Method of producing hydrocarbons from methane

Abstract

A method for producing hydrocarbons and hydrogen from methane. The method includes packing a catalyst comprising platinum, bismuth and a support material into a reactor; introducing a reactant mixture containing methane into the reactor such that the reactant mixture containing methane is in close contact with the reactant mixture; and heating the reactant mixture containing methane to a temperature for a period of time.

Claims

1. A method for producing hydrocarbons and hydrogen from methane comprising: packing a catalyst comprising platinum, bismuth and a support material into a reactor; introducing a reactant mixture containing methane and an inert gas into the reactor; and subjecting the reactant mixture to a methane coupling reaction to produce hydrocarbons comprising ethane, the coupling reaction comprising a temperature between 500 C. to 700 C. and a time between 1 and 8 h, wherein the reactant mixture containing methane is converted to ethane with a carbon selectivity of at least 90%.

2. The method of claim 1, wherein the contact time is in the range of 50-1500 min.g.sub.cat/mol.

3. The method of claim 1, wherein the partial pressure of methane in the reactant mixture is in the range 0.1-1.0 atmosphere.

4. The method of claim 1, wherein the reactant mixture does not contain oxygen.

5. The method of claim 1, wherein the inert gas is one of argon, helium and nitrogen.

6. The method of claim 1, wherein platinum loading in the catalyst is in the range of 0.1-5.0 weight %.

7. The method of claim 1, wherein bismuth loading in the catalyst is in the range of 0.1-5.0 weight %.

8. The method of claim 1, wherein the support material is activated carbon.

9. The method of claim 8, wherein the specific surface area of the activated carbon is in the range of 200-2000 m.sup.2/g.

10. The method of claim 1, wherein the support material is ZSM-5 zeolite.

11. The method of claim 10, wherein the specific surface area of the ZSM-5 zeolite is in the range of 100-800 m.sup.2/g.

12. The method of claim 1, wherein the particle size of the support material is from 200 mesh to 10 mesh.

13. The method of claim 10, wherein the Si/Al ratio of ZSM-5 zeolite support is from 22 to 250.

14. The method of claim 1, the reactor is a tubular reactor.

Description

BRIEF DESCRIPTION OF DRAWINGS

(1) Some of the figures shown herein may include dimensions. Further, some of the figures shown herein may have been created from scaled drawings or from photographs that are scalable. It is understood that such dimensions or the relative scaling within a figure are by way of example, and not to be construed as limiting.

(2) FIG. 1A shows Product Distribution at 650 C. and 0.1 atm Methane Partial Pressure over the 1% Pt/ZSM-5 Catalyst

(3) FIG. 1B shows Product Distribution at 650 C. and 0.1 atm Methane Partial Pressure over the 1% Pt-0.1% Bi/ZSM-5 Catalyst

(4) FIG. 1C shows Product Distribution at 650 C. and 0.1 atm Methane Partial Pressure over the 1% Pt-0.2% Bi/ZSM-5 Catalyst

(5) FIG. 1D shows Product Distribution at 650 C. and 0.1 atm Methane Partial Pressure over the 1% Pt-0.5% Bi/ZSM-5 Catalyst

(6) FIG. 1E shows Product Distribution at 650 C. and 0.1 atm Methane Partial Pressure over the 1% Pt-0.8% Bi/ZSM-5 Catalyst

(7) FIG. 1F shows Product Distribution at 650 C. and 0.1 atm Methane Partial Pressure over the 1% Pt-1% Bi Catalyst

(8) FIG. 2A shows Ethane Selectivity for Different PtBi/ZSM-5 Catalysts under Various Methane Conversions, at 650 C. and 0.1 atm Methane Partial Pressure.

(9) FIG. 2B shows Turnover Frequency (TOF) for Different PtBi/ZSM-5 Catalysts under Various Methane Conversions, at 650 C. and 0.1 atm Methane Partial Pressure.

(10) FIG. 3A shows a Temperature-Programmed Investigation showing H.sub.2 Desorption (H.sub.2-TPD) from Different PtBi/ZSM-5 Catalysts 0.1 atm Methane Partial Pressure and 600 min.Math.g.sub.cat/mol Contact Time.

(11) FIG. 3B shows another Temperature-Programmed Investigation showing Surface Reaction (TPSR) Profiles for 1% Pt-0.8% Bi/ZSM-5 Catalyst at 0.1 atm Methane Partial Pressure and 600 min.Math.g.sub.cat/mol Contact Time.

(12) FIG. 4A shows Effect of Temperature on Conversion and Selectivity at 0.1 atm Methane Partial Pressure and 600 min.Math.g.sub.cat/mol Contact Time.

(13) FIG. 4B shows Effect of Methane Partial Pressure on Conversion and Selectivity at 650 C. and 600 min.Math.g.sub.cat/mol Contact Time.

(14) FIG. 4C shows Effect of Contact Time on Conversion and selectivity at 0.1 atm Methane Partial Pressure and 650 C.

(15) FIG. 4D shows Effect of Catalyst Stability on Conversion and Selectivity at 0.1 atm Methane Partial Pressure, 650 C. and 300 min.Math.g.sub.cat/mol Contact Time.

DETAILED DESCRIPTION

(16) For the purposes of promoting an understanding of the principles of the disclosure, reference will now be made to the embodiments illustrated in the drawings and specific language will be used to describe the same. It will nevertheless be understood that no limitation of the scope of the disclosure is thereby intended.

(17) In this description, it is disclosed that the present disclosure describes that a catalyst containing platinum and bismuth supported on ZSM-5 zeolite selectively converts methane to ethane with high carbon selectivity (>90%) and typical methane conversion 2-3%, along with equivalent molar hydrogen generated as a by-product. The catalyst exhibits no deactivation for an 8-hour test, indicating good stability and prevention of coke formation. According to this disclosure, stable methane coupling is achieved in a continuous flow reactor, at relatively moderate temperatures (500-700 C.), with methane conversion >2% and carbon selectivity to C.sub.2 hydrocarbon species >90%. In the context of this disclosure the terms PtBi catalyst or PtBi bimetallic catalyst mean platinum and bismuth supported on a support material such as but not limited to ZSM-5 zeolite.

(18) In experiments leading to this disclosure, various PtBi bimetallic catalysts were prepared, characterized and tested in a fixed-bed reactor. These catalysts exhibit similar BET surface area (372-412 m.sup.2/g), pore size (2.8-3.5 nm), pore volume (0.33-0.41 cm.sup.3/g) and Pt metal dispersion (22-29%). TEM scans showed that metals were successfully loaded on ZSM-5 support and the metal dispersion (calculated by TEM-based particle size) values were consistent with the H.sub.2-O.sub.2 titration data. The XRD patterns for various PtBi/ZSM-5 catalysts are compared to diffraction patterns for unsupported MFI/ZSM-5. (ZSM-5 (MFI) is well understood by those skilled in the art. Mobil-5 (framework type MFI from ZSM-5 (five)) is an aluminosilicate zeolite belonging to the pentasil family of zeolites. Its chemical formula is Na.sub.nAl.sub.nSi.sub.96-nO.sub.192.16H.sub.2(0<n<27) reported in the International Zeolite Association (IZA) structure database. Supported and unsupported ZSM-5 exhibit similar patterns, likely due to low metal loading (1 wt % or less) and high Pt dispersion (20-30%). The fresh and used catalysts contained essentially the same amount of Pt and Bi as designed.

(19) As shown in FIG. 1, for the 1 wt % Pt catalyst, methane conversions were between 3% to 6%, while no hydrocarbon but only hydrogen was detected (FIG. 1A), owing to coke formation over the pure Pt surface. For the 1 wt % Bi catalyst, on the other hand, no methane conversion (<0.1%) was found. For the 1 wt % Pt-0.1 wt % Bi catalyst, methane conversion was similar to results of the 1 wt % Pt catalyst, with again no any hydrocarbon generated. For other four bimetallic catalysts with 1 wt % Pt and 0.1-1.0 wt % Bi, ethane was produced with a variety of carbon selectivity values ranging from 17% to 95%.

(20) FIG. 2A shows ethane selectivity for different PtBi/ZSM-5 catalysts under various methane conversions, at 650 C. and 0.1 atm methane partial pressure. Referring to FIG. 2A, it can be seen that by varying contact time of feed methane with packed catalyst, different methane conversions were obtained. (Unit of Contact Time (t) is obtained as follows: F (Species flowrate): mol/min W (Catalyst packing amount): g.sub.cat Definition of contact time: t=W/F=(g.sub.cat)/(mol/min)=min.Math.g.sub.cat/mol)
All methane conversions were less than 7%, limited by thermodynamic equilibrium under the operating conditions, corresponding to
CH.sub.4.fwdarw.0.5C.sub.2H.sub.6+0.5H.sub.2(1)
CH.sub.4.fwdarw.0.5C.sub.2H.sub.4+H.sub.2(2)
As shown in FIG. 2A, the carbon selectivity toward ethane always decreased with increase of methane conversion for all four catalysts. In particular, for the 1 wt % Pt-0.8 wt % Bi catalyst, carbon selectivity towards ethane was 85-95% when methane conversion was 1-5%. Note that equilibrium methane nonoxidative conversion to C.sub.2 species is about 2-3% at 650 C., while higher than equilibrium conversion was typically observed for methane nonoxidative conversion at short time on stream (TOS) in the literature. For consistency, all data reported in our work for catalytic performance comparison were taken at 1 h TOS. As reported in the literature, Bi addition to Pt could tune catalytic activity, where Bi functions as site blocker [28,29], while Bi alone shows poor catalytic activity. For increasing amounts of Bi addition to Pt, chemisorption of small molecules (e.g., H.sub.2, CO, and C.sub.2H.sub.4) was found to be attenuated, indicating relatively lower activity for reaction and higher tolerance for poison species. Coverage values of chemisorbed species, influenced by both geometric and electronic effects, also depend on molecular size, which indicates that, for a specific reaction, a particular Pt/Bi composition is favored. For example, it was reported that Pt.sub.1.00 Bi.sub.0.95 exhibits excellent activity for hydrogen evolution, while prior work described that 3% Pt-0.6% Bi provides the highest 1,3-dihydroxyacetone yield from glycerol selective oxidation.

(21) FIG. 2B shows turnover frequency (TOF) for different PtBi/ZSM-5 catalysts under various methane conversions, at 650 C. and 0.1 atm Methane Partial Pressure. Referring to FIG. 2B it can be seen that that over various catalysts tested in FIG. 2A, turnover frequencies (TOF) based on Pt surface dispersion were essentially constant (0.042-0.053 s.sup.1). This feature demonstrates that surface Pt is the active site for methane activation, as reported previously in literature.

(22) FIG. 3A shows H.sub.2 temperature-programmed desorption (H.sub.2-TPD). Profiles in FIG. 3A demonstrate that hydrogen uptake at room temperature was attenuated with increasing Bi addition to Pt/ZSM-5. Bi has been reported to function as a site blocker onto Pt surface, hence less activity of the PtBi bimetallic catalysts. For 1 wt % Bi catalyst, no hydrogen uptake was found, indicating inactive nature for Bi as shown in FIG. 2 A. Temperature-programmed surface reaction (TPSR) profiles in FIG. 3B describe that below 500 C. methane cannot be activated, owing to chemical stability of methane molecule. Between ca. 500 to 650 C., methane was converted to equivalent molar amounts of ethane and hydrogen, as indicated by reaction: Eq. (1). From ca. 700 to 800 C., methane conversion continued to increase, while ethane concentration decreased from ca. 2.5% to nearly zero. Hydrogen production rate from 700 to 900 C., however, continued to increase, implying further dehydrogenation of methane and leading to coke formation. As reported in the literature, not only initial activation of methane (CH.sub.4.fwdarw.CH.sub.3+H), but also further dehydrogenation of methane (e.g. forming CH.sub.2, CH and C species) occurs over Pt surface owing to relatively low reaction barriers of CH bond cleavage (<1 eV). Thus as compared to CC coupling (reaction barriers typically >2 eV over flat surface and 1-2 eV over step surface), Pt catalysts preferably promote further dehydrogenation of methane rather than CC coupling, eventually forming coke, which is consistent with the 1 wt % Pt curve in FIG. 2A. In addition to the Pt surface, CC coupling could also occur at acidic sites of ZSM-5, as reported previously. Since the 1% Pt/ZSM-5 catalyst, as described in FIGS. 1 and 2, did not lead to any C.sub.2 product, the acidic site in ZSM-5 appears to be inactive for CC coupling in NOCM conversion in the present study. Ethane dehydrogenation to ethylene and/or acetylene could occur over pure Pt surfaces. With the addition of a second metal to Pt, binding of molecules is typically weaker over bimetallic surfaces, indicating relatively higher reaction barriers. As reported in the literature, a shorter contact time favors lower reactivity of ethane dehydrogenation. These are likely reasons for the limited ethane dehydrogenation product in the present study. By adding Bi to Pt/ZSM-5 catalyst, as reported in FIGS. 2A and 3B, methane was activated under relatively low temperature (500-700 C.), while further dehydrogenation of methane, leading to coke deposit, were suppressed owing to the less active PtBi surface as compared to pure Pt surface.

(23) Temperature-programmed oxidation (TPO) investigations for used 1% Pt and used 1% Pt-0.8% Bi catalysts show thatinitial oxidation of used 1% Pt occurred at ca. 300 C., followed by two clear peaks at 440 and 540 C., respectively. For used 1% Pt-0.8% Bi, however, only one distinguished peak was identified, although it was followed by slight dragging (indicating another small peak). By integrating TPO curves, accumulated coke amounts were obtained. The 1% Pt-0.8% Bi after deployment as a catalyst contained much less coke (27 mg/g.sub.cat) than the used 1% Pt (497 mg/g.sub.cat). These observations suggest that by addition of Bi to Pt/ZSM-5 catalyst, methane was activated at relatively low temperature (600-700 C.), while further dehydrogenation of methane, leading to coke deposits, was suppressed owing to the less active PtBi surface in comparison to the pure Pt surface. In our prior works, Bi was used as a promoter for either tuning selectivity toward target products or improving catalyst stability. With the participation of guaiacol molecules over PtBi catalysts, it was proposed that CH.sub.4 partially decomposed on the Pt surface and methyls coupled to form ethane. It appears that, in the present work, Bi addition to Pt combines these two functions: promoting NOCM selectivity to ethane and extending catalyst lifetime.

(24) FIG. 4A shows temperature effect on NOCM over the range 500-700 C. Similar to results shown in FIG. 3B, methane conversion increased with temperature while ethane selectivity decreased, reaching maximum ethane yield (selectivityconversion) 1.8% at 650 C. For standard operating conditions, methane partial pressure was 0.1 atm. FIG. 4B shows that 0.1-1 atm of methane partial pressure gave essentially the same C.sub.2 selectivity, yet higher methane conversion at lower methane partial pressure. This feature occurs when thermodynamics dominates NOCM conversion. FIG. 4C illustrates the contact time effect on NOCM conversion. When long contact time was used, the main by-product was aromatic coke, although small amounts of ethylene and benzene were detected as well. It has been proposed that in all non-oxidative conversion of methane, C.sub.2 species was produced as intermediates for either heavier hydrocarbon or coke formation. Thus methane conversion typically follows a series reaction network: CH.sub.4.fwdarw.C.sub.2H.sub.6.fwdarw.C.sub.xH.sub.y (x>2, y0). In the present disclosure, since the intermediate C.sub.2 species was the target product, as shown in FIG. 4C, it exhibited a selectivity peak at ca. 600 min.Math.g.sub.cat/mol, as expected from kinetic analysis. FIG. 4D shows that, following an initial transient period, both methane conversion and carbon selectivity towards ethane were stable over the entire 8-hour test.

(25) From the foregoing discussion, it can be seen that, in general, existing technologies for direct transformation of methane are not followed industrially owing to inefficient carbon atom utilization. In the present disclosure a simple heterogeneous catalytic process is described which can be carried out under relatively moderate temperature (500-700 C.) for stable methane conversion into ethane with carbon selectivity >90% and methane conversion 2-3%. With incorporation of available separation and recycling schemes, the technology of this disclosure can be exploited on an industrial scale.

(26) From the foregoing detailed description, it is an objective of this disclosure to describe a method for producing hydrocarbons and hydrogen from methane. The method includes packing or placing a catalyst comprising Pt (primary metal), Bi (promoter) and a support for platinum/bismuth into a reactor, and introducing a reactant mixture containing methane into the reactor in which the catalyst is placed such that the reactant mixture comes into contact with the catalyst. Such packing or placing the catalyst in the rector is generally well understood by those skilled in the art. The reactant mixture containing methane is then heated to a temperature for a contact time. The phrase contact time is well understood by those skilled in chemical engineering processes and typical units for contact time are min.g.sub.cat/mol , as explained earlier (mol=mole).

(27) It should be noted that some embodiments of the methods of this disclosure, the reactor is a tubular reactor.

(28) A non-limiting range of the temperature to which is the reactant mixture is heated in the reactor is in the non-limiting range of 473 K-1273 K. The contact time for the methane feed form the reactant mixture is in the non-limiting range of 50-1500 min.gcat/mol. A non-limiting range for the partial pressure of methane in the reactant mixture is 0.1 to 1.0 atmosphere. In one version of the method, the reactant mixture does not contain any oxygen. In some versions of the method, the reactant mixture can include an inert gas such as, but not limited to argon or helium or nitrogen or a combination thereof.

(29) Methods of using support materials are well known to those skilled in the art and are well described in literature. A non-limiting range for particles comprising such a support material is 200 mesh to 10 mesh. Examples of such support materials suitable for the methods of this disclosure include but not limited to activated carbon and ZSM-5 zeolite. If activated carbon is used as a support material, a non-limiting range for the specific surface area of the activated carbon is 200-2000 m.sup.2/g. If ZSM-5 zeolite is used as a support material, a non-limiting range for the specific surface area of the ZSM-5 zeolite is 100-800 m.sup.2/g. Further, a non-limiting range for Si/Al ratio of ZSM-5 zeolite for use a support material for the catalysts of this disclosure is 22 to 250.

(30) The platinum loading in the platinum-bismuth-support material combination is in the non-limiting range of 0.1 to 5.0 weight percent. The bismuth loading in the platinum-bismuth-support material combination is in the non-limiting range of 0.1 to 5.0 weight percent. An example of such loading is 2% Pt-3% Bi-95% ZSM-5.

(31) While the present disclosure has been described with reference to certain embodiments, it will be apparent to those of ordinary skill in the art that other embodiments and implementations are possible that are within the scope of the present disclosure without departing from the spirit and scope of the present disclosure. Thus, the implementations should not be limited to the particular limitations described. Other implementations may be possible.