COMPOSITIONS COMPRISING A GRAPHENE-BASED MATERIAL AS LUBRICANT ADDITIVES

Abstract

Nanoparticle compositions contain a graphene-based material. A preparation process involves providing several components and milling a mixture. The nanoparticle compositions can be used as a lubricant additive to improve tribological performance, in particular to improve anti-friction and anti-wear performance on metal parts. A corresponding lubricant composition contains these nanoparticle compositions.

Claims

1: A nanoparticle composition, comprising: one or more graphene nanoparticle (A), one or more polymer (B), one or more silane compound (C), and one or more base fluid (D), wherein the one or more graphene nanoparticle (A) is a multilayered graphene-based material containing oxygen groups, with a surface area BET between 200 n/g and 1,500 m.sup.2/g, and G/D ratio between 0.5 and 2 in accordance with ISO/TS 80004-13, wherein the one or more polymer (B) is obtainable by polymerizing a monomer composition comprising: a) 1 to 30% by weight, based on a total weight of the monomer composition, of one or more functional monomer selected from the group consisting of: a1) aminoalkyl (meth)acrylates and aminoalkyl (meth)acrylamides; a2) nitriles of alkyl (meth)acrylic acid and other nitrogen-containing alkyl (meth)acrylates; a3) (meth)acrylates of ether alcohols; a4) oxiranyl alkyl (meth)acrylate; a5) phosphorus-, boron-A and/or silicon-containing alkyl (meth)acrylates; a6) heterocyclic alkyl (meth)acrylates; a7) vinyl halides; a8) vinyl esters; a9) vinyl monomers containing aromatic groups; a10) heterocyclic vinyl compounds; a11) vinyl and isoprenyl ethers; and a12) methacrylic acid and acrylic acid, b) 30 to 70% by weight of one or more alkyl (meth)acrylate monomer, wherein each alkyl group of the one or more alkyl (meth)acrylate monomer is independently linear, cyclic, or branched and comprises from 1 to 40 carbon atoms, based on the total weight of the monomer composition, and c) 20 to 60% by weight of one or more polybutadiene-based macromonomer having a number-average molecular weight (M.sub.n) of 500 to 10,000 g/mol, based on the total weight of the monomer composition, wherein the nanoparticle composition comprises 0.02 to 5% by weight, based on a total weight of the nanoparticle composition, of the one or more silane compound (C) of formula (IV)
Si(R)(M).sub.h(X).sub.3-h(IV), wherein 0h2; M is a branched or linear C.sub.1 to C.sub.4 alkyl residue, R is a branched or linear, aliphatic, aromatic, or mixed aliphatic-aromatic C.sub.1 to C.sub.30 carbon-based group, or R is a branched or linear, aliphatic, aromatic, or mixed aliphatic-aromatic C.sub.1 to C.sub.30 carbon-based group with a functional group selected from the group consisting of carboxy, carbonyl, hydroperoxycarbonyl, cyan, formyl, oxo, thioxo, hydroxy, amino, imino, hydrazino, and epoxy; X is selected from the group consisting of H, Cl, and a group OY, wherein Y is H or a C.sub.1 to C.sub.8 branched or linear alkyl-, alkenyl-, aryl-, or aralkyl-group, branched or linear C.sub.2 to C.sub.8 alkylether-group, or a mixture thereof; and wherein the nanoparticle composition is obtainable by milling.

2: The nanoparticle composition according to claim 1, wherein the one or more polybutadiene-based macromonomer c) has a number-average molecular weight (M.sub.n) of 1,500 to 7,500 g/mol.

3: The nanoparticle composition according to claim 1, wherein the one or more polymer (B) has a weight-average molecular weight (Mw) of 10,000 to 1,000,000 g/mol.

4: The nanoparticle composition according to claim 1, wherein the one or more polymer (B) is obtainable by polymerizing a monomer composition comprising: a) 1 to 30% by weight of the one or more functional monomer, as component a), based on the total weight of the monomer composition; and b1) 30 to 60% by weight of one or more alkyl (meth)acrylate of formula (I), as a first component b): ##STR00007## wherein R is hydrogen or methyl, R.sup.1 means a linear, branched, or cyclic alkyl residue with 1 to 8 carbon atoms, based on the total weight of the monomer composition; and b2) 0 to 20% by weight of one or more alkyl (meth)acrylate of formula (II), as a second component b): ##STR00008## wherein R is hydrogen or methyl, R.sup.2 means a linear, branched, or cyclic alkyl residue with 9 to 15 carbon atoms, based on the total weight of the monomer composition; and b3) 0 to 20% by weight of one or more alkyl (meth)acrylate of formula (III), as a third component b): ##STR00009## wherein R is hydrogen or methyl, R.sup.3 means a linear, branched, or cyclic alkyl residue with 16 to 40 carbon atoms, based on the total weight of the monomer composition; and c) 20 to 60% by weight of the one or more polybutadiene-based macromonomer having a number-average molecular weight (M.sub.n) of 500 to 10,000 g/mol, as component c), based on the total weight of the monomer composition.

5: The nanoparticle composition according to claim 4, wherein the one or more polymer compound (B) is obtainable by polymerizing a monomer composition comprising: a1) 0.5 to 5% by weight of an aminoalkyl, as a first component a), based on the total weight of the monomer composition; a9) 5 to 15% by weight of a vinyl monomer containing aromatic groups, as a second component a), based on the total weight of the monomer composition; b1) 35 to 50% by weight of the alkyl (meth)acrylate monomer of formula (1), as the first component b), based on the total weight of the monomer composition; b2) 1 to 10% by weight of the alkyl (meth)acrylate monomer of formula (II), as the second component b), based on the total weight of the monomer composition; c) 30 to 50% by weight of the one or more polybutadiene-based macromonomer having a number-average molecular weight (M.sub.n) of 500 to 10,000 g/mol, as the component c), based on the total weight of the monomer composition.

6: The nanoparticle composition according to claim 1, wherein the weight contents of monomers a), b), and c) of the monomer composition sum up to 100% by weight, based on the total weight of the monomer composition.

7: The nanoparticle composition according to claim 1, wherein the one or more silane compound (C) of formula (IV) is octyltrimethoxysilane, hexadecyltrimethoxysilane, 3-aminopropyltriethoxysilane or 3-glycidyloxypropyltriethoxysilane.

8: The nanoparticle composition according to claim 1, wherein the nanoparticle composition comprises: 1 to 20% by weight of the or more graphene nanoparticle (A), 0.5 to 30% by weight of the one or more polymer (B), 0.02 to 5% by weight of the one or more silane compound (C), 45 to 98.48% by weight of the one or more base fluid (D), based on the total weight of the nanoparticle composition.

9: The nanoparticle composition according to claim 8, wherein components A), B), C, and D) sim up to 100% by weight, based on the total weight of the nanoparticle composition.

10: A process for preparing the nanoparticle composition as defined in claim 1, the process comprising: (i) providing the one or more graphene nanoparticle (A); (ii) providing the one or more polymer (B); (iii) providing the one or more silane compound (C); (iv) providing the one or more base fluid (D); (v) combining components (A) to (D) to obtain a mixture; and (vi) milling the mixture of (v).

11: The process according to claim 10, wherein in (v) components (A) and (C) are first mixed together by spraying or ball milling and then mixed with components (B) and (D).

12: A lubricating oil composition, comprising: the nanoparticle composition as defined in claim 1, and one or more base oil (E).

13: The lubricating oil composition according to claim 12, wherein the lubricating oil composition further comprises one or more additive component (F) selected from the group consisting of an antioxidant, an anti-wear additive, a pour point depressant, a corrosion inhibitor, a metal passivator, an electrostatic discharge depressant, a defoaming agent, a seal fix, a seal compatibility agent, and a mixture thereof.

14. The lubricating oil composition according to claim 13, wherein the lubricating oil composition comprises, 50 to 9999% by weight of the one or more base oil (E), 0.01 to 50% by weight of the nanoparticle composition, and 0 to 20% by weight of the one or more additive component (F), based on a total weight of the lubricating oil composition.

15: A method for preparing a lubricating oil composition, the method comprising: combining the nanoparticle composition as defined in claim 1 with one or more base oil.

16: The nanoparticle composition according to claim 1, wherein in the formula (IV), R is selected from the group consisting of a linear aliphatic C.sub.8 carbon-based group, a linear aliphatic C.sub.16 carbon-based group, a linear aliphatic 3-aminopropyl group, and a 3-glycidyloxypropyl group, and/or X is methoxy or ethoxy.

17: The nanoparticle composition according to claim 3, wherein the one or more polymer (B) has a weight-average molecular weight (Mw) of 150,000 to 350,000 g/mol.

18: The nanoparticle composition according to claim 4, wherein the monomer composition comprises: 10 to 20% by weight of the component a), 35 to 50% y w % eight of the first component b), 1 to 10% by weight of the second component b), 0 to 10% by weight of the third component b), and 30 to 50% by weight of the component c), based on the total weight of the monomer composition.

19: The nanoparticle composition according to claim 5, wherein in the monomer composition: the first component a) is N-(3-dimethyl-aminopropyl)methacrylamide, the second component a) is styrene, the first component b) is methyl methacrylate and/or butyl methacrylate, the second component b) is lauryl methacrylate, and the component c) is a macromonomer derived from a reaction of an ester of a (meth)acrylic acid and a hydroxylated hydrogenated polybutadiene having a number-average molecular weight (Mu) of 1,500 to 5,500 g/mol.

20: The method according to claim 15, wherein the lubricating oil composition is a gear oil composition, a transmission oil composition, a hydraulic oil composition, an engine oil composition, a marine oil composition, an industrial lubricating oil composition, or grease.

Description

BRIEF DESCRIPTION OF THE DRAWING

[0019] For the purpose of better illustrating the advantages and properties of the claimed nanoparticle composition, object of the present invention, one graph is attached as a non-limiting example:

[0020] FIG. 1 is a graph showing the development of light transmittance values at 800 nm of an oil lubricating composition comprising 0.05% by weight of the nanoparticle composition IE1 as a function of storage time.

DETAILED DESCRIPTION OF THE INVENTION

[0021] Nanoparticle composition according to the invention Thus, the present invention relates to nanoparticle composition comprising one or more nanoparticle (A), one or more polymer (B), one or more silane compound (C) and one or more base fluid (D), wherein [0022] (A) the one or more nanoparticle (A) is a multilayered graphene-based material containing oxygen groups, with a surface area BET between 200 m.sup.2/g and 1,500 m.sup.2/g, and G/D ratio between 0.5 and 2, preferably with a surface area BET between 250 m.sup.2/g and 1,000 m.sup.2/g, more preferably between 350 m.sup.2/g and 800 m.sup.2/g, in accordance with ISO/TS 80004-13, [0023] (B) the one or more polymer (B) is obtainable by polymerizing a monomer composition comprising: [0024] a) 1 to 30% by weight, based on the total weight of the monomer composition, of one or more functional monomer selected from the list consisting of: [0025] a1) aminoalkyl (meth)acrylates and aminoalkyl (meth)acrylamides, preferably N-(3-dimethyl-aminopropyl)methacrylamide, 3-diethylaminopentyl (meth)acrylate, 3-dibutyl-aminohexadecyl (meth)acrylate; [0026] a2) nitriles of alkyl (meth)acrylic acid and other nitrogen-containing alkyl (meth)acrylates, preferably N-(methacryloyloxyethyl)diisobutylketimine, N-(methacryloyloxyethyl)dihexadecyl-ketimine, (meth)acryloylamidoacetonitrile, 2-methacryloyloxyethylmethylcyanamide, cyanomethyl (meth)acrylate; [0027] a3) (meth)acrylates of ether alcohols, preferably tetrahydrofurfuryl (meth)acrylate, methoxyethoxyethyl (meth)acrylate, 1-butoxypropyl (meth)acrylate, cyclohexyloxyethyl (meth)acrylate, propoxyethoxyethyl (meth)acrylate, benzyloxyethyl (meth)acrylate, furfuryl (meth)acrylate, 2-butoxyethyl (meth)acrylate, 2-ethoxy-2-ethoxyethyl (meth)acrylate, 2-methoxy-2-ethoxypropyl (meth)acrylate, ethoxylated (meth)acrylates, 1-ethoxybutyl (meth)acrylate, methoxyethyl (meth)acrylate, 2-ethoxy-2-ethoxy-2-ethoxyethyl (meth)acrylate, esters of (meth)acrylic acid and methoxy polyethylene glycols; [0028] a4) oxiranyl alkyl (meth)acrylate, preferably 2, 3-epoxybutyl (meth)acrylate, 3,4-epoxybutyl (meth)acrylate, 10,11 epoxyundecyl (meth)acrylate, 2,3-epoxycyclohexyl (meth)acrylate, oxiranyl (meth)acrylates such as 10,11-epoxyhexadecyl (meth)acrylate, glycidyl (meth)acrylate; [0029] a5) phosphorus-, boron- and/or silicon-containing alkyl (meth)acrylates, preferably like 2-(dimethyl-phosphato)propyl (meth)acrylate, 2-(ethylphosphito)propyl (meth)acrylate, 2 dimethylphosphinomethyl (meth)acrylate, dimethylphosphonoethyl (meth)acrylate, diethylmethacryloyl phosphonate, dipropylmethacryloyl phosphate, 2 (dibutylphosphono)ethyl (meth)acrylate, 2,3-butylenemethacryloylethyl borate, methyldiethoxymethacryloylethoxysiliane, diethylphosphatoethyl (meth)acrylate; [0030] a6) heterocyclic alkyl (meth)acrylates, preferably like 2-(1-imidazolyl)ethyl (meth)acrylate, 2-(4-morpholinyl)ethyl (meth)acrylate, oxazolidinylethyl (meth)acrylate and N-methacryloylmorpholine; [0031] a7) vinyl halides, preferably vinyl chloride, vinyl fluoride, vinylidene chloride and vinylidene fluoride; [0032] a8) vinyl esters, preferably vinyl acetate; [0033] a9) vinyl monomers containing aromatic groups, preferably styrene, substituted styrenes with an alkyl substituent in the side chain, such as alpha-methylstyrene and alpha-ethylstyrene, substituted styrenes with an alkyl substituent on the ring such as vinyltoluene and p-methylstyrene, halogenated styrenes such as monochlorostyrenes, dichlorostyrenes, tribromostyrenes and tetrabromostyrenes; [0034] a10) heterocyclic vinyl compounds, preferably 2-vinylpyridine, 3-vinylpyridine, 2-methyl-5-vinylpyridine, 3-ethyl-4-vinylpyridine, 2,3-dimethyl-5-vinylpyridine, vinylpyrimidine, vinylpiperidine, 9-vinylcarbazole, 3-vinylcarbazole, 4-vinylcarbazole, 1-vinylimidazole, 2-methyl-1-vinylimidazole, N-vinylpyrrolidone, 2-vinylpyrrolidone, N-vinylpyrrolidine, 3-vinylpyrrolidine, N-vinylcaprolactam, N-vinylbutyrolactam, vinyloxolane, vinylfuran, vinylthiophene, vinylthiolane, vinylthiazoles and hydrogenated vinylthiazoles, vinyloxazoles and hydrogenated vinyloxazoles; [0035] a11) vinyl and isoprenyl ethers; [0036] a12) methacrylic acid and acrylic acid, and [0037] b) 30 to 70% by weight of one or more alkyl (meth)acrylate monomer, wherein each of the alkyl group of the one or more alkyl (meth)acrylate monomer is independently linear, cyclic or branched and comprises from 1 to 40 carbon atoms, based on the total weight of the monomer composition, and [0038] c) 20 to 60% by weight of one or more polybutadiene-based macromonomer having a number-average molecular weight (M.sub.n) of 500 to 10,000 g/mol, based on the total weight of the monomer composition, [0039] (C) 0.02 to 5% by weight, based on the total weight of the nanoparticle composition, of the one or more silane compound (C) of formula (IV)

Si(R)(M).sub.h(X).sub.3-h(IV) [0040] where 0h2; preferably h is 0, [0041] M is a branched or linear C.sub.1 to C.sub.4 alkyl residue, [0042] R is a branched or linear, aliphatic, aromatic or mixed aliphatic-aromatic C.sub.1 to C.sub.30 carbon-based group, or R is a branched or linear, aliphatic, aromatic or mixed aliphatic-aromatic C.sub.1 to C.sub.30 carbon-based group with a functional group selected from carboxy, carbonyl, hydroperoxycarbonyl, cyan, formyl, oxo, thioxo, hydroxy, amino, imino, hydrazino, epoxy; preferably R is selected from a linear aliphatic C.sub.8 carbon-based group, a linear aliphatic C.sub.16 carbon-based group, a linear aliphatic 3-aminopropyl group, or a 3-glycidyloxypropyl group, [0043] X is selected from H, Cl or a group OY, wherein Y is H or a C.sub.1 to C.sub.8 branched or linear alkyl-, alkenyl-, aryl-, or aralkyl-group, branched or linear C.sub.2 to C.sub.8 alkylether-group or a mixture thereof; preferably X is methoxy or ethoxy,
wherein the nanoparticle composition is obtainable by milling the nanoparticle composition, preferably via a ball mill process.

[0044] Preferably, the one or more polybutadiene-based macromonomer c) has a number-average molecular weight (M.sub.n) of 1,500 to 7,500 g/mol, more preferably 3,500 to 7,000 g/mol, even more preferably 4,000 to 6,000 g/mol, most preferably 4,500 to 5,500 g/mol.

[0045] According to the present invention, it is preferred that the one or more polymer (B) has a weight-average molecular weight (M.sub.w) of 10,000 to 1,000,000 g/mol, more preferably 50,000 to 800,000 g/mol, even more preferably 100,000 to 500,000 g/mol, most preferably 150,000 to 350,000 g/mol.

[0046] According to another preferred aspect of the invention, the one or more polymer (B) is obtainable by polymerizing a monomer composition comprising: [0047] a) 1 to 30% by weight, more preferably 5 to 30% by weight, even more preferably 10 to 20% by weight of the one or more functional monomer as component a), based on the total weight of the monomer composition; and [0048] b1) 30 to 60% by weight, more preferably 30 to 50% by weight, even more preferably 35 to 50% by weight of one or more alkyl (meth)acrylate of formula (I), as first component b):

##STR00001## [0049] wherein R is hydrogen or methyl, R.sup.1 means a linear, branched or cyclic alkyl residue with 1 to 8 carbon atoms, preferably 1 to 5 carbon atoms, and more preferably 1 to 4 carbon atoms, based on the total weight of the monomer composition; and [0050] b2) 0 to 20% by weight, more preferably 1 to 15% by weight, even more preferably 1 to 10% by weight of one or more alkyl (meth)acrylate of formula (II), as second component b):

##STR00002## [0051] wherein R is hydrogen or methyl, R.sup.2 means a linear, branched or cyclic alkyl residue with 9 to 15 carbon atoms, preferably 12 to 15 carbon atoms, and more preferably 12 to 14 carbon atoms, based on the total weight of the monomer composition; and [0052] b3) 0 to 20% by weight, more preferably 0 to 15% by weight, even more preferably 0 to 10% by weight of one or more alkyl (meth)acrylate of formula (III), as third component b):

##STR00003## [0053] wherein R is hydrogen or methyl, R.sup.3 means a linear, branched or cyclic alkyl residue with 16 to 40 carbon atoms, preferably 16 to 30 carbon atoms, and more preferably 6 to 20 carbon atoms, based on the total weight of the monomer composition; and [0054] c) 20 to 60% by weight, more preferably 20 to 50% by weight, even more preferably 30 to 50% by weight of one or more polybutadiene-based macromonomer having a number-average molecular weight (M.sub.n) of 500 to 10,000 g/mol, based on the total weight of the monomer composition.

[0055] Preferably, the weight contents of monomers a), b) and c) of the monomer composition to prepare the polymer (B) sum up to 100% by weight, based on the total weight of the monomer composition.

[0056] Preferably, the one or more silane compound (C) of formula (IV) is octyltrimethoxysilane, hexadecyltrimethoxysilane, 3-aminopropyltriethoxysilane or 3-glycidyloxypropyltriethoxysilane.

[0057] Preferably, the nanoparticle composition comprises: [0058] 1 to 20% by weight of one or more nanoparticle (A), more preferably 5 to 20% by weight, even more preferably 8 to 17% by weight of one or more nanoparticle (A), and [0059] 0.5 to 30% by weight of one or more polymer (B), more preferably 3 to 30% by weight, even more preferably 5 to 25% by weight of one or more polymer (B), and [0060] 0.02 to 5% by weight of one or more silane compound (C), more preferably 0.05 to 3% by weight, even more preferably 0.1 to 2% by weight of one or more silane compound (C), and [0061] 45 to 98.48% by weight of one or more base fluid (D), more preferably 47 to 91.95% by weight, even more preferably 56 to 86.9% by weight of one or more base fluid (D),
all amounts based on the total weight of the nanoparticle composition.

[0062] According to another preferred aspect of the present invention, the weight contents of components A), B), C) and D) sum up to 100% by weight, based on the total weight of the composition.

[0063] According to another preferred aspect of the present invention, the one or more base fluid (D) is selected from the list consisting of an API Group I base oil, an API Group II base oil, an API Group III base oil, an API Group IV base oil, an API Group V base oil, or a mixture thereof.

[0064] Graphene Nanoparticles (A)

[0065] According to the present invention, the one or more graphene nanoparticle (A) is a multilayered graphene-based material containing oxygen groups, with a surface area BET between 200 m.sup.2/g and 1,500 m.sup.2/g, and a G/D ratio between 0.5 and 2, preferably with a surface area BET between 250 m.sup.2/g and 1,000 m.sup.2/g, more preferably between 350 m.sup.2/g and 800 m.sup.2/g, in accordance with ISO/TS 80004-13.

[0066] The one or more graphene nanoparticle (A) in accordance with ISO/TS 80004-13 is preferably selected from a one to ten layer graphene, more preferably from a one to ten layer graphene selected from the group consisting of exfoliated graphene, graphene nanoplate, graphene nanoplatelet, graphene nanosheet, graphene microsheet, graphene nanoflakes, graphene oxide, graphene oxide nanosheet, multi-layer graphene oxide, reduced graphene oxide, or a mixture thereof.

[0067] Further details on graphenes, production thereof, properties and applications thereof can also be found in technical literature, such as in Angew. Chem. Int. Ed. 2014, 53, 7714-7718 or Mater. Today 2012, 15(3) 86-97.

[0068] Preferably, the nanoparticle composition according to the present invention comprises 1 to 20% by weight of one or more nanoparticle (A), more preferably 5 to 20% by weight, even more preferably 8 to 17% by weight of one or more nanoparticle (A), based on the total weight of the nanoparticle composition.

[0069] Polymer (B)

[0070] According to the invention, the one or more polymer compound (B) is obtainable by polymerizing a monomer composition comprising: [0071] a) 1 to 30% by weight, preferably 5 to 30% by weight, more preferably 10 to 20% by weight of the one or more functional monomer as component a), based on the total weight of the monomer composition; and [0072] b) 30 to 70% by weight, preferably 30 to 60% by weight, more preferably 35 to 60% by weight of one or more alkyl (meth)acrylate monomer, wherein each of the alkyl group of the one or more alkyl (meth)acrylate monomer is independently linear, cyclic or branched and comprises from 1 to 40 carbon atoms, based on the total weight of the monomer composition, and [0073] c) 20 to 60% by weight, more preferably 20 to 50% by weight, even more preferably 30 to 50% by weight of one or more polybutadiene-based macromonomer having a number-average molecular weight (M.sub.n) of 500 to 10,000 g/mol, based on the total weight of the monomer composition.

[0074] In a preferred embodiment the amount of monomers a), b) and c) of the monomer composition sum up to 100% by weight, based on the total weight of the monomer composition for preparing the polymer (B).

[0075] According to the present invention, it is preferred when the one or more polymer (B) has a weight-average molecular weight (M.sub.w) of 10,000 to 1,000,000 g/mol, more preferably 50,000 to 1,000,000 g/mol, even more preferably 100,000 to 800,000 g/mol, most preferably 200,000 to 600,000 g/mol.

[0076] Preferably, the nanoparticle composition according to the present invention comprises 0.5 to 30% by weight of one or more polymer (B), more preferably 3 to 30% by weight, even more preferably 5 to 25% by weight of one or more polymer (B), based on the total weight of the nanoparticle composition.

[0077] In the present invention, the weight-average molecular weights (M.sub.w) of the polymers (B) were determined by gel permeation chromatography (GPC) using polystyrene calibration standards according to DIN 55672-1 using the following measurement conditions: [0078] Eluent: tetrahydrofuran (THF) including 0.02M 2-diethylamino ethylamine [0079] Operation temperature: 35 C. [0080] Columns: the column set consists of one pre-column (SDV 10; 850 mm) and four columns: SDV 10.sup.6 , SDV 10.sup.5 and 2SDV 10.sup.3 (PSS Standards Service GmbH, Mainz, Germany), all four columns with the size of 3008 mm and an average particle size of 10 m [0081] Flow rate: 1 mL/min [0082] Injected volume: 100 L [0083] Instrument: Agilent 1100 series consisting of an autosampler, pump and column oven Detection device: a refractive index detector from Agilent 1260 series.

[0084] Functional Monomer a)

[0085] As already defined above, the one or more functional monomer a) according to the present invention are selected from the list consisting of: [0086] a1) aminoalkyl (meth)acrylates and aminoalkyl (meth)acrylamides; [0087] a2) nitriles of alkyl (meth)acrylic acid and other nitrogen-containing alkyl (meth)acrylates; [0088] a3) (meth)acrylates of ether alcohols; [0089] a4) oxiranyl alkyl (meth)acrylate; [0090] a5) phosphorus-, boron- and/or silicon-containing alkyl (meth)acrylates; [0091] a6) heterocyclic alkyl (meth)acrylates; [0092] a7) vinyl halides; [0093] a8) vinyl esters; [0094] a9) vinyl monomers containing aromatic groups; [0095] a10) heterocyclic vinyl compounds; [0096] a11) vinyl and isoprenyl ethers; [0097] a12) methacrylic acid and acrylic acid.

[0098] Preferably, the functional monomer a) is selected from an aminoalkyl (meth)acrylate a1) or an aminoalkyl (meth)acrylamide a1) or a heterocyclic alkyl (meth)acrylate a6) or a vinyl monomer containing aromatic groups a9) or a mixture thereof. More preferably, from an aminoalkyl (meth)acrylamide a1) or a vinyl monomer containing aromatic groups a9) or a mixture thereof.

[0099] Even more preferably, the functional monomer a) is selected from aminoalkyl (meth)acrylamide, most preferably N-(3-dimethyl-aminopropyl)methacrylamide, as first component a), and a vinyl monomer containing aromatic groups, most preferably styrene, as second component a).

[0100] Alkyl (Meth)Acrylate Monomer b)

[0101] The term C.sub.1-40 alkyl (meth)acrylates refers to esters of (meth)acrylic acid and straight chain, cyclic or branched alcohols having 1 to 40 carbon atoms. The term encompasses individual (meth)acrylic esters with an alcohol of a particular length, and likewise mixtures of (meth)acrylic esters with alcohols of different lengths.

[0102] In one embodiment of the invention the monomer composition further comprises as component b) one or more alkyl (meth)acrylate monomer wherein each of the alkyl group of the one or more alkyl (meth)acrylate monomer independently is linear, cyclic or branched and comprises from 1 to 40 carbon atoms.

[0103] As already indicated above, according to the invention, the one or more alkyl (meth)acrylate monomer b) comprises [0104] b1) one or more alkyl (meth)acrylate of formula (I):

##STR00004## [0105] wherein R is hydrogen or methyl, R.sup.1 means a linear, branched or cyclic alkyl residue with 1 to 8 carbon atoms, preferably 1 to 5 carbon atoms, and more preferably 1 to 4 carbon atoms, [0106] b2) one or more alkyl (meth)acrylate of formula (II):

##STR00005## [0107] wherein R is hydrogen or methyl, R.sup.2 means a linear, branched or cyclic alkyl residue with 9 to 15 carbon atoms, preferably 12 to 15 carbon atoms, and more preferably 12 to 14 carbon atoms, [0108] b3) one or more alkyl (meth)acrylate of formula (III):

##STR00006## [0109] wherein R is hydrogen or methyl, R.sup.3 means a linear, branched or cyclic alkyl residue with 16 to 40 carbon atoms, preferably 16 to 30 carbon atoms, and more preferably 16 to 22 carbon atoms.

[0110] The term C.sub.1-8 alkyl (meth)acrylates refers to esters of (meth)acrylic acid and straight chain or branched alcohols having 1 to 8 carbon atoms. The term encompasses individual (meth)acrylic esters with an alcohol of a particular length, and likewise mixtures of (meth)acrylic esters with alcohols of different lengths.

[0111] According to the invention each of the one or more monomer according to formula (I), i.e. the C.sub.1-8 alkyl (meth)acrylates, may independently be selected from the group consisting of (meth)acrylates derived from saturated alcohols, preferably methyl (meth)acrylate, ethyl (meth)acrylate, n-propyl (meth)acrylate, isopropyl (meth)acrylate, n-butyl (meth)acrylate, tert-butyl (meth)acrylate, pentyl (meth)acrylate, hexyl (meth)acrylate, cycloalkyl (meth)acrylates, cyclopentyl (meth)acrylate, cyclohexyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, heptyl (meth)acrylate, 2-tert-butylheptyl (meth)acrylate, n-octyl (meth)acrylate and 3-isopropylheptyl (meth)acrylate, the most preferred monomer according to formula (II) is methyl methacrylate.

[0112] Particularly preferred C.sub.1-8 alkyl (meth)acrylates are methyl (meth)acrylate and n-butyl (meth)acrylate; methyl methacrylate and n-butyl methacrylate are especially preferred.

[0113] The term C.sub.9-15 alkyl (meth)acrylates refers to esters of (meth)acrylic acid and straight chain or branched alcohols having 9 to 15 carbon atoms. The term encompasses individual (meth)acrylic esters with an alcohol of a particular length, and likewise mixtures of (meth)acrylic esters with alcohols of different lengths.

[0114] According to the invention each of the one or more monomer according to formula (II), i.e. the C.sub.9-15 alkyl (meth)acrylates, may also independently be selected from the group consisting of nonyl (meth)acrylate, decyl (meth)acrylate, isodecyl (meth)acrylate, undecyl (meth)acrylate, 5-methylundecyl (meth)acrylate, n-dodecyl (meth)acrylate, 2-methyldodecyl (meth)acrylate, tridecyl (meth)acrylate, 5-methyltridecyl (meth)acrylate, n-tetradecyl (meth)acrylate, pentadecyl (meth)acrylate, oleyl (meth)acrylate, cycloalkyl (meth)acrylates, cyclohexyl (meth)acrylate having a ring substituent, tert-butylcyclohexyl (meth)acrylate, trimethylcyclohexyl (meth)acrylate, bornyl (meth)acrylate and isobornyl (meth)acrylate.

[0115] Particularly preferred C.sub.9-15 alkyl (meth)acrylates are (meth)acrylic esters of a linear C.sub.12-14 alcohol mixture (C.sub.12-14 alkyl (meth)acrylate).

[0116] The term C.sub.16-40 alkyl (meth)acrylates refers to esters of (meth)acrylic acid and straight chain or branched alcohols having 16 to 40 carbon atoms. The term encompasses individual (meth)acrylic esters with an alcohol of a particular length, and likewise mixtures of (meth)acrylic esters with alcohols of different lengths.

[0117] According to the invention each of the one or more monomer according to formula (III), i.e. the C.sub.16-40 alkyl (meth)acrylates, may also independently be selected from the group consisting of hexadecyl (meth)acrylate, 2-methylhexadecyl (meth)acrylate, heptadecyl (meth)acrylate, 5-isopropylheptadecyl (meth)acrylate, 4-tert-butyloctadecyl (meth)acrylate, 5-ethyloctadecyl (meth)acrylate, 3-isopropyloctadecyl (meth)acrylate, octadecyl (meth)acrylate, nonadecyl (meth)acrylate, eicosyl (meth)acrylate, cetyleicosyl (meth)acrylate, stearyleicosyl (meth)acrylate, docosyl (meth)acrylate, behenyl (meth)acrylate, eicosyltetratriacontyl (meth)acrylate, cycloalkyl (meth)acrylates, 2,4,5-tri-t-butyl-3-vinylcyclohexyl (meth)acrylate, and 2,3,4,5-tetra-t-butylcyclohexyl (meth)acrylate.

[0118] Preferably, the C.sub.1-40 alkyl (meth)acrylates include a mixture of C.sub.1-8 alkyl (meth)acrylates and C.sub.9-15 alkyl (meth)acrylates, more preferably is a C.sub.12-14 alkyl (meth)acrylate.

[0119] Macromonomer Component (c)

[0120] According to the invention, the above-defined monomer composition comprises as component c) one or more polybutadiene-based macromonomer having a number-average molecular weight of 500 to 10,000 g/mol. The polybutadiene-based macromonomers c) of the invention are esters of (meth)acrylic acid, which are either the reaction product of one ester of (meth)acrylic acid with one hydroxylated hydrogenated polybutadiene (by transesterification), or the reaction product of one (meth)acrylic acid with one hydroxylated hydrogenated polybutadiene (by direct esterification).

[0121] In this context, the polymer compound (B) of this invention comprises a first polymer, which is also referred to as backbone or main chain, and a multitude of further polymers which are referred to as side chains and are bonded covalently to the backbone. In the present case, the backbone of the polymer is formed by the interlinked unsaturated groups of the mentioned (meth)acrylic acid esters. The alkyl groups and the hydrogenated polybutadiene chains of the (meth)acrylic esters form the side chains of the polymer.

[0122] The reaction product of one ester of (meth)acrylic acid and one hydroxylated hydrogenated polybutadiene or the reaction product of one (meth)acrylic acid and one hydroxylated hydrogenated polybutadiene corresponds to monomer c) and is also referred in the present invention as macromonomer or polybutadiene-based macromonomer c) having a number-average molecular weight of 500 to 10,000 g/mol.

[0123] The number-average molecular weight M.sub.n of the macromonomer is determined by gel permeation chromatography (GPC) using polybutadiene calibration standards according to DIN 55672-1 using the following measurement conditions: [0124] Eluent: tetrahydrofuran (THF) [0125] Operation temperature: 35 C. [0126] Columns: the column set consists of one pre-column (PSS-SDV; 10; 850 mm), four PSS-SDV columns with a size of 3008 mm and an average particle size of 10 m (SDV-LXL, SDV-LinL, 2 columns SDV 100 (PSS Standards Service GmbH, Mainz, Germany)), and one solvent-peak separation column with a size of 8100 mm (KF-800D from the company Shodex) [0127] Flow rate: 1 mL/min [0128] Injected volume: 100 L [0129] Instrument: Agilent 1100 series consisting of an autosampler, pump and column oven [0130] Detection: a refractive index detector from Agilent 1100 series

[0131] The one or more polymer compound (B) prepared with a monomer composition comprising the components a), b) and c) can be characterized on the basis of its molar degree of branching (f-branch). The molar degree of branching refers to the percentage in mol % of macromonomers (component (c)) used, based on the total molar amount of all the monomers in the monomer composition. The molar amount of the macromonomers used is calculated on the basis of the number-average molecular weight (M.sub.n) of the macromonomers. The calculation of the molar degree of branching is described in detail in WO 2007/003238 A1, especially on pages 13 and 14, to which reference is made here explicitly.

[0132] Preferably, the one or more polymer compound (B) has a molar degree of branching f.sub.branch of 0.1 to 6 mol %, more preferably 1 to 4 mol % and most preferably 1.5 to 3 mol %.

[0133] The one or more polybutadiene-based macromonomer for use as component c) in accordance with the invention have a number-average molecular weight (M.sub.n) of 500 g/mol to 10,000 g/mol. Because of their high molecular mass, the hydroxylated hydrogenated polybutadienes can also be referred to as macroalcohols in the context of this invention. The corresponding esters of (meth)acrylic acid can also be referred to as macromonomers in the context of this invention.

[0134] Component c) may comprise a single type of macromonomer or may comprise a mixture of different macromonomers based on different macroalcohols.

[0135] The hydroxylated hydrogenated polybutadiene may be a single polybutadiene with a single number-average molecular weight (M.sub.n) or it may be a mixture of different polybutadienes having different number-average molecular weight (M.sub.n).

[0136] According to the present invention, the monomer composition comprises as component c) 20 to 60% by weight, preferably 20 to 50% by weight, more preferably 30 to 50% by weight, of one or more polybutadiene-based macromonomer having a number-average molecular weight (M.sub.n) of 500 g/mol to 10,000 g/mol, based on the total weight of the monomer composition.

[0137] In a preferred embodiment the one or more one or more polybutadiene-based macromonomer for use as component c) in accordance with the invention have a number-average molecularweight (M.sub.n) of 1,500 to 7,500 g/mol, preferably of 3,500 to 7,000 g/mol, more preferably 4,000 to 6,000 g/mol, even more preferably 4,500 to 5,500 g/mol.

[0138] In another preferred embodiment, component c) may be one macromonomer prepared using one or more macroalcohols having different molecular weights, the first macroalcohol having a number-average molecular weight of 1,500 to 2,500 g/mol, more preferably 1,800 to 2,500 g/mol, most preferably 1,900 to 2,300 g/mol, and the second macroalcohol having a number-average molecular weight of 3,500 to 7,000 g/mol, preferably 4,000 to 6,000 g/mol, more preferably 4,500 to 5,500 g/mol. Component c) may also comprise a mixture of two macromonomers, the first macromonomer being prepared with a macroalcohol having a number-average molecular weight of 1,500 to 2,500 g/mol, more preferably 1,800 to 2,500 g/mol, most preferably 1,900 to 2,500 g/mol, and the second macromonomer being prepared with a macroalcohol having a number-average molecular weight of 3,500 to 7,000 g/mol, preferably 4,000 to 6,000 g/mol, more preferably 4,500 to 5,500 g/mol.

[0139] According to a preferred embodiment of the present invention, by combining two macromonomers of different number-average molecular weights, the weight proportion of the lower molecular weight macromonomer to the higher molecular weight macromonomer is preferably one or more, more preferably 1.5 to 15, even more preferably 2 to 7, most preferably 3 to 6.

[0140] In a preferred embodiment, the hydroxylated hydrogenated polybutadiene is a monohydroxylated hydrogenated polybutadiene, preferably a hydroxyethyl-terminated or hydroxypropyl-terminated hydrogenated polybutadiene.

[0141] In another preferred embodiment of the invention, the one or more ester of (meth)acrylic acid of the component c) used for the preparation of the polymer compound (B) is methyl (meth)acrylate or ethyl (meth)acrylate.

[0142] Preferably, the one or more hydroxylated hydrogenated polybutadiene has a hydrogenation level of at least 99%. An alternative measure of the hydrogenation level which can be determined on the polymer of the invention is the iodine number. The iodine number refers to the number of grams of iodine which can be added onto 100 g of polymer. Preferably, the polymer of the invention has an iodine number of not more than 5 g of iodine per 100 g of polymer. The iodine number is determined by the Wijs method according to DIN 53241-1:1995-05.

[0143] Preferred hydroxylated hydrogenated polybutadienes can be obtained according to GB 2270317.

[0144] As used herein, the term hydroxylated hydrogenated polybutadiene refers to a hydrogenated polybutadiene that comprises one or more hydroxyl group. The hydroxylated hydrogenated polybutadiene may further comprise additional structural units, such as polyether groups derived from the addition of alkylene oxides to a polybutadiene or a maleic anhydride group derived from the addition of maleic anhydride to a polybutadiene. These additional structural units may be introduced into the polybutadiene when the polybutadiene is functionalized with hydroxyl groups.

[0145] Preference is given to monohydroxylated hydrogenated polybutadienes. More preferably, the hydroxylated hydrogenated polybutadiene is a hydroxyethyl- or hydroxypropyl-terminated hydrogenated polybutadiene. A preference is given to hydroxypropyl-terminated polybutadienes.

[0146] These monohydroxylated hydrogenated polybutadienes can be prepared by first converting butadiene monomers by anionic polymerization to polybutadiene. Subsequently, by reaction of the polybutadiene monomers with an alkylene oxide, such as ethylene oxide or propylene oxide, a hydroxy-functionalized polybutadiene can be prepared. The polybutadiene may also be reacted with more than one alkylene oxide units, resulting in a polyether-polybutadiene block copolymer having a terminal hydroxyl group. The hydroxylated polybutadiene can be hydrogenated in the presence of a suitable transition metal catalyst.

[0147] These monohydroxylated hydrogenated polybutadienes can also be selected from products obtained by hydroboration of (co)polymers of having a terminal double bond (e.g. as described in U.S. Pat. No. 4,316,973); maleic anhydride-ene-amino alcohol adducts obtained by an ene reaction between a (co)polymer having a terminal double bond and maleic anhydride with an amino alcohol; and products obtained by hydroformylation of a (co)polymer having a terminal double bond, followed by hydrogenation (e.g. as described in JP Publication No. S63-175096).

[0148] The macromonomers c) for use in accordance with the invention can be prepared by transesterification of alkyl (meth)acrylates. Reaction of the alkyl (meth)acrylate with the hydroxylated hydrogenated polybutadiene forms the ester of the invention. Preference is given to using methyl (meth)acrylate or ethyl (meth)acrylate as reactant.

[0149] This transesterification is widely known. For example, it is possible for this purpose to use a heterogeneous catalyst system, such as lithium hydroxide/calcium oxide mixture (LiOH/CaO), pure lithium hydroxide (LiOH), lithium methoxide (LiOMe) or sodium methoxide (NaOMe) or a homogeneous catalyst system such as isopropyl titanate (Ti(OiPr).sub.4) or dioctyltin oxide (Sn(OCt).sub.2O). The reaction is an equilibrium reaction. Therefore, the low molecular weight alcohol released is typically removed, for example by distillation.

[0150] In addition, the macromonomers c) can be obtained by a direct esterification proceeding, for example, from (meth)acrylic acid or (meth)acrylic anhydride, preferably under acidic catalysis by p-toluenesulfonic acid or methanesulfonic acid, or from free methacrylic acid by the DCC method (dicyclohexylcarbodiimide).

[0151] Furthermore, the present hydroxylated hydrogenated polybutadiene can be converted to an ester by reaction with an acid chloride such as (meth)acryloyl chloride.

[0152] Preferably, in the above-detailed preparations of the esters of the invention, polymerization inhibitors are used, for example the 4-hydroxy-2,2,6,6-tetramethylpiperidinooxyl radical and/or hydroquinone monomethyl ether.

[0153] Preferable Monomer Compositions for Preparing the Polymer (B)

[0154] According to a preferred aspect of the invention, the one or more polymer compound (B) is obtainable by polymerizing a monomer composition comprising: [0155] a1) 0.5 to 5% by weight of an aminoalkyl (meth)acrylamide, most preferably N-(3-dimethyl-aminopropyl)methacrylamide, as first component a), based on the total weight of the monomer composition; [0156] a9) 5 to 15% by weight of a vinyl monomer containing aromatic groups, most preferably styrene, as second component a), based on the total weight of the monomer composition; [0157] b1) 35 to 50% by weight of an alkyl (meth)acrylate monomer of formula (I), most preferably methyl methacrylate and/or butyl methacrylate, as first component b), based on the total weight of the monomer composition; [0158] b2) 1 to 10% by weight of an alkyl (meth)acrylate monomer of formula (II), most preferably lauryl methacrylate, as second component b), based on the total weight of the monomer composition; [0159] c) 30 to 50% by weight of one or more polybutadiene-based macromonomer having a number-average molecular weight (M.sub.n) of 500 to 10,000 g/mol, most preferably having a number-average molecular weight (M.sub.n) of 1,500 to 5,500 g/mol, as component c), based on the total weight of the monomer composition.

[0160] In an even preferred embodiment, the amounts of all monomers a), b) and c) of the monomer composition sum up to 100% by weight, based on the total weight of the monomer composition.

[0161] Preparation of the Polymer Compound (B)

[0162] According to the present invention, the above-mentioned polymers may be prepared following the method comprising the steps of: [0163] (a) providing a monomer composition as describe above; and [0164] (b) initiating radical polymerization in the monomer composition.

[0165] Standard free-radical polymerization is detailed, inter alia, in Ullmann's Encyclopedia of Industrial Chemistry, Sixth Edition. In general, a polymerization initiator and optionally a chain transfer agent are used for this purpose.

[0166] The polymerization can be conducted under standard pressure, reduced pressure or elevated pressure. The polymerization temperature is also uncritical. In general, however, it is in the range from 20 to 200 C., preferably 50 to 150 C. and more preferably 80 to 130 C.

[0167] The polymerization step (b) may be performed with or without dilution in oil. If dilution is performed, then the amount of the monomer composition, i.e. the total amount of monomers, relative to the total weight of the reaction mixture is preferably 20 to 90% by weight, more preferably 40 to 80% by weight, most preferably 50 to 70% by weight.

[0168] Preferably, the oil used for diluting the monomer mixture is an API Group I, II, III, IV or V oil, or a mixture thereof. Preferably, a Group III oil or a mixture thereof is used to dilute the monomer mixture.

[0169] Preferably, step (b) comprises the addition of a radical initiator.

[0170] Suitable radical initiators are, for example, azo initiators, such as azobis-isobutyronitrile (AIBN), 2,2-azobis(2-methylbutyronitrile) (AMBN) and 1,1-azobiscyclohexanecarbonitrile, and peroxy compounds such as methyl ethyl ketone peroxide, acetylacetone peroxide, dilauryl peroxide, tert-butyl per-2-ethylhexanoate, ketone peroxide, tert-butyl peroctoate, methyl isobutyl ketone peroxide, cyclohexanone peroxide, dibenzoyl peroxide, tert-butyl peroxybenzoate, tert-butyl peroxyisopropylcarbonate, 2,5-bis(2-ethylhexanoylperoxy)-2,5-dimethylhexane, tert-butyl peroxy-2-ethylhexanoate, tert-butyl peroxy-3,5,5-trimethylhexanoate, dicumyl peroxide, 1,1-bis(tert-butylperoxy)cyclohexane, 1,1-bis(tert-butylperoxy)-3,3,5-trimethylcyclohexane, cumyl hydroperoxide, tert-butyl hydroperoxide and bis(4-tert-butylcyclohexyl) peroxydicarbonate.

[0171] Preferably, the radical initiator is selected from the group consisting of 2,2-azobis(2-methylbutyronitrile), 2,2-bis(tert-butylperoxy)butane, tert-butylperoxy 2-ethylhexanoate, 1,1-di-tert-butylperoxy-3,3,5-trimethylcyclohexan, tert-butyl peroxybenzoate and tert-butylperoxy-3,5,5-trimethylhexanoat. Particularly preferred initiators are tert-butylperoxy 2-ethylhexanoate and 2,2-bis(tert-butylperoxy)butane.

[0172] Preferably, the total amount of radical initiator relative to the total weight of the monomer mixture is 0.01 to 5% by weight, more preferably 0.02 to 1% by weight, most preferably 0.05 to 0.6% by weight.

[0173] The total amount of radical initiator may be added in a single step or the radical initiator may be added in several steps over the course of the polymerization reaction. Preferably, the radical initiator is added in several steps. For example, a part of the radical initiator may be added to initiate radical polymerization and a second part of the radical initiator may be added 0.5 to 3.5 hours after the initial dosage.

[0174] Preferably, step (b) also comprises the addition of a chain transfer agent. Suitable chain transfer agents are especially oil-soluble mercaptans, for example n-dodecyl mercaptan or 2-mercaptoethanol, or else chain transfer agents from the class of the terpenes, for example terpinolene. Particularly preferred is the addition of n-dodecyl mercaptan.

[0175] It is also possible to divide the monomer composition into an initial part and a second part and to add a part of the radical initiator to the initial part only to start the polymerization reaction therein. Then, the second part of the radical initiator is added to the second part of the monomer composition which is then added over the course of 0.5 to 5 hours, preferably 1.5 to 4 hours, more preferably 2 to 3.5 hours, to the polymerization reaction mixture. After addition of the second monomer mixture, a third part of the radical initiator may be added to the polymerization reaction as described above.

[0176] Preferably, the total reaction time of the radical polymerization is 2 to 10 hours, more preferably 3 to 9 hours.

[0177] After completion of the radical polymerization, the obtained polymer is preferably further diluted with the above-mentioned oil to the desired viscosity. Preferably, the polymer is diluted to a concentration of 5 to 60% by weight polymer, more preferably 10 to 50% by weight, most preferably 20 to 40% by weight.

[0178] Silane Compound (C)

[0179] According to the present invention, the one or more silane compound (C) is of formula (IV)

Si(R)(M).sub.h(X).sub.3-h(IV) [0180] where 0h2; preferably h is 0, [0181] M is a branched or linear C.sub.1 to C.sub.4 alkyl residue, [0182] R is a branched or linear, aliphatic, aromatic or mixed aliphatic-aromatic C.sub.1 to C.sub.30 carbon-based group, or R is a branched or linear, aliphatic, aromatic or mixed aliphatic-aromatic C.sub.1 to C.sub.30 carbon-based group with a functional group selected from carboxy, carbonyl, hydroperoxycarbonyl, cyan, formyl, oxo, thioxo, hydroxy, amino, imino, hydrazino, epoxy; preferably R is selected from a linear aliphatic C.sub.8 carbon-based group, a linear aliphatic C.sub.16 carbon-based group, a linear aliphatic 3-aminopropyl group, or a 3-glycidyloxypropyl group, [0183] X is selected from H, Cl or a group OY, wherein Y is H or a C.sub.1 to C.sub.8 branched or linear alkyl-, alkenyl-, aryl-, or aralkyl-group, branched or linear C.sub.2 to C.sub.8 alkylether-group or a mixture thereof; preferably X is methoxy or ethoxy,

[0184] The nanoparticle composition according to the present invention comprises 0.02 to 5% by weight of one or more silane compound (C), preferably 0.05 to 3% by weight, more preferably 0.1 to 2% by weight of one or more silane compound (C), based on the total weight of the nanoparticle composition.

[0185] Preferably, the one or more silane compound (C) of formula (IV) is octyltrimethoxysilane, hexadecyltrimethoxysilane, 3-aminopropyltriethoxysilane or 3-glycidyloxypropyltriethoxysilane.

[0186] Base Fluid (D)

[0187] The base fluid (D) in the nanoparticle composition can be a base oil selected from the list consisting of an API Group I base oil, an API Group II base oil, an API Group III, an API Group IV base oil and an API Group V base oil or a combination thereof.

[0188] The base fluid (D) may also be defined as specified by the American Petroleum Institute (API) (see April 2008 version of Appendix E-API Base Oil Interchangeability Guidelines for Passenger Car Motor Oils and Diesel Engine Oils, section 1.3 Sub-heading 1.3. Base Stock Categories).

[0189] The API currently defines five groups of lubricant base stocks (API 1509, Annex EAPI Base Oil Interchangeability Guidelines for Passenger Car Motor Oils and Diesel Engine Oils, September 2011). Groups I, II and III are mineral oils which are classified by the amount of saturates and sulphur they contain and by their viscosity indices; Group IV are polyalphaolefins; and Group V are all others, including e.g. ester oils. The table below illustrates these API classifications.

TABLE-US-00001 TABLE 1 API definition of lubricant base oils. Group Saturates Sulphur content Viscosity Index (VI) I <90% >0.03% 80-120 II at least 90% not more than 0.03% 80-120 III at least 90% not more than 0.03% at least 120 IV All polyalphaolefins (PAOs) V All others not included in Groups I, II, III or IV (e.g. ester oils)

[0190] Further base oils which can be used in accordance with the present invention as base fluid (D) are Group II-III Fischer-Tropsch derived base oils.

[0191] Fischer-Tropsch derived base oils are known in the art. By the term Fischer-Tropsch derived is meant that a base oil is, or is derived from, a synthesis product of a Fischer-Tropsch process. A Fischer-Tropsch derived base oil may also be referred to as a GTL (Gas-To-Liquids) base oil. Suitable Fischer-Tropsch derived base oils that may be conveniently used as the base oil in the lubricating composition of the present invention are those as for example disclosed in EP 0 776 959, EP 0 668 342, WO 97/21788, WO 00/15736, WO 00/14188, WO 00/14187, WO 00/14183, WO 00/14179, WO 00/08115, WO 99/41332, EP 1 029 029, WO 01/18156, WO 01/57166 and WO 2013/189951.

[0192] Preferably, the base fluid (D) in the nanoparticle composition is an API Group III base oil.

[0193] Process for Preparing the Nanoparticle Composition of the Invention

[0194] Another aspect of the present invention is a process for preparing a graphene nanoparticle composition according to the invention, which comprises the following steps [0195] (i) providing one or more nanoparticle compound (A) as defined herein; [0196] (ii) providing one or more polymer compound (B) as defined herein; [0197] (iii) providing one or more silane compound (C) as defined herein; [0198] (iv) providing one or more base fluid (D) as defined herein; [0199] (v) combining (A) to (D) to obtain a mixture; and [0200] (vi) milling the mixture of step (v).

[0201] The milling technology according to the invention described in step (vi) can be high pressure homogenization, high shear mixing, ball milling or ultrahigh-pressure technology (jet mill) or a combination thereof. Indeed, the particle size of the agglomerates is reduced using these milling technologies.

[0202] Preferably, the mixture of one or more nanoparticle (A), the one or more polymer compound (B), the one or more silane compound (C) and the one or more base fluid (D) is milled via a ball mill process in step (vi). More preferably, in step (v), either the compounds (A) and (C) are first mixed together and then mixed with (B) and (D) or (B), (C) and (D) are first mixed and (A) is added into this mixture prior to the ball milling step (vi).

[0203] Preferably, the ball mill process comprises introducing 0.1 to 10 kWh/kg, preferably 0.5 to 5 kWh/kg, more preferably 1 to 3 kWh/kg energy into the mixture.

[0204] In another preferred embodiment, the mixture of graphene nanoparticle (A), the one or more polymer compound (B) the one or more silane compound (C) and a one or more base fluid (D) is milled using ultrahigh-pressure technology (e.g. jet mill equipment Sugino Ultimaizer HJP-25050). At least two flows of this mixture are sprayed by means of pumps, preferably high-pressure pumps, through one nozzle (0.10 or 0.25 mm diameter) each into a grinding chamber enclosed by a reactor housing onto a collision point, characterized in that the grinding chamber is flooded with the mixture and the finally milled mixture is removed from the grinding chamber by the overpressure of the continuous flow into the grinding chamber. The pump pressure is between 100 to 4,000 bar, preferably between 400 to 3,000 bar, more preferably between 1,000 to 2,500 bar.

[0205] According to this invention, the milling step (vi) is defined by a resulting change of particle size distribution of the graphene nanoparticle composition measured using dynamic light scattering technology (DLS).

[0206] Pre-Treatment

[0207] Preferably, in step (v) the compounds (A) and (C) are first mixed together by spraying method or ball milling method, and then mixed with (B) and (D).

[0208] By the pre-treatment method of spraying, the graphene nanoparticles (A) are first sprayed with water, if needed and appropriate, and subsequently with the silane compound (C). Spraying may also take place in the opposite order. The water used may have been acidified with an acid, preferably hydrochloric acid, to a pH of 7 to 1. If two or more silane compounds (C) are employed, they can be applied separately or as a mixture.

[0209] The one or more silane compound (C) may have been dissolved in suitable solvents. The end of spraying may be followed by mixing for 5 to 30 minutes more.

[0210] The mixture is subsequently treated thermally at a temperature of 20 to 400 C. over a period of 0.1 to 6 h. The thermal treatment may take place under inert gas, preferably nitrogen.

[0211] The pre-treatment can be carried out in heatable mixers and dryers with spraying installations, continuously or batchwise. Suitable apparatus may for example be the following: ploughshare mixers, plate dryers, fluidized-bed dryers or fluid-bed dryers.

[0212] By the pre-treatment of ball milling, the graphene nanoparticles (A) are milled with silane compound (C), optionally previously dissolved in a solvent, preferably ethanol, using a ball mill at a rotational speed between 100 and 1,000 rpm, preferably 400 to 800 rpm for 1 to 120 min, preferably 5 to 25 min.

[0213] Use of the Nanoparticle Composition According to the Invention

[0214] A further aspect of the invention is the use of the nanoparticle composition according to the invention as an additive in a lubricating oil composition. Preferably, the lubricant additive is favorably used for driving system lubricating oils (such as manual transmission fluids, differential gear oils, automatic transmission fluids and belt-continuously variable transmission fluids, axle fluid formulations, dual clutch transmission fluids, and dedicated hybrid transmission fluids), hydraulic oils (such as hydraulic oils for machinery, power steering oils, shock absorber oils), engine oils (for gasoline engines and for diesel engines) and industrial oil formulations (such as wind turbine).

[0215] In a preferred embodiment according to the invention, the nanoparticle composition improves the anti-friction performance of moving metal parts of an engine, a gearbox or pump of an automobile, a wind turbine, or a hydraulic system.

[0216] Lubricating Oil Composition

[0217] Yet another aspect of the invention is a lubricating oil composition comprising a nanoparticle composition as defined herein and at least one or more base oil (E).

[0218] In a preferred embodiment of the invention the base oil (E) is selected from the list consisting of an API Group I base oil, an API Group II base oil, an API Group III, an API Group IV base oil and an API Group V base oil or a mixture of one or more of these base oils, as described above in the paragraph relating to the base fluid (D).

[0219] The base oil (E) to be used in the lubricating oil composition preferably comprises an oil of lubricating viscosity. Such oils include natural and synthetic oils, oils derived from hydrocracking, hydrogenation, and hydro-finishing, unrefined, refined, re-refined oils or mixtures thereof.

[0220] Especially for transmission oil formulations, base oils of API Group III and mixtures of different Group III oils are used. In another preferred embodiment, the base oil may also be a mixture of one or more API Group V base oil with one or more API Group III base oil.

[0221] According to the present invention, the lubricating oil composition comprising the nanoparticle composition according to the invention and one or more base oil (E), may also optionally further comprise additives (F) as disclosed below. Preferably, the lubricating oil composition further comprises one or more additives (F) selected from the group consisting of antioxidants, anti-wear additives, pour point depressants, corrosion inhibitors, metal passivators or electrostatic discharge depressants, defoaming agents, seal fix or seal compatibility agents, or a mixture thereof.

[0222] According to the present invention, it is preferred that the lubricating oil composition comprises: [0223] 0.01 to 50% by weight, more preferably 0.01 to 35% by weight, even more preferably 0.1 to 25% by weight of the nanoparticle composition, based on the total weight of the lubricating oil composition, [0224] 50 to 99.99% by weight, more preferably 65 to 99.99% by weight, even more preferably 75 to 99.9% by weight of base fluid (E) and [0225] 0 to 20% by weight, more preferably 0.05% to 15% by weight, even more preferably 5% to 15% by weight, of one or more additive component (F), based on the total weight of the lubricating oil composition.

[0226] Preferably, the amounts of the nanoparticle composition, the base fluid (E), the one or more additive component (F) add up to 98% by weight, more preferably add up to 100% by weight, based on the total weight of the lubricating oil composition.

[0227] The lubricating oil composition according to the invention may also further contain, as component (F), further additives selected from the group consisting of dispersants, defoamers, detergents, antioxidants, pour point depressants, antiwear additives, extreme pressure additives, anticorrosion additives, yellow metal passivator, friction modifiers, dyes and mixtures thereof.

[0228] Appropriate dispersants include poly(isobutylene) derivatives, for example poly(isobutylene)succinimides (PIBSIs), including borated PIBSIs; and ethylene-propylene oligomers having N/O functionalities.

[0229] Dispersants (including borated dispersants) are preferably used in an amount of 0 to 20% by weight, more preferably 0 to 15% by weight, based on the total amount of the lubricant composition.

[0230] Suitable defoamers are silicone oils, fluorosilicone oils or fluoroalkyl ethers.

[0231] The defoaming agent is preferably used in an amount of 0.001 to 0.2% by weight, based on the total amount of the lubricant composition.

[0232] The preferred detergents include metal-containing compounds, for example phenoxides; salicylates; thiophosphonates, especially thiopyrophosphonates, thiophosphonates and phosphonates; sulfonates and carbonates. As metal, these compounds may contain especially calcium, magnesium and barium. These compounds may preferably be used in neutral or overbased form.

[0233] Detergents are preferably used in an amount of 0.2 to 8% by weight, preferably 0.2 to 4% by weight, based on the total amount of the lubricant composition.

[0234] The suitable antioxidants include, for example, phenol-based antioxidants and amine-based antioxidants.

[0235] Phenol-based antioxidants include, for example, octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate; 4,4-methylenebis(2,6-di-tert-butylphenol); 4,4-bis(2,6-di-t-butylphenol); 4,4-bis(2-methyl-6-t-butylphenol); 2,2-methylenebis(4-ethyl-6-t-butylphenol); 2,2-methylenebis(4-methyl-6-t-butyl phenol); 4,4-butylidenebis(3-methyl-6-t-butylphenol); 4,4-isopropylidenebis(2,6-di-t-butylphenol); 2,2-methylenebis(4-methyl-6-nonylphenol); 2,2-isobutylidenebis(4,6-dimethylphenol); 2,2-methylenebis(4-methyl-6-cyclohexylphenol); 2,6-di-t-butyl-4-methylphenol; 2,6-di-t-butyl-4-ethyl-phenol; 2,4-dimethyl-6-t-butylphenol; 2,6-di-t-amyl-p-cresol; 2,6-di-t-butyi-4-(N,N-dimethylaminomethylphenol); 4,4thiobis(2-methyl-6-t-butylphenol); 4,4-thiobis(3-methyl-6-t-butylphenol); 2,2-thiobis(4-methyl-6-t-butylphenol); bis(3-methyl-4-hydroxy-5-t-butylbenzyl) sulfide; bis(3,5-di-t-butyl-4-hydroxybenzyl) sulfide; n-octyl-3-(4-hydroxy-3,5-di-t-butylphenyl)propionate; n-octadecyl-3-(4-hydroxy-3,5-di-t-butylphenyl)propionate; 2,2-thio[diethyl-bis-3-(3,5-di-t-butyl-4-hydroxyphenyl)propionate], etc. Of those, especially preferred are bis-phenol-based antioxidants and ester group containing phenol-based antioxidants.

[0236] The amine-based antioxidants include, for example, monoalkyldiphenylamines such as monooctyldiphenylamine, monononyldiphenylamine, etc.; dialkyldiphenylamines such as 4,4-dibutyldiphenylamine, 4,4-dipentyldiphe nylamine, 4,4-dihexyldiphenylamine, 4,4-diheptyldiphenylamine, 4,4-dioctyldiphenylamine, 4,4-dinonyldiphenylamine, etc.; polyalkyldiphenylamines such as tetrabutyldiphenylamine, tetrahexyldiphenylamine, tetraoctyldiphenylamine, tetranonyldiphenylamine, etc.; naphthylamines, concretely alpha-naphthylamine, phenyl-alpha-naphthylamine and further alkyl-substituted phenyl-alpha-naphthylamines such as butylphenyl-alpha-naphthylamine, pentylphenyl-alpha-naphthylamine, hexylphenyl-alpha-naphthylamine, heptylphenyl-alpha-naphthylamine, octylphenyl-alpha-naphthylamine, nonylphenyl-alpha-naphthylamine, etc. Of those, diphenylamines are preferred to naphthylamines, from the viewpoint of the antioxidation effect thereof.

[0237] Suitable antioxidants may further be selected from the group consisting of compounds containing sulfur and phosphorus, for example metal dithiophosphates, for example zinc dithiophosphates (ZnDTPs), OOS triesters=reaction products of dithiophosphoric acid with activated double bonds from olefins, cyclopentadiene, norbornadiene, -pinene, polybutene, acrylic esters, maleic esters (ashless on combustion); organosulfur compounds, for example dialkyl sulfides, diaryl sulfides, polysulfides, modified thiols, thiophene derivatives, xanthates, thioglycols, thioaldehydes, sulfur-containing carboxylic acids; heterocyclic sulfur/nitrogen compounds, especially dialkyldimercaptothiadiazoles, 2-mercaptobenzimidazoles; zinc bis(dialkyldithiocarbamate) and methylene bis(dialkyldithiocarbamate); organophosphorus compounds, for example triaryl and trialkyl phosphites; organocopper compounds and overbased calcium- and magnesium-based phenoxides and salicylates.

[0238] Antioxidants are used in an amount of 0 to 15% by weight, preferably 0.01 to 10% by weight, more preferably 0.01 to 5% by weight, based on the total amount of the lubricant composition.

[0239] Suitable anticorrosion additives are succinic acid partial esters, succinic acid partial ester amine salts, organic carboxylic acids, sulfonates and suitable yellow metal passivators are thiadiazoles, triazoles and high molecular phenolic antioxidants.

[0240] Anticorrosion additives are used in an amount of 0 to 5% by weight, yellow metal passivators are used in an amount of 0 to 1% by weight, all amounts based on the total weight of the lubricant composition.

[0241] The pour-point depressants include ethylene-vinyl acetate copolymers, chlorinated paraffin-naphthalene condensates, chlorinated paraffin-phenol condensates, polymethacrylates, polyalkylstyrenes, etc. Preferred are polymethacrylates having a weight-average molecular weight (M.sub.w) of from 5,000 to 200,000 g/mol.

[0242] The amount of the pour point depressant is preferably from 0.1 to 5% by weight, based on the total amount of the lubricant composition.

[0243] The preferred antiwear and extreme pressure additives include sulfur-containing compounds such as zinc dithiophosphate, zinc di-C.sub.3-12-alkyldithiophosphates (ZnDTPs), zinc phosphate, zinc dithiocarbamate, molybdenum dithiocarbamate, molybdenum dithiophosphate, alkyl dithiophosphate, disulfides, sulfurized olefins, sulfurized oils and fats, sulfurized esters, thiocarbonates, thiocarbamates, polysulfides, etc.; phosphorus-containing compounds such as phosphites, phosphates, for example trialkyl phosphates, triaryl phosphates, e.g. tricresyl phosphate, amine-neutralized mono- and dialkyl phosphates, ethoxylated mono- and dialkyl phosphates, phosphonates, phosphines, amine salts or metal salts of those compounds, etc.; sulfur and phosphorus-containing anti-wear agents such as thiophosphites, thiophosphates, thiophosphonates, amine salts or metal salts of those compounds.

[0244] The antiwear agent may be present in an amount of 0 to 3% by weight, preferably 0.1 to 1.5% by weight, more preferably 0.5 to 0.9% by weight, based on the total amount of the lubricant composition.

[0245] The preferred friction modifiers may include mechanically active compounds, for example molybdenum disulphide, graphite (including fluorinated graphite), poly (trifluorethylene), polyamide, polyimide; compounds which form adsorption layers, for example long-chain carboxylic acids, fatty acid esters, ethers, alcohols, amines, amides, imides, phosphonates, phosphite; compounds which form layers through tribochemical reactions, for example saturated fatty acids, phosphoric acid, boric acid esters and thiophosphoric esters, xanthogenates, sulphurized fatty acids; compounds which form polymer-like layers, for example ethoxylated dicarboxylic acid partial esters, dialkyl phthalates, methacrylates, unsaturated fatty acids, sulphurized olefins and organometallic compounds, for example molybdenum compounds (molybdenum dithiophosphates and molybdenum dithiocarbamates MoDTC) and their combinations with ZnDTPs, copper-containing organic compounds.

[0246] Some of the compounds listed above may fulfil multiple functions. ZnDTP, for example, is primarily an antiwear additive and extreme pressure additive, but also has the character of an antioxidant and corrosion inhibitor (here: metal passivator/deactivator).

[0247] The above-detailed additives are described in detail, inter alia, in T. Mang, W. Dresel (eds.): Lubricants and Lubrication, Wiley-VCH, Weinheim 2001; R. M. Mortier, S. T. Orszulik (eds.): Chemistry and Technology of Lubricants.

[0248] The all-in-once lubricant formulation comprising the nanoparticle composition of the invention combines stability over the time, as well as improved anti-friction properties as shown below in the experimental part. This approach may therefore avoid any incompatibilities between different package components, dispersing agents, and other additives in the lubricant formulation as a single additive combines all properties.

EXPERIMENTAL PART

[0249] The invention is further illustrated in detail hereinafter with reference to examples and comparative examples, without any intention to limit the scope of the present invention.

Abbreviations

[0250] 9116 hexadecyltrimethoxysilane [0251] AMEO 3-aminopropyltriethoxysilane [0252] C.sub.1 AMA C.sub.1-alkyl methacrylate (methyl methacrylate; MMA) [0253] C.sub.4 AMA C.sub.4-alkyl methacrylate (n-butyl methacrylate) [0254] C.sub.12-14 AMA C.sub.12-14-alkyl methacrylate [0255] DMAPMAA N-3-Dimethylaminopropylmethacrylamid [0256] f.sub.branch degree of branching in mol % [0257] GLYEO 3-glycidyloxypropyltriethoxysilane [0258] MMA methyl(meth)acrylate [0259] MA-1 macroalcohol (hydroxylated hydrogenated polybutadiene Mn=4,900 g/mol) [0260] MM-1 macromonomer of hydrogenated polybutadiene MA-1 with methacrylate functionality (M.sub.n=4,900 g/mol) [0261] M.sub.n number-average molecular weight [0262] MTM Mini Traction Machine equipment [0263] M.sub.w weight-average molecular weight [0264] NB3020 Nexbase3020, Group III base oil from Neste with a KV.sub.100 of 2.2 cSt [0265] NB3043 Nexbase 3043, Group III base oil from Neste with a KV.sub.100 of 4.3 cSt [0266] OCTMO octyltrimethoxysilane [0267] PDI polydispersity index, molecular weight distribution calculated via M.sub.w/M.sub.n [0268] PS standard polystyrene calibration standards [0269] Si69 bis[3-(triethoxysilyl)propyl]polysulfid

[0270] Synthesis of a Hydroxylated Hydrogenated Polybutadiene (Macroalcohol) MA-1

[0271] The macroalcohol was synthesized by anionic polymerization of 1,3-butadiene with butyllithium at 20-45 C. On attainment of the desired degree of polymerization, the reaction was stopped by adding propylene oxide and lithium was removed by precipitation with methanol. Subsequently, the polymer was hydrogenated under a hydrogen atmosphere in the presence of a noble metal catalyst at up to 140 C. and 200 bar pressure. After the hydrogenation had ended, the noble metal catalyst was removed and organic solvent was drawn off under reduced pressure to obtain a 100% macroalcohol MA-1. Table 2 summarizes the characterization data of MA-1:

TABLE-US-00002 TABLE 2 Characterization data of used macroalcohol. Hydrogenation OH functionality M.sub.n [g/mol] level [%] [%] MA-1 4,900 >99 >98

[0272] Synthesis of Macromonomer MM-1

[0273] In a 2 L stirred apparatus equipped with saber stirrer, air inlet tube, thermocouple with controller, heating mantle, column having a random packing of 3 mm wire spirals, vapor divider, top thermometer, reflux condenser and substrate cooler, 1000 g of the above-described macroalcohol are dissolved in methyl methacrylate (MMA) by stirring at 60 C. Added to the solution are 20 ppm of 2,2,6,6-tetramethylpiperidin-1-oxyl radical and 200 ppm of hydroquinone monomethyl ether. After heating to MMA reflux (bottom temperature about 110 C.) while passing air through for stabilization, about 20 mL of MMA are distilled off for azeotropic drying. After cooling to 95 C., LiOCH.sub.3 is added and the mixture is heated back to reflux. After the reaction time of about 1 hour, the top temperature has fallen to 64 C. because of methanol formation. The methanol/MMA azeotrope formed is distilled off constantly until a constant top temperature of about 100 C. is established again. At this temperature, the mixture is left to react for a further hour. For further workup, the bulk of MMA is drawn off under reduced pressure. Insoluble catalyst residues are removed by pressure filtration (Seitz T1000 depth filter). Table 3 summarizes the MMA and LiOCH.sub.3 amounts used for the synthesis of macromonomer MM-1.

TABLE-US-00003 TABLE 3 Macroalcohol, MMA and catalyst amounts for the transesterification of the macromonomer Amount Amount Macromonomer Macroalcohol MMA [g] LiOCH.sub.3 [g] MM-1 MA-1 500 1.5

[0274] As described above, the polymer weight-average molecular weights (M.sub.w) of all inventive and comparative polymers were measured by gel permeation chromatography (GPC) using polystyrene calibration standards according to DIN 55672-1.

[0275] Preparation of Inventive ExampleAmine- and Macromonomer-Containing Polymer (P1):

[0276] 85 grams of Nexbase 3020, 85 grams of Berylane 230SPP, 98 grams of macromonomer, 107 grams of butyl methacrylate, 28 grams of styrene, 12.5 grams of lauryl methacrylate, 8.6 grams of dimethylaminopropylmethacrylamide, 0.5 grams of methyl methacrylate and 0.1 grams of n-dodecylmercaptan were charged into a 2-liter, 4-necked round bottom flask. The reaction mixture was stirred using a C-stirring rod, inerted with nitrogen, and heated to 115 C. Once the reaction mixture reached the setpoint temperature, 0.9 grams of tertbutyl-2-ethyleperoxyhexanoate were fed into the reactor over 3 hours. 0.5 grams of 2,2-di-(tert-butylperoxy)-butane were added in 30 minutes and 3 hours after the previous feed. The reaction was allowed to stir for one hour, and then an additional 175 grams of Nexbase 3020 were added to the reactor and allowed to mix for 1 hour. The polymer obtained has a weight-average molecular weight (M.sub.w) of 238,000 g/mol (PS standard).

[0277] Preparation of Comparative Example Polymer (P2):

[0278] 200 grams of Nexbase 3043, 28.36 grams of benzylmethacrylate, 255.2 grams of lauryl methacrylate (C.sub.12-14 AMA, 5.53 grams of n-dodecyl mercaptan (n-DDM) 5.53 grams of 2-Ethylhexylthioglycolate (TGEH) were charged into 2 liter, 4-necked round bottom flask. The reaction mixture was stirred using a C-stirring rod, inerted with nitrogen, and heated to 90 C. Once the reaction mixture reached the setpoint temperature, 2.83 grams t-butylper-2-ethylhexanoate was fed into the reactor over 2 hours. After 2 hours the mixture was heated up to 100 C. and after reaching the setpoint 1.42 grams oft-butylper-2-ethylhexanoate and 1.13 grams oftert-butylperpivalate were fed in one hour. Residual monomer was measured by gas chromatography to ensure good monomer conversion. The polymer obtained has a weight-average molecular weight (M.sub.w) of 9,470 g/mol (PS standard).

[0279] For the examples P1 and P2, the monomer components add up to 100%. The amount of initiator and chain transfer agent is given relative to the total amount of monomers. Table 4 below shows the monomer composition and reactants to prepare the polymers P1 and P2, as well as their final characterization.

TABLE-US-00004 TABLE 4 Composition, weight-average molecular weight and PDI of polymers according to the present invention. MM-1 styrene C.sub.4 AMA C.sub.1 AMA C.sub.12-14 AMA benzyl-methacrylate DMAPMA f.sub.branch Initiator CTA M.sub.w Ex [wt %] [wt %] [wt %] [wt %] [wt %] [wt %] [wt %] [%] [%] [g/mol] PDI P1 38.5 11.0 42.0 0.2 4.9 3.4 1.8 0.75 0.04 238,000 2.66 P2 90.0 10 1.9 3.9 9,470 1.47

[0280] Preparation of Nanoparticle Compositions According to the Invention

[0281] Inventive Example Dispersion IE1:

[0282] The ball mill equipment (Netzsch Laboratory Mill Micro Series) is pre-loaded with 230.85 g NB3043 oil and 82.4 g of P1 and 1.75 g silane (Dynasylan OCTMO) while the peristaltic pump is set to 90 rpm and the ball mill to 1000 rpm. Afterwards, 35 g of graphene nanoparticles (surface area of 700 m.sup.2/g and a G/D ratio of 1,1) are given into this solution. The peristaltic pump is adjusted to 130 rpm and the ball mill is set to a rotation speed of 3900 rpm. The dispersion is treated for 120 minutes (1.0 kWh energy is introduced). The particle size distribution (measured in Tegosoft DEC oil using dynamic light scattering equipment, LB-500, Horiba Ltd., Japan) shows a d90 value of 85 nm.

[0283] Inventive Example Dispersion IE2:

[0284] The ball mill equipment (Netzsch Laboratory Mill Micro Series) is pre-loaded with 230.85 g NB3043 oil and 82.4 g of P1 and 1.75 g silane (Dynasylan 9116) while the peristaltic pump is set to 90 rpm and the ball mill to 1000 rpm. Afterwards, 35 g of graphene nanoparticles (surface area of 700 m.sup.2/g and a G/D ratio of 1.1) are given into this solution. The peristaltic pump is adjusted to 130 rpm and the ball mill is set to a rotation speed of 3900 rpm. The dispersion is treated for 120 minutes (1.0 kWh energy is introduced). The particle size distribution (measured in Tegosoft DEC oil using dynamic light scattering equipment, LB-500, Horiba Ltd., Japan) shows a d90 value of 76 nm.

[0285] Inventive Example Dispersion IE3:

[0286] The ball mill equipment (Netzsch Laboratory Mill Micro Series) is pre-loaded with 229.1 g NB3043 oil and 82.4 g of P1 and 3.5 g silane (Dynasylan OCTMO) while the peristaltic pump is set to 90 rpm and the ball mill to 1000 rpm. Afterwards, 35 g of graphene nanoparticles (surface area of 700 m.sup.2/g and a G/D ratio of 1.1) are given into this solution. The peristaltic pump is adjusted to 130 rpm and the ball mill is set to a rotation speed of 3900 rpm. The dispersion is treated for 120 minutes (1.0 kWh energy is introduced). The particle size distribution (measured in Tegosoft DEC oil using dynamic light scattering equipment, LA-950, Horiba Ltd., Japan) shows a d90 value of 75 nm.

[0287] Inventive Example Dispersion IE4:

[0288] The ball mill equipment (Netzsch Laboratory Mill Micro Series) is pre-loaded with 231.9 g NB3043 oil and 82.4 g of P1 and 0.7 g silane (Dynasylan OCTMO) while the peristaltic pump is set to 90 rpm and the ball mill to 1000 rpm. Afterwards, 35 g of graphene nanoparticles (surface area of 700 m.sup.2/g and a G/D ratio of 1.1) are given into this solution. The peristaltic pump is adjusted to 130 rpm and the ball mill is set to a rotation speed of 3900 rpm. The dispersion is treated for 120 minutes (1.0 kWh energy is introduced). The particle size distribution (measured in Tegosoft DEC oil using dynamic light scattering equipment, LB-500, Horiba Ltd., Japan) shows a d90 value of 73 nm.

[0289] Inventive Example Dispersion IE5:

[0290] The ball mill equipment (Netzsch Laboratory Mill Micro Series) is pre-loaded with 230.85 g NB3043 oil and 82.4 g of P1 and 1.75 g silane (Dynasylan OCTMO) while the peristaltic pump is set to 90 rpm and the ball mill to 1000 rpm. Afterwards, 35 g of graphene nanoparticles (surface area of 500 m.sup.2/g and a G/D ratio of 1.0) are given into this solution. The peristaltic pump is adjusted to 130 rpm and the ball mill is set to a rotation speed of 3900 rpm. The dispersion is treated for 120 minutes (1.0 kWh energy is introduced). The particle size distribution (measured in Tegosoft DEC oil using dynamic light scattering equipment, LB-500, Horiba Ltd., Japan) shows a d90 value of 96 nm.

[0291] Inventive Example Dispersion IE6:

[0292] The ball mill equipment (Netzsch Laboratory Mill Micro Series) is pre-loaded with 230.85 g NB3043 oil and 82.4 g of P1 and 1.75 g silane (Dynasylan OCTMO) while the peristaltic pump is set to 90 rpm and the ball mill to 1000 rpm. Afterwards, 35 g of graphene nanoparticles (surface area of 250 m.sup.2/g and a G/D ratio of 1.5) are given into this solution. The peristaltic pump is adjusted to 130 rpm and the ball mill is set to a rotation speed of 3900 rpm. The dispersion is treated for 120 minutes (1.0 kWh energy is introduced). The particle size distribution (measured in Tegosoft DEC oil using dynamic light scattering equipment, LB-500, Horiba Ltd., Japan) shows a d90 value of 194 nm.

[0293] Inventive Example Dispersion IE7:

[0294] The pre-treated graphene-based material was prepared as follows: Ethanol (p.a.) was presented in an amount of 3 ppw. 1 ppw of silane (Dynasylan OCTMO) were carefully added with a syringe and stirred for about 10 min at room temperature. A clear phase was obtained. 10 ppw of graphene nanoparticles (surface area of 700 m.sup.2/g and G/D ratio of 1.1) were filled into the grinding vessel of a ball mill and 4 ppw of the clear phase were added. Moreover, 4 ppw grinding balls with diameters of 2 to 10 mm were added. The reaction took place in the ball mill at a rotational speed of 600 rpm for 15 min. The obtained functionalized graphene-based material was subsequently cleaned with ethanol (p.a.) by means of a Soxhlet apparatus, pre-dried overnight in the fume hood and subsequently dried at the rotary evaporator at 100 C. and at a pressure of 30 hPa during 3 h.

[0295] Milling Process:

[0296] The ball mill equipment (Netzsch Laboratory Mill Micro Series) is pre-loaded with 221.85 g NB3043 oil and 82.4 g of P1 while the peristaltic pump is set to 90 rpm and the ball mill to 1000 rpm. Afterwards, 35 g of pre-treated graphene nanoparticles are given into this solution. The peristaltic pump is adjusted to 130 rpm and the ball mill is set to a rotation speed of 3900 rpm. The dispersion is treated for 120 minutes (1.0 kWh energy is introduced). The particle size distribution (measured in Tegosoft DEC oil using dynamic light scattering equipment, LB-500, Horiba Ltd., Japan) shows a d90 value of 100 nm.

[0297] Inventive Example Dispersion IE8:

[0298] The pre-treated graphene-based material was prepared as follows: Ethanol (p.a.) was presented in an amount of 3 ppw. 1 ppw of silane (Dynasylan 9116) were carefully added with a syringe and stirred for about 10 min at room temperature. A clear phase was obtained. 10 ppw of graphene nanoparticles (surface area of 700 m.sup.2/g and G/D ratio of 1.1) were filled into the grinding vessel of a ball mill and 4 ppw of the clear phase were added. Moreover, 4 ppw grinding balls with diameters of 2 to 10 mm were added. The reaction took place in the ball mill at a rotational speed of 600 rpm for 15 min. The obtained functionalized graphene-based material was subsequently cleaned with ethanol (p.a.) by means of a Soxhlet apparatus, pre-dried overnight in the fume hood and subsequently dried at the rotary evaporator at 100 C. and at a pressure of 30 hPa during 3 h.

[0299] Milling Process:

[0300] The ball mill equipment (Netzsch Laboratory Mill Micro Series) is pre-loaded with 221.85 g NB3043 oil and 82.4 g of P1 while the peristaltic pump is set to 90 rpm and the ball mill to 1000 rpm. Afterwards, 35 g of pre-treated graphene nanoparticles are given into this solution. The peristaltic pump is adjusted to 130 rpm and the ball mill is set to a rotation speed of 3900 rpm. The dispersion is treated for 120 minutes (1.0 kWh energy is introduced). The particle size distribution (measured in Tegosoft DEC oil using dynamic light scattering equipment, LB-500, Horiba Ltd., Japan) shows a d90 value of 75 nm.

[0301] Inventive Example Dispersion IE9:

[0302] Preparation of pre-treated graphene-based material: The pre-treated graphene-based material was prepared as follows: Ethanol (p.a.) was presented in an amount of 3 ppw. 1 ppw of silane (Dynasylan AMEO) were carefully added with a syringe and stirred for about 10 min at room temperature. A clear phase was obtained. 10 ppw of graphene nanoparticles (surface area of 700 m.sup.2/g and G/D ratio of 1.1) were filled into the grinding vessel of a ball mill and 4 ppw of the clear phase were added. Moreover, 4 ppw grinding balls with diameters of 2 to 10 mm were added. The reaction took place in the ball mill at a rotational speed of 600 rpm for 15 min. The obtained functionalized graphene-based material was subsequently cleaned with ethanol (p.a.) by means of a Soxhlet apparatus, pre-dried overnight in the fume hood and subsequently dried at the rotary evaporator at 100 C. and at a pressure of 30 hPa during 3 h.

[0303] Milling Process:

[0304] The ball mill equipment (Netzsch Laboratory Mill Micro Series) is pre-loaded with 221.85 g NB3043 oil and 82.4 g of P1 while the peristaltic pump is set to 90 rpm and the ball mill to 1000 rpm. Afterwards, 35 g of pre-treated graphene nanoparticles are given into this solution. The peristaltic pump is adjusted to 130 rpm and the ball mill is set to a rotation speed of 3900 rpm. The dispersion is treated for 120 minutes (1.0 kWh energy is introduced). The particle size distribution (measured in Tegosoft DEC oil using dynamic light scattering equipment, LB-500, Horiba Ltd., Japan) shows a d90 value of 79 nm.

[0305] Inventive Example Dispersion IE10:

[0306] The pre-treated graphene-based material was prepared as follows: Ethanol (p.a.) was presented in an amount of 3 ppw. 1 ppw of silane (Dynasylan GLYEO) were carefully added with a syringe and stirred for about 10 min at room temperature. A clear phase was obtained. 10 ppw of graphene nanoparticles (surface area of 700 m.sup.2/g and G/D ratio of 1.1) were filled into the grinding vessel of a ball mill and 4 ppw of the clear phase were added. Moreover, 4 ppw grinding balls with diameters of 2 to 10 mm were added. The reaction took place in the ball mill at a rotational speed of 600 rpm for 15 min. The obtained functionalized graphene-based material was subsequently cleaned with ethanol (p.a.) by means of a Soxhlet apparatus, pre-dried overnight in the fume hood and subsequently dried at the rotary evaporator at 100 C. and at a pressure of 30 hPa during 3 h.

[0307] Milling Process:

[0308] The ball mill equipment (Netzsch Laboratory Mill Micro Series) is pre-loaded with 221.85 g NB3043 oil and 82.4 g of P1 while the peristaltic pump is set to 90 rpm and the ball mill to 1000 rpm. Afterwards, 35 g of pre-treated graphene nanoparticles are given into this solution. The peristaltic pump is adjusted to 130 rpm and the ball mill is set to a rotation speed of 3900 rpm. The dispersion is treated for 120 minutes (1.0 kWh energy is introduced). The particle size distribution (measured in Tegosoft DEC oil using dynamic light scattering equipment, LB-500, Horiba Ltd., Japan) shows a d90 value of 81 nm.

[0309] Inventive Example Dispersion IE11:

[0310] The ball mill equipment (Netzsch Laboratory Mill Micro Series) is pre-loaded with 171.37 g NB3020 oil and 123.5 g of P1 and 2.63 g silane (Dynasylan OCTMO) while the peristaltic pump is set to 90 rpm and the ball mill to 1000 rpm. Afterwards, 52.5 g of graphene nanoparticles (surface area of 500 m.sup.2/g and a G/D ratio of 1.0) are given into this solution. The peristaltic pump is adjusted to 130 rpm and the ball mill is set to a rotation speed of 3900 rpm. The dispersion is treated for 120 minutes (1.0 kWh energy is introduced). The particle size distribution (measured in Tegosoft DEC oil using dynamic light scattering equipment, LB-500, Horiba Ltd., Japan) shows a d90 value of 83 nm.

[0311] Inventive Example Dispersion IE12:

[0312] The ball mill equipment (Netzsch Laboratory Mill Micro Series) is pre-loaded with 232.42 g NB3043 oil and 82.4 g of P1 and 0.18 g silane (Dynasylan OCTMO) while the peristaltic pump is set to 90 rpm and the ball mill to 1000 rpm. Afterwards, 35 g of graphene nanoparticles (surface area of 500 m.sup.2/g and a G/D ratio of 1.0) are given into this solution. The peristaltic pump is adjusted to 130 rpm and the ball mill is set to a rotation speed of 3900 rpm. The dispersion is treated for 120 minutes (1.0 kWh energy is introduced). The particle size distribution (measured in Tegosoft DEC oil using dynamic light scattering equipment, LB-500, Horiba Ltd., Japan) shows a d90 value of 86 nm.

[0313] Preparation of Nanoparticle Compositions as Comparative Examples

[0314] Comparative Example Dispersion CE1:

[0315] The ball mill equipment (Netzsch Laboratory Mill Micro Series) is pre-loaded with 230.85 g NB3043 oil and 82.4 g of P1 while the peristaltic pump is set to 90 rpm and the ball mill to 1000 rpm. Afterwards, 35 g of graphene nanoparticles (surface area of 700 m.sup.2/g and a G/D ratio of 1.1) are given into this solution. The peristaltic pump is adjusted to 130 rpm and the ball mill is set to a rotation speed of 3900 rpm. The dispersion is treated for 120 minutes (1.0 kWh energy is introduced). The particle size distribution (measured in Tegosoft DEC oil using dynamic light scattering equipment, LB-500, Horiba Ltd., Japan) shows a d90 value of 98 nm.

[0316] Comparative Example Dispersion CE2:

[0317] 2 g of graphene nanoparticles (surface area of 700 m.sup.2/g and a G/D ratio of 1.1) are given into a solution of 16 g NB3043 and 2 g silane (Dynasylan OCTMO) while this mixture is treated with ultrasound (ultrasound processor UP400S with 400 Watt, 24 kHz with Ti-sonotrode), respectively. The mixture was thickening tremendously after 4 min of treatment. US treatment had to be stopped. The particle size distribution (measured in Tegosoft DEC oil using dynamic light scattering equipment, LB-500, Horiba Ltd., Japan) shows a d90 value of 552 nm.

[0318] Comparative Example Dispersion CE3:

[0319] 1 g of graphene nanoparticles (surface area of 700 m.sup.2/g and a G/D ratio of 1.1) are given into a solution of 18 g NB3043 and 1 g silane (Dynasylan OCTMO) while this mixture is treated with ultrasound (ultrasound processor UP400S with 400 Watt, 24 kHz with Ti-sonotrode). The particle size distribution (measured in Tegosoft DEC oil using dynamic light scattering equipment, LB-500, Horiba Ltd., Japan) shows a d90 value of 494 nm.

[0320] Comparative Example Dispersion CE4:

[0321] 2 g of graphene nanoparticles (surface area of 700 m.sup.2/g and a G/D ratio of 1.1) are given into a solution of 13.3 g NB3043 and 4.7 g P1 while this mixture is treated with ultrasound (ultrasound processor UP400S with 400 Watt, 24 kHz with Ti-sonotrode) for 60 min. The particle size distribution (measured in Tegosoft DEC oil using dynamic light scattering equipment, LB-500, Horiba Ltd., Japan) shows a d90 value of 93 nm.

[0322] Comparative Example Dispersion CE5:

[0323] 2 g of graphene nanoparticles (surface area of 700 m.sup.2/g and a G/D ratio of 1.1) are given into a solution of 14.6 g NB3043, 3.3 g P1 and 0.1 g silane (Dynasylan OCTMO) while this mixture is treated with ultrasound (ultrasound processor UP400S with 400 Watt, 24 kHz with Ti-sonotrode) for 60 min. The particle size distribution (measured in Tegosoft DEC oil using dynamic light scattering equipment, LB-500, Horiba Ltd., Japan) shows a d90 value of 93 nm.

[0324] Comparative Example Dispersion CE6:

[0325] The ball mill equipment (Netzsch Laboratory Mill Micro Series) is pre-loaded with 280 g NB3043 oil and 35 g of P2 while the peristaltic pump is set to 90 rpm and the ball mill to 1000 rpm. Afterwards, 35 g of graphene nanoparticles (surface area of 700 m.sup.2/g and a G/D ratio of 1.1) are given into this solution. The peristaltic pump is adjusted to 130 rpm and the ball mill is set to a rotation speed of 3900 rpm. (1.0 kWh energy is introduced). The particle size distribution (measured in Tegosoft DEC oil using dynamic light scattering equipment, LB-500, Horiba Ltd., Japan) shows a d90 value of 573 nm.

[0326] Comparative Example Dispersion CE7:

[0327] The ball mill equipment (Netzsch Laboratory Mill Micro Series) is pre-loaded with 230.85 g NB3043 oil and 82.4 g of P1 and 1.75 g silane (Dynasylan Si 69) while the peristaltic pump is set to 90 rpm and the ball mill to 1000 rpm. Afterwards, 35 g of graphene nanoparticles (surface area of 700 m.sup.2/g and a G/D ratio of 1.1) are given into this solution. The peristaltic pump is adjusted to 130 rpm and the ball mill is set to a rotation speed of 3900 rpm. The dispersion is treated for 120 minutes (1.0 kWh energy is introduced). The particle size distribution (measured in Tegosoft DEC oil using dynamic light scattering equipment, LB-500, Horiba Ltd., Japan) shows a d90 value of 76 nm.

[0328] Comparative Example Dispersion CE8:

[0329] The ball mill equipment (Netzsch Laboratory Mill Micro Series) is pre-loaded with 230.85 g NB3043 oil and 82.4 g of P1 and 1.75 g silane (Dynasylan OCTMO) while the peristaltic pump is set to 90 rpm and the ball mill to 1000 rpm. Afterwards, 35 g of graphene nanoparticles (surface area of 170 m.sup.2/g and a G/D ratio of 2.8) are given into this solution. The peristaltic pump is adjusted to 130 rpm and the ball mill is set to a rotation speed of 3900 rpm. The mixture showed tremendous thickening after 120 min of treatment. (1.0 kWh energy is introduced). The particle size distribution (measured in Tegosoft DEC oil using dynamic light scattering equipment, LB-500, Horiba Ltd., Japan) shows a d90 value of 1267 nm.

[0330] Comparative Example Dispersion CE9:

[0331] The ball mill equipment (Netzsch Laboratory Mill Micro Series) is pre-loaded with 230.85 g NB3043 oil and 82.4 g of P1 and 1.75 g silane (Dynasylan OCTMO) while the peristaltic pump is set to 90 rpm and the ball mill to 1000 rpm. Afterwards, 35 g of graphene nanoparticles (surface area of 110 m.sup.2/g and a G/D ratio of 2.6) are given into this solution. The peristaltic pump is adjusted to 130 rpm and the ball mill is set to a rotation speed of 3900 rpm. The mixture showed tremendous thickening after 120 min of treatment. (1.0 kWh energy is introduced). The particle size distribution (measured in Tegosoft DEC oil using dynamic light scattering equipment, LB-500, Horiba Ltd., Japan) shows a d90 value of 1807 nm.

[0332] Table 5 below summarizes the inventive nanoparticle compositions (inventive dispersions IE1 to IE11) according to the invention and the comparative nanoparticle compositions (comparative dispersions C1 to C9). The listed weight percentages are based on the total weight of the respective nanoparticle compositions.

TABLE-US-00005 TABLE 5 Comparison of dispersions according the present invention Graphene (A) in Graphene Graphene Raman Polymer Nexbase 3043 (D) Example wt % BET [m2/g] G/D Polymer (B) in wt % Silane (C) Silane in wt % in wt % IE1 10 700 1.1 P1 10 OCTMO 0.5 79.5 IE2 10 700 1.1 P1 10 9116 0.5 79.5 IE3 10 700 1.1 P1 10 OCTMO 1 79 IE4 10 700 1.1 P1 10 OCTMO 0.2 79.8 IE5 10 500 1.0 P1 10 OCTMO 0.5 79.5 IE6 10 250 1.5 P1 10 OCTMO 0.5 79.5 IE7 10 700 1.1 P1 10 OCTMO 1 79 IE8 10 700 1.1 P1 10 9116 1 79 IE9 10 700 1.1 P1 10 AMEO 1 79 IE10 10 700 1.1 P1 10 GLYEO 1 79 IE11 15 500 1.0 P1 15 OCTMO 0.75 69.25 (Nexbase 3020) IE12 10 500 1.0 P1 10 OCTMO 0.05 79.95 CE1 10 700 1.1 P1 10 80 CE2 10 700 1.1 OCTMO 10 80 CE3 5 700 1.1 OCTMO 5 90 CE4 10 700 1.1 P1 7 83 CE5 10 700 1.1 P1 7 OCTMO 0.5 82.5 CE6 10 700 1.1 P2 10 80 CE7 10 700 1.1 P1 10 Si69 0.5 79.5 CE8 10 170 2.8 P1 10 OCTMO 0.5 79.5 CE9 10 110 2.6 P1 10 OCTMO 0.5 79.5

[0333] Dynamic Light Scattering (DLS)

[0334] The particle size distribution was measured in Tegosoft DEC oil using the dynamic light scattering equipment LB-500 produced by Horiba Ltd.

[0335] Dynamic light scattering (DLS) is a technique in physics that can be used to determine the size distribution profile of small particles in suspension or polymers in solution. This equipment can be used to measure the particle size of dispersed material in the range from 3 nm to 6 m. The measurement is based on the Brownian motion of the particles within the medium and the scattering of incident laser light because of a difference in refraction index of liquid and solid material.

[0336] The resulting value is the hydrodynamic diameter of the particle's corresponding sphere. The values d.sub.v50, d.sub.v90 and d.sub.v99 are common standards for discussion, as these describe the hydrodynamic diameter of the particle below which 50%, 90% or 99% of the particles are within the particle size distribution. The lower these values, the better the particle dispersion. Monitoring these values can give a clue about the particle dispersion stability. If the values increase tremendously, the particles are not stabilized enough and may tend to agglomerate and sediment over time resulting in a lack of stability. Depending on the viscosity of the medium, it can be stated, that a d90 value of <200 nm (e.g. for Nexbase base oil) is an indication for a stable dispersion as the particles are held in abeyance over time.

[0337] Example IE1, Example IE7 and Example IE9 of Table 5 were submitted to a stability test where these were characterized by measuring the particle size distribution using the DLS method previously described. This has been done after production, after one week and after four weeks, respectively, as shown in Table 6 below.

TABLE-US-00006 TABLE 6 Change of DLS values over time for chosen examples. Example # IE1 IE7 IE9 d50 values: after preparation [nm] 63 66 60 1 week [nm] 64 59 56 4 weeks [nm] 65 63 64 d90 values: after preparation [nm] 85 100 79 1 week [nm] 81 78 73 4 weeks [nm] 86 80 80 d99 values: after preparation [nm] 113 147 111 1 week [nm] 140 124 120 4 weeks [nm] 129 119 104

[0338] The results of Table 6 demonstrate the excellent stability of the nanoparticle compositions according to the invention and show that very little agglomeration occurs in these dispersions over a long period of time. The particle size values do not increase significantly.

[0339] Within the time frame of 4 weeks the d.sub.v50, d.sub.v90 and d.sub.v99 values are comparable and can be considered to correspond to a stable dispersion. Indeed, the values remain below the aforementioned d.sub.v90 of 200 nm, and taking into account the accuracy of the measurement method (approximately 10 relative %) the d90 values of the examples in Table 6 are close to the initial measured values after production. As a comparison, it may be mentioned that a dispersion using graphene particles according to the invention, but without the use of polymer compound (B) (example CE2) results in DLS values of 484, 552, 581 nm (d.sub.v50, d.sub.v90, d.sub.v99, respectively). These are much higher than the particles dispersed in the inventive dispersion system of the present invention.

[0340] Dispersion Stability Test by Visual Appearance

[0341] According to this invention, the performance of our nanoparticle compositions is judged by two further stability tests. Therefore, each sample was diluted to a 0.1 wt % solution of the nanoparticle composition, based on the total weight of the different compositions. The dilution was prepared by blending one concentrate chosen from the inventive examples or comparative examples in a 10 mL glass vial at room temperature. For example, 0.05 grams of inventive example IE1 were mixed with 4.95 grams of NB3043 to obtain a 0.1 wt % solution of graphene nanoparticles IE1-1.

[0342] The corresponding dilution was stored at room temperature. The vials were checked after 1 week, and after 4 weeks for signs of sedimentation or other instabilities (e.g. clearing up). The stability of the dispersion was judged visually by the amount of sedimentation after slowly tilting the vial. Sedimentation is the tendency for particles in suspension to settle out of the fluid in which they are entrained and come to rest against a barrier. Adverse effects resulting from the settlement of particles are usually handled by the use of dispersing agent. The sedimentation behavior was classified into 4 categories: o: no sedimentation (no particles settled at the bottom of the vial); A: minor sedimentation (some particles start to settle at the bottom of the vial); +: moderate sedimentation (thin layer at the bottom of the vial), and +++: nearly complete sedimentation (a great amount of particles have settled).

[0343] The results obtained are shown below in Table 7 for inventive examples and Table 8 for comparative examples.

[0344] Dynamic Viscosity

[0345] The dynamic viscosity was measured with the Physica MCR 301 from Anton Paar using the rotational viscosity method and a measuring plate PP25 with the distance set to 0.5 mm.

[0346] The motor of the viscometer drives a bob inside a fixed cup. The rotational speed of the bob is preset and produces a certain motor torque that is needed to rotate the measuring bob. This torque must overcome the viscous forces of the tested substance and is therefore a measure for its viscosity.

[0347] Data are measured at a shear rate of 100 s.sup.1 and 22 C.

[0348] Dispersion Stability Test by Monitoring Viscosity Changes

[0349] Key of the present invention is the production of stable, highly filled graphene nanoparticles dispersions. Over time, dispersed particles tend to interact with one another, especially if their surfaces show different polarity compared to the surrounding media. Additives are used within a dispersion to prevent this interaction. On the one hand, this interaction can cause agglomeration and sedimentation, which has been evaluated in the former section. On the other hand, this interaction might lead to a formation of networks within the fluid, which leads to a significant increase in viscosity of the dispersion.

[0350] To investigate the latter behavior, we conducted viscosity measurements of the dispersions after 1 and 4 weeks and calculated the change in viscosity. In respect of the present invention, this is the most important test. Out of the comparative examples, only those are submitted to this test, which were showing 1. a d.sub.v90 value smaller than 200 nm and 2. no strong sedimentation.

[0351] Viscosity measurements are always performed with the concentrated inventive and comparative examples (10 or 15 wt %) to properly judge the change of viscosity.

[0352] As shown below in Table 7, the inventors of the present invention were able to prepare nanoparticle dispersions which do not show a significant increase of viscosity after 4 weeks.

[0353] In contrast, the comparative nanoparticles dispersions in Table 8 show a significant viscosity increase after four weeks. The comparative example CE1 shows even a viscosity increase of more than 50% after only one week.

TABLE-US-00007 TABLE 7 Results from the stability check of the formulations according to the invention (inventive examples). IE1 IE2 IE3 IE4 IE5 IE6 IE7 IE8 IE9 IE10 IE11 IE12 Sedimentation Particle 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 test concentration wt % wt % wt % wt % wt % wt % wt % wt % wt % wt % wt % wt % (visual) in formulation Sedimentation So So So So So S So So So So So So (after 1 week) Sedimentation So S So So S S+ S So So So S So (after 4 weeks) Development Particle 10 10 10 10 10 10 10 10 10 10 15 10 of concentration wt % wt % wt % wt % wt % wt % wt % wt % wt % wt % wt % wt % viscosity in formulation Viscosity [mPas] 239 259 240 235 181 193 248 214 249 237 516 207 Change after Vo Vo Vo V Vo Vo Vo Vo Vo Vo Vo Vo 1 week Change after V V V V Vo Vo Vo Vo V V Vo Vo 4 weeks Judgement of sedimentation for Table 7: So: no sedimentation (no particles settled at the bottom of the vial) S: minor sedimentation (some particles start to settle at the bottom of the vial) S+: moderate sedimentation (thin layer at the bottom of the vial) S+++: nearly complete sedimentation (a big amount of particles have settled) Judgement of viscosity change for Table 7: Vo : no change of viscosity (<10% difference to original value) V: minor change of viscosity (>10%) V+: moderate change of viscosity (>20%) V+++: big change of viscosity (>50%)

TABLE-US-00008 TABLE 8 Results from the stability check of the formulations (comparative examples) CE1 CE2 CE3 CE4 CE5 CE6 CE7 CE8 CE9 Sedimentation Particle concentration 0.1 wt % 0.1 wt % 0.1 wt % 0.1 wt % 0.1 wt % 0.1 wt % 0.1 wt % 0.1 wt % 0.1 wt % test in formulation (visual) Sedimentation 0 +++ +++ +++ +++ + 0 +++ (after 1 week) Sedimentation 0 +++ +++ +++ +++ +++ 0 + +++ (after 4 weeks) Development Particle concentration 10 wt % n.m. due to sediment 10 wt % n.m. due n.m. due to of in formulation to sediment viscosity Viscosity [mPas] 615 308 particle Change after 1 week V+++ V size Change after 4 weeks V+++ V++ Judgement of sedimentation for Table 8: So: no sedimentation (no particles settled at the bottom of the vial) S: minor sedimentation (some particles start to settle at the bottom of the vial) S+: moderate sedimentation (thin layer at the bottom of the vial) S+++: nearly complete sedimentation (a big amount of particles have settled) Judgement of viscosity change for Table 8: Vo : no change of viscosity (<10% difference to original value) V: minor change of viscosity (>10%) V+: moderate change of viscosity (>20%) V+++: big change of viscosity (>50%) n.m .: not measured

[0354] As shown in Tables 7 and 8, the nanoparticle compositions, which do not contain any silane compound, do not show a good stability overtime (see comparative examples CE1, CE4 and CE6). This is either due to the fact that those show strong sedimentation or a big increase in viscosity. Nanoparticle dispersions solely produced by ultrasound treatment also do not show a good stability (see comparative examples CE2, CE3 and CE4). Although the particle size distribution can be low, a strong sedimentation is visible after 4 weeks. A milling treatment according to the present invention is needed to achieve stable nanoparticle compositions according to this invention.

[0355] Only the inventive examples according to the present invention show a combination of particle size lower than 200 nm (d.sub.v90), good visual stability without any significant amount of sediment and no big increase in viscosity after 4 weeks. The formulation prepared with a nanoparticle composition comprising a low amount of silane compound (C) also shows great dispersion stability without any particle sedimentation being observed and no increase in viscosity after four weeks (see inventive example IE12 prepared with a nanoparticle composition comprising 0.05% by weight of silane compound (C), based on the total weight of the nanoparticle composition). In case other polymers (see comparative example CE6) or graphene nanoparticles not fulfilling the definition according to the present invention (see comparative examples CE8 and CE9) are used, too high particle size (d.sub.v90), or strong sedimentation is observed.

[0356] Light transmittance measurement using a spectrophotometer Inventive example 1 has been diluted to 0.005 wt % particle content in NB3043 base oil to allow a light transmittance measurement with optical spectroscopy (resulting in a lubricant composition comprising 0.05 wt % of IE1). Using a cuvette with 1 cm width this sample was submitted to a measurement of the light absorption and transmittance using a Perkin Elmer Lambda 950S UV/Vis/NIR spectrophotometer. The light transmittance at 800 nm has been recorded after different days of storage.

[0357] These results in FIG. 1 show, that the compositions according to the invention are very stable against dilution and sedimentation over time. Indeed, the light transmittance of the sample only increases by about 1% after 28 days of storage (see FIG. 1). Compared to the state-of-the-art results as disclosed in U.S. Pat. No. 8,703,666 B2, where the light transmittance increases by about 45% after 28 days of storage, a much better performance can be achieved with the dispersions according to the present invention. This strong improvement in stability enables a good and reproducible usage in industrial applications.

[0358] Determination of the Reduction in Friction Via Mini Traction Machine (MTM)

[0359] The coefficient of friction was measured using a Mini traction machine named MTM2 from PCS Instruments following the test method described in Table 9 below. SRR refers to the Sliding Roll Ratio. This parameter was maintained constant during the 2 hours test and is defined as (U.sub.Ball-U.sub.Disc)/U wherein (U.sub.BallU.sub.Disc) represents the sliding speed and U the entrainment speed, given by U=(U.sub.Ball+U.sub.Disc)/2. Stribeck curves for each sample were measured according to protocol in Table 9.

TABLE-US-00009 TABLE 9 Protocol to measure the Stribeck curves. Method 1 Test Rig MTM 2 from PCS Instruments Disc Highly polished stainless Steel AISI 52100 Disc diameter 46 mm Ball Highly polished stainless Steel AISI 52100 Ball diameter 19.05 mm Speed 5-2500 mm/s Temperature 100 C. Load 30N SRR 50%

[0360] According to MTM Method 1, the friction coefficient was recorded over the complete range of speed for each blend and a Stribeck curve is obtained. The friction tests were performed according to these conditions for lubricating oil formulations comprising the inventive nanoparticle composition IE1 listed in Table 10. Friction test results thereof are disclosed in Tables 11 to 13 below. The listed weight percentages are based on the total weight of the different formulations.

[0361] The fully formulated industrial gear oil (IGO) composition according ISO VG 68 used in Table 10 comprises [0362] 79.5 wt % Nexbase 3060 (Base oil) [0363] 18.0 wt % VISCOBASE 5-220 (Base oil) [0364] 0.7 wt % PPD [0365] 1.8 wt % ADDITIN RC9420 (DI package) [0366] 0.2 wt % VISCOPLEX 14-520 (defoamer).

TABLE-US-00010 TABLE 10 Lubricating oil formulations according to the invention. Particle concentration Dispersion in formulation Lubricant IE1 Formulation 1 0.5 wt % 95 wt % 5.0 wt % Nexbase 3043 Formulation 2 0.5 wt % 95 wt % 0W-16 5.0 wt % engine oil Formulation 3 0.5 wt % 95 wt % ISO 5.0 wt % VG 68 IGO oil

[0367] To express in % the friction reduction, a quantifiable result can be expressed as a number and is obtained by integration of the friction value curves using the obtained corresponding Stribeck curves in the range of sliding speed 5 mm/s-60 mm/s using the trapezoidal rule. The area corresponds to the total friction over the selected speed regime. The smaller the area, the greater the friction-reducing effect of the product examined. The percentage friction reductions were calculated by using the values of the reference oil Nexbase 3043, which generates an area of friction of 6.32 mm/s. Positive values indicate a decrease of friction coefficients. Values in relation to the reference oil are compiled in Tables 11-13 below.

TABLE-US-00011 TABLE 11 Friction reduction in boundary regime for the formulation according to the invention compared to base oil. Friction area Reduction of Example from 5-60 mm/s Friction in % Reference 6.32 0 Nexbase 3043 Formulation 1 2.85 54.8

TABLE-US-00012 TABLE 12 Friction reduction in boundary regime for the formulation (top up on genuine engine oil 0W-16) according to the invention compared to genuine engine oil 0W-16 alone. Friction area Reduction of Example from 5-60 mm/s Friction in % Reference 3.80 0 0W-16 engine oil Formulation 2 2.57 32.3

TABLE-US-00013 TABLE 13 Friction reduction in boundary regime for the formulation (top up on fully formulated industrial gear oil ISO VG 68) according to the invention compared to fully formulated industrial gear oil ISO VG 68. Friction area Reduction of Example from 5-60 mm/s Friction in % Reference fully formulated 4.99 0 ISO VG 68 IGO Formulation 3 2.49 50.1

[0368] The experimental results show great friction reduction performance in comparison to the base oil reference. Indeed, the results of the calculated total friction in the range of sliding speed 5 mm/s-60 mm/s clearly show that the lubricating oil formulations comprising the nanoparticle compositions according to the invention strongly improve the reduction in friction.

[0369] Determination of the Wear Reduction in 4Ball Wear Test According DIN 51315-2

[0370] The same lubricating oil formulation 1 as used for the friction tests shows a diameter of the callotes on the state balls of 0.496 mm. Compared to the reference Nexbase 3043 oil alone the graphene dispersion decreases the wear by 41.2%.

[0371] The tribological results show that the graphene compositions of the present invention have not only a great anti-friction performance but also very good anti-wear properties thanks to highly stable dispersions over a long period of time.

[0372] It has been found that the nanoparticle composition of the present invention can comprise high concentrations of graphene particles (even at 10 wt % concentration) without having any problem of stability (agglomeration or viscosity increase in oil), while maintaining good friction and wear reduction properties. The graphene nanoparticles having both the BET and G/D ratio within the ranges as defined in claim 1 outperform any other tested graphene nanoparticles not fulfilling the BET and G/D ratio requirements of the invention in terms of dispersion stability. Indeed, the graphene nanoparticles not fulfilling the BET and G/D ratio requirements of the invention lead to a viscosity increase and sedimentation when dispersed in oil (comparative dispersion examples C8 and C9).