Localized electron beam induced deposition of silicon carbide

Abstract

A method for produce a silicon-carbide film by admitting a gaseous silicon-carbide precursor into a vacuum chamber containing a substrate and directing an electron beam into the vacuum chamber onto to the surface of the substrate. The electron beam dissociates the gaseous silicon-carbide precursor at the surface of the substrate creating non-volatile fragments that bind to the substrate surface forming a silicon-carbide film.

Claims

1. A method of producing a silicon-carbide film, comprising the steps of: admitting a gaseous silicon-carbide precursor into a vacuum chamber containing a substrate with a substrate surface wherein said gaseous silicon-carbide precursor absorbs to said substrate surface, and directing an electron beam or ion beam to said substrate surface, wherein said electron beam or ion beam dissociates said gaseous silicon-carbide precursor creating non-volatile fragments that bind to said substrate surface forming a silicon-carbide film, and wherein said step of directing an electron beam or ion beam to said substrate surface comprises using a scanning electron microscope for directing an electron beam or ion beam to said substrate surface.

2. A method of producing a silicon-carbide film, comprising the steps of: admitting a gaseous silicon-carbide precursor into a vacuum chamber containing a substrate with a substrate surface wherein said gaseous silicon-carbide precursor absorbs to said substrate surface, and directing an electron beam or ion beam to said substrate surface, wherein said electron beam or ion beam dissociates said gaseous silicon-carbide precursor creating non-volatile fragments that bind to said substrate surface forming a silicon-carbide film, and wherein said step of directing an electron beam or ion beam to said substrate surface comprises using an electron flood gun for directing an electron beam or ion beam to said substrate surface.

3. The method of producing a silicon-carbide film, comprising the steps of: delivering a gaseous silicon-carbide precursor to a substrate in a vacuum chamber thereby provide an interface of said gaseous silicon-carbide precursor and said substrate in said vacuum chamber, directing focused charged particles to said interface of said gaseous silicon-carbide precursor and said substrate, wherein said step of directing focused charged particles to said interface of said gaseous silicon-carbide precursor and said substrate comprises using a scanning electron microscope for directing focused electrons to the said interface of said gaseous silicon-carbide precursor and said substrate, and moving said focused charged particles relative to said substrate to produce the silicon-carbide film.

4. A method of producing a silicon-carbide film, comprising the steps of: delivering a gaseous silicon-carbide precursor to a substrate in a vacuum chamber thereby provide an interface of said gaseous silicon-carbide precursor and said substrate in said vacuum chamber, directing focused charged particles to said interface of said gaseous silicon-carbide precursor and said substrate, wherein said step of directing focused charged particles to said interface of said gaseous silicon-carbide precursor and said substrate comprises using an electron flood gun for directing focused electrons to the said interface of said gaseous silicon-carbide precursor and said substrate, and moving said focused charged particles relative to said substrate to produce the silicon-carbide film.

5. A method of producing a silicon-carbide film, comprising the steps of: providing a gaseous silicon-carbide precursor; providing a vacuum chamber; directing a beam of electrons into said vacuum chamber; providing a substrate, wherein said substrate has a substrate surface; positioning said substrate in said vacuum chamber; admitting said gaseous silicon-carbide precursor into said vacuum chamber; and directing said beam of electrons in said vacuum chamber onto said gaseous silicon-carbide precursor and onto said substrate surface wherein said gaseous silicon-carbide precursor absorbs to said substrate surface, wherein said electron beam or ion beam dissociates said gaseous silicon-carbide precursor creating non-volatile fragments that bind to said substrate surface forming a silicon-carbide film, wherein said steps of directing a beam of electrons into said vacuum chamber and directing said beam of electrons in said vacuum chamber onto said gaseous silicon-carbide precursor and onto said substrate surface comprises using a scanning electron microscope for directing a beam of electrons into said vacuum chamber, and directing said beam of electrons in said vacuum chamber onto said gaseous silicon-carbide precursor and onto said substrate surface.

6. A method of producing a silicon-carbide film, comprising the steps of: providing a gaseous silicon-carbide precursor; providing a vacuum chamber; directing a beam of electrons into said vacuum chamber; providing a substrate, wherein said substrate has a substrate surface; positioning said substrate in said vacuum chamber; admitting said gaseous silicon-carbide precursor into said vacuum chamber; and directing said beam of electrons in said vacuum chamber onto said gaseous silicon-carbide precursor and onto said substrate surface wherein said gaseous silicon-carbide precursor absorbs to said substrate surface and wherein said electron beam or ion beam dissociates said gaseous silicon-carbide precursor creating non-volatile fragments that bind to said substrate surface forming a silicon-carbide film, wherein said steps of directing a beam of electrons into said vacuum chamber and directing said beam of electrons in said vacuum chamber onto said gaseous silicon-carbide precursor and onto said substrate surface comprises using an electron flood gun for directing a beam of electrons into said vacuum chamber and directing said beam of electrons in said vacuum chamber onto said gaseous silicon-carbide precursor and onto said substrate surface.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) The accompanying drawings, which are incorporated into and constitute a part of the specification, illustrate specific embodiments of the apparatus, systems, and methods and, together with the general description given above, and the detailed description of the specific embodiments, serve to explain the principles of the apparatus, systems, and methods.

(2) FIG. 1 is a flow chart illustrating one embodiment of the inventor's methods.

(3) FIG. 2 is a schematic illustration of an electron beam or ion beam induced deposition system according to one embodiment of the invention.

(4) FIG. 3 is a schematic illustration of an electron beam or ion beam induced deposition system according to another embodiment of the invention.

DETAILED DESCRIPTION OF SPECIFIC EMBODIMENTS

(5) Referring to the drawings, to the following detailed description, and to incorporated materials, detailed information about the apparatus, systems, and methods is provided including the description of specific embodiments. The detailed description serves to explain the principles of the apparatus, systems, and methods. The apparatus, systems, and methods are susceptible to modifications and alternative forms. The application is not limited to the particular forms disclosed. The application covers all modifications, equivalents, and alternatives falling within the spirit and scope of the apparatus, systems, and methods as defined by the claims.

(6) The inventor provides the application of electron beam or ion beam induced deposition to a specific type of material (silicon carbide) and the use of an electron microscope to control/localize the deposition of silicon carbide. Gaseous precursor (tetramethylsilane) is delivered to a substrate in a vacuum chamber. Adsorbed molecules are dissociated by a beam of electrons. Non-volatile fragments remain on the substrate leading to formation of a deposit (silicon carbide). The stoichiometry, deposition rate and physical properties of the deposit are all dependent on the precursor gas pressure, mixing gas (if any), electron flux and energy, and substrate temperature.

(7) The vacuum chamber and beam of electrons are provided by a scanning electron microscope system. The scanning electron microscope is capable of providing a focused (1 nm) beam of electrons which is used to control the deposit feature size. The beam can be scanned over the substrate to pattern features. The stage can be used for patterning larger features across the substrate.

(8) Substrate heating during deposition can be provided by a thermal stage heating accessory or laser induced heating to change the film growth properties and quality. Post-processing the deposits by heating in vacuum or hydrogen can also be used to change the film quality.

(9) Gas delivery is achieved by filling the vacuum chamber with gaseous precursor or using a standard gas delivery nozzle located above the substrate in a high vacuum chamber condition.

(10) Referring now to the drawings, and in particular to FIG. 1, a flow chart illustrates one embodiment of the inventor's methods. This embodiment is designated generally by the reference numeral 100. The flow chart illustrates a number of individual steps that encompass the inventor's methods. The flow chart 100 includes the steps listed below.

(11) Step 102flow a gaseous silicon-carbide precursor into a vacuum chamber containing a substrate with a substrate surface wherein said gaseous silicon-carbide precursor absorbs to said substrate surface,

(12) Step 104maintain the substrate at room temperature or heat the substrate,

(13) Step 106irradiate a region of the substrate with electrons from an electron beam or ion beam to dissociate the gaseous silicon-carbide precursor creating non-volatile fragments that bind to the substrate surface, and

(14) Step 106anneal the substrate with the non-volatile fragments that bind to the substrate surface.

(15) The embodiment 100 of the inventor's methods for method of producing a silicon-carbide film provides and electron beam or ion beam induced deposition (EBID) process wherein a gaseous silicon-carbide precursor is admitted into the vacuum chamber where it adsorbs to the substrate surface. The electron beam or ion beam dissociates adsorbed precursor molecules creating non-volatile fragments that bind to the surface forming a solid. In one embodiment the gaseous silicon-carbide precursor is an alkylsilane. In another embodiment the gaseous silicon-carbide precursor is a tetraorganosilane. In another embodiment the gaseous silicon-carbide precursor is tetramethylsilane. In another embodiment the gaseous silicon-carbide precursor is a mixture of alkane and silane precursors. In one embodiment the non-volatile fragments that bind to the substrate surface form a deposit and the deposit is heated to a temperature greater than 800 degrees Celsius.

(16) Referring now to FIG. 2, an example embodiment of the inventor's system for producing a silicon-carbide film is illustrated. The system is designated generally by the reference numeral 200. The system 200 illustrated in FIG. 2 includes the components listed below. Component 102vacuum chamber, Component 104scanning electron microscope focused beam source, Component 106precursor gas source, Component 108substrate, Component 110X-Y stage, and Component 112beam.

(17) The system 200 operates by admitting a gaseous silicon-carbide precursor into a vacuum chamber containing a substrate with a substrate surface wherein the gaseous silicon-carbide precursor absorbs to the substrate surface, and directing an electron beam or ion beam to the substrate surface wherein the electron beam or ion beam dissociates the gaseous silicon-carbide precursor creating non-volatile fragments that bind to the substrate surface forming a silicon-carbide film. In one embodiment the gaseous silicon-carbide precursor is an alkylsilane. In another embodiment the gaseous silicon-carbide precursor is a tetraorganosilane. In another embodiment the gaseous silicon-carbide precursor is tetramethylsilane. In another embodiment the gaseous silicon-carbide precursor is a mixture of alkane and silane precursors. In one embodiment the non-volatile fragments that bind to the substrate surface form a deposit and the deposit is heated to a temperature greater than 800 degrees Celsius.

(18) Referring now to FIG. 3; another example embodiment of the inventor's systems for producing a silicon-carbide film is illustrated. This embodiment system is designated generally by the reference numeral 300. The system 300 illustrated in FIG. 3 includes the components listed below. Component 302vacuum chamber, Component 304scanning electron microscope focused beam source, Component 306precursor gas source, Component 308substrate, Component 310substrate heater, Component 312beam, Component 314computer/controller, and Component 316 X-Y stage.

(19) The system 300 utilizes a focused beam source of a scanning electron microscope 304, a vacuum chamber 302, a precursor material source 306, a substrate 308, and heater 310. The system 300 operates by admitting the gaseous silicon-carbide precursor into the vacuum chamber containing the substrate 310 with a substrate surface wherein the gaseous silicon-carbide precursor absorbs to the substrate surface, and directing the electron beam or ion beam 312 to the substrate surface wherein the electron beam or ion beam dissociates the gaseous silicon-carbide precursor creating non-volatile fragments that bind to the substrate surface forming a silicon-carbide film by moving the electron beam or ion beam 312 using x-y stage 316. The computer/controller 314 is used to provide the steps of the inventor's methods. In one embodiment the gaseous silicon-carbide precursor is an alkylsilane. In another embodiment the gaseous silicon-carbide precursor is a tetraorganosilane. In another embodiment the gaseous silicon-carbide precursor is tetramethylsilane. In another embodiment the gaseous silicon-carbide precursor is a mixture of alkane and silane precursors. In one embodiment the non-volatile fragments that bind to the substrate surface form a deposit and the deposit is heated to a temperature greater than 800 degrees Celsius.

(20) Although the description above contains many details and specifics, these should not be construed as limiting the scope of the application but as merely providing illustrations of some of the presently preferred embodiments of the apparatus, systems, and methods. Other implementations, enhancements and variations can be made based on what is described and illustrated in this patent document. The features of the embodiments described herein may be combined in all possible combinations of methods, apparatus, modules, systems, and computer program products. Certain features that are described in this patent document in the context of separate embodiments can also be implemented in combination in a single embodiment. Conversely, various features that are described in the context of a single embodiment can also be implemented in multiple embodiments separately or in any suitable subcombination. Moreover, although features may be described above as acting in certain combinations and even initially claimed as such, one or more features from a claimed combination can in some cases be excised from the combination, and the claimed combination may be directed to a subcombination or variation of a subcombination. Similarly, while operations are depicted in the drawings in a particular order, this should not be understood as requiring that such operations be performed in the particular order shown or in sequential order, or that all illustrated operations be performed, to achieve desirable results. Moreover, the separation of various system components in the embodiments described above should not be understood as requiring such separation in all embodiments.

(21) Therefore, it will be appreciated that the scope of the present application fully encompasses other embodiments which may become obvious to those skilled in the art. In the claims, reference to an element in the singular is not intended to mean one and only one unless explicitly so stated, but rather one or more. All structural and functional equivalents to the elements of the above-described preferred embodiment that are known to those of ordinary skill in the art are expressly incorporated herein by reference and are intended to be encompassed by the present claims. Moreover, it is not necessary for a device to address each and every problem sought to be solved by the present apparatus, systems, and methods, for it to be encompassed by the present claims. Furthermore, no element or component in the present disclosure is intended to be dedicated to the public regardless of whether the element or component is explicitly recited in the claims. No claim element herein is to be construed under the provisions of 35 U.S.C. 112, sixth paragraph, unless the element is expressly recited using the phrase means for.

(22) While the apparatus, systems, and methods may be susceptible to various modifications and alternative forms, specific embodiments have been shown by way of example in the drawings and have been described in detail herein. However, it should be understood that the application is not intended to be limited to the particular forms disclosed. Rather, the application is to cover all modifications, equivalents, and alternatives falling within the spirit and scope of the application as defined by the following appended claims.