Mesoporous catalysts of magnetic nanoparticles and free-radical-producing enzymes, and methods of use
10316313 ยท 2019-06-11
Assignee
Inventors
- Stephane C. Corgie (Ithaca, NY, US)
- Patarawan KAHAWONG (Nakhonsithammarat, TH)
- Emmanuel P. Giannelis (Ithaca, NY)
- Larry P. Walker (Ithaca, NY, US)
Cpc classification
C12N9/0065
CHEMISTRY; METALLURGY
B01J35/33
PERFORMING OPERATIONS; TRANSPORTING
Y02P20/52
GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
C12P2201/00
CHEMISTRY; METALLURGY
C12N11/14
CHEMISTRY; METALLURGY
C08H6/00
CHEMISTRY; METALLURGY
B82Y30/00
PERFORMING OPERATIONS; TRANSPORTING
C12P17/181
CHEMISTRY; METALLURGY
C12Y111/01007
CHEMISTRY; METALLURGY
International classification
B82Y30/00
PERFORMING OPERATIONS; TRANSPORTING
C12N11/14
CHEMISTRY; METALLURGY
C12P17/18
CHEMISTRY; METALLURGY
B01J35/00
PERFORMING OPERATIONS; TRANSPORTING
B01J31/00
PERFORMING OPERATIONS; TRANSPORTING
Abstract
A composition comprising mesoporous aggregates of magnetic nanoparticles and free-radical producing enzyme (i.e., enzyme-bound mesoporous aggregates), wherein the mesoporous aggregates of magnetic nanoparticles have mesopores in which the free-radical-producing enzyme is embedded. Methods for synthesizing the enzyme-bound mesoporous aggregates are also described. Processes that use said enzyme-bound mesoporous aggregates for depolymerizing lignin, removing aromatic contaminants from water, and polymerizing monomers polymerizable by a free-radical reaction are also described.
Claims
1. A composition comprising self-assembled mesoporous aggregates of magnetic nanoparticles and a lactoperoxidase, wherein said lactoperoxidase is magnetically-entrapped without a bonding agent in mesopores of said self-assembled mesoporous aggregates of magnetic nanoparticles, and said lactoperoxidase functions by converting a diffusible substrate into a diffusible product.
2. The composition of claim 1, wherein said self-assembled mesoporous aggregates of magnetic nanoparticles have an iron oxide composition.
3. The composition of claim 1, wherein said self-assembled mesoporous aggregates of magnetic nanoparticles have a magnetic nanoparticle size distribution in which at least 90% of magnetic nanoparticles have a size of at least 3 nm and up to 30 nm, and an aggregated particle size distribution in which at least 90% of said self-assembled mesoporous aggregates of magnetic nanoparticles have a size of at least 10 nm and up to 500 nm.
4. The composition of claim 1, wherein said self-assembled mesoporous aggregates of magnetic nanoparticles possess a saturated magnetization of at least 10 emu/g.
5. The composition of claim 1, wherein said self-assembled mesoporous aggregates of magnetic nanoparticles possess a remanent magnetization up to 5 emu/g.
6. The composition of claim 1, wherein said lactoperoxidase is contained in said self-assembled mesoporous aggregates of magnetic nanoparticles in up to 100% of saturation capacity.
7. The composition of claim 1, wherein said mesopores are characterized by a pore size distribution in which at least 90% of said pore volume is attributed to pores having a pore size of at least 2 nm and up to 20 nm.
8. The composition of claim 1, wherein said mesopores are characterized by a pore size distribution in which at least 95% of said pore volume is attributed to pores having a pore size of at least 2 nm and up to 20 nm.
9. The composition of claim 1, further comprising an oxidase.
10. The composition of claim 9, wherein said oxidase is glucose oxidase.
11. The composition of claim 1, wherein said self-assembled mesoporous aggregates of magnetic nanoparticles and lactoperoxidase reside within submicrometric particles having a size of at least 20 nanometers.
12. A composition comprising self-assembled mesoporous aggregates of magnetic nanoparticles and an enzyme, wherein said enzyme is magnetically-entrapped without a bonding agent in mesopores of said self-assembled mesoporous aggregates of magnetic nanoparticles, and said enzyme functions by converting a diffusible substrate into a diffusible product, wherein said enzyme is selected from the group consisting of EC 1.1.2, EC 1.10.2, EC 1.14 oxidoreductase, cytochrome-b5 reductase, cytochrome-c reductase, and cytochrome-c peroxidase.
13. The composition of claim 12, wherein said self-assembled mesoporous aggregates of magnetic nanoparticles have an iron oxide composition.
14. The composition of claim 12, wherein said self-assembled mesoporous aggregates of magnetic nanoparticles have a magnetic nanoparticle size distribution in which at least 90% of magnetic nanoparticles have a size of at least 3 nm and up to 30 nm, and an aggregated particle size distribution in which at least 90% of said self-assembled mesoporous aggregates of magnetic nanoparticles have a size of at least 10 nm and up to 500 nm.
15. The composition of claim 12, wherein said self-assembled mesoporous aggregates of magnetic nanoparticles possess a saturated magnetization of at least 10 emu/g.
16. The composition of claim 12, wherein said self-assembled mesoporous aggregates of magnetic nanoparticles possess a remnant magnetization up to 5 emu/g.
17. The composition of claim 12, wherein said enzyme is contained in said self-assembled mesoporous aggregates of magnetic nanoparticles in up to 100% of saturation capacity.
18. The composition of claim 12, wherein said mesopores are characterized by a pore size distribution in which at least 95% of said pore volume is attributed to pores having a pore size of at least 2 nm and up to 20 nm.
19. The composition of claim 12, wherein said mesopores are characterized by a pore size distribution in which at least 90% of said pore volume is attributed to pores having a pore size of at least 2 nm and up to 20 nm.
Description
BRIEF DESCRIPTION OF THE FIGURES
(1)
(2)
(3)
(4)
(5)
(6)
(7)
(8)
(9)
(10)
(11)
(12)
(13)
(14)
(15)
(16)
(17)
(18)
(19)
(20)
(21)
(22)
(23)
(24)
(25)
(26)
(27)
(28)
(29)
(30)
(31)
(32)
(33)
(34)
(35)
(36)
DETAILED DESCRIPTION OF THE DISCLOSURE
(37) In one aspect, the invention is directed to a free-radical producing (FRP) composition that includes magnetic nanoparticles bound to FRP enzyme. Magnetic nanoparticles bound to FRP enzyme is herein also referred to as a bionanocatalyst or BNC. As used herein, the term bound is intended to include any of the means by which FRP enzyme can be attached to magnetic nanoparticles without the release of FRP enzyme from the magnetic nanoparticles under conditions in which they are used or stored for later use. The FRP enzyme can be bound by, for example, covalent, ionic, hydrogen bonding, affinity, or van der Waals interactions. The FRP enzyme may be located anywhere on the magnetic nanoparticle, e.g., on the surface and/or embedded within the magnetic nanoparticle, such as in mesopores of the magnetic nanoparticles if the magnetic nanoparticles are porous. As used herein, the term magnetic encompasses all types of useful magnetic characteristics, including permanent magnetic, superparamagnetic, paramagnetic, ferromagnetic, and ferrimagnetic behaviors.
(38) The magnetic nanoparticle or BNC has a size in the nanoregime, i.e., generally no more than 500 nm. As used herein, the term size can refer to a diameter of the magnetic nanoparticle when the magnetic nanoparticle is approximately or substantially spherical. In a case where the magnetic nanoparticle is not approximately or substantially spherical (e.g., substantially ovoid or irregular), the term size can refer to either the longest the dimension or an average of the three dimensions of the magnetic nanoparticle. The term size may also refer to an average of sizes over a population of magnetic nanoparticles (i.e., average size). In different embodiments, the magnetic nanoparticle has a size of no more than, for example, 500 nm, 400 nm, 300 nm, 200 nm, 100 nm, 50 nm, 40 nm, 30 nm, 25 nm, 20 nm, 15 nm, 10 nm, 5 nm, 4 nm, 3 nm, 2 nm, or 1 nm, or a size within a range bounded by any two of the foregoing exemplary sizes.
(39) The magnetic nanoparticles described above or BNCs thereof may be clustered, i.e., as aggregates or agglomerations, in which case the above-described magnetic nanoparticles are considered to be primary nanoparticles (i.e., primary crystallites) and the magnetic nanoparticle sizes provided above can be considered to be primary nanoparticle sizes. The aggregates generally have a size (i.e., secondary size) of at least 5 nm. In different embodiments, the aggregates have a size of precisely, about, or at least, for example, 5 nm, 8 nm, 10 nm, 12 nm, 15 nm, 20 nm, 25 nm, 30 nm, 35 nm, 40 nm, 45 nm, 50 nm, 60 nm, 70 nm, 80 nm, 90 nm, 100 nm, 150 nm, 200 nm, 300 nm, 400 nm, 500 nm, 600 nm, 700 nm, or 800 nm, or a size within a range bounded by any two of the foregoing exemplary sizes.
(40) Typically, the primary and/or aggregate magnetic nanoparticles or BNCs thereof have a distribution of sizes, i.e., they are generally dispersed in size, either narrowly or broadly dispersed. In different embodiments, any range of primary or aggregate sizes can constitute a major or minor proportion of the total range of primary or aggregate sizes. For example, in some embodiments, a particular range of primary particle sizes (for example, at least 1, 2, 3, 5, or 10 nm and up to 15, 20, 25, 30, 35, 40, 45, or 50 nm) or a particular range of aggregate particle sizes (for example, at least 5, 10, 15, or 20 nm and up to 50, 100, 150, 200, 250, or 300 nm) constitutes at least or above 50%, 60%, 70%, 80%, 90%, 95%, 98%, 99%, or 100% of the total range of primary particle sizes. In other embodiments, a particular range of primary particle sizes (for example, less than 1, 2, 3, 5, or 10 nm, or above 15, 20, 25, 30, 35, 40, 45, or 50 nm) or a particular range of aggregate particle sizes (for example, less than 20, 10, or 5 nm, or above 25, 50, 100, 150, 200, 250, or 300 nm) constitutes no more than or less than 50%, 40%, 30%, 20%, 10%, 5%, 2%, 1%, 0.5%, or 0.1% of the total range of primary particle sizes.
(41) The aggregates of magnetic nanoparticles (i.e., aggregates) or BNCs thereof can have any degree of porosity, including a substantial lack of porosity depending upon the quantity of individual primary crystallites they are made of. In particular embodiments, the aggregates are mesoporous by containing interstitial mesopores (i.e., mesopores located between primary magnetic nanoparticles, formed by packing arrangements). The mesopores are generally at least 2 nm and up to 50 nm in size. In different embodiments, the mesopores can have a pore size of precisely or about, for example, 2, 3, 4, 5, 10, 12, 15, 20, 25, 30, 35, 40, 45, or 50 nm, or a pore size within a range bounded by any two of the foregoing exemplary pore sizes. Similar to the case of particle sizes, the mesopores typically have a distribution of sizes, i.e., they are generally dispersed in size, either narrowly or broadly dispersed. In different embodiments, any range of mesopore sizes can constitute a major or minor proportion of the total range of mesopore sizes or of the total pore volume. For example, in some embodiments, a particular range of mesopore sizes (for example, at least 2, 3, or 5, and up to 8, 10, 15, 20, 25, or 30 nm) constitutes at least or above 50%, 60%, 70%, 80%, 90%, 95%, 98%, 99%, or 100% of the total range of mesopore sizes or of the total pore volume. In other embodiments, a particular range of mesopore sizes (for example, less than 2, 3, 4, or 5 nm, or above 10, 15, 20, 25, 30, 35, 40, 45, or 50 nm) constitutes no more than or less than 50%, 40%, 30%, 20%, 10%, 5%, 2%, 1%, 0.5%, or 0.1% of the total range of mesopore sizes or of the total pore volume.
(42) The magnetic nanoparticles can have any of the compositions known in the art. In some embodiments, the magnetic nanoparticles are or include a zerovalent metallic portion that is magnetic. Some examples of such zerovalent metals include cobalt, nickel, and iron, and their mixtures and alloys. In other embodiments, the magnetic nanoparticles are or include an oxide of a magnetic metal, such as an oxide of cobalt, nickel, or iron, or a mixture thereof. In some embodiments, the magnetic nanoparticles possess distinct core and surface portions. For example, the magnetic nanoparticles may have a core portion composed of elemental iron, cobalt, or nickel and a surface portion composed of a passivating layer, such as a metal oxide or a noble metal coating, such as a layer of gold, platinum, palladium, or silver. In other embodiments, metal oxide magnetic nanoparticles or aggregates thereof are coated with a layer of a noble metal coating. The noble metal coating may, for example, reduce the number of charges on the magnetic nanoparticle surface, which may beneficially increase dispersibility in solution and better control the size of the BNCs. Noble metal coating protects the particles against oxidation, solubilization by leaching or by chelation when chelating organic acids such as citrate, malonate, tartrate for examples are used in the biochemical reactions or processes. The passivating layer can have any suitable thickness, and particularly, at least, up to, or less than, for example, 0.1 nm, 0.2 nm, 0.3 nm, 0.4 nm, 0.5 nm, 0.6 nm, 0.7 nm, 0.8 nm, 0.9 nm, 1 nm, 2 nm, 3 nm, 4 nm, 5 nm, 6 nm, 7 nm, 8 nm, 9 nm, or 10 nm, or a thickness in a range bounded by any two of these values.
(43) In particular embodiments, the magnetic nanoparticles have an iron oxide composition. The iron oxide composition can be any of the magnetic or superparamagnetic iron oxide compositions known in the art, e.g., magnetite (Fe.sub.3O.sub.4), hematite (-Fe.sub.2O.sub.3), maghemite (-Fe.sub.2O.sub.3), or a spinel ferrite according to the formula AB.sub.2O.sub.4, wherein A is a divalent metal (e.g., Zn.sup.2+, Ni.sup.2+, Mn.sup.2+, Co.sup.2+, Ba.sup.2+, Sr.sup.2+, or combination thereof) and B is a trivalent metal (e.g., Fe.sup.3+, Cr.sup.3+, or combination thereof).
(44) In some embodiments, the magnetic nanoparticles or aggregates thereof or BNCs thereof reside on the surface of ferromagnetic sub-micrometric particles. By residing on the surface of ferromagnetic microparticles, the magnetic nanoparticles or aggregates or BNCs are attached to the surface of the ferromagnetic microparticles by any suitable associative, adsorptive, or bonding interaction. The ferromagnetic microparticles may or may not be coated with a metal oxide or noble metal coating layer. Moreover, the ferromagnetic microparticles may possess any suitable surface groups, as well known in the art, which may promote attachment of the magnetic nanoparticles thereto. In different embodiments, the ferromagnetic microparticles have a size of about, precisely, or at least 20, 30, 40, or 50, 60, 70, 80, 90, 100, 100, 200, 300, 400, 500, 600, 700, 800, 900, 1000 nm, or a size within a range bounded by any two of the foregoing exemplary sizes. By virtue of their larger size (ultrastructure), BNCs attached onto the surface of ferromagnetic particles can be more easily captured by an external magnetic field. The larger size also helps to preserve enzymatic activities. These bigger magnetic particles can be easily captured by external magnetic fields. BNCs attached onto the surface of ferromagnetic submicrometric particles are not prone to over aggregation when subjected to magnetic fields.
(45) The magnetic nanoparticles or aggregates thereof or BNCs thereof possess any suitable degree of magnetism. For example, the magnetic nanoparticles or aggregates thereof or BNCs thereof can possess a saturated magnetization (M.sub.s) of at least or up to 5, 10, 15, 20, 25, 30, 40, 45, 50, 60, 70, 80, 90, or 100 emu/g. The magnetic nanoparticles or aggregates thereof preferably possess a remanent magnetization (M.sub.r) of no more than (i.e., up to) or less than 5 emu/g, and more preferably, up to or less than 4 emu/g, 3 emu/g, 2 emu/g, 1 emu/g, 0.5 emu/g, or 0.1 emu/g. The surface magnetic field of the magnetic nanoparticles or aggregates thereof can be about or at least, for example, 5, 10, 50, 100, 200, 300, 400, 500, 600, 700, 800, 900, or 1000 Gauss (G), or a magnetic field within a range bounded by any two of the foregoing values.
(46) The magnetic nanoparticles or aggregates thereof can be made to adsorb a suitable amount of FRP enzyme, up to or below a saturation level, depending on the application, to produce the resulting BNC. In different embodiments, the magnetic nanoparticles or aggregates thereof may adsorb about, at least, up to, or less than, for example, 1, 5, 10, 15, 20, 25, or 30 pmol/m.sup.2 of FRP enzyme. Alternatively, the magnetic nanoparticles or aggregates thereof may adsorb an amount of FRP enzyme that is about, at least, up to, or less than, for example, 10%, 20%, 30%, 40%, 50%, 60%, 70%, 80%, 90%, or 100% of a saturation level.
(47) The magnetic nanoparticles or aggregates thereof or BNCs thereof possess any suitable pore volume. For example, the magnetic nanoparticles or aggregates thereof can have a pore volume of about, at least, up to, or less than, for example, 0.01, 0.05, 0.1, 0.15, 0.2, 0.25, 0.3, 0.35, 0.4, 0.45, 0.5, 0.55, 0.6, 0.65, 0.7, 0.75, 0.8, 0.85, 0.9, 0.95, or 1 cm.sup.3/g, or a pore volume within a range bounded by any two of the foregoing values.
(48) The magnetic nanoparticles or aggregates thereof or BNCs thereof possess any suitable specific surface area. For example, the magnetic nanoparticles or aggregates thereof can have a specific surface area of about, at least, up to, or less than, for example, 50, 60, 70, 80, 90, 100, 110, 120, 130, 140, 150, 160, 170, 180, 190, or 200 m.sup.2/g.
(49) The FRP enzyme can be any enzyme that produces free radicals. Moreover, the FRP enzyme can be from any source, e.g., fungal, microbial, animal, or plant. In particular embodiments, the FRP enzyme is an oxidoreductase belonging to the EC 1 family of enzymes. The EC 1 oxidoreductase can be, for example, an EC 1.1 oxidoreductase acting on the CHOH groups of donors, an EC 1.2 oxidoreductase acting on the aldehyde or oxo group of donors, an EC 1.3 oxidoreductase acting on the CHCH group of donors, an EC 1.4 oxidoreductase acting on the CHNH.sub.2 group of donors, an EC 1.5 oxidoreductase acting on the CHNH group of donors, an EC 1.6 oxidoreductase acting on NADH or NADPH, an EC 1.7 oxidoreductase acting on various nitrogeneous compounds as donors, an EC 1.8 oxidoreductase acting on a sulfur group as donor, an EC 1.9 oxidoreductase acting on a heme group of donors, an EC 1.10 oxidoreductase acting on diphenols and related substances as donors, an EC 1.11 oxidoreductase acting on peroxide as an acceptor, an EC 1.12 oxidoreductase acting on hydrogen as a donor, an EC 1.13 oxidoreductase acting on single donors with incorporation of molecular oxygen (oxygenases), an EC 1.14 oxidoreductase acting on paired donors with incorporation or reduction of molecular oxygen, an EC 1.15 oxidoreductase acting on superoxide as an acceptor, an EC 1.16 oxidoreductase that oxidize metal ions, an EC 1.17 oxidoreductase acting on CH or CH.sub.2 groups, an EC 1.18 oxidoreductase acting on iron-sulfur proteins as a donor, an EC 1.19 oxidoreductase acting on reduced flavodoxin as a donor, an EC 1.20 oxidoreductase acting on phosphorus or arsenic as a donor, an EC 1.21 oxidoreductase acting on XH and YH to form an XY bond, an EC 1.97 oxidoreductase, an EC 1.98 oxidoreductase that uses hydrogen as a reductant, and an EC 1.99 oxidoreductase that uses oxygen as an oxidant. The oxidoreductase may also be more particularly identified as belonging to a sub-genus of any of the EC 1.1 groupings provided above.
(50) In a first particular set of embodiments, the FRP enzyme is selected from the EC 1.1 genus of oxidoreductase enzymes. The EC 1.1 enzyme can further be identified as belonging to any of the following sub-genuses: EC 1.1.1 with NAD or NADP as acceptor, EC 1.1.2 with a cytochrome as acceptor, EC 1.1.3 with oxygen as acceptor, EC 1.1.4 with disulfide as acceptor, EC 1.1.5 with quinone or similar compound as acceptor, and EC 1.1.99 with other acceptors. In more particular embodiments, the FRP enzyme is identified as belonging to a sub-genus of any of the EC 1.1 sub-genuses provided above. For example, the FRP enzyme can be identified as belonging to any of the sub-genuses of EC 1.1.3, such as EC 1.1.3.3 (malate oxidase), EC 1.1.3.4 (glucose oxidase), EC 1.1.3.5 (hexose oxidase), EC 1.1.3.6 (cholesterol oxidase), EC 1.1.3.7 (aryl-alcohol oxidase), EC 1.1.3.8 (L-gulonolactone oxidase), EC 1.1.3.9 (galactose oxidase), EC 1.1.3.10 (pyranose oxidase), EC 1.1.3.11 (L-sorbose oxidase), EC 1.1.3.12 (pyridoxine 4-oxidase), EC 1.1.3.13 (alcohol oxidase), EC 1.1.3.14 (catechol oxidase), EC 1.1.3.15 (2-hydroxy acid oxidase), EC 1.1.3.16 (ecdysone oxidase), EC 1.1.3.17 (choline oxidase), EC 1.1.3.18 (secondary-alcohol oxidase), EC 1.1.3.19 (4-hydroxymandelate oxidase), EC 1.1.3.20 (long-chain alcohol oxidase), EC 1.1.3.21 (glycerol-3-phosphate oxidase), EC 1.1.3.22, EC 1.1.3.23 (thiamine oxidase), EC 1.1.3.24 (L-galactonolactone oxidase), EC 1.1.3.25, EC 1.1.3.26, EC 1.1.3.27 (hydroxyphytanate oxidase), EC 1.1.3.28 (nucleoside oxidase), EC 1.1.3.29 (N-acylhexosamine oxidase), EC 1.1.3.30 (polyvinyl alcohol oxidase), EC 1.1.3.31, EC 1.1.3.32, EC 1.1.3.33, EC 1.1.3.34, EC 1.1.3.35, EC 1.1.3.36, EC 1.1.3.37 D-arabinono-1,4-lactone oxidase), EC 1.1.3.38 (vanillyl alcohol oxidase), EC 1.1.3.39 (nucleoside oxidase, H.sub.2O.sub.2 forming), EC 1.1.3.40 (D-mannitol oxidase), and EC 1.1.3.41 (xylitol oxidase).
(51) In a second particular set of embodiments, the FRP enzyme is selected from the EC 1.10 genus of oxidoreductase enzymes. The EC 1.10 enzyme can further be identified as belonging to any of the following sub-genuses: EC 1.10.1 with NAD or NADP as acceptor EC 1.10.2 with cytochrome as acceptor, EC 1.10.3 with oxygen as acceptor, and EC 1.10.99 with other acceptors. The EC 1.10.1 enzyme can be more specifically, for example, EC 1.10.1.1, i.e., trans-acenaphthene-1,2-diol dehydrogenase. The EC 1.10.2 enzyme can be more specifically, for example, EC 1.10.2.1 (cytochrome-b5 reductase) or EC 1.10.2.2 (cytochrome-c reductase). The EC 1.10.3 enzyme can be more specifically, for example, EC 1.10.3.1 (catechol oxidase), EC 1.10.3.2 (laccase), EC 1.10.3.3 (L-ascorbate oxidase), EC 1.10.3.4 (o-aminophenol oxidase), EC 1.10.3.5 (3-hydroxyanthranilate oxidase), EC 1.10.3.6 (rifamycin-B oxidase), EC 1.10.3.7, or EC 1.10.3.8. The EC 1.10.99 enzyme can be more specifically, for example, EC 1.10.99.1 (plastoquinol-plastocyanin reductase), EC 1.10.99.2 (ribosyldihydronicotinamide dehydrogenase, quinone), or EC 1.10.99.3 (violaxanthin de-epoxidase).
(52) In a third particular set of embodiments, the FRP enzyme is selected from the EC 1.11 genus of oxidoreductase enzymes. The EC 1.11 enzyme can further be identified as belonging to the sub-genus EC 1.11.1 (peroxidases). The EC 1.11.1 enzyme can be more specifically, for example, EC 1.11.1.1 (NADH peroxidase), EC 1.11.1.2 (NADPH peroxidase), EC 1.11.1.3 (fatty acid peroxidase), EC 1.11.1.4, EC 1.11.1.5 (cytochrome-c peroxidase), EC 1.11.1.6 (catalase), EC 1.11.1.7 (peroxidase), EC 1.11.1.8 (iodide peroxidase), EC 1.11.1.9 (glutathione peroxidase), EC 1.11.1.10 (chloride peroxidase), EC 1.11.1.11 (L-ascorbate peroxidase), EC 1.11.1.12 (phospholipid-hydroperoxide glutathione peroxidase), EC 1.11.1.13 (manganese peroxidase), EC 1.11.1.14 (diarylpropane peroxidase), or EC 1.11.1.15 (peroxiredoxin).
(53) In particular embodiments, the FRP enzyme is a peroxidase. The peroxidase may also be further specified by function, e.g., a lignin peroxidase, manganese peroxidase, or versatile peroxidase. The peroxidase may also be specified as a fungal, microbial, animal, or plant peroxidase. The peroxidase may also be specified as a class I, class II, or class III peroxidase. The peroxidase may also be specified as a myeloperoxidase (MPO), eosinophil peroxidase (EPO), lactoperoxidase (LPO), thyroid peroxidase (TPO), prostaglandin H synthase (PGHS), glutathione peroxidase, haloperoxidase, catalase, cytochrome c peroxidase, horseradish peroxidase, peanut peroxidase, soybean peroxidase, turnip peroxidase, tobacco peroxidase, tomato peroxidase, barley peroxidase, or peroxidasin. In particular embodiments, the peroxidase is horseradish peroxidase.
(54) In some embodiments, a single FRP enzyme is used. In other embodiments, a combination of FRP enzymes is used, such as any two or three oxidoreductase enzymes selected from any of the above classes or sub-classes therein. In some embodiments, a combination of FRP enzymes (e.g., EC 1 enzymes) is used. In particular embodiments, a combination of EC 1.1 enzymes is used. In other particular embodiments, a combination of EC 1.10 enzymes is used. In other particular embodiments, a combination of EC 1.11 enzymes is used. In other embodiments, a combination of any of the particular FRP enzymes described above and a peroxidase is used (e.g., a combination of a EC 1.1 or EC 1.1.3 enzyme and a peroxidase). When a combination of FRP enzymes is used, the two or more enzymes may be arranged in a core-shell type of arrangement, i.e., a first FRP enzyme is either in a core portion or surface portion of the magnetic nanoparticle or aggregate thereof, and a second (different) FRP enzyme covers the region where the first FRP enzyme is located. The second FRP enzyme may be an aggregate of the magnetic nanoparticle or on the surface thereof, overlaying the first enzyme. In the case of multiple enzyme systems, manipulating the distribution of the different enzymes within the mesoporous aggregates offers the advantage of decoupling the different reactions and permitting diffusion of the substrates and products of the reactions from one layer to another layer or to the core of the BNCs. Therefore, when performing the enzymatic reactions in the confined pore structures of the BNCs, core/shell distributions offer the possibility of better controlling the kinetics of the different entrapped FRP enzymes. Combining enzymes that perform similar reactions (such as two, or more, peroxidases or a peroxidase and a laccase for example) but having different reaction requirements (substrates, substrate concentration, etc.) can beneficially increase the versatility of the BNCs to perform in broad and variable process conditions at a high level of efficiency. Combining enzymes with coupled reactions can ensure the production of the substrate in the vicinity of the enzyme and bypass the need for hazardous and labile chemical substrates, such as hydrogen peroxide. For example, a glucose oxidase enzyme can generate hydrogen peroxide from glucose, which is an inexpensive and non-hazardous compound.
(55) The invention is also directed to methods of producing the enzyme-included (i.e., enzyme-bound, enzyme-trapped, or enzyme-embedded) magnetic nanoparticles and aggregates thereof. In particular embodiments, the enzyme-included magnetic nanoparticles or aggregates thereof are prepared by including an FRP enzyme in the reaction conditions used for preparing the magnetic nanoparticles or aggregates. For example, an FRP enzyme can be included in the process of generating metallic nanoparticles (e.g., cobalt, nickel, or iron) or metal oxide magnetic nanoparticles (e.g., an oxide of cobalt, nickel, or iron). Synthetic methods for producing metallic and metal oxide magnetic nanoparticles are well known in the art. One known method for producing metallic nanoparticles includes the reduction of metal ions (e.g., as a metal salt) in solution. The reduction can be accomplished by, for example, a reductive chemical method (e.g., by reaction with a reducing agent, such as hydrogen, a borane, hydrazine, hypophosphate, or citrate) or a reductive or decompositional physical method (e.g., sonication or thermal treatment in solution). The method may alternatively decompose a zerovalent metal complex (e.g., a Ni carbonyl or phosphine complex) by, for example, sonication, thermal treatment, or exposure to a radiative source, such as ultraviolet light. A particular known method for producing metal oxide magnetic nanoparticles involves alkaline reaction with a metal salt (e.g., a metal halide) under conditions where metal oxide nanoparticles precipitate. For example, by well-established procedures, iron oxide nanoparticles can be produced by co-precipitation of iron (II) and iron (III) ions (e.g., as found in FeCl.sub.2 and FeCl.sub.3) in solution by reaction with a base, such as NaOH. The FRP enzyme can be included in any such method, as long as the method is not substantially detrimental to the activity of the FRP enzyme.
(56) In other embodiments, the magnetic nanoparticles or aggregates thereof are first prepared, and then FRP enzyme is included on or in the magnetic nanoparticles or aggregates thereof. Particularly in the situation where the magnetic nanoparticles or aggregates are porous, the FRP enzyme can be embedded into the pores of the magnetic nanoparticles or aggregates in an aqueous-based solution by simple diffusion, adsorption, or self-assembly. In other embodiments, the surfaces and/or pores of the magnetic nanoparticles or aggregates thereof are derivatized with a bonding agent that causes or promotes bonding of the FRP enzyme to the magnetic nanoparticles or aggregates thereof. The bonding agent can be, for example, a difunctional linker that possesses a reactive end that binds to the magnetic nanoparticle and another reactive end that binds to the FRP enzyme. In the case of metallic nanoparticles, the reactive end that binds to the magnetic nanoparticle can be, for example, an amino, mercapto, mercaptoether, or phosphine group. In the case of metal oxide nanoparticles, the reactive end that binds to the magnetic nanoparticle can be, for example, a phosphate, phosphonate, sulfate, or sulfonate group. In either case, the reactive end that binds to the FRP enzyme can be, for example, any of the amine-reactive groups (e.g., N-hydroxysuccinimide group) known in the art, or any of the other groups known in the art for conjugating an enzyme or other protein to another moiety. The bonding agent may alternatively be, for example, based on affinity coupling, e.g., producing a magnetic nanoparticle-biotin or -avidin conjugate and reacting this with a FRP-avidin or -biotin conjugate, respectively.
(57) The magnetic nanoparticles or aggregates thereof or BNCs thereof may also be coated with a noble metal, such as gold, platinum, or palladium. Any suitable method for coating the magnetic nanoparticles may be used. For example, in particular embodiments, magnetic nanoparticles are dispersed in a solution containing a noble metal salt, and the noble metal salt subjected to reducing conditions. The foregoing method can be facilitated by binding difunctional molecules onto the surface of the magnetic nanoparticles before the noble metal salt is reduced. The difunctional molecules used for this purpose should contain a portion useful for binding to the magnetic nanoparticles (as described above) as well as a noble metal binding portion (e.g., an amine, thiol, phosphine, or chelating moiety) for binding noble metal ions. Optionally, once metal ions are bound to the nanoparticle surface, the magnetic nanoparticles can be washed of excess noble metal salt (e.g., by filtration or decanting). Since noble metal ions are attached to the surface, the foregoing methodology provides a more selective method for producing a noble metal coating (i.e., without concomitant production of noble metal nanoparticles) as well as a more uniform coating. In some embodiments, the noble metal coating is applied before FRP enzyme is included with the magnetic nanoparticles, in which case FRP enzyme is later bonded to the noble metal coating. The FRP enzyme can be bonded to the noble metal coating by, for example, functionalizing the noble metal coating with difunctional molecules that bind to the noble metal coating and possess another reactive group for binding to the FRP enzyme.
(58) The enzyme-containing magnetic nanoparticles or aggregates thereof, or noble-metal coated versions thereof, may also be bonded or adhered onto (i.e., be made to reside onto) the surface of ferromagnetic microparticles. In one embodiment, the enzyme-containing magnetic nanoparticles or aggregates thereof, or noble-metal coated versions thereof, are made to adhere onto the surface of ferromagnetic microparticles by contacting them in an aqueous-based solution and allowing the nanoparticles to adhere onto the surface of the microparticles. In other embodiments, the nanoparticles and microparticles are suitably functionalized with surface agents to facilitate a binding interaction, which may be based on, for example, covalent, ionic, affinity, hydrogen bonding, or van der Waals (dispersion) interactions.
(59) In another aspect, the invention is directed to a process for depolymerizing lignin, i.e., a lignin depolymerization process, in which any of the enzyme-bound magnetic nanoparticles or aggregates thereof (i.e., BNCs) described above is used for depolymerizing or facilitating the depolymerization of lignin. The lignin being depolymerized can be any lignin-containing material. The precursor lignin can be any of a wide variety of lignin compositions found in nature or as known in the art.
(60) As known in the art, there is no uniform lignin composition found in nature. Lignin is a random polymer that shows significant compositional variation between plant species. Many other conditions, such as environmental conditions, age, and method of processing, influence the lignin composition. Lignins differ mainly in the ratio of three alcohol units, i.e., p-coumaryl alcohol, guaiacyl alcohol, and sinapyl alcohol. The polymerization of p-coumaryl alcohol, coniferyl alcohol, and sinapyl alcohol forms the p-hydroxyphenyl (H), guaiacyl (G) and syringyl (S) components of the lignin polymer, respectively. The precursor lignin can have any of a wide variety of relative weight percents (wt %) of H, G, and S components. Besides the natural variation of lignins, there can be further compositional variation based on the manner in which the lignin has been processed. For example, the precursor lignin can be a Kraft lignin, sulfite lignin (i.e., lignosulfonate), or a sulfur-free lignin.
(61) Lignin is the most abundant aromatic based biopolymer on Earth, but it is chemically recalcitrant to conversion and bioconversion due to the apparent randomness of its chemical composition and physical structure. Lignin can be considered a glue or epoxy between polysaccharide fibers that provides strength, rigidity, and protection to the cell walls of vascular plants. From a chemical standpoint, lignin is a highly heterogeneous polymer formed by the polymerization of phenyl-propanoid molecules including coniferyl, sinapyl and coumaryl alcohols via aryl linkages, ether linkages, and carbon-carbon bonds.
(62) Based on the assumption that 100 gallons of ethanol are produced from 1 ton of biomass and that biomass (e.g., wood and grass) contains on average about 20% lignin, one can quickly estimate that a biorefinery operating on a 100 million gallon per year capacity would produce about 200,000 tons of lignin material. To meet a 20% replacement of gasoline for the U.S. only by 2020, equivalent to about 35 billion gallons of ethanol, a total of approximately 700 million tons of lignin would be produced per year. The actual production of lignin, mostly Kraft lignin as byproduct of the paper industry, is approximately 90 million tons per year worldwide. In other words, the lignin production worldwide would be increased by more than an order of magnitude.
(63) Lignin can be used for low- or high-priced products based on the application and the degree of chemical purity. Until recently, markets for lignin products have not been large, competitive, or attractive enough to compensate for the cost of isolation and purification compared to the recovered energy derived from its burning. This is mainly because the cost of oil is still low enough and the supplies are high enough to provide the building blocks for the chemical and material industries. However, in a carbohydrate economy framework based on biofuels and bioproducts co-production, high-purity isolated lignin dedicated for conversion could be estimated at $1.10 per kg of raw material compared to $0.04, when used for co-firing. Low-end applications are mostly directed to dispersants, soil conditioners for carbon sequestration, adsorbents for fertilizers and pesticides, as well as fuels, which require little or no further conversion after extraction. High-end applications requiring depolymerization of lignin include the production of phenolic precursors (DMSO, vanillin, phenol, and aromatic compounds) and polymer components (e.g., epoxy resins, polyurethane foams, phenolic resins powders, carbon fibers and glue and binders).
(64) In nature, the conversion of lignin is performed by specialist microbes, particularly fungi and bacteria. Lignocellulosic bacteria and fungus have the ability to depolymerize lignin in order to gain access to cellulosic fractions of biomass. To that end, lignocellulosic bacteria and fungus excrete an array of oxidoreductase enzymes, which include laccases, oxidases, and peroxidases, along with organic acids and H.sub.2O.sub.2-producing catalases. The most potent oxidoreductase enzymes are produced by a specific group of fungi known as white rot fungi, which specialize in lignocellulosic degradation. Various types of fungal peroxidases differ in the nature of their substrates.
(65) Lignin peroxidase (LiP, E.C. 1.11.1.14) catalyzes the oxidative cleavage of CC bonds in a number of model compounds, and oxidizes benzyl alcohols to aldehydes or ketones. Typical reactions catalyzed by lignin peroxidases are CaCa cleavage, Ca oxidation, alkyl aryl cleavage, aromatic ring cleavage, demethylation, hydroxylation and polymerization. Lignin peroxidases are involved in the oxidative breakdown of lignin in white-rot basidiomycetes. Lignin peroxidase catalyzes the oxidation of non-phenolic aromatic rings into aryl cation radicals by H.sub.2O.sub.2. A typical example is the oxidation of veratryl alcohol (3,4-dimethoxybenzyl alcohol) into veratryl aldehyde (3,4-dimethoxybenz aldehyde) via the intermediary formation of veratryl cation and benzyl radicals: veratryl alcohol+H.sub.2O.sub.2.fwdarw.veratryl aldehyde+2H.sub.2O. Manganese peroxidase (MnP; E.C. 1.11.1.13) has lower redox potentials (up to 1.1 V) than LiP (up to 1.5 V) and catalyzes the Mn-mediated oxidation of lignin and phenolic compounds. This enzyme catalyzes the oxidation of Mn(II) to Mn(III) by H.sub.2O.sub.2. The highly reactive Mn(III) is stabilized via chelation in the presence of dicarboxylic acid: 2Mn(II)+2H.sup.++H.sub.2O.sub.2.fwdarw.2Mn(III)+2H.sub.2O. The purpose of MnP is to generate small and potent oxidizing agents that diffuse into the lignified cell wall and achieve depolymerization of lignin from within. Versatile peroxidase (syn. hybrid peroxidase, manganese-lignin peroxidase: VeP EC 1.11.1.16) is a fairly new ligninolytic enzyme, combining catalytic properties of manganese peroxidase (oxidation of Mn(II)), lignin peroxidase (Mn-independent oxidation of non-phenolic aromatic compounds) and plant peroxidase (oxidation of hydroquinones and substituted phenols). Any one or a combination of the above-mentioned peroxidases may be used in the lignin depolymerization process described herein.
(66) In a first embodiment, the lignin-containing material is a form of lignin partially or substantially separated from other components of wood (e.g., cellulosic and hemicellulosic components), as is generally provided from a pretreatment process of lignocellulosic material, the details of which are well known in the art of lignocellulosic processing and conversion. The pretreatment process serves to either separate lignin from other components of the lignin-containing source, or to weaken the bonds between lignin and the other components. As is also well known in the art, the lignin may be further isolated by, for example, extraction. In a second embodiment, the lignin-containing material is a lignin-containing consumable product, such as paper or cardboard, which may or may not be pretreated. In a third embodiment, the lignin-containing material is a lignin-containing natural source (i.e., raw lignocellulosic material), such as woodchips, grasses (e.g., switchgrass and mixed grasses), corn stover (e.g., leaves, husks, stalks, or cobs of corn plants), sugarcane, saw dust, hemp, or a combination thereof, all of which are generally pretreated to make the lignin sufficiently available for depolymerization.
(67) In the lignin depolymerization process, any of the enzyme-bound magnetic nanoparticles or aggregates thereof, described above, is contacted with a lignin-containing material under conditions where partial or complete depolymerization of lignin occurs by free-radical activity of the enzyme-bound magnetic nanoparticles or aggregates thereof. The enzyme-bound magnetic nanoparticles or aggregates thereof and the lignin-containing material are generally made to contact by combining them in an aqueous solution, such as an aqueous solution used in a pretreatment process of the lignin-containing material. In some embodiments, a room temperature condition (e.g., at least 15, 18, 20, or 22 C. and up to 25 C. or 30 C.) is used during the depolymerization process. In other embodiments, an elevated temperature condition (e.g., above 30 C., or at least or above 35, 40, 45, 50, or 60 C., or up to the temperature that the FRP enzyme degrades or suffers a substantial loss in activity) is used during the depolymerization process. In other embodiments, a reduced temperature condition (e.g., below 15 C., or up to or below 10, 5, or 0 C.) is used during the depolymerization process. By being depolymerized, the lignin is broken down into shorter segments compared to its original form. A complete depolymerization results in the conversion of all or a substantial portion (e.g., at least 80, 90, or 95%) of the lignin into at least one or more of the basic building blocks of lignin, i.e., coniferyl, sinapyl, and coumaryl alcohols, and derivatives thereof. A partial depolymerization generally results in less than 80%, or up to 70, 60, 50, 40, 30, 20, 10, 5, or 1% of lignin being converted to primary building blocks, with the rest of the lignin being converted to segments containing two, three, four, or a higher multiplicity (even up to 10, 20, 50, 100, 200, 500, or 1000) of building blocks (e.g., p-hydroxyphenyl, guaiacyl, and syringyl units derived from coumaryl, coniferyl, and sinapyl alcohols, respectively). Since different degrees of lignin depolymerization may be preferred for different applications, the depolymerization conditions can be suitably adjusted to provide an appropriate degree of depolymerization or to favor one or more types of depolymerization products over others.
(68) Since each lignin-containing material has a different distribution and relative amount of each building block, the relative amount of each product produced from depolymerization is very much dependent on the type of lignin-containing material. Other depolymerization products, e.g., aromatic aldehydes, ketones, alcohols, and acids, are generally also produced during the polymerization process, typically in lesser amounts. In embodiments where such other products are not desired, they may be advantageously minimized or eliminated as a product by adjustment of reaction conditions, including appropriate selection of the FRP-bound magnetic nanoparticle or aggregate thereof.
(69) Any of the enzyme-bound magnetic nanoparticle and aggregate compositions described above can be used for the lignin depolymerization process. In particular embodiments, the FRP enzyme used in the lignin depolymerization process is a peroxidase, and particularly, a lignin-degrading peroxidase, such as a lignin peroxidase, versatile peroxidase, manganese peroxidase, or combination thereof (including a core-shell combination thereof). The FRP enzyme may also more particularly be a fungal, microbial, or plant peroxidase. In specific embodiments, the FRP enzyme is a system of two FRP enzymes, such as a fungal peroxidase combined with a glucose oxidase, or a peroxidase and/or oxidase combined with a laccase.
(70) In some embodiments, the lignin depolymerization process is coupled (i.e., integrated) with a downstream process in which depolymerization product produced in the lignin depolymerization process is used for the production of other products. The downstream process may convert lignin depolymerization product into, for example, biofuel or an industrial chemical product, e.g., a polymer, plastic, polymer precursor (monomer), solvent, adhesive, paint, detergent, lubricant, food product, medicinal product, or aroma, or a precursor therefore. The downstream process may alternatively incorporate the lignin depolymerization product into any such end product.
(71) In some embodiments, the lignin depolymerization process is coupled with an upstream process in which lignin-containing material is provided for use in the lignin depolymerization process described herein. The upstream process can be, for example, a paper or pulp producing process, a biomass-to-biofuel process (i.e., where primarily cellulosic material is hydrolyzed and converted to biofuel), or a biomass-to-ethanol fermentation process (i.e., where primarily cellulosic material is hydrolyzed and converted to ethanol).
(72) In another aspect, the invention is directed to a process for removing aromatic contaminants from water (i.e., a water remediation process). In the process, water contaminated with one or more aromatic substances is contacted with any of the enzyme-bound magnetic nanoparticles or aggregates thereof, described above, to cause the aromatic substances to precipitate, i.e., as insoluble material. The precipitated (i.e., sedimented) material is preferably then further separated, such as by centrifugation or settling, and removed from the water by, for example, filtration or decanting. Without being bound by any theory, it is believed that the aromatic substances react with free radicals produced by the enzyme-bound magnetic nanoparticles to produce a polymerized material derived from the aromatic substances. The aromatic contaminant can be any aromatic substance, including those more commonly found in contaminated water. In some embodiments, the aromatic contaminant is benzene, or a benzene derivative, such as a halogenated benzene (e.g., chlorobenzene, dichlorobenzenes, bromobenzenes, or a polychlorinated biphenyl, i.e., PCB), alkylbenzene (e.g., toluene, ethylbenzene, or a xylene), phenolic substance (e.g., phenol, resorcinol, catechol, or a cresol), etherified benzene (e.g., anisole), fused ring compound (e.g., naphthalene, or polyaromatic hydrocarbon), aniline substance (e.g., aniline and N-alkyl or N,N-dialkyl substituted anilines), or benzoic acid compound (e.g., benzoic acid, esters thereof, and hydroxy-substituted derivatives of benzoic acid). In other embodiments, the aromatic contaminant is a heteroaromatic substance, such as furan, pyran, dioxin, thiophene, pyridine, pyrazine, pyrimidine, pyrrole, imidazole, indole, and derivatives thereof.
(73) Any of the enzyme-bound magnetic nanoparticle and aggregate compositions described above can be used for the water remediation process. In particular embodiments, the FRP enzyme used in the water remediation process is horseradish peroxidase, or horseradish peroxidase in combination with an oxidase.
(74) In another aspect, the invention is directed to a process for polymerizing monomers polymerizable by a free-radical mechanism. In the process, one or more types of monomers are reacted with any of the enzyme-bound magnetic nanoparticles or aggregates thereof, described above, to cause the monomers to polymerize. The monomers can be, for example, any of the substances provided above for the water remediation process. In particular embodiments, the monomers are or include vinyl-addition monomers. Upon polymerization, a vinyl-addition polymer is produced. Some examples of such monomers include ethylene, propylene, butadiene, the acrylates and esters thereof, methacrylates and esters thereof, acrylonitriles, vinyl acetate, styrene, divinylbenzene, vinyl fluorides, and vinyl chlorides. In other embodiments, the monomers are phenolic compounds. Upon polymerization, a phenolic resin or polymer is produced. The polymerization process can utilize any of the conditions and apparatuses well known in the art for practicing polymerization reactions, and in particular, free-radical initiated polymerization reactions.
(75) For any of the processes described above, the enzyme-bound magnetic nanoparticles or aggregates thereof can advantageously be captured by magnetic separation in order to prevent contamination of the final product. Moreover, a further advantage of the enzyme-bound magnetic nanoparticles or aggregates thereof described herein is their ability in many cases to retain their activity and re-form after capture, which permits them to be re-used after capture. BNCs showing a loss of activity after several cycles can advantageously be easily extracted and concentrated to their solid form to provide a less wasteful and more efficient process. Metal-coated BNCs can be repurposed by denaturation of the enzymes, sonication, and purification in order to be restored and re-used with fresh functional enzymes. Micro-Bionanocatalysts (Micro-BNC) made of self-assembled BNCs magnetically trapped on a surface are attractive for process applications that use lower intensity magnetic fields. Larger and denser ferromagnetic particles have a higher mass susceptibility compared to mesoporous and low density aggregates of MNPs. MicroBNCs maintain stable, nanosized, and mesoporous structures, which helps to maintain enzyme activity while increasing the overall density and mass susceptibility of the magnetic catalyst. These ultrastructures lend themselves to easier manipulation by external magnetic fields as produced by permanent small magnets and weak field electromagnets. The reaction solution can be purged and replaced while the Micro-BNCs are magnetically trapped, hence allowing for sequential use of the Micro-BNC as long as the enzyme retains process level activities.
(76) Examples have been set forth below for the purpose of illustration and to describe the best mode of the invention at the present time. However, the scope of this invention is not to be in any way limited by the examples set forth herein.
EXAMPLES
Reagents and Instrumentation
(77) The enzymes used in this study were Horseradish Peroxidase (HRP, E.C. 1.11.1.7, type VI-A), Lignin Peroxidase (LiP, E.C. 1.11.1.14), Manganese Peroxidase (MnP; E.C. 1.11.1.13) Versatile Peroxidase (syn. hybrid peroxidase, manganese-lignin peroxidase: VeP EC 1.11.1.16), and laccase. All enzymes used herein were obtained from commercial sources. Horseradish Peroxidase (HRP, E.C. 1.11.1.7, type VI-A) had a Reinheitszahl index (OD A.sub.403/A.sub.280) of around 2.9. High activity forms were obtained by further purification by FPLC (AKTA Explorer, GE Bioscience) using an anionic exchange column (Resource Q, GE Bioscience). Laccase was used without further purification. Protein signal was monitored at 280 nm and the heme signal at 405 nm. For each enzyme, the fractions with a RZ above 1 were pulled together, concentrated and aliquoted. Phenol, homovanillic acid, veratryl alcohol, methoxylphenol, 4-aminoantipyrine (AAP), glucose (the foregoing being at 98% purity), sodium phosphate buffer (PBS) of pH 7.4 and 67 mM, magnetite microsphere powder, manganese sulfate, hydrogen peroxide, FeCl.sub.3.6H.sub.2O, and FeCl.sub.2.4H.sub.2O, O-phosphoethydiamine, gold tetrachlorohydrate, and malonate and tartrate disodium salts were obtained from commercial sources.
(78) Synthesis of Iron Oxide Magnetic Nanoparticles
(79) Magnetite nanoparticles were synthesized by co-precipitation of Fe.sup.2+ and Fe.sup.3+ under alkaline conditions in a bubbling nitrogen atmosphere at 25 C. (M25) or 90 C. (M90). An acidic solution (25 ml) of the iron salts (2 g of FeCl.sub.2.4H.sub.2O and 5.2 g of FeCl.sub.3.6H.sub.2O) was added dropwise to NaOH (250 ml, 1.5 M) under constant stirring. Non-oxidizing conditions were achieved by bubbling all solutions with nitrogen for 15 minutes prior to reaction. The instantaneous black precipitation of Fe.sub.3O.sub.4 was captured with a neodymium magnet, washed, and neutralized, and kept in distilled water until further use.
(80) Coating of Iron Oxide Magnetic Nanoparticles with Gold
(81) The coating of magnetite nanoparticles was achieved by mild reduction of gold tetrachloroaurate ions onto 0-phosphoethydiamine (OPEA) functionalized MNPs under sonication. The coating procedures were performed under nitrogen using a modified rotary evaporator apparatus coupled to a sonic bath. Briefly, 20 mg of MNPs (1 mg/ml) were sonicated for 30 min. OPEA (2 g) was added and allowed to react with the MNPs (40 mL final volume) under sonication and rotation for 2 hours. OPEA-functionalized MNPs were capture with a rare-earth magnet and rinsed 3 times to remove excess OPEA. OPEA-functionalized MNPs were re-suspended in milliQ water with 100 L of nitric acid (1N) and were agitated for 1H under sonication. Gold tetrachloroaurate (10 up to 30 mg) was added to the OPEA-functionalized MNPs and allowed to react for 30 minutes. The temperature of the sonic bath was raised to 85 C., at which point citric acid/citrate (50:50, 50 mM total, pH5.5) was injected. The gold coating was performed under sonication and fast rotation speed in varying volume (up to 100 mL) and different coating times (up to 60 min). The reaction vessel was placed on ice and the reaction was stopped by adding 5 g of CaCO.sub.3. MNP-OPEA-Au nanoparticles were captured magnetically, rinsed four times to remove excess reagents, and stored until further use.
(82) Bionanocatalyst (BNC) Synthesis
(83) All BNCs were formed with either M90 or M25 magnetite nanoparticles, gold-coated or not. The BNCs were formed with either Horseradish peroxidase, Lignin Peroxidase, Manganese Peroxidase or Versatile Peroxidase. Typical BNC synthesis required the MNPs to be initially monodispersed (i.e., individualized and non-aggregated MNPs). MNPs were sonicated in an ultrasonic bath for 20 minutes at room temperature and used immediately to form the BNCs. In preliminary experiments, the effects of buffer composition, buffer strength, and incubation time were investigated to measure their influence on the formation of the BNCs and the activity of the enzymes. Formation of BNCs in water for more than one hour was found to be the most efficient due to the lack of ionic compensative charges; this protocol was implemented for the rest of the study. The final concentration of the peroxidases used for the assays ranged from 0.1 to 10 nM. It was also found that the increased activity was higher for BNCs with 50% or less saturation (per surface area), and therefore, the quantity of MNPs added to the enzymes were adjusted accordingly. Typically, the final concentrations of MNPs in the assay were between 0.5 and 50 g.Math.ml.sup.1. A typical ratio is 1 nM of enzyme (HRP) for 2 g.Math.ml.sup.1 of MNPs (final concentrations in the assay). The enzyme and the MNPs were added simultaneously and were incubated under constant agitation at 4 C. for at least 12 hours. Typically, the BNCs were formed in stock solution at 5 or 10 times the concentration needed to perform the biochemical reactions. BNCs were finally diluted to the final concentration required in the assay just before the assay. For the synthesis of core/shell poly-enzyme systems BNCs, a core BNC was first formed by reacting the first enzyme (peroxidase or glucose oxidase core enzyme) and sonicated MNPs for 7 hours, then the second enzyme (peroxidase or glucose oxidase=shell enzyme) was added with the appropriate ratio of sonicated MNPs and incubated for a least 7 hours. For random BNCs of glucose oxidase and peroxidase, the sonicated MNPs and enzymes were added simultaneously and incubated for 14 hours.
(84) Micro-Bionanoparticle (Micro-BNC) Synthesis
(85) Micro-BNCs (BNCs) were synthesized by reacting formed BNCs with commercial submicrometric magnetite particles. Submicroparticles were suspended in water and sonicated for 20 minutes in an ultrasonic bath. Preformed BNCs and sonicated microparticles were incubated for 6 hours in water under constant agitation and at 4 C. The quantity of submicrometric commercial particles was at least one order of magnitude higher than the quantity of the MPNs forming BNCs on a weight basis. The capture of the BNCs was considered complete when no nanoparticle was detected in the supernatant after magnetic capture with a small magnet.
(86) Characterization of Magnetic Nanoparticles and Mesoporous Aggregates
(87) Magnetic properties were measured using a MPMS XL (Quantum Design) magnetometer utilizing Superconducting Quantum Interference Device (SQUID) technology. Magnetization hysteresis curves were determined at 300K for external magnetic fields ranging from 40 Oe to 50 kOe. Transmission electron microscopy (TEM) image processing was used to measure the average particle size, size distribution and cluster sizes. TEM measurements were performed with an UHV-STEM microscope (VG, UK). Images were processed using Image Analysis Image J software (NIH, Washington D.C.) and JMicroVision (V1.27). Nanoparticle and cluster size distributions were calculated from a minimum of 1000 particles. Nitrogen adsorption-desorption isotherms were obtained on a Micrometrics ASAP 2020 physisorption instrument. Pore size distributions were calculated from the N.sub.2 adsorption isotherm using the Barrett-Joyner-Halenda (BJH) method.
(88) Elucidation of Magnetic Nanoparticles
(89) The X-ray diffraction pattern shown in
(90) Quantification of Entrapped Enzyme Using Horseradish Peroxidase (HRP)
(91) Quantification of denatured HRP with magnetite nanoparticles was achieved by using a high-throughput FTIR spectrometer (HTS-XT-Vertex70, Bruker, Germany). Fifty microliters of BNC slurry was dried out on a transmittance silicon 96-well plate at 60 C. under vacuum for one hour and left to dry under vacuum at room temperature overnight. The spectra were recorded between 4,000 and 400 cm.sup.1, 32 scans, and the background was recorded before each sample. Samples were analyzed in triplicates; on-plate standards of magnetite and magnetite plus HRP were used to measure the concentration of proteins and nanoparticles in each sample. Adsorption isotherms parameters were extracted by fitting the quadratic form of the Langmuir equation using a least-square fitting method using Matlab software:
(92)
(93) In Formula (1) above, Q is the adsorbed enzyme on the surface (nmol.Math.m.sup.2), C* is the initial enzyme concentration (nmol.Math.m.sup.2), Q.sub.m is the maximum amount of bound enzyme (nmol.Math.m.sup.2), and K.sub.a is the adsorption constant (m.sup.2.Math.mol.sup.1). These parameters were applied in the kinetic experiments to directly calculate the bound fraction of HRP at equilibrium from the initial concentration of HRP.
(94) Characterization of Peroxidase Enzyme Activities
(95) Phenol/AAP Assay:
(96) The peroxidase activity of native HRP and BNC was monitored using the chromogenic phenol/AAP assay that generates phenoxy radicals that readily react with aminopyrene to form the pink-colored quinoneimine dye. An automated plate-reader (Synergy 4, Biotek) with injection capabilities and temperature-controlled chamber was used to record the absorbance of the solution at 510 nm in 96-well plates (4 replicates) for 30 minutes. The standard reagent concentrations of the assay (200 l) were 80 mM and 13 mM for phenol and AAP respectively. Different buffer and buffer strength were tested. Hydrogen peroxide was injected to initiate the reaction with concentrations ranging between 10.sup.7 M and 1 M. The background contribution due to the nanoparticles and substrates was subtracted. For HRP, the quantity of free enzymes was calculated by difference with the bound amount estimated with the Langmuir adsorption parameters as the quantity of free enzyme could not be estimated directly because of low HRP concentrations and high background from the MNPs. For each run, a velocity standard curve was established for the free enzyme and used to correct for the contribution of the free enzyme to the total activity when not all enzyme molecules were bound. The velocities (V) and specific activity, A (mmol.sub.product.Math.s.sup..Math.mmol.sub.enzyme.sup.1) were calculated based on the initial rates of the reaction.
(97) Fungal Peroxidase Activities Using Model Substrates:
(98) Colorimetric assays were performed in 96-well UV transparent microplates (Falcon) using standardized colorimetric protocols in sodium tartrate or malonate (LiP: Veratryl alcohol, pH 3, 310 nm; MnP: 2,6 dimethoxyphenol, pH 4.5, 468 nm and 270 nm for the formation of Mn.sup.3+-organic acid complex; VeP: veratryl alcohol or 2,6 methoxyphenol, pH 4.5, 310 nm, 468 nm, 270 nm).
(99) Peroxidase Activities with Homovanillic Acid (HVA) Fluorescent Assay:
(100) A fluorescent assay was developed to measure the initial rate of the peroxidase kinetics. HVA free radicals can polymerize to form a fluorescent dimer (.sub.ex 310 nm, .sub.em405 nm). An automated sequential procedure was implemented on a Biotek Plate Reader with syringe mixing capabilities to perform the dilution of the reaction initiators (H.sub.2O.sub.2 or glucose). A chemically-reacted stock of fluorescent dimer was synthesized by reacting HVA (10 mM) with sodium ferrocyanide (15 mM) and ammonium hydroxide (15 mM) and was used as quantitative standards in the buffers used for the enzymatic reactions. All the reactions were performed in triplicate and data expressed in relative fluorescent units (mRFU).
(101) Lignin Depolymerization Assays:
(102) A Kraft lignin depolymerization assay was conducted using HRP, LiP, VeP and MnP, and BNCs thereof. MnP and VeP assays were performed in presence of manganese. Assays were performed in triplicates in sodium tartrate or sodium malonate buffer, pH 5.5. Kraft lignin slurries (10 mg/ml) were incubated for 1 or 4 hours then filtered through 0.2 m pore membrane filter to remove particulates. The UV-Vis spectra of the solutions were acquired with a Biotek Plate Reader. The release of aromatic molecules from lignin depolymerization was monitored at 280 and 310 nm. The spectra were corrected for the background.
(103) Phenol Polymerization Assays:
(104) The phenol removal assay was a two-step procedure. The first step consisted in forming polyphenols with Horseradish Peroxidase in 1 mM PBS buffer. Reaction volumes were fixed at 2 ml or 10 mL. The final concentration of phenol was fixed at 1 mM and HRP at 30 nM. The BNCs formed with M90 were varying in enzyme-to-nanoparticles ratio. The second step was the precipitation of these polyphenols by adding sodium chloride (500 mM). The samples were centrifuged at 12,000 g for 20 minutes and the supernatant collected. The soluble phenol in solution was measured at 280 nm with a Biotek Plate Reader.
(105) Kinetic Parameters
(106) The specific activity, A (mmol.sub.product.Math.s.sup.1.Math.mmol.sub.HRP.sup.1), was calculated as the ratio V/mmol.sub.HRP using the extinction of the respective products formed at the wavelength monitored. A H.sub.2O.sub.2 substrate inhibition model derived from the ping-pong bi-bi 2 substrate inhibition model was used to extract the kinetic parameter of the reaction with a least-square fitting method using GraphPad Prism (La Jolla, Calif., USA). The modified equation from the model is:
(107)
(108) In Formula (2), V.sub.max is the maximum enzyme velocity (mmol.Math.s.sup.1), the maximum rate the enzyme reaction can achieve, expressed in the same units as V, K.sub.m is the Michaelis-Menten constant (mM), K.sub.i is the inhibition constant for H.sub.2O.sub.2 (mM). k.sub.cat (s.sup.1) was calculated from V.sub.m and the total quantity of bound HRP.
(109) Formation, Characterization and Activities of Magnetite BNCs Formed with HRP
(110) The entrapping of enzyme molecules in the MNP clusters was confirmed by the overall increase in size of the BNC clusters (
(111) M90 had a higher K.sub.a, thus indicating a higher affinity for the enzyme compared to M25 (
(112) Temporal free-radical concentrations were measured using the phenol/AAP assay, and these measurements were used to calculate the normalized activities of the BNC. Normalized activities were calculated as the ratio of the BNC activity divided by the free enzyme activity at the same concentration. For M90-BNC, the maximum activity compared to the free enzyme was reached after 1 hour of pre-incubation. The increase of normalized activity was shown to be stable over 24 hours. As shown by
(113) Initial reaction velocities were used to estimate K.sub.m, V.sub.max, K.sub.i and k.sub.cat, as further demonstrated by the plots shown in
(114) The M90-BNC activities were further investigated for different buffer, pH, and temperature (
(115) BNCs Activities for Other Enzyme Systems
(116) Activities of Versatile Peroxidase-BNCs:
(117) BNCs were formed with Versatile Peroxidase enzyme (
(118) Activities of Manganese Peroxidase-BNCs:
(119) BNCs were formed with manganese peroxidase (
(120) Activities of Laccase-BNCs:
(121) BNCs were formed with laccase (
(122) Activities of Glucose Oxidase and Peroxidase System:
(123) BNCs were formed with a dual glucose oxidase/peroxidase system (
(124) These new BNCs were further immobilized on larger ferromagnetic magnetite submicrometric particles. Scanning electron microscope (SEM) micrographs of commercial magnetic particles and their surface functionalization with BNCs are shown in
(125) Lignin Depolymerization by Magnetite BNCs Formed with Fungal Peroxidases
(126) Lignin depolymerization using BNCs was demonstrated. A lignin depolymerization assay was conducted in order to detect the production of soluble aromatics (e.g., coniferyl, sinapyl, and coumaryl alcohols or derivatives thereof). As shown by the absorbance plot in
(127) Polymerization of Phenol with BNCs Formed with HRP
(128) Phenol removal using Horseradish Peroxidase using BNCs was demonstrated. As pictographically shown in
(129) While there have been shown and described what are at present considered the preferred embodiments of the invention, those skilled in the art may make various changes and modifications which remain within the scope of the invention defined by the appended claims.