METHOD FOR IMPREGNATING A FIBROUS PREFORM USING A SEAL, AND A METHOD FOR MANUFACTURING A MATRIX REINFORCED BY A FIBROUS PREFORM

Abstract

A method for impregnating a fibrous preform by injection or infusion, the method including the steps of providing a mold having at least two portions, said mold presenting an inlet orifice and a vent orifice placed on opposite sides of the mold; placing a fibrous preform in a portion of the mold; placing a seal in a passage formed between an inside wall of the mold and the fibrous preform, said passage extending substantially along the direction extending between the opposite sides of the mold; closing the mold so that the two portions of the mold co-operate with the seal in such a manner as to shut off said passage; and impregnating the fibrous preform with an impregnation material.

Claims

1. A method for impregnating a fibrous preform by injection or infusion, comprising the steps of: providing a mold having at least two portions, said mold presenting at least one inlet orifice and at least one vent orifice placed on opposite sides of the mold; placing a fibrous preform in a portion of the mold; placing at least one seal in at least one passage formed between an inside wall of the mold and the fibrous preform, said passage extending substantially along the direction extending between the opposite sides of the mold and respectively presenting the inlet orifice and the vent orifice; closing the mold so that the two portions of the mold co-operate with the seal in such a manner as to shut off said passage; and impregnating the fibrous preform with an impregnation material.

2. A method for impregnating a fibrous preform according to claim 1, wherein the seal is placed so that it extends in the mold over substantially the entire length of the fibrous preform between said opposite sides of the mold.

3. A method for impregnating a fibrous preform according to claim 1, wherein the seal presents a cross-section of circular or equivalent shape.

4. A method for impregnating a fibrous preform according to claim 1, wherein the seal presents an L-shaped cross-section.

5. A method for impregnating a fibrous preform according to claim 1, wherein the seal presents a U-shaped cross-section.

6. A method for impregnating a fibrous preform according to claim 5, wherein an edge of the fibrous preform is engaged in the cavity of the U-shape of the seal.

7. A method for impregnating a fibrous preform according to claim 1, wherein the impregnation material is a resin.

8. A method for fabricating a matrix reinforced by a fibrous preform, comprising the steps of: impregnating a fibrous preform in accordance with the method according to claim 1 for impregnating a fibrous preform, thereby obtaining a reinforced raw matrix; and machining at least a portion of the reinforced raw matrix that was in contact with the seal during impregnation.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0037] The invention and its advantages can be better understood on reading the following detailed description of various embodiments of the invention given as non-limiting examples. The description refers to the sheets of the accompanying figures, in which:

[0038] FIGS. 1A and 1B show a first step in an impregnation method in which a fibrous preform is placed in a portion of a mold;

[0039] FIGS. 2A and 2B show a second step of the impregnation method in which a seal is placed between the preform and a wall of the mold;

[0040] FIG. 3A shows a third step in which the mold is closed, and FIGS. 3B and 3C show variant seal shapes;

[0041] FIG. 4 shows a fourth step of the impregnation method in which the preform is impregnated; and

[0042] FIG. 5 shows a step of machining the raw matrix reinforced with the fibrous preform as obtained after the step shown in FIG. 4 at the end of the impregnation method.

DETAILED DESCRIPTION OF EMBODIMENTS

[0043] The figures show a mold, a seal, and a fibrous preform in highly diagrammatic manner in order to clarify the present disclosure. The person skilled in the art will naturally have no difficulty in transposing the teaching of the present disclosure to shapes that are appropriate for fabricating real parts of shapes that are more complex.

[0044] The impregnation method is described below with reference to FIGS. 1A to 4. It should be observed that FIGS. 1B and 2B are respectively views of FIGS. 1A and 2A on section plane B as shown in FIG. 1A.

[0045] FIGS. 1A and 1B show a first step during which a fibrous preform 10 is placed within a portion 12A of a mold 12. The mold 12 has an inlet orifice 14 for introducing an impregnation material into the mold. The mold 12 also has a vent orifice 16 for evacuating air and/or surplus impregnation material during impregnation.

[0046] The inlet orifice 14 and the vent orifice 16 are placed on two opposite sides 13A and 13B of the mold 12. These sides are opposite along an axial direction X. In this example, the mold 12 is of rectangular shape and the axial direction extends parallel to the long side of the rectangular shape. Naturally, the orifices could be placed on the short sides of the rectangular shape, and the axial direction would then extend parallel to the short sides of the rectangular shape. More generally, the axial direction is the direction that extends between any pair of opposite sides, these sides presenting respectively the inlet orifice and the vent orifice.

[0047] Passages 20 and 22, formed between the preform 10 and the inside walls of the mold 12, extend in the direction that extends between the opposite walls 13A and 13B. In other words, the passages 20 and 22 extend between the preform 10 and the mold 12 in a direction that is substantially parallel to the axial direction X. In this example, the passages 20 and 22 are parallel to the axial direction X.

[0048] A second step of the impregnation method is shown in FIGS. 2A and 2B. During this second step, seals 24 and 26 are placed respectively in the passages 20 and 22. In this example, the seals 24 and 26 are placed in such a manner as to extend over substantially the entire length of the preform 10 as considered between the opposite sides 13A and 13B of the mold 12 (i.e. the axial length of the preform). In this example, the seals 24 and 26 extend over 100% of the length L of the preform 10.

[0049] Naturally, it can be understood that the first step and the second step could be performed in the opposite order: specifically, it is possible to place the preform 10 in a portion of the mold 12 before putting the seal(s) 24 or 26 into place, or vice versa. Or indeed, it is possible to place at least one seal in a portion of the mold, then to put the preform into place, and then put at least one other seal into place.

[0050] It should be observed that the seals 24 and 26 have sections of circular or equivalent shape, and more particularly in this example of oval shape. In this example, the height of the seals in the height direction Y, perpendicular to the axial direction X, which extends in the opening/closing direction of the mold 12, is greater than the height of the portion of the preform 10 that is adjacent to the seal 24, 26 in the same direction Y. Thus, while the mold 12 is being closed, the second portion 12B of the mold co-operates with the seals 24 and 26, whereby the seals deform in such a manner as to fill in the passages 20 and 22, respectively. This step of closing and shutting off the passages by means of the seals deforming is shown in FIG. 3A. The arrow (bold line) shows the direction of approach of the second portion 12B of the mold relative to the first portion 12A, while the mold 12 is being closed. In general, it should be understood that the height of the seals is greater than the height of the mold cavity, but not necessarily greater than the height of the preform.

[0051] FIG. 3B shows a first variant in which the seals present an L-shaped cross-section. In this example, the preform 10 presents sacrificial portions 10A and 10B, each of which is received in the inside corner of the L-shape of a respective one of the seals 24 and 26. It should be observed that the branch of the L-shape of each of the seals 24 and 26 that is not placed in a passage 20, 22, presents in cross-section, a beveled shape of thickness that decreases on moving away from the corner of the L-shape. This enables co-operation with the preform 10 to be progressive and avoids generating unacceptable forces and deformation in the preform 10. This also makes it possible to avoid potentially forming localized paths between the seal and the fibrous preform.

[0052] FIG. 3C shows a second variant in which the seals present a U-shaped cross-section. In this example, the preform 10 presents sacrificial portions 10A and 10B each of which is received in the U-shaped cavity of a respective one of the seals 24 and 26. In this example, the sacrificial portions 10A and 10B of the preform 10 present shoulders configured to co-operate with the vertical branches of the U-shapes of the seals. Thus, the seals 24 and 26 are assembled together with the preform 10 by engaging the edges 11A and 11B in the cavities of the U-shapes of the seals.

[0053] However, as with the L-shaped seal, these vertical branches of the U-shape may naturally present, in cross-section, a beveled shape of thickness that decreases on moving away from the horizontal bottom branch of the U-shape. Conversely, in yet another variant, the branch of the L-shaped section of the seal shown in FIG. 3B and that is not placed in a passage 20, 22, may present a shape that is rectangular and may co-operate with a shoulder of the preform.

[0054] FIG. 4 shows the FIG. 3A assembly during the step of impregnating the preform 10. In this example, impregnation is performed by injecting resin 28, however it is naturally possible to perform impregnation by infusion. Likewise in this example the impregnation material is a resin, but other materials such as a ceramic or a metal could equally well be envisaged. The material of the seal should therefore be selected accordingly.

[0055] As shown in FIG. 4, as a result of the seals 24 and 26 that have expanded and that have shut off the passages 20 and 22, the resin 28 is forced to pass through the fibrous preform 10, whereby the resulting injection front F is substantially plane. It should be observed in this example that a passage 30 perpendicular to the axial direction X is left upstream from the preform 10 between the preform 10 itself and the mold 12. This passage 30 forms an inlet manifold serving to diffuse the resin 28 uniformly within the preform 10. Likewise, a passage 32 perpendicular to the axial direction X is provided downstream from the preform 10 between the preform 10 itself and the mold 12. This passage 32 forms an outlet manifold enabling the resin 28 that has passed through the preform 10 to leave in uniform manner, thereby obtaining uniform diffusion and thus uniform impregnation of the resin 28 within the preform.

[0056] At the end of the impregnation method as described with reference to FIGS. 1A to 4, a raw matrix 50 is obtained that is reinforced by a fibrous preform. This impregnation method forms the first step in a method for fabricating a matrix reinforced by a fibrous preform. A following step of the fabrication method comprises machining at least a portion of the raw preform in contact with a seal in the mold 12. FIG. 5 shows such a machining step. In this example, the machining is performed using a cutter 60 to mill an edge 50A of the reinforced raw matrix 50, which edge 50A is adjacent to the seal 24 in the mold 12. The edge 50B adjacent to the seal 26 in the mold 12 may also be milled. For clarity of description, although in the step shown in FIG. 4 the raw matrix 50 is not yet formed in full, the references 50A and 50B are nevertheless marked on the corresponding portions of the preform 10 while it is being impregnated.

[0057] In addition, with reference to FIGS. 3B and 3C, the machining shown in FIG. 5 may also aim to remove all or part of the sacrificial portions 10A, 10B, 10A and/or 10B.

[0058] Although the present invention is described with reference to specific embodiments, it is clear that modifications and changes may be undertaken on them without going beyond the general ambit of the invention as defined by the claims. In particular, individual characteristics of various embodiments shown and/or mentioned may be combined in additional embodiments. Consequently, the description and the drawings should be considered in a sense that is illustrative rather than restrictive.

[0059] It is also clear that all of the characteristics described with reference to a method are transposable, singly or in combination, to a device, and vice versa, all of the characteristics described with reference to a device are transposable, singly or in combination to a method.