Low temperature molybdenum film deposition utilizing boron nucleation layers

Abstract

The disclosure relates to a method of making molybdenum films utilizing boron and molybdenum nucleation layers. The resulting molybdenum films have low electrical resistivity, are substantially free of boron, and can be made at reduced temperatures compared to conventional chemical vapor deposition processes that do not use the boron or molybdenum nucleation layers. The molybdenum nucleation layer formed by this process can protect the substrate from the etching effect of MoCl.sub.5 or MoOCl.sub.4, facilitates nucleation of subsequent CVD Mo growth on top of the molybdenum nucleation layer, and enables Mo CVD deposition at lower temperatures. The nucleation layer can also be used to control the grain sizes of the subsequent CVD Mo growth, and therefore controls the electrical resistivity of the Mo film.

Claims

1. A method of making a molybdenum layer, the method comprising: reaction of a boron comprising nucleation layer on a substrate with a vapor composition comprising molecules containing molybdenum and chlorine atoms, the substrate being at a temperature of between from 450 C. to 550 C.; said reaction consuming at least a portion of the boron nucleation layer and forming a molybdenum nucleation layer atop the substrate.

2. The method of claim 1 wherein the thickness of the boron comprising nucleation layer is between from about 5 to about 50.

3. A method of making a molybdenum layer, the method comprising: reaction of a boron comprising nucleation layer on a substrate with a vapor composition comprising molecules containing molybdenum and chlorine atoms, the substrate being at a temperature of between from 450 C. to 550 C.; said reaction consuming at least a portion of the boron nucleation layer and forming a molybdenum nucleation layer atop the substrate, wherein the boron comprising nucleation layer is substantially consumed by said reaction, such that the molybdenum layer comprises less than 5 wt % boron, optionally less than 1 wt % boron, by elemental analysis.

4. The method of claim 3 comprising depositing the boron comprising nucleation layer atop the substrate, the substrate being at a temperature of between from 300 C. to 550 C.

5. The method of claim 3 further comprising: depositing a further boron comprising nucleation layer atop said molybdenum nucleation layer atop said substrate, the substrate being at a temperature of between from 300 C. to 550 C.; and reaction of the further boron comprising nucleation layer with a vapor composition comprising molecules containing molybdenum and chlorine atoms, the substrate being at a temperature of between from 450 C. to 550 C.; said reaction consuming at least a portion of the further boron nucleation layer and forming a further molybdenum nucleation layer.

6. The method of claim 5 wherein the thickness of the further boron comprising nucleation layer is between from about 5 to about 50.

7. The method of claim 5, wherein the deposited thickness of the further boron comprising nucleation layer is less than the deposited thickness of the boron comprising nucleation layer atop the substrate.

8. The method of claim 5 comprising vapor depositing the boron comprising nucleation layer atop the substrate for a first period of time and vapor depositing the further boron comprising nucleation layer for a second period of time, the second period of time being shorter than the first period of time.

9. The method of claim 5, wherein the further boron comprising nucleation layer is substantially consumed by said reaction, such that the further molybdenum layer comprises less than 5 wt % boron, optionally less than 1 wt % boron by elemental analysis.

10. The method of claim 5 wherein the steps of depositing and reaction are repeated thereby forming a plurality of further molybdenum nucleation layers.

11. The method of claim 3, wherein the temperature of the substrate is between from 450 C. to 480 C. during the reaction of the boron comprising nucleation layer(s).

12. The method of claim 3, wherein the vapor composition is at a pressure of from between 10 torr to 60 torr.

13. The method of claim 3, wherein the vapor composition is substantially free of a reducing gas.

14. The method of claim 3, wherein the molybdenum nucleation layer atop the substrate, or a further molybdenum nucleation layer, constitutes a top molybdenum nucleation layer.

15. The method of claim 14, comprising vapor depositing a molybdenum complex to form a bulk molybdenum layer atop the top molybdenum nucleation layer at a temperature between from 450 C. to 550 C.

16. The method of claim 15, wherein the molybdenum complex comprises MoCl.sub.5 or MoOCl.sub.4.

17. The method as claim 15, wherein the thickness of the molybdenum film is 200 angstroms or more and the resistivity of the bulk molybdenum layer is 20% of the resistivity of a bulk molybdenum layer of substantially similar thickness 20% deposited from said molybdenum complex on a substrate at 700 C. that is absent the molybdenum nucleation layer.

18. The method of claim 15, comprising making a molybdenum film comprising the bulk molybdenum layer and one or more molybdenum nucleation layers, the film having an electrical resistivity measured at room temperature that is less than 20 .Math.cm for a molybdenum film thickness of 200 angstroms or more.

19. The method of claim 3, wherein the substrate comprises one or more molybdenum nucleation layers.

20. The method of claim 3, wherein the substrate comprises a semiconductor substrate.

Description

DETAILED DESCRIPTION

(1) The disclosure relates to methods of making molybdenum films on substrates utilizing boron and molybdenum nucleation layers. The resulting molybdenum films may have low electrical resistivity, may be substantially free of boron, and can be made at reduced temperatures compared to conventional chemical vapor deposition processes that do not use the boron or molybdenum nucleation layers. The molybdenum nucleation layer formed by this process can protect the substrate from the etching effect of chlorine containing precursors like MoCl.sub.5 or MoOCl.sub.4, can facilitate nucleation of subsequent CVD Mo growth atop of the molybdenum nucleation layer, and enables molybdenum CVD deposition at lower temperatures. The molybdenum nucleation layer can also be used to control the grain sizes of the subsequent CVD molybdenum growth, and therefore control the electrical resistivity of the final molybdenum film.

(2) The boron nucleation layer can be formed by first exposing the substrate (which may include a thin overlying film), to B.sub.2H.sub.6 gas in the temperature range from 300 C. to 550 C. and pressure range of from 10 Torr to 60 Torr. A solid nucleation or decomposition layer comprising boron is formed on the substrate surface (or overlying thin film) and the thickness of this boron comprising nucleation layer or boron comprising decomposition layer can be controlled by B.sub.2H.sub.6 flow and dose time. The thickness of this boron comprising nucleation layer can be between from 5 to 100 . Suitably, the thickness of the boron comprising nucleation layer may be in the range of from about 5 to about 50 angstroms, optionally in the range of from 5 to about 30 angstroms, for example in the range of from about 5 to about 20 angstroms.

(3) The molybdenum nucleation layer can be formed by exposure and reaction of the boron nucleation layer to a vapor composition that includes molybdenum, chlorine, and optionally oxygen at elevated temperatures. This reaction with the vapor composition consumes the boron nucleation layer and replaces it with a molybdenum nucleation layer. The vapor composition can include MoCl.sub.5, MoOCl.sub.4 or other materials. For example, the substrate with the boron nucleation layer can held at a temperature of between 450 C. and 550 C. on a stage in the reactor and can be exposed to a composition that comprises or consists only of MoCl.sub.5, or exposed to a composition that can be a mixture including MoCl.sub.5 and an inert gas like argon (Ar), or exposed to a composition that can be a mixture including MoCl.sub.5 and a reducing gas like hydrogen (H.sub.2). In another example, the substrate on a heated stage with the boron nucleation layer can be held at a temperature of between 450 C. and 550 C. and exposed to a composition that comprises or consists of MoOCl.sub.4, or exposed to a composition that can be a mixture including MoOCl.sub.4 and an inert gas like argon (Ar), or exposed to a composition that can be a mixture including MoOCl.sub.4 and a reducing gas like hydrogen (H.sub.2). Exposure of the boron nucleation layer at a temperature of between 450 C. and 550 C. to one or more of these compositions converts the boron nucleation layer into a molybdenum comprising nucleation layer.

(4) BCl.sub.3 or other boron containing volatile materials can be generated as a byproduct of the conversion of the boron nucleation layer to the molybdenum nucleation layer. This reaction has temperature cutoff of approximately 450 C.

(5) In the presence of H.sub.2, the reaction by-products may include HCl, BCl.sub.3 and OCl.sub.2 (in the case of vapor composition comprising MoOCl.sub.4). The reaction can occur with or without H.sub.2 co-reactant on the boron nucleation layer.

(6) The thickness of the resulting molybdenum nucleation layer depends on the starting thickness of the boron nucleation layer. In some versions a vapor composition that includes molybdenum, chlorine, and optionally oxygen, but that does not include a reducing gas, can be used to convert the boron nucleation layer into the molybdenum nucleation layer. The thickness of the resulting molybdenum nucleation layer is proportional to the thickness of boron nucleation layer.

(7) Advantageously, the steps of depositing a boron nucleation layer and reaction of the boron nucleation layer to form a molybdenum nucleation layer may be repeated to form one or more further boron nucleation layers.

(8) Where a plurality of boron nucleation layers are formed, these may be made in substantially identical fashion. Alternatively, differing conditions may be employed for different layers, e.g. as described anywhere herein.

(9) The method may comprise making a top molybdenum nucleation layer. The molybdenum nucleation layer atop said substrate, or a further molybdenum nucleation layer, may constitute the top molybdenum nucleation layer.

(10) Versions of the molybdenum film forming process can further include the act or step of vapor depositing a molybdenum complex on a top molybdenum nucleation layer on the substrate to form a bulk molybdenum layer. The bulk molybdenum layer and one or more underlying molybdenum nucleation layers make up the molybdenum film and the molybdenum film can have a thicknesses that range from 50 to 3000 ; in some versions the thickness of the molybdenum film can be from 200 to 1000 . The substrate can be at temperatures between from 450 C. to 550 C. during this bulk vapor deposition act or step. In some versions the molybdenum complex can be a vapor composition comprising molybdenum and chlorine atoms, and in other cases the molybdenum complex can be a vapor composition comprising molybdenum, chlorine, and oxygen atoms. Examples of molybdenum complexes that can be used in versions of the method include MoCl.sub.5 and MoOCl.sub.4.

(11) A composition comprising molecules containing molybdenum and chlorine atoms or a molybdenum complex containing molybdenum and chlorine atoms can be vaporized to make vapor compositions containing molybdenum and chlorine atoms for use in the molybdenum film forming method. The composition or complex can separately comprise MoCl.sub.5 (in some versions at a molecular purity of 99% or higher) or MoOCl.sub.4 (in some versions at a molecular purity of 99% or higher). In some versions the molybdenum complex can be an organometallic molybdenum compounds containing cyclopentadienyl and other ligands. The molybdenum complex can be purified by sublimation to a molecular purity of greater than 99.99%. For example, MoCl.sub.5 can be purified by sublimation to remove trace amounts of higher vapor pressure MoOCl.sub.4. Versions of the disclosure can include an ampoule adapted for used in a vapor deposition process, the ampoule contains MoCl.sub.5 at a molecular purity of greater than 99.99%. Another version of the disclosure can include an ampoule adapted for used in a vapor deposition process, the ampoule contains MoOCl.sub.4 at a molecular purity of greater than 99.99%. Sublimation can be used to purify the MoCl.sub.5 or MoOCl.sub.4 and remove unwanted metal halides and metal oxyhalides.

(12) Reference to the boron nucleation layer being substantially consumed in versions of the method of making a molybdenum film may refer to no boron being visible by SEM analysis of a cross section of a sample that had one or more boron nucleation layers replaced with one or more molybdenum nucleation layers. Substantially consumed may additionally or alternatively refer to less than 5 wt %, and in some cases less than 1 wt % boron being present in a molybdenum film and in any underlying molybdenum nucleation layers. The boron content can be determined by acid dissolution of the film from a substrate and measured by elemental analysis. Substantially consumed can also refer to a molybdenum film that has a resistivity measured at room temperature (RT, 20 C.-23 C.) that is within 20% or less of a molybdenum layer of similar thickness (10%) vapor deposited on a similar substrate at 700 C. from MoCl.sub.5.

(13) Thermal budget refers to the cumulative thermal energy imparted to a semiconductor microelectronic transistor, logic gate, or photovoltaic by all thermal processing steps during manufacturing. Controlling the thermal budget of a process can help prevent dopant redistribution injunctions and the diffusion of metals through barrier layers. If high temperatures are required during manufacturing, a moderate thermal budget may be achieved by limiting the duration of the process. Similarly, if a process requires significant time to complete, the temperature can be reduced to avoid an excessive thermal budget. In versions of the method, the molybdenum nucleation layers and bulk molybdenum layers can be deposited at temperatures below 500 C. and with similar deposition times compared to the 700 C. molybdenum process without the Mo nucleation layers. The lower deposition temperature for the new method disclosed herein can be used to decrease the demand on the thermal budget for processes where molybdenum films are used in semiconductor device manufacturing. Additionally, the lower process temperatures achieved by the current process can reduce costs by allowing the utilization of less expensive process equipment and designs.

(14) In versions of the method of making a molybdenum film, the decomposition layer or nucleation layer comprising boron is substantially free of borides. Similarly, the molybdenum nucleation layer and molybdenum film are substantially free of borides. Borides are materials that are formed between boron and a more electronegative element like silicon. Boride layers have been suggested as barrier layers in the manufacture of integrated circuits to inhibit the diffusion of metals and other impurities into regions underlying barrier layers. Borides are typically formed using chemical vapor deposition (CVD) techniques. For example, a metal tetrachloride may be reacted with diborane to form a metal diboride using CVD. However, when Cl-based chemistries are used to form boride barrier layers, reliability problems can occur. In particular, boride layers formed using CVD chlorine-based chemistries typically have a high chlorine content (e.g., chlorine content greater than about 3%). A high chlorine content is undesirable because the chlorine may migrate from the boride barrier layer into adjacent interconnection layers, which can increase the contact resistance of such interconnection layers and potentially change the characteristics of integrated circuits made therefrom. Molybdenum films prepared by the methods disclosed herein have been found to protect the substrate from the etching effect of MoCl.sub.5, MoOCl.sub.4.

(15) In versions of forming a molybdenum film atop a substrate, the bulk molybdenum, the molybdenum nucleation layer(s), and the boron nucleation layers, can be deposited by vapor deposition. Vapor deposition includes any of chemical vapor deposition (CVD), atomic layer deposition (ALD), high and low pressure versions of these, and versions including assisted versions of these such as but not limited to plasma enhanced CVD, laser assisted, and microwave assisted.

(16) In some versions of the disclosure there is a layer of material overlying the substrate. This layer can be for example, but is not limited to, titanium nitride, molybdenum, or other material that would underlie a bulk molybdenum layer in a semiconductor device. For example, when refractory elemental metals like molybdenum are used in polysilicon-metal gate electrode structures, a thin conductive diffusion barrier can be disposed between the polysilicon and the elemental metal to prevent silicidation of the elemental metal during high-temperature processing. The diffusion barrier is typically comprised of conductive metal nitrides such as tungsten nitride (WN), titanium nitride (TiN), tantalum nitride (TaN) and/or respective silicon-containing ternary compounds such as WSiN, TiSiN, and TaSiN.

(17) In some versions, the substrate comprises a molybdenum nucleation layer, for example a molybdenum nucleation layer previously formed in accordance with the invention.

(18) Substrates that can be used in versions of the method include silicon, silicon oxide, gallium arsenide, alumina, and other ceramics and metals with suitable chemical and temperature properties.

(19) A boron nucleation layer or boron decomposition layer can have a thickness that ranges from about 5 angstroms (5 ) to about 100 angstroms (100 ). A molybdenum nucleation layer can have a thickness that ranges from about 5 angstroms (5 ) to about 100 angstroms (100 ). The boron nucleation layer can be deposited on the substrate or a layer on top of the substrate that is heated to a temperature that is between 250 C. up to and including 550 C. In some versions the boron nucleation layer can be deposited on the substrate or a layer on top of the substrate that is heated to a temperature that is between 300 C. up to and including 450 C. Boron nucleation layers made between 300 C. up to and including 450 C. provide bulk molybdenum layers that are smooth and that have low resistivity. The one or more B.sub.2H.sub.6 nucleation layers can be deposited by exposing the substrate to B.sub.2H.sub.6 gas in the temperature range from 300 C. to 550 C. and pressure range from 10 Torr to 60 Torr.

(20) Bulk molybdenum vapor deposition from a molybdenum complex onto the top nucleation layer can occur in the presence of a reducing gas like hydrogen. For example, the molybdenum pentachloride MoCl.sub.5 complex can be delivered to the reaction chamber by sublimation from a vessel or ampoule with a flow of N.sub.2 or Ar carrier gas. An ampoule vessel containing the molybdenum pentachloride as the complex can for example be heated to a temperature of between 70 C. and 100 C. The temperature for the vaporization will vary depending on the molybdenum complex used. Lower ampoule temperatures are beneficial for all vapor generation because it can decrease the decomposition of the molybdenum complex and thereby provide more consistent molybdenum deposition rates.

EXAMPLE 1

(21) This example illustrates deposition of molybdenum on top of a 50 thick titanium nitride layer on a substrate. The thickness of the titanium nitride layer after deposition of the molybdenum nucleation layer and bulk molybdenum was within 20% of the thickness of the initially measured TiN layer thickness illustrating that the molybdenum nucleation layer provided etch resistance to the underlying TiN from chlorine-containing precursor and byproducts.

(22) The molybdenum film atop the substrate was deposited by a multi-step process at varying temperatures and pressures as detailed in Table 1 below. The first step included sub-steps of: depositing a solid boron nucleation layer on a titanium nitride layer on top of a SiO.sub.2 substrate; and exposure of the solid boron nucleation layer (or boron decomposition layer) to a composition that included MoCl.sub.5 and hydrogen resulting in substantial replacement of the boron nucleation layer with a molybdenum nucleation layer.

(23) The next step was the deposition of a new boron nucleation layer atop the molybdenum nucleation layer in a shorter soak than the first boron layer nucleation, and then a bulk molybdenum deposition that began by substantially consuming the new boron nucleation to form molybdenum followed seamlessly by bulk deposition of molybdenum to form the molybdenum film on the substrate by reaction of MoCl.sub.5 with H.sub.2.

(24) The electrical resistivity of the film was measured at room temperature (RT, 20 C. to 23 C.).

(25) TABLE-US-00001 TABLE 1 Post Measurement B.sub.2H.sub.6 soak MoCl.sub.5/H.sub.2 Resistivity Stage Dep Stage Pressure Dep Mo film @RT (four- temp Time temp Chamber Time thickness point Sample Process ( C.) (seconds) ( C.) (Torr) (seconds) () .Math. cm) 9 Nuc 300 60 480 10 30 1.6 NA Bulk 300 30 480 10 600 10 Nuc 300 60 480 40 30 683.8 12.9 Bulk 300 30 480 40 600 11 Nuc 300 60 460 40 30 563.2 13.7 Bulk 300 30 460 40 600 12 Nuc 300 60 450 40 30 297.6 16.9 Bulk 300 30 450 40 600

(26) As detailed in Table 1, the deposition temperature of molybdenum nucleation layer was conducted at temperatures of from 480 C. to 450 C. and specifically at temperatures of 480 C., 460 C., or 450 C. The pressure for the nucleation or bulk molybdenum deposition step was changed between 10 Torr and 40 Torr. The MoCl.sub.5 ampoule temperature (Amp temp C.) was 90 degrees Celsius.

(27) The results of this example show that at 10 Torr process pressure, little or no Mo deposition was obtained at 480 C. However at 40 Torr process pressure, Mo film deposition rates resulted in films that were about 300 or thicker and that the deposition rate decreased as deposition temperature decreased. At 480 C. and 40 Torr pressure the molybdenum deposition rate was about 65 /min; at 460 C. and 40 Torr pressure the molybdenum deposition rate was about 54 /min; and at 460 C. and at 40 Torr pressure the molybdenum deposition rate was about 28 /min.

(28) The results of this example also show that molybdenum films were made comprising the bulk molybdenum layer and one or more molybdenum nucleation layers which had a four point electrical resistivity measured at room temperature (RT, 20 C.-23 C.) that was between from 12 .Math.cm to 20 .Math.cm for the molybdenum films having a thickness of from between 700 angstroms to 300 angstroms respectively. All films showed low resistivity of below 20 .Math.cm when measured at room temperature (RT, 20 C.-23 C.).

EXAMPLE 2

(29) This comparative example illustrates the deposition of molybdenum on a substrate without a molybdenum nucleation layer. Deposition was tested at stage temperatures of from 550 C. to 700 C. and deposition times were varied from 30 seconds to 600 seconds. Deposits of MoCl.sub.5 to form Mo were made on a 100 TiN layer on top of a SiO.sub.2 substrate. The MoCl.sub.5 ampoule was heated to 70 C., the chamber pressure was 60 Torr, H.sub.2 flow rate was 2000 sccm, and argon carrier gas flow was 50 sccm.

(30) The results in Table 2 show that CVD deposition of Mo film was achieved on TiN coated substrates using MoCl.sub.5/H.sub.2 at stage temperature above 550 C. At lower temperature (e.g. <550 C. stage temperature) Mo ceased to deposit due to substrate etching effect from MoCl.sub.5 and inadequate nucleation.

(31) TABLE-US-00002 TABLE 2 Resistivity Molybdenum (four-point Stage (substrate) Dep. Time film .Math. cm) Sample temperature ( C.) (seconds) thickness () @RT 322-237-15 700 30 64.4 27.5 322-237-12 700 180 340.8 16.1 322-237-13 700 120 231.2 21.8 322-399-7 600 60 59.9 40.4 322-399-5 600 180 150.5 28.3 322-399-3 600 300 248.2 30.3 322-399-9 550 600 241.7 60.0 322-399-13 550 180 37.1 56.0

(32) The results of this example show that at approximately the same deposition time of 180 seconds, the thickness of the deposited molybdenum film decreased from 341 at 700 C. (deposition rate of 1.89 /sec), to 150 at 600 C. (deposition rate of 0.83 /sec), and was as low as 37 at 550 C. (deposition rate of 0.2 /sec). For films of similar thickness prepared at the different temperatures, the molybdenum film resistivity measured at room temperature (RT, 20 C.-23 C.) increased with decreasing deposition temperature. For example the 241 thick Mo film deposited at 550 C. had a resistivity of 60 .Math.cm; the 248 thick Mo film that was deposited at 600 C. had a resistivity of 30.3 .Math.cm, while the 231 thick film that was deposited at 700 C. had resistivity of 21.8 .Math.cm.

EXAMPLE 3

(33) This example illustrates making a molybdenum film comprising one or more molybdenum nucleation layers and a bulk molybdenum layer deposited by vapor deposition from MoCl.sub.5.

(34) The resulting molybdenum films were made and characterized as detailed in Table 3. The substrates used had a 50 titanium nitride layer atop SiO.sub.2. Formation of the solid boron nucleation layer on the TiN layer was performed at a stage temperature of 300 C. chamber pressure of 40 Torr, a B.sub.2H.sub.6 flow of 35 sccm and an argon flow of 250 sccm; times were varied between 60 and 30 seconds depending on whether a boron nucleation layer was being formed on the TiN or on the initial molybdenum nucleation layer. The estimated thickness of the boron nucleation layer was 5 to 30 angstroms.

(35) MoCl.sub.5 ampoule temperature was 90 C., chamber pressure was 20 Torr, argon carrier flow was 100 sccm, H.sub.2 was 2000 sccm and stage temperature varied from 480 C. to 500 C. Reaction times were varied between 30 seconds and 600 seconds depending on whether a molybdenum nucleation layer was being formed by consuming the initial boron nucleation layer or whether the second molybdenum nucleation layer was being formed followed by bulk Mo CVD.

(36) TABLE-US-00003 TABLE 3 B.sub.2H.sub.6 soak MoCl.sub.5/H.sub.2 Post Measurement Substrate Substrate Mo film Resistivity Temp Temp Time Thickness (4-point, Sample Process ( C.) Time (sec) ( C.) (sec) () .Math. cm)@RT A Nuc 300 60 500 30 638.9 14.3 Bulk 300 30 500 600 B Nuc 300 60 480 30 385.5 19.1 Bulk 300 30 480 600

(37) These molybdenum films had electrical resistivities measured at room temperature that ranged between from 12 .Math.cm to 25 .Math.cm for the molybdenum layer having a thickness of from between 800 angstroms to 200 angstroms respectively.

(38) The results of this example further show that low resistivity molybdenum films can be made at substrate temperatures of between from 480 C. and 500 C. by consuming a boron nucleation layer via the reaction of the boron comprising nucleation layer on the substrate with a vapor composition comprising molecules containing molybdenum and chlorine atoms. The resistivity of the bulk molybdenum film in this example was 20% of the resistivity as measured at room temperature of a bulk molybdenum layer of substantially similar thickness (10%) deposited from the same molybdenum complex on a similar substrate at 700 C. that was absent the molybdenum nucleation layer. For example, the deposition of molybdenum on a similar substrate using the molybdenum complex of sample 322-237-12 in Example 2 gave a film with a resistivity of about 16.1 .Math.cm for a 340 thick film.

EXAMPLE 4

(39) This example illustrates the detrimental effect of excessive residual boron on resistivity of molybdenum films deposited with boron nucleation layers and the cutoff temperature for the deposition of molybdenum using boron nucleation layers.

(40) The molybdenum thickness following deposition at substrate temperatures 450 C., 500 C., and 550 C. were measured after 1, 2, 3, 4, 5 cycles. After 5 nucleation cycles, the molybdenum film thickness at the 450 C. deposition temperature was less than 25 . After 5 nucleation cycles, the molybdenum film thickness at the 500 C. deposition temperature was about 275 . After 5 nucleation cycles, the molybdenum film thickness at the 550 C. deposition temperature was about 410 . Based on these results the cutoff temperature for the reaction between MoCl.sub.5 and boron was determined to be between 450 C. and 500 C.

(41) The molybdenum film resistivities measured at room temperature following deposition at substrate temperatures 500 C., and 550 C. were measured after 1, 2, 3, 4, 5 cycles. The resistivity after 1 nucleation cycle at 500 C. was too high to measure, while the resistivity of molybdenum film after 1 nucleation cycle at 550 C. was about 310 .Math.cm. The resistivity after 2 nucleation cycles for the molybdenum film formed at 500 C. was about 250 .Math.cm, while the resistivity of molybdenum film after 2 nucleation cycle at 550 C. was about 275 .Math.cm. The resistivity after 5 nucleation cycles for the molybdenum film formed at 500 C. was about 250 .Math.cm, while the resistivity of molybdenum film after 5 nucleation cycle at 550 C. was about 340 .Math.cm. The resistivities after 2 nucleation cycles in this example are much higher than similar films made after 2 nucleation cycles in Example 1 for example, and without wishing to be bound by theory, is believe to be due to the presence of the boron in the films.

EXAMPLE 5

(42) This example illustrates the deposition of molybdenum on a substrate without a boron nucleation layer that had a TiN layer. The substrate was heated to 700 C. on a stage in the reactor and treated with a composition comprising MoCl.sub.5 vapor and differing amounts of hydrogen gas. Process conditions included an inert argon gas flow of 50 sccm, a chamber pressure of 60 Torr, and a low hydrogen flow rates of 2000 sccm and a high hydrogen flow rate of 4000 sccm.

(43) The results of this example show that the 4 point measured electrical resistivity of the molybdenum film deposited on the substrate without a nucleation layer ranged from about 15.Math.cm to 23 .Math.cm for a 200 thick molybdenum film deposited without a boron nucleation layer to about 10 .Math.cm to 16 .Math.cm for a 600-800 thick molybdenum film deposited without a boron nucleation layer. The resistivity of all films prepared using the higher hydrogen flow rate were lower than those prepared at the lower hydrogen flow rate and for approximately 800 thick molybdenum films, the resistivity of the film made at the higher hydrogen flow rate was lower by about 5 .Math.cm compared to samples made at the lower hydrogen flow rate. The molybdenum film resistivity decreased with increasing film thickness.

(44) While various compositions and methods are described, it is to be understood that this invention is not limited to the particular molecules, compositions, designs, methodologies or protocols described, as these may vary. It is also to be understood that the terminology used in the description is for the purpose of describing the particular versions or embodiments only, and is not intended to limit the scope of the present invention which will be limited only by the appended claims.

(45) It must also be noted that as used herein and in the appended claims, the singular forms a, an, and the include plural reference unless the context clearly dictates otherwise. Thus, for example, reference to an nucleation layer is a reference to one or more nucleation layers and equivalents thereof known to those skilled in the art, and so forth. Unless defined otherwise, all technical and scientific terms used herein have the same meanings as commonly understood by one of ordinary skill in the art. Methods and materials similar or equivalent to those described herein can be used in the practice or testing of embodiments of the present invention. All publications mentioned herein are incorporated by reference in their entirety. Nothing herein is to be construed as an admission that the invention is not entitled to antedate such disclosure by virtue of prior invention. Optional or optionally means that the subsequently described event or circumstance may or may not occur, and that the description includes instances where the event occurs and instances where it does not. All numeric values herein can be modified by the term about, whether or not explicitly indicated. The term about generally refers to a range of numbers that one of skill in the art would consider equivalent to the recited value (i.e., having the same function or result). In some embodiments the term about refers to 10% of the stated value, in other embodiments the term about refers to 2% of the stated value. While compositions and methods are described in terms of comprising various components or steps (interpreted as meaning including, but not limited to), the compositions and methods can also consist essentially of or consist of the various components and steps, such terminology should be interpreted as defining essentially closed or closed member groups.

(46) Although the invention has been shown and described with respect to one or more implementations, equivalent alterations and modifications will occur to others skilled in the art based upon a reading and understanding of this specification and the annexed drawings. The invention includes all such modifications and alterations and is limited only by the scope of the following claims. In addition, while a particular feature or aspect of the invention may have been disclosed with respect to only one of several implementations, such feature or aspect may be combined with one or more other features or aspects of the other implementations as may be desired and advantageous for any given or particular application. Furthermore, to the extent that the terms includes, having, has, with, or variants thereof are used in either the detailed description or the claims, such terms are intended to be inclusive in a manner similar to the term comprising. Also, the term exemplary is merely meant to mean an example, rather than the best. It is also to be appreciated that features, layers and/or elements depicted herein are illustrated with particular dimensions and/or orientations relative to one another for purposes of simplicity and ease of understanding, and that the actual dimensions and/or orientations may differ substantially from that illustrated herein.