative electrode according to claim 7, wherein, the active material particles having a particle diameter of 1 .Math.m to 30 .Math.m are prepared into the slurry that is coated on the lithium metal layer.

9. The method for manufacturing the negative electrode according to claim 7, wherein the active material particles comprise a carbon-based material, a lithium metal oxide, a metallic compound capable of alloying with lithium, a metal oxide, a lithium-metal alloy, or a mixture of two or more thereof.

10. The method for manufacturing the negative electrode according to claim 7, wherein the rolling the preliminary negative electrode is performed in a moisture controlled dry environment.

11. The method for manufacturing the negative electrode according to claim 7, further comprising dropping and wetting 10 to 500 .Math.l of a reduction-resistant liquid on the protective layer.

12. The method for manufacturing the negative electrode according to claim 7, wherein the rolling the preliminary negative electrode is performed under a pressure of 0.1 MPa to 5 MPa.

13. A battery comprising: a battery housing; and an electrode assembly accommodated in the battery housing with a lithium non-aqueous electrolyte, the electrode assembly comprising: a negative electrode comprising a metal current collector substrate; a lithium metal layer formed on at least one surface of the metal current collector substrate; a pre-lithiation layer formed on the lithium metal layer; a lithium electrodeposition layer formed on the pre-lithiation layer, the pre-lithiation layer comprising a pre-lithiated active material; a positive electrode comprising a positive electrode mixture including an active material, the positive electrode mixture being coated on at least one surface of a positive electrode current collector; and a separator between the negative electrode and the positive electrode.

14. The battery according to claim 13, wherein the active material is a carbon-based material, a lithium metal oxide, a metallic compound capable of alloying with lithium, a metal oxide, a lithium-metal alloy, or a mixture of two or more thereof.

15. The battery according to claim 13, wherein the lithium electrodeposition layer is formed- by charging the battery.

16. The method for manufacturing the negative electrode according to claim 7, wherein the active material particles having a particle diameter of 1 nm to 1000 nm are prepared into the dispersion that is coated on the lithium metal layer.

17. The method for manufacturing the negative electrode according to claim 7, wherein the step of dropping and wetting 10 to 500 .Math.l of the reduction-resistant liquid on the protective layer is performed after coating and drying the slurry or dispersion on the lithium metal layer.

18. The negative electrode according to claim 1, wherein the lithium metal layer has a thickness of at least 1 .Math.m.

19. The battery according to claim 13, wherein the lithium metal layer has a thickness of 1 .Math.m to 100 .Math.m.

20. An electrode assembly comprising: a negative electrode comprising a metal current collector substrate; a lithium metal layer formed on at least one surface of the metal current collector substrate; a pre-lithiation layer formed on the lithium metal layer; a lithium electrodeposition layer formed on the pre-lithiation layer; a positive electrode comprising a positive electrode mixture, the positive electrode mixture being coated on at least one surface of a positive electrode current collector; and a separator between the negative electrode and the positive electrode.

Description

DESCRIPTION OF DRAWINGS

[0038] The accompanying drawings illustrate embodiments of the present disclosure, and together with the detailed description of the present disclosure described below, serve to provide a further understanding of the technical aspects of the present disclosure, and thus the present disclosure should not be construed as being limited to the drawing.

[0039] FIG. 1 is an image of a reference negative electrode in which a protective layer is not formed;

[0040] FIG. 2 is an image of the negative electrode of Comparative Example 1; and

[0041] FIG. 3 is an image of the negative electrode of Example 1.

DETAILED DESCRIPTION

[0042] Hereinafter, the present disclosure will be described in more detail for a better understanding.

[0043] Terms or words used in the present specification and claims should not be construed as being limited to ordinary or dictionary terms, and the present disclosure should be construed with meanings and concepts that are consistent with the technical idea of the present disclosure based on the principle that the inventors may appropriately define concepts of the terms to appropriately describe their own disclosure in the best way.

[0044] The technical terms provided herein is merely used for the purpose of describing particular embodiments only, and is not intended to be limiting of the present disclosure. The singular forms “a,” “an,” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise.

[0045] Further, throughout the specification, when a portion is referred to as “including” a certain component, it means that the portion can further include other components, without excluding the other components, unless otherwise stated.

[0046] According to one embodiment of the present disclosure, a negative electrode for a lithium metal battery may be provided. The lithium metal battery may comprise a metal current collector substrate, a lithium metal layer formed on at least one surface of the metal current collector substrate, and a pre-lithiation layer formed on the lithium metal layer. The pre-lithiation layer may comprise a pre-lithiated active material, and the lithium metal layer may have a thickness of 1 .Math.m or more.

[0047] The metal current collector substrate may be one selected from the group consisting of copper, stainless steel, aluminum, nickel, titanium, calcined carbon, copper that is surface-treated with dissimilar metal, stainless steel that is surface-treated with dissimilar metal, and an aluminum-cadmium alloy.

[0048] The metal current collector substrate may be a metal including copper.

[0049] The lithium metal layer is a negative electrode active material, and the thickness and amount thereof may be determined according to the desired purpose, but is not limited thereto. In the present disclosure, the lithium metal layer may exist to the extent that it can act as a negative electrode active material even after the pre-lithiation layer is formed to function as a lithium metal battery, and the lithium metal layer may have at least a thickness of 1 .Math.m or more, 5 .Math.m or more, 10 .Math.m or more, 20 .Math.m or more. Further, the lithium metal layer may have a thickness of 200 .Math.m or less, 100 .Math.m or less, 80 .Math.m or less, or 50 .Math.m or less so that the volume of the entire negative electrode does not become too large and outside of a predetermined range of volume.

[0050] When the thickness of the lithium metal layer is too thin and outside the above range, lithium may not be sufficient as an active material, but the lithium electrodeposition layer may be formed during charging and discharging of the secondary battery and may function like an active material. Since the energy density relative to the volume may be decreased when the thickness of the lithium metal layer is too thick. Accordingly, it is most to satisfy the above range for the lithium metal layer.

[0051] That is, the present disclosure describes a negative electrode for a lithium metal battery having a lithium metal layer that exists even after pre-lithiation.

[0052] Further, the thickness ratio of the lithium metal layer and the pre-lithiation layer may be designed in consideration of the amount of excess Li provided, energy density, and the like. However, in order to prepare the lithium metal battery of the present disclosure, both the lithium metal layer and the pre-lithiation layer may exist to have a predetermined thickness or more. Thus, the thickness ratios between the metal layer and the pre-lithiation layer may be in a range of 99:1 to 1:99, and specifically in a range of 5:1 to 1:5. More specifically, as the pre-lithiation layer is formed, the lithium of the lithium metal layer may be intercalated into the pre-lithiation layer. The thickness of the lithium negative electrode layer that is vapor-deposited or electrodeposited during the manufacturing process may be partially reduced compared to the thickness of the lithium negative electrode layer, so that the thickness may be made smaller than the thickness of the pre-lithiation layer. The thickness ratio may be 1:1.1 to 1:5, specifically, 1:2 to 1:5, and more specifically, 1:2 to 1:4.

[0053] When the thickness of the lithium metal layer is too thin and outside the above range, the present disclosure may exhibit the same energy density versus volume as that of a lithium ion/polymer battery by using an existing carbon-based material or the like as a negative electrode active material, rather than a lithium metal battery for exhibiting high energy density by using a lithium metal as an active material, which is not preferable. When the thickness of the pre-lithiation layer is too thin and outside the above range, the provision of Li is not sufficient, and the lithium electrodeposition layer may also be formed at a low density, and thus side reactions due to direct contact with the electrolyte may be severe, and rapid deterioration of the lifespan characteristics may occur, which is not preferable.

[0054] Meanwhile, the pre-lithiation layer can be formed by pre-lithiating a material capable of occluding and releasing lithium so as to provide the excess Li, whereby the active material, that is, an active material capable of occluding and releasing lithium may be included in a pre-lithiated state.

[0055] The active material may be, for example, a carbon-based material, a lithium metal oxide, a metallic compound capable of alloying with lithium, a metal oxide, a lithium-metal alloy, or a mixture of two or more thereof. Specifically, the active material may be a carbon-based material, a lithium metal oxide, a metallic compound, or a metal oxide, which is a material with a large capacity capable of occluding lithium, which may be a Si-based material, a Sn-based material, or a mixture thereof.

[0056] Accordingly, the pre-lithiation layer may include an active material in which the above-mentioned materials are pre-lithiated.

[0057] By “is pre-lithiated” is meant herein a form in which lithium is diffused and intercalated between active materials capable of occluding and releasing lithium, or lithium is combined with the active materials.

[0058] Herein, the carbon-based material may be, for example, carbon such as artificial graphite, natural graphite, graphitized carbon fiber, or amorphous carbon.

[0059] The lithium metal oxide may be, for example, Li.sub.xFe.sub.2O.sub.3(0≤x≤1), Li.sub.xWO.sub.2(0≤x≤1), Li.sub.aTi.sub.bO.sub.4(0.5≤a≤3, 1≤b≤2.5), and the like.

[0060] The metallic compound capable of alloying with lithium may be a compound including a metal forming an alloy with lithium, which may be a metal such as Al, Ge, Mg, Zn, Ag, Si, or Sn.

[0061] Further, the metal oxide may be, for example, a material such as SiO.sub.x(1≤x≤2), SnO, SnO.sub.2, PbO, PbO.sub.2, Pb.sub.2O.sub.3, Pb.sub.3O.sub.4, Sb.sub.2O.sub.3, Sb.sub.2O.sub.4, Sb.sub.2O.sub.5, GeO, GeO.sub.2, Bi.sub.2O.sub.3, Bi.sub.2O.sub.4, or Bi.sub.2O.sub.5.

[0062] Finally, the metal in the lithium-metal alloy may be a metal such as Na, K, Rb, Cs, Fr, Be, Sr, Ba, Ra, Mg, Ca, Al, Ge, Pb, As, Sb, Bi, Ag, Zn, Cd, P, or Hg, and the lithium-metal alloy may be an alloy of the above metals and lithium.

[0063] Meanwhile, the pre-lithiation layer may include materials that is often used as a negative electrode active material. In the absence of a binder, the binder effect may be supplemented through coating, drying, and rolling, and a conductive material may also not be included. However, when the thickness of the pre-lithiation layer becomes thicker, a binder for further binding them and a conductive material for enhancing conductivity may be additionally more included.

[0064] Specific examples of the binder may include polyvinylidene fluoride (PVDF), vinylidene fluoride-hexafluoropropylene copolymer (PVDF-co-HFP), polyvinyl alcohol, polyacrylonitrile, carboxymethylcellulose(CMC), starch, hydroxypropyl cellulose, regenerated cellulose, polyvinylpyrrolidone, polytetrafluoroethylene, polyethylene, polypropylene, ethylene-propylene-diene polymer (EPDM), sulfonated-EPDM, styrene butadiene rubber (SBR), fluororubber, or various copolymers thereof. The active material capable of occluding and releasing lithium and the binder may be included in a ratio of 7:3 to 99:1 based on their weight.

[0065] When the content of the binder is too large and outside the above range, the pre-lithiation layer may be formed and thus the amount of excess Li to be achieved may be reduced, and when the content of the binder is too small and outside the above range, binding to the lithium metal layer may not be performed well, which is not preferable.

[0066] According to another embodiment of the present disclosure, there is provided a method for manufacturing the negative electrode, the method comprising the steps of: (a) placing, electrodepositing or vapor-depositing lithium metal on at least one surface of the metal current collector substrate to form a lithium metal layer; (b) mixing or dispersing active material particles together with a solvent to prepare a slurry or dispersion; (c) coating the slurry or dispersion on the lithium metal layer of the step (a) and drying to form a protective layer, thereby producing a preliminary negative electrode; and (d) rolling the preliminary negative electrode and reacting lithium metal with the protective layer, thereby performing pre-lithiation of the protective layer, wherein in the step (a), the loading amount of the lithium metal is formed to be larger than the loading amount of the protective layer, so that the lithium metal layer exits even after pre-lithiation.

[0067] That is, according to the present disclosure, since the lithium metal must function as a negative electrode active material, the lithium metal layer should exist at a predetermined thickness or more even after pre-lithiation. Therefore, when forming the lithium metal layer, the loading amount of lithium metal should be formed to be larger than the loading amount of the protective layer.

[0068] In this case, even if the protective layer is pre-lithiated to form a pre-lithiation layer, the lithium metal layer can maintain a thickness equal to or greater than a predetermined thickness as described above.

[0069] For example, when the loading amount of the protective layer is formed as 3 mAh/cm.sup.2, the lithium metal layer has a loading amount of 3 mAh/cm.sup.2 at the time of having a thickness of 15 .Math.m, and therefore must have a thickness of 16 .Math.m or more.

[0070] Meanwhile, in the manufacturing method, a protective layer is formed by coating on the lithium metal layer formed on at least one surface of the metal current collector substrate, and pre-lithiation is performed thereon, but the manufacturing method differs depending on the particle diameter of the active material particles contained in the protective layer.

[0071] Specifically, in the step (b), the particles may have a particle diameter (D50) of 1 .Math.m to 30 .Math.m. In this case, the step can be performed by a process of preparing a slurry such as an active material slurry and coating it onto the lithium metal layer. In the step (b), the particles may have a particle diameter (D50) of 1 nm to 1000 nm. In this case, the step can be performed by a process of preparing a pre-dispersion liquid containing these particles and coating it onto the lithium metal layer, as in a method of preparing a conductive material pre-dispersion.

[0072] The particle diameter (D50) is the average diameter (D50) of the particles, which means a particle diameter corresponding to a point of 50% in the cumulative distribution of the number of particles relative to the particle diameter. That is, D50 is the particle diameter corresponding to a point of 50% in the cumulative distribution of the number of particles relative to the particle diameter.

[0073] This can be measured by using a laser diffraction method. Specifically, the powder to be measured is dispersed in a dispersion medium, and then introduced into a commercially available laser diffraction particle size analyzer (e.g., Microtrac S3500). When the particles pass through the laser beam, the diffraction pattern difference according to the particle size is measured to calculate the particle size distribution. D50 can be measured by calculating the particle diameter corresponding a point of 50% in the cumulative distribution of the number of particles relative to the particle diameter in the analyzer.

[0074] In addition, in the manufacturing method as described above, in order to perform the pre-lithiation according to the present disclosure and obtain the effect resulting therefrom, the protective layer preferably has an appropriate porosity in order for lithium of the lithium metal layer to be easily intercalated. Specifically, the porosity of the protective layer preferably has a porosity of at least 5% or more, specifically 10% or more, and more specifically, 20% or more, and it preferably has a porosity of 70% or less, specifically 60% or less, and more specifically 50% or less.

[0075] Meanwhile, pre-lithiation of the particles contained in the protective layer can be performed by performing the rolling after forming the protective layer.

[0076] The present inventors confirmed that by performing the rolling in this way, the lithium of the lithium metal layer reacts with the active materials of the protective layer to perform the pre-lithiation.

[0077] Herein, the active material may be a carbon-based material, a lithium metal oxide, a metallic compound capable of alloying with lithium, a metal oxide, a lithium-metal alloy, or a mixture of two or more thereof.

[0078] Therefore, according to the present disclosure, since a separate electrolyte solution or the like becomes unnecessary, pre-lithiation can be performed in a simpler and easier way. Therefore, it is possible to save manufacturing cost as well, and impurities such as other solutions are not required, the problem of internal resistance increase does not occur, and thus, it is also excellent from the viewpoint of battery performance.

[0079] At this time, the rolling of the step (d) is preferably performed in a dry environment where moisture is controlled, but in some cases, between the steps (c) and (d), the wet rolling can also be performed further including (c’) a step of dropping and wetting 10 to 500 .Math. 1 of a reduction-resistant liquid on the protective layer.

[0080] The reduction-resistant liquid may be, for example, selected from the group consisting of carbonate-based solvents such as dimethyl carbonate, diethyl carbonate, and ethylmethyl carbonate, and ether-based solvents such as 1,2-dimethoxyethane and 1,3-dioxolane, which can facilitate the rapid pre-lithiation even at ultra-low pressure when there is a time constraint

[0081] The rolling in the step (d) is not limited as long as it is the extent that pre-lithiation from the lithium metal layer to the protective layer is possible, and the time may differ depending on the strength of rolling, but specifically, the rolling can be performed at a pressure of 0.1 MPa to 5 MPa, and it can be performed, for example, for 30 minutes to 90 hours until the time when the protective layer is completely pre-lithiated.

[0082] When the pre-lithiation is performed at a very low pressure or for a very short time and outside the above range, the pre-lithiation cannot be sufficiently performed. When the pre-lithiation is performed at a very high pressure or for a very long time, the process time increases compared to the improved effect, which is not preferable in terms of process efficiency.

[0083] According to yet another embodiment of the present disclosure, there is provided a lithium metal battery in which an electrode assembly is built together with a lithium non-aqueous electrolyte in a battery case (or housing), with the electrode assembly comprising: a negative electrode which comprises a metal current collector substrate, a lithium metal layer formed on at least one surface of the metal current collector substrate, a pre-lithiation layer formed on the lithium metal layer, and a lithium electrodeposition layer formed on the pre-lithiation layer, wherein the pre-lithiation layer comprises a pre-lithiated active material, and wherein the lithium metal layer has a thickness of 1 .Math.m or more; a positive electrode having a structure in which a positive electrode mixture including an active material is coated onto at least one surface of a positive electrode current collector; and a separator interposed between the negative electrode and the positive electrode.

[0084] Herein, the active material may be a carbon-based material, a lithium metal oxide, a metal compound capable of alloying with lithium, a metal oxide, a lithium-metal alloy, or a mixture of two or more thereof.

[0085] Meanwhile, the lithium electrodeposition layer is formed by charging a lithium metal battery.

[0086] That is, according to an embodiment of the present disclosure, a lithium metal battery is provided using a lithium metal layer, and a lithium electrodeposition layer subsequently formed as a negative electrode active material, wherein even by a simpler method of forming a protective layer on the lithium metal layer and performing the pre-lithiation by rolling, side reactions and the like that cause problems during the manufacturing process of the lithium metal battery and during the operation process thereof can be prevented, and the lifespan characteristics can be improved by providing excess Li.

[0087] Meanwhile, the positive electrode has a structure in which a positive electrode mixture including an active material is coated onto at least one surface of a positive electrode current collector.

[0088] The positive electrode current collector is not particularly limited as long as it has conductivity while not causing chemical changes to the battery, and for example, stainless steel, aluminum, nickel, titanium, calcined carbon, or aluminum or stainless steel having a surface treated with carbon, nickel, titanium, silver, and the like can be used. In addition, the positive electrode current collector may have a thickness of 3 to 500 .Math.m, and may have fine irregularities formed on the surface of the current collector to increase the adhesion of the positive electrode active material. For example, it may be used in various forms such as films, sheets, foils, nets, porous bodies, foams, and nonwoven fabrics.

[0089] The positive electrode active material as the active material may include, for example, a layered compound such as lithium nickel oxide (LiNiO.sub.2), or a compound substituted with one or more transition metals; lithium manganese oxides such as chemical formulae Li.sub.1+xMn.sub.2-xO.sub.4 (where x = 0 ~ 0.33), LiMnO.sub.3, LiMn.sub.2O.sub.3, LiMnO.sub.2; lithium copper oxide (Li.sub.2CuO.sub.2); vanadium oxides such as LiV.sub.3O.sub.8, LiV.sub.3O.sub.4, V.sub.2O.sub.5, and Cu.sub.2V.sub.2O.sub.7; a Ni-site type lithium nickel oxide represented by chemical formula LiNi.sub.1-xM.sub.xO.sub.2 (where M = Co, Mn, Al, Cu, Fe, Mg, B or Ga, and x= 0.01~ 0.3); lithium manganese composite oxide represented by chemical formulae LiMn.sub.2-xM.sub.xO.sub.2 (where M = Co, Ni, Fe, Cr, Zn or Ta, and x = 0.01~0.1) or Li.sub.2Mn.sub.3MO.sub.8 (where M = Fe, Co, Ni, Cu or Zn ); LiNi.sub.xMn.sub.2-xO.sub.4; LiMn.sub.2O.sub.4 in which a part of Li in the chemical formula is substituted with an alkaline earth metal ion; a disulfide compound; Fe.sub.2(MoO.sub.4).sub.3, and the like, without being limited thereto.

[0090] The positive electrode mixture may further include a conductive material and a binder together with the positive electrode active material described above.

[0091] The conductive material is typically added in an amount of 0.1 to 30% by weight, specifically 1 to 10% by weight, and more specifically 1 to 5% by weight based on the total weight of the positive electrode mixture layer. The conductive material is not particularly limited as long as it has high conductivity without causing a chemical change in the corresponding battery, and for example, graphite such as natural graphite and artificial graphite; carbon blacks such as carbon black, acetylene black, ketjen black, channel black, furnace black, lamp black, and thermal black; conductive fibers such as carbon fiber and metal fiber; carbon fluoride powder; metal powders such as aluminum powder, and nickel powder; conductive whiskey such as zinc oxide and potassium titanate; conductive metal oxides such as titanium oxide; conductive materials such as polyphenylene derivatives can be used.

[0092] The binder is a component that assists in coupling of an active material, a conductive material, and the like, and in coupling of a current collector, and typically, may be added in an amount of 0.1 to 30% by weight, specifically 1 to 10% by weight, more specifically 1 to 5% by weight based on the total weight of the positive electrode mixture layer. An example of the binder may include polyvinylidene fluoride, polyvinylidene fluoride-hexafluoropropylene, polyvinyl alcohol, carboxymethyl cellulose (CMC), starch, hydroxypropyl cellulose, regenerated cellulose, polyvinylpyrrolidone, polytetrafluoroethylene, polyethylene, polypropylene, ethylene-propylene-diene polymer (EPDM), sulfonated EPDM, styrene-butadiene rubber, fluorine rubber, various copolymers, and the like.

[0093] The separator is an insulating thin film having high ion permeability and mechanical strength. The pore diameter of the separator is generally 0.01 to 10 .Math.m, and the thickness is generally 5 to 300 .Math.m. As such separator, for example, chemical resistant and hydrophobic olefin-based polymers such as polypropylene; sheets or non-woven fabrics made of glass fiber or polyethylene is used. When a solid electrolyte such as a polymer is used as the electrolyte, the solid electrolyte may also serve as a separator.

[0094] The lithium non-aqueous electrolyte may include a lithium salt and a non-aqueous solvent. As the non-aqueous solvent, a non-aqueous organic solvent, an organic solid electrolyte, an inorganic solid electrolyte, or the like is used, but is not limited thereto.

[0095] As examples of the non-aqueous electrolyte, mention may be made of non-protic organic solvents, such as N-methyl-2-pyrrolidone, propylene carbonate, ethylene carbonate, butylene carbonate, dimethyl carbonate, diethyl carbonate, gamma-butyro lactone, 1,2-dimethoxy ethane, tetrahydrofuran, 2-methyl tetrahydrofuran, dimethylsulfoxide, 1,3-dioxolane, formamide, dimethylformamide, dioxolane, acetonitrile, nitromethane, methyl formate, methyl acetate, phosphoric acid triester, trimethoxy methane, dioxolane derivatives, sulfolane, methyl sulfolane, 1,3-dimethyl-2-imidazolidinone, propylene carbonate derivatives, tetrahydrofuran derivatives, ether, methyl propionate, and ethyl propionate.

[0096] Examples of the organic solid electrolyte include polyethylene derivatives, polyethylene oxide derivatives, polypropylene oxide derivatives, phosphoric acid ester polymers, poly agitation lysine, polyester sulfide, polyvinyl alcohols, polyvinylidene fluoride, and polymers containing ionic dissociation groups, and the like.

[0097] Examples of the inorganic solid electrolyte include nitrides, halides and sulfates of lithium (Li) such as Li.sub.3N, LiI, Li.sub.5NI.sub.2, Li.sub.3N—LiI—LiOH, LiSiO.sub.4, LiSiO.sub.4—LiI—LiOH, Li.sub.2SiS.sub.3, Li.sub.4SiO.sub.4, Li.sub.4SiO.sub.4—LiI—LiOH, and Li.sub.3PO.sub.4—Li.sub.2S—SiS.sub.2.

[0098] The lithium salt is a material that is readily soluble in the non-aqueous electrolyte. The lithium salt may include, for example, LiCl, LiBr, LiI, LiClO.sub.4, LiBF.sub.4, LiB.sub.10Cl.sub.10, LiPF.sub.6, LiCF.sub.3SO.sub.3, LiCF.sub.3CO.sub.2, LiAsF.sub.6, LiSbF.sub.6, LiAlCl.sub.4, CH.sub.3SO.sub.3Li, CF.sub.3SO.sub.3Li, (CF.sub.3SO.sub.2).sub.2NLi, chloroborane lithium, lower aliphatic carboxylic acid lithium, lithium tetraphenyl borate, and imide.

[0099] In addition, in order to improve charge/discharge characteristics, flame retardancy and the like, the non-aqueous electrolyte may further include, for example, pyridine, triethylphosphite, triethanolamine, cyclic ether, ethylenediamine, n-glyme, hexaphosphoric triamide, nitrobenzene derivatives, sulfur, quinone imine dyes, N-substituted oxazolidinone, N,N-substituted imidazolidine, ethylene glycol dialkyl ether, ammonium salts, pyrrole, 2-methoxy ethanol, aluminum trichloride, or the like. In some cases, in order to impart incombustibility, the electrolyte may further include halogen-containing solvents, such as carbon tetrachloride and ethylene trifluoride. Furthermore, in order to improve high-temperature retention characteristics, the electrolyte may further include carbon dioxide gas. In addition, it may further include fluoroethylene carbonate (FEC), propene sultone (PRS), and the like.

[0100] The battery case (or housing) is not limited as long as it has a structure capable of housing an electrode assembly, and may be a pouch type battery, or a prismatic or cylindrical battery case (or housing) made of a metal can, which is known in the art.

[0101] Hereinafter, preferred examples of the present disclosure, comparative examples for comparing them, and experimental examples for evaluating them are described. However, it will be obvious to those skilled in the art that these examples are for illustrative purposes only and various changes and modifications can be made without deviating from the scope and spirit of the present description, and it goes without saying that such modifications and modifications fall within the scope of the appended claims.

Comparative Example 1

[0102] A commercially available copper current collector (I2B, Iljin Materials) was prepared as a metal current collector substrate.

[0103] A lithium foil (Li foil, thickness: 20 .Math.m) was placed so as to be opposed to one surface of the copper current collector, and then the current collector and the lithium foil were laminated and roll-pressed to the extent that they did not detach, thereby forming a lithium metal layer.

[0104] Further, artificial graphite (particle diameter (D50): 9 .Math.m), and binder (PVDF) were mixed in a weight ratio of 9:1 in an NMP solvent so that the solid content : NMP solvent was 5:5 by volume, thereby forming a protective layer slurry. The resulting slurry was coated to a thickness of 40 .Math.m onto the lithium metal layer, dried to form a protective layer. Thereby, the negative electrode of Comparative Example 1 was obtained.

Comparative Example 2

[0105] A commercially available copper current collector (I2B, Iljin Materials) was prepared as a metal current collector substrate.

[0106] A lithium foil (Li foil, thickness: 30 .Math.m) was placed so as to be opposed to one surface of the copper current collector, and then the current collector and the lithium foil were laminated and roll-pressed to the extent that they did not detach, thereby forming a lithium metal layer.

[0107] Further, artificial graphite (particle diameter (D50): 9 .Math.m), and binder (PVDF) were mixed in a weight ratio of 9:1 in an NMP solvent so that the solid content : NMP solvent was 5:5 by volume, thereby forming a protective layer slurry. The resulting slurry was coated to a thickness of 40 .Math.m on the lithium metal layer, dried to form a protective layer. Thereby, the negative electrode was obtained. 1M LiPF.sub.6 was dissolved in a mixed solvent of ethylene carbonate (EC) and diethyl carbonate (DEC) in a volume ratio of 50:50 to prepare a pre-lithiation solution. The above produced negative electrode was impregnated in this solution, and then left at a temperature of 25° C. Finally, a negative electrode of Comparative Example 2 having a thickness of 60 .Math.m was obtained in the same manner as in Comparative Example 1, excluding the current collector.

Comparative Example 3

[0108] A commercially available copper current collector (I2B, Iljin Materials) was prepared as a metal current collector substrate.

[0109] A lithium foil (Li foil, thickness: 15 .Math.m) was placed so as to be opposed to one surface of the copper current collector, and then the current collector and the lithium foil were laminated and roll-pressed to the extent that they did not detach, thereby forming a lithium metal layer.

[0110] Further, artificial graphite (particle diameter (D50): 9 .Math.m), and binder (PVDF) were mixed in a weight ratio of 9:1 in an NMP solvent so that the solid content : NMP solvent was 5:5 by volume, thereby forming a protective layer slurry. The resulting slurry was coated to a thickness of 60 .Math.m onto the lithium metal layer, dried to form a protective layer, thereby obtaining the negative electrode. The negative electrode was rolled at a pressure of 1 MPa, left in a dry room for 12 hours, and all active material layers were pre-lithiated, so that a negative electrode of Comparative Example 3 having a thickness of 60 .Math.m was obtained in the same manner as in Comparative Example 1, excluding the current collector.

Example 1

[0111] A commercially available copper current collector (I2B, Iljin Materials) was prepared as a metal current collector substrate.

[0112] A lithium foil (Li foil, thickness: 30 .Math.m) was placed so as to be opposed to one surface of the copper current collector, and then the current collector and the lithium foil were laminated and roll-pressed to the extent that they did not detach, thereby forming a lithium metal layer.

[0113] Further, artificial graphite (particle diameter (D50): 9 .Math.m), and binder (PVDF) were mixed in a weight ratio of 9:1 in an NMP solvent so that the solid content : NMP solvent was 5:5 by volume, thereby forming a protective layer slurry. The resulting slurry was coated to a thickness of 40 .Math.m onto the lithium metal layer, dried to form a protective layer, thereby obtaining a negative electrode. The negative electrode was rolled at a pressure of 1 MPa, and then left in a dry room for 12 hours, so that a negative electrode of Example 1 having a thickness of 60 .Math.m was obtained in the same manner as in Comparative Example 1, excluding the current collector.

Example 2

[0114] A commercially available copper current collector (I2B, Iljin Materials) was prepared as a metal current collector substrate.

[0115] A lithium foil (Li foil, thickness: 25 .Math.m) was placed so as to be opposed to one surface of the copper current collector, and then the current collector and the lithium foil were laminated and roll-pressed to the extent that they did not detach, thereby forming a lithium metal layer.

[0116] Further, lithium metal oxide Li.sub.4Ti.sub.5O.sub.12 (particle diameter (D50): 1 .Math.m), and binder (PVDF) were mixed in a weight ratio of 9:1 in an NMP solvent so that the solid content: NMP solvent was 5:5 by volume, thereby forming a protective layer slurry. The resulting slurry was coated to a thickness of 40 .Math.m on the lithium metal layer, dried to form a protective layer. Then, the resulting negative electrode was rolled at a pressure of 1 MPa, left in a dry room for 12 hours, and all active material layers were pre-lithiated, so that a negative electrode of Example 2 having a thickness of 60 .Math.m was obtained in the same manner as in Comparative Example 1, excluding the current collector.

Experimental Example 1

[0117] A negative electrode in which a protective layer was not formed was used as a reference, and surface photographs of the reference negative electrode as well as the negative electrodes of Comparative Example 1 and Example 1 were taken, and are shown in FIGS. 1 to 3 below.

[0118] Referring to FIGS. 1 to 3, it can be confirmed that the negative electrode of Comparative Example 1 in which the protective layer was formed was coated with a carbon-based material to form a black protective layer unlike FIG. 1 in which only the lithium metal layer was coated. Meanwhile, referring to FIG. 3, it can be confirmed that the carbon-based material was coated similarly, but was pre-lithiated with the lithium metal layer by rolling, and the color was changed to gold. It can be confirmed therefrom that the pre-lithiation was well performed by rolling.

Experimental Example 2

[0119] LiNi.sub.0.8Mn.sub.0.1Co.sub.0.1O.sub.2 as a positive electrode active material, carbon black as a conductive material, and polyvinylidene fluoride (PVdF) as a binder were used, respectively. The positive active material: the conductive material: the binder were mixed in a weight ratio of 96:2:2, and NMP as a solvent was added to the resulting mixture to prepare a positive electrode active material slurry.

[0120] The positive electrode active material slurry was coated at a loading amount of 4.05 mAh/cm.sup.2 per one side of an aluminum current collector, and then dried and rolled to obtain a positive electrode.

[0121] The electrolyte solution contains a solvent in which propylene carbonate (PC), diethyl carbonate (DEC) and dimethyl carbonate (DMC) were mixed in a volume ratio of 1:2:1 (PC:DEC:DMC). The electrolyte solution containing 1M LiFSI, 1M LiPF.sub.6 and 30 wt.% of fluoroethylene carbonate (FEC) in the total amount of the electrolyte solution was prepared.

[0122] A polyethylene separator (thickness: 20 um) was interposed between the negative electrodes of Comparative Examples 1 to 3 and Examples 1 to 2 and the positive electrode, then the electrolyte solution was injected, and a CR2032 coin cell was manufactured according to a conventional method to obtain lithium metal batteries.

[0123] The lithium metal batteries manufactured above were charged and discharged 300 times under the following conditions, and then the 300-time discharge capacity retention relative to the one-time discharge capacity was calculated, and the results are shown in Table 1 below. Charge: 0.2 C, CC/CV, 4.25 V, ⅟20C cut-off Discharge: 0.5 C, CC, 3.0 V, cut-off

TABLE-US-00001 one-time discharge capacity (mAh) 300-time capacity retention (%) Comp arative Example 1 6.05 80 Comp arative Example 2 6.13 88 Comp arative Example 3 6.10 87 Exam ple 1 6.15 98 Exam ple 2 6.17 97

[0124] Referring to Table 1, it was confirmed that all the assembled cells exhibited similar initial discharge capacity.

[0125] However, it was confirmed that in the case of the cells in which a part of the lithium metal layer was reacted with the protective layer and the pre-lithiation of the protective layer was performed (Examples 1 and 2), the lifespan characteristics were excellent.

[0126] Meanwhile, it can be confirmed that in the case of Comparative Example 3, in which all of the lithium metal layers was reacted with the protective layer, the lithium metal layer disappeared, and only the pre-lithiated protective layer remained, the lifespan characteristics were better than Comparative Example 1 in which pre-lithiation was not performed, but sufficient lifespan characteristics were not exhibited as compared with Examples 1 and 2, in which a part of the lithium metal layer remained and the lithium metal was sufficiently used as an active material as in the present disclosure.

[0127] In addition, it can be confirmed that Comparative Example 2, in which pre-lithiation was performed with an electrolyte solution, also had better lifespan characteristics than Comparative Example 1 in which pre-lithiation was not performed, but as compared to the case of performing pre-lithiation by rolling as in the present disclosure, sufficient lifespan characteristics could not be exhibited due to the increased internal resistance of the cell due to the occurrence of a side reaction of the electrolyte solution.

[0128] Based on the above disclosure, various applications and modifications can be carried out by those of ordinary skill in the art without deviating from the spirit and scope of the present disclosure.

[0129] As described above, the negative electrode according to an embodiment of the present disclosure includes a pre-lithiation layer as a protective layer on the lithium metal layer, and thus it is possible to minimize the lithium metal from reacting with the atmosphere during the assembly process of the secondary battery, which is thus effective in lowering the increase in resistance.

[0130] Further, by performing the pre-lithiation rather than simply forming a protective layer with materials capable of occluding and releasing lithium, it is possible to increase the excess Li and improve the lifespan characteristics.

[0131] Moreover, the pre-lithiation may be performed by adopting a very simple method, for example, rolling, whereby not only the process is simplified but also the cost is reduced. In addition, there is no problem such as internal resistance increase by solvents, as compared with the pre-lithiation method using an electrolytic solvent, which is thus preferable in terms of battery performance.