MAGNETOSTRICTIVE MATERIAL AND MAGNETOSTRICTION TYPE DEVICE USING THE SAME

Abstract

A magnetostrictive material includes a FeGaC alloy that is represented by Expression (1),

F.sub.(100-x-y)Ga.sub.xC.sub.y(1) (in Expression (1), x and y are respectively a content rate (at. %) of Ga and a content rate (at. %) of C, and satisfy that y0.5x7.75, yx+20, and y0.5).

Claims

1. A magnetostrictive material comprising: a FeGaC alloy that is represented by Expression (1),
Fe.sub.(100-x-y)Ga.sub.xC.sub.y(1) (in Expression (1), x and y are respectively a content rate (at. %) of Ga and a content rate (at. %) of C, and satisfy that y0.5x7.75, yx+20, and y0.5).

2. The magnetostrictive material of claim 1, wherein in Expression (1), x and y satisfy that y0.5x8, y0.5x8.75, yx+19, and yx+19.75.

3. The magnetostrictive material of claim 2, wherein an orientation difference of <100> orientation of the FeGaC alloy is in a range of 0 or greater and 10 or less, with respect to a maximum strain direction of the magnetostrictive material.

4. A magnetostriction type device comprising: the magnetostrictive material of claim 3, wherein a maximum strain direction of the magnetostrictive material is configured to form an inclination angle of 0 or greater and 10 or less, with respect to a predetermined direction of a dimensional change of the magnetostriction type device.

5. A magnetostriction type device comprising: the magnetostrictive material of claim 2, wherein a maximum strain direction of the magnetostrictive material is configured to form an inclination angle of 0 or greater and 10 or less, with respect to a predetermined direction of a dimensional change of the magnetostriction type device.

6. A magnetostriction type device comprising: the magnetostrictive material of claim 1, wherein a maximum strain direction of the magnetostrictive material is configured to form an inclination angle of 0 or greater and 10 or less, with respect to a predetermined direction of a dimensional change of the magnetostriction type device.

7. The magnetostrictive material of claim 1, wherein an orientation difference of <100> orientation of the FeGaC alloy is in a range of 0 or greater and 10 or less, with respect to a maximum strain direction of the magnetostrictive material.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0014] FIG. 1 is a schematic diagram when one example in which a maximum strain direction of a magnetostrictive material is configured to form an inclination angle of 0, with respect to a predetermined direction of a dimensional change of a magnetostriction type device according to an embodiment is viewed from above.

[0015] FIG. 2 is a schematic diagram when one example in which the maximum strain direction of the magnetostrictive material is configured to form the inclination angle of , with respect to the predetermined direction of the dimensional change of the magnetostriction type device according to the embodiment is viewed from above.

[0016] FIG. 3 is a diagram representing a relationship between a content rate of Ga and a content rate of C in which a magnetostriction quantity becomes 400 ppm or greater in Example 2 of the present disclosure.

[0017] FIG. 4 is a diagram representing the relationship between the content rate of Ga and the content rate of C in which the magnetostriction quantity becomes 480 ppm or greater in Example 2 of the present disclosure.

DESCRIPTION OF EMBODIMENTS

[0018] Hereinafter, a magnetostrictive material, a method for manufacturing the same, and a magnetostriction type device according to an embodiment of the present disclosure will be described, but the present disclosure is not limited to such an embodiment.

Magnetostrictive Material and Magnetostriction Type Device

[0019] The magnetostrictive material according to the present embodiment includes a FeGaC alloy that is represented by Expression (1),

Fe.sub.(100-x-y)Ga.sub.xC.sub.y(1)

[0020] (in Expression (1), x and y are respectively a content rate (at. %) of Ga and a content rate (at. %) of C, and satisfy that y0.5x7.75, yx+20, and y0.5).

[0021] In the present disclosure, a material in which a dimensional change may be generated by applying a magnetic field is referred to as a magnetostrictive material. The magnetostrictive material of the present embodiment may have any suitable form or shape so long as the magnetostrictive material is formed of the FeGaC alloy described above. The magnetostrictive material may have any suitable shape, may have a bulk shape (or a massive shape), for example, a cylindrical shape, a cubic shape, a rectangular parallelepiped shape, or other three-dimensional shapes, or may be a sheet (thin film shape, thin band shape, or the like) that may have a sheet shape, for example, a circular shape, an elliptical shape, a rectangular shape, or other planar shapes (or surfaces).

[0022] In the present disclosure, the content rate of an element is a proportion of the number of atoms of each element to the number of atoms of the whole FeGaC alloy, and is represented using a unit of at. % (atomic percent). In more detail, the FeGaC alloy is analyzed with an electron probe micro analyzer (EPMA), thereby, it is possible to measure the content rate of each element.

[0023] In the magnetostrictive material of the present embodiment, composition of the FeGaC alloy may include a trace element (for example, oxygen that is less than 0.005 at. %) which is inevitably mixed so long as being substantially configured by the exemplified element.

[0024] In the magnetostrictive material according to the present embodiment, C is added to the composition of a FeGa alloy, and tetragonal strain is induced into a Fe lattice, thereby, it is possible to realize high magnetostriction quantification. The content rate of C in the FeGaC alloy is in a range (y0.5x7.75, yx+20, and y0.5, see FIG. 3 described later) which is represented by the expression described above, thereby, it is possible to induce the tetragonal strain into the Fe lattice, it is possible to realize improvement of the magnetostriction quantity, and it is possible to maintain mechanical strength, in comparison with a FeGaAl-based alloy of the related art as described in Japanese Patent Unexamined Publication No. 2008-69434.

[0025] A proportion of the dimensional change due to a magnetostriction effect in the magnetostrictive material is referred to as a magnetostriction quantity. In more detail, in the present disclosure, the magnetostriction quantity (ppm) is represented by a value obtained by subtracting strain that is measured when the magnetic field is applied perpendicularly to a gauge axis of a strain gauge, from the strain of a sample when the magnetic field is applied parallel to the gauge axis of the strain gauge.

[0026] In the magnetostrictive material according to the present embodiment, in Expression (1), x and y satisfy that y0.5x8, y0.5x8.75, yx+19, and yx+19.75 (see FIG. 4 described later), thereby, it is possible to realize the high magnetostriction quantification more effectively.

[0027] In the present embodiment, the FeGaC alloy may have any crystal structure, and may have, for example, a monocrystalline structure or a polycrystalline structure.

[0028] In the present embodiment, for example, it is possible to make an orientation difference of <100> orientation of the FeGaC alloy be in the range of 0 or greater and 10 or less, with respect to a maximum strain direction of the magnetostrictive material. Such an orientation difference is preferably 0 or greater and 8 or less, more preferably 0 or greater and 6 or less, and further preferably 0 or greater and 4 or less.

[0029] By making the magnetostrictive material be in a crystal state in this manner, it is possible to favorably and easily obtain magnetostrictive properties more efficiently, and the magnetostrictive material may be more appropriately used when being used in the magnetostriction type device described later. This is considered that the present disclosure is not bound by any theory, but the <100> orientation is an orientation which is likely to be magnetized in the FeGaC alloy, and the magnetostrictive properties are obtained more efficiently, by making the orientation difference of the <100> orientation of the FeGaC alloy with respect to the maximum strain direction of the magnetostrictive material be in the range of 10 or less as small as possible (for example, the larger magnetostriction quantity is obtained by applying the same magnetic field, or the same magnetostriction quantity is obtained by applying the smaller magnetic field, in comparison with a case where the orientation difference described above exceeds 10).

[0030] In the present disclosure, the maximum strain direction of the magnetostrictive material means a direction in which the strain (dimensional change proportion) of the magnetostrictive material becomes the maximum in a case where the magnetic field is applied to the magnetostrictive material that may have any shape (in a case where the crystal structure of the magnetostrictive material is not clear, for example, the maximum strain direction of the magnetostrictive material is capable of being determined in trial and error manner, by measuring the strain in any direction of the magnetostrictive material while appropriately adjusting an applying direction of the magnetic field). In the present disclosure, the orientation difference of the <100> orientation of the FeGaC alloy may be determined by a known method, with respect to the maximum strain direction of the magnetostrictive material, and may be determined by, for example, an electron backscatter diffraction (EBSD) method. In more detail, it is possible to determine such an orientation difference, by applying a crystal orientation map due to the EBSD method to the surface of the FeGaC alloy of the magnetostrictive material according to the present embodiment, and measuring a distribution condition of the <100> orientation with respect to the maximum strain direction (this is understood as a sample direction, or a specified direction in a sample coordinate system) of the magnetostrictive material (the surface may be a surface which the magnetostrictive material originally has, or may be a surface which is exposed when the crystal orientation map is applied, and may be selected in accordance with the maximum strain direction of the magnetostrictive material). Specifically, for example, the orientation difference of the <100> orientation of the FeGaC alloy is in the range of 0 or greater and 10 or less, with respect to the maximum strain direction of the magnetostrictive material means that at the time of this measurement, in a case where a measuring point in which the <100> orientation with respect to the maximum strain direction of the magnetostrictive material is oriented to be 0 or greater and 10 or less is sought, the proportion of such measuring points to the measuring points in a measurable area is 100%, that is, in all measuring points of the measurable area, the <100> orientation with respect to the maximum strain direction of the magnetostrictive material is oriented to be 0 or greater and 10 or less. Other numerical value ranges relating to the orientation difference may be understood in the same manner.

[0031] In the present embodiment, the magnetostriction type device including the magnetostrictive material as described above is also provided. In the present disclosure, the magnetostriction type device indicates a device that includes the magnetostrictive material described above, in more detail, includes the magnetostrictive material as a configuration element (for example, a magnetostriction element), and has a structure which may extract energy (for example, power generation energy) using the same. Specifically, for example, various kinds of magnetostriction type apparatuses such as a magnetostriction type vibration power generation device, a magnetostriction type sensor, and a magnetostriction type actuator are cited. In the devices, the magnetostrictive material is included as a portion thereof in a structure and/or a shape suitable for each apparatus.

[0032] In the magnetostriction type device according to the present embodiment, the maximum strain direction of the magnetostrictive material may be configured to form an inclination angle of 0 or greater and 10 or less, with respect to a predetermined direction of the dimensional change of the magnetostriction type device. The inclination angle is more preferably 0 or greater and 8 or less, further preferably 0 or greater and 6 or less, and more further preferably 0 or greater and 4 or less.

[0033] The magnetostriction type device is configured with such an inclination angle, thereby, it is possible to obtain the magnetostrictive properties more efficiently. This is because it is possible to use the magnetostrictive properties of the magnetostrictive material more efficiently, by making the inclination angle between the maximum strain direction of the magnetostrictive material and the predetermined direction of the dimensional change of the magnetostriction type device be in the range of 10 or less as small as possible (for example, it is possible to use the larger magnetostriction quantity for the device by applying the same magnetic field, or it is possible to use the same magnetostriction quantity for the device by applying the smaller magnetic field, in comparison with a case where the inclination angle described above exceeds 10).

[0034] In the present disclosure, the predetermined direction of the dimensional change of the magnetostriction type device is a direction in which the dimensional change of the magnetostrictive material is predetermined or desired in the magnetostriction type device, for example, in order to extract the energy from the magnetostriction type device, and is a direction that may be determined in accordance with the applying direction of the magnetic field to the magnetostrictive material in the magnetostriction type device, and the shape, the structure and/or a use purpose of the magnetostriction type device. In the present disclosure, the inclination angle of the maximum strain direction of the magnetostrictive material is determined in a state where the magnetostrictive material is incorporated into the magnetostriction type device, with respect to the predetermined direction of the dimensional change of the magnetostriction type device.

[0035] A specific example of the magnetostriction type device will be described with reference to drawings. FIG. 1 is a schematic diagram when one example in which the maximum strain direction of the magnetostrictive material is configured to form the inclination angle of 0, with respect to the predetermined direction of the dimensional change of the magnetostriction type device according to the embodiment is viewed from above. As illustrated in FIG. 1, in magnetostriction type device 1, maximum strain direction 1 of magnetostrictive material 2 which is determined by the method described before becomes parallel, that is, forms the inclination angle of 0, with respect to predetermined direction 1 of the dimensional change thereof. FIG. 2 is a schematic diagram when one example in which the maximum strain direction of the magnetostrictive material is configured to form the inclination angle of , with respect to the predetermined direction of the dimensional change of the magnetostriction type device according to the embodiment is viewed from above. As illustrated in FIG. 2, in magnetostriction type device 2, maximum strain direction 132 of magnetostrictive material 4 which is determined by the method described before forms the inclination angle of , with respect to predetermined direction 2 of the dimensional change thereof. In this case, may form the inclination angle of 0 or greater and 10 or less, as described before. A configuration with such an inclination angle may be made, thereby, it is possible to obtain the magnetostrictive properties by the magnetostrictive material more efficiently.

Method for Manufacturing Magnetostrictive Material

[0036] It is possible to use any suitable alloy manufacturing method so long as a method for manufacturing the magnetostrictive material according to the present embodiment is a method for obtaining the magnetostrictive material of the FeGaC alloy, and the method for manufacturing the magnetostrictive material according to the present embodiment is not particularly limited. For example, Czochralski method (CZ method), Bridgman method, a rapid solidification method, or the like is cited. If the manufacturing is performed by the CZ method, it is possible to accurately manufacture chemical composition and crystal orientation, in a large-sized crystal.

EXAMPLES

[0037] Hereinafter, the present disclosure will be described in more detail by Examples and Comparative Examples, but the present disclosure is not limited to Examples.

Example 1

[0038] In Example 1, a sample of a FeGaC alloy in which C is added to a FeGa alloy is manufactured, measurements in mechanical strength and magnetostriction quantity are performed, and effectiveness of addition of C is confirmed.

Manufacturing of Sample for Measurement of FeGaC alloy

[0039] As illustrated in Table 1 later, a plurality of samples (Example 1-1 to Example 1-3, and Comparative Example 1-1 to Comparative Example 1-3) of the FeGaC alloys which are configured by the content rate (at. %) of Ga, the content rate (at. %) of C, and the content rate (at. %) of a balance Fe are prepared.

[0040] In order to manufacture each alloy sample, first, Fe (purity of 99.999%), Ga (purity of 99.999%), and C (purity of 99.99%) are respectively weighed using an electronic balance. The content rate of each element in each alloy sample is measured and adjusted by an EPMA analysis.

[0041] Each alloy sample is grown using a high-frequency induction heating type CZ furnace. A crucible of an outer diameter of 45 mm which is made of dense alumina is disposed on an inside of a graphite crucible of an inner diameter of 50 mm, and 400 g of a raw material of Fe, Ga, and C is put into each weighed alloy sample. After the crucible into which the raw material is put is put into a growth furnace, and vacuum is made in the furnace, an argon gas is introduced thereto. Thereafter, the heating of the apparatus is started, in a time point at which the inside of the furnace reaches atmospheric pressure, and the heating is performed for 12 hours, until a melting liquid is made. FeGa single crystal which is cut out in the <100> orientation is used as a seed crystal, and the seed crystal descends close up to the melting liquid. The seed crystal gradually descends while rotating at 5 ppm, and a tip of the seed crystal is in contact with the melting liquid.

[0042] While a temperature is gradually decreased, thereafter, the seed crystal is increased at a speed of which a pulling-up speed is 1.0 mm/hr, and a crystal growth is performed. As a result, a single crystal alloy of which a diameter is 10 mm, and a length of a straight body is 80 mm is obtained. The obtained single crystal alloy is cut out into each sample shape for the measurement described hereinafter, by wire electric discharge machining.

Measurement of Mechanical Strength (Tensile Strength (MPa) and Elongation (%))

[0043] The measurement of the mechanical strength is performed under a room temperature environment (25 C.) using a tensile tester. The sample for the measurement is a specimen of a dumbbell shape, and a fixer thereof is set to be the diameter of 6 mmthe length of 20 mm, and a neck thereof is set to be the diameter of 3 mmthe length of 20 mm. A distance between gripers of the tester is set to 20 mm, and load is applied in an axis direction until the specimen is broken, after the specimen is fixed. Elongation (%) is a proportion of an increment of the distance between the grippers at the time of the breakage to 20 mm of the distance between the grippers before the test. For example, in a case where the distance between the grippers at the time of breaking the specimen is 40 mm, the elongation is that (4020)/20100=100(%).

Measurement of Magnetostriction Quantity (ppm)

[0044] The measurement of the magnetostriction quantity is performed under the room temperature environment (25 C.), by a strain gauge method which is generally used. A vibrating material type magnetometer is used in a magnetic field generation apparatus. The strength of the magnetic field is 5000 Oe. As a sample for the measurement, a sample obtained by cutting out the single crystal alloy (the diameter of 10 mm the length of the straight body of 80 mm) described above into the shape of the diameter of 10 mma thickness of 1 mm is used. At this time, the <100> orientation which is an easy axis of magnetization of the crystal is cut out to be a thickness direction of the sample. That is, an upper surface direction and a bottom surface directions of the sample of which the diameter is 10 mm, and the thickness direction of 1 mm are made 0, with respect to the <100> orientation of the FeGaC alloy. The strain gauge is attached to the upper surface of the sample of which the diameter is 10 mm. At this time, the strain gauge is attached to be parallel to the <100> orientation of the FeGaC alloy. In other words, the properties of the magnetostriction quantity of the sample are measured to be parallel to the maximum strain direction (to form the inclination angle of 0), with respect to the pulling-out direction of magnetostrictive energy. The strain (.sub.//) of the sample when the magnetic field is applied parallel to the gauge axis of the strain gauge, and the strain (.sub.1) of the sample when the magnetic field is applied perpendicularly to the gauge axis of the strain gauge are recorded with a data logger. Magnetostriction quantity (ppm) is calculated as (ppm)=.sub.//.sub.1, and is evaluated, from the recorded numerical values.

[0045] Table 1 illustrates measurement results of the mechanical strength (tensile strength and elongation) and the magnetostriction quantity, in conjunction with the alloy composition of each sample of the FeGaC alloy in Example 1-1 to Example 1-3, and Comparative Example 1-1 to Comparative Example 1-3.

TABLE-US-00001 TABLE 1 Magneto- Tensile Elonga- striction Fe Ga C Strength tion Quantity [at. %] [at. %] [at. %] [MPa] [%] [ppm] Example 1-1 80.8 18.5 0.7 473 1.2 487 Example 1-2 80.5 18.5 1 481 1.1 483 Example 1-3 80.2 18.5 1.3 477 1.1 476 Comparative 80.8 19.2 0 350 0.9 250 Example 1-1 Comparative 80.5 19.5 0 347 0.95 220 Example 1-2 Comparative 80.2 19.8 0 337 0.9 210 Example 1-3

[0046] As illustrated in Table 1, in Example 1-1 to Example 1-3 in which C is added to the FeGa alloy, the magnetostriction quantity is 400 ppm or greater, while the excellent mechanical strength is maintained such that the tensile strength is 400 MPa or greater, and the elongation is 1% or greater. The result thereof is improved than those of Comparative Example 1-1 to Comparative Example 1-3 to which C is not added. This is considered because the magnetostriction quantity is improved by inducing the tetragonal strain into the Fe lattice due to the addition of C. Accordingly, it is determined that the addition of C is effective in order to improve the magnetostriction quantity while maintaining the mechanical strength.

Example 2

[0047] In Example 2, various samples in which the content rate (at. %) of C is changed in the FeGaC alloy are prepared, the magnetostriction quantity is measured, and the range of the content rate (at. %) of C in which the addition of C becomes effective is clarified.

Manufacturing of Sample for Measurement of FeGaC Alloy

[0048] As a sample for the measurement, as illustrated in Table 2 later, the plurality of samples (Example 2-1 to Example 2-13 and Comparative Example 2-1 to Comparative Example 2-7) of the FeGaC alloys which are configured by the content rate (at. %) of Ga, the content rate (at. %) of C, and the balance Fe (the numerical value thereof is not illustrated in Table 2) are prepared. The method for manufacturing the sample for the measurement of the FeGaC single crystal alloy, and the method (wire electric discharge machining) for cutting out the sample for the measurement are the same as those of Example 1 described above.

Measurement and Determination of Magnetostriction Quantity (Ppm)

[0049] The shape of the sample for the measurement of the magnetostriction quantity (ppm) of each sample, and a measurement method thereof are the same as those of Example 1 described above. In a case where the magnetostrictive material is used for the vibration power generation device, if the magnetostriction quantity is less than 400 ppm, power generation density is less than 0.3 mW/cm.sup.3. Therefore, the effectiveness of the magnetostriction quantity (ppm) is determined to be Good in a case of 400 ppm or greater, and is determined to be Poor in a case of less than 400 ppm. In a case where the magnetostrictive material is used for a torque sensor, if the magnetostriction quantity is 480 ppm or greater, output sensitivity of 1 V/Nm or greater is obtained, and it is possible to use the torque sensor of the magnetostriction material in an electric assist bicycle or the like. Therefore, the sample of which the magnetostriction quantity is 480 ppm or greater is determined to be Excellent.

[0050] Table 2 illustrates the measurement result and a determination result of the magnetostriction quantity, in conjunction with the alloy composition of each sample of the FeGaC alloy in Example 2-1 to Example 2-13, and Comparative Example 2-1 to Comparative Example 2-7.

TABLE-US-00002 TABLE 2 Magneto- striction Ga C Quantity [at. %] [at. %] [ppm] Determination Example 2-1 16.5 0.5 458 Good Example 2-2 17.5 0.5 449 Good Example 2-3 18.5 0.5 492 Excellent Example 2-4 19 0.5 472 Good Example 2-5 19.5 0.5 473 Good Example 2-6 17.5 0.75 451 Good Example 2-7 18.5 0.75 485 Excellent Example 2-8 19 0.75 490 Excellent Example 2-9 17.5 1 440 Good Example 2-10 18 1 482 Excellent Example 2-11 19 1 455 Good Example 2-12 18.5 1.25 481 Excellent Example 2-13 18.5 1.5 455 Good Comparative 17.5 0.4 355 Poor Example 2-1 Comparative 18.5 0.4 371 Poor Example 2-2 Comparative 16.4 0.5 366 Poor Example 2-3 Comparative 19.6 0.5 342 Poor Example 2-4 Comparative 17.5 1.1 369 Poor Example 2-5 Comparative 19 1.1 331 Poor Example 2-6 Comparative 18.5 1.6 302 Poor Example 2-7

[0051] As illustrated in Table 2, the magnetostriction quantities of Example 2-1 to Example 2-13 are 400 ppm or greater, and all the determinations thereof are Excellent or Good. This is considered because it is possible to induce the tetragonal strain into the Fe lattice, by adding C to the FeGa alloy.

[0052] In a case where the content rate of Cis 0.4 at. % in Comparative Example 2-1 and Comparative Example 2-2, the magnetostriction quantity is less than 400 ppm, and the determination becomes Poor. This is considered because it is not possible to express the effect of the addition of C by inducing the tetragonal strain into the Fe lattice, since the content rate of C is small.

[0053] In a case where the content rate of Ga is 16.4 at. %, and the content rate of C is 0.5 at. % in Comparative Example 2-3, the magnetostriction quantity is less than 400 ppm, and the determination becomes Poor. This is considered that the effect of the addition of C is not obtained since the content rate of Ga is small with respect to the content rate of Fe, an Fe phase becomes a main body, and the magnetostriction quantity is lowered.

[0054] In a case where the content rate of Ga is 19.6 at. %, and the content rate of C is 0.5 at. % in Comparative Example 2-4, or in a case where the content rate of Ga is 19 at. %, and the content rate of C is 1.1 at. % in Comparative Example 2-6, the magnetostriction quantity is less than 400 ppm, and the determination becomes Poor. This is considered that the magnetostriction quantity is lowered since the total content rate of Ga and C is more than 20 at. %, thereby, a body-centered cubic structure which is the crystal structure of the FeGa alloy collapses, and a compound such as Fe.sub.3Ga of an ordered lattice of a face-centered cubic structure precipitates.

[0055] In a case where the content rate of Ga is 17.5 at. %, and the content rate of C is 1.1 at. % in Comparative Example 2-5, the magnetostriction quantity is less than 400 ppm, and the determination becomes Poor. This is considered that the magnetostriction quantity is lower since C is not capable of intruding into the Fe lattice, when the content rate of C is large with respect to the content rate of Ga.

[0056] In a case where the content rate of C is 1.6 at. % in Comparative Example 2-7, the magnetostriction quantity is less than 400 ppm, and the determination becomes Poor. This is considered that a FeC compound precipitates, and the magnetostriction quantity is lowered in order to reach a solid solubility limit of the FeGa alloy.

[0057] FIG. 3 is a diagram representing a relationship between the content rate of Ga and the content rate of C in which the magnetostriction quantity becomes 400 ppm or greater in Example 2 of the present disclosure. A vertical axis indicates the content rate (at. %) of C, and a horizontal axis indicates the content rate (at. %) of Ga. A black circle represents a spot at which the magnetostriction quantity is 400 ppm or greater in Example 2-1 to Example 2-13. A white circle represents a spot at which the magnetostriction quantity is less than 400 ppm in Comparative Example 2-1 to Comparative Example 2-7. As illustrated in FIG. 3, a boundary at which the magnetostriction quantity is 400 ppm or greater is present, in the relationship between the content rate of C and the content rate of Ga. If approximate lines along the boundary are sought, it is found out that y=0.5x7.75, y=x+20, and y=0.5, respectively. In other words, if the content rate of C and the content rate of Ga are present on the inside of an area including a borderline that is surrounded by the approximate lines illustrated by oblique lines in FIG. 3, the magnetostriction quantity becomes 400 ppm or greater. That is, if the magnetostrictive material is the FeGaC alloy that is represented by Expression (1): Fe.sub.(100-x-y)Ga.sub.xC.sub.y . . . (1) (in Expression (1), x and y are respectively the content rate (at. %) of Ga, and the content rate (at. %) of C, and satisfy that y0.5x7.75, yx+20, and y0.5), the magnetostriction quantity becomes 400 ppm or greater.

[0058] FIG. 4 is a diagram representing the relationship between the content rate of Ga and the content rate of C in which the magnetostriction quantity becomes 480 ppm or greater in Example 2 of the present disclosure. Specifically, FIG. 4 is a diagram in which a spot at which the magnetostriction quantity is 480 ppm or greater is particularly represented by a double circle, among the black circles at which the magnetostriction quantities are 400 ppm or greater. As illustrated in FIG. 4, the boundary at which the magnetostriction quantity is 480 ppm or greater is present, in the relationship between the content rate of C and the content rate of Ga. If the approximate lines along the boundary are sought, it is found out that y=0.5x8, y=0.5x8.75, y=x+19, and y=x+19.75, respectively. In other words, if the content rate of C and the content rate of Ga are present on the inside of the area including a dashed borderline that is surrounded by the approximate lines in the oblique lines of FIG. 4, the magnetostriction quantity becomes 480 ppm or greater. That is, if the magnetostrictive material is the FeGaC alloy that is represented by Expression (1): Fe.sub.(100-x-y)Ga.sub.xC.sub.y . . . (1) (in Expression (1), x and y are respectively the content rate (at. %) of Ga, and the content rate (at. %) of C, and satisfy that y0.5x8, y0.5x8.75, yx+19, and yx+19.75), the magnetostriction quantity becomes 480 ppm or greater.

Example 3

[0059] In Example 3, various samples in which the inclination angle with respect to the <100> orientation is changed, at the time of cutting out the sample for the measurement of the FeGaC single crystal alloy are prepared, the magnetostriction quantity is measured, and an influence which the inclination angle with respect to the <100> orientation of the alloy has on the magnetostriction quantity is searched.

Manufacturing of Sample for Measurement of FeGaC Alloy

[0060] As a sample for the measurement, as illustrated in Table 3 later, samples (Example 3-1 to Example 3-6, and Comparative Example 3-1 to Comparative Example 3-2) of the FeGaC alloys which are configured by the content rate of Ga which is 17.5 at. %, the content rate of C which is 1 at. %, and the balance Fe are prepared. The method for manufacturing the sample for the measurement of the FeGaC single crystal alloy, and the method (wire electric discharge machining) for cutting out the sample for the measurement are the same as those of Example 1 described above.

Measurement and Determination of Magnetostriction Quantity (Ppm)

[0061] The shape of the sample for the measurement of the magnetostriction quantity (ppm) of each sample is a shape of the diameter of 10 mm the thickness of 1 mm, and is the same as that of Example 1. However, per sample, the upper surface and the bottom surface (surface that is parallel to a surface which is orthogonal to the thickness direction of the sample) of the sample of which the diameter is 10 mm are cut out to form the different inclination angles as illustrated in Table 3, with respect to the <100> orientation of the single crystal of the FeGaC alloy. The measurement method of the magnetostriction quantity (ppm) of each sample is the same as the method of Example 1 described above, but even in a case of the sample according to Example 3 which is cut out with the inclination angle, the strain gauge is attached to the upper surface of the sample of which the diameter is 10 mm, in the same manner. Accordingly, the properties of the magnetostriction quantity of the sample are measured such that the maximum strain direction of the magnetostrictive material forms the inclination angle which is the same as that of Table 3, with respect to the pulling-out direction of the magnetostrictive energy. The effectiveness of the magnetostriction quantity (ppm) is determined to be Good in a case of 400 ppm or greater, and is determined to be Poor in a case of less than 400 ppm.

[0062] Table 3 illustrates the measurement result and the determination result of the magnetostriction quantity, in conjunction with the alloy composition and the inclination angle of each sample of the FeGaC alloy in Example 3-1 to Example 3-6, and Comparative Example 3-1 to Comparative Example 3-2.

TABLE-US-00003 TABLE 3 Magneto- Inclination striction Ga C Angle Quantity [at. %] [at. %] [] [ppm] Determination Example 3-1 17.5 1 0 440 Good Example 3-2 17.5 1 2 431 Good Example 3-3 17.5 1 4 426 Good Example 3-4 17.5 1 6 419 Good Example 3-5 17.5 1 8 411 Good Example 3-6 17.5 1 10 404 Good Comparative 17.5 1 11 396 Poor Example 3-1 Comparative 17.5 1 12 390 Poor Example 3-2

[0063] As illustrated in Table 3, in a case where the content rate of Ga is 17.5 at. %, and the content rate of C is 1 at. %, in Example 3-1 to Example 3-6 of which the inclination angle is 0 or greater and 10 or less, the magnetostriction quantity is 400 ppm or greater, and the favorable result is obtained, in comparison with Comparative Example 3-1 to Comparative Example 3-2 having the same alloy composition. This is considered because the easy axis of magnetization of the FeGaC alloy is the <100> orientation. Accordingly, practically, for example, it is found out to be more useful that the direction in which the dimensional change for extracting the energy of the magnetostriction type device is desired, and the maximum strain direction of the magnetostrictive material are configured to form the inclination angle of 0 or greater and 10 or less, in order to obtain the magnetostrictive properties more efficiently.

[0064] Since the magnetostrictive material of the present disclosure exhibits the large magnetostriction quantity, and is excellent in mechanical strength, it is possible to apply the magnetostrictive material of the present disclosure to a magnetostriction type vibration power generation device, a magnetostriction type sensor, or a magnetostriction type actuator which may be a clue to the realization of the IoT.