A PRODUCTION METHOD

Abstract

A production method for an electrode including activated carbon. The production method includes the steps of mixing 5-90% by weight of activated carbon granules with a 5-90% by weight of a thermoplastic powder; adding 3-10% by weight of water to the mixture; heating the aqueous mixture to 135-145 C.; stirring the heated mixture at the temperature for a predetermined period of time; pouring the hot mixture into a mold and pressing it at a pressure of 500-2000 bar so as to produce an electrode and removing the produced electrode from the mold so as to allow it to cool down.

Claims

1. A production method of an electrode comprising activated carbon, characterized by comprising the following steps: mixing 5-90% by weight of activated carbon granules with a 5-90% by weight of a thermoplastic powder; adding 3-10% by weight of water to the said mixture; heating the aqueous mixture to 135-145 C.; stirring the heated mixture at the said temperature for a predetermined period of time; pouring the hot mixture into a mold and pressing it at a pressure of 500-2000 bar so as to produce an electrode; removing the produced electrode from the mold so as to allow it to cool down.

2. A production method according to claim 1, characterized in that said thermoplastic is polyethylene.

3. A production method according to claim 1, characterized in that at the step of mixing activated carbon granules and thermoplastic powder, activated carbon granules are, by weight, 85%

4. A production method according to claim 1, characterized in that at the step of mixing activated carbon granules and thermoplastic powder, thermoplastic powder is, by weight, 15%.

5. A production method according to claim 1, characterized in that at the step of adding water to the mixture, the water is, by weight, 5%.

6. A production method according to claim 1, characterized in that at the step of heating the mixture, temperature is 140 C.

7. A production method according to claim 1, characterized in that at the step of pouring the hot mixture into the mold and pressing it, the pressure is 800 bar.

8. A production method according to claim 1, characterized by comprising the step of bringing the activated carbon granules and thermoplastic powder to the desired dimensions before the step of mixing the activated carbon granules with the thermoplastic powder.

Description

DESCRIPTION OF THE INVENTION

[0009] Activated carbon is a material which has a high surface area and which is mainly used for adsorption process and is generally in powder/granule form. In electrosorption applications, activated carbon is used as electrodes. In case activated carbon is used as an electrode, it must have a monolithic structure. In conventional production methods of monolithic activated carbons, the surface area of the activated carbon is reduced while activated carbon granules are combined. Reduction in the surface area of the activated carbon results in a decrease in efficiency in applications where activated carbon is used as an electrode. Therefore, with the present invention, there is provided a production method of an electrode comprising activated carbon granules and having high surface area.

[0010] The production method according to the present invention comprises the steps of mixing 5-90% (preferably 85%) by weight of activated carbon granules with a 5-90% (preferably 15%) by weight of a thermoplastic (i.e. polyethylene) powder; adding 3-10% (preferably 5%) by weight of water to the said mixture; heating the aqueous mixture to 135-145 C. (preferably 140 C.); stirring the heated mixture at the said temperature for a predetermined period of time; pouring the hot mixture into a mold and pressing it at a pressure of 500-2000 bar (preferably 800 bar) so as to produce an electrode; removing the produced electrode from the mold so as to allow it to cool down.

[0011] In the production method according to the present invention, since the said thermoplastic is mixed with powdered activated carbon granules and water, the mixture is made homogeneous. By heating the mixture to 135-145 C., the powdered thermoplastic in the mixture melts and takes liquid form. Since the said temperature is lower than 145 C., the thermoplastic in liquid form is maintained in a thick form. Thus, thermoplastic is not allowed to penetrate into all spaces between the activated carbon granules so that it does not reduce the activated carbon surface area in the electrode produced. Additionally, the water in the mixture ensures that the mixture is homogenous, and also it evaporates during the stirring at the said temperature to allow the mixture to be heated homogenously. In the electrode production method according to the present invention, since the activated carbon granules are not bound onto a carrying material and not sintered, the surface area of activated carbon in the electrodes produced is increased.

[0012] In an illustrative embodiment of the invention, the size of the said active carbon granules is in the range of 0.5-1.5 mm. In another illustrative embodiment, the size of the said thermoplastic powders is in the range of 0.1-0.5 mm. Said size is varied based on the physical properties of the electrode to be produced (i.e. conductivity and iodine index). In a preferred embodiment of the invention, said production method comprises the step of bringing the activated carbon granules and thermoplastic powder to the desired dimensions before the step of mixing the activated carbon granules with the thermoplastic powder. Bringing the activated carbon granules and thermoplastic powder to the desired dimensions is preferably performed by using a sieve. In an illustrative embodiment, activated carbon granules are passed through a sieve and separated into two groups of 0.5-1 mm and 1-1.5 mm. Similarly, said thermoplastic powder is passed through a sieve and separated into two groups of 0.1-0.315 mm and 0.315-0.5 mm. Based on the physical properties of the electrode to be produced, the size of the activated carbon granules and that of the thermoplastic powder to be mixed to each other may vary. In illustrative embodiments, activated carbon granules of 0.5-1 mm and thermoplastic powder of 0.1-0.315 mm; activated carbon granules of 0.5-1 mm and thermoplastic powder of 0.315-0.5 mm; activated carbon granules of 1-1.5 mm and thermoplastic powder of 0.1-0.315 mm; activated carbon granules of 1-1.5 mm and thermoplastic powder of 0.315-0.5 mm may be mixed together. In this manner, the obtained electrode has the desired physical properties.

[0013] In the electrode production method according to the present invention, said molds may be selected based on the shape and size of the electrodes to be produced. In illustrative embodiments, said molds may be cylindrical, elliptic or prismatic.

[0014] In the production method according to the present invention, since the mixture of activated carbon granule, thermoplastic and water is heated to 135-145 C., thermoplastic is prevented from being fluidized and filling the space between the activated carbon granules. Furthermore, thanks to the water in the mixture, the mixture is not only made homogeneous, but also heated homogeneously. In this manner, a high surface area of the activated carbon of the electrode produced as a monolithic structure is achieved.