IMPROVED ACRYLIC LIQUID APPLIED SOUND DAMPERS

Abstract

Novel water-based acrylic coating compositions which provide superior noise suppression are disclosed. Water-based compositions comprised of acrylic polymer, resins, and/or plasticizer, after curing, provide improved vibration damping to solid substrates. Such substrates include the metal surfaces of passenger and commercial vehicles. Resins and plasticizers which provide superior and unexpectedly high vibration damping are disclosed.

Claims

1. An acrylic coating composition comprising: (a) an acrylic polymer component; (b) a resin; and (c) a plasticizer, wherein the resin is present in the composition from about 0 to about 40 phr relative to the sum total of the acrylic polymer component, and wherein the plasticizer is present in the composition from about 0 to about 15 phr relative to the sum total of the acrylic polymer component, wherein the total amount of resin and plasticizer is at least 2 phr relative to the sum total of the acrylic polymer component.

2. The composition of claim 1, wherein the plasticizer is present in the composition at 0 phr relative to the sum total of the acrylic polymer component; and the resin is present in the composition from about 2 to about 40 phr.

3. The composition of claim 1, wherein the plasticizer is present in the composition from about 2 to 10 phr relative to the sum total of the acrylic polymer component; and the resin is present in the composition at 0 phr.

4. The composition of claim 1, wherein the plasticizer is present in the composition from about 1 to about 5 phr relative to the sum total of the acrylic polymer component, and the resin is present in the composition at less than about 20 phr relative to the sum total of the acrylic polymer component.

5. The composition of claim 1, wherein the plasticizer is chosen from orthophthalates; terephthalates; isophthalates; trimellitates; adipates; cyclohexanedicarboxylates; benzoates; phosphates; diesters of ethylene glycol, propylene glycol, their oligomers, or mixtures thereof; citrates; succinates; alkyl sulfonates; fatty acid esters and epoxidized fatty acid esters, optionally substituted; triglycerides and epoxidized triglycerides, optionally substituted; dianhydrohexitol diesters; pentaerythritol-based tetraesters; furan-based esters; glycerol esters; other esters; ketals; and/or polymeric plasticizers.

6. The composition of claim 5, wherein the plasticizer is chosen from terephthalates, benzoates, or glycerol esters.

7. The composition of claim 6, wherein the plasticizer is chosen from diethylene glycol dibenzoate, dipropylene glycol dibenzoate, triethylene glycol dibenzoate, bis-n-butyl terephthalate, or 1,2,3-triacetoxypropane.

8. The composition of claim 1, wherein the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins.

9. The composition of claim 8, wherein the resin comprises rosin glycerol esters, hydrogenated rosin pentaerythritol esters, or aromatic-modified C5 hydrocarbon resin.

10. The composition of claim 1, wherein the acrylic polymer component comprises an acrylic polymer chosen from a methacrylic ester-acrylic ester copolymer or an acrylic ester-styrene copolymer.

11. The composition of claim 1, further comprising other components chosen from fillers, pigments, stabilizers, foaming agents, hollow materials, surfactants, coalescing aids, defoamers, biocides, rheology control additives, or adhesion promoters.

12. The composition of claim 1, wherein the fillers comprise calcium carbonate, magnesium carbonate, silica, clay, mica, graphite, or zinc oxide.

13. The composition of claim 11, wherein the adhesive promoters comprise polyamidoamines, blocked isocyanates and isocyanurates, or silanes.

14. The composition of claim 1, wherein the dried composition has a maximum Tan Delta (Tan .sub.max) occurring at a temperature range of between 20 C. to 70 C. and wherein the Tan .sub.max ranges from 1.0 to 5.0, when measured on a circular sample of 8 mm diameter and nominally 1-2 mm thickness using a Dynamic Mechanical Analyzer with 8 mm stainless steel parallel plates at an automatic strain adjustment from 0.1% to 15% and at a frequency of 1 Hz and a temperature ramp rate of 5 C./min.

15. A method of improving vibration damping of a substrate comprising affixing the composition of claim 1 onto the substrate.

16. The method of claim 15, wherein the affixing comprises (a) applying the composition onto the substrate; (b) drying the composition to produce an acrylic-coated substrate; and (c) cooling the acrylic-coated substrate to ambient temperature.

17. The method of claim 16, wherein the applying of the composition onto the substrate comprises coating the substrate with the composition.

18. The method of claim 15, wherein the affixing comprises (a) fusing the composition into a sheet; and (b) adhering the sheet to the substrate.

19. The method of claim 16, wherein the drying occurs at a temperature range from 20 C. to 175 C. for a time period ranging from 1 minute to 24 hours.

20. The method of claim 15, wherein the substrate is part of a wheeled vehicle.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0014] As used herein the term and/or, when used in a list of two or more items, means that any one of the listed items can be employed by itself, or any combination of two or more of the listed items can be employed. For example, if a composition is described as containing components A, B, and/or C, the composition can contain A alone; B alone; C alone; A and B in combination; A and C in combination; B and C in combination; or A, B, and C in combination.

[0015] As used herein the term chosen from when used with and or or have the following meanings: A variable chosen from A, B and C means that the variable can be A alone, B alone, or C alone. A variable A, B, or C means that the variable can be A alone, B alone, C alone, A and B in combination, A and C in combination, or A, B, and C in combination.

[0016] The term affixing, as used herein, refers to providing continuous and intimate contact between the composition and the substrate such that the dried composition (acrylic coating) remains on the substrate. For example, an acrylic coating can be affixed to a car inner- or under-body via spray coating the composition onto a car inner- or under-body and subjecting the coated car inner- or under-body to conditions to dry the composition. The term adhering as used herein, refers to using an adhesive to affix an acrylic coating in the form of a sheet to a substrate.

[0017] The term composition, as used herein, refers to either a liquid dispersion of polymeric particles, optionally with other ingredients, or the solid acrylic coating. The liquid dispersion can be an aqueous dispersion. The term dried composition and, as used herein, refers to the solid acrylic coating that is formed upon drying the composition and subsequently cooling to a desired temperature. The term drying, as used herein, refers to heating of the composition to a temperature sufficient to yield a solid structure with mechanical integrity.

[0018] The term resin, as used herein, means a natural or semi-synthetic substance derived from plant secretions, or a synthetic or semi-synthetic substance that has similar properties to natural resins. The term resin when used in conjunction with parts per hundred parts has a different meaning. The term resin in this case is the acrylic polymer component, expressed on a 100% solids basis. The amount of plasticizer, resin, or any other component in the acrylic coating composition disclosed herein, can be measured as parts per hundred parts resin (phr), on a weight per weight basis. For example, if 30 grams of plasticizer is added to 100 grams of the acrylic polymer component, then the plasticizer content of the resulting acrylic coating composition would be 30 phr.

[0019] The term rosin, as used herein, is a mixture of eight closely related rosin acids characterized by three fused six-carbon rings, double bonds that vary in number and location, and a single carboxylic acid group. Three sources of rosin are used for resin manufacture, gum rosin, wood rosin and tall oil rosin, all generated from the pine tree. The term rosin ester resin, as used herein, refers to the manufactured product made by reacting rosin with an alcohol.

[0020] The term softening point, as used herein, refers to the temperature at which a material softens as determined by a ring and ball method such as ASTM E28 or ISO 4625.

[0021] The term substrate, as used herein, refers to the material that provides the surface onto which the composition is affixed. In one embodiment, the material providing the substrate is the material that transfers the sound or vibration energy. In one embodiment, the substrate is a metal surface.

Composition

[0022] The present application discloses an acrylic coating composition comprising: (a) an acrylic polymer component; (b) a resin; and (c) a plasticizer, wherein the resin is present in the composition from about 0 to about 40 phr relative to the sum total of the acrylic polymer component, and wherein the plasticizer is present in the composition from about 0 to about 15 phr relative to the sum total of the acrylic polymer component, wherein the total amount of resin and plasticizer is at least 2 phr relative to the sum total of the acrylic polymer component.

[0023] In one embodiment, the plasticizer is present in the composition at 0 phr relative to the sum total of the acrylic polymer component; and the resin is present in the composition from about 2 to about 40 phr.

[0024] In one class of this embodiment, the dried composition has a maximum Tan Delta (Tan .sub.max) occurring at a temperature range of between 20 C. to 70 C. and wherein the Tan .sub.max ranges from 1.0 to 5.0, when measured on a circular sample of 8 mm diameter and nominally 1-2 mm thickness using a Dynamic Mechanical Analyzer with 8 mm stainless steel parallel plates at an automatic strain adjustment from 0.1% to 15% and at a frequency of 1 Hz and a temperature ramp rate of 5 C./min.

[0025] In one class of this embodiment, the resin is present in the composition from about 2 to about 10 phr. In one subclass of this class, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins; and the plasticizer is chosen from terephthalates, benzoates, or glycerol esters.

[0026] In one class of this embodiment, the resin is present in the composition from about 10 to about 20 phr. In one subclass of this class, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins; and the plasticizer is chosen from terephthalates, benzoates, or glycerol esters.

[0027] In one class of this embodiment, the resin is present in the composition from about 20 to about 40 phr. In one subclass of this class, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins; and the plasticizer is chosen from terephthalates, benzoates, or glycerol esters.

[0028] In one embodiment, the plasticizer is present in the composition from about 2 to 10 phr relative to the sum total of the acrylic polymer component; and the resin is present in the composition at 0 phr.

[0029] In one class of this embodiment, the dried composition has a maximum Tan Delta (Tan .sub.max) occurring at a temperature range of between 20 C. to 70 C. and wherein the Tan .sub.max ranges from 1.0 to 5.0, when measured on a circular sample of 8 mm diameter and nominally 1-2 mm thickness using a Dynamic Mechanical Analyzer with 8 mm stainless steel parallel plates at an automatic strain adjustment from 0.1% to 15% and at a frequency of 1 Hz and a temperature ramp rate of 5 C./min.

[0030] In one class of this embodiment, the plasticizer is chosen from terephthalates, benzoates, or glycerol esters. In one class of this embodiment, the plasticizer is chosen from diethylene glycol dibenzoate, dipropylene glycol dibenzoate, triethylene glycol dibenzoate, bis-n-butyl terephthalate, or 1,2,3-triacetoxypropane.

[0031] In one class of this embodiment, the plasticizer is present in the composition from about 2 to about 5 phr. In one subclass of this class, the plasticizer is chosen from terephthalates, benzoates, or glycerol esters. In one subclass of this class, the plasticizer is chosen from diethylene glycol dibenzoate, dipropylene glycol dibenzoate, triethylene glycol dibenzoate, bis-n-butyl terephthalate, or 1,2,3-triacetoxypropane.

[0032] In one class of this embodiment, the plasticizer is present in the composition from about 5 to about 10 phr. In one subclass of this class, the plasticizer is chosen from terephthalates, benzoates, or glycerol esters. In one subclass of this class, the plasticizer is chosen from diethylene glycol dibenzoate, dipropylene glycol dibenzoate, triethylene glycol dibenzoate, bis-n-butyl terephthalate, or 1,2,3-triacetoxypropane.

[0033] In one embodiment, the plasticizer is present in the composition from about 1 to about 5 phr relative to the sum total of the acrylic polymer component.

[0034] In one class of this embodiment, the dried composition has a maximum Tan Delta (Tan .sub.max) occurring at a temperature range of between 20 C. to 70 C. and wherein the Tan .sub.max ranges from 1.0 to 5.0, when measured on a circular sample of 8 mm diameter and nominally 1-2 mm thickness using a Dynamic Mechanical Analyzer with 8 mm stainless steel parallel plates at an automatic strain adjustment from 0.1% to 15% and at a frequency of 1 Hz and a temperature ramp rate of 5 C./min.

[0035] In one class of this embodiment, the plasticizer is chosen from terephthalates, benzoates, or glycerol esters. In one class of this embodiment, the plasticizer is chosen from diethylene glycol dibenzoate, dipropylene glycol dibenzoate, triethylene glycol dibenzoate, bis-n-butyl terephthalate, or 1,2,3-triacetoxypropane.

[0036] In one class of this embodiment, the resin is present in the composition at less than about 20 phr. In one subclass of this class, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins; and the plasticizer is chosen from terephthalates, benzoates, or glycerol esters.

[0037] In one class of this embodiment, the resin is present in the composition at less than about 15 phr. In one subclass of this class, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins; and the plasticizer is chosen from terephthalates, benzoates, or glycerol esters.

[0038] In one class of this embodiment, the resin is present in the composition at less than about 10 phr. In one subclass of this class, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins; and the plasticizer is chosen from terephthalates, benzoates, or glycerol esters.

[0039] In one class of this embodiment, the resin is present in the composition from about 1 to about 20 phr. In one subclass of this class, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins; and the plasticizer is chosen from terephthalates, benzoates, or glycerol esters.

[0040] In one class of this embodiment, the resin is present in the composition from about 1 to about 15 phr. In one subclass of this class, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins; and the plasticizer is chosen from terephthalates, benzoates, or glycerol esters.

[0041] In one class of this embodiment, the resin is present in the composition from about 1 to about 10 phr. In one subclass of this class, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins; and the plasticizer is chosen from terephthalates, benzoates, or glycerol esters.

[0042] In one embodiment, the plasticizer is present in the composition from about 5 to about 10 phr relative to the sum total of the acrylic polymer component.

[0043] In one class of this embodiment, the dried composition has a maximum Tan Delta (Tan .sub.max) occurring at a temperature range of between 20 C. to 70 C. and wherein the Tan .sub.max ranges from 1.0 to 5.0, when measured on a circular sample of 8 mm diameter and nominally 1-2 mm thickness using a Dynamic Mechanical Analyzer with 8 mm stainless steel parallel plates at an automatic strain adjustment from 0.1% to 15% and at a frequency of 1 Hz and a temperature ramp rate of 5 C./min.

[0044] In one class of this embodiment, the plasticizer is chosen from terephthalates, benzoates, or glycerol esters. In one class of this embodiment, the plasticizer is chosen from diethylene glycol dibenzoate, dipropylene glycol dibenzoate, triethylene glycol dibenzoate, bis-n-butyl terephthalate, or 1,2,3-triacetoxypropane.

[0045] In one class of this embodiment, the resin is present in the composition at less than about 20 phr. In one subclass of this class, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins; and the plasticizer is chosen from terephthalates, benzoates, or glycerol esters.

[0046] In one class of this embodiment, the resin is present in the composition at less than about 15 phr. In one subclass of this class, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins; and the plasticizer is chosen from terephthalates, benzoates, or glycerol esters.

[0047] In one class of this embodiment, the resin is present in the composition at less than about 10 phr. In one subclass of this class, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins; and the plasticizer is chosen from terephthalates, benzoates, or glycerol esters.

[0048] In one class of this embodiment, the resin is present in the composition from about 1 to about 20 phr. In one subclass of this class, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins; and the plasticizer is chosen from terephthalates, benzoates, or glycerol esters.

[0049] In one class of this embodiment, the resin is present in the composition from about 1 to about 10 phr. In one subclass of this class, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins; and the plasticizer is chosen from terephthalates, benzoates, or glycerol esters.

[0050] In one embodiment, the plasticizer is present in the composition from about 10 to about 15 phr relative to the sum total of the acrylic polymer component.

[0051] In one class of this embodiment, the dried composition has a maximum Tan Delta (Tan .sub.max) occurring at a temperature range of between 20 C. to 70 C. and wherein the Tan .sub.max ranges from 1.0 to 5.0, when measured on a circular sample of 8 mm diameter and nominally 1-2 mm thickness using a Dynamic Mechanical Analyzer with 8 mm stainless steel parallel plates at an automatic strain adjustment from 0.1% to 15% and at a frequency of 1 Hz and a temperature ramp rate of 5 C./min.

[0052] In one class of this embodiment, the plasticizer is chosen from terephthalates, benzoates, or glycerol esters. In one class of this embodiment, the plasticizer is chosen from diethylene glycol dibenzoate, dipropylene glycol dibenzoate, triethylene glycol dibenzoate, bis-n-butyl terephthalate, or 1,2,3-triacetoxypropane.

[0053] In one class of this embodiment, the resin is present in the composition at less than about 20 phr. In one subclass of this class, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins; and the plasticizer is chosen from terephthalates, benzoates, or glycerol esters.

[0054] In one class of this embodiment, the resin is present in the composition at less than about 15 phr. In one subclass of this class, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins; and the plasticizer is chosen from terephthalates, benzoates, or glycerol esters.

[0055] In one class of this embodiment, the resin is present in the composition at less than about 10 phr. In one subclass of this class, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins; and the plasticizer is chosen from terephthalates, benzoates, or glycerol esters.

[0056] In one class of this embodiment, the resin is present in the composition from about 1 to about 20 phr. In one subclass of this class, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins; and the plasticizer is chosen from terephthalates, benzoates, or glycerol esters.

[0057] In one class of this embodiment, the resin is present in the composition from about 1 to about 15 phr. In one subclass of this class, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins; and the plasticizer is chosen from terephthalates, benzoates, or glycerol esters.

[0058] In one class of this embodiment, the resin is present in the composition from about 1 to about 10 phr. In one subclass of this class, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins; and the plasticizer is chosen from terephthalates, benzoates, or glycerol esters.

[0059] In one embodiment, the resin is present in the composition from about 1 to 20 phr relative to the sum total of the acrylic polymer component.

[0060] In one class of this embodiment, the dried composition has a maximum Tan Delta (Tan .sub.max) occurring at a temperature range of between 20 C. to 70 C. and wherein the Tan .sub.max ranges from 1.0 to 5.0, when measured on a circular sample of 8 mm diameter and nominally 1-2 mm thickness using a Dynamic Mechanical Analyzer with 8 mm stainless steel parallel plates at an automatic strain adjustment from 0.1% to 15% and at a frequency of 1 Hz and a temperature ramp rate of 5 C./min.

[0061] In one class of this embodiment, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, an aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins. In one class of this embodiment, the resin comprises rosin glycerol esters, hydrogenated rosin pentaerythritol esters, or aromatic-modified C5 hydrocarbon resins.

[0062] In one embodiment, the resin is present in the composition from about 1 to 15 phr relative to the sum total of the acrylic polymer component.

[0063] In one class of this embodiment, the dried composition has a maximum Tan Delta (Tan .sub.max) occurring at a temperature range of between 20 C. to 70 C. and wherein the Tan .sub.max ranges from 1.0 to 5.0, when measured on a circular sample of 8 mm diameter and nominally 1-2 mm thickness using a Dynamic Mechanical Analyzer with 8 mm stainless steel parallel plates at an automatic strain adjustment from 0.1% to 15% and at a frequency of 1 Hz and a temperature ramp rate of 5 C./min.

[0064] In one class of this embodiment, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, an aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins. In one class of this embodiment, the resin comprises rosin glycerol esters, hydrogenated rosin pentaerythritol esters, or aromatic-modified C5 hydrocarbon resins.

[0065] In one embodiment, the resin is present in the composition from about 1 to 10 phr relative to the sum total of the acrylic polymer component.

[0066] In one class of this embodiment, the dried composition has a maximum Tan Delta (Tan .sub.max) occurring at a temperature range of between 20 C. to 70 C. and wherein the Tan .sub.max ranges from 1.0 to 5.0, when measured on a circular sample of 8 mm diameter and nominally 1-2 mm thickness using a Dynamic Mechanical Analyzer with 8 mm stainless steel parallel plates at an automatic strain adjustment from 0.1% to 15% and at a frequency of 1 Hz and a temperature ramp rate of 5 C./min.

[0067] In one class of this embodiment, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, an aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins. In one class of this embodiment, the resin comprises rosin glycerol esters, hydrogenated rosin pentaerythritol esters, or aromatic-modified C5 hydrocarbon resins.

[0068] In one embodiment, the resin is present in the composition from about 20 to 40 phr relative to the sum total of the acrylic polymer component.

[0069] In one class of this embodiment, the dried composition has a maximum Tan Delta (Tan .sub.max) occurring at a temperature range of between 20 C. to 70 C. and wherein the Tan .sub.max ranges from 1.0 to 5.0, when measured on a circular sample of 8 mm diameter and nominally 1-2 mm thickness using a Dynamic Mechanical Analyzer with 8 mm stainless steel parallel plates at an automatic strain adjustment from 0.1% to 15% and at a frequency of 1 Hz and a temperature ramp rate of 5 C./min.

[0070] In one class of this embodiment, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins. In one class of this embodiment, the resin comprises rosin glycerol esters, hydrogenated rosin pentaerythritol esters, or aromatic-modified C5 hydrocarbon resins.

[0071] In one embodiment, the resin has a softening point in the range of from about 60 C. to about 100 C. In one embodiment, the resin has a softening point in the range of from about ranges from 65 C. to 95 C.

[0072] In one embodiment, the resin comprises unhydrogenated or hydrogenated rosin esters, unhydrogenated or hydrogenated rosin acids, aromatic modified hydrocarbon resins, or aliphatic hydrocarbon resins.

[0073] In one class of this embodiment, the resin has a softening point in the range of from about 60 C. to about 100 C. In one class of this embodiment, the resin has a softening point in the range of from about ranges from 65 C. to 95 C.

[0074] In one class of this embodiment, the resin comprises unhydrogenated rosin esters. In one class of this embodiment, the resin comprises hydrogenated rosin esters. In one class of this embodiment, the resin comprises unhydrogenated rosin acids. In one class of this embodiment, the resin comprises hydrogenated rosin acids. In one class of this embodiment, the resin comprises aromatic modified hydrocarbon resins. In one class of this embodiment, the resin comprises aliphatic hydrocarbon resins.

[0075] In one class of this embodiment, the resin comprises rosin glycerol esters, hydrogenated rosin pentaerythritol esters, or aromatic-modified C5 hydrocarbon resins. In one subclass of this class, the resin has a softening point in the range of from about 60 C. to about 100 C. In one subclass of this class, the resin has a softening point in the range of from about ranges from 65 C. to 95 C.

[0076] In one class of this embodiment, the resin comprises rosin glycerol esters. In one class of this embodiment, the resin comprises hydrogenated rosin pentaerythritol esters. In one class of this embodiment, the resin comprises aromatic-modified C5 hydrocarbon resins.

[0077] In one class of this embodiment, the resin is a water-based dispersion comprising rosin esters or aromatic-modified hydrocarbon resins. In one subclass of this class, the resin has a softening point in the range of from about 60 C. to about 100 C. In one subclass of this class, the resin has a softening point in the range of from about ranges from 65 C. to 95 C.

[0078] The plasticizer component is not particularly limited. In one embodiment, the plasticizer is chosen from orthophthalates; terephthalates; isophthalates; trimellitates; adipates; cyclohexanedicarboxylates; benzoates; phosphates; diesters of ethylene glycol, propylene glycol, their oligomers, or mixtures thereof; citrates; succinates; alkyl sulfonates; fatty acid esters and epoxidized fatty acid esters, optionally substituted; triglycerides and epoxidized triglycerides, optionally substituted; dianhydrohexitol diesters; pentaerythritol-based tetraesters; furan-based esters; glycerol esters; or polymeric plasticizers. In one class of embodiment, the plasticizer is chosen from terephthalates, benzoates, or glycerol esters. In one class of this embodiment, the plasticizer is chosen from diethylene glycol dibenzoate, dipropylene glycol dibenzoate, triethylene glycerol dibenzoate, bis-n-butyl terephthalate, or 1,2,3-triacetoxypropane.

[0079] The acrylic polymer component is not particularly limited. In one embodiment, the acrylic polymer component is derived from an (C.sub.1-8)alkyl acrylate, (C.sub.1-8)alkyl methacrylates, or mixtures of the two. In one class of this embodiment, the acrylic polymer component is derived from an (C.sub.1-4)alkyl acrylates, an (C.sub.1-4)alkyl methacrylates, or mixtures of the two. In one class of this embodiment, the acrylic polymer component is derived from an (C.sub.1-8)alkyl acrylate. In one class of this embodiment, the acrylic polymer component is derived from an (C.sub.1-8)alkyl methacrylate. In one class of this embodiment, the acrylic polymer component is derived from a mixture of an (C.sub.1-8)alkyl acrylate and an (C.sub.1-8)alkyl methacrylate. In one class of this embodiment, the acrylic polymer component is derived from an (C.sub.1-4)alkyl acrylate. In one class of this embodiment, the acrylic polymer component is derived from an (C.sub.1-4)alkyl methacrylate. In one class of this embodiment, the acrylic polymer component is derived from a mixture of an (C.sub.1-4)alkyl acrylate and an (C.sub.1-4)alkyl methacrylate.

[0080] Other copolymerizable monomers can be included in the acrylic polymer. Such monomers include but are not limited to styrene. In one class of this embodiment, the acrylic polymer component comprises 3 a methacrylic ester-acrylic ester copolymer, or an acrylic ester-styrene copolymer. Other polymeric components optionally can be blended into the acrylic emulsion.

[0081] In one embodiment of the acrylic coating composition, the acrylic coating composition further comprises other components. In one class of this embodiment, other components are chosen from fillers, pigments, stabilizers, foaming agents, hollow materials, surfactants, coalescing aids, defoamers, biocides, rheology control additives, or adhesion promoters. In one subclass of this class, the other components are present in the range of 5 to 250 phr relative to the sum total of the acrylic polymer component. In one subclass of this class, the other components are present in the range of 5 to 50 phr relative to the sum total of the acrylic polymer component. In one subclass of this class, the other components are present in the range of 50 to 100 phr relative to the sum total of the acrylic polymer component. In one subclass of this class, the other components are present in the range of 100 to 150 phr relative to the sum total of the acrylic polymer component. In one subclass of this class, the other components are present in the range of 150 to 250 phr relative to the sum total of the acrylic polymer component.

[0082] In one embodiment, the acrylic coating compositions further comprises fillers. In one class of this embodiment, the filler is inorganic. In one class of this embodiment, the fillers can represent between 5 wt % and 70 wt % by weight. In one class of this embodiment, the fillers can represent between 10 wt % and 60 wt %. In one class of this embodiment, the fillers can represent between 5 to 250 phr relative to the sum total of the acrylic polymer component. In one class of this embodiment, the fillers can represent between 5 to 50 phr relative to the sum total of the acrylic polymer component. In one class of this embodiment, the fillers can represent between 50 to 100 phr relative to the sum total of the acrylic polymer component. In one embodiment, the fillers can represent between 100 to 150 phr relative to the sum total of the acrylic polymer component. In one class of this embodiment, the fillers can represent between 150 to 250 phr relative to the sum total of the acrylic polymer component. Suitable fillers include but are not limited to calcium carbonate, magnesium carbonate, silica, clay, mica, graphite, and/or zinc oxide. Pigments can be incorporated into the inventive compositions to achieve desired visual effects, as known to those skilled in the art.

[0083] In one embodiment, the acrylic composition can be formulated or produced in a manner which incorporates more free volume into the cured coating. In one such technique, mechanical frothing can be applied to produce a foamed composition. In one embodiment, a chemical foaming agent which results in a foamed structure after curing is incorporated. One non-limiting example of such a foaming agent is azodicarbonamide. Other examples of foaming agents include isocyanates, sodium carbonate, sodium bicarbonate, 5-hydroxytetrazole, p-phenylene-bis(5-tetrazole), 5-methyltetrazole, 5-phenyltetrazole, and 5-(benzyl)-tetrazole, 5-(p-toluyl)-tetrazole, and sodium borohydride. In one embodiment, a catalyst is used along with the chemical foaming agent. In other one embodiment, foam stabilizers are used. In embodiment, hollow materials are incorporated into the formulation. Such materials include glass beads, microbeads, and microspheres, which can be produced from either inorganic or polymeric organic substances. In one embodiment, the hollow materials are thermoplastic microspheres.

[0084] In one embodiment, additives to control rheology can be incorporated into the inventive water-based acrylic composition. Thickeners can be added to boost viscosity as desired. Materials and techniques for adjusting acrylic rheology are well known to those skilled in the art.

[0085] In one embodiment, adhesion promoters can be incorporated into the acrylic composition. Suitable adhesion promoters include but are not limited to polyamidoamines, blocked isocyanates and isocyanurates, and silanes.

[0086] In on embodiment, formulation aids can be incorporated, such as, surfactants, defoamers, biocides, coalescing aids, as known to those skilled in the art

[0087] In one embodiment, the dried composition has a maximum Tan Delta (Tan .sub.max) occurring between 20 C. and 70 C. and the Tan .sub.max ranges from 1.0 to 5.0, when measured on a circular sample of 8 mm diameter and nominally 1-2 mm thickness using a Dynamic Mechanical Analyzer with 8 mm stainless steel plates at an automatic strain adjustment from 0.1% to 15% and at a frequency of 1 Hz and a temperature ramp rate of 5 C./min.

[0088] In one embodiment, the dried composition has a maximum Tan Delta (Tan .sub.max) occurring between 10 C. and 40 C. and the Tan .sub.max ranges from 1.0 to 5.0, when measured on a circular sample of 8 mm diameter and nominally 1-2 mm thickness using a Dynamic Mechanical Analyzer with 8 mm stainless steel plates at an automatic strain adjustment from 0.1% to 15% and at a frequency of 1 Hz and a temperature ramp rate of 5 C./min.

Method of Improving Vibration

[0089] The present application discloses a method of improving vibration damping of a substrate comprising affixing an acrylic coating composition onto the substrate, wherein the acrylic coating composition comprises: (a) an acrylic polymer component; (b) a resin; and (c) a plasticizer, wherein the resin is present in the composition from about 0 to about 40 phr relative to the sum total of the acrylic polymer component, and wherein the plasticizer is present in the composition from about 0 to about 15 phr relative to the sum total of the acrylic polymer component, wherein the total amount of resin and plasticizer is at least 2 phr relative to the sum total of the acrylic polymer component. The acrylic coating composition can have any combination of the attributes described herein above.

[0090] The substrate is not particularly limited. In one embodiment, the substrate is a metal. In one embodiment, the substrate comprises steel. In one embodiment, the substrate comprises aluminum. In one embodiment, the substrate is part of a wheeled vehicle. In one embodiment, the substrate is on the under-body of a wheeled vehicle. In one embodiment, the substrate is on the inner-body of a wheeled vehicle. In one embodiment, the substrate is a wood or a ceramic.

[0091] In one embodiment, the method of affixing the composition onto the substrate comprises (a) applying the composition onto the substrate, (b) drying the composition to produce an acrylic-coated substrate, and (c) cooling the acrylic-coated substrate to ambient temperatures.

[0092] In one class of this embodiment, the substrate is metal. In one class of this embodiment, the substrate comprises steel. In one class of this embodiment, the substrate comprises aluminum. In one class of this embodiment, the substrate is part of a wheeled vehicle. In one class of this embodiment the substrate is on the under-body of a wheeled vehicle. In one class of this embodiment the substrate is on the inner-body of a wheeled vehicle. In one class of this embodiment, the substrate is wood or ceramic.

[0093] In one class of this embodiment, the drying occurs at a temperature range from 20 C. to 220 C. for a time period ranging from 1 minute to 24 hours. In one subclass of this class, the substrate is metal. In one subclass of this class, the substrate comprises steel. In one subclass of this class, the substrate comprises aluminum. In one subclass of this class, the substrate is part of a wheeled vehicle. In one subclass of this class, the substrate is on the under-body of a wheeled vehicle. In one subclass of this class, the substrate is on the inner-body of a wheeled vehicle. In one subclass of this class, the substrate is wood or ceramic.

[0094] In one class of this embodiment, the drying occurs at a temperature range from 20 C. to 175 C. for a time period ranging from 1 minute to 24 hours. In one subclass of this class, the substrate is metal. In one subclass of this class, the substrate comprises steel. In one subclass of this class, the substrate comprises aluminum. In one subclass of this class, the substrate is part of a wheeled vehicle. In one subclass of this class, the substrate is on the under-body of a wheeled vehicle. In one subclass of this class, the substrate is on the inner-body of a wheeled vehicle. In one subclass of this class, the substrate is wood or ceramic.

[0095] In one class of this embodiment, the drying occurs at a temperature range from 100 C. to 175 C. for a time period ranging from 1 minute to 24 hours. In one subclass of this class, the substrate is metal. In one subclass of this class, the substrate comprises steel. In one subclass of this class, the substrate comprises aluminum. In one subclass of this class, the substrate is part of a wheeled vehicle. In one subclass of this class, the substrate is on the under-body of a wheeled vehicle. In one subclass of this class, the substrate is on the inner-body of a wheeled vehicle. In one subclass of this class, the substrate is wood or ceramic.

[0096] The method for applying the composition onto the substrate is not particularly limited. In one class of this embodiment, applying the composition onto the substrate comprises coating the substrate with the composition. Non-limiting examples of coating include spray coating and/or extrusion coating. In one subclass of this class, the drying occurs at a temperature range from 20 C. to 220 C. for a time period ranging from 1 minute to 24 hours.

[0097] In one class of this embodiment, the method of affixing the composition to the substrate comprises (a) drying the composition into a sheet and (b) adhering the sheet to the substrate. In one subclass of this class, the drying occurs at a temperature range from 20 C. to 175 C. for a time period ranging from 1 minute to 24 hours.

[0098] The acrylic-coated substrate comprises the substrate and the acrylic coating made up of the dried composition. In one embodiment, the acrylic coating on the substrate has a thickness in the range of from about 1 mm to about 6 mm. In one embodiment, the coating on the substrate has a thickness in the range of from about 1 mm to about 3 mm.

[0099] In one embodiment, the acrylic coating on the substrate has a mass in the range of from about 1 kg/m.sup.2 to about 3 kg/m.sup.2. In one embodiment, the acrylic coating on the substrate has a mass in the range of from about 2 kg/m.sup.2 to about 3 kg/m.sup.2. In one embodiment, the acrylic coating on the substrate has a mass that is less than 3 kg/m.sup.2.

Examples

Abbreviations

[0100] Pz is plasticizer; g is gram; C. is degrees Celsius; Ex is example; Comp. Ex is comparative example; mm is millimeter; d is day(s); DMTA is dynamic mechanical thermal analysis; Hz is Hertz; Temp is temperature; phr is parts per hundred resin; rt is room temperature; Benzoflex 2088 Plasticizer (benzoate esters), Eastman Effusion Plasticizer (dibutyl terephthalate), and Eastman Triacetin Plasticizer (1,2,3-propanetriol triacetate) are commercially available (Eastman Chemical Company, Kingsport, Tenn.) and were used without further processing. The resin dispersions listed in Table 1 are commercially available (Eastman Chemical Company, Kingsport, Tenn.) and were used without further processing. The acrylic resin dispersions listed in Table 2 were used without further processing.

[0101] The resins, plasticizers, and acrylics used in the examples are listed in Table 1(a)-1(c).

TABLE-US-00001 TABLE 1(a) Resins used in Examples Softening Resin ID Chemical type point, C. Trade names Resin R1 Glycerol ester of rosin 71 Tacolyn 3179H resin dispersion Resin R2 Hydrogenated 92 Tacolyn 3100 resin pentaerytritol ester of dispersion rosin Resin R3 Aromatic-modified C5 70 Tacolyn 1070 resin hydrocarbon resin dispersion Resin R4 C5 hydrocarbon resin 70 Tacolyn 5070 resin dispersion

TABLE-US-00002 TABLE 1(b) Plasticizers used in Examples Plasticizer ID Chemical type Trade Names Pz 1 Benzoate Esters Benzoflex 2088 Plasticizer Pz 2 bis-n-butyl terephthalate Eastman Effusion Plasticizer Pz 3 1,2,3-propanetriol triacetate Eastman Triacitin Plasticizer

TABLE-US-00003 TABLE 1(C) Acrylics used in Examples Acrylic ID Chemical type Trade names Supplier Acrylic 1 methacrylic ester-acrylic Acousticryl Dow Chemical ester copolymer AV-2240 Company Acrylic 2 acrylic ester-styrene Revacryl Synthomer copolymer AE3723 Acrylic 3 acrylic ester-styrene Revacryl Synthomer copolymer AE6030

General Preparation of Acrylic Formulations and Samples for DMTA Evaluation

[0102] To a mixing cup was added 0-2 g of plasticizer. To this 25 g of acrylic emulsion was slowly added, while stirring continuously. Then 0-11 g of resin dispersion was added to the mixing cup, and the formulation was mixed so that a homogeneous mixture was obtained. Based on the solids content of the acrylic emulsion and the solids content of the resin dispersion, the correct required weight of resin dispersion was calculated to obtain the specified phr of resin.

[0103] Samples for DMTA analysis were prepared by casting the acrylic formulation into a silicone coated mold, in a wet layer thickness of 2-4 mm, resulting in a dry layer thickness of 1-2 mm. The filled molds were placed in an air circulation oven at 35 C. for 3 d to cure, unless otherwise specified. From the cured film, samples of 8 mm diameter were cut using a hollow punch tool.

[0104] DMTA measurements were performed on these samples using an 8 mm steel parallel plate fixture on an ARES-G2 rheometer from TA Instruments. Storage modulus, loss modulus, and tan delta (tan ) results were recorded at a frequency of 1 Hz, during heating of the sample from 50 C. to 80 C. at a heating rate of 5 C./min. Automatic strain adjustment, from 0.1% to 15%, was used to stay within the limits of the rheometer transducer and the linear viscoelastic range of the sample for the full temperature range.

Examples 1-7 and Comparative Examples C1

[0105] Ex 1-7 were made according to the general procedure without any plasticizer and with Acrylic 1 and the specific resin as shown in Table 2. The weights of the components are displayed as parts by weight of the acrylic solids. Comp Ex C1 was made according to the general procedure using Acrylic 1 without any plasticizer or resin.

[0106] The results show that the Comp Ex C1 can provide a maximum tan peak in the temperature range of interest (0-40 C.). However, blending the same acrylic with Resin R1, Resin R2, or Resin R3, provides the tan peak to be higher. A higher resin concentration results in a higher tan peak. The resin slightly shifts the tan peak to a higher temperature for Resin R2 and Resin R3. Resin R4 does not change the height or position of the tan peak.

TABLE-US-00004 TABLE 2 Acrylic 1, Resins R1-R4, and No Plasticizer. Temp Comp ( C.) Ex C1 Ex 1 Ex 2 Ex 3 Ex 4 Ex 5 Ex 6 Ex 7 Resin (phr) R1 (5) R1 (40) R2 (5) R2 (40) R3 (5) R3 (40) R4 (20) Acrylic 1 (phr) 100 100 100 100 100 100 100 100 Tan 50 0.06 0.05 0.04 0.05 0.06 0.05 0.05 0.05 40 0.07 0.06 0.04 0.06 0.08 0.06 0.06 0.06 30 0.08 0.07 0.05 0.07 0.09 0.07 0.08 0.08 20 0.13 0.12 0.08 0.11 0.11 0.11 0.10 0.14 10 0.29 0.27 0.16 0.24 0.16 0.26 0.17 0.33 0 0.39 0.42 0.46 0.41 0.33 0.41 0.42 0.48 10 0.56 0.57 0.83 0.54 0.67 0.53 0.71 0.62 20 1.21 1.23 1.59 1.15 1.08 1.15 1.23 1.22 25 1.56 1.61 1.96 1.58 1.54 1.59 1.82 1.57 30 1.50 1.53 1.73 1.59 1.83 1.59 1.91 1.54 40 1.09 1.09 1.23 1.13 1.40 1.13 1.34 1.17 50 0.94 0.96 1.17 0.97 1.21 0.97 1.16 1.07 60 0.98 1.01 1.35 1.01 1.29 1.00 1.24 1.17 70 1.14 1.19 1.72 1.18 1.56 1.16 1.46 1.37 80 1.37 1.40 2.26 1.39 1.96 1.36 1.79 1.50

Examples 8-14 and Comparative Examples C2

[0107] Ex 8-14 were made according to the general procedure without any plasticizer and with Acrylic 2 and the specific resin as shown in Table 3. The weights of the components are displayed as parts by weight of the acrylic solids. Comp Ex C2 was made according to the general procedure using Acrylic 2 without any plasticizer or resin.

[0108] The results show that the Comp Ex C2 can provide a maximum tan peak in the temperature range of interest (0-40 C.). However, blending the same acrylic with Resin R1, Resin R2, or Resin R3, provides the tan peak to be higher. A higher resin concentration results in a higher tan peak. The resin slightly shifts the tan peak to a higher temperature for Resin R2 and Resin R3. Resin R4 does not increase the tan peak height.

TABLE-US-00005 TABLE 3 Acrylic 2, Resin R1-R4, and No Plasticizer Temp Comp ( C.) Ex C2 Ex 8 Ex 9 Ex 10 Ex 11 Ex 12 Ex 13 Ex 14 Resin (phr) R1 (5) R1 (40) R2 (5) R2 (40) R3 (5) R3 (40) R4 (20) Acrylic 2 (phr) 100 100 100 100 100 100 100 100 tan 40 0.04 0.04 0.03 0.04 0.04 0.04 0.04 0.04 30 0.05 0.05 0.04 0.04 0.04 0.05 0.04 0.04 20 0.06 0.06 0.05 0.06 0.05 0.06 0.05 0.06 10 0.09 0.09 0.08 0.09 0.07 0.08 0.08 0.09 0 0.19 0.19 0.18 0.18 0.11 0.16 0.13 0.19 10 0.81 0.71 0.59 0.60 0.23 0.83 0.41 0.85 20 2.38 2.42 3.03 2.45 1.09 2.46 2.15 1.63 25 1.69 1.65 2.41 1.77 2.11 1.74 2.77 1.21 30 1.13 1.11 1.55 1.34 2.69 1.17 1.98 0.91 40 0.60 0.60 0.78 0.69 1.38 0.62 0.97 0.63 50 0.35 0.35 0.46 0.39 0.74 0.36 0.55 0.51 60 0.25 0.25 0.33 0.27 0.44 0.26 0.35 0.46 70 0.22 0.23 0.31 0.23 0.32 0.23 0.29 0.44 80 0.23 0.24 0.32 0.23 0.31 0.23 0.29 0.35

Examples 22-30

[0109] Ex 22-30 were made according to the general procedure without any resin and with Acrylic 1 and the specific plasticizer as shown in Tables 4, 5, and 6 except that Ex 22-24 were air dried at rt for 3 d. The weights of the components are displayed as parts by weight of the acrylic solids. Comp Ex C1 was made according to the general procedure using Acrylic 1 without any plasticizer or resin.

[0110] The results show that the plasticizers lower the temperature of the maximum tan peak. The shift is determined by the amount of plasticizer. Pz 1 increases the tan peak height. Pz 2 lowers the tan peak height and Pz 3 does not change the tan peak height. The increase or decrease is determined by the amount of plasticizer. The plasticizers cause the sample surface to be tacky.

TABLE-US-00006 TABLE 4 Acrylic 1, Pz 1-3 (10 phr), and No Resin Comp Ex C1 Ex 22 Ex 23 Ex 24 Pz (phr) Pz 1 Pz 2 Pz 3 (10) (10) (10) Acrylic 1 (phr) Temp 100 100 100 100 ( C.) tan 50 0.06 0.06 0.07 0.08 40 0.07 0.08 0.11 0.12 30 0.08 0.18 0.23 0.21 20 0.13 0.47 0.43 0.45 10 0.29 0.96 0.65 0.68 0 0.39 1.40 1.15 1.27 5 0.44 10 0.56 1.22 1.49 1.52 15 0.81 20 1.21 1.07 1.14 1.11 25 1.56 1.04 1.02 0.99 30 1.50 1.02 0.95 0.94 40 1.09 1.07 0.96 0.98 50 0.94 1.25 1.07 1.14 60 0.98 1.48 1.25 1.38 70 1.14 1.73 1.45 Tacky No Yes yes yes sample surface?

TABLE-US-00007 TABLE 5 Acrylic 1, Pz 1-3 (10 pph), and No Resin. Comp Ex C1 Ex 25 Ex 26 Ex 27 Pz (pphr) Pz 1 Pz 2 Pz 3 (10) (10) (10) Acrylic 1 (phr) Temp 100 100 100 100 ( C.) tan 50 0.06 0.06 0.07 0.07 40 0.07 0.08 0.11 0.10 30 0.08 0.14 0.22 0.18 20 0.13 0.31 0.44 0.39 10 0.29 0.52 0.80 0.56 0 0.39 0.89 1.38 1.05 5 0.44 1.27 1.49 1.40 10 0.56 1.61 1.37 1.51 15 0.81 1.57 1.20 1.39 20 1.21 1.30 1.08 1.21 25 1.56 1.10 1.02 1.05 30 1.50 0.98 0.99 0.96 40 1.09 0.95 1.05 0.95 50 0.94 1.06 1.21 1.08 60 0.98 1.43 1.29 70 1.14 Tacky sample No surface?

TABLE-US-00008 TABLE 6 Acrylic 1, Pz 1-3 (5 phr), and No Resin. Comp Ex 1 Ex 28 Ex 29 Ex 30 Pz (phr) Pz 1 (5) Pz 2 (5) Pz 3 (5) Acrylic 1 (phr) Temp 100 100 100 100 ( C.) tan 50 0.06 0.05 0.06 0.07 40 0.07 0.07 0.08 0.08 30 0.08 0.10 0.14 0.12 20 0.13 0.21 0.29 0.25 10 0.29 0.38 0.46 0.42 0 0.39 0.49 0.74 0.59 10 0.56 1.01 1.32 1.22 15 0.81 1.45 1.45 1.57 20 1.21 1.66 1.37 1.54 25 1.56 1.45 1.21 1.31 30 1.50 1.18 1.08 1.11 40 1.09 0.95 0.97 0.93 50 0.94 0.95 1.01 0.96 60 0.98 1.08 1.17 1.11 70 1.14 1.30 1.33

Examples 15-21 and Comparative Example C3

[0111] Ex 15 was made according to the general procedure without any plasticizer and with Acrylic 3 and the specific resin as shown in Table 7. The weights of the components are displayed as parts by weight of the acrylic solids. Ex 16-21 were made according to the general procedure using Acrylic 3 and Resin R2 and the amount and type of plasticizer as shown in Table 7. Comp Ex C3 was made according to the general procedure using Acrylic 3 without any plasticizer or resin.

[0112] The results show that the Comp Ex C3 provides a maximum tan peak outside the temperature range of interest (0-40 C.). Blending Acrylic 3 with Resin R2 will increase the tan peak height, and will slightly increase the tan peak temperature. Blending the Acrylic 3 with Resin R2 and Pz 1-3 will increase the tan peak height, and will lower the tan peak temperature to the temperature range of interest. A higher plasticizer addition results in a lower tan peak temperature. Pz 1 and Pz 2 slightly lower the tan peak height at the higher addition level. Pz 3 greatly lowers the tan peak height at the higher addition level.

TABLE-US-00009 TABLE 7 Acrylic 3, Resin R2, and Pz 1-3. Temp Comp ( C.) Ex C3 Ex 15 Ex 16 Ex 17 Ex 18 Ex 19 Ex 20 Ex 21 Pz (phr) Pz 1 (2.5) Pz 1 (15) Pz 2 (2.5) Pz 2 (15) Pz 3 (2.5) Pz 3 (15) Resin R2 (phr) 20 20 20 20 20 20 20 Acrylic 3 (phr) 100 100 100 100 100 100 100 100 tan 30 0.03 0.04 0.03 0.06 0.04 0.08 0.04 0.07 20 0.04 0.06 0.04 0.08 0.04 0.13 0.04 0.09 10 0.04 0.07 0.05 0.12 0.05 0.20 0.05 0.15 0 0.06 0.09 0.07 0.23 0.07 0.42 0.07 0.34 10 0.09 0.14 0.11 0.78 0.12 1.27 0.12 1.18 20 0.17 0.23 0.23 2.72 0.28 2.53 0.28 1.60 30 0.50 0.48 0.89 1.84 1.00 1.35 1.25 1.29 40 2.55 2.32 2.85 0.92 2.70 0.75 2.65 0.90 45 2.15 2.85 2.27 0.71 2.12 0.59 2.06 0.67 50 1.46 1.99 1.50 0.56 1.43 0.48 1.41 0.52 60 0.78 0.96 0.79 0.39 0.77 0.36 0.77 0.38 70 0.47 0.57 0.49 0.33 0.48 0.33 0.48 0.35 80 0.32 0.38 0.35 0.34 0.35 0.35 0.37

[0113] Other embodiments will be apparent to those skilled in the art from consideration of the specification and practice of the embodiments disclosed herein. It will be understood that variations and modifications can be effected within the spirit and scope of the disclosed embodiments. It is further intended that the specification and examples be considered as exemplary only, with a true scope and spirit of the disclosed embodiments being indicated by the following.